By Shijie Wang

In pressure oxidation leaching of copper anode slimes, than 65% of the tellurium is m' cxtraoted during decopperizing. About l0- 15% of the selenium is also dissolved simultane¬ously by severe leach conditions. Current operation for the treatment of the leachate is to constantly recirculate the leach solution through a bed of copper turnings. The tellurium and sele¬nium are precipitated from the leach liquor as copper telluride and copper selenide and sepa¬rated from the solution by filtration. In order to improve the reaction efficiency and reduce the process cost, viz, minimize the copper addition, cut retention time, and reduce the energy consumption; a chemical reducing agent is studied and the cementation process tested in the laboratory. In this paper, the test results are presented and the process chemistry is discussed.

Jan 1, 2003

By Run-bo Wang, Zhe Wang, Fan-yi Meng, Jian-Liang Zhang

The influence of semicharcoal substitution for coke breeze on sintering performance was investigated by pot-grate sintering test. At a fixed fuel ratio, sinter productivity and strength decreased with the substitution increasing from 0 to 100% due to better combustibility. To enhance the utilization efficiency of 100% semicharcoal, sintering parameters (moisture and suction pressure) was adjusted. With the moisture increasing, sinter performance of 100% semicharcoal increased because of the suppression of semicharcoal incomplete combustion. As the moisture further increasing to 9.0%, sinter quality gave rise to a decrease trend. The results also showed that the increase of suction pressure was benefit for the increase of heat transfer rate, leading to the improvement of heat utilization energy. Measures to enhance magnetite oxidation during sintering are discussed based on current understanding of the fundamentals that control the sintering process.

Jan 1, 2015

By Tao Zhang, Wen-tao YU, Hai-bin ZUO, Jian-Liang Zhang

Sintering-pot tests and metallurgical performances of sinter with 4 kind of different Al2O3 contents are experimented in this paper. Results show: when the Al2O3 contents increase from 2.0% to 3.5%, acicular calcium ferrites in mine phase will be gradually replaced by plate-like iron calcium. The increase of Al2O3 contents will lead to the addition of liquid viscosity and the reduction of permeability of sinter bed. Sintering time will be prolonged. The rate of yield is stable basically but production is low; besides, the increase of liquid viscosity will decrease of drum strength. The change of permeability of the material layer will make RDI +3.15 decrease first and then increase when Al2O3 contents changed from 2.0% to 3.5%. RI of sinter shows a contrary trend because many open voids are formed by deterioration of liquidity first and then pores closed.

Jan 1, 2015

By Zhenjun Tan, Lei Zhang, Jigang Li, Yifang Zheng, Jilai Xue

"Water electrolysis in 0.4 mol/L NaOH solution for hydrogen generation was carried out with ultrasound introduced through the anode. It was found that the cell voltage reduced by 150-300 mV in the current range of 20 mA to 40 mA with ultrasound frequency at 25.3 kHz. The cell operation became unstable when the cell current was larger than 75 mA with ultrasound. This reduction in cell voltage was due to removal of the gas bubbles on the electrode surface, which can be directly observed in the see-through cell of water electrolysis. Ultrasound with frequency of 33.3 Hz was also tried, but no better effect was obtained. The results suggest that ultrasound assisted water electrolysis can have potential in energy savings for hydrogen production.IntroductionIn electrolytic process, the electrode that the bubbles generated on its surface usually covered a thin gas film, which can be caused an additional voltage about 0.15-0.25V[l,2], especially in aluminum electrolysis. To solve the problem, loading the ultrasound removes the gas bubbles from the electrodes, this subject had been researched in recent years. From 1995 Jilai Xue et al[3,4,5]. applied the ultrasound in aluminum electrolysis in lab. The results from Sheng-De Li et al.[6] reveals that can decrease the cell voltage and have influences about the hydrogen and oxygen's output ratio. Although there are many paper about the applying of ultrasound such as in electrolysis[5,6], deposition[7,8], plating[9,10], oxidation of salts substance on the surface of electrodes[l 1] and so on, the effect of different frequencies ultrasound hadn't been investigated deeply.We focus on the anode voltage by different frequencies ultrasound and the bubble behaviors in this paper. The environment of this experiment is in alkaline solution. Through this exploration it can offer a basis for the applying of ultrasound in electrolysis."

Jan 1, 2011

By Shenghui Guo, Ying Lei, Hao Niu, Huilong Luo, Jinhui Peng, Libo Zhang, Yu Li

"In this work, the combination of microwave drying (MWD) and heat pump drying (HPD) drying experiments were designed by response surface methodology (RSM) based on central composite design (CCD) using design expert software (Version 7.15), and the process parameters were optimized. The conditions given by software are: the MWD time is 4.6 or 4.4 min; the HPD time is 9.0 or 8.6 min; and the sample mass is 620 or 600 g. Under those conditions the moisture content is 1.0 10-2kg water/kg wet basis, and the effectiveness ratio is 0.70 kg water/kwh. The results of confirmatory experiments conducted under the optimized conditions show the combined drying have superiority of decrease of energy consumption and increase of handling capacity over the single MWD or HPD.1 IntroductionSilica sand is one of a silicate mineral with properties as hard, anti-friction and less reactive, commonly used as raw material for foundry and construction. The silica sand obtained from mineral dressing processes such as scrubbing, magnetic separation and flotation. Its moisture content is approximately 0.08~0.12 kg water/kg wet basis. The most common methods used for drying are solar drying and hot air drying. But these methods have some shortcomings: for example, the solar drying has longer process time due to low energy yield, [1] hot air drying has low-energy efficiency and a lengthy drying time. [2]Microwave is electromagnetic waves with frequency are 300MHz to 300GHz. The outstanding features of microwave heating are rapidity and selectivity. The water specific inductive capacity of 60~78 is much bigger than common materials, the moisture always quickly absorb electromagnetic wave and rapidly transfer to vapors. So, it can significant reduce the drying time. [3] Heat pumps (HPs) are devices for raising the temperature of low grade heat energy to a more useful level using a relatively small amount of high grade energy."

Jan 1, 2011

By Takashi Ikeda, Masafumi Maeda

"Demand for solar cells is increasing linearly throughout the world. Last year production totaled 3000 tons worldwide. The market size of solar silicon is expected to increase further because of international ""political"" demand to reduce carbonaceous emission from energy consumed. Most elemental silicon is produced by the carbon reduction of Silica in an electric arc furnace. Purity of silicon at this stage is 90-99%. Major impurities are Fe, Ti, Ca· and Al, and minor ones are P, B and carbon. The oxidizing metallurgical process is no longer effective to remove transitfon metals because those are less noble to silicon. Nonmetallic impurities such as phosphorus and boron must be reduced to 0.001ppm for semiconductor use. The most common process for high purity silicon is the Siemens C process, which is basically distillation of hydro-chlorinated silicon followed by CVD of SiHCl3. The cost of such silicon is expensive to allow its popular use in solar cells. Currently scrap silicon -of semiconductors is used for this; however, the supply-of that scrap is limited to just a portion of semiconductor production.In this paper world demand for silicon will be reviewed and some of the processes proposed summarized.IntroductionSilicon is element 14 in atomic number and has an atomic weight of 28.0855. Little elemental silicon is found in the earth, and it is mostly found as oxides or silicate. The Clark number of silicon is very large and the second in its number. If we were discussing the volatility of silicon element on the globe, we would never worry about it. However, it is very difficult to obtain pure elemental silicon because a high purity silicon compound is very rare. In most cases these are silica (silicon oxide SiO2). As shown in Table 1, there are many grades of silica ore classified mainly by their content of iron and alumina."

Jan 1, 2000

By Rainer Schmid-Fetzer

"Isothermal solidification can be used to form strong bonds at low temperature which remain solid at much higher temperatures. The exploitation of this principally known technique for new high temperature processing steps and applications in electronic assemblies is the aim of this study. Three basically different variants of this bonding process are given. A comprehensive metallurgical screening is performed and the feasibility of binary material systems is given on a quantitative scale. Very attractive systems are spotted that have never been studied before. Detailed examples for the realization of bonding with complex ternary and multilayer systems are given. A highly innovative example is the chip stack or wafer to wafer bonding of unmetallized Si or SiC at 250°C. The proposed bond remains stable above the melting point of Si and enables entirely new semiconductor manufacturing steps. An improved die bonding process was proposed and verified experimentally.1. IntroductionIsothermal solidification can be applied to form strong bonds at relatively low temperature which remain solid at higher temperatures. The general principle of this type of joining processes is illustrated in Fig. 1. An interlayer of a low melting component, Lo, is provided as a foil or a thin film coating between the high melting joint components, Hi. The assembly is heated under moderate pressure to the bonding temperature, T 8 , and a liquid filler forms, either because the melting point of Lo is exceeded or due to a eutectic reaction between Lo and Hi. This molten filler initiates a rapid interdiffusion or reaction diffusion between Lo and Hi and the subsequent approach to an equilibrium state results in isothermal solidification. The solid phases formed at T 8 in the joint region exhibit a remelt temperature above T8 •"

Jan 1, 1996

By J. M. Boxall

The electrolytic zinc plant at the Bartlesville division of Z.C.A. originally used lead anodes containing only 0.25% silver because only H.G. zinc and alloy was to be produced. In 1984, a small addition of strontium carbonate was made to control the surf ace morphology of the cathodes which reduced short circuits and increased current efficiency. Later a drastic reduction in colloid addition further reduced short circuits. Increased strontium additions allowed the production of some S.H.G. zinc. Increasing the silver content of the anodes reduced the lead in cathodes only slightly. More important, the anode scale that was not removed during anode cleaning, entered the electrolyte and contaminated the cathodes with lead. A piping system has been installed to purge the contaminated electrolyte directly back to the leaching section. This has allowed the plant to produce S.H.G. zinc consistently.

Jan 1, 1990

By Ahmad-Bitar¸ Riyad N., Shadia J. Ikhmayies

"CdSi-xTex thin films with O<x<0.3 were prepared on glass substrates by the annealing of CdS:In thin films produced by the spray pyrolysis technique. The annealing was performed in nitrogen atmosphere at 400 --,C in the presence of Te vapor. The compositions of the films were determined by energy dispersive X-ray detection (EDAX) measurements. Scanning electron microscopy (SEM) was used to investigate the morphology of the films. The transmittance of the films was measured at room temperature in the wavelength range 400-1100 nm and used to produce the absorbance of the films. The first derivative of the absorbance was used to estimate the optical bandgap energy Eg by using the minima in the first derivative. The relation between the bandgap energy and the fraction x was found to fit with a parabola and bandgaps in the range 2.196: =Eg: =2.480 e V were obtained. Urbach tailing in the bandgap was also investigated.IntroductionPolycrystalline thin film CdS/CdTe solar cells are promising candidates for low cost and high efficiency photovoltaic applications. The fabrication process of these cells involves the deposition of a p-type CdTe absorber layer on top of an n-type CdS one which acts as a window. The efficiency of the solar cell is affected by the method of preparation of both layers [1, 2].Interdiffusion processes taking place at the CdS/CdTe interface have largely been realized to significantly affect the device performance [3] by changing the bandgap of both CdTe and CdS which modifies the spectral response of the solar cell [ 4]. The formation of a mixed crystal or a graded layer causes a reduction in the lattice mismatch at the CdS/CdTe junction [5] which is about 9% [ 6] and then a reduction in the number of interfacial states and recombination centers, thus enhancing the solar cell performance [7, 8]. A complete understanding of the properties of the intermixed layers CdSxTe1-x that usually constitutes the interfacial region in the CdS/CdTe solar cell is essential. According to our knowledge, a lot of research was devoted to the investigation of the diffusion of S into CdTe [3-5, 9]; but little on the direct investigation of the diffusion of Te into CdS [6]."

Jan 1, 2011

By Chen Song

In the experiments of purifying the solution of chlorine leaching from nickel concentrate with N235, the effects of organic phase composition on purifying efficiency have been studied. From the results obtained, the optimal organic phase composition is found to be 25%N235+12%isomerous alcohol +63%sulfonic kerosene (VIV) and the saturated content of cobalt in organic phase is7.95 g*dm3. And then the serial experiment is carried out. The results show that at the given organic phase composition, the purified solution contains p(Ni) >200 gm dm3, p(Ni)l p(Co) >50000 and the contents of Cu, Fe, Mn, Zn meet the technical criterion of standard nickel electrolyte. The cobalt chloride solution contains p(Co) >I10 g L-1, p(Co) lp(Ni)>50000 and the enrichment of cobalt has been achieved.

Jan 1, 2006

By William Petruk

Mineralogical and image analysis studies have been performed on four volcanogenic base metal ores that contain 0.01 to 4.5 wt% Pb to determine the behaviour of galena during mineral processing. The galena in these ores is fine grained and is poorly liberated in both the primacy and regrind mill discharges. Consequently, low grade Pb concentrates are produced to obtain relatively high Pb recoveries. The Pb concentrates contain many impurities including high amounts of pyrite and sphalerite, and small amount of CU-, As-, Ag-, Bi-, and Se-sulfides. These impurities need to be rejected from the Pb bullion during smelting. The galena commonly contains up to 1 wt% Ag in solid solution with an average of 600 to 1460 ppu for the deposits studied to date. The Ag in galena accounts for up to 65% of the Ag in some ores.

Jan 1, 1990

By Y. Ikeda

Typical electric appliances were dismantled into component pieces to study the recyclability of these discarded goods. Types and weight ratios of these component materials were investigated and characterized. The results showed that if they are dismantled properly, these goods could be classified into several groups of similar materials and/or structures, namely those consisting of single materials, metal-plastic combinations, metal-metal combinations and complex combinations of many different materials. By separating each combination into recyclable materials and isolating hazardous materials, it was found that the final waste for disposal could be reduced and the recycling efficiency could be improved markedly as compared to the conventional shredding method. The metal-metal combinations account for 60% by weight of the total metal contents in electric appliances, and therefore, it becomes important to segregate these metals. For the complex combinations, a process consisting of pyrolytic decomposition of plastic contaminants followed by smelting of the residue is proposed. It is anticipated that nearly zero-emission recycling of electric appliances will be achieved by applying this treatment process.

Jan 1, 1995

By Huimin Lu, Shi Zhou, Lisha Yang

"The Zeolitic imidazolate frameworks (ZIFs) were successfully synthesized by applying a combination of ionothermal synthesis and microwave energies for rapid synthesis. The synthesis was proceeded under various conditions including different raw materials, reaction temperature as well as microwave irradiation time. Zeolitic imidazolate frameworks (ZIFs), also known as coordination polymers, are new type of porous materials formed by inerratic polyhedral in three-dimensional. They are the ideal crystalline substances for gas separation and storage. The assynthesized samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), thermal gravimetric analysis (TGA) and C02 adsorption test. Results illustrated that the synthesized samples had stable structure, high thermal stability (up to 530 °C) and C02 adsorption capacity (10.2 cm3/g at 0°C under ambient pressure). This novel method also showed great advantage with high energy efficiency, safe synthesis conditions, and rapid crystallization time (60 minutes).IntroductionNowadays, carbon dioxide capture has become imperative due to the global warming caused by the increase of C02 in the atmosphere, especially produced by the concentrated sources such as power plants [1]. Zeolitic imidazolate frameworks (ZIFs), also known as coordination polymers, are ideal crystalline substances for gas separation and storage due to their structure diversity, high thermal and chemical stability [2-5]. They are formed by inerratic polyhedra in threedimensional with large cages and small apertures. Traditionally, ZIFs are synthesized by solvothermal method in a sealed autoclave under autogenous pressure [6-9]. However, in order to generate the products, the solvothermal temperature should not be lower than 100°C according to the sovlothermal mechanism. Moreover, at such a temperature, molecules with a low boiling point (such as water) may generate high pressure in reactor which might cause danger [9]. Thus the synthesis requires the equipment to possess resistance to autogenous pressure and corrosion. Further, conventional solvothermal methods need a long time to prepare products, usually a few days, which is a large energy consumption and inefficiency. So it is interesting to synthesis ZIFs through other ways under mild reaction condition with high energy efficiency."

Jan 1, 2012

By QIE Jun-mao, DONG Fang, DENG Hao-hua

The DIL402C thermal dilatometer and STA449C thermal analyzer were employed to test the linear expansion and contraction coefficient，CP and DSC curve of 304 stainless steel. The result showed that the linear expansion coefficient range was 20.9700×10-6～21.5712×10-6 and the linear contraction coefficient range was 21.2528×10-6～21.9471×10-6.The linear expansion and contraction coefficient were higher than other steel grade，so the 304 stainless steel belonged to the crack sensitive steel. Because of the crystal phase transformation occurred during the 1000~1400 ℃,the curve of CP fluctuated obviously and the defects of casting blank occurred easily. Chosen 1414℃ as the liquidus temperature of 304 stainless steel based on the analysis results of DSC. The curve of DSC was unsmooth during 1450～1100℃，the crystal phase transformation occurs and thermal stability of slab was inferior.When the initial solidified shell formed in this temperature range,the thickness of the shell would be nonuniform and the surface defects occurred more easily.

Jan 1, 2015

By G. Van Weert

The pellet reactor was developed approximately 20 years ago in the Netherlands for softening drinking water. Since then, some 35 plants have been built, ranging in capacity up to 8500 m3/h. Applications now also include removal of phosphates and fluorides and the production of metal carbonates and sulphides from waste streams. The pellet reactor consists of a fluidized bed, wherein the process solution is thoroughly mixed with the precipitation reagent at special inlet nozzles to give over-saturation of the compound to be precipitated. In water softening applications, the compound is CaCO,. In the case of nickel or other metal waste streams, Na2CO3 solution is added in sufficient amounts to precipitate metal (hydroxy) carbonate on the fluid bed particles. These grow typically to dense spheroids, which are removed when they reach 0.8 to 1.0 mm diameter. These spheroids are easily dewatered, free flowing and low dusting. The latter property is becoming an attractive advantage in connection with new plant hygiene regulations. The operation of a 60 cm diameter pellet reactor on nickel containing plating waste is described and the properties of the produced nickel carbonate spheroids are discussed.

Jan 1, 1993

By Ramana. G. Reddy, Haoxing Yang

The electrodeposition of zinc from zinc oxide using urea and choline chloride mixture in a molar ratio 2:1 is investigated in different experimental variables, namely, the concentration of added [BMIM]HSO4, temperature, and applied cell voltage. The additive, [BMIM]HSO4, was determined to have beneficial effect on the current efficiency, energy consumed in the process and surface morphology of the deposits. The highest current efficiency (92.6%) and lowest energy consumption (2.92kWh/kg) was obtained for solution with 20mg/mL [BMIM]HSO4. The morphology showed the formation of absorbed additive layer on the cathode at higher concentration of additives. Experiments were conducted at different temperatures between 343K and 388K and at various applied cell voltages between 2.7V to 3.6V to determine the best experimental conditions. By varying temperature, highest current efficiency (91.3%) and lowest energy consumption (2.69 kWh/kg) was obtained at 373K. The electrodeposition process is enhanced between the applied voltage 3.0-3.3V by achieving lower energy consumption (2.75~3.06kWh/kg) and higher current efficiency (88.4~89.7%). SEM images showed grain size is significantly increased in higher applied voltages. While at higher temperatures, it seemed to generate particle growth as clusters at the outer deposit layer.

Jan 1, 2014

By R. G. Reddy

Nickel solubilities in spent pickling solutions (i.e. HF-HNO3-H2O solutions ) were measured as a function of HF and HNO3 acid concentrations. The chemical analysis of the industrial pickling solutions and sludges were made. The stable phases observed in the sludges are FeF3?3H2O, and ( FeCr ) F3?3H2O. Pure Ni, and stainless steel type 316 were used in this study. The results showed that the solubility of Ni increased with increase in concentrations of HF in pickling solution at a fixed concentration of HNO3: An excellent agreement between the experimental solubility data and the theoretical data was obtained. X-ray diffraction analysis showed that the solid solubility product formed is mainly NiF2?4H2O compound.

Jan 1, 1992

By Fumitaka Tsukihashi

Increasing amounts of steel scrap are being used as resources for steelmaking. Therefore, there has been a growing interest in the removal of harmful tramp elements such as antimony, zinc, tin, arsenic, bismuth, lead and copper from the molten steel. The problem that should be solved is the economic removal treatment of residual tramp elements in the steelmaking processes and the production of high quality steel by reducing the effect of the contaminated tramp elements and satisfying the environmental regulations. In this paper, the available thermodynamic data of the residual tramp elements in the molten steel arc summarized and the possibility of the removal of residual tramp elements from the molten steel is thermodynamically estimated.

Jan 1, 2003

By Robert E. Moore

Synthetic spinel is proving to be a highly effective refractory for specific applications, but its cost limits applications. Formation of spinel from a raw material such as diaspore or bauxite could provide a simple and less costly starting material. In the study reported here, finely ground (-325 mesh) diaspore from Missouri and bauxite from Guyana and China are combined with hard burned MgO (-325 mesh) in appropriate proportions to yield spinel and spinel with secondary phases. A classical sintering and dilatometer study was completed, followed by a microstructure study to determine completeness of the reactions and morphologies of the reaction products.

Jan 1, 1993

By Adolfo Pillihuaman Zambrano

Fe-Cr-C production is a very high electrical energy consuming process. Decrease up to 10% of this electrical energy is expected when self-reducing agglomerates are used. This research aims to understand how the synergetic effects are when stronger reductant, like Fe-Si, is substituted for coke in self reducing pellets. Brazilian chromites containing 41.2%Cr2O3 were mixed with petroleum coke and agglomerated with cement as the binder. Small amounts of 1%, 2% and 4% of Fe-75%Si were substituted for the equivalent petroleum coke, and pure silica plus hydrated lime were added for adjusting the slag composition. The mixture was pelletized, dried and submitted at 1773K up to complete the reactions. The results showed that the reduction reactions were 1.4 and 2 times faster with 1% and 2%Fe-Si addition, respectively, than with no addition. The microscopic analysis showed that it was formed a liquid phase, but the pellet did not collapse what indicates that the coalescence of the metallic phase depends on the dissolution of the pre-reduced particles of the chromites into slag.

Jan 1, 2008