By E. Oshima

In May 1991, a New Mitsubishi Continuous Copper Smelter Line started operation at Naoshima. Recently, it has been continuing steady operation and one and a half year campaign life has been achieved. In 1996, new records of on line time, the amount of copper concentrate treated and copper anode production were achieved. 1t proves the superiority of the process with respect to pollution control, energy efficiency, flexibility and easiness of the operation and over all economy including off gas handling cost. Furthermore, .plans are underway to prolong the campaign life for two years and to improve the process efficiency. This paper describes recent operation, improvements, and a future capability study.

Jan 1, 1998

By Riyad N. Ahmad-Bitar, Shadia J. Ikhmayies

"CdS/CdTe solar cells were built by depositing a 200 nm layer of Sn02:F on glass substrates by the spray pyrolysis (SP) technique, a 500 nm CdS:In layer by the same technique and a 1-1.5 µm CdTe layer by vacuum evaporation. The cells were CdCh heat-treated in nitrogen atmosphere for 30 minutes at 350 -.C. The photoluminescence (PL) spectra were measured at the CdS/CdTe interface for two cells with different values of the CdTe layer's thickness at temperature T = 60 K. A deconvolution peak fit was performed from which it is found that the peaks are characteristic of the solid solution CdSxTei-x· The parabolic relation that relates the bandgap energy with the composition was used to estimate x, where xis [S]/([Te]+[S]) and [Te], [S] are the concentrations of Te and S atoms respectively. The results show that the interface is smooth and the change of the bandgap occurs gradually.IntroductionCdS/CdTe heterojunctions represent a combination of materials promising various applications, and for solar energy conversion in the first place [1]. In photovoltaic cells the CdS material acts as a wide bandgap window. Direct bandgap CdTe with high optical absorption coefficient is used as an absorber [1]. Solar cells with efficiencies of 10 to 16% have been obtained with CdTe grown by close space sublimation, electrodeposition, vacuum evaporation and rf sputtering methods [2]. In this work the CdTe layer was prepared by vacuum evaporation because it results with films of minimum impurities, while the Sn02:F and CdS:In layers were deposited by the spray pyrolysis technique because it is a low cost method which enables intentional doping and large area thin films."

Jan 1, 2011

By P. N. Anyalebechi

The effects of application of steady and pulsed electric current on the cast microstructures of ingots of a 7050 type aluminum alloy have been experimentally investigated over a solidification rate range of 0.1-10 K/s. This involved the application of an electric current of 465-930 mA/cm2 of melt surface area to laboratory-size ingots solidified in a unidirectional manner. Within the ranges of electric current density and solidification rate investigated, the applied electric current reduced the average dendrite, grain, and second-phase particle size. It also made the size distribution of the second-phase particles more uniform. The mechanism for the observed refinement of the cast microstructure by the applied electric current is not well understood. The potential effects of heat-induced local convections, shear stress-induced fragmentation of dendrites, increased temperature gradient due to Joule heating and the thermal and constitutional supercooling engendered by Peltier, Thompson, and Joule heating are discussed.

Jan 1, 2009

By Juan Patricio Ibáñez

Separation of arsenic and copper from Cu-As-H2S04 electrolytes by electrodialysis has been investigated at room temperature. The effects of current density and pH were studied. An arsenic-free copper solution was obtained for all the tested conditions. The transport efficiency for copper ions was found to be higher than 98% after 3 hours' test. Transport of arsenic and copper through the ion exchange membranes was increased by increasing pH and current density. Solution pH was found to be a key parameter for the separation process, since it controls the speciation of the ions to be transported and the formation of unwanted precipitates which reduce the global efficiency of the electrodialysis process. The main conclusion is that electrodialysis is a promising technique to be used in separating and/or concentrating ions of interest in copper electrometallurgy.

Jan 1, 2003

By Ikuhiro Sumi

A new steelmaking process, in which manganese ore was intentionally reduced, was developed to achieve a higher manganese Yield using a combined blowing converter. In this study, manganese behavior was discussed through the introduction of a model. Apparent reduction rates of manganese were calculated by the two terms that were determined experimentally, with SOkg and 2S0ton combined blowing converters. The model calculated manganese changes during the operation. We applied the model to the actual operation and found that manganese behavior was predicted fairly well by this model.

Jan 1, 1996

"Mixing phenomena in a bottom blown air-stirred one-seventh water model of CLU (Creusot-Loire Uddeholm) reactor was studie9-using three different configurations of straight circular nozzles fitted axially at the bottom of the vessel. The mixing time has been determined by pH measurements at various gas flow rates, bath heights and nozzle orientations in the presence and in the absence of a second phase.Experimental results reveal that the mixing time decreases with increasing gas flow rate. For a given gas flow rate the mixing time increases non-linearly with increasing bath height. Off-center configuration gives slightly lower mixing times as compared to center configuration. It is found that the contribution of buoyancy to the total stirring energy density is very small, but its contribution increases with increasing bath height. In the presence of an upper oil layer, the mixing time increases significantly for all configurations.IntroductionIn high temperature metallurgical melts mixing is carried out by injection of a gas either from top or bottom of the vessel in order to accelerate the rates of chemical reactions and to promote bath homogenization. When a gas is injected into a liquid through a submerged lance, porous plug or nozzle, the gas, rising as a two phase plume to the surface, imparts momentum to the surrounding liquid and causes gross circulation in the bath which promotes mixing."

Jan 1, 1997

By B. Nowak

For sources with an iron-to-vanadium ratio of far above 1, it is proposed to leach in acid and to oxidize under autoclave conditions. During this oxidation process, it is experimentally shown that divalent iron contained in this solution will be oxidized to trivalent iron, whereas free acid contained will be consumed by this reaction. In case no acid is present or already fully consumed, a solid consisting of ferric compounds and an iron-vanadium-co-precipitate will form that can be filtered from the solution. If choosing the right reaction conditions, this filter cake has an iron-to-vanadium ratio of close to 1, whereas the liquid remainder is almost vanadium free. This precipitate, identified as FeVO4, 1.1 H2O, can be processed by conventional technologies such as caustic leaching, or probably salt roasting or reduction with aluminum, yielding common marketable products.

By M. L. Apel

A conceptual approach to the bioremediation of uranium mill tailings (UMT) is presented., This approach focuses on, biosorption to remediate the. effluent solution and bioleaching remediate the. solid fraction. Comparative biosorption studies were performed with synthetic single metal solutions using a commercially available biopolymer. The maximum rate of metal sorption by calcium alginate was found to be 5.43, 6,39, 6.48, and 9.74 mg dm-3 min-1 for U022*, Ba2+, Cd2+ and Zn2+, respectively. Activation energy (AEa) for barium uptake by calcium alginate beads was determined to be 11.5 kJ, indicating a diffusion controlled reaction mechanism. Thermodynamic values (AG+ AH+ and ASt) of the metal-alginate activated complex, as reported in the literature, were found to be in agreement with those calculated from this research. Results show that this biopolymer can be effectively applied in the removal of select metals prevalent in uranium mill tailing effluents and associated waste streams.

Jan 1, 1991

By A. Christlo

Short circuit detection in 1984 involved nine inspectors for production rates of 43,000 tpa. Trials indicated the feasibility of applying cell voltage monitoring to short circuit detection and improving operational efficiency. A computerised cell voltage monitoring system was commissioned in February 1986, to read voltages from 648 cells. The system incorporates 16 evenly distributed work face units which communicate with a central computer system. Provision has been made in the computer program for the automatic adjustment of cell reference voltages. This allows for the effect of polarization and other process variables which might other wise interfere with short circuit detection. The work face units can continue to work independently for several days should this become necssary. Current efficiencies have been maintained and the number of inspectors reduced from nine to five.

Jan 1, 1987

By P. Lussiez

Precipitates consisting of amorphous ferrihydrite and crystalline goethite have been prepared by aging hydrolyzed Fe (III) solutions at room temperature. The precipitates have been characterized by x-ray diffraction and differential thermal analysis. The amorphous ferrihydrite transforms to goethite with time. The ferrihydrite to goethite transformation is affected by the presence of small amounts of copper or nickel coprecipitated with the iron. .The addition of copper decreases the amount of goethite at a given aging time and increases the amount of coprecipitate which is initially dissolved in sulfuric acid, but it does not seem to affect the dissolution of the crystalline part'. It is proposed that adsorption of copper hydroxo species on goethite nuclei delays the ferrihydrite to goethite transformation. The effect of nickel is less dramatic than that of copper. Apparently a portion of the added nickel is adsorbed on the goethite crystallite surface rather than incorporated into the goethite lattice.

Jan 1, 1981

By A. Perillo

The process, realized in. the Kivcet furnace, can convert continuously lead concentrates, residues and secondary lead bearing materials into a lead bullion free of sulphur and a discardable slag. The lead recovery can be up to 99%. The long experience of about three years at Portovesme demonstrates the capability of the furnace to smelt a very. high range of lead raws without interruption of the operation. The operating costs are very competitive in comparison to the traditional technology. The work place and environment are clean and new tight regulations for the? hygiene control are met. The Kivcet furnace can be considered as consisting of three parts (reaction shaft, waste gas shaft and electro-furnace) connected with a common hearth. The technical basis of the furnace construction is the application of a number of design elements .which have mostly been used before in designs of industrial furnaces, such as open hearth furnace, refining furnace and other furnaces dealing with liquid meta1s. Refractory wear in the reaction shaft with typical pattern from watercooling soon has been stabilized and since maintained. No deformation of the furnace shell and no leakage of metal or s:l:ag through the bottom is? appeared after three years' operations.

Jan 1, 1990

By E. G. Noble

The potential for using heterotrophic microorganisms to solubilize manganese from low-grade domestic ores is being assessed at the Reno Research. center, U.S. Bureau of Mines. More than 90 pct of the manganese has been extracted from a variety of oxide ores in shake-flask tests using molasses as a source of .. nutrients for the microorganisms. It has also been demonstrated that high recoveries of manganese can be obtained from a domestic wad ore using column bioleaching. 'l'he isolation and identification of organisms responsible for manganese extraction is discussed, as are the mechanisms responsible for manganese solubilization.

Jan 1, 1991

By K. C. Liddell

"Cu/Ni multilayers exhibiting giant magnetoresistance were deposited from a single electrolyte under stepped potentiostatic control. To enable transport measurements to be made without remounting the multilayer film, we developed a novel method that involved plating on a thin metallic basal layer atop a rigid non-conducting Si substrate. Rotating ring-disk electrode techniques were used to monitor the composition and thickness of individual plated layers. Transmission electron microscopy confirmed that the interfaces between adjacent layers were sharp and that the structure of the layers was uniform throughout the film. Atomic force microscopy images indicated that the film's surface was smooth and free of defects.ELECTRODEPOSITION OF THIN MULTILAYER MAGNETIC MATERIALSI. IntroductionElectrodeposition of compositionally modulated films will in all likelihood continue to be used to produce the read heads for stored magnetic data. However, the next generation of head materials will require both improved sensitivity and reduced film thickness. Certain multi layers consisting of thin alternating ferromagnetic and nonmagnetic layers exhibit giant magneto resistance and consequently are promising candidates for read head applications. We have successfully made multilayer films with giant magnetoresistance that have total thicknesses as low as 25 nm, approximately 120 times thinner than the thinnest similar films reported in the literature. This paper describes early results from our work on electrodeposition and characterization of Cu/Ni multilayers, a model system with enhanced magnetic and mechanical properties, including the GMR effect. The structure and composition of the multilayers were determined using TEM, AFM, and electrochemical methods, and their magnetoresistance was measured by the standard four-probe technique. A novel method developed in this work enabled the transport properties of the ultrathin films to be measured reliably without the need to dissolve the cathode or handle the films. To provide a context for these results, short accounts of other work on giant magnetoresistance and multilayer electrodeposition are also included."

Jan 1, 1997

By K. Osseo-Asare

"The molecular structural and solution chemical characteristics that underlie the surface activity of solvent extraction reagents are highlighted, with particular emphasis on the tendency towards reverse micelle and microemulsion formation. The physicochemical factors that lead to microemulsion-enhanced solvent extraction with chelating extractants are elucidated. Membrane-based contactor systems are described which are uniquely suited for enhanced solvent extraction with microemulsions. The possibility of combining solvent extraction with microemulsion-mediated materials synthesis is discussed. IntroductionThe discovery of new selective extractants has resulted in major breakthroughs which have helped to establish solvent extraction as a versatile separation technology (1-3). A complementary strategy towards new process development is to seek new ways of using the available reagents. This paper explores this second approach. From a molecular structural standpoint, an extractant may be viewed in terms of two components: a polar functional group and a hydrocarbon radical. In the conventional view of solvent extraction, this molecular structure serves two main purposes: The polar functional group provides the binding sites for complexation of metal ions, while the organic group is needed to render the resulting metal-extractant complex organic-soluble. But are these the only properties of the organic and the polar groups that are relevant to the solvent extraction process?In this paper, attention is directed to the fact that solvent extraction reagents possess the molecular structures of amphiphiIes; that is, they are characterized by the presence of spatially separated hydrophilic and hydrophobic groups on the same molecule. A case is made for the view that this amphiphilicity offers interesting opportunities to develop new separation processes which collectively may be described as enhanced solvent extraction (4-6)."

Jan 1, 1996

By K. Osseo-Asare

The molecular structural and solution chemical characteristics that underlie the surface activity of solvent extraction reagents are highlighted, with particular emphasis on the tendency towards reverse micelle and microemulsion formation. The physicochemical factors that lead to microemulsion-enhanced solvent extraction with chelating extractants are elucidated Membrane-based contactor systems are described which are uniquely suited for enhanced solvent extraction with microemulsions. The possibility of combining solvent extraction with microemulsion-mediated materials synthesis is discussed.

Jan 1, 1996

By Jingbo Liu, Zhimin Wang, Wenchao Li

"IntroductionThe advantages of non-stoichiometric perovskite material are highlighted in many papers[l]and many of this family of materials are well-suited to integration into microsensor devices. Among them, barium titanate is the most promising due to it's piezoelectric, pyroelectric, dielectric properties. Through modification, BaTiO3-based materials can be utilized in many kinds fields, such as surface wave probe; pholoconducting devices, field-effect transistor, permanent memory permanent storage, and ultrasonic transducerl2-3l. In this Paper, a series of BaTiO3-based polycrystals were synthesized by sol-gel processing which appears to be a very promising method for the manufacture of ceramic, because it offers significant advantages such as high purity, chemical homogeneity, controlled particle sizes of ceramics, and lower processing temperatures [4]. In a sol-gel process, alkoxides of the constituent elements show different reactivity toward water so that the preparation of multi-component homogenous system is difficult. In the experiment, inorganic salt was substituted for some of the alkoxides. Acetic acid which is employed for the solvent and catalyst, acts as donor ligand to titanium alkoxide and controls, the hydrolysis polycondensation reaction. Taking these aspects into consideration, we select the system Ba(OAc)2, , La(OAc)3, Ti(O11Bu)4 and acetic acid which is used as both solvent and homogeneous catalyst for the first time.ExperimentalA series of La3+-doped BaTiO3-based nano-crystals were prepared with sol-gel technology using various parameters. The precursor solution was prepared in the presence of barium acetate, lathanium acetate, and titanium tetrabutoxide monomer in butyl alcohol. According to the flow chart (fig. I.), Ba(OAc)2, La(OAch dissolved in the glacial acetic acid (0. lmol/40ml) in a three-neck flask were mixed with a solution of titanium tetrabutoxide monomer in butyl-alcohol(l 7ml/20ml) at room temperature and under constantly, vigorous stirring conditions. In most cases, the resultant solution was golden yellow and stable in the air. To this precursor solution, containing Ba, La, Ti in the desired ratio, water was added incrementally for hydrolysis under continuous stirring until sol was formed. After aging for more than 2 hours, sol was transformed to gel at room temperature. If heated during aging, the gel was formed in a shorter time. The wet gel was allowed to dry at 50°C for more than 10 hours. The dried gel was transparent or light yellow. In order to obtain BaTiO3-based nano-crystals, the amorphous dry gel was calcined at 600°C, 700°C, 800°C, 900°C, 1000°C respectively[5]. The ceramic humidity sensor was formed through the cold-pressed, aged, capsulated routes. The dried gels were crushed in an agate mortar and then pressed into discs of ? 1.5 X l.5mm (l.5mm diameter and l.5mm thickness), then held at about 16.5 MPa pressure for 3 min [6]. The disc was sintered at 1350°C and 1400°C for I hour respectively. During the processing, an Ag-Pt electrode was inserted in the sensor [7]. (See the flow chart.)"

Jan 1, 2000

By P. N. Anyalebechi

"The effects of solidification rate, initial melt hydrogen concentration, and grain refining on porosity formation in aluminum alloy 2024 have been investigated with unidirectionally cooled laboratory-size ingots. The ingots were prepared from melts containing hydrogen concentration of 0.059-0.27 cm3/100 g and solidified at 0.2-37 °C/s. As expected, the amount of porosity, average pore size, and pore number density increased with increase in melt hydrogen concentration and decrease in solidification rate. However, the effect of solidification rate was greater at the very low melt hydrogen concentration (0.059 cm3/100 g). These results are consistent with reported effects of solidification rate and melt hydrogen content on porosity formation in other aluminum alloys. Interestingly, addition of grain refiner slightly increased the amount of porosity and the average pore size, especially at solidification rates above 1°C/s. IntroductionIn shaped castings and wrought products fabricated from ingots, billets, bars, or slabs of aluminum and its alloys porosity formation is a problem. This is because it compromises their tensile strength, fracture toughness, and fatigue properties [ 1-18]. The pores are usually the crack initiation and propagation sites [6,8,9] and the largest pores tend to dictate the fatigue life of the aluminum products [9,10,14]. Porous regions within an aluminum product probably yield first due to the reduced tensile load bearing capacity, causing the concentration of the strain near the voids which subsequently results in premature fracture. In aluminum alloy ingots, billets, bars and slabs porosity formation is particularly problematic because of its persistence through fabrication and potential for reappearance or exacerbation during subsequent thermal treatment processes before and/or after fabrication [19]. In fact, persistence of microporosity is a serious problem in large thick plates of wrought aluminum alloy products that must be rolled from correspondingly large direct-chill or electromagnetic cast ingots. Some of these thick plate products are machined into large aircraft components that are required in service to withstand multi-directional stresses and to possess high fatigue strength, fracture toughness, resistance to stress corrosion cracking, and strength in the short-transverse direction [1,20]."

Jan 1, 2011

By F. -Z. Ji

Carbon injection into metallurgical slag is important in electric arc furnace (EAF) steelmaking for foamy slag practices and in nonferrous slag cleaning operations. The current publication presents kinetic data for coal injection into EAF slag to understand the interaction between injected carbon and metallurgical slag. Coal particles were injected into EAF slag and the kinetics were followed by gas and slag analysis. The results were analyzed, in terms of fundamental rate equations for each possible reaction step, as a function of temperature and slag composition.

Jan 1, 2003

By E. Fregeau-Wu

The major obstacle in recycling steelmaking slags to the blast furnace is their phosphorus content. Removal of the phosphorus, which is primarily associated with the silicate and phosphate phases, would allow for greater recycle of these slags for their iron, manganese, and lime contents. Calculations show that separation of the silicates from the oxide phases would remove nearly 90% of the phosphorus from the slag. The variable grain size of the as-received slag made liberation by fine grinding difficult. Therefore, slow-cooling experiments were undertaken to improve the grain size distribution. The grain size distributions were determined using in-situ image analysis. The samples were ground to their apparent liberation size and high gradient magnetic separation was used to separate the magnetic oxides from the nonmagnetic silicates and phosphates. Liberation analysis and modeling was performed on selected separation products for discussion of benefication characteristics.

Jan 1, 1995

By Shengqi Chen

The reduction smelting of nickel laterites produces slag, consisting principally of the chemical components MgO, "FeO", SiO2, and A12O3, and ferro-nickel alloy. Despite the fact that the phase equilibria for the ternary MgO-"FeO"-SiO2 up to 1500°C is well established limited experimental data are available in the MgO-"FeO"-SiO2-Al2O3 system, which is relevant to commercial operation of the process. A methodology has been developed for the experimental investigation of the liquidus temperatures for the multi-component system MgO-"FeO"-SiO2-Al2O3-Cr2O3 in equilibrium with metallic iron. Experiments have been carried out using high temperature equilibration, quenching, followed by electron probe X-ray microanalysis (EPMA). Liquidus temperatures have been determined in the silica primary phase field in the composition ranges directly relevant to the Cerro Matoso S.A. ferro-nickel smelting slag. Liquidus isotherms have been determined for temperatures between 1450 to 1600°C. The study enables the liquidus to be described for a range of MgO/FeO ratios. It was found that liquidus temperatures in the silica primary phase field decrease significantly with the addition of AI2O3. Keywords: Liquidus temperature, ferro-nickel, pyrometallurgy, smelting

Jan 1, 2004