By Lijuan Li, Zheng Lu, Xin Xia, Qijie Zhai, Qingchun Li

"Pulsed current and pulsed magnetic field have been applied to the bainite transformation of Cr5 steel. Three groups of experiments were conducted. In the first group, ordinary resistance furnace was used for heat treatment. The Cr5 specimens were rapidly heated up to austenitization temperature 940 °C, held for 20 min, air cooled to bainite transformation temperature 350 °C, held for 10, 20, or 40 min and then air cooled to room temperature. The second and the third group shared the same temperature-time curve with that of the first group, but their heat resources came from the Joule heat produced by pulsed current. 1.5 T pulsed magnetic field was exerted on the third group specimens when they were held at 350 °C, but the second group specimens did not undergo the treatment of magnetic field. It was found that both pulsed current and pulsed magnetic field obviously retarded the bainite transformation. The phenomena were discussed in terms ofliterature results.IntroductionApplying pulsed current and pulsed magnetic field technology are very pronnsmg ways to change the microstructure of materials by affecting the phase transformation process. People had found that pulsed current dramatically influences the behaviors of materials, for example, electromigration effect [l], the solidification of metals and alloys [2, 3], electroplasticity [4, 5], crystallization of amorphous alloys [6], healing of metal materials [7] and so on. As to pulsed magnetic field technology, a lot of effort had been spent on grain refinement in solidification of metals [8, 9], recrystallization of cold-worked metals and alloys [10] and Fe-based alloys solid-state phase transformation [11, 12]. Though application of pulsed current and pulsed magnetic field technology have proliferated in recent years, investigation on their effects on solid/solid phase transformation, especially bainite transformation, is lacking. The aim of this paper is to show the effects of pulsed current treatment (C-T) and the combined treatment of pulsed current and pulsed magnetic field (CM-T) on bainite transformation of commercial Cr5 steel"

Jan 1, 2014

By J. W. Matousek

In the flash smelting of copper sulfide concentrates, the course of reactions from the burner tip, through flame "burn-out" (the point of oxygen depletion), to settled matte and slag is of particular interest in understanding the mechanisms of the process. Numerous reaction sets can be proposed to describe the chemical changes that might be taking place, but from outside the furnace no one set offers an obvious advantage in explaining the actual processes involved. Only a combination of mathematical modeling and flame and bath sampling can achieve this result. This paper shows that flash smelting, while still reasonably orderly, is a more complex process than suggested by the technical literature.

Jan 1, 1993

By Patrick R. Taylor

This investigation studied the inflight calcination kinetics of nuclear waste simulant using a thermal plasma reactor. A series of experiments were performed to determine the conversion of insoluble aluminum compounds to the soluble compounds and the decomposition of complex organic and nitrite compounds present in the simulant waste. Thermodynamic calculations based on free energy minimization were performed to establish a theoretical basis for this investigation. A kinetic model to describe the conversion of gibsite to sodium aluminate has been proposed. The products of the calcination were characterized using XRD, Gas Chromatography, and chemical analysis by ICP. The results of this investigation indicated 85% gibsite conversion to sodium aluminate, 90% of nitrate decomposition, 52% TOC decomposition and 90% conversion of chromium to soluble compounds. A process is identified for inflight calcination of wastes. Key words: Plasma, waste, simulant, calcination

Jan 1, 1996

By P. Hajiani

Rare earth elements (REEs) are critical materials in many leading-edge technology products. However, REE separation outside China has remained a challenge in addressing environmental concerns of current production. The author has worked on a technique employing the emphasised variability in the electrophoretic mobility (μi) of REE for the purpose of REE separation. In continuation of the results presented in IMPC 2016 [1], this contribution summarizes the progress achieved in 2016 and 2017. The major goal was to increase the REEs concentration by a factor of 1000 and to attenuate the consequent drawbacks, specifically joule heating effect. Amphiprotic hydroxylic solvent was selected to replace water, which has a major impact on the complexation mechanism and buffer requirement. Non-aqueous media result in a significant drop in the specific molar conductivity of the electrolyte, whilst μi reduces several times only. Moreover, a quasi-steady state electrophoretic separation in conjunction with temperature gradient focusing is adapted to improve scalability.

By Tracie Zoeller, G. Paul Neitzel, Jr. Sanders

"As-cast aluminum alloy microstructures are highly segregated. Coring occurs when solute is rejected during solidification resulting in a non-uniform solute distribution across the dendrite arms. Furthermore, coarse constituent phases are formed in the interdendritic channels as a result of coring. These constituents are either soluble or insoluble and can form from the major solute elements, or the impurity elements iron and silicon. The dissolution of these constituents, or precipitates, is an important consideration in determining the microstructural evolution of an alloy. The properties of an alloy are significantly affected by the morphology of the precipitates. Precipitates can be either beneficial or detrimental to the properties of the alloy. Regardless of the nature of the precipitates present, it is useful to understand the dissolution process. A diffusion-limited dissolution model for planar precipitates is presented and compared to an analytical solution and to models in the literature. Experimental data for the dissolution of AhCu precipitates in a dilute alloy are compared to the proposed model, and found to have good agreement.IntroductionDuring the processing of precipitation hardening alloys, beginning with the solidification step and ending with the final solution heat treatment step, there are a variety of particles that form. Some of these particles must be dissolved and solute redistributed and re-precipitated in a more homogeneous distribution than as it first appears in the as-cast microstructure. The particles can be classified by size as microstructure develops during processing. Coarse particles that form during solidification can either be soluble, partially soluble or insoluble. These particles can be the result of coring of the major solute elements as well as the limited solubility of elements such as iron and silicon. Iron and silicon can combine with the major solute elements such as copper in 2xxx alloys forming coarse phases often referred to as constituents. Figure l(a) shows the as cast microstructure with the constituent phases, Al2Cu and the insoluble phases containing Al-Fe-Mn-Cu-Si [7]. During preheating the soluble phases such as AhCu that were formed by eutectic decomposition must be taken back into solution, whereas the insoluble phases remain essentially unchanged by most thermal operations. Figure l(b) and (c) show some of these constituents after subsequent preheating steps. In Figure l(b), AhCu platelets are shown and in Figure l(c) the remnants of the AhCu phase are noticeable, along with Mn-bearing dispersoid phases. Reduction in the volume fraction and size of these phases improves the ductility and fracture toughness as well as reducing the inhomogeneities that occur during coring. Also adjacent to the dendrite arm boundaries are smaller AhCu phases that precipitate by a solid-state transformation on cooling to room temperature."

Jan 1, 2004

By K:-I. Rhee

The recovery of tellurium from Te-cement obtained during the processing of copper anode slimes was carried out by a series of hydrometallurgical processes, i.e. leaching Te-cement in NaOH solution, precipitation of impurites with the addition of Na2S followed by direct electrowinning of tellurium in NaOH solution. The optimum conditions for each process were determined and discussed in terms of various parameters associated with each step to maximize the recovery and purity of tellurium. The final purity of tellurium from electrowinning in alkaline solution was found to be more than 99.9 %.

Jan 1, 1997

By Pierre-François Bareel

EU legislation imposes ambitious recycling targets for various consumer goods. End-of-Life Vehicles (ELVs), scrap iron and various proportions of Waste Electrical and Electronic Equipment (WEEE) are processed by shredding plants which recover most of the metals but produce Shredder Residues (SR) which are landfilled. They represent 20 to 25 wt.% of the shredder input. Energy issues for the coarse fraction of SR are now largely studied. However, below 2 mm, the calorific value falls off drastically. These Fine Shredder Residues (FSR) represent up to 55 wt.% of the total SR. To meet European objectives other alternatives to landfilling must be considered for the FSR. The present paper describes a study carried out to characterise the FSR and investigates ways to process them and produce marketable products. Applying Gy's theory, a sampling procedure was conducted over two years to statistically quantify the variability of the physical and chemical properties of FSR produced by a Belgian post-shredding treatment plant. Macroscopic characterisation has led to the identification of four material categories which could be separated according to their physical properties: ferrous metals (more or less oxidised), non-ferrous metals, an organic fraction (plastics, rubber, textiles, foams, wood) and a minerals fraction (glass, ceramic, concrete). The entrainment of small metallic particles within the pores of organic fragments will affect the quality of the separations.

Jan 1, 2006

By Dominic T. Jordan, Quinn G. Reynolds, Christopher J. Hockaday, Ian J. Barker

A direct-current (DC) plasma arc furnace is a type of electric furnace used for metallurgical operations. The successful operation of DC furnaces depends to a large extent on gaining a fundamental understanding of the arc phenomenon itself, and ensuring its presence in the furnace at all times. A method for detection of the presence of the arc in a DC circuit is presented, along with discussion of why this may be of value for certain modes of furnace operation such as brush-arc. The theoretical development of the method is presented along with supporting experimental work conducted on large-scale pilot-plant facilities.

Jan 1, 2014

By Wenbo Luo, Kang Liu, Fusheng Mao, Jilai Xue, Jun Zhu, Chunlei Yang

Extracting alumina from coal fly ash (CFA) is of great interest for both environmental protection and recycling valuable alumina content. In this study, ultrasonic aided leaching process as an effective method was investigated to enhance extracting Al2O3 from CFA via concentrated sulfuric acid sintering. The influence of ultrasonic power and processing time were tested under the conditions as the same as those without ultrasound. It is found that the alumina extraction rate can reach 90.5 % with ultrasound assistance, while the ultrasonic treatment can reduce almost 15 ~ 30 min in leaching time and 5 ~ 10 oC in leaching temperature than those without ultrasonic operation at the same Al2O3 extraction rate. In addition, the ultrasonic can reduce calcium content by 6 ~ 8 % dissolved into the leaching liquid. SEM analysis also shows that the residue particle size with ultrasound is smaller than that without ultrasonic treatment.

Jan 1, 2015

By K. S. Kumar

FLS miljø, Inc. markets, designs and supplies particulate collection devices for dusts, fumes, and mists; In this paper, the application of both wet and dry electrostatic precipitators (ESPs) in smelting, and roasting plants is discussed.

Jan 1, 1998

By Yoshisada Michiura, Junko Umeda, Katsuyoshi Kondoh

Rice husks or straws, one of the main agricultural wastes in South-east Asia, have a large possibility to be employed as usefully renewable resources to produce energy and high-purity silica (SiO2), because they consist of about 70% organics such as cellulose or hemi-cellulose, and 20% amorphous SiO2. The former is utilized as bio-mass energy; for example, thermal or electric energy, and bio-mass ethanol. High-purity silica can be used as raw materials in the industrial uses. It would be possible to extract silica elements from rice husks and straws by burning them in air because their main contents are organics. In the previous studies, a strong acid leaching treatment on rice husks before burning was carried out by using H2SO4, HCl and HNO3 to prepare high-purity silica materials. This was available to accelerate the hydrolysis of celluloses and hemicelluloses contained in rice husks, and remove the above metallic impurities. A strong acid leaching treatment, however, is significantly hazardous to environment and human life, and causes an increase of the process cost. In this study, the environmentally benign, harmless to human and economically effective process to produce high-purity amorphous SiO2 materials from rice husks has been established without using strong acids. From a viewpoint of the harmless influence on human body, the carboxylic acids were used in the leaching treatment on rice husks. TG-DTA measurement and GCMS analysis indicated that the leaching was effective for the hydrolysis of celluloses and hemicelluloses contained in rice husks at 473K~873K, which produced the same results in using the conventional sulfuric acid. The metallic impurities could be also removed from the husks via a chelate reaction between carboxyl groups (-COOH) and the metal elements. In particular, it was clarified that cadmium (Cd) were completely removed from rice straws by this reaction. Concerning the burning conditions of rice husks after the acid leaching, it was necessary to supply a suitable amount of air to completely combust organics; for example it required air supplement of 50 ml/min. or more. The burning temperature should be less than 1273K to obtain amorphous structured silica. High-purity amorphous silica materials with 99% or more were prepared from rich husks by applying the citric acid leaching treatment and burning process at 1073K in air.

Jan 1, 2008

By Bret Boster

Facilities at Amax Gold's Sleeper Mine process some 330 kt of high grade ore and 4100 kt of low grade ore annually to produce 6.8 t of gold and 7.8 t of silver. High grade ore is processed in a conventional milling facility employing gravity concentration, CIC and CIP unit operations for gold and silver recovery. Low grade ore is processed using heap leaching and carbon adsorption methods.. Presented are the evolution and descriptions of the Sleeper processing facilities and discussions of selected' operating results.

Jan 1, 1989

By A. M. Strachan

The arising and behavioural pattern of polonium-210 in the Capper Pass & Son Limited non-ferrous metal smelting and refining circuit is briefly discussed. The process developed for the removal of polonium from lead, solder and bismuth is discussed in detail, together with the essential personnel safety and environmental protection precautions which must be taken during the refining and subsequent storage of the active dross.

Jan 1, 1992

By Ilie Butnariu

Steel manufacture in VOD procedure needs a very attentive correlation and pursuit of the technological stages ,on the background of keeping the influence factors within best performances zones. For a better co-ordination of the main stages specific to this process ,this work presents a detailed study of the optimization possibilities for each stages ,beginning with the furnace charging ,going on with the pre-aftinage and aftinage stages in the electrical furnace and then with the refinement stages in the VOD installation. One has intended the effective emphasis of the main influence factors with global implications on the process and especially on the purity and quality of the stainless steel ,Among the main novelties proposed by this work , we can emphasize the following: - a computer assisted charging method ,with the possibility of using a large scale of wastage, also respecting the density proportions of the components of the charges; - the advanced recuperation of the elements of the charge by reducing the combustion of the valuable elements ; - the optimization of the oxygen blast conditions and of the aftinage stage ,by establishing some calculations concerning critical carbon content , that requires the oxidation to be continued very carefully; - the simulation of the thermic and chemical parameters by modeling the alloying process of the stainless steel in the case of some large amounts of additions.

Jan 1, 1994

By P. Thapliyal

The petroleum refining industry generates over a million tons of spent catalyst per year, containing valuable metals. Currently, these materials are recycled to smelting furnaces, but the fundamental mechanisms controlling the recovery processes are poorly understood. Furthermore, submerged injection of finely divided materials is potentially a means to obtain high recoveries of pay metals. In this study, a catalyst containing 10% Ni and 1% Co was injected into 45 kg heats of matte. A copper matte was chosen so that the nickel and cobalt recoveries were measurable. It was found that the recovery ranged from 40 to 700Al, increasing with catalyst feed rate, decreasing with catalyst particle size and decreasing with the oxygen content of the carrier gas. A mathematical model was developed to account for the results, and to permit extrapolation to nickel mattes. The industrial implications are discussed.

Jan 1, 1996

By Wei Yin, Bin Xu, Qian Li, Yongbin Yang, Tao Jiang

Copper anode slime is an increasingly significant resource for precious metals such as Au, Ag and Pd. The extraction of Au, Ag and Pd from decopperized anode slime by different pretreatments and different lixiviants including cyanide, chloride, thiourea and thiosulfate have been investigated. When oxidizing roasting pretreatment was carried out under the conditions of roasting time 120min and temperature 625 ℃, the removal ratios of S and Sb could reach 82.18% and 98.52%, respectively. And the following alkaline leaching of calcine could result in the dissolution of 46.40% Cu and 98.48% Pb. The optima leaching ratios of Au, Ag and Pd reached 99.48%, 97.69%, 94.79% by cyanide leaching, and 95.01%, 79.84%, 96.59% by chloride leaching, and about 95.21%, 95.66%, 48.79% by thiourea/thiosulfate leaching.

Jan 1, 2015

By Kongfang Feng, Fei Ruan, Zhiyu Liu, Jieyu Zhang, Xin Hong, Shaobo Zheng, Jixu Wang, Jinyin Xie

"Mixing phenomena in smelting reduction furnaces with asymmetric side blowing were studied in this paper. Mixing phenomena in a smelting reduction furnace was represented as the mixing time by electrical conductivity measurements. Experiments were performed in a water model under various operating conditions to determine the effects of horizontal angle, radial angle, inserting depth, flow rate of the upper and the lower side nozzle, the included angle between the upper side nozzle, and the lower side nozzle on mixing phenomena in smelting reduction furnace. Comparing mixing time and mixing phenomena, the optimal conditions were obtained for an asymmetric side blowing process.IntroductionIn recent years, many countries have put forward development strategies for saving resources and environment-friendly, the development of various industries had to face its influence for resources and the environment .As we all know, the steel industry is a pillar industry of the global economy, in which ironmaking is an important part of it. In the modern ironmaking process, the blast furnace is regarded as the most important equipment and tool. But with the increasing scarcity of metallurgical coke resources and considering the environmental impact of such processes, metallurgists proposed the concept of smelting reduction. Smelting reduction processes to produce hot metal from iron ore and coal were being developed as a possible alternative to the traditional blast furnace. At present, a number of smelting reduction processes had been developed all over the world, they were mainly included COREX, HISMELT, FINEX, DIOS, etc."

Jan 1, 2012

By Yong Xian, Zhaohui Sun, Honggang Zhong, Qijie Zhai, Jie Sun

Vacuum refining is admitted as an effective means to remove impurities in the process of alloy smelting. In this paper, Orthogonal and single factor experiments were carried out to investigate effects of multiple factors, such as superheat degree of the melt, degassing time and vacuum degree, on the vacuum refining process. The results showed that the best removal rate of oxygen and nitrogen is up to 82.71% and 61.3%, respectively, due to high vacuum degassing efficiency. It is found that the superheat degree is minimal impact on the deoxidization rate, in addition, nitrogen removal is controlled by the degassing time. The inclusions exist in the AlV55 alloy are mainly composed of oxides and vanadium-nitrogen compounds.

Jan 1, 2015

By M. Z. Mubarok

Effect of single addition of a lignin-based biopolymer additive, DP 2782, at various dosages as well as in combination with thiourea on cathode polarization during copper deposition was investigated by performing potentiodynamic and galvanostatic measurements using a potentiostat. The result of electrochemical measurements was compared with the behaviour of cathode deposition with glue and thiourea additives. Surface micro-appearance of the copper deposit after 1 h galvanostatic scan under current density of 330 A/m2 and various additive type and dosage was evaluated by scanning electron microscopy (SEM) examination. It was found that the addition of 2.5 mg/l biopolymer gave sufficiently polarizing effect of copper deposition. SEM examination of the cathode surface after galvanostatic scan revealed that the combination of the biopolymer with thiourea (2.5 and 3.5 mg/l) resulted in a compact deposit which is comparable with that resulted from the test with glue and thiourea.

By C. P. Broadbent

Due to growing .public awareness of environmental issues and greater sensitivity towards waste management, many countries around the world are implementing more stringent legislation governing the storage and disposal of hazardous wastes containing heavy metals such as As, Sb, Pb, Cd or Hg. These wastes can no longer be dumped without providing clear guarantees that the material concerned is environmentally safe and will not leach toxic elements to the surroundings. In the Netherlands the current dumping charge for chemical waste (i.e. worst category) is $280/t, and for industrial waste this cost reduces to $75/t. If the material can be reused there may be a small positive credit for selling it, for example discard slag as an aggregate to the construction industry. A number of (pyre)-metallurgical operations, mostly associated with the extraction of metals from sulphidic ores, produce arsenic residues in the form of As2O3 containing flue dusts and speises. If the flue dust is of high purity it can be sold, though many traditional uses are being substituted by other materials. In many cases upgrading the quality of the arsenical dusts is not possible for either technical or economic reasons. Traditional practice is to dissolve these dusts in acid prior to precipitation as ferric arsenate, which is at present classified by many countries as industrial waste and can be dumped. Recent work, however, has cast doubt on the stability of arsenates for disposal and alternative disposal routes have been investigated. Tests have shown that up to 10% (dm) As can be incorporated into "glassy" silicate slags with very low levels of arsenic leaching in the cooled product. Calcium arsenate was added to a range of synthetic and industrial slags from the system SiO2-FexOy-CaO-A12O3-AsmOn, under mildly oxidising conditions and quenched subsequently in water. It would appear that this represents an environmentally acceptable method for the disposal of many arsenical residues and there is some optimism that this method will be equally applicable to the disposal of other toxic metal residues.

Jan 1, 1994