By Kazuyoshi Shimakage, Shinji Hirai, Kenji Wada

"An amorphous zirconium oxide coating was prepared by the sol-gel process using zirconium tetra-n-butoxide on the surface of aluminum to improve the corrosion resistance to salt, acid and alkaline attacks. The coating films formed on the smooth aluminum substrates under UV-irradiation indicated an excellent corrosion resistance for salt, acid and alkaline attack tests. For example, the corroded area of coating film in salt attack test for 3600ks in the order of sol-gel coating· film< chromate film <boehmite film, and the sol-gel coating film had the best corrosion resistance. The coating film prepared on the coarse aluminum substrate by a boiling treatment after heat treatment at 573K also had greater corrosion resistance, and a water-avid surface appeared a contact angle of approximately 3°.IntroductionAs given in a previous paper1; a composite film consisting of a porous layer of anodically grown aluminum oxide filled with amorphous zirconium oxide and an amorphous zirconium oxide coating layer deposited thereon via the sol-gel process utilizing the dip-coating technique, was prepared to improve the alkaline corrosion resistance of aluminum. The alkaline corrosion resistance of these composite films was increased in the range of 24 to 50 times those of conventional anodic oxide films anodized in sulfuric acid. As a result, it was proved that heat treatment at 573K after dip-coating was an important process to .remove organic component from gel film and to accelerate the densification of coating layer. Furthermore, the effect of ultraviolet (UV) irradiation at ambient temperature on the densification of coating layer was also examined to lower the heat-treatment temperature2.Then, a sol-gel film prepared by UV irradiation at ambient temperature indicated that alkaline corrosion resistance of aluminum was superior in the range of 2.4 times to 2. 6 times that of the conventional composite film heated at 573K."

Jan 1, 2000

By F. M. Wang, J. P. Lin, G. Y. Tang, H. C. Zhou, Y. F. Liang, F. Ye

"Fe-6.5%Si alloy is a very excellent soft magnetic material compared with conventional Si steel (Si content ~ 3.5%), especially in high frequencies with reduced iron losses and noises. But it is hard to be fabricated due to its brittleness at room temperature. Dynamic electropulsing is applied to the cold rolled Fe-6.5%Si sheet during tensile deformation. Mechanical and microstructural properties are investigated with different electropulsing and strain rate. It is found that the yield stress decreases and the elongation increases dramatically with the application of dynamic electropulsing. It is indicated that the work hardening could be reduced with the dynamic electropulsing during deformation, which provides a promising way to fabricate this alloy sheet much easier.Introduction Fe-6.5%Si (weight percent, same as below) alloy has more excellent soft magnetic properties compared with conventional silicon steel (Si content ~ 3.5%), such as higher resistivity, higher permeability, near zero magnetostriction, etc. and exhibits much lower core losses and noises [1]. However, Fe-6.5%Si is very brittle at room temperature and hard to be fabricated in strip by conventional hot-cold rolling process [2]. This lack of low-temperature ductility has been generally attributed to structural ordering ofB2 and D03 phases [3]. Several methods have been developed to avoid its brittleness, such as chemical vapor deposition (CVD) [4], rapid quenching [5, 6], dipping and diffusion [7, 8], direct powder rolling (DPR) [9], etc. However, hot-cold rolling method is still of interest for industrial applications. In our previous work, this alloy can be cold rolled after certain thermomechanical process and heat treatment [10-13]. The cold rolled sheet exhibits some extent of ductility [11]. However, side cracks are common for the rolled sheet, it is very necessary to improve the ductility of this alloy by other technical applications."

Jan 1, 2012

By D. P. Cook, Jr. Jones, J. W. Evans

"It is well understood that the flow of liquid metal in the mold region of the caster can have a notable effect on the overall solidification behavior in aluminum casting. Previously our group has characterized the flow in this region in a water model, using particle imaging velocimetry. The flow is significantly effected by the specifics of the metal delivery system, i.e. size, geometry, used during the cast. Recently, a time-averaged 3D numerical model of the nozzle, combo bag and sump region has been developed and its validity has been tested against experimental data. Cases were run for different sized combo bags as well as bags that have been blocked. The results show satisfactory agreement between the physical and mathematical models.IntroductionFluid flow in the head of an electromagnetic (EM) and direct chill (DC) ingots has been shown to effect many important operational parameters in casting such as superheat removal, macrosegregation, and hot cracking. In most cases, the momentum from the nozzle is diverted through a delivery system, termed a bag, before entering the mold region. The specific geometries of the bags vary widely from operator to operator suggesting that there is still some question as to the optimum design. Several studies [1-4] have been carried out to understand the influence of the bag design on the solidification behavior in aluminum casters. However, few studies have included numerical prediction with experimental verification. Unfortunately, many simulations performed today still do not accurately account for flow in such devices.Recently, a significant amount of research into the flow resulting from the metal delivery systems has been performed [5-8]. The thrust of this research has been characterizing the flow patterns by a measurement technique called particle imaging velocimetry. The data suggest that the method of delivering the liquid metal into the mold region has a significant effect on the nature of the flow. With a detailed set of quantitative data from a water model, a numerical model can be built and tested to ensure a proper description of the flow field. The computational model used in these simulations is designed to represent a laboratory scale model of a caster in which ""combo"" bags were simulated. Such bags are mostly of a densely woven glass fiber material with low permeability to aluminum. ""Windows"", of a more open weave, permit aluminum to flow from the bag, see Fig. I. Two different sized combo bags were modeled, each subject to two different outflow window configurations. Furthermore, experimental measurements [9] were used to validate the model results."

Jan 1, 1999

By K. B. Shedd

Questions regarding possible adverse health effects from exposure to zeolites arose when the inhabitants of two villages in Turkey were found to have high incidences of mesothelioma, a disease generally identified with exposure to asbestos. No asbestos deposits are known in the area, but some fibrous zeolites have been found. Further investigations have resulted in conflicting opinions as to whether fibrous zeolites are related to the high incidence of mesothelioma in Turkey. The U.S. Department of the Interior, Bureau of Mines examined the habits of domestic zeolites by scanning and transmission electron microscopy. Only erionite and mordenite particles possessed acicular to fibrous habits. With the exception of a rarely occurring woolly erionite sample, the fibrous zeolites were not dimensionally equivalent to asbestos.

Jan 1, 1982

By J. R. Parga

A shortage of landfill space and growing environmental concerns in Mexico are renewing interest in the recyclability of scrap from automobiles. This work describes a pyroumetallurgical process for the recovery of metallic lead from waste lead paste. Argentopyrite concentrate is commingled with lead paste residue and smelted in a fuming process thereby transferring the precious metals into lead bullion. The process consists of smelting lead paste and argentopyrite, sodium carbonate, and metallic iron at smelting temperatures of about 1100 T. The reaction products are slag and molten lead bullion enriched with precious metals. A major feature of this process is the removal of precious metals from the bullion by means of zinc, whereby a silver-zinc intermetallic compound is formed and floats out of the lead. The recoveries of precious metals are about 98%.

Jan 1, 1996

By Zhihao Yue, Honglie Shen, Yahui Teng, Ye Jiang

"In this paper, manganous nitrate [Mn(NO3)z] was used to assist the etching of silicon wafer in hydrofluoric acid (HF) for the antireflective application, and alumina (Al2O3) layer was deposited on the surface of the etched sample by atomic layer deposition method for further antireflection. The surface morphological and compositional studies of these samples were performed by scanning electron microscopy attached with an energy-dispersive X-ray spectrometer. The surface reflectance measurements were carried out using UV-Vis-NIR spectrophotometer. Binary structures of pyramids and nanopores were obtained by etching the alkaline textured monocrystalline silicon wafer in HF and Mn(NO3)z mixed solution for not more than 15 min. But excessive increase of etching time of up to 30 min resulted in the whole destruction of pyramids. The average reflectances of the 5-min-etched sample before and after being coated with 75-nm-thick Al2O3 layer are 4.62% and 3.47% in the range of 200-1000 nm, respectively.1. IntroductionAs we know, the reflectance of silicon wafer after being sliced is so high that the maximal photoelectric conversion efficiency of silicon based solar cells is limited. Therefore, alkaline texturization process was used for silicon solar cell in industrial production. But the reflectance of this alkaline textured wafer is still greater than 10% and this process can only be used for monocrystalline silicon solar cell."

Jan 1, 2013

By Y. A. Chang, J. Woodford, C. R. Kao

Reactive diffusion studies between NbC and Si were carried out at 1300 °C under a vacuum of 10-5 torr and a uniaxial pressure of 1 MPa. The annealing time ranged from 8 to 100 hours. The Si used was single crystal silicon; the NbC was hot-pressed powder compact. A NbSi2+SiC two-phase reaction layer formed with NbSi2 as the matrix and SiC as discontinuous particles. The microstructure of the reaction product is homogeneous, dense, and fine. The NbSi2 grain size and SiC particle size are in the micron range. The growth of the reaction products follows parabolic kinetics. Extrapolation of the data to zero thickness suggests an apparent incubation time of 3.5 hours. However, for short annealing time «60 hours), the thickness data can be approximated by linear kinetics with an initial growth rate of about 2 11m/hr. Based on these experimental observations, a growth mechanism for the reactive diffusion between Si single crystal and NbC powder compact is proposed. We propose that the nucleation sites for the SiC particles are at the voids of the NbC powder compact. This proposed nucleation mechanism offers a potential way of controlling the SiC particle size by changing the void size and void density of the NbC powder compact. This hypothesis, if proven to be true, will allow us to control mechanical properties of the composites by tailoring the SiC particles formed. It is also pointed out that the microstructure requires Si to be the dominant diffusing species and to diffuse through the reaction layer, while Nb and Conly have to undergo local rearrangement.

Jan 1, 1996

By Michael K. Rhodes

A 120 tonne per day BacTech bacterial oxidation plant treating refractory gold concentrates for Gold Mines of Australia&apos;s Youanmi project in Western Australia commenced operation September 1994. This was the first commercial application of the BacTech process. A pilot plant trial on concentrates produced from Youanmi ore was carried out at BacTech&apos;s laboratory in Perth. Results and measurements from this trial were used by Signet Engineering Pty Ltd to design the commercial plant. This paper cover the results obtained from the piloting, their implementation in the plant design and the initial commissioning of the full scale plant.

Jan 1, 1995

By C. -S. Jiang

In most copper refineries, addition agents are added at predetermined rates with no further monitoring of their activity or concentration in the electrolyte. Increasingly stringent cathode quality requirements, and a desire for better process control in tankhouse operations, have recently directed a number of refineries to search for a better addition agent control strategy. Extensive development work has been carried out at the Noranda Technology Centre for the monitor in of glue and thiourea in copper refinery electrolyte using cyclic voltammetry (cv~. Data from both synthetrc and commercial electrolytes are presented, showing the ability of CV to produce reliable and easily identifiable fingerprints of addition agent concentrations in copper refinery electrolyte.

Jan 1, 1991

By Charles A. Sorrell

Two red muds, two fly ashes, and several aluminosilicate minerals were subjected to direct treatment with concentrated H2SO4 at temperatures of 175°C and below. X-ray analysis showed that virtually all the sulfate reaction products remained in the solid residue because of their low solubilities in x SO Substantial portions of the Al2O3 Fe2O3TiO2, Na2O, and K2O components of the materials reacted to form water soluble sulfates, which were then removed by H2O leaching at 55°C. The solid residue after water leaching consisted largely of amorphous silica and, in lime bearing compounds, CaSO4, The reaction and leaching processes were effective in removing all or nearly all the Al2O3. Fe2O3, TiO2, Na2O, and in lime components in the fly ashes, red muds, china clay, bentonites, the nephelioe fraction of nepheline syenite, and a plaster insulating brick composed of anorthite and mullite. Reaction with potassium feldspar and petalite took place, with formation of alkali aluminum sulfates, but the reaction rates and yields were extremely low. Potassium feldspar can be heated with Na2O and x O in air at 700°C for 24 hours, or with CaO at 1000°C for 24 hours, after which the reaction product kaliophilite, nepheline, and leucite-like phases, prove to be very susceptible to H2SO4, reaction and H2O leaching, providing yields near 100% of the Al2O2 content. An alternative method of H SO treatment consists of heating the sample in a silica tube and passing H2SO4 vapor over it. Preliminary results indicate that this method can be effective in enhancing the kinetics of reaction with the Al O component of potassium feldspar and offer the possibility that formation of Al2 (SO ) Fe2(SO4)3 and TiOSO4 can be accomplished selectively by taking advantage of the fact that the upper stability limits of the respective sulfates in the presence of H2SO4 vapor will be different.

Jan 1, 1982

By Chen Chen, Wang Yanze, Hong Xin

Furnace superalloy was applied in harsh environment within the erosion of high temperature and oxidizing atmosphere. With plasma powder surfacing technology, iron-based alloy powder was sprayed on the surface of 310S stainless steel to form oxidation layer that increases the oxidation resistance and reduces the cost of materials. With optimum technological parameters, in this paper, oxidation test of 100 hours on iron-based cladding alloy and furnace alloy were carried out at 1200 . The technique of XRF, XRD and EDS were used to characterize composition, oxide morphologies and surface mechanical properties. The results showed that Element composition of cladding layer formed by Plasma powder surfacing was well distributed. Its oxidation weight gain rate of 100 hours was 0.4552g/m2h, belonged to antioxidant level. The oxidation weight gain rate of furnace alloy was 1.4617g/m2h, belonged time-antioxidant level. And on the mechanical comparison test, surfacing alloy is relatively excellent than furnace alloy.

Jan 1, 2016

By Jinjing Dua, Jun Zhua, Kuiren Liub, Bin Wang, Xiaolei Wua

V-Ti-Fe as hydrogen storage alloy was prepared by reducing metal oxides with a metallothermic reduction method. The deoxidation process of the V-Ti-Fe alloy was performed by electro-deoxidation and vacuum induction melting method, respectively. The results showed that the content of oxygen impurity can be controlled at about 0.2wt% after electrolyzing for 240min. Both the maximum values of hydrogen absorption capacity and the effective hydrogen desorption capacity are 2.65wt% and 1.01wt%, respectively. The deoxidization effect of vacuum induction melting process is more remarkable, with Ce as the reducing agent. It is found that Ce addition is beneficial for reducing the componential segregation, promoting the hydrogen absorption activation of V-Ti-Fe alloy. When m(Ce)/m(alloy) is up to 5%, the oxygen content has been reduced to 0.05wt% and the maximum hydrogen absorption capacity and the effective hydrogen desorption capacity are up to 3.36wt% and 1.85wt%, respectively.

Jan 1, 2015

By Yanlong Li, Lifeng Zhang, Ying Ren

In this work, a multiphase mathematical model for the fluid flow in argon-stirred steel ladles was established and validated by experimental measurement of wood's metal. Alloy dispersion in the molten steel was calculated. The melting and mixing of alloy was faster with smaller size of the alloy particles, larger superheat and bigger slip velocity. The current mixing time is approximately 300 s with 30 mm alloy diameter and 91.5 K superheat.

Jan 1, 2014

By Larry G. Twidwell

The removal of dissolved arsenic from mine waste waters utilizing a lime/phosphate precipitation technique has been studied on a laboratory scale at Montana Tech of The University of Montana and on a pilot scale at MSE Technology Applications as a wastewater treatment process potentially capable of removing dissolved arsenic to <50 µg/L. Arsenic bearing lime and lime/phosphate slurries were subjected to laboratory extended-time air-sparged aging for over four years. The lime slurries released their arsenic back into solution in a relatively short period of time, whereas the lime/phosphate slurries showed limited release of arsenic. The developed process has been pilot scale tested by MSE-TA for the EPA Mine Waste Technology Program on three waters, ASARCO smelter blowdown water, ASARCO thickener overflow water, and Mineral Hill Mine groundwater. The laboratory study results will be presented and discussed in this presentation. The pilot scale results will be presented and discussed in a companion presentation. Stability, Aging, Apatite, Johnbaumite

Jan 1, 2005

By Kang-In Rhee

Nonferrous metal recycling not only provides energy saving and environmental benefits but also is a significant factor in the supply of various types of metals used in our society. Recycling plays an important role in establishing the sustainability of materials. The total amount of recycled nonferrous metals by weight accounts for less than 5% but their value is larger than 50% compared to ferrous metal recycling which consists of about half of the total metal recycling in weight. This paper describes trends and typical achievements in nonferrous metal recycling and overviews the present and future of nonferrous metal recycling technology and business in Korea.

Jan 1, 2006

By Ali P. Gordon, James Williams

Joints gasketed with viscoelastic seals often receive an application of a secondary torque, i.e., retorque, in order to ensure joint tightness and proper sealing. The motivation of this study is to characterize and analytically model the load and deflection re-torque response of a single 25% glass-fiber reinforced polytetrafluorethylene (PTFE) gasket-bolted joint with serrated flange detail. The Burger-type viscoelastic modeling constants of the material are obtained through isolating the gasket from the bolt by performing a gasket creep test via a MTS electromechanical test frame. The re-load creep response is also investigated by re-loading the gasket after a period of initial creep to observe the response. The modeling constants obtained from the creep tests are used with a Burger-type viscoelastic model to predict the re-torque response of a single boltgasket test fixture in order to validate the ability of the model to simulate the re-torque response under various loading conditions and flange detail.

Jan 1, 2015

By Xiangru Chen, Honggang Zhong, Qijie Zhai, Qingqing Sun

"A horizontal directional solidification equipment, with an in-situ pouring system, was employed to physically simulate the solidification behavior of continuous casting. In this paper, the 2304 duplex stainless steel (DSS 2304) was investigated using this equipment due to its microstructure produced by continuous casting process was usually not satisfied. The grain size combined with the position of columnar to equiaxed transition (CET) of DSS 2304 were observed and the results showed these microstructure characteristics were very close to those of the continuous casting slabs. In addition, the influences of pouring temperatures and cooling conditions on the CET behavior were investigated. The results revealed that the length of the columnar grains decreased with decreasing the pouring temperatures and flow rates of the cooling water. Besides, the content of austenite decreases with increasing the distance from the chilled sidewall.IntroductionDuplex Stainless Steels (DSSs) have been widely used in industry for their excellent mechanical strength and superior corrosion resistance in Cl- environments when compared with other stainless steels [1,2]. Their good performances are mostly on account of the duplex phase structure-ferrite (d) and austenite (?) and the high proportion of alloying elements. Although, DSSs have good ductility, but worse formability compared to the austenitics, and this is the key to restrict DSSs application [3]. This is due to the differences properties between the two phases. The hot workability of ferrite (d) is better than austenite (?) and exhibits a lower flow stress during hot rolling processing [4]. The early workers had revealed that coalescent force of phase interface, microstructure, difference of mechanical property between two phases and the precipitations are the main factors affecting the formability of DSSs [5,6]. Another important reason that affects the alloy’s mechanical properties is columnar to equiaxed transition (CET) [7]. It often occurs during continuous casting solidification process and induces inhomogeneous mechanical properties and the microstructure varies with different processing parameters, such as pouring temperatures, cooling conditions (water flow rates in the cooling zones) and casting speed [8]."

Jan 1, 2012

By S. P. Vanka, B. G. Thomas, S. Sivaramakrishnan

"During the continuous casting of steel, transient 'flow events can be very important to the generation of quality problems, such as shear entrainment, surface level fluctuations and bubble entrainment. These phenomena can be better predicted using Large Eddy Simulation (LES) models than the K-E models, which have been extensively studied. In this work the turbulent transient flow in a water model of a continuous caster has been both simulated using LES models and measured using Particle Image Velocimetry (PIV). The results of PIV and LES have been compared to validate the LES model and also to enhance the understanding of the prominent transient features of the flow field. The flow near the top surface in PIV was found to contain periods of 5-1 Os when the velocities were three to four times their mean values, which is of importance to the shear entrainment of the liquid flux. In both simulation and PIV the upper roll structure is found to change chaotically from a single large recirculation structure to a set of distinct vortices. The inlet swirl in PIV is seen to persist more than halfway across the mold, causing a characteristic staircase velocity vector pattern when viewed in a plane parallel to the wide faces. The lower rolls in PIV are significantly asymmetric for very long periods of time (- I-hour) and go through a repeating sequence of features. One of these features involving a short circuit between the upward and downward flow in the lower roll is also seen in the simulation and is of significance to bubble entrapment.IntroductionThe turbulent flow through the nozzle and in the mold of the continuous caster has been studied extensively using computational Reynolds Averaged Navier Stokes (RANS) models of turbulent flow [1,2]. Defects, such as internal inclusion of liquid fl4x through surface shear, pencil pipe defects due to bubble entrapment, surface defects due to level fluctuations are caused by transient flow phenomena oc'curring in the mold. These phenomena can be better predicted using transient Large Eddy Simulation [3] or ""LES"" models."

Jan 1, 2000

By B. R. Adams

This paper discusses the use of a reacting CFD model to determine chalcopyrite kinetics in a drop tube furnace and to predict the reaction of a chalcopyrite concentrate in the reaction shaft of an industrial smelter. Reacting CFD codes can be applied to determine the consequences of the interaction of gas with particles and therefore improve the ability to derive kinetic parameters that take into account the temperature and oxidation histories that different particles will see. This paper describes the application of such a model to derive improved kinetic parameters for the pyrolysis and oxidation of chalcopyrite. The reaction shaft model includes the effects of turbulent fluid mechanics, entrained flow mixing, turbulent particle dispersion, heterogeneous particle reactions, radiative and convective heat transfer, and&apos; surface and bath deposition rates. Particle reaction and composition characteristics are predicted as a function of particle trajectory and deposition and are used to aid in evaluating shaft performance.

Jan 1, 1999

By Yuanbo Zhang, Qian Li, Helei Zhang, Heng Yu, Guanghui Li, Tao Jiang

"Large reserves of specularite iron ores have been found all over the world, which is characterized by high total iron grade, low gangues content, as well as low commercial price. However, it has not been widely used in sinter or pellet production due to its inferior sintering and roasting behaviors. It has shown that the proportion of specularite ores was increased as high as 40%~50% and good results was achieveed by using Composite Agglomeration Process (CAP), an innovative agglomeration process invented by Central South University. But the mineralization of specularite is still unknown during composite agglomeration processing. In this paper, the induration characteristic of specularite ore is studied by simulating CAP in laboratory, as well as microstructure analysis of CAP product. The results show that specularite pellet is mainly indurated through recrystallization of Fe2O3, calcium ferrite within high basicity sinters matrix interweaves with the recrystallized Fe2O3 on the surface of the pellet, which forms an integral microstructure, and ensures high strength of CAP product for ironmaking.IntroductionLarge reserves of specularite iron ores have been found all over the world, especially in Minas Gerais of Brazil, Xuanhua city and Anshan city of China, Elba island of Italy, St.Gotthard of Switzerland, Cumberland of Britannic, and so on. The specularite ores have a smooth surface, as well as a good crystallization and dense texture. When specularite is used to produce pellets, the specularite ore grains are difficult to adhere onto green ball due to its poor ballability. Moreover, specularite pellet requires high roasting temperature over 1300°C [1]. When specularite ore is used in sintering, the permeability of sintering bed gets bad and the quality of sinter is diminished. The practice in a few sintering plants finds that the output and strength of sinter decrease with the increase of specularite proportion, and the consumption of coke increases [2-4]. Therefore, the utilization of specularite has been limited. Composite Agglomeration Process (CAP) is an innovative technology invented by Central South University [5-7]. The process has the following merits: making reasonable utilization of different iron ore resources; improving the quality and output of sinters; manufacturing sinters with low basicity; significantly reducing energy consumption, etc[8-9]. It has been shown that large proportion specularite ores, as high as 40%~50% can be used well by CAP [10], but the mineralization of specularite pellet is still unknown during composite agglomeration processing. In this investigation, the induration characteristics of specularite ore pellets is studied by simulating CAP in laboratory, and the phase composition and microstructure of CAP product are also characterized by using microscope and Leica image analyzer (Germany, Leica DM RXp)."

Jan 1, 2011