Search Documents

By W. Joseph Schlitt

The types of copper leaching and recovery operations in the United States are reviewed, along with characteristics and trends in the industry. The contribution of the various leach operations to total mine output is discussed in order to provide a perspective on the relative importance of copper leaching as a method of production.

Jan 1, 1980

Feb. 5. Society for Applied Spectroscopy, 6 pm, supper, Tosca's; 8 pm, meeting, Socony-Vacuum Training Center, 63 Park Row, New York. Feb. 6, AIME, Chicago Section, Chicago Bar Assn., 29 S. La Salle St., Chicago. Feb. 18-21, AIME, annual meeting, Hotel Statler, New York. Feb. 19, Michigan College of Mining and Technology, alumni reunion, Skytop Room, Hotel Statler, New York. Feb. 21, AIME, Utah Section, Newhouse Hotel, Salt Lake City. Feb. 28, Bituminous Coal Research, Inc., annual meeting, Edgewater Beach Hotel, Chicago. Mar. 3-7, ASTM, spring meeting and committee week, Hotel Statler, Cleveland. Mar. 5, AIME, Chicago Section, Ladies' Night, Chicago.

Jan 1, 1952

By William Loblowitz

A simplified system of flotation testing has been developed recently at the Bureau of Mineral Research of Rutgers University. The technique involves the known principle of skin flotation and can be used with minute quantities of sample and reagents in a beaker. A vessel containing the conditioned sample with added water and flotation reagents is held inclined and rotated slowly. Water-repellent particles come in contact with air and float on the surface of the liquid, while wettable particles are submerged. The float is poured off and filtered whereas the nonfloat remains in the beaker. The filtrate may be returned to repeat the process. This procedure can be made quantitative. Separations are obtained and are remarkably complete and repeatable. The effect of different reagents, optimum quantities, pH and other variables can be determined in a fraction of the time required for conventional testing. However, the method gives no information on the effect of frothers and the quality of froth to be expected in a cell, and it is not practical for particles finer than 200-mesh. Unlike other preliminary tests, separate float and nonfloat products are obtained, and their contents can be determined quantitatively by chemical analysis or grain counts. After the optimum reagent combination has been determined, the effect of fines and frothing may be verified in the conventional flotation cell. On the other hand, agglomeration-tabling can be directly duplicated from beaker tests. Procedure: Five to ten grams of sample are weighed into a 100-ml beaker. Flotation reagents and a small initial quantity of water are stirred together; additional water is then added to produce the proper water-solids ratio. The beaker is then tilted to 45" and rotated slowly. After three to five rotations, liquid and float are poured off and filtered; the filtrate may be recycled until the separation is completed. One test generally requires less than 10 min. Reagent concentration and pH remain quite constant because of the recycling of the filtrate. Two to four tests may be made simultaneously, and the effect of varied conditions may be observed by comparison. Considerable time is saved in preparation and handling since small quantities of sample suffice for a series of systematic tests. Repeatability One test was repeated four times under constant conditions. The sample used was a quartz sand containing approximately 24 pct feldspar and some clay aggregates. The +28-mesh grains had been screened out, and most of those finer than 100-mesh had been removed by hydraulic classification. The results are presented in Table I. For comparison, 500 g of the sample were separated by agglomeration-tabling using the same reagent combination and quantities as given in Table I. The weight percent float was 18.3 pct, composed almost entirely of feldspar and with only traces of quartz. Most of the remaining feldspar was recovered in a middling product with 2.2 pct by weight.

Jan 1, 1952

By R. H. Frazier, C. H. Lorig, F. W. Boulger

THERE are both advantages and disadvantages in using semikilled steels in place of killed steels. One advantage of semikilled steels is they provide a higher ingot-to-product yield. This is especially important to shipbuilders in the time of national emergency. By using semikilled steel for hull plates, a greater number of ships can be built from the same ingot tonnage. Consequently, if semikilled steel plates are adequate for the service, the advantage of the higher product yield is of considerable importance. The performance of hull plates is closely associated with the ductile-to-brittle transition temperature, and this, in turn, is strongly dependent on the composition of the steel. A low transition temperature is desirable because it indicates that the steel is less likely to fail at low ambient temperatures. Killed steels are known to have lower transition temperatures than semikilled steels. It is believed that the better qualities of killed steels in this respect are due mainly to the low oxygen contents of the steel. The principal deoxidizers, aluminum, silicon, and manganese, lower the oxygen content. Fundamental studies1-0 have shown that the oxygen content remaining after the addition of one of these three elements is influenced by the residual amounts of the other two present. In the current study, therefore, various amounts of silicon and aluminum were added to steels containing different manganese contents for the purpose of studying the influence of silicon and aluminum on the notched-bar properties of hot-rolled steels. Eleven types of steels were studied. The temperature at which the plates were finish-rolled was care- fully controlled at 1850°F. All plates were rolled to ¾-in. thickness, and tested in the as-rolled condition. The total number of steels prepared in the laboratory for this study was 95. The charge consisting of ingot iron and ferrosilicon equivalent to 0.10 pct Si was melted in a 200-lb induction furnace under an atmosphere of argon to insure low, uniform nitrogen contents. After the charge was melted and the desired temperature was obtained, the melt was partly deoxidized with either silicomanganese or aluminum. Aluminum was used for this purpose in only those steels with very low silicon contents, where the finished steel was to contain some aluminum. This initial deoxidizing addition was made to obtain consistent recoveries of subsequent additions of ferro-manganese, ferrosilicon, and aluminum. Carbon, in the form of graphite, was added, either just prior to tap or to the final aluminum addition. The entire heat of 200 lb was poured directly into a 6x6-in. big-end-up mold. The ingots of semikilled steel were capped with a steel plate. The killed steels, on the other hand, were poured with a hot-top containing 14 pct of the total volume of the ingot. The ingots were processed by heating to 2250°F, followed by forging to slabs 1¾ in. thick and 6 in. wide. After reheating to 2250°F, the slabs were rolled to 0.9-in. gage, using reductions of approximately 1/6 in. per pass. The 0.9-in. thick plates were immediately recharged in a furnace held at 1850°F. After 30 min in the furnace at 1850°F, the plates were rolled to ¾ in. in one pass. Following the final pass, the plates were stacked on edge on a brick floor, with a brick separating one from another, where they were allowed to cool in air. Drillings for chemical analysis were taken from the plates at locations corresponding to the top and bottom of each ingot. Carbon, manganese, silicon, phosphorus, sulfur, and nitrogen contents of each sample were determined. The analysis of each steel was carefully controlled so that the contents of

Jan 1, 1957

By Rclssell Gibson, F. S. Turneaure

The tin deposit of Monserrat; Bolivia, consists of one major vein 1600 m in length. The ore is unusual because of the notable quantity of teallite, even though cassiterite is the principal tin mineral. The deposit, formed at shallow depth under a wide range in temperature, may be classed as xenothermal. Polished sections reveal a complex history of replacement, with low-temperature minerals deposited before high-temperature minerals.

Jan 1, 1950

By V. M. Dobrynin

Experimental data demonstrate that physical properties of porous rocks change under pressure. In this paper an assumption is made and proved that under pressure the changes of physical properties such as porosity, density, permeability, resistivity and velocity of elastic waves are controlled to a large extent by the pore compressibility of rocks. It is also shown that the pore compressibility of rocks can be determined, within the range of pressures from 0 to 20,000 psi, by knowing the maximum pore compressibility and the magnitude of the pressure. Mathematical equations were developed which permit one to define changes in physical properties of porous rocks under pressure. These equations were verified by experimental data obtained from the study of sandstones. INTRODUCTION In studying the behavior of porous rocks under pressure in the field of petroleum technology, the most interesting aspect is the observation of those properties which characterize the rocks as possible reservoirs — for example, porosity, permeability, resistivity, density and the velocity of elastic waves. The literature dealing with this problem mainly contains data concerning the study of only one or at most two of these parameters, but not of the group as a whole. An attempt is made in this paper to find general equations involving each of these parameters, which will permit the study of the behavior of rocks under pressure. All experimental data used here were obtained from the investigation of consolidated sandstones. EXPERIMENTAL In addition to the use of published experimental data, an experiment was carried out which studied the main physical properties of sandstones under pressure. Two homogeneous quartz sandstones were chosen for this purpose: (1) the Torpedo sandstone from Kansas, and (2) the Medina sandstone from Ohio. The porosity of the Torpedo sandstone was 20.2 per cent, and that of the Medina 8.7 per cent. Permeabilities were 45 md and less than 1 md, respectively. Each sandstone contained about 5 per cent clay minerals, consisting mostly of kaolinite and chlorite, which were distributed quite evenly throughout the samples. One cylindrical sample 2 in. in diameter and 5 in. in length was cut from each sandstone and then saturated in a vacuum with a 3N solution of NaC1. This high concentration was used in order to obtain true formation factors and to decrease the swelling of the clay minerals. The methods of mounting the samples and measuring the changes in porosity and resistivity were practically the same as those described by Fatt and Mann.1,2 Changes of resistivity under pressure were studied for sandstones with 100 per cent water saturation, and for sandstones with the irreducible water saturation. The irreducible saturation was obtained by enclosing the saturated rock samples in relatively fine silicate powder so as to remove the water by capillary action. This procedure is described by Orkin and Kuchinski.3 Changes of permeability with pressure were determined at room temperature using nitrogen as the flowing medium. In studying the effects of pressure, one series of measurements was made using an internal pore pressure Pi equal to the atmospheric pressure, while the overburden pressure Pe ranged from 0 to 20,000 psi. A second series of measurements was used over the same range of overburden pressure, but with an internal pore pressure of 1,800 psi. When the results were compared on the basis of net overburden pressure (Pe — 0.85 Pi ), there was practically no difference for these two sandstones. The origin of the factor 0.85 in the expression for net overburden pressure is given by Brandt,4 Fatt5 and Geertsma.6 The relatively large bulk volumes of the sample (about 15 cu in.) made it possible to observe a

Jan 1, 1931

By Luiz C. Correa da Silva, Robert F. Mehl

A. D. Le Claire and R. S. Barnes (Atomic Energy Research Establishment, Harwell, Didcot, Berks., England)-—This much awaited paper admirably confirms that the Kirkendall effect is a true diffusion phenomenon and likely to be found in all diffusing systems. The most likely explanation put forward so far to account for the shift of interface is that the two components of the system, diffusing in opposite directions, do so with unequal rates so that there is a net loss of material from that half of the diffusion zone rich in the more rapidly diffusing component. This loss is accompanied, and at least partly compensated for, by a closing up or decrease in volume of this latter half of the diffusion zone and an expansion of the other half so as to tend to keep constant the overall volume per atom. This is manifest as a movement of the original interface. If this is a true picture of what is taking place then there are at least two important matters requiring further study."1—The quantitative relating of the observed shift with the independently measured separate diffusion coefficients of the two diffusing species."2—A detailed study of the mechanism and characteristics of the closing up process."We would like first to make a few remarks pertinent to these topics. In connection with the first of these, it is a pity that more and detailed measurements were not made on the Au-Ag system, the only one for which the separate diffusion coefficients of the two species have been measured.'" One of us (A. D. Le C.) has calculated from Johnson's results the shift to have been expected in samples D.2 and D.3. Darken4 showed that the velocity v with which the markers move is related to the separate diffusion coefficients Dau, Dag, by the eauation:"dN"v = (Dag — Dau "dx"dN"where .is the concentration gradient at the mark-ax"ers. Under certain conditions,4, 20 it can also be shown that:"Xm"v = "2t"where x, is the total marker shift after time, t:"dN". . xm = 2t (Dag — Dau) [9]"dX"Johnson measured Dag and DAu in a chemically homogeneous alloy and so his reported figures represent the true or ideal diffusion coefficients"; the same quantities in eq 9 represent the actual diffusion coefficients as would be measured in the presence of a chemical concentration gradient, so we need to multiply Johnson's reported values of Dag and Dau by the"1 before insert-dlogN "ing them in eq 9. 7 is the activity coefficient of Ag at the concentration prevailing near the markers which we shall assume to be - 50 pct. The values of the thermodynamic factor for N = 0.5 and the temperatures at which D.2 and D.3 were annealed were obtained from thermodynamic data quoted by Darken.' aN/ax was computed from the coefficient of inter-diffusion of Au and Ag given by Johnson on the assumption that in the samples D.2 and D.3, the concentration distance curve could be represented by the standard equation:""No is the original difference in concentration between the two halves of the couple, and + is the error or probability function."aN/ax at x = 0 is then given by:"adN/dx "2/nDt"and we assume that this represents the concentration gradient at the markers, although it is probable that the figure is slightly high."When all the appropriate quantities are inserted in eq 9, we find that the expected shifts are: for D.2, 0.0134 cm and for D.3, 0.0119 cm."The agreement between these results and those

Jan 1, 1952

By R. E. Ogilvie, A. R. Kaufmann, S. H. Gelles

The solid-solubility limits of iron in beryllium were determined between 850o and 1200oC by analysis of differential type multiphase diffusion couples, using an X-ray absorption technique. The maximum value of the solubility limit was found to be 0.92 ± 0.02 at. pct (5.46 wt pet) at the eutectic temperature 1225°C. The solubilities of nickel and beryllium were determined between 900°and 1200°C by the same technique and the maximum solubility was found to be 4.93 + 0.01 at. pct (25.2 wt pet) at the eutectoid temperature, 1065°C. A previously unreported high-temperature phase which decomposes eutectoidally at 1065 °C was found to exist in the beryllium-nickel system at a composition of approximately 8 at. pct Ni (36 wt pet) by diffision-couple analysis. The presence of this phase was confirmed by thermal analysis and metallo-graphic analysis of the structure resulting from the eutectoid decomposition. G. V. Raynor1 has treated the solid solubilities of some of the elements in beryllium on the basis of the "Hume-Rothery" rules2 which have been modified to include ionic size and ionic distortion effects. It was predicted that the solubility of iron and nickel in beryllium should be slightly less than that of copper. The lowering of the solubility, according to Raynor, is due to a more unfavorable relative valency effect and an ionic size effect. Kaufmann and corzine3 have compiled data on the solubilities of elements in beryllium and have discussed them in the light of the Raynor paper. These authors feel that, because the elements having the greatest solubility in beryllium systematically fall in the Group VIII and IB Columns of the periodic table, the electronic structure greatly influences the maximum solid solubility of elements in beryllium. The solubility of iron in beryllium was determined by Teitel and cohen4 as part of the study of the beryllium-iron phase diagram. The determination was carried out by X-ray and thermal analysis and according to the phase diagram presented, the maximum solubility of iron in beryllium is 0.41 at. pct (2.5 wt pct) at 1225oC. However, it is estimated that the uncertainty in the position of the a-beryllium primary solid-solution boundary is about 0.5 at. pct (3wtpct). Losana and Goria3 in studying the beryllium-nickel phase diagram, determined the solid solubility of nickel in beryllium by thermal analysis. They found the maximum solubility to be between 1.65 and 2.65 at. pct (10 to 15 wt pct) at 1240°C. This value decreased rapidly with decreasing temperature. In determining approximate ranges of solubilities for different elements in beryllium, Kaufmann, et al,8 reported a value of between 1.3 and 1.7 at. pct (7.9 to 10.1 wt pct) for the solubility of nickel in beryllium. The value was obtained by metallographic examination of quenched alloys and lattice-parameter measurements. However, the authors also noted a single-phase structure for a 1.7 at. pct Ni alloy (10 wt pct) on cooling from the liquid. This would indicate a higher solubility range than was reported. ~isch,' in his X-ray studies of beryllium-copper, beryllium-nickel, and beryllium-iron intermetallic compounds, reports the disappearance of a second phase (Ni,Be2) in the beryllium primary solid solution at approximately 4 at. pct (20 wt pct). THEORY The analysis of concentration gradients in diffusion couples has proven to be a useful tool in determining phase equilibria.8-14 In this particular study the diffusion couples were chosen to straddle the expected composition range of the phase boundary, then heat treated at a given temperature and the concentration gradient evaluated. The composition of the phase boundary for a given temperature appears at a point of discontinuity of the composition gradient. Examples of typical phase diagrams and the concentration gradients which should be found in such systems are shown in Fig. 1. In the present work, gradients of the form of Fig. l(c) were obtained in diffusion couples made of pure beryllium and two-phase alloys of beryllium with either iron or nickel. The composition at the point where the gradient becomes discontinuous, Cs, corresponds to the solubility limit of either iron or nickel in beryllium. The analysis of the concentration gradients was carried out by an X-ra absorption method developed and applied by Ogilvie and later used by Moll13 and Hilliard.l4 It depends on the fact that the absorption of X-rays by matter is determined by the concentration and type of the various atomic species present. The relationship for the intensity, I, of a monochro-

Jan 1, 1960

By A. M. Gaudin

Activation of sphalerite with silver ions results from the exchange of two Ag ions for one Zn ion in the sphalerite lattice. The exchange is proportional to the logarithm of time and proceeds until either of the reactants is consumed. Sodium cyanide prevents the activation of sphalerite by controlling the ratio [Zn++]/[Ag+]' in solution. If sphalerite has already been activated with excess silver, cyanide ions can deactivate sphalerite provided oxygen is present. SOLUBLE: silver salts are effective activators for flotation of sphalerite with potassium ethyl xan-thate as collector.* Since sphalerite takes up large quantities of silver ions rapidly,2-4 investigation of this system appeared fruitful for studying the mechanism of sphalerite activation and deactivation. Experimental data presented here comprise studies of the mechanism and rates of activation and deactivation of sphalerite with silver and cyanide ions. A 20-lb sample of sphalerite from Ottawa County, Oklahoma, was handpicked, crushed, screened, hy-drosized to produce a 65/100-mesh fraction, and purified by electrostatic separation. The sphalerite was then leached with benzene and absolute ethyl alcohol to remove possible organic contaminants and with 0.1 M NaCN to remove any copper that might have been picked up during screening. The benzene had been specially purified by grinding with fine sphalerite for 12 hr to remove trace impurities that might have had a specific affinity for sphalerite. Ii'inally, the mineral was washed, dried in flowing nitrogen, and stored in large ground-glass stoppered weighing bottles under a small nitrogen pressure. The specific surface of two samples from the 65/100-mesh sphalerite stock, measured by krypton gas adsorption," was 420 cm2 per g. Compared with spheres of the same size and specific gravity, the prepared mineral had five times as much surface. Results of a wet chemical analysis and of a spectro-graphic study are given in Table I. Manganese, nickel, tin, indium, thallium, cobalt, and magnesium were not detected spectrographically. All solutions were preparid by -adding reagent-grade chemicals to conductivitv water. which had been previously saturated with the desired gases. Nitrogen and oxygen were purified, but no attempt was made to purify the laboratory air. Radioanalysis was carried out with prepurified Ag110 tracer obtained from the Oak Ridge National Laboratory. The complete decay scheme for Ae is complex. Its primary emissions are 0.09 and 0.55 mev ß rays and 1.48 mev y raysB and its half-life is believed to be 270 days. In preparation of solutions of AgNO3, the amount of Ag110 added was negligible compared to that of the inert silver. Abstraction of silver from solution by sphalerite was measured after agitation of 1.5 g sphalerite with 20 ml of solution in 50-ml pyrex flasks. All sample preparations were carried out in a dry box so that the proper atmosphere could be maintained. After the mineral had been agitated in the silver nitrate solution, an aliquot of the solution and a sample of the wet mineral were transferred to separate counting vials and weighed. The solid sample was dried and re-weighed and the activity in both vials measured by means of a scintillation counter. With scintillation counting it is possible to count y radiation from the solid and liquid, a distinct advantage over the older ß-ray counting techdiques.4 All measurements of silver activity were made using a sodium-iodide well-type scintillation counter. The amount of zinc in solution was measured colorimet-rically by the monocolor method of Sandell.7 Activation Studies Exchange Between Zinc Ions and Silver Ions During Activation: The increase of Zn++ in solution during activation with Ag+ is shown in Table 11. These data indicate a replacement of one Zn++ by two Ag+. Analysis of a separate two-month agitation test indicated that the replacement of Zn++ by Ag+ was, as expected, in the molar ratio of 2.0.

Jan 1, 1958

PRESIDENT BENJAMIN B. THAYER,1 NEW YORK, N. Y. PAST PRESIDENTS JAMES F. KEMP,1 NEW YORK, N. Y. CHARLES F. RAND,2 NEW YORK, N. Y. FIRST VICE-PRESIDENT SIDNEY J. JENNINGS,1 NEW YORK, N. Y. TREASURER GEORGE C. STONE,1 NEW YORK, N. Y. SECRETARY EMERITUS ROSSITER W. RAYMOND, NEW YORK, N. Y.

Jan 4, 1914

By W. L. Phillips

Stress-train curves were obtained for single crystals of silver, Ag-5 pct Zn, Ag-10 pct Zn, and Ag-20 pct Zn tested in tension and shear at 78°, 195°, and 297°K. At room temperature the critical resolced shear stress gC increased, the length of' the easy-glide region increased, and the rate of' work hardening dwving easy glide decreased with increasixg zinc concentration. The change in the ratio of uc at room temperature to that at lower temperatures was significantly greater for the alloys than for pure silver. It was found that an increment in stress was necessary to continue slip when the slip direction was rotated 60 deg. The magnitude of this increment increased with strain for all alloys, increased with zinc concentration for a given strain, and for a given strain increased with decreasing -temperature. DESPITE its practical importance in improving the mechanical properties, alloying is not fully understood. Except for copper alloys few sets of systematic data are available. Von Goler and Sachs' studied the deformation of Cu-Zn alloys of increasing zinc content and found that, for dilute alloys, the critical resolved shear stress increases linearly with concentration. The range of easy glide was found to increase with increasing zinc content. Schmid and seliger,2 Sachs and Weerts,3 and Osswald4 have shown that with Mg-A1, Au-Ag, and Cu-Ni crystals, respectively, the critical resolved shear stress also varies linearly with concentration. More recently, Linde and his coworkers have investigated the variation of the critical shear stress of copper alloyed with tin , antimony, indium, germanium, silicon, nickel, and gold. They found that the slope of the critical resolved shear stress is related to the change of lattice parameter with composition, and also to the difference in Goldschmidt's atomic diameter between solvent and solute atoms. Garstone, Honey-combe, and creetham6 have shown that similar relationships can be found for small additions of silver, gold, and germanium to pure copper. They found that, with increasing silver or gold concentration, the critical shear stress for glide is increased by alloying, and so is the range of easy glide, which reaches as much as 60 pct for 0.50 pct Ag alloy and 0.62 pct Au alloy, as compared to 6 pct for pure copper of similar initial orientation. They also found that the alloying additions had little effect on the rate of hardening during easy glide, the slope scarcely changing with increasing alloy content. General secondary slip was detected only when the crystals began to harden rapidly. Although the slip appeared to be very fine in the early stages of deformation, coarser slip bands were formed towards the end of the extensive easy-glide range. The present investigation describes the deformation characteristics of single crystals of Ag-Zn containing different concentrations of zinc. Tension and shear testing were used for this study. EXPERIMENTAL PROCEDURE The method of growing the single crystals, sample preparation, and method of testing have been described in detail previously.' EXPERIMENTAL RESULTS A) Tension-Room Temperature. The initial orientations and stress-strain curves of single crystals of silver, Ag-10.0 pct Zn, and Ag-20.0 pct Zn are shown in Fig. 1. It is evident that there is considerable change in the stress-strain characteristics as a function of zinc concentration. The effects of zinc concentration on the critical resolved shear stress for both CU-zn8 and Ag-Zn alloys are summarized in Fig. 2. At all concentrations the resolved shear stress of the Cu-Zn alloys is higher than that of the Ag-Zn alloys. The resolved shear stress increases parabolically as a function of composition for both alloy systems. The length of easy-glide region increased with increasing zinc concentration, Fig. 3b). As the length increased the slope (do/de) decreased slightly, Fig. 3(b). Metallographic investigations demonstrated two significant effects of increasing zinc concentration. First, the amount of clustering increased, compare Figs. 4(a) and (b). The slip lines changed from uniform in pure silver to clustered in the Ag-20 pct Zn and Ag-30 pct Zn alloys. Second, the amount of cross slip decreased as the amount of clustering decreased.

Jan 1, 1968

By H. R. Ogden, E. S. Bartlett, A. G. Imgram

Unmodified disilicide coatirigs were applied to sheet-tensile specimens ofCb-Dg3 and Mo-TZM veJractovy- metal alloys. Coating thickness, degree of coating-substrate interdiffusion, and specimen geonzetry (notched and plain were included in the variables studied. Tensile tests were made to determine the ductile-lo-brittle transition temperature. The disilicide coating modestly increased the transition temperatlre of TZM, but had no effect on 043. Neither material condition (recrystallized or stress-velieved) nor specimen geometry (notched or unnotched) significantly altered the effects of coatings on the transilion temperatures of. the alloys. Cracks in the brittle coatings did not propagate into the substrate, and fracture modes appeared to be the same for both un-coated and coated specimens. MOST potential structural applications for refractory metals and alloys involve exposures to oxidizing environments at elevated temperatures. The general lack of oxidation resistance of these metals will require protective coatings to allow fulfillment of their potential. Currently preferred coatings for the oxidation protection of refractory metals are brittle intermetallic aluminides or silicides. These are typically formed on the surface of the refractory-metal substrate by a diffusion reaction between the substrate and a gaseous or liquid medium that is rich in aluminum or silicon. Because of the brittleness of these coatings, they will sustain no plastic deformation at low temperatures. They are frequently cracked by cooling from the coating temperature because of the thermal-expansion mismatch with the substrate alloy. Even if they survive cooling intact, they crack rather than sustain deformation under load at low temperatures. Thus, when a coated refractory metal is strained beyond the elastic limit of the coating at low temperatures, the mechanical environment of the substrate would include both static and dynamic cracks. These might be expected to influence the flow and fracture behavior of the substrate. This could be manifested in an altered fracture mode and/or an increase in the normal ductile-to-brittle transition temperature of the refractory-metal substrate. This paper presents the results of a research program that was conducted to determine the influence of the presence of a brittle surface coating on the low-strain-rate tensile behavior of typical refractory metals at low temperatures. EXPERIMENTAL PROCEDURES Material Preparation. Thirty-mil-thick sheets of molybdenum TZM alloy (Mo-0.5Ti-O.1Zr) and colum-bium D43 alloy (Cb-IOW-1Zr-O.1C) were obtained commercially. These alloys were selected as substrate materials representing two classes of materials important in current refractory-metal technology. The TZM was in the stress-relieved condition, and exhibited a heavily fibered grain structure. The D43 had been processed by the duPont "optimum" fabrication schedule,' and exhibited slightly elongated grains typical of this process. Tensile specimens of two geometries were prepared from these materials: 1) plain specimens with 0.2-in.-wide 1.0-in.-long gage sections; 2) specimens similar to above, but with a 0.06-in.-diam hole drilled in the center of the gage section, providing a stress concentration factor, Kt, of 2.5. The "notch" geometry was selected to represent a typical condition of a rivet hole or other geometric discontinuities as might be encountered in various applications. Machined specimens were degreased, with a final rinse in acetone, prior to the application of coatings. Specimens of each substrate and configuration were pack-siliconizedin a particulate mixture of 80 pct A1203, 17 pct Si, and 3 pct NaF. Specimens were embedded in this mix (contained in graphite retorts) and coated in an electrically heated argon-atmosphere furnace under time-temperature conditions to effect nominal 1- and 3-mil-thick silicide coatings: Coating Thickness, mils Thermal Treatment 0.6 to 1.4 24 hr at 982°C 2.4 to 3.2 48 hr at 1093°C Coating kinetics were similar for both the TZM and D43 substrates. These treatments had little or no visible effect on the substrate microstructure as determined by optical metallography. The coatings on TZM were essentially single-phase unmodified disilicides, while those on D43 showed substantial evidence of modification by proportionate reaction with the respective substrate elements or phases, as shown in Fig. 1. It was recognized that these coatings might not be particularly desirable regarding protective capability. However, it was desired to circumvent possible inter -ferring chemical interaction with the substrate by pack additives such as chromium, titanium, boron, aluminum, and other elements that typify the better protective coatings for these materials.' Thus, the results presented apply specifically to the simple silicide coatings investigated. They may not be rep-

Jan 1, 1967

By C. B. Alcock, R. G. Hudson

Sulfur pressure measurements above FeS in equilibrium with iron have been carried out by the Knudsen orifice method. A comparison is made of the weight loss of the cell per unit time obtained in the above experiments, that calculated from Richardson and Alcock's measurements of the S2 pressure above FeS in equilibrium with iron, and the dissociation constant for diatomic sulfur from spectroscopic and thermal data. EXTENSIVE equilibrium measurements have been made to determine the sulfur potentials of a great many systems of metallurgical interest.' In order to confirm their reliability, to supply data which may be of use in further thermodynamic calculations, and to establish the reliability of the Knudsen orifice in obtaining accurate thermodynamic values at high temperatures, the present investigation on the pressure of the gaseous species above FeS in equilibrium with iron has been carried out. The Knudsen orifice method has been used for these pressure measurements. Experimental The apparatus and general technique for this investigation are the same as that reported for the determination of the vapor pressure of silver.' To reduce the residual gas pressure in the evacuated chamber, a titanium getter, maintained at run temperature, was introducbed. Several types of Knudsen cells were used—platinum, zircon, and fused silica. The orifice in the zircon cell was fashioned with a small diamond wheel. The same precautions were used in this investigation as were employed in the work on Mo2S2.3 The FeS-Fe mixture was prepared by heating a sample of pure FeS,, supplied by K. K. Kelley of the Bureau of Mines, with excess iron powder, cp grade, obtained from the Fisher Scientific Co. These two substances were heated in a closed Armco iron crucible at 960°C, held in a vacuum of less than 10" mm Hg for 24 hr. The mass was then removed from the cell and ground in an agate mortar. In this form it was charged to the various Knudsen cells. Heating the Knudsen cell for an additional two days was sufficient to obtain constant rates of weight loss of the cell. The data obtained in this investigation are recorded in Table I. To establish whether or not a sulfide of iron is volatile at these temperatures, 0.7646 g of the FeS-Fe mixture, described above and containing 69.2 pet Fe, was placed in the zircon Knudsen cell. Run Nos. 103 to 109 were performed on it. After the completion of these runs, the total amount of iron left in the cell was obtained by chemical analysis. It contained 0.537 g Fe, compared to 0.529 g in the original charge. Thus, there was an apparent gain in iron of 1.5 pet. This is attributed to unknown experimental error, and the conclusion is that no sulfide of iron is volatile. The vapor pressure of pure iron4 is about one thousandth that of the sulfur pressure' at these temperatures. The vapor pressure of iron inside the Knudsen cell will be almost exactly that of pure iron, since in the iron-rich phase the percentage of sulfur is of the order of 0.025 pet.At this low percentage of sulfur Henry's law is probably obeyed by the sulfur. Thus, the iron will obey Raoult's law. In any event, the vapor pressure of iron will be lower than that of pure iron and, since the vapor pressure of pure iron is negligible compared to the pressure of sulfur, the weight loss of the cell due to the vaporization of iron should be negligible. Since neither iron nor FeS is volatile to an appreciable extent, the total weight loss of the cell must be due to the vaporization of sulfur. Discussion and Calculations On the assumption that S, is the only gaseous species present in appreciable quantity, its pressure

Jan 1, 1957

By R. W. Regehr, R. A. Burmeister

Epitaxial growth of GaAs 1-xPx on germanium substrates was achieved using an open tube vapor transport system. The compositional range of 0.3 < x < 0.4 was examined. The best results were obtained with (311) orientation of the germanium substrate. The physical and chemical properties of the resulting layers were investigated using several techniques. Spectrographic analyses of the layers indicate substantial incorporation of germanium into the GaAs t-X Px layer. Evidence is presented which indicates that this incorporation occurs via a vapor phase transport process rather than by solid phase dijfu-sion. Electrical measurements suggest that the germanium thus incorporated behaves predominantly as a deep donor in the compositional range of 0.33 < x * 0.40 and has a deleterious effect upon the luminescent properties of GaAs1-x Px. The increasing technological importance of GaAs1-xPx for use in light-emitting devices has led to an evaluation of several aspects of existing growth processes. The method most commonly used to prepare GaAs1-xPx for electroluminescent device applications is vapor phase epitaxial growth on GaAs substrates.&apos;-4 In a typical electroluminescent diode structure the active region of the diode is entirely within the epitaxial layer and thus the electrical properties of the substrate are relatively unimportant since it is effectively a simple series resistance (assuming hetero-junction effects to be negligible). The use of germanium rather than GaAs as the substrate material is of interest for several reasons. First, GaAs of reasonable structural quality has been epitaxially grown on germanium4-2 and it is reasonable to expect that GaAs1-xPx could subsequently be deposited on the GaAs layer. Second, germanium substrates are readily available with both lower dislocation densities and larger areas than GaAs. Finally, single crystals of germanium are more economical than GaAs single crystals. The principal objective of the present investigation was to test the feasibility of growing GaAs1-xPx epi-taxially on germanium substrates, and to evaluate the properties of such layers with regard to electroluminescent device requirements. The approach used was to a) demonstrate epitaxial growth of GaAs1-xPx on germanium, and b) characterize the relevant structural, electrical, and optical properties of the GaAs1-xPx layers. The possibility of germanium incorporation into the grown layers was of special interest since there was some indication of this in previous studies of GaAs growth on germanium.5&apos;11,12 Although a study of the electrical properties of germanium in GaAs1-xPx was not an intent of this investigation, several features of the electrical properties of the layers grown in the present study which appear to be due to germanium are described. EXPERIMENTAL PROCEDURE The open-tube vapor transport system used for the epitaxial growth of GaAs1-xPx is illustrated in Fig. 1. This system utilizes the GaC1-GaC13 transport reaction and is similar in most respects to the larger system described elsewhere.&apos; The germanium substrates were n-type, with a resistivity of 40 ohm-cm (Eagle-Picher Co.). These were cut to the orientations of {100), {111), and (3111, and were mechanically polished and chemically etched in CP-4 (5 min at 0°C) prior to growth. In some cases, a GaAs substrate was employed in addition to the germanium. The orientation of the latter was {loo}, and they were also mechanically polished and chemically etched prior to growth. The initial composition of the deposited layer was pure GaAs. After approximately 10 microns of GaAs was deposited on the germanium substrate, the phosphorus content of the layer was gradually increased over a distance of approximately 15 microns to the desired concentration and maintained at this value throughout the remainder of the growth. Typical operating parameters used during growth are given in Table I. Selenium was used as a n-type dopant in several runs to facilitate comparison of the electrical properties of the layers grown on germanium with those of layers grown on GaAs substrates, which are usually doped with selenium. The concentration of H2Se in the gas phase was adjusted to a value which would normally yield a carrier density of 1 to 5 x 101 7 at room temperature in layers grown on GaAs substrates. The terminal surfaces of the epitaxial layers were examined by optical microscopy for structural characteristics. Laue back-reflection photographs (Cu radi-ation) were also made on the terminal surface to verify the epitaxial nature of the deposit. After these steps

Jan 1, 1970

By R. B. Toombs

The national and international importance of Canada&apos;s minerals and metals producing industry is reported. The growth of the Canadian industry is traced from 1945, through the period of rapid development of the early 1950&apos;s, to the consolidation and expansion activities of the late 1950&apos;s and early 1960&apos;s. Mineral production in Canada during 1963-including steel, nonferrous metals, and fuels -is reported. It is estimated that by 1970 the Canadian industry will produce $3.9 billion worth of metals, nonmetals, and fuels.

Jan 8, 1964

PRESIDENT L. D. RICKETTS,1 NEW YORK, N. Y. PAST PRESIDENTS BENJAMIN B. THAYER,1 NEW YORK, N, Y. WILLIAM L. SAUNDERS,2 NEW YORK, N. Y. FIRST VICE-PRESIDENT SIDNEY J. JENNINGS,1 NEW YORK, N. Y. TREASURER GEORGE C. STONE,1 NEW YORK, N. Y. SECRETARY EMERITUS ROSSITER W.. RAYMOND NEW YORK, N. Y SECRETARY BRADLEY STOUGHTON NEW YORK, N. Y.

Jan 6, 1916

Jan 1, 1947

By V. W. Aubel

Among the iron-bearing ores of the world, the titaniferous iron sands of New Zealand are probably the least known to American engineers. This is not surprising in view of the fact that American ironmasters look with disfavor on any, even domestic, ores containing over 1 per cent. titanium. The possibilities of smelting titanium-bearing ores in the blast furnace are still undetermined, but the problem of their efficient reduction is becoming more important each year. There seems to be little inclination on the part of American furnace operators to tackle this problem, and they will no doubt continue to utilize the non-titanium ores at their command, leaving research and experiment to those countries not so fortunately endowed. New Zealand has, however, been intensely interested in her deposits of titanium-bearing iron sand, and during the last 50 years considerable English and New Zealand capital has been expended on this problem. The extent of the New Zealand iron-sand deposits is almost beyond measure. From Patea north to Manuka Heads, along almost the entire west coast of the North Island, these deposits exist. Wherever there is beach sand along this 300 mi. of coast line, the sand is iron bearing. It varies considerably in grade; but wherever the contour of the coast affords small bays and inlets, large dunes are found that are remarkably uniform in quality. Several of these large deposits, especially those at New Plymouth and Patea, are noted for their high iron content. The dune at New Plymouth runs between 55 and 60 per cent. of metallic iron; the panning action of the prevailing westerly winds and northwesterly currents has no doubt resulted in this concentration. Whatever the origin of this material may be, there is no doubt that deposition is going on continuously. At New Plymouth, a small artificial harbor, protected from the drifting sand by a large breakwall, has been dredged. Here sailing vessels have for years been loaded with iron sand for ballast by means of a crane and grab bucket operated from the wall of the breakwater. Thousands of tons of sand have been removed from this spot yet each succeeding storm renews the supply. The sand dune shown in Fig. 1 has been tested to a depth of 50 ft. (15 m.) without losing its

Jan 1, 1920

Jan 1, 1947