By Elmars Ence, Harold Margolin

The titanium-aluminum system has been investigated in the composition region 0 to 34 pct Al in the temperature range 800" to 1450°C. The phases encountered in this region were: a,ß, TiAl3, The reactions observed are as follows: 13 ; L - 6T. A1, 0 (15 pct Al) + 6 (18 pct Al) - yTi Al (16.5 pct Al) at -1170°C andP (7 pctpct Al) + y (9.2 pet Al) - ah(9 pct Al) at - 1060°C. A eutectoid reaction: y — a +d belm 700°C is postulated. THE Ti-A1 system has been the sub.ect of a number of investigations. Several of these1-3 have indicated extensive solubility of A1 in both a and ß titanium. Ence and Margolin, as a result of work on the Ti-A1-0 system:'5 have shown that the a solubility ofalumi-num is considerably restricted, and found that a compound, Ti2A1 existed in the region formerly designated as Q a This structure was identified as hexagonal with c/a = 0.803. Pietrokowsky confirmed the existence of this phase7 and pointed out that the structure was isomorphous with Ti3Sn.8 Although the existence of Ti,A1 has been confirmed by others,9-12 there has been considerable disagreement regarding the composition and mode of formation. A detailed reinvestigation of the Ti-A1 system has been published by Sagel et al.13 The tentative diagram indicated two phases, a, and e, occurring in the former all a region. The a, phase has the same structure as Ti2A1 and was indicated as having a broad region of solubility. Epsilon, a tetragonal phase, was shown to form within the a, solubility region. AS a result of unpublished work,14 Ence and Mugy3 olin disagreed with the interpretation of Sage1 et al., although some common features existed. The present study was conducted in an attempt to clarify prevailing uncertainties. EXPERIMENTAL PROCEDURE Alloy Preparation—Alloys were prepared from iodide titanium (99.9 pct Ti with less than 0.01 pct Zr) or Bureau of Mines electrolytic titanium (BHN-73) and high purity aluminum (99.99 pct). Alloys were arc-melted in argon or helium atmosphere as 15-g buttons in the composition range up to 34 pct Al. Depending on need, alloys were made in increments varying from 0.25 to 2 pct Al. Up to five 15-g buttons of some compositions were made. Weight losses during melting did not exceed about 1 pct of the charge and chemical analysis revealed that both titanium and aluminum were evaporated. In general, nominal and analyzed compositions agreed within 0.5 pct and therefore nominal compositions were used in plotting the data. Unavoidably, some overlap of composition occurred, particularly where small increments of A1 were used. The small increments were primarily used to obtain alloys which would fall into the narrow a -, r region and this purpose was achieved. In general, the data obtained from Bureau of Mines base titanium and iodide titanium alloys were in agreement. Forging—Both as-cast and forged samples were employed. Samples were heated for hand forging by an oxygen-hydrogen torch to the region 1200" to 1300°C. A titanium anvil and cover plate were used to prevent any iron pick-up and consequent formation of a low melting point compound. Frequent reheating kept the temperature in the desired range. Under these conditions, alloys containing up to 15.5 pct could be successfully forged. To check on the depth of contamination, forged alloys were heated slightlybelow the ß transformation temperature. Metal was removed to a depth below the contaminated surface so revealed, and the subsequent results obtained from these samples agreed closely with those secured from as-cast material. Heat Treatment—Prior to heat treatment, all alloys were vacuum annealed to remove hydrogen. Samples

Jan 1, 1962

By A. M. Turkalo

IT is a well-known fact that martensitic steels show a greater resistance to brittle fracture than do pearlitic and bainitic steels. It was, therefore, thought worthwhile to investigate the mode of brittle fracture with respect to structure by studying the effect of various austenite decomposition products on the propagation of brittle fracture in steel by means of electron microscopy. Newly developed replication techniques together with the advantages of the electron microscope such as great depth of field, available high magnification and easy adaptation to stereophotography make electron microscopy very suitable for fracture studies. EXPERIMENTAL PROCEDURE An essentially plain carbon steel containing 0.56 pct C, 1.30 pct Mn, 0.02 pct P, 0.03 pct S and 0.22 pct Si was used in this investigation. The following table gives the heat treatments used to obtain the various austenite decomposition products: The resulting austenite grain size from the 870°C austenitization treatment was about an ASTM No. 7 grain size. The specimens which were 2 in. long, 1/4-in. diam bars were austenitized in a tube furnace through which argon gas was blown. The tube was not, however, air-free and the specimens were not completely oxide-free. Isothermal treatments were done in a lead bath. With the exception of the fully hardened specimen and the one as-isothermally transformed at 300°C the heat treated specimens were notched in the following fashion with a jeweler's saw. A cut about 0.08 in. deep was made perpendicular to the length of the bar. The specimen then was rotated about 45 deg and another cut about 0.08 in. deep was made. In the case of the hard martensitic and bainitic specimens, only one cut was made and the depth was not controlled. The design of the two-cut notch caused fracture to initiate at the point of intersection of the two saw cuts. The specimens were broken at -196°C in a Charpy impact testing machine. In order to hold the specimens securely in the impact machine two square pieces of mild steel were made about 5/8 in. long having the same cross section as that of a standard Charpy specimen but containing a hole 1/4 in. diam through the center of the cross-section. These adapters were slipped over the ends of the test specimen which was then secured tightly by means of set screws in the adapters. The specimen with the adapters was cooled to -196°C in liquid N,, then placed in the impact machine and broken within 3 sec. One half of the broken specimen was used for the electron microscope study of the actual fracture surface. The other half was nickel-plated and a cross section through the notch and fracture was polished for electron microscope examination. Carbon replicas of the fracture specimens for the electron microscope study were made essentially according to Bradley's evaporation technique.' Both direct carbon and two-stage carbon replication techniques were used. In the case of the direct carbon technique, a thin layer of carbon was evaporated first at an angle of about 45 deg to the mean fracture surface and then another film of carbon was evaporated normally to the fracture surface. The carbon replica was freed electrolytically.2 The specimen was made an anode in a 10 pct Nital polishing solution. It was etched intermittently by shutting off the power now and then. The freed replica was washed in 40 to 50 pct water solution of nitric acid for 10 min or so, then washed in water and picked up on a screen for examination. The two-stage carbon replication technique involved first making a primary replica of cellulose * acetate from which a carbon replica was then made. One side of a strip of cellulose acetate wet with acetone was pressed lightly against the surface of the specimen, allowed to dry and then stripped. Prior to the deposition of carbon, which was done at 90 deg to the cellulose acetate replica surface, chromium was evaporated at 45 deg. After the carbon evaporation the cellulose acetate was dissolved in acetone according to the Jaffe method3 leaving the carbon replica preshadowed with chromium for examination.

Jan 1, 1961

By M. E. True, B. L. Stone

To cope with the problems encountered when drilling at greater depths and to reduce the amount of physical effort required on the part of drilling crews in making round trips, a new type of semiautomatic power-operated drilling machinery has been developed which permits round trips to be made without the drill pipe being touched by hand. This equipment consists of hy-draulically operated tongs which perform the stabbing, spinning, and tong-ing operations, and two power-operated racking units mounted in the derrick for carrying the pipe to and from the center of the hole and positioning it on the mat and in the rack. With this equipment all of the operations of the various units are controlled remotely by manipulation of hydraulic valve levers and electric switches. INTRODUCTION As horsepower rises to meet the demand for deeper drilling, it is necessary to increase the weight of surface drilling equipment. Also, the duration of repetitive operations in making round trips to change bits is greatly increased with depth. Harder formations encountered at greater depths reduce bit life rapidly, resulting in more frequent round trips and in some instances more time is consumed in changing bits than in drilling. Since the introduction of the first rotary employed to drill for oil in 18951, there has been relatively little change in the general procedure for making up, breaking out, stabbing, and racking drill pipe in making round trips to change bits. The conventional method of making round trips with the drill pipe requires that drilling crews lend strenuous physical assistance to manually operated tools. Although many new devices have been developed to improve efficiency, increase speed of making round trips, improve safety, and reduce the amount of physical effort required in handling drill pipe, it is considered a vital necessity to substitute automatic or semiautomatic power-operated machinery for many of our more or less manual operations if extremely deep drilling is to be carried out successfully on a production basis in the same manner as our shallower drilling of today. Field tests have been made of remotely controlled power-operated tongs, spinner, stabber, and racking equipment. The tongs, which include a built-in pipe spinner, are mounted on a column, are capable of gripping and supporting the weight of a 90-foot stand of drill pipe, and are provided with means for moving the pipe vertically as well as to and from the center of the hole. The racking equipment consists of two units, one at the level of the conventional monkey board and the other at the first girth on the ladder side of the derrick. Most of the physical effort of making round trips with drill pipe has been eliminated in that all of the operations of tonging, spinning, stabbing, and racking of pipe on the floor are controlled by an operator in a seated position by manipulation of hydraulic and electric valve levers and buttons. The driller is relieved of operating the cathead, leaving only the hoisting and slips to be controlled. Complete round trips are made without the drill pipe being touched by the drilling crews. Although the speed of pulling or running a single stand with the power-operated equipment is approximately the same as that with conventional equipment, it is possible to maintain this rate for long periods, whereas fatigue slows crews working conventionally during round trips, especially under adverse weather. After completing round trips with this equipment, drilling crews are not exhausted, consequently, are able to perform effectively their duties while drilling, which is essential for maximum over-all efficiency. Safety is substantially improved as the derrickman performs his duties from a platform enclosed by rails and the tong lines and spinning chain are eliminated from the derrick floor. The hazards encountered in racking drill pipe on the floor and in stabbing are also eliminated. Figure 1 shows a drawing of a derrick equipped with the power-operated drill'pipe handling equipment.

Jan 1, 1949

By M. E. True, B. L. Stone

To cope with the problems encountered when drilling at greater depths and to reduce the amount of physical effort required on the part of drilling crews in making round trips, a new type of semiautomatic power-operated drilling machinery has been developed which permits round trips to be made without the drill pipe being touched by hand. This equipment consists of hy-draulically operated tongs which perform the stabbing, spinning, and tong-ing operations, and two power-operated racking units mounted in the derrick for carrying the pipe to and from the center of the hole and positioning it on the mat and in the rack. With this equipment all of the operations of the various units are controlled remotely by manipulation of hydraulic valve levers and electric switches. INTRODUCTION As horsepower rises to meet the demand for deeper drilling, it is necessary to increase the weight of surface drilling equipment. Also, the duration of repetitive operations in making round trips to change bits is greatly increased with depth. Harder formations encountered at greater depths reduce bit life rapidly, resulting in more frequent round trips and in some instances more time is consumed in changing bits than in drilling. Since the introduction of the first rotary employed to drill for oil in 18951, there has been relatively little change in the general procedure for making up, breaking out, stabbing, and racking drill pipe in making round trips to change bits. The conventional method of making round trips with the drill pipe requires that drilling crews lend strenuous physical assistance to manually operated tools. Although many new devices have been developed to improve efficiency, increase speed of making round trips, improve safety, and reduce the amount of physical effort required in handling drill pipe, it is considered a vital necessity to substitute automatic or semiautomatic power-operated machinery for many of our more or less manual operations if extremely deep drilling is to be carried out successfully on a production basis in the same manner as our shallower drilling of today. Field tests have been made of remotely controlled power-operated tongs, spinner, stabber, and racking equipment. The tongs, which include a built-in pipe spinner, are mounted on a column, are capable of gripping and supporting the weight of a 90-foot stand of drill pipe, and are provided with means for moving the pipe vertically as well as to and from the center of the hole. The racking equipment consists of two units, one at the level of the conventional monkey board and the other at the first girth on the ladder side of the derrick. Most of the physical effort of making round trips with drill pipe has been eliminated in that all of the operations of tonging, spinning, stabbing, and racking of pipe on the floor are controlled by an operator in a seated position by manipulation of hydraulic and electric valve levers and buttons. The driller is relieved of operating the cathead, leaving only the hoisting and slips to be controlled. Complete round trips are made without the drill pipe being touched by the drilling crews. Although the speed of pulling or running a single stand with the power-operated equipment is approximately the same as that with conventional equipment, it is possible to maintain this rate for long periods, whereas fatigue slows crews working conventionally during round trips, especially under adverse weather. After completing round trips with this equipment, drilling crews are not exhausted, consequently, are able to perform effectively their duties while drilling, which is essential for maximum over-all efficiency. Safety is substantially improved as the derrickman performs his duties from a platform enclosed by rails and the tong lines and spinning chain are eliminated from the derrick floor. The hazards encountered in racking drill pipe on the floor and in stabbing are also eliminated. Figure 1 shows a drawing of a derrick equipped with the power-operated drill'pipe handling equipment.

Jan 1, 1949

By H. W. Graham

THE young metallurgist of today who thinks casually of the technical literature of the steel industry might conclude that little has been published concerning the Bessemer process. This conclusion is true as relating to the last decade or two, but there is a fairly voluminous Bessemer literature in the period of 1860 to 1910, Since that time, however, an entirely new level of metal-lurgical knowledge of steelmaking has been reached; and the present paper is simply an effort to look broadly from this new level and to bring the recorded history of the process up to date, It is an effort to appraise the acid Bessemer method of steelmaking in the light of today's technical knowledge thereof. In this paper matters of history will be dealt with only insofar as they contribute to an understanding of today's situation. Attention will be directed to the apparent causes of past developments in seeking to perceive the true direction of trends now in existence and effective as bearing upon future developments. The paper will discuss the economics of the Bessemer process, but only to the extent that will bear upon the metallurgist's understanding of his respon-sibility. The problem of the quality of Bes-semer steel will be reviewed and examples will be given of the technical data upon which the reasoning of the paper is based, Matters of engineering design, mechanical maintenance, operation and metallurgical investigation will be surveyed. Compari-sons will be made between the Bessemer and open-hearth processes for the sake of clear and ready understanding,

Jan 1, 1940

THOSE MARKED THUS * ARE MEMBERS, MARKED THUS ?ARE ASSOCIATES. THESE SIGNS DOUBLED INDICATE LIFE MEMBERS AND ASSOCIATES RESPECTIVELY. THE FIGURES AT THE END OF THE ADDRESS INDICATE THE YEAR OF ELECTION. HEAVY-FACED TYPE SIGNIFIES HONORARY MEMBERSHIP. *AARONS, J. BOYD, Vivian Gold Mining Co., Ltd., Harris, West. Australia. '05 *ABADIE, EMILE R., Cons. and Min. Engr., 214 Union Savings Bank Bldg., Oakland, Cal. '76 ?ABBÉ, MAX F., Prest., Abbé Engineering Co, 220 Broadway, New York, N.Y. '07 ? ABBÉ, PAULO., Secy.,Abbé Engineering Co., 220 Broadway, New York, N.Y. '07 *ABBOTT, AI ARTHUR Morococlia, Peru, So. America. '95 *ABBOTT, CLARENCE Chief EDgr., Iron Mines, Dic Tennessee Caol, Iron & R. R. Co., Bessemer, Ala. '04 *ABBOTT, JAMES W., Min. Engr: Ploche, Lincoln Co., Nev. '94 *ABE, MASAYOSHI, Prof. of Mining, Imperial University Kyoto, Japan. '05 ? ACKER, E. O'C., Supt., Treatment Dept., Bethlehem Steel Co., So. Bethlehem, Pa. '86

Jan 1, 1910

By AIME AIME

THE quarters provided for the session on Milling Methods, Monday afternoon, Feb. 17, were filled to capacity. Galen H. Clevenger presided and notables, such as A. W. Fahrenwald, A. O. Gates, F. A. Thomson, W. L. Zeigler and others who had not graced a milling meeting in New York in recent years, or per- haps even never before, were actually present and spoke "in person." The first paper, by A. W. Fahrellwald (T. P. 275), entitled "Classifier Efficiency ; An experimental Study," was summarized by the author, who clearly showed the inconsistency of determining the efficiency of a classifier by means of sizing tests, especially where the material classified consists of a mixture of minerals of different specific gravities. In place of sieve analysis the procedure recommended involves the use of a glass settling-tube which is considered to give ideal classification and thus serve as a standard against which mill classification will be compared and relative efficiency calculated. This procedure sounds logical. Perhaps the greatest difficulty may lie in securing an ideal classifier acceptable to every one.

Jan 1, 1930

By T. Katayanagi, J. Shimoiizaka, K. Nakatsuka

Feldspar has been separated from silica by cationic collector using hydrofluoric acid as an activator of feldspar (1,2). Recently, one of the authors developed a new flotation process separating feldspar from quartz without using hydrofluoric acid. Presently, some silica sand mills are operating to introduce this process in Japan (3). In this flotation, feldspar is floated from silica using normal alkyltri-methylene diamine acetate together with sodium petroleum sulfonate as collectors in a hydrochloric or sulfuric acid circuit of about pH 2. From fundamental studies, it was found that, though the aliphatic diamine by itself did not adsorb on feldspar sufficiently to give a satisfying flotation in acidic circuit., the adsorption of collector was promoted by the simultaneous use of petroleum sulfonate and resulted in sufficient flotation of feldspar. On the other hand, quartz did not float in this flotation process. The application of this flotation was attempted for some types of natural samples and satisfying results were obtained. Further, an example of practical plant was introduced and the advantages in the process are emphasized.

Jan 1, 1976

By G. D. Rieck, G. H. G. Vaessen, D. L. Vogel

Both doped and undoped tungsten single crystals exhibit hardness anisotropy with respect to the direction of testing in each of the crystallographic phes investigated. The hardness anisotropy of undoped single-crystal tungsten is rather pronounced in (001) and (110) planes but very minor in (111) planes. The anisotropy in (122) planes of the doped and drawn tungsten after recrystallization is in accordance with a previously published concept of a stringlike distribution of the doping material in the metal. ANISOTROPY in mechanical properties of single-crystal tungsten was investigated by Rose et al., Garlick and Probst,2 and Beardmore and Hull. 3 Although data on the Vickers microhardness of tungsten have been published (see, e.g., Boosz 4 and the references cited by him), no data on the microhardness anisotropy are available. We report, therefore, some of our own results on the microhardness and its anisotropy. The microhardness has been determined of the following samples. A) Polycrystalline tungsten samples taken from: 1) powder metallurgical tungsten "normally" doped with potassium-silicon-aluminum oxides (final contents inppm: K, 100; Si, 100; Al, 20; Cr, 20; Fe, 50; Mo, 400; Ni, 10) and in the form of: a) a 10-mm-diam swaged ingot annealed at 1600°C, the grain sizes varying between 15 and 250 p; b) a sheet rolled at about 800°C and recrystallized at 2000°C7 the grain sizes varying between 15 and 150 p; c) a 2-mm-diam swaged rod, as-worked, with elongated grains (average diameter of about 25 , lengths up to 1 mm); 2) undoped electron-beam-melted tungsten with very large grains (contaminations in ppm: K < 10; Fe < 20; Cr < 10; Cu < 0.1; Ni not detectable; inter-stitial~ not determined). B) Single-crystal samples taken from: 1) pure tungsten grown on a Pintsch wire by the van Arkel procedure (main contaminations inppm: Mo, 100; Si < 10; Cu and Fe, 2; A1 < 2; interstitials not determined); 2) zone-melted undoped tungsten (analysis as under A2); 3) large crystals in secondary recrystallized tungsten

Jan 1, 1969

By D. Brion, J. J. Prédali, J. Hayer

The need to grind volcanic-sedimentary ores very finely (d80 < 20 µm) so as to liberate Pb, Zn, and Cu sulfides from their pyritic gangue causes difficulties in selective flotation. The pyrite, which accounts for 70-80% of the mineral content, is insufficiently depressed by the usual pH and NaCN techniques. To determine better depressing methods, the surface evolution of pyrite during flotation was followed by ESCA spectroscopy to compare the stability range in the Eh-pH diagram. Surface iron hydroxide was formed, which is the main pyrite-depressing factor. NaCN appears to play a more restrictive part, since no ferricyanides were detected, except for very small amounts at pH 7.

Jan 1, 1980

By Stuart Croasdale

NOT long ago I was called upon to conduct some experiments on the treatment of ores from the New Cornelia copper mine, Ajo mountains, Arizona, for the Calumet & Arizona Copper Co. The problem was a very interesting one and contained some unusual features. Incidental with this problem was the utilization of a large amount of low-grade pyrite in the Bisbee mines of the company, provided this could be accomplished by any feasible method. The New Cornelia mine is situated 45 miles south of Gila Bend, the nearest railroad point, on the Southern Pacific Railroad. It is about 160 miles, almost due west, from Tucson. This section is one of the most arid in the United States. The normal annual precipitation, as given by the United States Weather Bureau covering a period from 1870 to 1901, is 3 to 5 in. During June and July, 1913, the records kept by the company gave the following results. These are all I have available, but they show the enormous evaporation that can be expected, which may be a factor in leaching operations on a large scale.

Jan 8, 1914

By L. L. McDaniel

DURING the past few years a number of improvements in smelting and power equipment have been made at the Douglas smelter of the FIG. 1.-GENERAL PLAN OF SMELTER. Phelps Dodge Corporation at Douglas, Ariz. In the summer of 1935 work was started on the first unit of a new reverberatory waste-heat boiler plant which ultimately was to furnish steam for a modern high-pressure power plant. A second reverberatory waste-heat boiler unit

Jan 1, 1939

By Thomas E. Howard

Tunneling is at the threshold of a new era. An exciting new technology is becoming available. And, supplying the increasing quantities of minerals required by a growing and socially advancing world population, together with providing the subsurface facilities attendant to the rapid urbanization of the more developed countries of the world, will require underground excavation during the next decades on a scale that would have seemed fantastic a few years ago. It is estimated that world mineral consumption will increase fivefold by the year 2000. Projections for the United States indicate that domestic consumption of nonfuel minerals may increase two to three times by the end of the century. Meeting these requirements will entail opening up many new underground mines, even if present trends toward surface mining continue. And, at least in the United States, new factors that are becoming increasingly important may modify these trends. We are depleting our shallow easy- to-find and easy-to-mine mineral deposits; and, if we are to avoid becoming dangerously dependent on imports, we must turn more and more toward deeper deposits that are not amenable to surface mining. Growing public concern with environmental quality is apparently leading toward increasingly stringent regulation of surface mining which also will tend to make underground mining economically more attractive. The world market for underground construction is also growing rapidly. The most conservative projections indicate that in the United States alone more than $7.0 billion will be spent on excavation for underground facilities during the next ten years. And these estimates do not include any of the bold, imaginative new applications for underground excavation that have been proposed, such as extensive underground power transmission, the Chicago Deep Tunnel plan, and the Northeast Corridor Transportation project. There can be little doubt then that the market for tunnels for conventional applications is increasing rapidly and that the trend will continue. It

Jan 1, 1970

By Theodore Holt

Outline of the Process THE Mines Operating Co.&apos;s plant at Park City, Utah, was designed to treat the low-grade fillings in the old stopes of the Ontario mine. These fillings carry 6 to 14 oz. of silver, 1 to 2 lb. copper, 0.01 to 0.015 oz. of gold, and a small percentage of lead and zinc. The treatment consists in mixing the crushed ore with coal dust and salt and then roasting in a new type of furnace y combustion of the contained fuel. The roasted ore is leached with an acid salt solution to dissolve the silver, gold, copper, and lead. At present these metals are precipitated together on scrap iron and the product sold to a refinery. The only new feature of importance in this scheme of treatment is the roasting process, which makes possible the chloridizing of ores without any loss of the valuable metals, and at a very low cost. History of the Development of the Process The roasting process had its beginning in connection with research work at the Utah State School of Mines. N. C. Christensen, Jr., who held one of the School of Mines&apos; fellowships, was engaged in some experimental work on blast roasting. At the same time I was doing some work on the insoluble gold in Mercur base ores. Mr. Christensen roasted some of this base gold ore in his pot furnace, and found that when he mixed a sufficiently low percentage of fuel with the ore, it did not sinter but roasted to a leachable product. We considered this a new application of blast roasting, and proceeded to test out a large number of ores in several different types of small roasters which we constructed. This experimental work continued well into the summer of 1911.

Jan 7, 1914

By P. A. Beck

ACCORDING to a recent hypothesis of Sully,&apos; xY. binary CT phases are characterized by 1.7 bonding 3d electrons per atom, which completely fill the first Brillouin zone. This hypothesis appears to imply that there are no empty 3d orbitals in the u phase, and that, correspondingly, this phase must be dia-magnetic, or at most weakly paramagnetic. On the other hand, Bowen and Hoar&apos; reported that a u phase extracted electrolytically from an alloy steel became ferromagnetic when cooled to about —113°C. In view of the fundamental interest of the problem from the point of view of the electron structure of the u phase, it seemed worthwhile to study the magnetic properties of massive u phase specimens of various known compositions. Sigma specimens of the following compositions were tested: 1—40 atomic pct Fe, 40 atomic pct Cr, and 20 atomic pct Mo 2—35 atomic pct Fe, 35 atomic pct Cr, and 30 atomic pct Mo 3—48.7 atomic pct Fe, 50.2 atomic pct Cr, and 1.1 atomic pct W 4—40.7 atomic pct Co and 59.3 atomic pct Cr All specimens were found to be strongly paramagnetic at room temperature, particularly alloy No. 1. At liquid nitrogen temperature, alloy No. 1 be- came ferromagnetic; the other u alloys remained paramagnetic. Even though apparently not all u alloys become ferromagnetic at liquid nitrogen temperature, in view of their strong paramagnetism it is probable that the electron structure proposed by Sully is not correct. Similar qualitative studies were made with the p, P, and 8 phases." A p phase specimen of 57.2 atomic pct Co and 42.8 atomic pct Mo; a P specimen of 19.9 atomic pct Cr, 37.8 atomic pct Ni, and 42.3 atomic pct Mo; and a 8 specimen of 50.4 atomic pct Ni and 49.6 atomic pct Mo were tested at room temperature, and all were found to be paramagnetic, although considerably weaker than the u phase specimens described above. A test at liquid nitrogen temperature gave similar results for all specimens; none became ferromagnetic. Thanks are due to D. K. Das for preparing several of the alloys and to Pol Duwez of California Institute of Technology for kindly loaning four specimens of cr alloys. References 1 A. H. Sully: The Sigma Phase in Binary Alloys of the Transition Elements. Journal Inst. Metals (1951) 80, p. 173. - K. W. J. Bowen and T. P. Hoar: Low Temperature Ferromagnetism of Sigma Phase in an Alloy Steel. Research (1950) 3, p. 484. 3 S. Rideout, W. D. Manly, E. L. Kamen, B. S. Lement, and P. A. Beck: Intermediate Phases in Ternary Alloy Systems of Transition Elements. Trans. AIME (1951) 191, p. 872; Journal of Metals (October 1951).

Jan 1, 1953

By A. Yoshikawa, T. Sugeno

To detenmine the origin of the sharp fatigue limit in many ferrous metals, S-N curvces were determined in push-pull fatigue at 18.6 kc per sec at room temperature and - 67°C for various kinds of iron. These differed in carbon and nitrogen content and grain size (25 and 2500 grains per sq mm). Sharp knees appeared in the S-N curves of fine-grained specimens with high interstitial content at both temperatures. In coarse-gruined specimens, knees were not sharp .regardless of the interstitial content and the testing temperature. It is concluded from these results that the controlling factov for the appeavance of the sharp fatigue limit is not strain aging but grain size. It has already been mentioned that iron and some iron alloys show fatigue curves characterized by a more or less sharp knee and a fatigue limit.&apos; Explanations of the origin of this characteristic behavior of fatigue in iron appear to fall into two broad classes. One is concerned with interstitial impurities through the aging or locking effect and the other is based on intrinsic plastic properties of iron. Levy and sinclair2 and Lipsit and Horne3 have suggested that the fatigue limit observed generally in iron and steel is due to interstitial solute aging during the course of fatigue. On the other hand, Thompson and wadsworthl have suggested that the fatigue limit may be analogous to the sharp yield point, in the sense that alternating stresses above the fatigue limit are necessary to break down the dislocation locking. However, there are some experimental results which cast doubt on the general validity of these suppositions.4-8 Ferro and Montalenti&apos; have recently suggested that the typical form of the fatigue curve of iron seems to come from an intrinsic plastic characteristic of the iron structure. This suggestion is based on the experimental result that pure iron containing an insufficient amount of interstitial solute to alldw appreciable strain-aging effects still showed a fatigue limit at room temperature. Although systematic investigations on the effect of grain size are scarce, it is thought that this effect is important in relation to the sharp fatigue limit. In fact, sensible differences were observed by Oates and Wilson4 in fatigue behaviors of a low-carbon steel depending on grain size. Ideally, the fatigue limit will be defined as the upper limit of stress amplitudes at which the life is infinite. This ideal fatigue limit can never be determined because of the limited time available for experiments, and moreover scattered data points often leave the construction of S-N curves somewhat arbitrary. And, it is usually stated that a material has a fatigue limit when its statistical S-N curve becomes apparently parallel to the N axis with a more or less sharp knee. The meaning of the fatigue limit and the sharp knee will be discussed in detail in relation to the construction of S-N curves. The origin of this sharp knee was investigated by determining S-N curves of iron for various interstitial contents, testing temperatures, and grain sizes. EXPERTMENTAL PROCEDURE The material as received was a commercial-grade low-carbon steel in the form of 4-mm-diameter rods with the following composition in weight percent: C, 0.09; Si, 0.017; Mn, 0.43; P, 0.006; S, 0.012; Cu, 0.11. Five different groups of specimens were tested. The grain sizes and interstitial contents in each group are given in Table I. The specimens of group C-02 were decarburized by annealing for 100 hr at 700°C, followed by an additional 100 hr at 850°C in wet hydrogen. Specimens of groups N-2 and N-9 nitrided in a mixed atmosphere of ammonia and hydrogen after an initial treatment identical to group C-02. The specimens of group C-9 were prepared in a manner similar to those of group C-02, except heat treatment was carried out in a vacuum. After polishing their surface with emery paper, the specimens of all groups were given a final anneal for 30 min at 930°C and air-cooled in an evacuated quartz tube. For group C*-9 this

Jan 1, 1965

By Gregory L. Gullord

In September, 1975, production was begun at the new milling facility of ASARCO Incorporated, the Young Mill. The mill is located adjacent to the Young Mine 35 km (22 miles) east of Knoxville, Tennessee. The Young Mill replaced the obsolete Mascot Mill which had been operating since 1913. The basic flow sheet of Mascot was retained for the construction of the Young Mill, with a 20% increase in capacity included in the design. The Young Mill is capable of processing 7710 - t/d (8500 stpd) of crude ore from three underground mines (Young, Immel and Coy) yielding 300 - t/d (330 stpd) of 63% zinc concentrate. The Young Mill is unique in that 92.5% of the ore milled is recovered as saleable products, including zinc concentrate, construction aggregate, sand and agricultural limestone. Processing at the Young Mill is divided into five basic stages: two-stage crushing, heavy media separation, grinding-flotation, concentrate filtering and drying, and limestone by-products recovery. The ore bodies are located in the Knox formation, which consists of primary dolomite, secondary dolomite and limestone with silicas in the form of chert and jasperoid. The zinc mineralization occurs as an exceptionally pure sphalerite. The ore contains an occasional abundance of pyrite and traces of fluorite and barite. TWO STAGE CRUSHING Ore enters the crushing section from two points. The Young Mine ore is hoisted into a 816 ton (900 st) bin which feeds a 1.52m (60 in) conveyor via a 1.52 m (60 in) vibrating feeder. The Immel ore is trucked 10 km (6 miles) by an independent contractor and weighed on automatic recording truck scales at the entrance to the property.

Jan 1, 1977

By J. B. Wagner, B. Swaroop

The atomic ratios of oxygen to iron in zlarious corn-posilions of wustite in the vicinity oj the reported p to n transformation were determined in the temperalure range between 950" and 1250°C. For these conditions, equilibrium vacancy concenrations have also been determined at vatious mixtures of C0,-CO. The data show a continuos introduction of iron vacancies as oxygen is introduced into wuistite. No phase change is observed with in the wuustite field. However, the value of n in the isothermal oxygen pressure dependence, the weight change shifts to 1ower values as the concentration of oxygen increases. WUSTITE is a metal deficit semiconductor with the majority lattice disorder being cation vacancies. Using the notation similar to that of Kroger and ink,&apos; the dissolution of oxygen into wiistite using C02-CO mixtures is represented by, WHere v+! denotes a cation vacancy with k effective negative charges and kh • denotes k electron holes, h -. Applying the law of mass action and assuming a dilute solution of defects in the wiistite yields Where the square brackets denote concentrations. Furthermore, when k = 2 the cation vacancies are completely ionized, and both the concentration of cation vacancies and the concentration of electron holes are proportional to the third root of the ratio, PC /PCo. This analysis is valid for one particular mael based on an ideal solution at elevated temperatures (in this case t > 1000°C). At lower temperatures, it has been shown2 that the pressure dependence of the electronic conductivity changes in a manner which suggests that vacancies interact with or "trap" electron holes. At the very high concentrations of defects, 10&apos;&apos; to 10" per cu cm, these simple models no longer hold. Recently Tannhauser,3 Geiger et a1.&apos; Bransky and Tannhauser; and Hillegas&apos; have found an apparent p to n transformation in wiistite in the temperature range of 950" to 1300°C. This junction was found by thermoelectric and electronic conductivity measurements. Geiger eta1.&apos; found that the electronic conductivity became almost independent of the oxygen pressure at high temperatures and oxygen concentrations within the experimental error. In addition, Vallet, Raccah, and coworkers6&apos;7 have reported the existence of several "varieties" of wiistite which were reported to exist within what was heretofor presumed to be a

Jan 1, 1968

By L. Zwell, H. A. Wriedt

In describing their procedure for measuring the lattice parameters of solid solutions, Abrahamson and Lopata report (p. 77) the final heat treatment of their alloy specimens as "700°C for 100 hr, followed by a furnace cool". The isothermal part of this treatment may be expected to precipitate solute in excess of the stable a solid-solution limit at 700°C; the subsequent slow cooling is likely to reduce the dissolved solute still further. Fig. 1 (upper) presents the data for titanium alloys so he;rt-treated and shows the lattice parameters of solid solutions containing up to 3.5 at. pct Ti; Fig. 17 (lower) shows 2 at. pct Ti as the solubility limit in a iron at 700°C. Figs. 1 and 17 are thus incompatible. The paper contains comparable incon~patibilities for zirconium alloys, for niobium alloys, and for tantalum alloys. The final heat treatment at 700°C may also be responsible for the anomalous "knee" in the lattice-parameter data for nickel alloys, Fig. 3. The "knee" composition is located near the 700°C limit of the stable a solid-solution field;37 alloys of the experimental composition range with more nickel than the "knee" composition are two-phase at 700 C and prolonged heat treatment of them at 700°C would tend to produce inhomogeneity rather than homogeneity. In Figs. 4 and 7, the composition ranges of the zirconium, hafnium, and niobium alloys examined terminate at alloy concentrations of 0.1 to 0.2 at. pct. These metals form very stable oxides and their partial removal from solid solution in iron by impurity oxygen may be expected. We believe that the authors should have reported the procedure by which they distinguished the amounts of alloying elements in solution and in oxide. The diagrams pertaining to copper in Figs. 3 and 18 (lower) are almost certainly incorrect. Three recent investigations of this system38-40 all substantially agree on the solubility of copper in a iron, finding it to be much larger than that reported by Abrahamson and Lopata. The change of the lattice parameter with composition reported by Abrahamson and Lopata is too large by a factor of three to five, as seen by comparison with the findings of other investigators.41738 Moreover, the authors violate, in Fig. 18, the accepted Fe-Cu constitution diagram37 by ignoring the eutectoid at about 850°C.

Jan 1, 1967

By H. B. Pulsifer

ABOUT 15 varieties, or modifications, of the best magnesium available were prepared and subjected to etching tests, then examined for microstructure. Of the 30-odd etching reagents that were tried, nearly half, mostly ammonium salts, etched the metal satisfactorily. The surfacing and etching of magnesium is shown to be a very simple and quick operation. The density and hardness of magnesium were determined. The most interesting new observations relate to the finding of the hexagonal etch figures, the crystal laminations, and the fact that the metal is plastic, cold, when restrained or quickly deformed. Under slowly applied pressure cold metal deforms slightly, then shears to fracture without plastic flow. The chief structural features of magnesium are presented in two reduced photographs and 30 photomicrographs. MATERIALS TESTED There are only two sources in the United States from which new metal can be procured: the American Magnesium Corpn. and the Dow Chemical Co. No pronounced structural or property differences in the metals from these two companies were disclosed by the work of this investigation. The following materials were obtained from the manufacturers: 1. Massive crystals of distilled metal (American Magnesium Corpn.). 2. Rods of hot-extruded metal, ½ -in. squares and 5/8-in. rounds (American Magnesium Corpn.). 3. Sheet magnesium, 0.005-in. thick (American Magnesium Corpn.). 4. Cast stick metal, 1 3/8-in. dia. (Dow Chemical Co.). 5. Magnesium-aluminum alloy, hot-rolled plate, ½ in. thick (American Magnesium Corpn.). From these materials, were prepared: 6. Sections from a furnace-cooled ingot made from distilled crystal. 7. Cold-strained pieces from (6), (4) and (2). 8. Pieces cold-squeezed to fracture from (6), (4) and (2). 9. Hammer-struck pieces from (6), (4) and (2). 10. Steam-hammer struck pieces from (6), (4) and (2). 11. Sections from furnace-cooled ingot of the magnesium-aluminum alloy.

Jan 1, 1928