NEW MEMBERS The following list comprises the names of those persons who became members during the period of June 10, 1917, to July 10, 1917. BANKS, LEON MAXWELL Agent 3. Supt., Grant Leasing Co. Metcalf Ariz. BEAUCHAMP, HENRY CLAY : Mine Operator, Sisson, Siskiyou Co., Cal. BOCKING, CHARLES, Asst. Mgr., Butte & Superior ,Mining Co., Rialto Bldg., Butte, Mont. BEYER, HERMAN E., Chief Engr., Condenser Dept., Ingersoll-Rand Co., 11 Broadway, New York, N. Y. BLACK, HERBERT F 1512 Oliver Bldg., Pittsburgh, Pa. BRENNAN, PATRICK J., Gen'l. Supt., Elkhorn Division, Consolidation Coal Co., Jenkins, Ky. BUTNER, DANIEL W., Chem. & Supt., Underground Min., Spanish American Iron Co., Daiquiri, Santiago de Cuba, Cuba. CARLTON, DAVE P Nevada-Douglas Cons. Copper Co., Ludwig, Nev. DE AROZENA, JOE Min. Engr., 321 Preusser St., San Angelo, Texas. DICKIE, CHARLES HERBERT, Pres., Georgia River Min. Co., Duncan, Vancouver Island, B. C., Canada. DOBBINS, WALTER Mill Foreman, Chino Copper Co., Hurley, New Mexico. DRURY, CHARLES W., Asst. Professor of Met., Queen's University, Kingston Out. Canada.

Jan 8, 1917

By Frank F. Poland

TEE purpose of this paper-is to describe a new process for the refining of secondary copper-base metals and a specially designed high-temperature electric-resistor furnace used in the process for the distillation of zinc from these metals. The process was used for the conversion of nickel silver to cupronickel and to recover the zinc content in metallic form. It also proved applicable and economical for the treatment of scrap brass for separating and reclaiming the copper and zinc. The relatively large furnace developed for the distillation of zinc is described in detail, for it made economically possible the direct recovery of metallic zinc from scrap brass, which is a new step in the processing of such material. Considerable interest has been shown in the utilization of the distillation furnace for other metallurgical processes, where it is of advantage to operate in a controlled neutral or reducing atmosphere, or to avoid having the processed metal in contact with refractories other than carbon, or to operate at temperatures between 3000 and 4000°F. PURPOSE OF DEVELOPMENT It was recognized early in the war effort that nickel would become a critical metal, therefore all nickel stock and alloys containing relatively high percentages of nickel were frozen immediately. Among these alloys were considerable quantities of various grades of nickel silver, an alloy containing copper, nickel, zinc, and in some grades lead, also minor amounts of iron, manganese and other constituents. At the time there was no existing plant or process to eliminate the zinc, lead, and minor constituents so as to convert this metal to cupronickel, one of the important alloys needed by the U. S. Navy for condenser parts. Therefore the Bureau of Industrial Conservation of the War Production Board requested the executives of the leading nonferrous metal companies to have their metallurgical staffs study the problem of converting this metal to cupronickel conforming to U. S. Navy Specification 44T40. The composition specified therein is as follows: nickel, 29 to 32 per cent; zinc, 1.00; iron, 0.00 to 0.60; lead, 0.05; tin, 1.20; manganese, 0.00 to 1.00; total of other elements (maximum), 0.50; copper, remainder. The problem in converting these alloys to cupronickel was the elimination of zinc, lead, iron, manganese, and other elements without appreciable loss of nickel to slags or other by-products. Revere Copper and Brass Incorporated, through its Research and Development Department, undertook to solve this problem. A Government-owned plant was built at Rome, N. Y., and there the con- version was successfully made.

Jan 1, 1946

By Robert P. Burrows

Discussion of the paper of R. P. Burrows, presented `at the New York meeting, February, 1916, and printed in Bulletin No. 107, November, 1915, pp. 2237 to 2245. EDWIN M. CHANCE, Wilkes-Barre, Pa.-I have been very much interested in the comprehensive and able discussion of the important topic of mine lighting just given by Mr. Burrows, especially as I know by common report Mr. Burrows' ability and his close touch with the development of the electric mine lamp, and its use in mines in connection with a portable electric lamp. It is regrettable that Mr: Burrows was not able to acquaint himself more closely with the cost of mine illumination, the actual cost, as produced by a portable light as carried by miners, whether a flame safety lamp or an open light. Had he been able to acquaint himself more closely with these data, he perhaps would not have arrived at some of the conclusions which he has presented to us in his paper. For example, we find Mr. Burrows advises that the open torch is by far the cheapest source of illumination, as produced by a portable light. I am very sure that is not the fact. The cost of miners' oil varies from about 25.c. a gallon to 90b. a gallon. The various States have passed laws from time to time rendering it mandatory that the miner shall use, whether he is willing or not, a so-called better or higher grade of burning oil. These laws have entailed the use of an oil so expensive that the use of the oil torch has become practically impossible, and the acetylene or carbide miners' lamp has largely taken its place. I have evolved a few figures showing the relative efficiency and usefulness of the open oil torch and the acetylene miners' lamp. For example, the acetylene miners' lamp consumes or burns 4 liters of acetylene per hour, or 0.14 cu. ft.; the oxygen consumed is 10 liters, or 0.35 cu. ft. per hour; air consumed, 50 liters, or 1.76 cu. ft. per hour; black-damp produced, 40 liters, or 1.41 cu. ft. per hour; air rendered extinctive to the acetylene flame, 112 liters, or 3.95 cu. ft. per hour; carbide con- sumed, 13 g. per hour. The open oil torch, on the other hand, burns about 20 g. of oil per hour; the oxygen consumed is 48 liters, or 1.69 cu. ft. per. hour; air consumed, 240 liters, or 8.47 cu. ft. per hour; blackdamp produced, 191 liters, or 6.73 cu. ft. per hour; air rendered extinctive to oil flame is 1,413 liters, or 49.92 cu. ft. per hour.

Jan 5, 1916

By E. K. C. Williams, Nathaniel Arbiter

INTRODUCTION The surface processes involved in preparing ores for flotation and for operations depending on their flocculation/dispersion characteristics * vary widely in agitation dependence. Most of the reagents used for these purposes are added to grinding circuits, pump sumps, launders, or directly to flotation cells with the turbulent flow conditions usually adequate both for mixing reagents and for surface reactions without special conditioners. However, some reagent systems do require specific control of agitation intensities and reaction times, the more important of these being the following: 1. Activation of ZnS with CuSO4. With the usual conditions pH about 10, with collector added with the CuSO4, Cu 2+ is almost completely precipitated as basic compounds and as collector salt. As a result the levels of reagent in solution are extremely low which probably accounts for the need for separate conditioning. The agitation intensities are at about the 0.01 HP/ton level.** 2. Flocculation with natural or synthetic polymers. In this case the agitation problem is two-fold; first, to insure adequate initial mixing of the viscous stock solution of the

Jan 1, 1980

By O. D. Gonzalez, H. A. Wriedt

Alloys ranging from pure iron to pure nickel were saturated with nitrogen gas at 918°, 999°, and 1217°C and analyzed. The solubility of nitrogen at 1-atm pressure was obtained as a function of nickel content for the whole range of iron-nickel alloys and the temperature dependence of solubility is shown for the experimental alloy compositions. The heat of solution and the entropy of solution of nitrogen in the alloys as func-tiom of composition up to 41 pct Ni are given. 1 HE acquisition of more exact thermodynamic information for systems composed of iron with various alloying elements continues to interest ferrous metallurgists. The interstitial alloying elements, especially carbon, hydrogen, and nitrogen, comprise a field of particularly intense study. A recent investigation of carbon solubility in Fe-Ni alloys held at 1000°C in gases of fixed carbon activity showed an unpredicted minimum in the solubility near 72 pct Ni.1 The present investigation was undertaken to see if a similar anomaly in solubility existed for nitrogen in Fe-Ni alloys. The solubility of nitrogen in ? iron at known nitrogen activities has been measured several times.&apos;-&apos; Corresponding information for the solubility of nitrogen in solid Ni and Fe-Ni alloys is not available. Juza and sachsze9 reported that metallic nickel dissolved 0.07 pct N in equilibrium with Ni3N at 445°C. This result was regarded as dubious by Turkdogan and Ignatowicz10 who found less than 0.0004 pct N in nickel specimens equilibrated at 600°C with ammonia-hydrogen mixtures having fugacities of N2 gas up to 35,000 atm. Such fragmentary reports indicate only that nitrogen gas has a very much lower solubility in nickel than in iron. MATERIALS A purified iron from Battelle Memorial Institute was used for solubility measurements. This grade contained more than 99.95 pct Fe, the highest content of any measured individual impurity being 50 ppm for each of As, C, Cu, and Pb. The nickel and iron-nickel alloys, supplied by the International Nickel Co., contained 0.02 to 0.04 pct C, 0.17 to 0.19 pct Mn, 0.04 to 0.08 pct Si, < 0.01 pct P, <0.03 pct S, and <0.20 pct Co as principal impurities. The Fe-0.59 pct Mn alloy was of zone-melted quality, the highest concentration of any individual impurity being 15 ppm Al. The "prepurified" grade of nitrogen gas from Matheson Co. had a nominal nitrogen content of 99.996 pct. An "electrolytic" grade of hydrogen gas from National Cylinder Gas. CO. in which the principal impurity is water vapor was admixed with the nitrogen to prevent oxidation of these specimens. This grade was preferred to a purer grade because the presence of some oxygen helps in suppressing contamination of the specimens, for instance, by silicon from the porcelain furnace tube. EXPERIMENTAL PROCEDURE The specimens were equilibrated in vertical tube furnaces through which a 99 pct N2-1 pct H2 gas was passed at ambient pressure. For the 915", 918", and 999°C runs, a wound-resistance furnace was used, and for the 1217°C runs, a furnace with a tubular silicon carbide element was used. The temperature control system on both furnaces was similar: a Weston "Celectray" controller with a modulator, responding to the electromotive force of a thermocouple with its hot junction in the furnace, switched the furnace current between high and low settings. The temperature distributions in the working zones of the furnaces were determined with calibrated Pt/Pt-10 pct Rh thermocouples. The overall uncertainty in temperature was estimated to be ±3° at 915° to 999°C and ±5° at 1217°C . Consideration of the small temperature coefficients of the equilibria studied, together with the error limits in the method of analyzing for nitrogen, showed that further refinement in temperature uniformity would give no improvement in resultant accuracy. The reactive gas was generated by mixing together "prepurified" nitrogen and "electrolytic" hydrogen directly from cylinders commercially supplied. The flow rates of nitrogen and of hydrogen were fixed by setting with bleeders the pressure drops across the individual calibrated flow meters of constant resistance. For any given alloy, the solubility of nitrogen at 1-atm pressure (% N) was obtained from the analyzed nitrogen content of equilibrated specimens (% Na)according to Sieverts&apos; law, thus

Jan 1, 1962

By Günter Petzow, Siegfried Steeb

DURING an investigation of the U-Co-A1, U-Ir-A1, and U-Ni-A1 ternary systems, three previously unknown phases have been identified which correspond to the phases UCoA1, UIrA1, and UNiA1, and which be- long to the C22 (Fe2P) type (P 6 2m). In the following the structure determination of the new ternary phases is reported. The alloys have been prepared in an arc furnace under purified argon from 99.97 wt pct U, 99.83 wt pct Co, 99.99 wt pct Al, 99.95 wt pct Ni, and 99.97 wt pct Ir. The pellets obtained were bright and brittle; chemical analyses agreed with the nominal compositions. To obtain equilibrium, the samples were annealed in evacuated quartz capsules at 950°C for 30 hr and then quenched in water. Guinier photographs were processed and evaluated according to a method already described previously.1,2 The hkl&apos;s, measured and calculated sin2 6 values, and in the case of UCoAl only calculated and estimated intensities, are given in Tables I to 111. Lattice parameters refined according to the least-squares method and the respective mean-square variations are presented in Table IV. Lattice parameters, especially the c/a ratio, lead to the assumption that the three phases are crystallizing in the C22-type structure. For the calculation of the intensities given in Table I, the atomic positions recently reported by wyckoff3 have been accepted for the C22 (Fe2P) type. The uranium atoms were assumed to be in phosphorus sites; furthermore the scattering amplitudes of the boron atoms have been averaged in the stoichiometric formula UB2 according to atomic percentages; i.e., for these atoms a statistical distribution on the iron sites was assumed. The two smallest distances between a uranium and

Jan 1, 1967

[Separates of all the Technical Publications published in 1928 are available at Institute headquarters. All the papers are on file in public, university and technical libraries, and when so indicated in the list, may be found either in the TRANSACTIONS or in the special volumes issued by the Institute.; METAL MINING TECH- NICAL TRANS. PUBLI- TITLE AUTHOR MEETING VOLUME CATION AND PAGE* No. 50 The Eötvös Torsion Balance D. C. Barton New York Method of Mapping Geologic Feb., 1928 Structure 52 A Cartographic Correction for the C. A. Heiland New York Eötvös Torsion Balance Feb., 1928 61 Liquid-oxygen Blasting at Chuqui- H. C. Schultz, New York camata, Chile F. K. Middleton Hunter Feb., 1928 76, 108, 123 64 Working Methods of Practical Geo- Hans Haalck New York physics Feb., 1928 65 Experiments with Eötvös Torsion P. W. George New York Balance in the Tri-State Zinc and Feb., 1928 Lead District 74 Gravity Surveying in Great Britain H. Shaw New York Feb., 1928 75 The Computation of Eötvös Gravity E. Lancaster-Jones New York Effects Feb., 1928 82 Earth-resistivity Measurements in W. O. Hotchkiss, New York the Lake Superior Copper Country W. J. Rooney, Feb., 1928 James Fisher 83 Mining Methods and Records at the Roy W. Moore New York 76, 56, 90 United Eastern Mine Feb., 1928 98 Recent Results in Electrical Pros- Hans Lundberg New York specting for Ore Feb., 1928 101 Relation between the Oxygen Bal- G. St. J. Perrott, New York ance and Propulsive Strength of N. A. Tolch, Feb., 1928 Eight Gelatin Dynamites J. E. Crawshaw 102 Effect of Oxygen Balance of Gelatin G. W. Jones, New York Dynamites on the Gaseous Prod- G. St. J. Perrott Feb., 1928 ucts of Detonation 108 The Financial Report of a Min- Henry B. Fernald New York ing Company-Its Content and Feb., 1928 Meaning 116 What Duty to Support the Surface R. G. Bosworth New York Does a Subsurface Owner Owe? Feb., 1927 136 Comparison of Branch Raise and C. A. Mitke Los Angeles 76, 93, 103 Combined Shrinkage and Caving Sept., 1928 Methods 141 A Mining Company Balance Sheet G. F. Wolff New York Feb., 1928

Jan 1, 1927

The suggestions of the members of the Institute are very much desired by the Committee on Nominations prior to deciding upon its nominations to fill the places of those officers who retire early in 1917. The Committee must make its final report to the Board of Directors early in October. The members are, therefore, asked to send in promptly their suggestions for Directors as well as for Vice-Presidents and President. The Committee hopes to hear from a large number of the members. The officers to be elected at the annual meeting in February, 1917, are: One officer, known as Director and President. Two officers, known as Director and Vice-President. Five officers, known as Director. The attention of members is called to Articles V and VII of the Constitution, and to By-Law XIII, which reads as follows: "The geographical districts to be considered by the Committee on Nominations shall be as follows, until otherwise ordered by the Board. District No. 1. New England, New York, and New Jersey, excepting New York City and district, which is provided for in the Constitution. (N. B.-New York City and district is designated District 0.) District No. 2: Pennsylvania.

Jan 6, 1916

The suggestions of the members of the Institute are very much desired by the Committee on Nominations prior to deciding upon its nominations to fill the places of those officers who retire early in 1917. The Committee must make its final report to the Board of Directors early in October. The members are, therefore, asked to send in promptly their suggestions for Directors as well as for Vice-Presidents and President. The Committee hopes to hear from a large number of the members. The officers to be elected at the annual meeting in February, 1917, are: One officer, known as Director and President. Two officers, known as Director and Vice-President. Five officers, known as Director. The attention of members is called to Articles V and VII of the Constitution, and to By-Law XIII, which reads as follows: "The geographical districts to be considered by the Committee on Nominations shall be as follows, until otherwise ordered by the Board. District No. 1. New England, New York, and-New Jersey, excepting New York City and district, which is provided for in the Constitution. (N. B.-New York City and district is designated District 0.)

Jan 7, 1916

By Ralph W. M. Lai, D. W. Fuerstenau

This paper presents the results of a study of the principles which control the distribution of ultrafine particles between an oil phase and an aqueous phase. Alkyl sulfonates were used to control the wettability of fine alumina particles and to stabilize the water-isooctane emulsion system in the extraction process. The effects of sulfonate chain length, sulfonate adsorption, pH, and oil-water ratio on the recovery of solids in the oil phase were investigated. Higher extraction was found under conditions which yield higher hydrophobicity and large interfacial area of the oil-water emulsion. Today there is considerable interest in developing methods for the recovery of fine particles from disseminated ores. One such method might be the extraction of fine particulate solids from aqueous suspensions into an oil phase, and one example of a successful industrial process based on oil-water distribution phenomena is the emulsion flotation process used in concentrating manganese ore.&apos; The oil agglomeration process of Farnand, Smith, and Puddington has been suggested for concentrating tin ore. Patents 3-4 for oil flotation processes extend back to that of William Haynes in 1860. The basis of all these processes is directly related to the stabilization of emulsions with solid particles. The first extensive study of oil-water emulsions stabilized by finely divided solids was made by Pickering. Later, Briggs,6 weston, 7 Chessman and King,8 and Leja and Schulman9 experimentally demonstrated how solid particles control water-oil and oil-water systems. Hildebrand10 suggested that fine particles can stabilize an emulsion because the fine particles are partially wettable by both oil and water, that is, that the contact angle must be finite. Takakuwa and Takamori 11 recently applied emulsion inversion to the study of collector adsorption in flotation systems. At the Royal School of Mines, Shergold and Mellgren12 are currently carrying out a comprehensive study of the extraction of fine particles into an organic liquid phase. In the present study of the liquid extraction or oil flotation of ultrafine particles, the recovery of hydro-philic alumina particles of 0.1-µ average diameter was determined after separating an isooctane-water mixture (emulsion) into its two phases. Alkyl sulfonates of different chain lengths were used to change the wettability of the alumina and to effect emulsifi-cation of the oil-water mixture. The effects of the oil-water volume ratio, sulfonate adsorption, and pH on the recovery of the fine particles were investigated. Since the surface charge on an oxide such as alumina is determined by the adsorption or interaction of H+ and OH- with the surface, pH control is extremely important. Furthermore, since the zero point of charge (zpc) of alumina13-14 occurs at pH 9 to 9.4, major adsorption effects with anionic collectors in these systems will occur below pH 9. The results of the foregoing investigation are discussed in terms of the recovery of the fine particles, the oil-water ratio, contact angles, surface tension, the adsorption of sulfonate onto the solid surface, and the emulsifica-tion of oil. MATERIALS AND EXPERIMENTAL METHODS Materials: The particulate solid used in all the experiments was Linde "A" alumina, a high-purity, readily available form of a-alumina. The surface area of the alumina, as evaluated from measurements of stearic acid adsorption from benzene, was 14.5 sq m per gm, based on a value of 20.5 sq Å for the cross-sectional area of stearic acid.13 All aqueous solutions were prepared from triply distilled conductivity water. Other materials included high-purity crystals of sodium alkyl sulfonates, isooctane, and, for pH adjustments, reagent grade hydrochloric acid and sodium hydroxide-Because sulfonic acids are strong acids, they are

Jan 1, 1969

By R. S. Shoemaker, F. W. McQuiston

CARLIN GOLD MINING COMPANY 1974 Operating Data to October MINE LOCATION: 40 miles from Elko, Nevada ORE DESCRIPTION: Gold with minor amounts of mercury occurring in siltstone and carboniferous limey shales. TYPE OF MINE: Open pit ORE HAULAGE TO MILL: By trucks up to a distance of 12 mi1es MILLING CAPACITY: 2500 tons per day ORE GRADE: 0.20 oz per ton oxide ore 0.25 oz per ton carbon type ore PRODUCTS: Gold bullion 993 fineness, by product quicksilver RECOVERIES: Oxide ore 887&apos;0 Carbon ore 83% POWER FOR GRINDING: 7 Kwh/T POWER, other than grinding: 14 Kwh/T WATER SUPPLY: Pumped from wells 2- 112 miles through 13,000 ft of 8" buried pipe 6 ft underground. Consumption 0.60 tons of new water per ton of mill feed. TAILINGS: By 10" woodstave pipe a distance of 2500 ft to mine waste filled dam. RUNNING TIME: 10 ft x 10 ft mill on oxide ore, 98% 7 ft x 8 ft mill on carbon ore, 937&apos;0 Principal causes of lost time, power outages and problems of feeding gaseous chlorine to carbon ore agitators. LABOR, TONSIMAN SHIFT: See detailed data sheet ILL BUILDING DESCRIPTION: Framed structural steel with sandwich type walls of marine plywood, then packaged pre - fabricated insulation and outer sheeting of galvanized corrugated steel.

Jan 1, 1975

By N. Mungan

Formation damage, i.e.. reduclion in permeability, has been generally attribuled to clay minerals which expand or disperse upon contact with water that is less saline than the connate water. Luboratory, studies show that penneahility reduction can also occur in formalions containing only nonexpandable clays such as illite or kaolinite, and can be caused also by changes in pH. Furthermore, pH changes can damage even formations that are essentially free of clays. It is suggested that permeability reduction is due to the small passages being blocked by particles, which may be dispersed clays, cemenlion material or other fine parricles. These particles are dislodged by dispersion of clays due to changes in salinity or by dissolution of calcareous cement by acids, or of silicaceous cement by alkaline solutions. In working with reservoir cores, it was found that extracted cores damaged more easily and extensively than nonextracted cores. The extent of damage depended also on tenlperatltre. INTRODUCTION Permeability is an important property of porous media and has been the subject of many studies by engineers and geologists. Many of these studies are conccrned with formation damage, i.e., reduction in permeability, resulting from exposure of oil-producing formations to water substantially less saline than the connate water. This effect causes understandable concern since during drilling, completion and production phases formations are often exposed to fresh water. The damage resulting from contact with relatively fresh water has been attributed to expansion and dispersion oF clay minerals. During laboratory investigation of the use of NaOH as a wettability reversal agent to increase oil recovery from oil-wet reservoirs, several cores used in the displacement studies suffered loss in permeability. Despite the traditional usage of NaOH for conditioning aqueous mud systems, the role of the caustic filtrate in wellbore damage seems to have been overlooked. Browning2 as recently reported on the effects of NaOH in dispersing clay minerals but he was concerned only with complications that may arise in drilling massive shale beds. The following study was made to examine the role of pH and salinity changes in core damage. Where cores from reservoirs were used, tests were performed with extracted and nonextracted cores both at room and reser- voir temperatures, since it was felt that the test environment and core condition may affect the results. Because of its limited coverage and exploratory nature, this study is not intended to provide answers to field formation damage problems. It is hoped that it will encourage research into new aspects of the permeability reduction problems, particularly those allied to new recovery and production processes. PROCEDURE In all permeability tests, fluids were pumped through the cores at a constant volumetric rate. Only deaerated fluids and reagent grade chemicals were used. The fluids were passed through two ultrafine filters before injection to remove any entrained particles. The cores, with the exception of the unconsolidated cores, were mounted in Hassler holders. Water was used to transmit pressure to the sleeve. The inlet endpiece had two entry ports which permitted scavenging one fluid with another to avoid any mixing in the small holdup volume. The cores were flushed with CO2 gas, evacuated for 5 to 6 hours and saturated with the first liquid at a pressure of 1,000 psi for 24 hours to eliminate any free gas from the cores. Pressure differences up to 20 psi were measured by transducers, calibrated in inches of water and continuously recorded. For greater pressure drops, gauges were used. All reservoir cores were cleaned with a light refined mineral oil, then with heptane, and finally dried with CO2. Compatibility tests showed that no precipitates formed when mineral oil and the crudes were mixed. Some cores were extracted in Dean-Stark-type solvent extractors using xylene and trichloroethane and dried in a vacuum oven at 450F. Each test consisted of a sequence of water, test solution, and again water flow. RESULTS AND DISCUSSION STUDIES IN BEREA CORES Salinity Contrast Berea cores 2-in. in diameter and 12-in. long were cut from sandstone quarried in Cleveland, Ohio. The clay minerals were identified by X-ray diffraction to be chlorite, kaolinite, illite and incerlayered illite. Flow of fresh water or 30,000 ppm brinc does not cause any permeability reduction (Fig. 1). However, after injection of brine the core is readily damaged by fresh water. Damage starts almost instantly as the fresh water injection is begun, and at a cumulative injection of 1.2 PV fresh water, the permeability has dropped from 190 to 0.9 md. Upon continued injection, the effluent contains clay minerals dislodged from the core. The final core per-

Jan 1, 1966

By James P. Savely, Victor L. Kastner

Inspiration Consolidated Copper Company is currently mining in four pit areas; Live Oak, Red Hill, Thornton and Joe Bush Extension, near Globe, Arizona. Small satellite orebodies lying outside the main pits have been mined out in a series of small open pits. Major slope instability has affected production in every pit. Some consequences of the instability have been; (1) Serious interruption of mining plans, which resulted in deferred ore production, lost ore, reduced mining rates and increased stripping requirements. (2) Forced replacement of crushing facilities. (3) Serious effects on other production facilities. The introduction of a slope stability monitoring and control function as an integral part of mine planning has been successful in reducing the impact of these failures and will eventually result in economic pit design based on probabilistic slope analysis. This case history presents a brief review of the problems associated with slope instability at Inspiration&apos;s mines followed by a more detailed report on one specific failure area in the Thornton pit where the use of horizontal drain holes for slope stabilization appears to be successful. Relationships between slope movement rate, rainfall, and mining activity are shown.

Jan 1, 1983

By Benjamin Petkof

The mineral mica, which has been known to man since ancient times, has played an impor¬tant role in the development of our modern industry. In the latter part of the 19th century sheet mica began finding use as a dielectric insulating material in the newly developing electrical industry. Later, when modern elec¬tronics began to develop, it became a vital insulating and dielectric material for use in electronic equipment. Both the electrical and electronic industries were greatly dependent on some form of natural mica. The manufacture of electric motors of varying sizes, electronic tubes, and other electronic items was dependent on an adequate supply of sheet mica. During World War II this material was so vital to national defense that special efforts were made to mine it in the United States as well as to obtain it from overseas mica-producing areas. However, advancing technology has successfully begun the progressive development of man-made mica-based and non-mica-based materials that can replace mica for many uses. In addition, developing technology has dictated changes that have made sheet mica unnecessary for some uses. As the demand for sheet mica declined, the demand for scrap and flake mica has continued to increase. In fact, today the domestic production and use of scrap and flake mica far outshadows the necessity for good¬quality sheet mica in this country. Historically the United States has always been dependent on foreign sources of material for good-quality sheet mica and imports practically its entire requirement. In the case of scrap and flake mica, the United States is the dominant world producer and consumer. End Uses Sheet mica (Chowdhury, 1941; Rajgarhia, 1951; Skow, 1962) is available in many com¬mercial forms, but these forms can be broadly classified into manufactured and unmanufac¬tured mica. Manufactured mica consists of mica that has been shaped, punched, or other¬wise processed into some form, suitable for a particular end use. Unmanufactured mica con¬sists of partially hand-trimmed or processed material that has not been prepared for any particular end use. Unmanufactured mica is broken into two commercial classes consisting of sheet mica and scrap and flake mica. These classes of mica differ greatly in their ultimate end uses and marketed forms. Sheet muscovite mica can be classified by color, degree of prep¬aration of the crude material, thickness, size, visual appearance, and electrical quality. In addition, phlogopite mica is also classified by its thermal stability. Scrap and flake mica consist of mine, trimming shop, and factory scrap that occurs as remnants from mining, processing, and manufacturing operations, and small particle size mica that is available from the beneficiation of pegmatites, clays, schists, or other mica-rich host rock. The end uses for sheet mica vary so greatly from those of scrap and flake mica that it is necessary to discuss them separately. Sheet Mica Sheet mica consists of relatively flat sheets of material which have been mined as naturally occurring books or runs of mica. These sheets are hand-trimmed to remove any imperfections and are punched or stamped into specified shapes for industrial use. Sheet mica can be further processed and is described or specified as block, film, or splittings based on thickness. Block mica is not less than 0.007 in. thick with a minimum usable cross-sectional area of 1 sq in. Film mica is split from the better quali¬ties of block mica to specified thickness groups ranging from 0.0012 to 0.004 in. Splittings are sheets of mica with a maximum thickness of 0.0012 in. and a minimum usable area of 0.75 in. Other small sized, lower quality block mica

Jan 1, 1975

By J. D. Defilippi, E. M. Gilbert, K. G. Brickner

FCC chromium-manganese-nitrogen (Cr-Mn-N) steels differ from most other fcc materials in that these steels undergo a ductile-to-brittle transition. Transformation to martensite is considered to be responsible for this behavior in some metastable Cr-Mn-N steels. However, very stable Cr-Mn-N steels also exhibit a ductile-to-brittle transition. The results of this study indicate that deformation faulting is the probable cause of the brittle behavior of stable Cr-Mn-N steels. Deformation faulting accounts for the ductile behavior of these steels in a tension test at -320°F and brittle behavior in an impact test at -320°F. Deformation faulting also accounts for the toPological features observed on the fracture surfaces of impact specimens of these steels. FACE- centered- cubic chromium-manganese-nitrogen (Cr-Mn-N) steels differ from most other fcc materials in that these steels undergo a ductile-to-brittle transition. Many Cr-Mn-N steels transform to martensite during deformation,l-5 and several investigatorsl-3 have suggested that the brittle behavior of these steels is caused by martensite formation. However, very stable Cr-Mn-N steels also exhibit brittle behavior. Schaller and Zackeyl reported that a very stable Cr-Mn-N steel (less than 3 pct martensite formed at -320°F) exhibited a transition temperature higher than that for steels in which large volume fractions of martensite formed during testing. The explanation given by Schaller and Zackey for this observation was that in the very stable steel the martensite, because of its higher interstitial content, was more brittle than that formed in their other steels. This explanation was questioned by Tisinai and samans4 and Baldwin.6 Moreover, because the toughness of stainless martensite at cryogenic temperatures is generally very low, this explanation does not account for Thompson&apos;s7 observation that small additions of nickel (1 to 3 pct) greatly improve the toughness of high nitrogen (0.35 pct) Cr-Mn-N steels. The present paper summarizes the results of an investigation of the low-temperature brittleness in very stable Cr-Mn-N steels. The importance of the mode of deformation on the toughness of these steels is discussed. Table I. Compositions of the Steels Invertigated, Pet Steel C Mn P S Si Ni Cr N - A 0.09 14.70 0.018 0.011 0.47 0.22 18.40 0.54 B 0.12 14.90 0.001 0.008 0.48 0.14 17.80 0.38 C 0.12 14.95 0.004 0.005 0.62 3.95 18.43 0.38 MATERIALS AND EXPERIMENTAL WORK The compositions of the steels investigated are shown in Table I. Steels A and B had compositions within the limits of a proprietary Cr-Mn-N stainless steel,* whereas Steel C was similar in composition to the proprietary steel except for its 3.95 pct Ni content. All steels were hot-rolled to 1/2-in. thick plate. The plates were subsequently annealed for 1 hr at 2000°F and water-quenched. Standard longitudinal and transverse Charpy V-notch impact specimens were machined from the annealed plates. Duplicate longitudinal and transverse impact specimens were tested at 212", 80°, 32", 0°, -100°,-160°,-200°,-256", and -320°F. Longitudinal tension-test specimens were also machined from the plates and tested at a crosshead speed of 0.05 in. per min at the aforementioned temperatures. The fractured impact and tension-test specimens of all three steels were examined to determine whether martensite had formed during testing. Magnetic, X-ray, electron-diffraction, and electron-microscopy techniques were used to detect the presence of martensite in the highly deformed areas of these specimens. Metallographic examination of highly deformed areas of impact and tension-test specimens revealed the presence of dark-etching bands, such as those shown in Fig. 1. These bands were observed only in deformed samples and were thought to be associated with the low-temperature brittleness of the Cr-Mn-N steels. Accordingly, a sample 1 in. wide by 3 in. long was cut from the 1/2-in.-thick plate of Steel C. This sample was surface-ground to a in. and then cold-rolled 60 pct at -320°F. Thin foils were prepared from the cold-rolled sample and examined in a JEM electron microscope. Brightfield, dark-field, and selected-area diffraction techniques were used to determine the cause of the dark-etching bands. Fractographic experiments were also performed. Impact specimens Of Steels A, B, and C were broken at -320oF, and the fracture surfaces of these specimens were immediately shadowed with carbon. The carbon replicas were examined in a Siemens electron microscope, and attempts were made to correlate the topological features of the fracture surfaces with the deformation mechanisms that could be occurring during an impact test of these steels.

Jan 1, 1970

By L. F. Mondolfo

R301 is a clad aluminum alloy, composed of a core of a duralumin-type alloy clad with a magnesium silicide alloy. It differs from other well-known clad alloys in that the cladding and the core respond to the same heat-treatments. and therefore the cladding contributes appreciably to the mechanical properties of the material. In Table I are reported the compositions of the core and cladding alloy for the material used for the experiments. Table i.—Chemical composition of R~OI Used for the Experiments Element Core Cladding Cu........................ . 0.01 Fe......................... . 0.42 Si......................... 0. 0.71 Mg........................ . 0.99 Mn ........................ . 0.54 In clad aluminum alloys where the core contains copper and the cladding does not, at elevated temperatures the copper tends to diffuse from the core through the cladding. This fact is well known and many investigations have been conducted to determine the features of this diffusion. Most of those investigations cover materials clad with pure aluminum; the present investigation covers a material clad with an alloy. Since the cladding thickness on R~OI varies with the gauge, as shown in Table 2, several gauges were investigated. Material and Procedure he material used was sheet of the following gauges: o.o2~, 0.040, 0.064, 0.102, 0.170 Cut in pieces approximately 3 by 5 in., it was in the cold-rolled state and was soaked for increasing times at the following temperatures: glo°F., 940°F., 970°F. A Lindberg cyclone furnace was used for the experiments. The procedure was as follows: The furnace was started empty with controlling pyrometer set at the determined temperature. After the furnace had reached that temperature, it was run for some 20 to 30 min. empty, in order to allow the temperature inside to become stabilized. Then the first samples were introduced. A load thermocouple, with recording pyrometer, was connected with the sample of the heaviest gauge. About 10 min. was required for the material to reach temperature and the soaking time was counted from that point. After zoo min. soaking, the second group of samples was introduced without stopping the furnace. After 200 min. more, the third group of samples was introduced, and so on, until the last sample had been introduced. Every time the furnace was opened and new samples were added, a drop of temperature was registered by the thermocouple connected with the material

Jan 1, 1946

By L. F. Mondolfo

R301 is a clad aluminum alloy, composed of a core of a duralumin-type alloy clad with a magnesium silicide alloy. It differs from other well-known clad alloys in that the cladding and the core respond to the same heat-treatments. and therefore the cladding contributes appreciably to the mechanical properties of the material. In Table I are reported the compositions of the core and cladding alloy for the material used for the experiments. Table i.—Chemical composition of R~OI Used for the Experiments Element Core Cladding Cu........................ . 0.01 Fe......................... . 0.42 Si......................... 0. 0.71 Mg........................ . 0.99 Mn ........................ . 0.54 In clad aluminum alloys where the core contains copper and the cladding does not, at elevated temperatures the copper tends to diffuse from the core through the cladding. This fact is well known and many investigations have been conducted to determine the features of this diffusion. Most of those investigations cover materials clad with pure aluminum; the present investigation covers a material clad with an alloy. Since the cladding thickness on R~OI varies with the gauge, as shown in Table 2, several gauges were investigated. Material and Procedure he material used was sheet of the following gauges: o.o2~, 0.040, 0.064, 0.102, 0.170 Cut in pieces approximately 3 by 5 in., it was in the cold-rolled state and was soaked for increasing times at the following temperatures: glo°F., 940°F., 970°F. A Lindberg cyclone furnace was used for the experiments. The procedure was as follows: The furnace was started empty with controlling pyrometer set at the determined temperature. After the furnace had reached that temperature, it was run for some 20 to 30 min. empty, in order to allow the temperature inside to become stabilized. Then the first samples were introduced. A load thermocouple, with recording pyrometer, was connected with the sample of the heaviest gauge. About 10 min. was required for the material to reach temperature and the soaking time was counted from that point. After zoo min. soaking, the second group of samples was introduced without stopping the furnace. After 200 min. more, the third group of samples was introduced, and so on, until the last sample had been introduced. Every time the furnace was opened and new samples were added, a drop of temperature was registered by the thermocouple connected with the material

Jan 1, 1946

By N. J. Grant, D. Carne, J. B. Seabrook

IT is unnecessary to review much of the literature on hydrogen embrittlement of steel since several excellent reviews and bibliographies exist.1-3 Hot acid pickling and cathodic charging have been known to cause hydrogen embrittlement of steel and have been used as laboratory methods to charge steels with hydrogen.4-8 Experimental Procedure The problem of prime concern in all instances, except in the work of Sims and coworkers,10 is that at no time was there a definite known hydrogen value reported which could be related to a particular value of the degree of embrittlement. It was the purpose of this research to determine the relationship between hydrogen content and degree of em-brittlement quantitatively. The 1020 stock used for the specimens was hot-rolled 7/16 in. diam rod of the following analysis: 0.19 pct C, 0.40 pct Mn, 0.012 pct P, 0.036 pct S&apos; Vacuum-fusion analyses for nitrogen and oxygen gave 0.014 pct O2 and 0.0011 pct N2. Cathodic charging was used to cause embrittle-ment. The advantages of this method were that no quenching was necessary, the impregnation was reasonably controllable, and representative samples for analysis could be prepared simultaneously with the charging of the tensile bars. Analyses for hydrogen were made in a vacuum-fusion type of apparatus which extracted gas from the samples by fusion in a molten tin-iron bath&apos; This apparatus, which has recently been described in detail elsewhere, will not be discussed here.". " Consecutive samples can be analyzed every 15 min with an accuracy of 0&apos;03 ppm. A A from an electrolytic or pickling bath can be charged for analysis in about 3 min, and analysis completed in 15 min. Samples of as-received 1020 stock were analyzed and found to contain a negligible amount of hydrogen (0.06 ppm). Preliminary pickling and electrolytic charging gave highly variable results. Cold-worked samples showed higher values but ranged from 0.6 to 6.0 ppm of hydrogen. Charging at 90°C gave higher values of charged hydrogen, but troublesome films on many of the specimens resulted. It was not until a few drops of a catalytic poison, prepared from 2 g of yellow phosphorus dissolved in 40 ml of carbon disulphide,8 was added to the electrolytic cell that fairly consistent high values of hydrogen could be charged into the as-received 1020 steel at room temperature. The cell used is sketched in fig. 1. The anode and fixture for the tensile specimens were fastened to the cell cover as shown, and the specimen was screwed in place, centrally located with respect to the anode. At first, anodes of lead and graphite were tried, but they contaminated the electrolyte and gave a slight deposit on the specimen. Later, a platinum wire was used in the form of a uniform helix. A current of 2 amp, corresponding to about 0.5 amp per sq in. of cathode, was used for most specimens. The electrolyte was 4 pct H2SO4 solution. Fig. 1 shows the form of the special tensile bar, the main portion of which was an ordinary 1/4 in. diam, 1 in. gauge length test bar, except that two to four small cylinders of stock were left attached by small links to the bottom end of the tensile bar for the purpose of providing samples for hydrogen analysis. Thus the bars and samples were charged with hydrogen simultaneously and an analysis could be made while the bar was being tested mechanically. Experiments were performed to determine how representative the test cylinders were of the middle of the test bar proper. While the bar center was being analyzed, the small cylinder was stored in dry ice, since it had been shown that such storage prevents loss of hydrogen for many hours.12 The results of these checks are shown in table 1. The checks are very good (0.3 ppm) and indicate that it is permissible to use the small end cylinders to establish the hydrogen content of the tensile test bar proper-

Jan 1, 1951

By James F. Kemp

The Bulletin of the Institute for March, 1911, is chiefly devoted to papers upon the iron ores of northeastern Cuba. At that time information about the new developments in the peculiar brown hematites of the region was becoming widely circulated and interest was especially keen. For some years exploration had been conducted with pits and trenches and so great an area had been shown to contain ore in the Mayari, Moa, and Cubitas or San Felipe districts, that the reserves conveniently situated for the consumption of American furnaces were estimated as quite two billions of tons. In the subjoined footnote will be found a list of the principal papers of special interest which have already been published.&apos; The further remark may, however, be made that the

Jan 1, 1915

By P. R. Swann, J. G. Parr

Quenched structures were studied in alloys containing up to 12.5 pct cobalt. The subsequent decomposition of a 10 pct cobalt retained-ß phase alloy was investigated using metallographic and X-ray diffraction methods. Hardness measurements also were made during the decomposition process. Precipitation of Ti2Co is by nucleation and growth; and an activation energy of 50,000 cal per mole was determined. The values of the coefficient ß suggest that the precipitate is pearlitic at temperatures between 450 and 475°C, and spheroidal between 500 and 525°C. THIS paper describes part of a series of invesligations into phase transformations in binary alloys of titanium with transition elements. The general approach is similar to that taken in work on titanium-iron and titanium-nickel alloys.&apos; Previous investigators&apos;&apos; have established the titanium-rich end of the titanium-cobalt phase diagram, reproduced in Fig. 1. Orrell and Fontana&apos; showed that alloys containing more than about 6 pct" cobalt quenched from the ß range, produced 100 pcl retained-p phase. The isothermal decomposition of alloys containing between 0.8 pct Co and 15.5 pct CO was investigated by the same workers in the temperature range 650 to 1000°C. They reported that these alloys transformed into a or Ti,Co depending on the cobalt content, but no quantitative data were given. In the work to be described a series of alloys containing 0.8 pct Co to 12.5 pct Co was examined in the quenched condition. The 10 pct Co alloy (the lowest cobalt content to retain 100 pct ß on quenching) was selected for further work on the tempering kinetics of the ß decomposition. Experimental Procedure Since our own melting equipment was not installed at the outset of this work, the Physical Metallurgy Division of the Department of Mines and Technical Surveys (Ottawa, Canada) prepared the alloys. These were made of Japanese sponge, (which when melted had a value of 103 DPH, using a 1-kg load), and electrolytically prepared cobalt. The al- loys, made up to contain 0.8, 1.6, 3.3, 5.8, 8.3, 10.0 and 12.5 pct Co, were homogenized by swaging into rods at 900°C. Filings were taken from the rods, and any iron chips from the file were separated magnetically. Size fractions of both plus and minus 200 mesh (about 75p) were shown by their constitution, after annealing just below the eutectoid temperature, to contain the same cobalt content. Consequently, it was permissible to use the —200-mesh fraction, knowing it to be representative of the rod composition. Quenching in argon was carried out in a newly designed furnace, whose features include (1) an Inconel furnace tube, (2) a positive pressure of argon maintained at all times in the furnace—even when a sample is removed or inserted. The furnace is shown in Fig. 2 and is described in the Appendix. The tempering processes were carried out on powder samples sealed in evacuated quartz capsules. Since the highest tempering temperature was 525OC, no protection against reaction with the quartz was necessary. (Tests were made on filings of iodide titanium and showed no hardness increase after equivalent heat-treatments.) A thermocouple was attached to the capsule, which was heated to the

Jan 1, 1959