Part XII - Communications - On the Ternary Phases UCoAI, UlrAI, and UNiAl of the C22 (Fe2P) Type

DURING an investigation of the U-Co-A1, U-Ir-A1, and U-Ni-A1 ternary systems, three previously unknown phases have been identified which correspond to the phases UCoA1, UIrA1, and UNiA1, and which be- long to the C22 (Fe2P) type (P 6 2m). In the following the structure determination of the new ternary phases is reported. The alloys have been prepared in an arc furnace under purified argon from 99.97 wt pct U, 99.83 wt pct Co, 99.99 wt pct Al, 99.95 wt pct Ni, and 99.97 wt pct Ir. The pellets obtained were bright and brittle; chemical analyses agreed with the nominal compositions. To obtain equilibrium, the samples were annealed in evacuated quartz capsules at 950°C for 30 hr and then quenched in water. Guinier photographs were processed and evaluated according to a method already described previously.1,2 The hkl's, measured and calculated sin2 6 values, and in the case of UCoAl only calculated and estimated intensities, are given in Tables I to 111. Lattice parameters refined according to the least-squares method and the respective mean-square variations are presented in Table IV. Lattice parameters, especially the c/a ratio, lead to the assumption that the three phases are crystallizing in the C22-type structure. For the calculation of the intensities given in Table I, the atomic positions recently reported by wyckoff3 have been accepted for the C22 (Fe2P) type. The uranium atoms were assumed to be in phosphorus sites; furthermore the scattering amplitudes of the boron atoms have been averaged in the stoichiometric formula UB2 according to atomic percentages; i.e., for these atoms a statistical distribution on the iron sites was assumed. The two smallest distances between a uranium and