By H. O. Hofman

At the Lake Superior meeting, September, 1904, Messrs. A. Gibb and R. C. Philp presented a paper entitled " The Constitution of Mattes Produced in Copper-Smelting,"' in which they concluded that ferrous and cuprous sulphides formed the chemical compound, 5 Cu2S, FeS. They arrived at this inference from the observed fact that a matte containing Cu,S, 90.4, and FcS, 9.6 per cent. (or, in round figures, Cu2S, 90, and FeS, 10 per cent.), did not contain any metallic copper, while one with more than 10 per cent. of FeS readily dissolved copper, and with less than this amount retained copper in mechanical suspension. Although they determined the melting-points of five mattes containing from 32.6 to 80.1 per cent. of copper, they did not draw a freezing-point curve, as the necessary apparatus was not available. A microscopical examination of 11 polished samples gave them a grayish-black field of very uniform appearance, except that five of the specimens showed the presence of metallic copper. The object of the present investigation was to supplement the above paper by drawing the freezing-point curve of the ferrous sulphide-cuprous sulphide series, and to see how the constitution could be further revealed by microscopical work. The results obtained lead to conclusions very different from those of Gibb and Philp. While their paper bears the date 1904, it was published only in 1906.2 In the meantime, Bolles3 had presented his paper, " The Concentration of Gold and Silver in Iron-Bottoms." The raw material which formed the basis of the research was a matte containing Fe, 61.68, and Cu, 11.20

Jan 1, 1908

By Charles Burgess

THE improvement, in the quality of cast iron by means of alloy additions has been a metallurgical accomplishment of recent years. Work in this field has shown that chromium is one of the most effective of such additions but, in general, the influence of chromium has been studied only in. connection with other alloying additions, with irons other than foundry irons, or with relatively high percentages of chromium. The present study was initiated for the purpose of determining the influence of small additions of chromium (0.25 to 1.00 per cent) on the quality and resultant properties of cast irons of various foundry grades. The effect of small chromium additions on cast iron was investigated with particular reference to casting characteristics, hardness vs. section, strength, machinability, heat resistance and structure. MATERIAL TESTED Three separate types of cast iron were investigated as to the effect of small chromium additions. The first series of these irons was prepared from remelted foundry cast iron at the Union Carbide and Carbon Research Laboratories, and the other two -series consisted of cupola melts made under usual operating conditions. The first series was made by melting 30-lb. charges of foundry scrap iron containing - 2.86 per cent carbon, 2.72 silicon, 0.50 manganese, 0.062 sulfur and 0.794 phosphorus in a carbon resistance furnace. The chromium was added as high-carbon ferrochrome just before pouring. The irons were cast at approximately 1250° C. (2282° F.). The analysis and physical properties of these irons are given in Table 1, test 1. The second set of cast irons was made in a cupola in accordance with normal practice, 'the charge containing approximately 42 per cent steel scrap and the chromium additions being made to the ladle. Analysis and tests of these heats are shown In Table 1, test 2. A small amount of copper was present in heat C of this series.

Jan 1, 1932

By Y. C. Liu

IN the study of the rolling recrystallization of face-centered-cubic metals, a most unusual observation is the frequent occurrence of a sharp re-crystallization texture of cube orientation. Although the general conditions under which this texture occurs are known,2,3 its origin is still not well understood. Based on the observed relationship between the {110}<112> deformation texture and the (113}<211> recrystallization texture, regardless of the effect of alloying elements2,4,5 or the symmetry of the deformation texture,&apos; there is a strong indication that a specific component of the deformation texture is related to a specific component of the recrystallization texture. Using the rotational reorien-tation relationship as a means of correlating the deformation and recrystallization textures, it was proposed that the deformation component which related the cube texture has {358)<523> indices."&apos; The investigation reported here was undertaken to seek experimental evidence for the validity of this proposition. Experimental Procedure Two copper single crystals having an initial orientation within 2" of (358) [523] indices were prepared in the manner described in Ref. 5. The purity of the copper was between 99.94 and 99.97 pct. The original dimensions of the crystals were as follows: specimen A, 0.465 in. thickness, 0.844 in. width, and 0.955 in. length; specimen B, 0.535 in. thickness, 1.120 in. width, and 1.36 in. length: Rolling was done on a laboratory rolling mill according to the following schedule: 0.010 in. per pass to 50 pct reduction in thickness, 0.005 in. per pass to 70 pct reduction inthickness, 0.002 in. per pass to 85 pct reduction in

Jan 1, 1958

By S. Robinson Brainard

In 1957 the pay of chief executives in the nonferrous metals industry was well above average when compared with other major industries. Furthermore, it continued to rise last year while sales declined 8.2 pct and profits plummeted 32.7 pct on the average. Compensation of Chief Executives: One of the primary objectives of the survey is to measure year-to-year changes in top-management total compensation as it relates to company size and industry characteristics. Total compensation includes salary, bonuses, and the value of deferred contingent compensation awards.

Jan 10, 1958

Executive SIDNEY J. JENNINGS, Chairman GEORGE D. BARRON J. E. JOHNSON, JR. EDWIN LUDLOW ROBERT M. RAYMOND Membership KARL EILERS, Chairman LEWIS W. FRANCIS J. E. JOHNSON, JR. LOUIS D. HUNTOON ARTHUR L. WALKER Finance GEORGE D. BARRON, Chairman CHARLES F. RAND BENJAMIN B. THAYER Library E. GYBBON SPILSBURY,1 Chairman ALEX C. HUMPHREYS2 GEORGE C. STONE2 J. H. JANEWAY4 BRADLEY STOUGHTON1

Jan 3, 1918

By R. A. Vandermeer

It is usually assumed that the rate-determining step in the migration of a grain boundary involves the thermally activated transfer of single atoms across the interface. Chemical reaction rate theory then gives a migration rate which is proportional to the driving force when this is small compared to kT.1 In their recrystallization studies on aluminum, Gordon and vandermeer2 obtained data which was capable of providing the first experimental test of this proportionality. They correlated stored energy (driving force) release measurements determined calorimetrically with fraction recrystal-lized kinetic (growth rate) data acquired metallo-graphically at a temperature where a significant amount of recovery takes place concurrently with recrystallization. Within experimental error, the results of Gordon and Vandermeer confirmed experimentally, at least over a limited range, the linear dependence of boundary migration (growth) rate on driving force in accordance with theory. In obtaining these results, however, an incorrect, implicit assumption was made in relating the average instantaneous growth rate of the recrystallized grains to the measured fraction recrystallized kinetic data. The purpose of this present note is to point out and correct this assumption. An alternate approach, whereby a more proper average growth rate can be calculated from the recrystallization kinetic data, is presented. The earlier data, reevaluated in terms of this new approach, show the same general trend as before so that the original conclusion of Gordon and vandermeer2 is still valid. As was shown in a detailed study3 of the geometrical features of recrystallization in aluminum, the colonies of recrystallized grains can be regarded as uniform cylinders embedded in a three-dimensional matrix, the number of such colonies being constant. Thus during the early stages of recrystallization the volume fraction recrystallized, Xv, can be written as Xv=ynvlr2 [l] where y is a shape factor and i and r are defined as the average length and radius of a recrystallized colony and are spatial averages over the specimen. -nv, is the number of such colonies in a unit of volume. The erroneous assumption made in the earlier paper2 was that r in Eq. [I] could be replaced by

Jan 1, 1965

By R. E. Reed-Hill, W. H. Hartt

High-purity magnesium single crystals, oriented with basal plane parallel to stress axis, were deformed in tension at room temperature so as to form second-order (1011)- (1012) twins. Investigation by optical and replica electron microscopy revealed that these twins can support very large internal strains approaching 1000 pct and that fracture follows as a direct consequence of these strains. At low strains the basal plane within (10i1)- (10i2) twins rotates with increasing deformation until it becomes approximately parallel to the twin boundaries. This rotation is not consistent with deformation by basal slip in the double twin, but may be rationalized in terms of nonbasal slip. Observations also indicate that basal slip in the primary (1011) twin, prior to second-order twinning, may contribute to this rotation. Deformation markings that are difficult to interpret in terms of slip on previously observed systems were noted in the twin bands. A possible means of rationalizing these markings is to relate them to grain boundary shear. The fracture associated with these twins is thought to initiate by formation of voids at the twin boundaries. These grow into microcracks, with ultimate fracture occurring by tearing of the interconnecting regions. THE significance of deformation and fracture along second-order (10i1)-(10i2) twins in polycrystalline magnesium1-&apos; and many magnesium alloys4 was discussed in a previous paper.5 It was noted that this double twinning mode effectively controls the room-temperature deformation and fracture of magnesium single crystals, oriented with the basal plane parallel to the tensile axis. Reed-Hill and Robertson6 observed that, although these crystals may fracture at a macroscopic strain of less than 1 pct, shear strains up to 1000 pct could occur within (1011)- (10i2) twin bands. They concluded that the fracture was "ductile" and resulted from concentrating the deformation into a very small volume. The present research was undertaken to obtain a better understanding of the deformation and fracture associated with these twins. EXPERIMENTAL TECHNIQUES The experimental procedure involved straining high-purity magnesium single crystals in tension at room temperature. Specimens were oriented so that the applied stress direction was within 2 deg of the [1010] crystal axis. The specimen cross section was rectangular with faces closely parallel to (1210) and (0002). The specimen preparation and testing procedures have been described in detail elsewhere.5 Second-order (1011)- (1072) twins nucleated during straining were studied using optical and replica electron microscopy techniques. For the latter, cellulose acetate-carbon double replicas were employed. Observations were made on the (1210) crystal surface, which is the plane of shear for twins of this type. In addition to the single crystals, some investigations were carried out on longitudinal polycrystalline specimens. These were obtained from high-purity magnesium plate with a texture in which the basal planes of the grains tended to be nearly parallel to the specimen axis. All. polycrystalline specimens were annealed prior to testing in order to produce a coarse grain structure, permitting Laue back-reflection X-ray photographs to be obtained from grains of interest. EXPERIMENTAL RESULTS a) Deformation Within ( 101 l )-( 1072) Twins. Fig. 1 is an optical micrograph demonstrating the extent of the plastic deformation that can occur in (1011)-(10i2) twin bands. Notice at the lower left corner of the photograph the large displacement of the dark band (a polishing step) where it crosses the twins. The shear strain in the twin band at this position was computed to be 700 pct, using the ratio of step width to twin thickness. It was previously shown5 that (1011)- (1012) twin bands are often composed of small, separate twins aligned close to the macroscopic habit plane. Fig. 2 is an electron micrograph from near the upper end of the twin band in Fig. 1. This illustrates that the twin habit often does not coincide exactly with the macroscopic band habit, but may be inclined at a slightly smaller angle to the matrix basal plane. Figs. 3 through 6 are electron micrographs of the twin band in Fig. 2 illustrating successive steps in the development of deformation inside the band. A twin band such

Jan 1, 1969

By R. Taggart, D. H. Polonis, W. C. Gallaugher

In the Ti-Cu system, the a&apos; phase can be produced over a wide range of alloy composition witJwut the retention of measurable amounts of the ß or ? phases. This paper reports on the decomposition of this hexagonal martensite phase front the standpoint of solute corzcentratiorz, tempering temperature, and coherency strain condition. The mechanism of precipitation during tempering comprises localized precipitation which is followed by discontinuous precipitation if sufficient coherency strains are present. The localized precipitation process in hypoeutectoid alloys is described by the generalized Johnson-hiehl equation and an activation energy of 46,000 cal per mole. In hypereutectoid alloys the corresponcEing activation energy is 51,000 cal per mole. The rate-controlling process has been proposed as the difision of copper along a&apos; platelet interfnces. SEVERAL investigations have been reported concerning the kinetics of decomposition of the mar-tensitic a&apos; phase in titanium binary alloys.&apos; In the Ti-Mo system,&apos; two modes of a&apos; decomposition have been observed in the presence of /3 phase; one of these involves the precipitation of fine a from a&apos;, and the other involves diffusion across the a&apos;-ß interface. In studies of the Ti-Cr system, Rostoker2 did not detect the formation of TiCr2 during tempering. In Ti-Ni alloys,3 the intermediate phase Ti2Ni has been found to precipitate directly from a&apos; along the interfaces between plates. With the exception of the study of Ti-Ni alloys the previous investigations of tempering phenomena in substitutional martensites are mainly qualitative and do not present a detailed description of the precipitation processes. The following limitations restrict the correlation of the microstruc-tural processes and reaction kinetics during tempering in most binary-alloy systems. 1) A mixture of at least two phases characterizes the constitution of quenched alloys. 2) Difficulties have been encountered in obtaining uniform structures throughout quenched samples. 3) The reaction products, and in particular their morphology. have not been clearly resolved. 4) The martensitic a&apos; phase forms over only a limited composition range for most titanium-base binary alloys. Gomez and polonis4 showed that the Ti-Cu system provides an excellent basis for investigating the tempering of a&apos; over a range of composition without the complication of retained P or the transition w phase. In the present work the effects of solute concentration, tempering temperature, and coherency strain conditions are considered with reference to the over-all precipitation process in quenched alloys of the Ti-Cu system. Both microstructural observations and kinetic data are correlated to define the rate-controlling processes which govern the observed localized and discontinuous precipitation reactions. An earlier paper5 was devoted to a discussion of the modes of heterogeneous nucleation of Ti2Cu from the martensitic a&apos; structure. The present paper will therefore emphasize the progress of the tempering reaction beyond the initial stages. EXPERIMENTAL METHODS The Ti-Cu alloys for this study were prepared by conventional arc-melting procedures. Chemical analysis revealed that the alloy buttons contained approximately 0.02 wt pct 0, 0.04 wt pct N, and within 0.1 wt pct of the intended copper concentration. The progress of the tempering reaction was followed by means of electrical-resistance measurements utilizing a Kelvin double bridge, microhard-ness readings with a 400-g load, and X-ray dif-fractometry patterns to reveal line-broadening effects. Metallographic specimens examined at magnifications greater than X1000 were shadowed with germanium to reveal fine structural details. Direct carbon replicas were prepared for the electron-microscopy studies. EXPERIMENTAL RESULTS Property Changes. The changes of microhardness that accompany the precipitation of Ti2Cu from a&apos; are shown in Figs. 1 and 2. As the solute concentration increases the peak hardness, for a given tempering temperature, increases. In alloys of given composition the time to reach the peak hardness agreed with the time to attain maximum X-ray diffraction peak breadth, as shown in Fig. 3. The maximum hardness and the maximum line breadth increased with lower tempering temperatures, and the time to reach the maximum also increased. The a&apos; peaks broadened during the initial stages of tem-

Jan 1, 1965

By Nicholas J. Grant, A. W. Mullendore

Measurements of grain boundary sliding were made on polycrystal and bicrystal tensile creep specimens of Al-2 pct Mg at 500oand 700oF. Grain and pain boundary orientation factors were studied with respect to their effect on the magnitude and direction of grain boundary sliding. It was concluded that a large part of the observed sliding may be caused by the operation of slip crossing the grain boundaries. Supporting evidence for this model from other investigations is also given. GRAIN boundary sliding in metals during elevated temperature deformation has frequently been thought of as an independent mechanism with its own characteristic stress, temperature, and structure dependence. Further, it is common to regard the grain boundary as the weak link during creep deformation since: 1) the strength of apolycrystallinemetal, as meas-sured by creep rate or rupture life, decreases at\a more rapid rate when sliding comes into action, and 2) grain boundary sliding, as revealed by "boundary darkening" and fold formation is often the first visible deformation. On the other hand, more quantitative observations, in both polycrystals and bicrystals, have shown boundary deformation to be closely related to the over-all deformation of the specimen. The curve of grain boundary contribution to elongation vs time takes a shape similar to that of the total creep curve,&apos;,&apos; and the apparent activation energy for sliding appears in most cases to have the same value as that for total creep.3 In order to reconcile these observations, one is left with these possibilities: 1) The grain boundary and grain deformation rates are both controlled by the same rate limiting processes. 2) The rate of sliding is limited by accommodation deformation in the grains. 3) Sliding is the consequence of grain deformation. 4) Grain deformation is dependent on prior grain boundary deformation. Alternatives 2) and 3) would view grain boundary sliding as occurring in series with another deformation process which could be rate controlling. McLean prefers item 3) as the sliding basis,4 where subgrain rotation results from dislocation accumulation in the substructure at the grain boundary. Crussard and Friedel&apos;s5 treatment of grain boundary migration considers that dislocations are forced into the grain boundary and are dissociated into dislocations with Burgers&apos; vectors nearly parallel to the grain boundary. The movement of these partial grain boundary dislocations then produces the sliding. The results of this investigation have indicated alternative 3) to be the most appropriate and it is this aspect of grain boundary sliding which will be analyzed. EXPERIMENTAL PROCEDURE Three types of tensile creep tests were employed in this study: (I) A constant load test of one very coarsegrained polycrystalline specimen at 500° F, 3600 psi, 1 pct per/hr strain rate to examine the grain and grain boundary orientation factors in grain boundary sliding. (II) Constant strain rate tests of polycrystalline specimens at 510o and 715o F, 2 pct per/hr strain rate to determine the grain boundary contribution to elongation at very low total strains. (m) Constant strain rate tests of bicrystals of various grain and grain boundary orientations at 500°F, 2 pct per/hr strain rate to obtain further information on the orientation effects in grain boundary sliding. The material used in the tests was a high-purity Al-1&apos;.92 mg alloy, kindly furnished by Alcoa. Its composition is given in Table I. The alloy is a solid solution at the test temperatures. The coarse grained polycrystalline specimen for test (I) was prepared by recrystallizingthe machined specimen, straining it about 1pct intension at room temperature and annealing at 900°F for 8hr. The constant strain rate specimens (11), with an 178 in. sq. by 1/2 in. long gage section, were cut from 1/8 in. thick sheet of cold rolled and annealed (8 hr at 1000oF) material. The latter specimens were supported in a special jig during the milling operations to avoid any bending, and the gage section was subsequently heavily electropolished to remove the cold-worked surface layer. The bicrystals (ID) were machined in the same

Jan 1, 1963

By A. R. Troiano, A. B. Greninger

There is need for an adequate working hypothesis that would describe at least qualitatively the crystallographic mechanism for the transformation from austenite to martensite in steel. A general theory would not only be of great assistance in the correlation of existing data and in planning future experimentation, but would also form the basis for an eventual explanation of the property changes that accompany lattice transformations. The mechanism of martensite formation described in the following pages is the outcome of two new experimental determinations: (1) the accurate evaluation of the lattice relationship between austenite and individual crystals of martensite, and (2) the measurement and analysis of the change in position that a volume of austenite undergoes when it transforms into a crystal of martensite. For this latter study, the stereographic analysis of shear was employed; this method greatly simplifies the solution of lattice-shear problems, and some space is devoted to its description. Lattiice Relationships and Habits PREVIOUS WORK The lattice relationships between austenite and martensite in carbon steels have been studied by Kurdjurnow-and Sachs,&apos; and by Wassermann;2 and in iron-nickel alloys by Nishiyama.3 Wassermann,2 and Mehl and Derge.4 The studies by Kurdjumow and Sachs and by Wassermann were made on single (austenite) crystals of quenched 1.4 pct carbon steel, and the results of these two independent studies agree closely with the postulated lattice relationships: (III)r||(0ll)a [101]r [111]a [1] Both Nishiyama and Wassermann worked with an alloy of iron plus 30 pct nickel (all austenite at room temperature), and "martensitic alpha" was formed by cooling in liquid air. They agree that the lattice relationships for these conditions are: (lll)r||(011)a [112]r[011]a [2] Mehl and Derge worked with a range of iron-nickel alloy compositions centered about 30 pct nickel. They concluded that when the transformation takes place near room temperature or above, relationship [l] holds, but if the same specimen is made to transform at -195°C, relationship [2] obtains;intermediate temperatures evidently produced a combination of these two relationships. Sachs and co-worker~,1,7 as well as Nishiyama,3 have proposed transformation mechanisms for martensite formation.* Both of the mechanisms picture the transformation as initiated by shearing movements along the octahedral [Ill] plane of austenite, followed by suitable expansion and contraction to complete the transformation. These mechanisms have been described and commented upon by Mehl, Barrett, and Smith,8 Mehl and Derge,4 Wassermann,2 and others, and generally accepted by investigators in this field. Greninger and Troiano9 have recently published the results of a detailed study of the shapes and orientation habits of martensite crystals in plain-carbon and nickel steels. They found that, contrary to previous assumptions, martensite plates form not along the octahedral planes but along austenite planes of very high indices; these results were in line with those of previous studies of martensite reactions in nonferrous alloy systems by Greninger and coworkers.6,10 Greninger and Troiano concluded that the transformation theories of Kurdjumow and Sachsl and of Nishiyama3 are untenable. Phragmén11 reached a similar conclusion. EXPERlMENTAL METHODS The object of this particular study was the evaluation of (1) lattice relationship between austenite and martensite, and (2) relationship between the martensite lattice and the martensite plate. The technique used for solving these problems was similar to that used by Greninger6 on martensitic structures in 8 copper-aluminum alloys. Briefly, the method consists of grinding and polishing a specimen on a surface parallel to an individual martensite plate and thus exposing a single martensite crystal for an area of l to 3 mm. The orientation of this exposed martensite crystal is then determined by means of a back-reflection Laue X ray pattern.12 Another pattern is obtained from the matrix crystal, and a stereo-graphic plot of data from these two patterns then provides the solution to the problem. It is necessary to repeat this process on several crystals in order to determine whether or not the solution is unique.

Jan 1, 1950

By H. J. Levinstein, H. J. Guggenheim, C. D. Capio

An optical incestigation of the phase transformations in RbFeF, has been conducted. Details of the ferromagwetic phase transition and the metamagnetic state are disczrssed. The three-dimensional magnetic domain structure existing in bulk crystals of RbFeF3 is described, as well as the effect of the magnitude and direction of the applied magnetic field on the domain struclure. The strong magnetoelastic interaction in RbFeF, is demonstrated. The results of the direct observation of the role of dislocation subboundaries and slip bands as nucleation sites and as pinning sites for magnetic domain walls are reported. THE perovskite compound RbFeF, has recently been shown to exhibit three magnetic states.&apos;&apos;&apos; Above 102°K it is paramagnetic, between 102" and 87°K it is antiferromagnetic. and below 87°K it is ferromagnetic (i.e., exhibiting remanence) with a modification of the magnetization occurring at 40°K. The changes in magnetic structure at 102o, 87°. and 40°K are accompanied by shear transformations to successively lower crystal symmetry classes.3 At 102°K a second-order phase transformation to a tetragonal crystal structure occurs. The c/o ratio increases with decreasing temperature to a value of 1.0034 at 87°K where the crystal undergoes another shear transformation to an ortho-rhombic crystal structure. The magnetic modification at 40 K is also accompanied by a shear transformation to a lower crystal symmetry. RbFeF3 is unique in that in the ferromagnetic state it is transparent in the bulk to visible light, has a low saturation magnetization, a large magnetic rotation. and has good optical properties.&apos; All these features make it an ideal material for the investigation of magnetic domain structures in bulk crystals. In addition a dislocation etch has been developed which reveals the point of emergence of dislocations with the (100) surfaces of RbFeF3,5 making it possible to determine the dislocation arrays in the material. As a result domain wall dislocation interactions can be observed in the bulk crystal. In this paper we report on 1) the crystallography of the phase transformations in RbFeF3. 2) the domain configurations as a function of magnetic field and crystal orientation. 3) the interaction of dislocations and magnetic domain walls in RbFeF,. EXPERIMENTAL PROCEDURE Since the temperature range of interest is below room temperature the dewar shown in Fig. 1 was employed. It was designed to fit on the stage of a Leitz panphot metallograph, and permitted examination of the sample at a magnification up to 150 times. The dewar consists of a double-walled glass cylinder bent into an L shape. The space between the walls is evacuated. The viewing wirldows were made of four optically flat quartz discs aligned parallel to each other and sealed to the sides of the concentric cylinders. The specimens were mounted in a holder attached to a flexible plastic shaft. Various holder designs were employed depending upon the type of observations to be made. For studies of the phase transformation between the antiferromagnetic and ferromagnetic state the holder shown in Fig. 2(d) was employed. This holder permitted accurate temperature control at 82" to 88°K by balancing the heat input from the carbon resistance heater against the heat loss to a heat sink immersed in liquid N2. Magnetic field studies were conducted by employing the holders shown in Figs. 2(a) and (b). The holder shown in Fig. 2(n) has a solenoid imbedded in it. such that the magnetic field direction is in the same direction as the incident light. The magnetic field provided by the holder in Fig. 2(b) is perpendicular to the incident light direction. The holder in Fig. 2(r) was employed when observations of the specimen were desired while an elastic bending stress was applied to the sample. The stress was applied to the sample by pulling a wire from outside of the dewar. The wire was attached to a lever pivoted on the holder. which caused the knife edge of the lever to push against the sample. The crystal growth and the sample preparation were described previously.&apos; PHASE TRANSFORMATIONS The first phase transformation in this system is from the cubic perovskite structure to n tetragonal

Jan 1, 1970

By N. Brown, H. Green

The effect of quenching temperature and of aging temperature and time on compression stress-strain curves of ß brass was investigated. Age softening occurs at a rate which decreases with decrease of quenching temperature below the critical temperature for ordering. The activation energy for softening is 15,400 cal per mol. No matter how rapidly brass is quenched or what the temperature from which it is quenched, practically complete order is obtained at room temperature. It has been demonstrated that with respect to the specific heat,&apos;,&apos; electrical resistivity," X-ray diffraction, and microstructure, the slowly cooled and rapidly quenched specimens are the same and that complete long range order exists in both cases. However, Smith" showed that the hardness of ß brass depended upon the cooling rate and the temperature from which brass is quenched. Smith showed that the hardness was a maximum for specimens quenched from about 445 °C and that the as-quenched structure softened at room temperature at a rate depending upon the temperature prior to quenching. This softening after quenching is in this paper referred to as age softening. The results of this investigation are qualitatively the same as the findings of Smith. However, a more detailed analysis of these phenomena has been possible since the stress-strain curve offers a more sensitive index of the state of the metal than hardness. It is the purpose of this paper to show how the mechanical properties are related to the ordering of ß brass. A 200-lb ingot made from electrolytic copper and electrolytic zinc was extruded to 1/2in. rod. Chemical analyses at frequent intervals along the rod showed that the alloy contained 51.5 pct Cu with the greatest impurity being iron, at 0.01 to 0.001 pct. To obtain a constant test material, the 1/2in. extruded rod was warm-rolled to % in. diameter at 200°C and then recrystallized to a grain size of 2.0 mm. The specimens for the compression test were % in. high and % in. in diameter. The specimen ends were polished on 600 metallographic paper and coated with Molykote for a lubricant. The compression rig consisted of an anvil resting on the machined table of the Baldwin Southwark testing machine and a plunger fixed to the movable cross

Jan 1, 1954

By N. A. D. Parlee, I. D. Shah

THIS communication reports the results of some work done on the effect of gold, palladium, and platinum on the liquid-gas-solid equilibrium in the Ag-O system,1,2 see Fig. 1. Recently several investigators3, 4, 5 have reported the effects of gold, palladium, platinum, and copper on the solubility of oxygen in liquid silver. This communication represents only a portion of the work done here on the solubility of oxygen in liquid silver and liquid Ag-Au, Ag-Pd, and Ag-Pt alloyss—the greater part having already been reprted. The apparatus, materials, and procedures used were similar to those of earlier work.&apos; l The main precautions observed in obtaining these freezing points at constant temperature and PO2 = 1 atm were as follows: 1) The points were approached very slowly from higher temperatures. 2) In the very near vicinity of the L-G-S equilibrium point precautions were taken to see that the melt was in equilibrium with oxygen at one atm. Equilibrium was considered to have been attained when no more absorption of oxygen was observed in the last 15 min at a fixed temperature. 3) In the case of these alloys, the freezing point of the melt at 1 atm of oxygen and the equilibrium amount of oxygen absorbed by the liquid "infinitesimally" above this point were determined by lowering the temperature in very, very small steps, equilibrating at

Jan 1, 1969

By J. V. Emmons

IT has long been known that the outside skin of tool steel frequently exhibits properties widely different from the interior of the mass. Within the last few years it has been generally recognized that many of these properties were clue to surface decarbonization. The origin and effects of this altering of the composition have been but little studied. C. M. Johnson&apos; arrives at the conclusion that, in annealing, "the most active agent in surface decarbonization is the rust or scale (present on the surface), which is actually reduced to metal at the expense of the carbon in the steel to which it adheres." W. H. Hatfield in his admirable paper, The Chemical Physics Involved in the Decarburization of Iron-Carbon Alloys,&apos; has given us the most tenable theory of the removal of carbon from iron. While Mr. Hatfield&apos;s work has been principally clone in connection with the annealing of white cast iron to produce malleable castings, it is frequently applicable to the decarbonization of tool steel. The following equations which he proposed have been fully borne out by the author&apos;s experiments: 2Fe3C + 2CO2 = 3Fe2 + 4C0 2C0 + 02 = 2C02 Continuous 2C02 + 2Fe3C = 3Fe2 + 4C0 It is the purpose of the author to show, in a quantitative manner, the effect of various treatments in eliminating the carbon in tool steel. Some of the phenomena of the decarbonized surface will also be described, as well as the practical problems they present to. the manufacturer and user of tool-steel products.

Jan 9, 1914

By M. E. Wadsworth, I. B. Cutler, R. W. Bartlett

The oxidation kinetics of ZrC was studied between 450" and 580°C in oxygen pressures from 6.5 x 10-to 1 atm using a ther mogravimetric apparatus and sized powder samples. Two parallel rate controlling processes were observed. A surface reaction occurring at the ZrC-ZrO2 phase boundary accounted for most of the oxidation and had an activation enthalpy of 46 kcal per mole. The other process, believed to be diffusion of oxygen into the ZrC lattice partially replacing carbon, had an activation enthalpy of 53 kcal per mole. The enthalpy for chemisorption of O2 on ZrC was determined to be —13 kcal per mole. Water vapor in the presence of oxygen accelerated the surface reaction rate. THERE has been little reporting of formal rate studies or attempts to ascertain the mechanism of oxidation of carbides. MacDonald and Ransley1 studied the oxidation of titanium carbide which has the same structure as zirconium carbide, fcc. They observed an initial increase in rate with increasing temperature followed by a rapid decrease through a rate minimum and a subsequent second increase at higher temperatures. The discontinuity in the rate rise was attributed to a phase change in the oxide which changed the rate determining step from the surface reaction at the carbide-oxide interface to diffusion through the oxide layer. Samsonov and Golybera 2 studied titanium carbide and reported that during the initial period of oxidation a dense film of Tic-TiO was formed followed by the formation of less adhering layers of higher oxides. The purpose of this investigation was to study the kinetics of oxidation of zirconium carbide and to attempt to gain some knowledge of the mechanism by which oxidation occurs. EXPERIMENTAL PROCEDURE Measurement of the weight gain associated with the oxidation of ZrC was used to determine oxidation rates. The principal experimental parameters were surface area, temperature, and oxygen pressure. Although moderately sized crystals of ZrC can be grown by the Van Arkel method, the only commercially available ZrC is a powder. In using powders, the surface area must be controlled either by fabricating the powder into a sintered pellet with a measurable surface area, relatively fixed during oxidation, or by using sized unconsolidated powder and applying appropriate geometric considerations to the shape of the grains to correct for their diminishing surface areas as they oxidize. Both techniques involve some difficulties. pellets of binder-free zirconium carbide can be made by hot pressing, but it is difficult to obtain densities greater than 90 pct of

Jan 1, 1963

By D. L. Wood

This investigation was concerned with the aluminum-oxide particle dispersions, the mechanical properties, and the re-c,uystallization characteristics of some internally oxidized copper-aluminum alloys. Obserued hardness vaviations are in agreement with variations in oxide particle size revealed by electron metallographic studies. The increase in yield strength caused by internal oxidation is quite sensitive to matrix grain size and is accompanied by a loss of ductility, particularly at higher temperatures. Elevated temperature ductility is con-side,vably improved if major grain reorientation is accomplished by ve recrystallization prior to testing. The oxide particles offer a considerable restraint to softening during annealing after cold deformation. THE diffusion of oxygen under appropriate conditions into a suitable alloy causes solute oxide particles to be precipitated at an inward moving interface.1,2 Previous work has shown that the hardness

Jan 1, 1960

By W. R. Hibbard

The term lineage was first introduced by Buergerl to denote dendritic branches, grown from a crystal nucleus during solidification from the liquid, with imper- fections in alignment of the order of 10 : to 10-4 cm. These imperfections are associated with distortions of the dendrites caused by the subsequent solidification of the inter-dendritic filling and are illustrated in Fig I. Buerger etched zinc single crystals made by the Bridgman3 method to develop this dendritic pattern and show lineage microscopically. Since maximum crystal growth in face-centered cubic metals occurs along the [IT] directions,2 lineage would appear in copper as small deviations of dendritic branches from these directions. Elam4 and others5"8 reported etching effects resulting from coring along the cube face traces of various copper alloy crystals. These traces were used by Samans8 to orient single crystals. Williamson9 noted a "lined structure (in alpha brass single crystals) consisting of an ordered arrangement of etch pits" which were probably traces of {IOO} planes but somewhat uncertain because they were never straight (that is, apparently lineage). Greningerl1 described the distortion and multiplicity of Laue spots in back reflection X ray photograms of copper single crystals showing lineage. The present investigation -includes metal-lographic, X ray, and property studies of lineage in large grain and single crystal specimens of copper. Preparation of Specimens specilnens 10 in. long 35 1/2 in. diam of oxygen-free copper (o.F.H.c.) (99.985 pet) were&apos; melted vertically in graphite crucibles under an atmosphere of commercial nitrogen purified through a gas train including sulfuric acid, potassium chloride, magnesium chiorate, hot copper chips and phosphorus pentoxide. After a temperature of 1200°C had been maintained for 1/2 hr, the furnace was turned off and the specimens cooled at a rate of about 150°c an hour&apos; This method of direct solidification was used by Greningerlo to produce single crystals with marked lineage and in this investigation produced a fair yield of single crystal specimens in

Jan 1, 1949

By W. R. Hibbard

The term lineage was first introduced by Buergerl to denote dendritic branches, grown from a crystal nucleus during solidification from the liquid, with imper- fections in alignment of the order of 10 : to 10-4 cm. These imperfections are associated with distortions of the dendrites caused by the subsequent solidification of the inter-dendritic filling and are illustrated in Fig I. Buerger etched zinc single crystals made by the Bridgman3 method to develop this dendritic pattern and show lineage microscopically. Since maximum crystal growth in face-centered cubic metals occurs along the [IT] directions,2 lineage would appear in copper as small deviations of dendritic branches from these directions. Elam4 and others5"8 reported etching effects resulting from coring along the cube face traces of various copper alloy crystals. These traces were used by Samans8 to orient single crystals. Williamson9 noted a "lined structure (in alpha brass single crystals) consisting of an ordered arrangement of etch pits" which were probably traces of {IOO} planes but somewhat uncertain because they were never straight (that is, apparently lineage). Greningerl1 described the distortion and multiplicity of Laue spots in back reflection X ray photograms of copper single crystals showing lineage. The present investigation -includes metal-lographic, X ray, and property studies of lineage in large grain and single crystal specimens of copper. Preparation of Specimens specilnens 10 in. long 35 1/2 in. diam of oxygen-free copper (o.F.H.c.) (99.985 pet) were&apos; melted vertically in graphite crucibles under an atmosphere of commercial nitrogen purified through a gas train including sulfuric acid, potassium chloride, magnesium chiorate, hot copper chips and phosphorus pentoxide. After a temperature of 1200°C had been maintained for 1/2 hr, the furnace was turned off and the specimens cooled at a rate of about 150°c an hour&apos; This method of direct solidification was used by Greningerlo to produce single crystals with marked lineage and in this investigation produced a fair yield of single crystal specimens in

Jan 1, 1949

By Klaus Schwerdtfeger, Hans-Jürgen Engell

Activities of silicon in Ni-Si melts have beelz determined in the temperature range 1480° to 1610°C from electromotive-force measurements involving the cells The data obtained are used to derive the activities of nickel and the integal free energies of mixing. Entropies of mixing are calculated from the free energies of mixing as obtained in the present study and the heats of mixing as available in the literature. ACTIVITIES in Fe-Si and Co-Si melts have been determined recently by the authors&apos; using galvanic cells consisting of alloy, an oxygen electrode, and an oxide melt as electrolyte. The present paper deals with activities in Ni-Si melts as measured with the same technique. A schematic diagram of the cell is shown in Fig. 1. The alloy and the electrolyte consisting of CaO and SiO2 are contained together in a silica-glass crucible. During the experiment the silica glass crystallizes to cristobalite on the surface of the crucible. Nickel contents of the electrolyte are very small (<0.1 pct as checked with chemical analysis), because of the noble character of nickel in comparison with silicon. A tapered silica tube is connected to the crucible through which a platinum or molybdenum wire is inserted, as shown in Fig. 1. A platinum tube reaches the surface of the CaO-SiO2 electrolyte from above. The platinum tube is provided with four holes on its side, through which oxygen of 1 atm pressure is blown over the electrolyte. The cell reaction is given by the equation Si(metal) + O2(gas) = SiO2(electrolyte) [3] and the galvanic electromotive force of the cell is given by the formula

Jan 1, 1965

By M. L. Fuller

The fundamental mechanism of the deformation of zinc has been thoroughly described by several prominent investigators, particularly Mark, Polanyi, and Schmid,1 Mathewson and Phillips,2 and Schmid and Wassermann.3 The deformation of zinc occurs primarily through slip along basal planes (00.11, and secondarily through twinning on pyramidal planes of the form (10.2). In addition to these basic studies on single crystals, there have been a number of determinations4,5 of preferred orientations developed in rolled, polycrystalline zinc. In no case, to our knowledge, has there been described the development of oriented structures in zinc as a result of a systematic series of rolling treatments. The work included in the present paper shows the changes in orientation produced in a zinc alloy by successively increasing degrees of cold-rolling reduction. This alloy has the same crystal form, hexagonal close-packed, as zinc, but its susceptibility to hardening for a given degree of working is much greater because of its higher recrystal-lization temperature. Experimental Procedure Composition of the Alloy and Rolling Treatment The alloy used in this investigation consisted of zinc of 99.9 per cent purity to which 1 per cent of copper and 0.01 per cent of magnesium had been added.

Jan 1, 1934