Part IX – September 1968 - Communications - The Effects of Gold, Palladium, and Platinum on the Liquid-Gas-Solid Equilibrium in the Ag-O System

THIS communication reports the results of some work done on the effect of gold, palladium, and platinum on the liquid-gas-solid equilibrium in the Ag-O system,1,2 see Fig. 1. Recently several investigators3, 4, 5 have reported the effects of gold, palladium, platinum, and copper on the solubility of oxygen in liquid silver. This communication represents only a portion of the work done here on the solubility of oxygen in liquid silver and liquid Ag-Au, Ag-Pd, and Ag-Pt alloyss—the greater part having already been reprted. The apparatus, materials, and procedures used were similar to those of earlier work.' l The main precautions observed in obtaining these freezing points at constant temperature and PO2 = 1 atm were as follows: 1) The points were approached very slowly from higher temperatures. 2) In the very near vicinity of the L-G-S equilibrium point precautions were taken to see that the melt was in equilibrium with oxygen at one atm. Equilibrium was considered to have been attained when no more absorption of oxygen was observed in the last 15 min at a fixed temperature. 3) In the case of these alloys, the freezing point of the melt at 1 atm of oxygen and the equilibrium amount of oxygen absorbed by the liquid "infinitesimally" above this point were determined by lowering the temperature in very, very small steps, equilibrating at