Search Documents

By J. Handin

Triaxial compression tests with independently applied external confining pressures and internal pore pressures show that the ultimate compressive strengths of representative oil well cements are nearly linear functions of effective pressure — the difference between external and internal pressures on the jacketed cylindrical specimens (to 15,000 psi). The strengths are little affected by the test temperature to 350F (not to be confused with the curing temperature). At an effective pressure of 15,000 psi, strengths are in the rage of 30,000 to 50,000 psi, comparable to those of sedimentary rocks under similar conditions. The cements become very ductile even under low effective pressures; permanent shortenings of 30 per cent or more are attainable without rupture. INTRODUCTION Since the pioneering work of Richart, Brandtzaeg and Brown1 on the failure of cement under combined compressive stresses, it has been recognized that ultimate compressive strength is greatly enhanced by the application of confining pressure. More recently, Mc Henry2 showed that the strength of concrete was a linear function of the effective pressure (the difference between the external confining pressure on a jacketed specimen and the internal fluid pore pressure), at least for a range of 0 to 1,500 psi. The effect of temperature had not been investigated, and no previous systematic triaxial compression testing of naterials used for oilwell cementing seems to have been done. The present work was suggested by the late J. hi. Bugbee3 who stated that "consideration of the common application of high-pressure hydraulic fracturing to the initial completion or recompletion of wells, and the large pressure drawdowns in some producing wells, particularly those in abnormally high-pressure gas-condensate reservoirs, raises the question of what is a suitable cement strength for various completions. The intuitive belief exists that cement strength need be no greater than formation strength. Tests should, however, be conducted at downhole conditions." The ultimate compressive strengths of rocks penetrated by the borehole must rise several fold with increasing depth.4 This marked enhancement of strength is due to the influence of the effective pressure, the total weight per unit area of the overburden less the hydrostatic pore pressure. (The effect of temperature due to the geothermal gradients is relatively small for depths to 30,000 ft.) .A significant comparison of the strengths of rocks and cements at downhole conditions requires knowledge of the confined compressive strengths of cements as well. EXPERIMENTAL PROCEDURES The theory and technique of triaxial compression testing are fully discussed in earlier reports.4-6 Briefly, cylindrical specimens 1-in. long and 0.5-in. in diameter are jacketed in thin copper tubes of negligible strength, placed in the test chamber and subjected to an external confining pressure of kerosene and loaded axially by the piston at a strain rate of 1 per cent per minute. Pore pressures of water (or kerosene) are applied independently through the hollow piston and are maintained constant during the shortening of the specimen, Tests at sensibly 0 pore pressure are arranged so that any free water in the cement can escape to the atmosphere. (If egress of water were denied, pore pressure would rapidly attain the value of the external confining pressure because of reduction of pore space.) The test chamber can be heated for high-temperature experiments. Unless otherwise noted, the cement samples were air dried for about a week. Recorded during a test are pore and confining pressures, shortening and axial differential force (total force less the product of the confining pressure and the area of the piston). True stress-strain curves are constructed by dividing the measured differential force by the actual cross-sectional area of the specimen at a given

Jan 1, 1966

By J. W. Matousek, C. S. Samis

me thermodynamic properties of the components in the Cu-Ni-S ternary system have been studied by measuring the H2S/H2 ratios in a gas phase equilibrated with the molten matte at 1200°C. The measured sulficr potentials have been extended by extrapolation and combtned with previously published data to permit the thermodynamic analysis of the ternary system by integration techniques. A simplifying assumption of ideality in the Ni3Sz-CuS pseudobinary has been made. SINCE copper and nickel metals were first extracted from their sulfide ores the interaction between the two metals and sulfur has been of industrial and theoretical interest. The processes developed to extract copper and nickel have been reported periodically in the literature. The theoretical studies on the Cu-Ni-S ternary have been restricted to problems directly associated with production. It is only within recent years that the binary systems related to this ternary have been analyzed thermodynamically and mathematical devices developed to permit a corresponding treatment of the ternary system. In 1910 an investigation of the role of nickel in Cu-Ni-Fe-S mattes was reported,' It was concluded from this work that nickel is not an element replacing iron in mattes, but rather that Cu-Ni alloys behave as a single metal during the matte converting operation. The laws which govern the converting of Cu-Ni alloys were found to be the same laws as those that govern the conventional converting of copper alone. Although considerable information has been reported on the theoretical aspects of copper smelting, little data is available on the smelting of Cu-Ni ores except for phase diagrams and process descriptions. The available information on the Cu-Fe-S ternary and related systems prior to 1953 has been summarized by Ruddle.2 Since Ruddle's publication, Rosenqvist and coworkers have completed phase equilibria investigations of the Fe-S, Co-S, and Ni-S binaries,3 the Fe-S-O ternary,4 and the Cu-Fe-S-O quaternary.4 An extensive investigation of the Cu-Fe-S ternary system at smelting temperatures has been made by Krivsky and Schuhmann.5 At these temperatures, the Cu-Fe-S system is very similar to the Cu-Ni-S ternary with respect to the location of the single-phase and two-phase liquid matte regions. In the former, however, the area of immiscibility is more extensive and the region of liquid matte-liquid metal-solid metal equilibria is much more extensive. Krivsky and Schumann observed that the Cu2S-FeS pseudobinary system is, for practical purposes, an ideal mixture. This investigation has served as a valuable guide in analyzing the Cu-Ni-S ternary. EXPERIMENTAL The experimental procedure employed in this investigation was the conventional technique of equilibration of the sulfide matte with gaseous mixtures of hydrogen and hydrogen sulfide at 1200°C. The thermodynamic properties of sulfur (S2) in the gas phase are determined by means of Eq. [I] and the activity of sulfur in the matte by Eq. [2].

Jan 1, 1963

By L. O. Brockway, W. C. Bigelow, J. A. Amy

Specimens of Inconel-X alloy solution-treated at 2050°F and aged for periods of 1, 10, 100, and 1000 hr at 1200°, 1400°, and 1600°F have been examined by electron microscopy and by electron and X-ray diffraction. Four minor phases were identified: titanium nitride, niobium nitride, an M23C6 complex carbide, and the intermetallic ? phase. The two nitrides were found in all of the aged specimens and in the solution-treated alloy, the y' phase formed at all aging temperatures, while the M23C6 carbide formed only on aging at 1200° and 1400°F. Variations in the hardness, rupture strength, creep strength, and yield strength of the alloy have been shown to be related to variation in the size and distribution of the particles of the y' phase within the matrix grains of the alloy, with maximum values of these properties occurring when there is a maximum amount of the phase present and a fine state of dispersion of the particles prevails. THE nickel-chromium alloys containing titanium and aluminum are widely used in applications requiring high strength at elevated temperatures. Studies on relatively simple ternary and quaternary alloys'-4 have indicated that the favorable high-temperature properties of these alloys are related to the precipitation of an intermetallic ?'-phase having a structure based On that of the Ni3A1 phase of the nickel-aluminum system. The present investigation was undertaken to identify the minor phases and to study the microstructural changes occurring in one of the more complex commercial alloys as a result of aging in the service temperature range, with particular emphasis on investigating the role of the ?' -phase. The microstructural changes were studied by electron microscopy and the minor phases were identified by X-ray and electron diffraction. MATERIALS AND METHODS Inconel-X alloy was selected for this investigation because the previous studies of Frey, Freeman, and white6 provided extensive information on the variations in metallurgical properties of this alloy resulting from high-temperature aging treatments. Specimens aged 1, 10, 100, and 1000 hr at 1200°, 1400°, and 1600°F were made available for the present use. These were taken from 1-in. round-bar stock of a commercial heat having the following weight composition: 0.04 C, 0.56 Mn, 6.59 Fe, 0.007 S, 0.38 Si, 0.03 Cu, 73.22 Ni, 14.97 Cr, 0.78 Al, 2.38 Ti, and 1-02 Nb. They were solutjon-treated at 2050 for 4 hr and then water-quenched prior to aging. Powder X-ray diffraction patterns were obtained from insoluble minor phases which were separated from the alloys by digestion in the reagent of Mahla and Nielsen.6 Back-reflection patterns were obtained from electrolytically polished surfaces of the bulk search to detect the ?'-phase' Cu-K a radiation was used in both cases. In the electron-diffraction studies, the general method developed by Heidenreich, Sturkey, and

Jan 1, 1959

By E. Hein, R. A. Dodd

The fatigue softening of prior strain-hardened poly crystalline copper has been determined by measuring changes inflow stress resulting from fatigue treatments. Tensile fatigue does not soften the metal, while the softening due to reversed stress fatigue depends on the extent to which fully reversed stressing is approached. True tensile fatigue is shown to be possible only in the case of long wire specimens. Annealing following fatiguing of strain-hardened metal shows that tensile fatigue is very effective in modifying normal recovery and recrys-tallization. OBSERVATIONS by Ludwik and Scheu,' Kenyon,' Polakowski and Palchoudhuri, Kemsley, and Broom and Ham,596 have shown beyond doubt that strain-hardened metals are softened by reversed-stress fatigue. To some extent the softening might be associated with a rearrangement of dislocations, but the results of Broom and Ham5 on the temperature dependency of the fatigue hardening of annealed copper, and those of McCammon and Rosenberg7 on the partial recovery at 100'C of fatigue-hardened copper suggest that point defects may be involved. Since lattice vacancies are the only species of point defect present in appreciable quantities in thermody-namic equilibrium, most attention has been accorded them in the various theories advanced to explain hardening and softening effects resulting from fatigue. Precise mechanisms remain uncertain, and while some effects may be due to single vacancies, defects arising from vacancy clusters may also contribute to the changes in properties. All types of plastic deformation result in point-defect formation, one frequently invoked formation mechanism involving the nonconservative motion of jogs formed by the intersection of, for example, mixed dislocations. But since fatigue deformation is thought to be a particularly effective way of forming point defects, additional mechanisms peculiar to fatigue must be sought. One possibility is that jogged loops contract during the unloading cycle to give rows of vacancies. A local high-vacancy concentration could conceivably promote polygonization and recovery by climb, and, therefore, could explain the fatigue softening of strain-hardened metals under appropriate conditions of temperature. Conversely, the experiments by Broom and Ham6 on the fatigue hardening of copper single crystals involving subsequent tensile testing of previously fatigued specimens, resulted in the observation of distinctly lowered yield points. This could be due to vacancy atmospheres associated with dislocations, possibly augmented by jogs on dislocations. In addition to the yield-point phenomenon, a post-yield hardening was observed, with a temperature-dependence resembling the friction-hardening of irradiated metals,9 this again suggesting a point-defect mechanism. An important development in this field has been the observation,10 by transmission electron microscopy, of high concentrations of prismatic loops in fatigued aluminum. By analogy with quenched aluminum filmso11 it seems certain that these loops originate in the collapse of vacancy clusters formed during deformation. Metals, such as copper, having a relatively low-stacking fault energy would tend to produce Frank sessile loops (in practice tetrahedral defects with stacking faults on all (111) planes) rather than the glissile prismatic loops observed in aluminum. The manner in which these various defects affect the different aspects of fatigue behavior has not yet been fully investigated. The present work was designed principally to indicate whether tensile fatigue gives rise to hardening and softening effects similar to those associated with reversed stress fatigue, and with the hope of providing additional information on the contribution of point defects to fatigue deformation. Despite the uncertain ty often associated with the interpretation of resistivity data, i.e., the relative contribution of stacking faults and other defects, such measurements are conveniently employed to study point defect pheno-

Jan 1, 1962

By A. J. M. Ross, R. G. Wayland

The Homestake mine is situated in Whitewood mining district, in the northern Black Hills of South Dakota, in the city of Lead, Lawrence County. The entire property, comprising 557 lode claims with a total area of 3343 acres, is held under United States Patent. The older claims were 300 by 1500 ft. under local regulations, the newer ones 600 by 1500 ft. The Homestake was discovered April 9, 1876, by Moses and Fred Manuel, and Jake Harney, who were drawn into the northern hills, from the Custer placer district, by news of the discovery of rich placer deposits in Deadwood Gulch. They located a number of additional lode claims and, in a short time, the whole country was covered with locations. The Manuel brothers built an arrastre the following winter and took out $5000. The next year the Homestake lode was sold to Senator George Hearst and associates, who organized the Homestake Mining Co. Other companies were formed to exploit other groups of claims and at one time fivc companies were operating on this deposit, the Father DeSmet, the Dead-wood-Terra, the Caledonia, the Highland, and the Homestake Mining Co. These companies, however, have been merged into the Homestake Mining Company. The first stamp mill, known as the "Eighty Mill," commenced operation on July 12, 1878, and production has been nearly continuous since that time. Geology The orebodies of the Homestake are found in an intensely folded and altered bed of dolomitic limestone occurring in a series of ancient rocks believed to be of Archean age, belonging to the Keewatin series. The Keewatin series is estimated to be 20,000 ft. thick and is made up essentially of quartz mica schists, garnet schists, quartzites, slates, and some green schists, probably derived from basic igneous rocks. The dolomitic limestone bed has a thickness of 40 to 60 ft. The great width of ore, as much as 400 ft. in some of the stopes, is due to the folding, wherein the bed is repeated. In other cases the bed is stretched and pinched out. Dikes of Tertiary rhyolite cut across the country and, in places, sills overlie the

Jan 1, 1925

By R. A. Swalin, A. H. Geisler

THIS study represents an investigation of the effect of annealing temperature on the texture of drawn molybdenum, iron, and an iron alloy containing 14 pct Al. The effect of temperature on annealing textures has not been widely investigated in the past. One of the obstacles in making such a study using usual X-ray diffraction techniques results from the

Jan 1, 1957

By Marc Lemieux

Computer pit design techniques generally make use of models in which the deposit is represented by a regular array of data. Using a regular system, the number of data points required to represent the air, waste and mineralization in a large deposit become excessive. The number of blocks used to describe the deposit is dependent upon the block size. The quality of the pit wall slope design also is dependent upon the block size used and the method of defining the slope. The error associated with reserve calculations becomes greater with increasing block size. A deposit model consisting of variable sized air and mineralized blocks has been developed at the University of British Columbia and improved upon at Climax for pit design work. The method permits put- ting the entire model in core for rapid data processing. This permits the use of a versatile cone generation technique which allows close adherence to variable slope constraints in all directions. The conical shape is approximated by rectangles on each level which equal the area of the ideal conical intersection. The shape of the intersection may vary from approximately circular to elipsoidal. The approximate cone shape is controlled by the slope constraints applicable at the point of intersection on the bench. The overall modeling technique greatly assists the pit design engineer in developing a high quality pit design.

Jan 1, 1977

By T. D. Yensen, N. A. Ziegler

AGING is a term that connotes a slow change in properties under ordinary operating conditions. It can be accelerated by increasing the temperature and by mechanical straining. The magnetic properties of iron and some of its alloys have for many years been known to be subject to such a change. But the cause of the change was not recognized until a few years ago after mechanical age-hardening in nonferrous alloys of the "duralumin" type had been definitely shown, by means of solid solubility curves, changes in electrical resistance and microanalysis, to be caused by slow precipitation of one or more constituents from the solid solution. The similarity between the solid solubility curves of such alloys (Fig. 1) and those for iron-nitrogen (Fig. 2) and iron-carbon alloys (Fig. 3) below the Al transformation point suggested at once that magnetic aging of iron might be caused by a similar process; namely, by the slow precipitation of carbon and nitrogen in the form of Fe4N and Fe3C at ordinary temperatures because of a cooling rate that had been too rapid to permit complete precipitation according to equilibrium conditions. This suggestion has since been amply confirmed, particularly by the comprehensive work of Köster1 on the effect of nitrogen and carbon. Typical curves are shown in Fig. 4 for the relationship between aging temperature and coercive force. Previous to the establishment of the precipitation-hardening theory it was thought that the effect of nonmetallic elements like C, N, 0, etc., on the magnetic properties of iron was greatest when these elements were retained in solid solution, atomically dispersed throughout the interstitial spaces of the iron lattice2.

Jan 1, 1935

By William E. Souder, Eugene R. Palowitch

INTRODUCTION The longwall method of mining coal underground is now a highly developed and accepted mining technology. However, it was only through a long history of successes and failures that this technology now has the potential for reversing the declining trend in underground mining productivity in the United States. From its early beginnings in the United States during the 1800's, several species of longwalls have evolved. The evolutionary record consists of a series of overlapping birth-death eras, with each era giving way to another unique longwall technology. Typically, an era begins when some new longwall technology appears in response to a new technical opportunity or economic need. This new technology is adopted initially by only a few innovators. Later, other imitators get on the bandwagon and the technology diffuses throughout the user population. But evolving technical demands and socio-economic circumstances eventually cause many of the adopters to discontinue its use. This paper chronicles seven eras in the history of the evolution and utilization of longwall technologies in the United States. Some of the important factors that have influenced this history are discussed. Some distinctions are drawn between the operators who were first to adopt longwalls (innovators), and the imitators who followed. Statistics are presented which show that longwall mining is being adopted at an exponentially increasing rate, substantiating the forecast for a significant number of new longwall installations in' the future. Potential barriers to this increased utilization of long- walls are noted.

Jan 1, 1981

Henry C. Carlisle: This is a husband-and-wife act, in which Mary Carlisle is going to listen, and break in as often as she feels like it. I am going to describe my career as a mining engineer. We are at Nantucket, in the 75 Main St. house; The year is 1959. Q: This is something the boys and I have wanted you to do for a long time. Carlisle: After leaving Columbia in 1910, I arrived at Ray, Ariz., January 1, 1911, and rustled a job from Louis Cates, Ralph Nowland and Sprott Boyd, who were running the Ray mine. I went to work as a surveyor's helper, made $90 a month, and paid $35 a month board. I lived in a dormitory where about 25 other engineers, graduates from different colleges, were living. It was very social and you made a lot of young friends early in the game. I did not think much of the idea of being a surveyor, or even a surveyors, helper; the higher-up surveyors only got $125 a month, and had been there quite a long time. So, I asked to be changed to underground sampling, where I would see the mine faces every day and learn more about mining. In about three months, I became an underground sampler and remained at this for a year, but in three months I was promoted to head sampler, with six people under me.

Jan 10, 1963

By S. E. Bronisz, J. O. Brittain

Experiments have been carried out to study the effect of an applied stress on strain aging in steel. It was found that the stress-induced strain aging reaction proceeds rapidly in the temperature range of 0° to 60°C. The variation of stress-induced strain aging with plastic strain, aging time, and temperatures is reported. The activation energy for the stress-induced strain aging was found to be 10,000 cal per mol for the steel used in this investigation. VARIOUS observations1-5 have been made of the influence of an applied stress upon the yielding of iron and steel. However, there have been only cursory studies of the effect of an applied tensile stress upon strain aging in iron and steel1,2 The following represents the results of a preliminary study of strain aging as influenced by the application of an external tensile load during the aging process. For the most part, previous experimental work on strain aging can be classified into two parts. First, the experimental technique involved a direct determination of mechanical properties of a suitable specimen that has been plastically deformed to a constant strain and aged generally at a temperature of the order of 200°C, with the aging times varying from about 1/10 to 2 hr.6-8 The second classification of strain aging experiments involves an indirect determination of strain aging by means of physical property such as electrical resistivity or internal friction as a function of the aging time at a constant temperature and strain.9-12 The latter results have

Jan 1, 1961

By J. H. Ffolliott

ALL, of the prospects that later became mines in the Ducktown district were discovered prior to 1854, and most of them were exploited before the turn of the century. It is the purpose of this paper to discuss the exploration and current development of the Boyd mine, discovered in 1853. It is in the heart of the Ducktown Basin, in the extreme southeast corner of Tennessee, and is being developed by the Tennessee Copper Co. GEOLOGY The geology of the district has been fully described in many papers. Probably the most complete description is that of Emmons and Laney.1 The rocks of the district are considered to be of Lower Cambrian age and are a part of the Great Smoky formation, consisting mainly of interbedded graywacke and mica schist, in which the ore deposits occur. The ore bodies are included in an area of about 6 sq. miles, 2 miles wide and 3 miles long striking N. 45° E., and may be grouped into three general lode systems. The northeast system, including the East Tennessee, London and Burra Burra ore bodies, and the southeast group, comprising the Polk County, Mary and Calloway deposits, are all characterized by relatively high copper values. The ores of the central system, which includes the Eureka, Boyd, Old Tennessee and Cherokee ore bodies, are low in copper and high in total sulphide content. Boyd mine lies roughly halfway between the Old Tennessee and Eureka ore bodies [ ] and 2500 ft. in the hanging wall of the Burra Burra mine (Fig. 1). Elevation of the surface is about 1725 ft. above sea

Jan 1, 1942

By C. W. Vaupell

THE Huitzuco mines lie in north central Guerrero, Mexico; production has been about 90,000 flasks of quicksilver since 1873. Near-surface ores fill extinct mud geysers and the deep deposits are chambered veins, stock-works in brecciated blocks, and replacements in limestone. The epigenetic minerals livingstonite, stibnite and sulphur occur in limestone, gypsum and dolomite through a developed vertical range of 260 meters. The deepest workings expose an increased amount of stibnite, which probably indicates that the lower limit of mercury mineralization is being approached. A resur-gence of heat and water formed geysers over an extended area after the period of mercury mineralization. Mud geysers, which are situated, in the outcrops, contain the secondary mercury minerals, cinnabar and barcenite in the gravel and mud filling the vents. A 150-ton flotation plant is in operation concentrating stope fills that assay 3.0 kg. of mercury per ton. In one open stope, which is more than one hectare in area and 60 m. high, 150,000 tons are available.

Jan 1, 1937

By M. K. Barnett

[ ] ENGINEERING research consists, broadly speaking, in the investigation of the effect of the variations in a number of factors on some property of a product or characteristic of a process. The unambiguous description of the product or process requires that the property or characteristic be expressible in quantitative terms. For the purpose of practical control, it is likewise desirable that the independently variable factors governing the product or process be quantities, although this ideal goal is not always attained. Maximum efficiency-i.e., the attainment of the maximum amount of reliable, useful information relating to the influence of the factors on the property of the product or characteristic of the process, for the least expense-is an important requirement for the satisfactory operation of a research organization. Obviously, a necessary condition for the attainment of maximum efficiency is an adequate knowledge of the specialized field in which the experimental research lies. While necessary, this condition is not sufficient. Proper attention must also be given to the general principles of experimental design together with the modem methods for the analysis and evaluation of experimental data. The present discussion is confined to a single design, the so-called "factorial" design. This design is of special interest in that it attains its goal, maximum efficiency, by directly departing from the

Jan 1, 1947

By P. G. Shewmon, H. E. Collins

A study has been made to determine the sites at which sulfur adsorption occurs on copper surfaces. measurements were made of the relative torques, Ys, at the intersection of twin boundaries with surfaces near the three low-index orientations, i.e., (100), @lo), and 011), over a range of H2S/H2 ratios. HZS concerztvations j'ro~n 3 to 1500pp)n between 830" and 1050°C were used. It is concluded that sulfur adsorption occurved preferentially though not exclusively at edge sites near the (100) and (110) surfaces in the HzS range — 700 Ppm giving rise to negative torques near these orientations. Beyond this HzS range, adsorption occurred at all sites. Near the (111) surface, 7/y little with HzS concentration up to approxiwzately 75pptn. Above this range, the results indicate adsorption is occurring OH both terrace and edge sites. SCIENTIFIC interest in surfaces and their interactions with a gaseous environment dates back to the beginning of the 19th century. The scientific luminaries of that period—Faraday, Maxwell, Rayleigh, Dewar, and Gibbs—were already concerned about such processes. However, it has only been within the past several decades that adsorption on metal surfaces has been actively studied. This increased interest in adsorption has been brought about by the advent of new and improved experimental techniques and apparatus, e.g., ultrahigh vacuum, and field-emission and ion microscopes. However, most of the work done using these techniques has been carried out at low temperatures. When adsorption studies have been made at either low or high temperatures, they usually gave no indication of the particular surface orientations or type of sites on which adsorption was occurring. In the last few years, there have been a series of studies in which the surface tension, y,, and/or its derivative with respect to orientation, 7, have been studied as a function of orientation and atmosphere.'-7 Nearly all of the work on the relative torque,* ~/y, silver annealed in hydrogen and air.6 Recently Winterbottom and Gjostein" have used a modified and more accurate Mykurian method to determine the y plot of gold in hydrogen The only work in which T/~, has been measured over a range of chemical potentials for a given solute, p2, is that of Robertson and shewmon7 on the Cu-0 system. They measured T/Y, vs Po, (10"" to 10- l3 atm) at 1000°C in various mixtures of Hz0 and HZ. From this work they estimated the value of p2 at which one half of the surface sites are occupied with oxygen, pg, as being in the range 10- l6 to 10- l5 atm of oxygen. They also found that increasing Pa increased the magnitude of ~/y, near the (111) and (100) orientations. This indicates that oxygen is not adsorbed preferentially at step edges, but uniformly over all surface sites. In addition, they did one experiment on sulfur adsorption on copper surfaces, which indicated that sulfur adsorption decreases ~/y, near the (100) orientation, while not affecting ~/y, near the (111). This could be interpreted as indicating that sulfur adsorbs preferentially at step edges near the (100). In this paper the primary objective of the work has been to carry out a study of sulfur adsorption on copper surfaces over a range of temperatures and p,. In conjunction with this work, thermal grooving at grain boundaries has been examined as a method of determining the effect of sulfur adsorption on y,. METHODS Ideally, one would like to have information on the quantity of solute adsorbed on a surface and the types of sites at which it is absorbed as a function of p2. The total quantity adsorbed or the surface excess is given by the thermodynamic equation Thus data on the variation of y, with pz indicates the value of p2 at which adsorption becomes appreciable and the quantity adsorbed. The type of adsorption site is more difficult to deduce but information on this can be obtained from the variation of rz with 8, the angular deviation of the surface orientation. This is obtained from the thermodynamic equationlg Data on t and ys as functions of p2 have been obtained by the following methods. 1) Twin Boundary Grooving—By determining the effect of adsorption on the torque, 7, where T is the variation of surface energy, y,, with orientation, it is possible to obtain some indication as to the preferred sites of adsorption. Experimentally, the torque value measured is the relative torque, 7/ys The twin boundary grooving technique suggested by Mykura'' was used in this study to determine near the three low-index orientations— (loo), (110), and (111). Mykura's equation relates 7 /yS to measurements of the di-

Jan 1, 1967

By W. A. Backofen, D. L. Holt

Push-pull fatigue tests have been carried out at 4.2°K, 77oK, and room temperature on two poly crystalline materials of widely different stacking-fault energy (?): pure copper (? - 70 ergs per sq cm) and the Cu-8 wt pct A1 alloy (? - 2.8 ergs per sq cm). Constant stress-amplilude was imposed and measurement was made of the plastic-strain amplitude (ep) at saturation. Lives extended from 104 to 106 cycles. Designating lives at the various temperatures by NRT, N77, and N4.2. the ratios N77/NNT and N4.2/N77 ranged from 3.5 to 18 under the condition of common Ep . Metallo-graphic examination revealed different crack morphology in Cu-8 Al fatigued at room temperature, and at 77" and 4.2oK. At room temperature, cracks lay in or near grain and lain boundavies; at 77o and 4.2oK. cvacks were transcrystalline. Tests on single crystals of Cu-8 A1 showed that such a change in the cracking mode in polycrystallitle material accounted for a factor of- about 3.25 in N77/NRT . The longer life at lower tewperatztre (conslant cp) has heels attributed to two deuelopinents: a reduced production of the dislocation tangles and subgrain boundaries which serve as paths of rapid cracking, and suppression of oxygen chetni-sorption at the crack tip It was concluded that in both materials the luller accounted for an extension of the life at 4.2oK beyond that at room temperature by a factor of 15. XV ECENT experiments on the fatigue of Cu-A1 alloys in the so-called high-cycle range (greater than lo4 cycles) have emphasized the importance of stacking-fault energy (y) as a quantity affecting crack propagation rate and fatigue life.1,2 It was found in comparisons at essentially fixed plastic-strain amplitude that crack growth rate decreased by a factor of about 5 over the composition range from copper (? - 70 ergs per sq cm) to Cu-8 wt pct Al (? - 2.8 ergs per sq cm). The argument was made that, when stacking-fault energy is high, cross slip and climb are favored, so that dislocation tangles and/or subgrain boundaries form more readily under cyclic loading. Since the boundaries and tangles act as paths of rapid crack propagation ,3, 4 life is shortened as a result. However, when stacking-fault energy is reduced (as by alloying), cross slip and climb become more difficult, with the result that substructure formation is retarded and growth rate is also reduced. A purpose of the present work was to investigate the substructure effect in relation to temperature. As temperature is lowered, ? is varied only slightly (if at all), but decreased thermal activation can interfere with cross slip and climb. Thus substructure formation could be curtailed and life increased. Fatigue life in the high-cycle range is also known to be strongly influenced by environment. Working with copper, Wadsworth and Hutchings observed that life in a vacuum of 10-8 mm Hg exceeded life in air by a factor of 20.5 They isolated oxygen as the agent that furthered cracking. While the details are still unclear, a requirement in any mechanism of oxygen-accelerated cracking is that there be chemisorption at the crack tip. That could prevent welding on the compression half cycle,= interfere with reversal of slip,1, 6 or aid in breaking metal-metal bonds at the crack tip.5'7 In the work being reported here, temperature was lowered by immersion in liquid nitrogen and helium, which also served to reduce both the oxygen concentration and chemisorption rate. A possible effect upon life, i.e., a lengthening, had to be recognized. Several researchers have determined fatigue lives at low temperatures presenting their results in the form of stress amplitude (S) vs cycles in life (N) curves.8-11 Such curves reflect, primarily, the fact that metal is strengthened by lowering temperature; effects of substructure and changing environment tend to be masked. The difficulty can be overcome by comparisons based on identical plastic-strain amplitudes, and in the present work the dependence of life on both plastic strain and stress amplitude was established. EXPERIMENTAL Materials. The principal materials were polycrystal-line copper (? - 70 ergs per sq cm)" and the Cu-8 wt pct Al alloy (? - 2.8 ergs per sq cm),I3 the latter being near the limit of solubility of aluminum in copper and having, therefore, the lowest stacking-fault energy in the CU-Al system. Specimens were machined from 0.118-in.-diam cold-swaged rods of high-purity (99.999 pct) copper and the Cu-8 Al alloy, the latter produced initially in a graphite boat by induction vacuum melting a mixture of 99.999 pct Cu and 99.99 pct Al. The machined specimens were annealed to produce mean grain diameters of about 0.070 mm in copper and 0.190 mm in the alloy. Specimen dimensions are given in Fig. 1. Values of the tensile yield stress, ultimate strength, uniform strain (determined by the Considgre construction), and reduction of area, for both materials at 4.2oK, 77oK, and room temperature, are listed in Table I. The tensile apparatus in which these results were obtained has already been described.14 Apparatus. Specimens were fatigued in push-pull with a machine that is illustrated schematically in Fig. 2. The specimen is first soldered into the top grip (1) with Woods metal, and the grip is then screwed into the inner tube (2) which is connected to the drive rod of the Goodmans vibration genera-

Jan 1, 1968

By A. L. Mincher, W. F. Sheely

Mechanical properties of columbium have been studied over the temperature range of -196 to 1093oC. The decreased strengthening influence of cold-work at temperatures below ambient has been interpreted in terms of the Peierls-Nabarro effect. Maxima in the rate of strain hardening observed during tensile testing in the range 250-600°C. have been correlated with interstitial impurities to indicate the temperature ranges at which carbon, oxygen, and nitrogen, respectively, are responsible for strain aging. THE growing need for structural materials for use above the useful service temperatures of the iron-, nickel-, or cobalt-base alloys has caused the refractory metals to be considered as potential engineering materials. These metals, which include columbium, tantalum, molybdenum, and tungsten, are called refractory because the lowest melting point among them,that of columbium, is about 1000°C higher than the average melting temperatures of conventional high-temperature alloys. They are all body-centered cubic transition metals and, as such, their mechanical properties have basic characteristics which distinguish them from the face-centered cubic metals. For example, all show a much steeper rise in strength with decreasing temperature below room temperature than do the face-centered cubic metals, and their mechanical properties are strongly influenced by interstitially dissolved impurities. In order that these new metals may be used efficiently, it is necessary that their characteristics of behavior be fully known. In this paper, the mechanical properties of columbium will be examined over a wide range of temperatures. In particular, the influences of cold-work and individual species of interstitial impurity atoms on mechanical properties will be described, and basic mechanisms which may control the observed characteristics will be explored. EXPERIMENTAL The material used in this investigation was Union Carbide Metals Co. columbium roundels consolidated to four 4-in. diam ingots, three by consumable-electrode arc melting and one ingot by electron beam melting. Impurity contents of the ingots and methods of ingot conversion and treatment are summarized in Table I. The only metallic impurity occurring in any significant quantity was tantalum at about 0.1 pct. Iron, silicon, titanium, and zirconium were each less than 0.015 pct; boron was 1 ppm or less. This should have no appreciable influence on properties. The electron beam melted material, being the purest, will be used as the basis for comparison in the discussions to follow. Tensile tests were conducted from-196 to 1093oC, on both cold-worked and fully recrystallized arc-melted and electron-beam melted columbium using standard 1/4-in. diam, 1-in. long gage length test specimens. A strain-rate of 0.005 in. per in. per min was employed until the 0.2 pct yield strength was achieved and then the strain-rate was increased to 0.05 in. per in. per min for the balance of the test. Samples were protected in an inert atmosphere at tests above 300°C. The tensile properties obtained on the electron-beam melted columbium, E, in both the cold-swaged and recrystallized conditions are given in Fig. 1. The yield strength data of Dyson, et al.,' obtained on recrystallized electron beam melted columbium and the tensile strength data reported by Tottle2 on powder metallurgy columbium are included in Fig. 1. The material used by Tottle had been purified by vacuum sintering. There is excellent agreement between Dyson's data and those obtained in the present investigation. The tensile strengths obtained by Tottle were slightly greater than those obtained in this investigation on electron-beam melted columbium but varied with temperature in a similar manner. Tottle's data showed a maximum in tensile strength near 500°C, as did our data on electron-beam melted material, and also showed a small maximum at 300°C. The significance of these maxima will become evident later in the discussion. The tensile properties of cold-swaged and recrys-tallized arc melted columbium are plotted in Fig. 2. It was found that the properties of the recrystallized arc-melted columbium from all three heats showed very close agreement except at temperatures between about 500" and 800°C. A reason for this range of disagreement will be suggested in the discussion. The generally good agreement, however, attests to the ability of cold-working and subsequent recrystal-lization to erase the effects of the three different primary breakdown procedures and to produce nearly equivalent structures in the samples derived from the three different heats. wesse13 reported tensile data on columbium having interstitial impurity contents between those of the

Jan 1, 1962

By G. Derge, Ling Yang, G. M. Pound

The specific conductance and its temperature dependence were measured over the entire composition range of the molten Cu2S-CuCI system. At a typical temperature of 1200°C, 10 rnol pet of the ionically conducting CuCl reduced the specific conductance from about 77 ohm-lcm-l for pure Cu2S to about 32 ohm -1cm -1, and 50 mol pet CuCl reduced the conductance to that for pure CuCI—about 5 ohm 1cm1. The nature of electrical conduction in molten Cu2S, FeS, CuCI, and mixtures was studied by measuring the current efficiency of electrolysis at about 1100°C. The Cu2S, FeS, and mattes were found to conduct exclusively by electrons, but addition of 1 5 wt pet CUS to Cu2S produces a small amount of electrolysis. Addition of CuCl to Cu2S suppresses electronic conduction, and ionic conduction reaches almost 100 pet at a CuCl concentration of about 50 mol pet. These facts are interpreted in terms of electron energy level diagrams by analogy to the situation in solids. RESULTS of electrical conductivity studies on molten Cu-FeS mattes as a function of composition and temperature have been reported.' The specific conductances ranged from about 100 ohm-' cm-' for pure Cu2S to 1500 ohm-' cm-1 for pure FeS. This is in sharp contrast with the low specific conductance of molten ionic salts for which the transfer of electricity is by migration of ions in the field. In general, these ionically conducting molten salts, such as NaC1, KC1, CuC1, etc., have a specific conductance of the order of magnitude of 5 ohm-' cm-'. It was concluded on the basis of this evidence that molten FeS and Cu,S exhibit electronic conduction. Pure molten FeS has a small negative temperature coefficient of specific conductance, resembling metallic conduction, while pure molten Cu2S has a small positive temperature coefficient, resembling semi-conduction. The molten Cu2S-FeS mattes follow a roughly additive rule of mixtures, both with respect to specific conductance and temperature coefficient. Savelsberg2 has studied the electrolysis of molten Cu2S and Cu2S + FeS. He concluded that while molten Cu2S is an electronic conductor, there is some ionic conduction in molten Cu2S + FeS3 owing to the formation of the molecular compound 2Cu2S.FeS and its dissociation into Cu1 and FeS2-1 ions. The present work does not verify his results. Chipman, Inouye, and Tomlinson" have studied the specific conductance of molten FeO and report a high specific conductance, about 200 ohm-1 cm-1 of the same order of magnitude as that found for molten mattes, and a positive temperature coefficient. They interpret these results in terms of p-type semiconduction in the ionic liquid by analogy to the situation in solid FeO.1 imnad and Derne' detected appreciable ionization in molten FeO by means of electrolytic cell efficiency measurements. In order to verify the conclusion that electrical conduction in molten Cu2S and mattes is electronic, and to gain further insight into the structure of molten sulfides, the following investigations were carried out in the present work: 1) The specific conductance, s of the molten system Cu2S-CuC1 was measured as a function of temperature over the entire composition range. As discussed later, molten CuCl is an ionic substance. It was thought that if molten Cu2S were simply ionic in nature, addition of small amounts of CuCl might not have a catastrophic effect in lowering the high conductance of the Cu2S. On the other hand, if much electronic conduction occurs, addition of the ionic CuCl should have a large effect in destroying the electronic conduction. 2) The electrolytic cell efficiency of the following molten systems was measured at about 1100°C in specially designed cells: Cu3; Cu2S + FeS, 50:50 by wt; FeS; Cu2S + CuS, 15 wt pet; Cu2S + CuC1, 5.9 to 46.4 mol pet; and CuC1. This gives a direct measure of the fraction of current carried by ions in these melts. Further, the cell efficiency, extrapolated to zero ionic current, is given by cell efficiency = (s leasile + s elexstronic). [1] s lucile for molten CulS would be expected to be no greater than that for molten CuC1, whose s lonle is about 5 ohm-' cm-1, as will be seen in the following. u,.,,.,.,.......for molten Cu,S is of the order of 100 ohm-' cm-'.' Thus, a large increase in cell efficiency from 0 to values of 10 to 100 pet upon addition of CuCl to Cu2S would indicate destruction of the electronic conductance. Conductance Measurements Experimental Procedure—The apparatus and experimental method were the same as those described in detail in connection with the study of electrical conduction in molten Cu,S-FeS mattes.' A four terminal conductivity cell and an ac poten-

Jan 1, 1957

By W. D. Forgeng, R. L. Folkman, D. C. Hilty

The solubility of oxygen in molten Fe-Cr alloys has been determined at 1550° , 1600°, and 1650°C for alloys containing up to alloyshasbeenabout 50 pct Cr and found to decrease as chromium increases to 6 pet and then to increase gradually. Phase relations in the Fe-Cr-0 system at steelmaking temperatures have been evaluated and two previously unreported oxides have been identified. OPERATIONS in the melting and refining of chromium steels are dependent to a major degree on the reactions of chromium and iron with oxygen and are primarily directed toward controlling and modifying these reactions to secure maximum advantage in the utilization of chromium. Although fairly effective practices have been developed empirically, understanding of the specific reactions is limited. Moreover, the ability of molten steel to dissolve oxygen that subsequently precipitates as oxide inclusions during solidification is well known, so that clarification of the effect of chromium on the nature and mechanism of formation of these inclusions is desirable. Study of the problem indicated that increased knowledge of the fundamental Fe-Cr-0 system is essential to further technical and economic improvement. Consequently, an investigation of the influence of chromium on the solubility of oxygen in molten iron and of phases and phase relations in the Fe-Cr-0 system was undertaken at the Metals Research Laboratories of the Electro Metallurgical Co. as part of a general program on the effective utilization of chromium in chromium steel production. Experimental Procedure All of the experimental runs made during this investigation were carried out in the rotating crucible induction furnace which has been described in detail in a previous publication.' In review, the principle underlying this furnace is that rotational forces in the crucible cause the molten metal to assume a concave shape in such a manner that the slag is contained in the molten metal cup, thereby minimizing slag/crucible contact and subsequent reaction. Practically all of the heats were melted in commercial-quality magnesia crucibles of the type usually furnished for laboratory induction furnaces. All of the runs were made under an argon atmosphere after the furnace chamber had been degassed. Bath temperatures were controlled by Pt—Pt-10 pct Rh thermocouples. The basic furnace charge consisted of a premelted 12 to 15 lb electrolytic iron slug which had been cast to a shape convenient for fitting into the rotating furnace crucible. A typical analysis of the electrolytic iron slugs is given in Table I. For certain runs, it was desirable to melt down charges containing high initial chromium contents. In these cases the chromium was added to the electrolytic iron during the premelting operations. Chromium was added to the rotating furnace bath in the form of electrolytic chromium of the analysis given in Table 11. In all of the constant temperature runs, the standard procedure was to melt down the electrolytic iron or alloy slug under vacuum, admit argon to slightly greater than atmospheric pressure, and adjust rotational speed to develop a well formed "cup" on the bath surface. The melt was then saturated with oxygen by an addition of ferric oxide and the temperature of the bath adjusted to within +5°C of the desired level. At this point the heat was permitted to come to equilibrium prior to sampling or further addition. This time interval was varied from 15 min to 2 hr but generally was about 20 min. After sampling, the desired chromium addition was made and the bath again equilibrated prior to subsequent sampling. This cycle of addition and sampling continued for the duration of the run which lasted from 4 to 8 hr. At the end of this period, power was shut off and the bath allowed to solidify in the furnace. Quenched metal samples were taken from the equilibrated melts by means of the "Taylor sampler" which has been described by Taylor and Chipman.' Before being submitted to chemical analysis, all samples were carefully examined for surface slag occlusions and cold shuts. Later in the study, each sample was radiographed and examined metal-lographically in cross-section to determine the presence of internal defects. On the basis of these examinations, sound and apparently clean specimens were selected from the Taylor samples for chemical analysis.

Jan 1, 1956

By H. D. Outmans

The paper presents a theoretical approach to the drilling problem based on rock mechanics and drilling fluid hydraulics at the bottom of the hole. The volume of the fractured rock around the vevtically penetrating bit tooth is expressed as a function of the tooth pressure, included tooth angle, drilling fluid pressure and formation characteristics on the assumption that fracturing is preceded by plastic flow. This assumption is verified by comparing the stress-strain state in the rock around the tooth to that in equivalent tri-axial compression tests described in the literature. An expression similar to the above is derived for the tooth penetration in the cuttings which have been retrained at the bottom. Combination of these two expressions leads to a relation between depth of tooth penetration in the virgin rock, the amount of cuttings retained and the other variables. By relating the cutting volume to the drilling rate, the hydraulic bit horsepower and the drilling fluid pressure, it is possible to arrive at formulas which express the drilling rate for viscous or turbulent flow at the cutting surface, for instant clearance, for retained cuttings, or for false tooth foundering as functions of such variables as the drilling fluid pressure, hydraulic horsepower at the bit, rotary speed and bit weight. Plotting the results as drilling curves and comparing them to published field and laboratory data justify the conclusion that the drilling model presented in this paper approximates the actual mechanism. The drilling curves serve to explain some characteristic features of the rotary drilling operation, and the equations may be used for numerical evaluation of the effect of changes in the magnitude of some of the variables on the drilling rate. INTRODUCTION Published laboratory data have established that consistent and relatively simple relations exist between the drilling rate and any one of the important variables. For instance, the drilling rate usually increases at an increasing rate with the bit weight. It increases at a decreasing rate with the rotary speed, decreases at a decreasing rate with increased drilling fluid pressure and plots as an S-shaped curve against the hydraulic horsepower at the bit. This relative simplicity seems difficult to understand considering that the drilling mechanism is a continuous process of generation and removal of innumerable individual cuttings, under different conditions for each. On the other hand, the drilling rate (although determined by this complicated process) only expresses the average rate at which cuttings are produced and cleared away. Ignorance of the drilling mechanism as far as individual cuttings are concerned, therefore, does not exclude the possibility of arriving at a concept of the drilling rate provided the mechanism is properly evaluated for the average cutting. It then may be concluded from the first sentence that this concept also should be rather simple in its final form, although not necessarily in its derivation. Two aspects of the drilling mechanism are difficult to evaluate — (1) the effect a penetrating drilling fluid has on the stresses around a bit tooth entering the formation and (2) the volume of rock fractured by a penetrating tooth which moves both vertically and horizontally. Thus, the scope of this paper has been limited to an evaluation of the drilling mechanism in formations which have a low permeability and are drilled with hard-formation bits. In the following sections, the drilling mechanism is analyzed in three steps. First, the effect of tooth pressure on the volume of fractured rock around the tooth is evaluated, assuming initially that the bottom of the hole is free of cuttings and, then, determining the effect of a layer of these cuttings. In the second section, the thickness of this layer is related to the drilling rate and the chip clearance time, and the latter to the hydraulic horsepower at the bit under conditions of laminar and viscous flow at the cutting surface. In the third section. the previous results are combined with the rotary speed into drilling equations which are then plotted and compared to experimental drilling curves. This section also contains some numerical examples of drilling rate computations. Some mathematical details are given in the appendixes. Finally, it should be mentioned that, although some drilling equations are already available, these equations (with the exception of one' which attempts to relate drilling rate to drilling fluid pressure) are all mathematical expressions for observed laboratory data; none considers the effect of delayed drill-cutting removal, an essential feature of the drilling mechanism.