By Daojin Cao

The chemical components in the saturated aqueous solution of ammonium dimolybdate (ADM) were investigated at room temperature by comparative Raman spectroscopy. In order to explore the further detailed results, a new method of qualitative and half quantitative analyses, based on the main vibrant frequencies and the intensity ratio of the strongest peak to the second strongest peak recorded in Raman spectrum of saturated aqueous solution of ammonium heptamolybdate tetra hydrate (AHM), was put forward and attempted to analyze the chemical components of saturated aqueous solution of ADM. The results showed that there was obvious difference between Raman spectrum of saturated aqueous solution of ADM and that of ADM, but there were good relationships between Raman spectrum of saturated aqueous solution of ADM and Raman spectra of the three samples including AHM, the saturated aqueous solution of AHM and monomolybdate ion in aqueous solution. It was found that aggregated dimolybdate ion ({Mo2O72-}n)did not exist in the saturated aqueous solution, and was changed into heptamolybdate ion (Mo7O246-) and monomolybdate ion (MoO42-), which were in equilibrium each other, but the distribution ratio of heptamolybdate ion was larger than that of monomolybdate ion. In addition, Raman spectral pattern of saturated aqueous solution of ADM was reported.

Jan 1, 2006

By T. Kozuka, K. Sassa, S. Asai

"A new atomization process is developed. The principle of this process is completely different from that of conventional processes. This process uses electromagnetic energy induced by direct electric current and direct magnetic field instead of kinetic energy produced by fluid impingement or disk rotation.Experimental work of this process was carried out using pure tin, and it was found that the crucial factor for a stable operation is the contact state of molten metal with the electrode. In order to control the condition, a delay time controlling unit was developed and combined with this process. It is noticed that this controller works well to produce uniformly sized particles.A linear relation between the impulse and the momentum of atomized particles is found by use of experimental data and is explained by theoretical analysis.IntroductionIn atomization processes prevailing in metal powder technology, kinetic energy is currently employed for atomizing molten metal. That is, molten metal is broken into small particles by other fluid (e.g. water, argon gas, etc) or by impinged upon a rotating solid disk. This splashing process is always accompanied with uncertain factors for shape and size of the particles. The diameter distribution of products, therefore, comparatively spreads over a wide range. From another standpoint, the restriction of atmosphere is inevitable in some of these processes. As a pulverizing technology, the process which can produce uniformly sized particles and permits the choice of atmosphere is strongly desired.On the other hand, a great attention has been paid to the spray casting process as a new near net shape casting. In this process, a small size spraying device is favorable."

Jan 1, 1988

By Michael F. Kitto

The production of sulphuric acid at base metals smelters is predominantly an involuntary activity and now comprises approximately 17% of all-forms sulphur supply in world terms. The majority of elemental sulphur is also produced involuntarily in response to environmental regulations regarding emissions from hydrocarbon processing plants. The paper examines the points of similarity and difference in the sulphur and smelter acid markets, and reviews their interactions. The reasons for the merchant acid market collapse of 1993 are analyzed, and the prospects of a recurrence are considered.

Jan 1, 1996

By David C. Lynch

The molecular form of trace elements in matte has been shown to depend on the chemical potential of sulfur and the propensity of the trace element to form a sulfide. Of the four trace elements (As, Sb, Bi and Pb) arsenic and lead behave nearly as opposites, with lead readily forming a sulfide while arsenic forms complexes with free copper and ion in the matte. Antimony and bismuth both display the dissolution characteristics as As and Pb, suggesting that these elements dissolve in matte in multiple forms of significant concentration. While in the present investigation the dissolution characteristics of all four trace elements are examined, the primary focus is on the multiple dissolution behavior of Sb and Bi.

Jan 1, 1995

By Sang-Su Lee

This paper shows the application of the porous plug system in the Mitsubishi continuous copper smelting and converting process. This system has already been adopted and utilized in the steel industry to enhance productivity. Recently, some copper smelters have adopted this system but the results have not been satisfactory. The porous plug system was installed at the anode furnace in December 2001 to reduce the oxidation time and decrease the oil consumption. A good effect was that the nitrogen stirring of the melt through porous plugs improved the melt heat transfer. As the result of the enhancing heat transfer the oil consumption and the build up inside the furnace were actually decreased. But until now the oxidation time has not been sufficiently reduced. In the future, further research and tests are needed in order to increase the productivity and save costs.

Jan 1, 2003

By Sang-Su Lee

This paper shows the application of the porous plug system in the Mitsubishi continuous copper smelting and converting process. This system has already been adopted and utilized in the steel industry to enhance productivity. Recently, some copper smelters have adopted this system but the results have not been satisfactory. The porous plug system was installed at the anode furnace in December 2001 to reduce the oxidation time and decrease the oil consumption. A good effect was that the nitrogen stirring of the melt through porous plugs improved the melt heat transfer. As the result of the enhancing heat transfer the oil consumption and the build-up inside the furnace were actually decreased. But until now the oxidation time has not been sufficiently reduced. In the future, further research and tests are needed in order to increase the productivity and save costs.

Jan 1, 2003

By Frank Mucciardi, Hujun Zhao, Pietro Navarra

"A heat pipe is a device having a very high effective thermal conductivity in which two-phase flow and heat transfer takes place. Recent research at McGill University has led to a new type of heat pipe that contains a flow modifier. This improvement has enabled the device to operate at the high heat fluxes encountered in the metallurgical industry.This paper summarizes the progress made to describe the fluid flow in the evaporator section of a McGill heat pipe with the goal of understanding how the flow modifier configuration is linked to the film boiling and dry-out limitations. A separated flow model, an instability analysis, a lift-off model and an energy balance model are used to calculate the theoretical CHF with varying flow modifier configurations and operation conditions. A summary of the current work to relate the flow modifier to the dry-out limitation is also given.Determining how the flow modifier affects both the film boiling and dry-out limitation will give insight into improving the flow modifier design so as to extend the operational range of McGill heat pipes in terms of maximum heat flux and heat load capabilities.IntroductionThe McGill heat pipe is a specialized two-phase heat exchanger developed for several metallurgical applications where temperatures and heat fluxes are typically close to or beyond the maximum safe range of conventional cooling technology.Over the last few years, several breakthroughs have brought this device beyond the proof-of concept stage and a series of industrial trials have been performed with success. These trials include two oxygen injection applications for the ferrous and non-ferrous industry [l], and two light metals permanent-mould casting applications [2,3]. Current projects include a blast furnace copper taphole cooling application [4], a copper smelting application and a thermal analysis probe application."

Jan 1, 2004

By Alain Jardy, Valerio De Felice, Jean-Pierre Bellot, Ismael Lis Alves Daoud, Stephane Hans

"Gas-stirring ladle treatment of liquid metal has been pointed out for a long time as the processing stage mainly responsible for the inclusion population of specialty steels. A steel ladle is a complex three-phase reactor, where strongly dispersed inclusions are transported by the turbulent liquid metal / bubbles flow. We have coupled a population balance model with CFD in order to simulate the mechanisms of transport, aggregation, flotation and surface entrapment of inclusions. The simulation results, when applied to an industrial gas-stirring ladle operation, show the efficiency of this modelling approach and allow us to compare the respective roles of these mechanisms on the inclusion removal rate.IntroductionThe reduction of the weight of high performance materials together with the improvement of mechanical properties and the increase of the recycling of used metal are new challenges which emphasize the importance of metal cleanliness. Ladle treatment of specialty steels has long been described as the secondary metallurgical process mainly responsible for the non-metallic inclusion derived from the deoxidation process. The treatment is accomplished by blowing argon through one or more porous plugs for the purposes of desulphurization, minor composition adjustments, and inclusion removal. Gas injection is applied on routine basis to achieve both the stirring of the liquid bath (thermal and chemical homogenization) and the entrapment of the inclusions by the bubbles (flotation). Furthermore, the turbulence produced in bubble swarms enhances the probability of inclusion collisions and makes aggregation the first mechanism for particle removal. The physical processes involved in gas stirred ladles are numerous and complex owing to the three dimensional and multiphase (metal-gas and inclusions) nature of the reactor. Despite these difficulties, the population balance equations can be implemented in CFD code11'21 and combined CFD-PBM (computational fluid dynamics - population balance method) models are investigated for steel ladle processes13'41 and produce very promising results in terms of inclusion removal efficiency."

Jan 1, 2012

By T. Gunawansa, T. L. Alford, Zhao Zhao, A. R. Lanz, N. David Theodore

Many sustainability issues arise during the manufacturing processes that are currently used for solar cells. Solar energy is a renewable energy source that is independent of the earth’s resources, and it is therefore important for the development of more sustainable technologies. Microwave annealing (MW) has been proposed as a technically feasible fabrication scheme for large area silicon solar cells. Apart from that, microwave annealing has been demonstrated to be a promising alternative for repairing damage and electrically activating dopants in ion-implanted semiconductors for integrated circuit manufacturing. A microwave oven is cheaper than conventional furnace systems. In addition, microwave heating is much more efficient than conventional furnace heating, as heating is directly produced inside the material. This minimizes the loss of energy due to heating of the ambient. There is a need for more efficient processing techniques. In this study, microwave annealing is used as an alternative to the current postimplantation processing. Arsenic-doped silicon was microwave annealed (with an aluminacoated silicon carbide susceptor) to activate dopant atoms and to repair damage that was caused by ion implantation. Sheet resistance and Hall effect measurements were used to assess the extent of dopant activation. Rutherford backscattering spectrometry (RBS) with ion channeling was conducted to determine the extent of recrystallization. The dopant activation and recrystallization resulting from microwave annealing is compared with that resulting from conventional rapid thermal annealing (RTA) with the same heating profile. The results show that when compared to RTA, susceptor-assisted microwave annealing results in better dopant activation for shorter anneal times under the same heating conditions.

Jan 1, 2015

By Philip L. LeHoux

"Kennecott Barneys Canyon Mining Co. is a gold heap leaching facility that has been in operation since 1989. In 1994, a flotation plant was commissioned to remove sulphide minerals from refractory sulphide ore. Tailings from the plant are mixed with oxide heap leach material in order to produce a geotechnically stable agglomerate from which the gold is leached and recovered in a conventional heap leach cyanidation process. The experience to arrive at an effective blending methodology is discussed.IntroductionAgglomeration is the practice of binding fine particles to coarser rock or other fines in order to avoid the deleterious effects of mobilizing the fines during the course of heap leaching(l-Chamberlin). Agglomeration has been considered a key component of successful operation at many heap leach sites. If the ore is of sedimentary origin and crushed, there is a high likelihood that the resulting product will contain a significant quantity of fines and a skewed gradation, that i~, a disproportionate amount of coarse and fine particles, with few in the intermediate size range. The exact methodology for determining whether the practice of agglomeration will have to be integrated into the operating scheme has been well discussed. These conditions are primarily geotechnical and geochemical. This paper will deal with the specific experiences of Kennecott Barneys Canyon Mining Company in modifying the agglomeration practices to suit evolving operational requirements."

Jan 1, 1997

By Steve Johnston, Mowafak Al-Jassim, Fei Yan, Omar Sidelkheir, Alain Blosse, Katherine Zaunbrecher

"Imaging techniques are applied to multi-crystalline silicon wafers and solar cells throughout the production process. Photoluminescence imaging, both band-to-band and defect-band, is used to characterize defects and wafer quality at all process steps. These steps include bricks sawn from ingots, wafer sawing, cleaning and texturing, emitter diffusion, edge isolation and glass removal, anti-reflective coating/passivation, and metallization of finished cells. Bricks, wafers, and cells can be imaged at a rate commensurate with in-line measurement, giving spatial information to characterize quality and defect content. Photoluminescence images on silicon bricks can be correlated to lifetime measured by photoconductive decay and could be used for high-resolution characterization of material before wafers are cut. The defect areas in as-cut wafers are compared to imaging results from electroluminescence and lock-in thermography, and cell parameters of near-neighbor finished cells, showing correlations to efficiency, open-circuit voltage, and short-circuit current.IntroductionImaging techniques can rapidly characterize material quality and defect density. Photoluminescence (PL) imaging can be applied to silicon from the brick level to all wafer process steps [1-8]. At the brick level, material thickness allows for measurement and correlation to lifetime where surface recombination effects are minimized [6, 7]. At the as-cut wafer level where thin unpassivated wafers prevent accurate lifetime assessment due to surfaces, defects can still be categorized and quantified to predict finished cell performance [3-5]. Defect regions can be identified by recombination-limited band-to-band PL or by defect-band emission [9-12]."

Jan 1, 2012

By A. V. Tarasov

The high efficiency of autoclave processes is attributed to the fact that they are suitable for processing of refractory raw materials, have low capital costs and high productivity, ensure integrated utilization of the feed materials, produce innovative saleable products, completely eliminate any air emissions, provide low-waste or waste-less technology, as well as mechanization and automation of production processes. In the immediate future, it might be expected that autoclave processes will find use on commercial scale for production of heavy non-ferrous metals in combination with other processes (hydrometallurgical, upgrading, sorption and solvent extraction, electrolytic, etc.) to ensure: -Integrated processing of refractory ores and concentrates (pyrrhotite, zinc, copper-zinc, lead-zinc, nickel-cobalt, copper, pyrite); -Production of metallic powders of base metals as commercial products (copper, cobalt, nickel, etc.), composites on their bases, final products and saleable salts. Processing technologies incorporating autoclave processes, especially, at the stage of liberation (chemical upgrading) of minerals, are characterized generally by high overall recoveries of valuable constituents significantly exceeding recoveries common for conventional pyrometallurgical processes (for some elements by several tens of percent). An example is processing of low-grade refractory pyrrhotite concentrates using autoclave liberation of feed material under pressure of a new reagent, i.e., sulfur dioxide. The use of sulfur dioxide ensures a significant improvement in the recoveries of non-ferrous metals and platinoids to sulfide concentrate and smelting of the latter increases the capacity of the smelting units employed and minimizes the yield of discard slag and loss of metals in slag; in addition, it resolves the problem of sulfur dioxide utilization.

Jan 1, 2003

By Peter J. Hancock

The pyrometallurgical .processing of non-ferrous, complex materials and wastes will be surveyed. Pyrometallurgy offers the most versatile way of processing a large variety of such materials because of its high temperatures, closely-controlled oxidation potential and the availability of commercially-proven reactor configurations. Some current industrial applications will be reviewed and possible new applications as well as future trends will be outlined.

Jan 1, 1994

By C. Lupi

Zinc chloride electrowinning presents difficulties in obtaining smooth, compact and dendrite free deposits with a high current efficiency due to the presence of undesirable metal ions. However, it is hard to define a level of impurities tolerable in zinc deposition, and despite a lot of research in this field, the reaction mechanisms of the undesired metal ions are still not clearly understood. In this study, the influence of Fe, Cd, Co, Ni and Cu additions were investigated, as well as their synergic effect on the zinc electrodeposition process from chloride electrolytes and on the obtained deposit morphology. The tests were all performed in presence of TBACl which reduces the harmful effect of such impurities on the zinc reduction.

Jan 1, 2003

By P. Felix

A discussion on the need of visualization and animation tools in modelling solidification processes is made. An outline of an approach for the production of a video computer animation is provided. A number of examples including, 2 and 3 dimensional melting, filling, and macrosegregation are presented.

Jan 1, 1993

By Akira Yazawa

The composition of ferrous calcium silicate slag is located on the tie line between FeOx and calcium silicates in ternary FeOx-SiO2-CaO system. This slag has never been used as copper smelting slag because of high sulfidic copper solubility. However, when the dissolved copper in slag is just oxidic, as in direct white metal production or in converting process, this slag is quite attractive and can be regarded as the third copper smelting slag after fayalite and calcium ferrite slags. Based on the authors' studies on phase separation thermodynamics and laboratory experiments, it was clarified that the oxidic copper loss in this ferrous calcium silicate slag become the minimum not only %Cu in slag but also the total copper loss when the amount of slag is taken into account. It has been proven that calcium ferrite slag is suitable for continuous converting where the dissolved copper is oxidic, but there exist some drawbacks such as limited solubility of silica, low lead removability and too high fluidity. To overcome these difficulties accompanying traditional slags, ferrous calcium silicate slag is the hopeful alternative. In view of the general trends of modem copper smelting processes, the interesting features of this new slag system are discussed.

Jan 1, 1999

By Joseph C. Milbourne

The selection of a suitable nitrate removal process depends on a variety of site-specific chemical and environmental issues. The dominant technologies for nitrate removal include biological denitrification and continuous countercurrent ion exchange. The decision to apply either of these technologies, or both together, depends on the nature of the waste water to be treated. Factors that affect the selection of the biological system include the feed composition and feed temperature. Ion exchange nitrate removal systems are less sensitive to the feed composition but require disposal or destruction of the concentrated pregnant eluate. The paper discusses Tetra's continuous countercurrent ion exchange technology (CCIXTM) and fixed film biological reactor, Denite°. The treatment of the ion exchange pregnant eluant is also discussed.

Jan 1, 1994

By M. J. King

The Chino Smelter embarked on a program to reduce smelter emissions. Fugitive sulfur dioxide and particulate emissions were reduced by (i) removing the flash furnace settling chamber and (ii) installing a baghouse, to treat converter secondary emissions. Neutralization plant capacity was increased, to accommodate increased flow from the flash furnace off-gas cleaning system and to reduce costs.

Jan 1, 1998

By S. Fitzel

The Betts process for electrorefining of lead has been in operation since 1902 in the Trail Operations Metallurgical complex. The Betts process allows production of high purity lead in a single electrochemical step. Process improvements and plant expansions have taken place over the many decades of operation of this process which has proven to be robust, flexible, and capable of successfully treating a large range of anode bullion compositions. This paper reviews the history of the Betts lead electrorefining process, the innovations and quick industrial adoption of new discoveries that took place at the end of the nineteenth century. The process was first implemented in Trail Operations and integrated very well with metallurgical needs then and now.

By E. Allaine

Carbochlorination kinetics of pure MoO3, Nb2O5, Ta2O5 and V2O5, by Cl2+CO+N2 gas mixtures was investigated between 380 and 1000 °C. Standard free energy of carhochlorination reactions and phase stability diagrams of these refractory metal compounds were calculated. The influence of total gas flow rate, temperature, reactants partial pressures on the reactivity of these oxides were investigated. The apparent activation energies were found to be about 83, 75, 110 and 100 kJ/mole below 650°C for MoO3, Nb2O5, Ta2O5 and V2O5, respectively. Above this temperature, the Arrhenius plots exhibit a rate anomaly attributed to thermal decomposition of COCl2 and/or structural changes of these refractory metal oxides. The apparent reaction order of carbochlorination of these oxides with respect to Cl2+CO was determined. For these refractory metal oxides, the reaction rate was maximum for a Cl2/CO ratio of about 1 in the chlorinating gas mixture. Results of carbochlorination of these oxides are compared and discussed.

Jan 1, 1995