By Philip L. Sibrell

A new process utilizing pulsed fluidized limestone beds was tested for the remediation of acid mine drainage at the Friendship Hill National Historic Site, in southwestern Pennsylvania. A 230 liter-per-minute treatment system was constructed and operated over a fourteen-month period from June 2000 through September 2001. Over this period of time, 50,000 metric tons of limestone were used to treat 50 million liters of water. The influent water pH was 2.5 and acidity was 1000 mg/L as CaCO3. Despite the high potential for armoring at the site, effluent pH during normal plant operation ranged from 5.7 to 7.8 and averaged 6.8. As a result of the high influent acidity, sufficient CO2 was generated and recycled to provide a net alkaline discharge with about 50 mg/L as CaCO3 alkalinity. Additions of commercial CO2 increased effluent alkalinity to as high as 300 mg/L, and could be a useful process management tool for transient high flows or acidities. Metal removal rates were 95% for aluminum (60 mg/L in influent), 50 to 90% for iron (Fe), depending on the ratio of ferrous to ferric iron, which varied seasonally (200 mg/L in influent), and <10% of manganese (Mn) (10 mg/L in influent). Ferrous iron and Mn removal was incomplete because of the high pH required for precipitation of these species. Iron removal could be improved by increased aeration following neutralization, and Mn removal could be effected by a post treatment passive settling/oxidation pond. Metal hydroxide sludges were settled in settling tanks, and then hauled from the site for aesthetic purposes. Over 450 metric tons of sludge were removed from the water over the life of the project. The dried sludge was tested by the Toxicity Characteristics Leaching Protocol (TCLP) and was found to be non-hazardous. Treatment costs were $43,000 per year and $1.08 per m3, but could be decreased to $22,000 and $0.51 per m3 by decreasing labor use and by on-site sludge handling. These results confirm the utility of the new process in treatment of acid impaired waters that were previously not amenable to low cost limestone treatment.

Jan 1, 2003

By Anastasia Alksnis

Pyrrhotite is an iron deficient, low nickel content sulfide mineral that is commonly associated with pentlandite, a nickel-rich sulfide; and are both main components of the nickel ore mined in Sudbury. Pyrrhotite tailings generated in the concentration of Ni ores are stored in tailing reservoirs and presents serious environmental risks including acid mine drainage. This study investigated the potential of converting pyrrhotite into a valuable resource through the use of fluidized bed roasting, in which the mineral will be oxidized to produce iron oxide and SO2 gas. These products can then be used to create iron for high-grade steel and elemental sulfur. Thermogravimetric analysis of Sudbury pyrrhotite was performed to study the oxidation kinetics, supporting the feasibility of this process. Further, energy and materials balance was carried out to establish the basic parameters of a possible roasting process.

By Alexander V. Derevyanko, Victor P. Popov, Alexander I. Raitchenko

"If an electric current flows along some electroconductive suspension in columnar form the solid particles are 'experienced thermal, mechanical, and electromagnetic influences.The objects were suspension Sn (liquid) - Ni-Cr-Mo-W alloy (solid particles). This is refractory alloy on the Ni base. The direct constant current (with density -106 A/m2 ) flowed through the named suspension during 180+300 sec. At the beginning of experiments samples were ones containing particles suspended uniformly in volume. Although density of solid particles was ~9x103 kg/m3 , i. e. higher than density of liquid Sn (-6.8x103 kg/m3 ), after end of this processing, the non-uniform distribution of particles in volume of samples was observed: concentration of Ni-alloy particles in lower part was smaller than their concentration in upper part of samples, and simultaneously their concentration is increased near outer surface. There was probably the natural convection of Benard-Rayleigh type which had carried, so lid particles upwards, and, in same time, there was the action of spatial Lorentz-forces directed to center forcing the radial movement.The knowledge of named phenomena can be useful for elaboration of technology of gradient dispersed materials and development of some materials science fields.IntroductionThe liquid metal with the electric current or under the alternating magnetic field is experienced compression. This action causes the pressure within metal and the change of the surface of the metal column (see, for example, [1-4]). One of results of such an electromagnetic compression is extraction of the foreign solid particles from a cylindrical liquid sample to surface in the radial directions. However, more complicated paths of the inclusions are observed under some conditions of electric treatment."

Jan 1, 1999

By Javier Antoñanzas, Susana Caballero, Eduardo Fernández, Jorge Aragón, Juan Carlos Múgica, Lourdes Yurramendi

Air Pollution Control (APC) residues treatment by plasma was studied as a technology for vitrification. During the project a protocol to verify the plasma technology was developed and afterwards applied to a specific case study: the APC residues from Municipal Solid Waste Incinerators (MSWI). Different operational conditions were tested and the vitrified products obtained were analyzed using standardized leaching tests in order to evaluate their new properties concerning safety storage. Two leaching tests were used for the evaluation, the European EN 12457-4 compliance test for leaching of granular waste materials and the French XP X 31-211 test for the determination of the leachability of a solid waste material initially massive or generated by a solidification process. Finally, conclusions about the environmental performances of the technology were obtained.

Jan 1, 2008

By F. J. Arriagada

Where gold is present in a finely disseminated form within sulfide particles, the porosity and surface area of the calcined material strongly influence leaching since they control the penetration of solution inside the gold-bearing grains. On the basis of a stability diagram for the Fe-O-S in the temperature range of 400 to 750aC, the expected sequence chemical transformations associated with the oxidation of pyrite is discus-sed. By using analytical techniques which include scanning electron microscopy, X-ray diffraction and BET gas adsorption, the chemical and structural changes experienced by auriferous pyrite-arsenopyrite concentrates and pure pyrite samples are studied under an oxidizing roasting atmosphere of com-position 80% N + 20% O2 in the temperature range of 450 to 750°C. The results indicate that as the roasting temperature increases, the surface area of the calcines decreases sharply after a maximum value attained at about 450-500°C. SEM micrographs show that the needle-shaped tips which characterize the surface of the oxide product become wider and the size of the pores between them is decreased when the roasting temperature is in-creased from 550 to 750°C. This effect suggests that the formation of a more "closed" hematite product at higher temperatures is due to sintering associated with a faster growth and crystallization of the oxide. A strong correlation is shown between increasing roasting temperature and increase in gold lost in cyanidation tailings, an effect which may be partly attributed to the loss in surface area of the calcines.

Jan 1, 1982

By K. Adham

"Fluidized beds are utilized in a wide range of high-temperature applications throughout the metals and materials industry. Their main advantage is the fast and uniform heat and mass transfer between the hot combustion gases and the particulate solid feed. A further benefit can be the lowering of the processing plant's energy consumption, through heat recovery from the fluid bed processes used for solids heating. Here, the enhanced energy efficiency of fluidized systems is investigated and the modeling results are discussed for three configurations: the flash tube, the single bubbling bed and the multi-stage fluid bed. Key thermal design aspects of each system are identified based on results from process simulations, in order to benchmark their main operating features and overall energy efficiency. Suitability and applicability of each configuration is also discussed based on a number of process and material property considerations.IntroductionCombustion based heating of particulate solids is commonly done using three different types of fluidized beds. The flash tube (FT) is similar to a hot pneumatic transport system. The single-stage fluidized bed (FB) typically uses in-bed combustion. The multi-stage fluidized bed (MSFB) can have two or more stages stacked into a tower.Flash tube (FT) suspends the incoming solid charge in a high-velocity stream of hot combustion gases. To maintain the solids suspension in the FT, two parameters are required: high velocity for elutriation of the particles and adequate solid-to-gas ratio for avoiding high pressure drops and solids drop-out [l].The fluid bed (FB) works at much lower velocities than the flash tube. Therefore, most of the solids are not conveyed in the gas stream, but are only suspended in a liquid-like manner. At minimum fluidization velocity (Umr), the gas flow exerts just enough force on the solids to keep them suspended in place [2].Multi-stage fluid bed (MSFB) heats up the solids as they are transferred from an upper bed level to a lower one, counter-current to the rising flow of hot gases generated at the lowest stage. As the temperature and volumetric flow of the gases decrease from bottom to the top stage, smaller bed diameters can be used in the energy recovery stages [3]."

Jan 1, 2014

By M. Waladan

The top submerged lancing Sirosmelt system has been developed through laborator.y scale testwork and pilot plant trials for recovery of zinc from ISF slag. The effects of the process variables of gas injection rate, method of coal feeding, and temperature on zinc fuming rates were studied in the laboratory. It was found that the rate of zinc elimination was dependent on all of these variabl.es. The rate of zinc removal from slag was independent of zinc content of slag down to approximately 1.5% Zn, below which the rate was proportional to zinc content in slag. Pilot plant trials were carried out to evaluate a proposed process and results followed predictions from the laboratory scale tests. A comparison of the proposed process with conventional slag fuming operations is made and it is shown that the process has a number of advantages which have a significant impact on the economics of zinc slag fuming.

Jan 1, 1990

By Y. Ono

In lightweight metal processing such as aluminum (AI) and magnesium (Mg), metal cleanliness is a crucial process parameter for refining, part manufacturing and recycling in order to obtain high quality parts and products. In this paper, techniques for cleanliness evaluation of molten AI and Mg using ultrasonic probes with clad steel buffer rods having high signal-to-noise ratio (SNR) are presented. Due to the high SNR of the ultrasonic probes used, backscattered ultrasonic signals from inclusions, which may be oxide films and/or particles, in molten Mg and those from silicon carbide particles, having an average size of 50f.Ull, added in molten AI are successfully detected with reflection configurations of pulse-echo and/or pitch-catch modes at an ultrasonic frequency of 10 MHz. In addition, relative cleanliness evaluation of molten Al and Mg is demonstrated. In order to establish the procedure and to investigate the optimum system configurations for cleanliness evaluation of molten metals, particle flow simulation system using water and polyvinyl chloride (PVC) particles has been constructed. Counting the number and measuring the size distribution of the PVC particles, having an average diameter of 128um, suspended in water with the PVC volume concentrations of 5ppm and 10ppm are performed with ultrasonic pitch-catch mode. The counted numbers of particles by the presented method and system have good agreement with the calculated results with a count error of less than 10% or two counts. Based on the results obtained with water simulation experiments, the prototype system for cleanliness evaluation of molten Mg by counting and sizing inclusions has been developed. Keywords: Ultrasound, Clad buffer rod, Molten metal, Aluminum, Magnesium, Inclusion detection, Cleanliness measurement, Counting, Sizing

Jan 1, 2003

By F. D. S. Marquis

An investigation of the mechanisms of formation of two types of porosity-primary and secondary-their characterization, evolution during processing, and effects on the mechanical behavior (fracture, fatigue, and failure) of 7X50 and 2X24 alloys has been conducted. The mechanisms of formation of three forms of primary or cast porosity were investigated, and each form was characterized: (a) macroscopic shrinkage porosity-MSP); (b) microscopic interdendritic porosity (MIP); and (c) hydrogen gas porosity (HGP) or primary hydrogen porosity (PHP). The mechanisms of formation of four forms of secondary or thermal/thermomechanical porosity were investigated, and each form of porosity was characterized: (a) high temperature oxidation (HTO). internal hydrogen precipitation (IHP), or secondary hydrogen precipitation (SHP); (b) preheating blistering porosity (PBP); (c) eutectic melting porosity (EMP);and, (d) dissolution micro void formation (DMF). The evolution and interactions of the primary and secondary types of porosity (w.ith special emphasis on PHP and SHP) during industrial and laboratory processing and their effects on the fracture and failure behavior of both types of alloys (with special focus on fatigue crack initiation and propagation) were investigated.

Jan 1, 1996

By S. Ozbilen

"Al-Li binary alloys with nominal Li contents of0.15, 1.1and2.8 (in wt%) were aged naturally at room temperature for two months, aged at low temperatures ( 65 and 1 OOEC) for up to 2 months and aged artificially at 190EC for 4 days after water quenching to 25EC following solutionizing at 530EC for 20 minutes. Ageing behavior of these binary alloys were studied by Vicker's Hardness measurements and DSC thermal analysis. Thermal analysis results indicate the formation of GP zones of Al-Li system in Al-2.8wt%Li binary alloy. In the same alloy, rapid quenching from one phase region (a) gives rise to precipitation of small o' particles in a matrix (a) with still high supersaturation. During ageing of this alloy below lOOEC an additional transformation, i.e., GP zone formation occurs proceeding at a very high rate which is described on the basis of the theoretical analysis for the quenched Al-Li system proposed by Khachaturyan et al [6]. Ageing at temperatures below 11 OEC takes place slowly by the formation of small d' particles of lower thermal stability than the quenched-in d precipitates in addition to GP zones resulting in an increase in hardness compared to water quenched samples. During artificial ageing, GP zones transform by dissolution to d' precipitates while d' particles already in the microstructure coarsen during under aged condition at which hardness increases with time till peak aged condition.IntroductionIn binary Al-Li alloys the d' (Al3Li) fully coherent internally ordered inetastable phase of Li2 structure with a=0.4038d [1-5] forms homogeneously between 120 and 190EC before the formation of stable d' (A!Li) phase and cause the superior mechanical properties. This is due to an appreciable age hardening effect resulting because of the d' precipitation during ageing [1]. The response of d' to decomposition and its formation kinetics have been studied previously and it is believed that the decomposition of the a-supersaturated solid solution occurs in a two stage process; i.e., a 6 d' (Al3Li) 6 d(A!Li). Khachturyan et al [6] theoretically investigated precipitation of the d' phase and gave an interpretation of the transformation paths of the quenched Al-Li alloys. They predict that the disordered supersaturated solid solution congruently orders, and then the uniformly ordered solution decomposes into ordered regions that differ in Li-content. Finally, ordered d' phase forms in the disordered matrix."

Jan 1, 1998

By Olexandr Gydin

The evolution of grain and dislocation structures during cold deformation of the new steel LH800 of Salzgitter AG is investigated in the frame of this work. The main feature of this material is its ability to air-harden by carbon content of about 0.1%. The initial ferrite structure of the metal provides high plasticity at cold deformation and subsequent heat treatment increases tensile strength approximately two times. Described are results of in-situ tensile tests in the SEM. SEM and TEM analysis of grain and dislocation structures evolution in samples, which have been uniaxially deformed to certain strains, are carried out. After statistical evaluation of results the grain elongation against strain is determined. A microstructure of a deep drawn cup is analyzed by means of SEM. A quantitative evaluation of grain elongation on the different cup zones and comparison of these data with prediction results based on tensile tests are carried out.

Jan 1, 2009

By R. Harris

Blister copper melts of 800 g to 1000 g containing less than 1 wt % S and up to 3 wt % Ni were desulfurized at 1523 K in air or by a pure oxygen jet blown at 75,500 and 1000 cm3/min, from 1 cm above the melt. Rates of desulfurization and oxygen pickup were measured and visible surface phenomena were photographed and videotaped. It was observed that SO2 was evolved from Cu-S melts in a manner reminiscent of the effervescence seen in carbonated drinks. The effervescence lasted up to 20 minutes and resulted in the ejection of material up to a height 50 cm above the melt surface. Sporadic discharge of large bubbles was also observed in a Ni containing melt top-blown with oxygen at 1000 cm3/min. The Cu-S melts top-blown with oxygen experienced faster sulfur elimination as compared to stagnant melts exposed to air and experienced only a single period of turbulent SO2 evolution, which occurred almost immediately after oxygen injection commenced. The Cu-S melts exposed to air experienced multiple episodes of effervescence. The stagnant blister copper melt containing nickel did not exhibit effervescent behaviour and experienced a lower rate of sulfur elimination compared to Cu-S melts tested under similar conditions. The present article examines the role of surface phenomena in determining the observed behaviour.

Jan 1, 1999

By Motohiro Horiguchi, Kazuo Ichii, Toshio Oishi

"As a fundamental study to prepare copper-based alloys with rare earths (RE: La, Gd, Nd, Ce and Y) without any inclusions, the solubility of rare earth in liquid copper was experimentally determined. Liquid copper alloys were equilibrated with carbon and rare earth carbide in a graphite crucible in an argon atmosphere at 1523-1873 K.Solubilities of rare earth in liquid copper were determined by approaching the equilibrium values from both the lower and the ·higher concentrations than those expected· in the preliminary experiments. They were expressed as a function of temperature. Carbon in Cu-RE alloy was also analyzed and thermodynamically discussed.IntroductionOver the past several years, the demand for highly conductive and high strength copper-based alloys, such as Cu-Cr, Cu-Zr and Cu-Cr-Zr for use in electronic materials has increased.1 -7 These alloying elements are very reactive and easily oxidized to form oxide inclusions during melting. To avoid the oxide inclusions, it may be effective to utilize the strong reducing power of carbon in conditions under which no carbides form.In this study, to provide fundamental data for producing Cu-RE( rare earth) alloys without any inclusions, the solubility of rare earth in liquid copper in equilibrium with .carbon .was determined and discussed on the basis of the experimental results and the thermodynamic data.ExperimentalSample preparation for equilibrium experimentsOxygen-free copper (99.99%), lanthanum (99.9%), gadolinium (99.9%), neodymium (99.9%), cerium (99.9%) and yttrium (99.9%), and their oxides were used as starting materials.Each rare earth carbide was prepared by mixing rare earth oxide with carbon, which is a little more than the stoichiometric composition, pressing it into a tablet form and sintering at about 2000.K for 20 ks in a vacuum furnace using a graphite crucible. Powder X-ray analysis showed that only the carbon and rare earth carbide (REC2) was present in each sample.Cu-RE mother alloys (5-20 mass % RE) were prepared beforehand by mixing metallic rare earth with oxygen-free copper, and melting in an electric arc furnace."

Jan 1, 2000

By E. T. de Groot, D. L. Verhelst

With the successful start-up of Cominco's new KIVCET smelter, the final key component is now in place for Trail Operations to operate efficiently as a modern integrated zinc-lead facility. Unique metallurgical, operational, planning and management issues apply to this operation. Along with presenting the current flowsheet for Trail Operations, this paper discusses issues such as the impact of recycles, operational re-stabilization following significant process changes, plant operation with just-in-time inventories, real-time process optimization, and management philosophy.

Jan 1, 2000

By Mark H. Hashiguchi

Examination of tensile bar surfaces shortly after destructive testing was conducted to search for clues that would aid in optimization of mechanical properties, especially tensile strength, yield strength and elongation to fracture. Cu-Ni-Si-Cr alloy bars in the as-cast, forged, rolled and extruded conditions were examined. Low ductility bars (<4% Elongation) showed dramatically different features than the fracture surfaces of high strength - high ductility bars (7 to 10% Elongation). Analysis of the fracture surfaces at 15X to 2000X and use of Energy-Dispersive X-Ray Spectroscopy (EDS) identified Ni-Si and Ni-Si-Cr precipitates of varying sizes and morphologies. Thermo-mechanical processing techniques to control the size and distribution of these precipitates show promise in improving the properties and performance of this alloy system and appear to correlate with improvements in the fracture surface morphology.

Jan 1, 2008

By J. J. Kim

In a study of buildup in a green-feed reverberatory furnace, it was determined that approximately half of the crucible area has a moderate buildup of 25 in. or less, and that the area extending 45 f t from the burner end of the furnace has only a slight buildup. The false bottom, averaging 6 in. in thickness, was found to cover the entire crucible area. The stratification of Cr2O3, A12O3, and SiO2 occurs throughout the slag layer; this phenomenon is the principal reason for the formation of the false bottom in the green-feed reverberatory furnace. The false bottom is caused primarily by the settling of FeO*(A1,Cr),03 aggregates, which are derived mainly from returned converter slag. The false bottom can be transformed to a solid permanent buildup in the furnace, particularly when the matte is completely withdrawn. From the material balance of Al2O3 and Cr2O3 around the furnace, It is estimated that the average rate of aluminum chromite accumulation is approximately 0.3 ton per day or less.

Jan 1, 1976

By Vincent Canaguier

Methane is increasingly considered as a promising reductant for metal oxides, including chromite. To assess the possibilities of such reduction route, the gas-solid reactions between Ar–CH4–H2 gas mixtures and synthetic chromites are studied between 950 and 1050 °C. The influence of Mg and Al additions on the reduction-caburization of (Fe,Mg)(Cr,Al)2O4 solid solution is investigated thermodynamically, structurally and kinetically. The product phases are examined by x-ray diffraction (XRD), scanning electron microscopy (SEM), and electron probe microanalysis (EPMA). The reaction rate is derived from real-time exhaust gas measurements and post-reaction product analyses such as oxygen analysis. Kinetic models are proposed based on the product phase morphologies and confronted with the empirical data.

By Saeid Pournaderi, Ahmet Geveci, Ender Keskinkilic, Yavuz A. Topkaya

There are mainly three commercial nickel laterites in Turkey: Gordes, Caldag and Sivrihisar. The first two appear in Western Anatolia. The third one, Sivrihisar (Yunusemre) laterites have been found in the first decade of the millennium, in the Central Anatolia region of Turkey. Since then, mining facilities have been continued in Yunusemre. Calcination, prereduction and smelting of Sivrihisar laterites have been extensively studied and published. In the current work, some results of the studies related to characterization of Sivrihisar laterites will be presented.

Jan 1, 2016

By K. Noda

Tamano Smelter of Hibi Kyodo Smelting Co., Ltd. started its operation adopting the Flash Smelting Furnace with Furnace Electrodes (FSFE). Thereafter, it developed a coke combustion technology based on C() concentration control, which made possible a low cost and high productivity operation without using electrodes. However, increase of treated concentrates and upgrading of matte grade for production expansion started to cause difficulties in operation control with then existing operation control system. This paper outlines recent improvements for stable operation of the Tamano Type Flash Smelting Furnace (T-FSF), such as computer aided operation guide system.

Jan 1, 2001

By Batric Pesic

The interactions of mineral-pyrite with T. ferrooxidans were studied by using a cyclic voltametry technique. The interactions with bacteria were carefully examined during the entire growth stage of bacteria (fermentation). Several very important discoveries were made. For example, the pyrite surface invariably drastically changed its properties at the second day of fermentation. Beyond two days of fermentation, the cyclic voltamograms were insensitive to convective diffusion produced by stirring. The SEM study revealed that bacteria populated the pyrite surface at an extremely high density levels. The high density of bacteria, and the solid reaction products formed on the pyrite surface created conditions for pore diffusion which explained why the CVs became insensitive to convective diffusion in solution (stirring).

Jan 1, 1990