By Shu Xinqian, Zhou Weining, Shan Zhiqiang, Feng Jifu

"Modified calcination conditions on the extraction of rubidium resources from muscovite (KAlz[AlSi301o](OH)2) ore are systematically studied. The impact of various factors on the rubidium leaching rate is also analyzed, including the agent types, roasting time, the mass ratio, roasting temperature, etc. The results indicate that the best agent is a combination of sodium chloride and calcium chloride, its mass ratio ofmuscovite/NaCl/CaClz is 1:0.25:0.25. Calcined at 8500 for 30 minutes, the rubidium leaching rate is up to 90%. The reaction of muscovite ore with the chlorinating agent CaC12 has been studied by TG/DSC, the calcined intermediates are identified by XRD, and the surface morphology before and after leaching is characterized by SEM. Rubidium chloride products can be obtained with a purity of 92% by using t-BAMBP extraction, hydrochloric acid reextraction and purification.IntroductionRubidium is one ofrare alkali metals, which is found in 1981 by German R.W. Bunsen and G.R. Kirchhof. Rubidium includes the following features: atomic number is 37, each atom weight 85, the body-centred cubic lattice, each unit cell has two metal atoms, and the density is 1.532g/cm3. The properties of low melting point (312.46 K) and malleability make rubidium have a strong chemical activity and photoemission. Rubidium provides a main material for manufacturing phototube with a wide range oflight waves, which possess high sensitivity and stability. Efforts are being made to carry out research on rubidium ion gngine, magnetic flux generators and thermoelectric transudcer, etc. Rubidium exists in muscovite ore(KA12[AlSh01o](OH)2 (monoclinic system and hexagonal layered structure) as isomorphism and replace the large radius of the potassium atoms, as well as part of rubidium locate between structure layers. The complex components bring great difficulty in comprehensive recycling."

Jan 1, 2013

By J. T. Stanley

The identification of crystal phases and crystal chemistry can be critical to understanding the mechanisms of waste material interaction with native soils. Understanding these mechanisms can suggest correct methods for remediation and treatment. A program is outlined and examples are given of the development of effective techniques for rapid phase identification of environmental samples using electron microscopy. The program concentrates on the development of integrated object oriented software to aid rapid searching of online databases and rapid simulation of potential crystal diffraction patterns. Examples come from dried sludge taken from a former hard-chrome plating facility.

Jan 1, 1993

By Jorge A. S. Tenorio, Chuanwei Zhuo, Joner O. Alves, Yiannis A. Levendis

"The ever increasing number of automobiles and the consequential increase in consumption of tires have generated a pressing environmental issue, concerning the disposal of unserviceable tires. The worldwide disposed of waste tires is approximately 1 billion units per year and this amount is expected to increase by 2% each year. This work presents a microstructural characterization of nanomaterials synthesized in a catalyst system from the effluent of burning waste tire chips in a horizontal two-stage laminar-flow furnace. Controlled combustion of waste tire chips took place at temperatures of 900 or 1000 °C, and stainless steel meshes were used to synthesize the nanomaterials at 1000°C. Produced materials were analyzed by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The catalyst meshes were covered by materials with diameters of 20 to 200 nm and lengths of about 40 µm. They possessed structures similar to those of carbon nanotubes.IntroductionThe motor vehicles on the road have been increasing annually. World motor vehicle production in 2009 approached 62 million units. Consequently, the consumption of tires has also been on the rise; about 1.4 billion units were produced around the world in 2007 [l]. The disposal of scrap tires is a serious environmental problem. The worldwide disposed of waste tires is almost 1 billion units per year with an expected increase of around 2% each year. However, less than 7% of produced waste tires are recycled (excluding reuse, retreading or incineration). The waste rubber tires are a thermoset polymer, which cannot be reprocessed like thermoplastics polymers, therefore the recycling of this material requires special techniques that demand big investments [2, 3].A solution to the disposal of waste tires is the sequential pyrolysis/combustion process. Past research showed that waste tires are an attractive potential fuel due the high heating value (29-3 7 MJ/kg), which is comparable, or even higher to those of typical bituminous coals [ 4, 5]. Pyrolysis is a process wherein the material is thermally decomposed at elevated temperatures at the absence of an oxidizing gas. Combustion is characterized by the addition of the oxidizing gases during the process. Several studies indicate that the pyrolysis and combustion processes for the tires treatment have a great energy conversion potential [4, 5, 6]."

Jan 1, 2011

By Jinjing Dua, Jun Zhua, Kuiren Liub, Bin Wang, Xiaolei Wua

V-Ti-Fe as hydrogen storage alloy was prepared by reducing metal oxides with a metallothermic reduction method. The deoxidation process of the V-Ti-Fe alloy was performed by electro-deoxidation and vacuum induction melting method, respectively. The results showed that the content of oxygen impurity can be controlled at about 0.2wt% after electrolyzing for 240min. Both the maximum values of hydrogen absorption capacity and the effective hydrogen desorption capacity are 2.65wt% and 1.01wt%, respectively. The deoxidization effect of vacuum induction melting process is more remarkable, with Ce as the reducing agent. It is found that Ce addition is beneficial for reducing the componential segregation, promoting the hydrogen absorption activation of V-Ti-Fe alloy. When m(Ce)/m(alloy) is up to 5%, the oxygen content has been reduced to 0.05wt% and the maximum hydrogen absorption capacity and the effective hydrogen desorption capacity are up to 3.36wt% and 1.85wt%, respectively.

Jan 1, 2015

By Bradley C. Bockrath

Some thirty coals were evaluated for liquefaction activity under a mixture of CO and H2 at 425° C. The viscosity of the liquid products was taken as an indicator of the degree of liquefaction. It was found that the direct liquefaction of a particular coal may be beneficially influenced by the presence of pyrite. Active pyrites are often found in the native mineral matter of the coal itself. For example, subbituminous and bituminous coals and lignites of relatively high pyrite content were found to liquefy more readily than similar coals or lignites which were poor in pyrite. The reactivity of inactive coals could be improved by using blends with active, pyrite-rich coals. In addition, pyrite was effective when added separately as pyrite concentrates obtained from coal beneficiation operations. Various other iron- and sulfur-bearing additives were also effective when used in combination as added slurry-phase catalysts, including iron oxides and mineral residues derived from liquefaction of active coals. Under liquefaction conditions, pyrrhotite ( Fe I- x5) is formed from pyrite or from the iron oxides and many sulfur containing species. Pyrrhotite was shown to be a hydrogenation/dehydrogenation catalyst for tetralin but is not active for initiating a variety of free radical reactions that do occur when pyrite is heated with tetralin. The role of pyrite in coal liquefaction is complex and still not well understood.

Jan 1, 1981

By Meifeng Zhi

Separation of uranium and molybdenum in the alkaline leach solution of a U–Mo ore was studied. A process of acidification-solvent extraction-precipitation uranium and molybdenum was determined. The influences of solution acidity and phase ratio of acidic scrubbing on separation of uranium and molybdenum were examined. The molybdenum extraction equilibrium isotherm was drawn. The results show that the separation of molybdenum and uranium can be achieved by acidifying the alkaline leach solution, solvent extracting molybdenum using trialkylamine at equilibrium pH 2.5, and scrubbing the loaded organic phase using sulfuric acid solution. The strip solution can directly precipitate ammonium molybdate. Uranium can be directly precipitated from the raffinat

By Sebastian Schmuck, Petrico von Schweinichen, Dieter Senk, Mohammad Peymandar

"At Department of Ferrous Metallurgy of the RWTH Aachen University in Germany steels in the system Fe-Mn-C(-Al) are investigated and produced in the framework of the SFB 761 ""steel-ab initio"". A new world of steel grades leads to special challenges regarding the production and recycling at the end-of-life cycle of product. In order to recycle high manganese steel alloys the EAF has to be chosen preferentially. A good slag practice is necessary avoiding loss of manganese content during melting in the EAF. This paper investigates on the reaction kinetics at the interface of slag and steel containing Mn (17-22 wt.-%) and up to 3 wt.-% Al. The effect of changes in the composition of slag and steel on the interfacial reaction kinetics is studied. The thermodynamic software FactSage™ is utilized to calculate the composition of slag and steel at equilibrium.IntroductionTRIP and TWIP steels are highly alloyed steels which show superior strength and ductility when compared to standard carbon steel and stainless steel alloys. These TRIP- and TWIPsteel grades contain typically 15-30 wt.-% manganese, 0-4 wt.-% silicon and aluminum, and up to 1 wt.-% carbon. Steels containing 18-28 wt.-% manganese and 0.7-1.2 wt.-% carbon together with aluminum addition from 3 to 12 wt. -% and without silicon refer to TRIPLEX high manganese steel alloys. These alloys combine high strength at even large ductility [ 1-4]. At the Department of Ferrous Metallurgy (IEHK) of the RWTH Aachen University in Germany, steels in the system Fe-Mn-C(-Al) is under investigation at the collaborative research center, SFB 761 ""Steel-ab initio"". In this project, high manganese alloyed TRIP and TWIP steels are in the focus.The mechanical properties such as high strength and high ductility make this kind of steels perfect candidates for impact absorption applications in auto body such as vehicle doors and bumpers [2, 5]. With increasing the use of TRIP-, TWIP- and TRIPLEX-steels more high manganese steel scraps will be available at the end of life cycle of products, which need to develop the technologies and metallurgical processes to recovery of high manganese steel. A new steel grade brings new challenges in recycling. In order to recycle high manganese steel scraps the electric arc furnaces (EAF) have to be chosen preferentially [1]. Nevertheless it's not easy to prevent the manganese loss during the process in EAF. During the oxygen refining of high manganese molten steel in EAF the manganese content decreases strongly by oxidation and vaporization, which is affected by slag composition, slag properties such as basicity and viscosity, slag weight as well as melt temperature [6-8]."

Jan 1, 2014

By Naiyang Ma

"High oil concentration is one of the major barriers for recycling of mill scale of steel hot rolling mills. It is of vital importance to find cost-effective technologies of reducing oil concentration in mill scale in order to recycle the mill scale without causing detrimental effects on production and environment. This paper discusses in-process separation of mill scale from oil at steel hot rolling mills. Formation of mill scale and status of oily wastewater at hot rolling mills are reviewed in the first place. A mathematical model is then formulated to relate oil concentration in mill scale to physical properties of mill scale, chemical and physical properties of wastewater and interacting parameters between mill scale particles and wastewater. From this model, three approaches of in-process separation of mill scale from oil are derived: (1) avoiding contacts between mill scale particles and oily wastewater, and (2) maintaining low oil concentration in wastewater, and (3) collecting mill scale in upper streams of wastewater flows. In-process separation of mill scale from oil might have advantages of lower capital cost, lower operating cost and less additional environmental concerns, compared to other strategies of separating mill scale from oil.IntroductionHot rolling is an inevitable step in producing finished steel products. Figure 1 schematically shows a steel hot rolling process. Semi-finished steel products, slabs here, are reheated first, and then the reheated slabs are discharged from the furnaces and transported on hot rolling trains to descaling units for removing scale with pressurized water. After being descaled, the slabs are rolled by roughing mills. After treated with cropping and the second descaling, the slabs are finally rolled into finished products, coils here, by finishing mills."

Jan 1, 2012

By Viktor. P. Popov, Oleksandr. V. Derev'yanko, Oleksandr. I. Raychenko

"This paper is devoted to scrutiny problem of obtaining electro-contacts by electro-discharge sintering technology. A new unconventional method of electro contacts production (on Aggraphite base) can yield essential optimization resource.Review of three electro-technological methods of processing contacts materials is presented:- using graphite powder cladded by Ag;- mixture of graphite powder(which is a non-cladded powder) with Ag powder and addition of Fe powder particles;- method of infiltration of melted Ag into graphite piece without deformation and rupture of object.This technological approach can give the possibility to increase of compression strength of electro-contacts materials up to 340 MPa and more under conditions of additional reinforcing components (for example, by Fe).IntroductionThe electric current can be an active ""participator"" of the powder metallurgy technology [l]. At the passage of electric current through powders or some powder mixtures the phenomena including phase transformations arise. Here such effects, which are observed in the Ag-graphite and Ag-Fe-graphite powder mixtures and in the pair Ag-porous graphite, are described.The Ag-graphite composition materials (CM) are used, for example, as electric contacts [2, 3]. Since a material being produced is destined for the contacts it is necessary to take into account the following aspects: commutating current, its character and voltage, active or reactive character of working load, geometrical dimensions of contacts, quantity and frequency of switching on and switching off, pressure on contacts, distance between contacts, method of arc control, surrounding medium, its content, pressure and temperature. Thus, these and, maybe, choice of some other circumstances influence design, materials and production technology of contacts. The range of problems concerned dictates such steps as alloying of contact materials, optimization of structure, selection of kind of graphite, its connection with metal [4-10]. It is expedient to recall the main procedures of the first stage of the conventional technology: dosage of the initial graphite powder and binder-phenolic resin plastic varnish (for example, Bakelite), mixing, densification, thermal treatment, crushing, grinding, sieving, drying, dosage of grained graphite, dosage of the initial silver powder, obtaining of the silver salt solution, settling of salt, filtration, washing, drying of the cladded graphite powder, thermal treatment, obtaining of the graphite powder of particles cladded by silver. The second stage of the convectional technology starts by obtaining of the cladded graphite powder and finishes by annealing of the pressed blanks (Fig. 1)."

Jan 1, 2004

By Jianxin Zhang

A process, in which arsenic in the residue is transformed directly into scorodite and copper dissolves into the solution simultaneously, was studied. The process was carried out in acidic ferrous sulfate solution under oxygen pressure. The optimum conditions of the process were determined as follows: the initial H2SO4 concentration of 10 g/L; liquid/solid ratio of 10; Fe/As molar ratio in the feedstock of 1; the addition of calcium lignosulphonate was 1% of sludge; oxygen pressure, temperature and reaction time were 1.5 MPa, 150 °C and 6 h, respectively. Under these conditions, arsenic transformed to crystalline scorodite in size of 5–10 μm, and the transformation efficiency reached 97.60%; meanwhile, the copper was leached with a high efficiency of 93.34%. The stability of the leaching residue was evaluated by TCLP testing, and the results indicated the concentration of arsenic in the leaching solution was extremely low as 0.04 mg/L and met the standard of safe stockpile.

By Clemens Schmetterer, Patrick J. Masset

"The surface tension represents an important property for the modelling of high temperature processes. In this study the surface tension of two Al2O3 – CaO – SiO2 model slags and the influence of the admixture of 5 up to 30 wt.% FeO were studied. The surface tension measurements were carried out using the sessile drop technique on BN substrates under Ar atmosphere (10-6 atm O2) up to 1500 °C.IntroductionThe aim of VIRTUHCON1 is the virtualization of high temperature conversion processes, a task that requires thorough understanding of these processes. In many of these conversion processes slag plays an important role to control the properties of the product, to protect the reactor lining or simply as waste. Slag surface tension is one of the materials properties that is needed for the description of such processes, since it influences the interactions between the components in the reactor, e.g. at the slag – Fe interface in the blast furnace.Surface and interfacial tensions have thus received considerable attention in research, but the number of investigations in this particular pseudo-quaternary system is surprisingly low. Furthermore, the literature data are subject to different measurement conditions and techniques which complicates the data analysis and comparison.The slag atlas [1] offers a compilation of the available literature until 1986 (shown in Table I), but literature search has not revealed more recent studies of this system until now. For example, Elliott and Mounier [2] determined the surface tension of ACSF slags using the double tube maximum bubble pressure technique at 1200 °C. They kept their slags in contact with Cu-S-F mattes, and the slag therefore contained a certain amount of sulphur which acts as a surfactant and lowers the surface tension. The compositions of their slags were scattered over a wide composition range and they did not use a common ACS base mixture for their tests, either. The surface tension values vary between 417 and 446 mN/m, but due to the reasons just mentioned no trend in the measurements can be observed and the influence of FeO admixture on the surface tension cannot be deduced. Further information including the temperature dependence is available from Pavlov et al. [3], Ishchanov and Shushkov [4] and Murav’eva and Kaplun [5]; the diagram on page 446 in Ref. [1] has been drawn from these sources. Both positive and negative temperature coefficients are reported in these works. SiO2 is the only pure constituent that has a positive temperature coefficient [6], but a correlation of the temperature coefficient with the SiO2 content was not found to be conclusive."

Jan 1, 2011

By Y. K. Rao

In the carbonyl process for the refining of crude nickel CO(g) reacts with nickel in the 310-370K range producing nickel tetracarbonyl, Ni(C0)4(g). Iron and cobalt impurities also form gaseous carbonyls but their partial pressures are low. The carbonyl is led to a decomposer plant wherein the gas disproportionates in the 500-600K range depositing pure metal on nickel pellets that move countercurrent to the gas-flow. This system serves to illustrate the fundamental principles involved in the vapor phase mass transport of elements, against temperature-gradient, under the influence of chemical potential gradient. Unlike in the crystal growth, the source is at a lower temperature (say 350K) whereas the seed is in the hot-zone (say 550K) of the closed ampoule-type reactor. By assuming virtual gas-solid equilibria in the end zones, with diffusion of gaseous species between them acting as a slight perturbation, the quasi-steady- state mass-transport rates are computed for a range of CO-pressures and temperatures.

Jan 1, 1993

By Robert P. Stevens

It is important for a refractory supplier to make systematic petro-graphic examinations of products which have been in service in the furnaces and kilns of customers. The petrographic examination of refractory service samples involves the microscopic study of polished and/or thin sections, supplemented by electron probe microanalysis, as well as the bulk chemical and XRD analysis of zones in the samples. The evolution of the A. P. Green Refractories Company petrographic laboratory is described, and the application of petrographic methods is illustrated in the examination of service refractories from a Portland cement rotary kiln and an AOD stainless steel vessel. The objectives of such studies are to assist the customer in the solution of his refractory problems, and to accumulate data which are of use in the design of improved refractory products.

Jan 1, 1981

By Mark C. Bronson

The feasibility of several pyrochemical approaches-for separating non-radioactive constituents from ICPP HLW calcine were examined. The removal of aluminum as AICI3 from aluminia calcine was successfully demonstrated. The examination of pyrochemical processes to remove non-radioactive constituents, primarily aluminium, zirconium, calcium and fluorine, from zirconia calcine showed that fluorine removal was required in order to chlorinate the calcine. A molten calcium chloride wash, a calcium reduction, and. a sulfuric acid treatment were examined as possible zirconia calcine pretreatment options for fluorine removal. Fluorine removal from simulated ICPP zirconia calcine was demonstrated by both a CaCl2 wash method and a sulfuric acid treatment method. X-ray fluorescence analysis indicated that greater than 97% of the fluorine can be removed by either method. Fluorine removal by a calcium reduction using an alloying agent, zinc, or a calcium reduction using, a filtration separation were also demonstrated, but the efficiencies of fluorine removal were considerably less ranging from 50 to 90%. Regeneration of CaCl2 from the salt and oxide residues of the CaCl2 wash experiments was also demonstrated 'by an aqueous dissolution method. From the salt residue, 85% or more of the CaCl2 was recovered and contained little if any CaF2 or CaO. From the oxide residue close to 100% of the CaC12 was recovered. Because of the overall success of the CaCI2 wash, it was determined to be the preferred fluorine removal process. The sulfuric acid treatment to remove fluorine is effective, but the proposed overall flowsheet has not' been adequately demonstrated.

Jan 1, 1995

By Ehsan Khajeh

In this study, the permeabilities of Al-15.5wt%Cu and Al-19.5wt%Cu have been determined by solving the full Navier-Stokes equations on 3D geometries of interdendritic channels obtained by X-ray microtomography (XMT). The samples for XMT were sectioned from different positions in directionally solidified cylinders in order to obtain a variety of microstructures for each composition. The flow has been solved using a 2nd-order accurate Finite Volume Method (FVM) approach. The effect of employing uniform or unstructured mesh on the calculated permeability has been studied. The Marching-cube triangulation method was necessary to extract accurate surfaces for unstructured volume meshing. Calculated values of permeability for this range of solid fractions show partial agreement with previous experiments. Observed deviations are attributed to the difficulties of experimental permeability measurements.

Jan 1, 2009

By Wang Chen

COREX process is briefly introduced. A static model combining a set of mass and heat balance equations has been developed. Taking the specified inputs from the graphical user interfaces, the model is capable of calculating the consumption of raw materials and fluxes, the volume and composition of the slag and the volume and composition of the generator gas. The model enables the examination of the changes of materials and energy flows induced by the variations of operational parameters and raw materials chemical analysis. The model allows a detailed process analysis and adjustment of the plant operation and can thus be used to improve plant operation.

Jan 1, 2008

By Halvor Dalaker, Alain Marc Ferber, Thor Anders Aarhaug, Pål Tetlie

Off-gas monitoring of experimental reactors give little information about intermediate reaction products and reflect chemical equilibria at reduced gas temperatures. A reactor design with optical access was designed and tested in order to be able to qualify and quantify gaseous species from their emission spectra. By use of a sequence of sapphire, UV fused silica and IR transparent sapphire and CaF2 windows and lenses optical access to a hot, maximum 1800 °C, reaction zone was gained. A cooled area behind the reaction zone was used as a background in order to avoid signal saturation from reactor walls. In addition to molecular emission spectra, atomic emission lines are used to characterize stable gas constituents and radicals. The setup has been designed for the study of methane dehydrogenation experiments in order to investigate the carbon activity of reduction of oxide with methane, but has also been used to monitor gaseous silicon suboxide.

Jan 1, 2015

By R. Vasant Kumar

Measurement and control of trace elements in molten metal are often critical in order to achieve optimum production, refining, alloying or recycling. Solid electrolyte sensors for monitoring oxygen and very recently for hydrogen have made major impact in the metal industry. It has not proved straightforward to develop solid electrolyte sensors for many other elements that can be industrially applied in metal production. Novel self-tuning chemical sensors have been developed by the authors that may open up new technological opportunities. Three such examples will be presented in this paper: (i) a self-selecting oxygen-sulfur dual sensor using a composite beta-alumina/zirconia solid electrolyte; (ii) a copper sensor for liquid matte based upon cusicon solid electrolyte operating in a current reversal mode; and (iii) an aluminium sensor on solid NaCl containing channels of molten NaAlCl4 electrolyte formed by electrochemical charging in molten zinc.

Jan 1, 2006

By S. Kang, D. G. C. Robertson

Slag cleaning furnaces require extensive wall cooling because they involve the use of a superheated slag bath. This is in direct contrast to smelting furnaces, where the wall is usually (but not always) protected by "banks" of solid charge. In order to understand the heat transfer and flow in slag cleaning furnaces a number of model studies have been carried out using molten wax to simulate the slag. Wax is a good model fluid because, like slag, it has a high Prandtl number. Wax models cannot simulate the behavior close to the electrodes (DC arc or AC submerged), but they can and do give a good simulation of the flow and heat transfer at the wall. An understanding of these phenomena is of great importance for the design of cooling panels in the walls of the furnace. Since superheated molten slag will eventually wear away any refractory bricks over time, the wall cooling must be designed to form a frozen layer of slag, referred to as a "freeze lining". The heat flux density (Q/A) required to do this is given by Q/A = h* ?T, where h is the heat transfer coefficient in the slag phase at the wall, and Li T is the superheat (bulk slag temperature - liquidus temperature). Both Q/A and h vary greatly with position and both are usually a maximum at the slag line. In the experimental work, molten wax baths were heated by block heaters to provide similar energy densities to those encountered in commercial slag cleaning furnaces. This procedure was considered to be valid since most of the electrical energy into a furnace bath is dissipated as heat. Gas stirring was used to simulate the gas evolved at the electrode in real furnaces - the quantity of this gas could be estimated from a knowledge of electrode consumption. The similarity criterion was equal gas flow per unit area of surface, in model and prototype. Heat transfer coefficients were measured in the models as a function of power density, gas stirring, superheat, etc., and could be related to the full-scale operations by the use of dimensional analysis.

Jan 1, 1999

By Musa Karakus

Ceramic build-ups are synthetic mineral deposits formed in critical locations in or near the throats of inductor units in channel induction furnaces, the preferred melting and holding furnaces used in iron foundries. The build-ups are undesirable because they slow down melt circulation, increase power consumption and cost. and decrease the quality of the metal. This study involved the determination of the mineralogy of build-up samples and the quantitative measurement of phase abundance in those build-ups by cathodoluminescence microscopy. These undesirable deposits usually are hard and dense and contain variable amounts of entrained metallic iron. The non-metallic phases dominantly consist of oxides and silicates of several refractory elements, AI, Mg. Ca, Si, and Fe. Minor amounts of the sulfides of Ca. Mg, Fe and REE elements, especially Ce and La. and the oxides and silicates of Ce and La elements are locally present in the build-ups. The build-up samples were found to be ideally suited for study by cathodoluminescence, which has provided an easy means for rapid re-cognition of the phases present in the build-ups. The phase compositions were determined by electron microprobe analysis. The phases identified and their characteristic cathodoluminescence shown in the ceramic build-up samples were: spinel (bright green, blue-green, and red). forsterite (red and purple), periclase (dark reddish-brown, blue. and orange), corundum (red, blue, orange, and white), anorthite (yellow, yellow-green, blue, and blue-purple), hibonite or calcium hexaluminate (dark green), mullite (dull red-brown), gehlenite (deep blue), silica(dark brown, pink, purple, red. and blue), monticellite (light violet blue and light pale yellow-orange), silicon carbide (orange), oldhamite (bright yellow and orange). Ce-La silicate phases (purple), and glass (orange, dull red, and purple). Non-luminescent phases were: hercynite, Fe-oxides, Ce-La-oxides, Fe-sulfides, and metallic iron.

Jan 1, 1989