Peculiarities of Phase Creating in the Ag-Fe-Graphite Compositions during Processing by Electric Current

"This paper is devoted to scrutiny problem of obtaining electro-contacts by electro-discharge sintering technology. A new unconventional method of electro contacts production (on Aggraphite base) can yield essential optimization resource.Review of three electro-technological methods of processing contacts materials is presented:- using graphite powder cladded by Ag;- mixture of graphite powder(which is a non-cladded powder) with Ag powder and addition of Fe powder particles;- method of infiltration of melted Ag into graphite piece without deformation and rupture of object.This technological approach can give the possibility to increase of compression strength of electro-contacts materials up to 340 MPa and more under conditions of additional reinforcing components (for example, by Fe).IntroductionThe electric current can be an active ""participator"" of the powder metallurgy technology [l]. At the passage of electric current through powders or some powder mixtures the phenomena including phase transformations arise. Here such effects, which are observed in the Ag-graphite and Ag-Fe-graphite powder mixtures and in the pair Ag-porous graphite, are described.The Ag-graphite composition materials (CM) are used, for example, as electric contacts [2, 3]. Since a material being produced is destined for the contacts it is necessary to take into account the following aspects: commutating current, its character and voltage, active or reactive character of working load, geometrical dimensions of contacts, quantity and frequency of switching on and switching off, pressure on contacts, distance between contacts, method of arc control, surrounding medium, its content, pressure and temperature. Thus, these and, maybe, choice of some other circumstances influence design, materials and production technology of contacts. The range of problems concerned dictates such steps as alloying of contact materials, optimization of structure, selection of kind of graphite, its connection with metal [4-10]. It is expedient to recall the main procedures of the first stage of the conventional technology: dosage of the initial graphite powder and binder-phenolic resin plastic varnish (for example, Bakelite), mixing, densification, thermal treatment, crushing, grinding, sieving, drying, dosage of grained graphite, dosage of the initial silver powder, obtaining of the silver salt solution, settling of salt, filtration, washing, drying of the cladded graphite powder, thermal treatment, obtaining of the graphite powder of particles cladded by silver. The second stage of the convectional technology starts by obtaining of the cladded graphite powder and finishes by annealing of the pressed blanks (Fig. 1)."