By Y. C. Liu, R. H. Richman

The effects of gel,manium and tin on the deformation and 9-e-crystallization textures of copper have been explored in detail with in the copper-rich terminal solid solutions. Addition of solute to copper produces a change in deformation texture from the copper type to the 70 :30 brass type. This transition has been measured quantitatively The types mid proportions of recrystal-lization components have been determined as a function of com-position, and correlation of recrystallization components with specific deformation components is discussed. On the basis of information available in the literature, it has been suggested that the effect of solute elements on the recrystallization texture of copper

Jan 1, 1961

By H. W. Highriter

THE method developed and used in this laboratory for the production of metallic uranium of such purity that it is ductile and can be cold-worked to fine wire or thin sheet by rolling has already been described1. It consists, briefly, in the electrolysis of potassium uranous fluoride (KUF5) in a molten bath composed of equal parts of sodium and calcium chlorides. The bath is contained in a graphite crucible, electrically heated to about 775° C., the crucible serving as the anode for electrolysis. The uranium deposits in finely divided form mixed with salts upon a molybdenum cathode suspended axially in the crucible. Upon com-pletion of the electrolysis the cathode is removed and cooled, the deposit broken and leached to remove salts. The metal powder is washed with water and dilute acetic acid and dried in vacuo to reduce oxidation. Suitable amounts are then pressed into pellets and heated in vacuo by high-frequency induction, using a thoria crucible. The uranium melts and flows away from the pellet, leaving a shell, which is largely oxide. In general, this method produced a satisfactory metal, although at times the uranium was not ductile. The investigations recorded here were made to find the cause of this embrittlement. It was known that the metal generally contained carbon, derived from disintegration of the graphite crucible in which electrolysis is conducted, in amounts dependent upon the thoroughness of washing the metal powder. Accordingly, analyses of several samples, both ductile and brittle, were made by combustion and absorption of C02 in Ascarite, using air instead of oxygen to reduce the temperature and rate of oxida-tion. Several of these metals were made with special precautions to reduce carbon content. The results show no relationship between ductility and carbon content in the range investigated (Table 1).

Jan 1, 1935

IT is difficult to judge how much influence the success attained during its first year, 186465, by the School of Mines at Columbia had on developments in education for the mineral industry elsewhere in the immediately subsequent years. The facts are as follows: 1. The Massachusetts Institute of Technology began giving instruction in February 1865, with a mining course included in its curriculum. 2. Early in 1865 the faculty of the Department of Science, Literature and the Arts of the University of Michigan requested permission from the Regents to establish "a course of study to be called the School of Mines . . . Also that the degree of Mining Engineering be conferred on students who should complete the course of study prescribed in the same." A resolution authorizing this was adopted by the Regents on March 28, 1865. 3. Samuel Hooper endowed a Sturgis-Hooper professorship of geology at Harvard in 1865 with the intention of making it a nucleus of a new School of Practical Mining and Geology. 4. Yale appointed Alfred P. Rockwell professor of mining in 1865. 5. Lafayette College appointed Henry S. Osborn professor of mining and metallurgy in 1865. 6. Washington College (as Washington and Lee was then known), rising out of the ashes of Civil War destruction, made a fresh start in 1865, with General Lee as its president, and offered a mining course in the first catalogue thereafter published. 7. Lehigh University, founded in 1866, had a mining curriculum from its beginning. 8. Rensselaer Polytechnic began offering a curriculum in mining and metallurgical engineering in 1867. It would be natural to suppose that these events were a reaction to the success of the school at Columbia, and possibly they

Jan 1, 1941

By R. J. Franklin, G. W. Beckman, D. Warren, E. Both, J. F. Libsch

BINARY and ternary alloys of iron, nickel and cobalt respond to annealing in a magnetic field by a characteristic change in the shape of their hysteresis 100p.l,2 An increase in retentivity and a decrease in coercive force produced by the magnetic treatment cause the hysteresis loop to approach the appearance of a rectangle. Materials with a rectangular hysteresis loop have made possible the contact-rectifier³ and have greatly improved the performance of pulse transformers4 and magnetic amplifiers." In the best material presently available for these applications, a 50 pct nickel-iron alloy," the desired characteristics are achieved by aligning the preferred crystallographic directions of magnetization along the rolling direction of the tape. The objective of the present study has been to produce rectangular hysteresis characteristics in materials with inherently high saturation. Iron-cobalt alloys, exhibiting saturation values up to 24,000 gausses' appeared to offer promise for the magnetic annealing technique, because they remain magnetic to very high temperatures,8 exhibit favorable magnetostriction properties: and show zero crystal energy at 42 pct cobalt.10 Among the ternary iron-cobalt-nickel alloys,7,11 response to heat treatment in a magnetic field is unfortunately limited to alloys having rather low saturation values.' It appeared interesting nevertheless, to study a series of compositions connecting the optimum composition (50/50) of the binary iron-cobalt system with the "Perminvar" composition (30 pct Fe, 25 pct Co, and 45 pct Ni). Very recently, R. Smoluchowski and R. W. Turner," have shown that under certain circumstances magnetic annealing can produce oriented recrystallization. A combination of this technique with the domain orientation utilized in the present study might well result in further improvements. The advantages of the powder metallurgy technique in preparing magnetic alloys for study have

Jan 1, 1951

By H. E. Howe, A. A. Smith

E. Schumacher.*—Mr. Smith has shown us once again how variable lead alloys can be. I have studied lead alloys for a good many years and know from experience that their behavior cannot be predicted by analogy with other alloys. I have always been interested in observing how the creep resistance of lead may be improved by the addition of as little as 0.03 per cent Ca. Without the presence of calcium the grains of extruded lead pipe are fairly equiaxed and motion can take place easily at the boundaries. The calcium addition of 0.03 per cent causes the grain boundaries to become very irregular and jagged, and results in creep resistance many times greater than that of pure lead. Mr. Smith showed that in the one per cent antimony-lead alloy creep is occasionally excessive even where low stresses are involved. We have observed this phenomenon many

Jan 1, 1945

By B. R. Palmer, G. Gutierrez B., M. C. Fuerstenau

Selective flotation in nonmetallic systems is often complicated by the presence of iron-bearing silicates occurring as gangue. Minerals such as augite, diopside, hornblende, and tourmaline respond readily to flotation under the same conditions as ore minerals. Mechanisms by which these minerals respond to flotation with anionic collectors must be established if selective separations are to be made in these systems. It was the objective of this investigation to determine the mechanisms involved in the flotation of two pyroxenes, augite and diopside, with potassium oleate. Experimental Materials and Methods Pure potassium oleate, prepared by neutralization of oleic acid with KOH, was used as collector, while reagent-grade HC1 or KOH were used for pH adjustment. Conductivity water, made by passing distilled water through a mixed-bed ion exchange column, was used in this investigation. Two pyroxenes, [ ], were involved in this work. One member of this class of minerals was augite and was found to contain 3.3% calcium, 4.6% iron, and 9.6% magnesium. The source of this mineral was Tillamook County, Ore. The other pyroxene involved was diopside which contained 8.3% calcium, 2.7% iron, and 7.6% magnesium. The source of this sample was Bancroft, Ont. Microflotation experiments were conducted with a Hallimond cell. Mineral samples were ground dry and sized to 100 x 200 mesh. One-gram charges were conditioned for 3 min in the presence of various additions of potassium oleate. Flotation was conducted for 1 min with a nitrogen flow rate of 50 cm3/min. The electrophoretic mobilities of these two minerals were measured with a Zeta Meter in the absence and presence of [ ] salts and in the presence of an indifferent electrolyte, NaC1, added to maintain ionic

Jan 1, 1978

By H. C. Gatos, Ahmed Azzam

A UTORADIOGRAPHY would appear to be sim-A pler and less time-consuming for diffusion studies than any of the radioactive tracer techniques commonly employed, namely, the sectioning, surface increase, and surface decrease techniques.' Accord- ingly, it was felt worthwhile to investigate the applicability of autoradiography to self-diffusion measurements, and gold was chosen for this purpose. The radioactive isotope Au'!'' was used, as obtained from the Brookhaven National Laboratory. Its radiation consists of p (0.97 mev) and y (0.41 mev) rays, and it has a half-life of 2.69 days. No-Screen X-ray film was found suitable for these experiments: the film has the desired high speed for recording P rays and yet is practically insensitive to y rays. On the other hand, due to the high atomic weight of gold, this metal is a strong absorber for p rays. The

Jan 1, 1953

By Jacob T. Wainwright

This stove has been designed to meet the requirements of a fur nave that must be operated with either a reducing or a neutral flame ; and more particularly to make feasible the operating of re duction-furnaces with the cheaper grades of gas-fuel, which has heretofore been impracticable. In general, cheap gas-fuels result from incomplete combustion, and, being suited for further combustion, answer very well for heat ing purposes; and high temperatures may be attained with them, when they are used in conjunction with regenerative stoves. But, in operating a reduction-furnace, a high temperature is not the only requirement. It is also necessary that the fuel shall not be cansumed beyond a certain degree, in order to insure a re ducing flame for the reduction-process ; consequently, it becomes necessary to dispense with combustion as much as possible previous to the use of the fuel-gases in the reduction-furnace. Moreover, these gases must be preheated to a high degree, in order that a sufficient temperature may be maintained in the furnace; and, since this preheating cannot be accomplished by a previous, partial combustion of the gases themselves, it follows that the stoves for pre heating these gases should be heated to as high degree as it is pos sible to attain with an inferior fuel. This result can best be accom plished by complete combustion of the heating gases, and is further facilitated by preheating all of the air and gas used for this com plete combustion. It is more particularly desirable to preheat the air, since the combustible gases used may generally be obtained directly from the furnace, or gas-producer. The reducing gases, escaping from a gas-fuel reduction-furnace, are capable of considerable further dilution with air to secure com plete combustion, and consequently may be utilized for heating the stove to a high temperature, provided the air be sufficiently preheated.

Jan 1, 1889

By Guy W. Crane

The geology of the Tintie mining district, fully treated, would occupy an elaborate monograph. This less comprehensive paper is devoted primarily to the occurrence and origin of the orebodies of the district, while space is given to those phases of the general geology only which seem necessary to a proper setting of such a discussion. The first geological report on the Tintic district to be issued was that by Tower and Smith, published in 1899, in the form of a paper in Part III of the Nineteenth Annual Report of the U. S. Geological Survey, and also as Folio No. 65, Geologic Atlas of the United States. About four years ago a second investigation was begun by Waldemar Lindgren and G. F. Loughlin, of the U. S. Geological Survey. With the exception of a paper on the oxidized zinc ores of the Tintic district by Mr. Loughlin, the results of their work are still unpublished. The writer's acquaintance with the district began in the fall of 1913, and has extended over a period of about two years. 1. Location The Tintic district lies about 65 miles due south of Salt Lake City, and on the west central slope of the Tintic Mountains, a short range, which forms the connecting link between the Oquirrh Mountains on the north and the Canyon Range on the south—the group constituting the first of the Basin ranges to the west of the Wasatch Mountains. The productive portion of the district embraces an area about 6 miles long and 2 miles wide, which is divided between Juab and Utah Counties. Within this area are the towns of Eureka, Mammoth, Robinson, Silver City, and Knightsville. All these points are tapped by the Denver & Rio Grande and S. P., L. A. & S. L. Railways. 2. Topography As in most of the Basin ranges, topographic relief is strong, dropping rapidly from peaks of 8,100 ft. above sea level to elevations of 5,600 ft. in Tintic Valley on the west and 4,500 ft. in Goshen Valley on the east.

Jan 1, 1916

By Robert E. Green, T. Hinton

The velocities of the three possible modes of elastic-wave Propagation have been calculated for single-crystal aluminum at 1-deg intervals throughout the standard steveographic triangle. The results are presented as isospeed contours. The deviations between the direction of maximum energy propagation and specirzen axes are presented as arrows drawn within the standard triangle. The orientation factors associated with dislocation nzotion on the primary slip system only and also on all twelve slip systenzs have been calculated for all three elastic waves. The orientation factors associated with a longitudinal standing--7aue resonant specivnen hazle also been calculated. The relevance of these results to ultrasonic attenuation measurements is discussed. DUE to the widespread use of ultrasonics in the investigation of the properties of solids a number of authors15 have discussed in detail the theory of elastic-wave propagation in solids. In this paper the modes of wave propagation are evaluated according to the procedure suggested by reeen' for the case of single-crystal aluminum at 1-deg intervals throughout the standard stereographic triangle. The wave speeds are presented in the form of contour diagrams within the standard triangle. The deviations between the direction of maximum energy propagation and the normals to the wave fronts are presented as arrows drawn within the standard triangle. The orientation-de pendent factors (orientation factors) associated with dislocation damping as derived in the preceding paper6 have been calculated for the case of aluminum at 1-deg intervals throughout the standard triangle. The orientation factors for dislocation motion on the primary slip system only and on all twelve slip systems are presented in the form of contour diagrams, for both the traveling- and the standing-wave conditions. The relevance of these results to ultrasonic attenuation measurements is discussed. ELASTIC-WAVE PROPAGATION Three waves can be propagated in a linear elastic homogeneous anisotropic medium. The velocity of propagation v of each of these waves in a medium of density p can be obtained from the determination of the eigenvalues and eigenvectors of the matrix equa- The A's are a series of moduli which are functions of the elastic constants cij and the direction cosines 1, m, and n of the specimen axis. In the case of cubic single crystals where there are only three nonzero elastic constants cll, c12, and C, the A's are, The solution of Eq. [I] will give the wave speeds (eigenvalues) and the direction cosines a, 0, and y of the particle displacements (eigenvectors). To obtain the direction of maximum energy flux requires the calculation of the energy-flux vector ET with com- w is the angular frequency, A, the amplitude, and v the velocity of the wave. The direction cosines a, b, and c of the energy flux vector are then given by

Jan 1, 1967

By G. R. Love, M. L. Picklesimer

Aboue 950°C the Nb-Zr system consists of a completely miscible bcc solid solution, commonly called the phase. Between 950 and 600°C, and between 20 and 85 pct Nb, the phase deconlposes, after sunciently long times, into two bcc solid solutions. The pct Zr alloys are conveniently descibecl with T-T-T (time-temperature-transformation) curves having a nose at about 2 hr at 700°C. The reaction rate varies only slowly with zirconium content and negligibly with oxygen contanzination; it is speeded up by a factor of 10 to 15 by 90 pct cold ulork and slowed dou by n factor oj 10 to 30 by a two-hundrecljold increase in grain size. Nb-r alloys with compositions between 40 and 85 pct Nb have been the basis for the majority of commercially important superconducting materials. In part because of their commercial promise, more is known about these alloys than about most other high-field superconducting materials. At the same time, there is considerable disputed or incomplete metallurgical information. For example, although Rogers and tkins&apos; indicate a monotectoid reaction at approximately 600°C and a two-phase 01 + 0, field extending between 20 and 85 pct Nb and to a maximum of 95OGC, erhout&apos; has reported that this entire region would be a single homogeneous B were it not for oxygen contamination. Again, although it has been shown that relatively short-time heat treatments in the vicinity of 700CZ significantly improve the ability of short wire samples to carry high currents in high magnetic fields at 4.2K, these observations have never been fully correlated with the structural change or changes occurring during the anneal. We intend to investigate in detail the effect of metallurgical variables, including heat treatment, on the superconducting properties of hard superconductors. To verify that our experimental techniques are valid and to establish a relative standard against which other materials may be measured, we feel it advisable to know the behavior of the Nb-Zr alloys under a variety of processing conditions. As an initial step toward this goal, we have determined in detail the kinetics of the transformations in Nb-Zr alloys. EXPERIMENT A number of problems had to be solved before beginning any fruitful work on the reaction kinetics in this system. While solving some of these problems, either by chance or by design, small amounts of information were obtained about alloys containing 40, 50, 60, 65, 67, 70, and 75 pct Nb, bal. Zr. In addition, a large range of grain sizes and a range of temperatures considerably greater than the range indicated by Rogers and Atkins phase diagram were examined. We will, however, report in detail only the results obtained for the Nb + 33 pct Zr and Nb + 25 pct Zr alloys at three grain sizes, two levels of oxygen contamination, and the temperature range 550 to 950°C. These data are most complete, but the other data are sufficiently complete to indicate the kind and magnitude of the variation of the transformation kinetics outside this range. The first and most difficult problem encountered in this inquiry was one of sample homogeneity. When Nb-Zr alloys are arc- or electron-beam-melted on a cooled copper hearth, solidification is sufficiently slow that there is appreciable coring in the cast structure and a large variation of grain size across the button thickness. Both these factors significantly affect the apparent reaction rate in the system. A two-step solution to the problem was attempted; an arc-melting and drop-casting technique has been developed by conald that greatly reduces the as-cast grain size and virtually eliminates coring segregation. Ingots made in this way exhibited no detectable (3 pct maximum) zirconium segregation. Before it was evident just how good this technique was, we attempted to supplement it with rather long-time, high-temperature annealing of the cast ingots. This annealing was carried out in evacuated and sealed (seal-off pressures < 1.0 x 106 torr) quartz capsules lined with tantalum foil at 1400 to 1450 C for 8 to 72 hr. There were two principal effects of this treatment: the grain size increased to a fairly uniform 150 p, and the surface and all grain boundaries near the surface acquired a film of a second phase, tentatively identified as an oxide (possibly additionally contaminated with silicon). There was no evidence that this 1400 C treatment had affected the zirconium segregation. High-temperature annealing was subsequently used only for grain-size control, but anneals of longer than 4 hr at temperatures greater than 1000°C were performed in dynamic vacuums (pressure no greater than 1.0 x lo torr). Any contamination resulting from these treatments was well below the limits of detection of our techniques. All samples, as cast, were cold-swaged to at least 85 pct reduction in area. The samples called cold-worked were tested as swaged. The minimum re-crystallization anneal for these alloys was about 12 hr at 1050 C; this produced an equiaxed grain diameter of about 4 to 8 P. Annealing for 4 hr at 1450°C produced a grain size of about 80 to 150 p; and annealing for 4 hr at 1650aC, close to the melting point of many of these alloys, produced a grain size of 0.5 to 1.0 mm. At all temperatures, the larger grain size was

Jan 1, 1967

By C. R. Knopp

Gas-oil relative permeability ratio is an important relationship in oil reservoir predictive calculations. A correlation has been developed from 107 gas-flood k/k tests on Venezuelan core samples. The correlating parameter is based on restored-state water saturation tests and&apos; is applicable to both consolidated and poorly consolidated sandstone reservoirs. Data of the correlation show that there are no distinguishah1e differences between the mass-data groupings for the two c1assifications A procedure is recommended for running .sufficient relative. permeability analyses to compute a geometric mean of the sample group. The geometric mean is more representative of the total core, and probably the entire reservoir. For example, while only one in four of the k,,/k,., test curves agreed closely with the resultant correlation of this report, the geometric mean curves of the 16 suites (three samples or more). showed good agreetment ill three cases out of four. INTRODUCTION The gas-oil relative permeability ratio is an important, fundamental relationship in most oil reservoir predictive calculations. Predictive calculations are made to estimate future reservoir production characteristics and ultimate oil recovery. The k1,/k2, relationship is specifically needed to relate the surface gas-oil ratio to the reservoir oil and gas saturation, and to calculate the relative movement of these phases within the reservoir whenever some of the more complex driving mechanisms are present. Laboratory k1/k2, tests are not generally run as a routine analysis. Consequently, k1/k2 data often are not available when needed because the cost of laboratory work could not be justified or the need for such data had not been properly anticipated. When laboratory k1/k2, data are available, they are often very difficult to interpret. For example, wide divergence is sometimes shown in a family of k1,/k1, tests representative of the producing horizon in a single well. With these considerations in mind, a study was made to determine if a relationship might exist between the k1,/k2, curve and some other simple laboratory test criteria. The most probable k1/k2, curve correlation for Venezuela described in this paper is the result of the investigation. The presented correlation defines the most probable gas-flood k,,/k,, curve through the medium of air-water capillary displacement and centrifuge water saturation tests. The laboratory procedures of these tests are. relatively simple, and inexpensive; test data should be. widely available- from routine analysis. DATA AVAILABLE, LABORATORY METHODS The report correlation utilized 107 gas-Hood k1/k2, tests run on sandstone cores of Venezuelan reservoirs. Table 1 is a general tabulation of data pertinent to the tests, while Table 2 summarizes the data. Thetests include 96 from Western Venezuela and 11 from Eastern Venezuela. Eighty-two- of the 107 test samples were sandstones that varied from poorly consolidated to-unconsolidated; 25 were consolidated. The average sample porosity was 26.7 per cent and the average permeability was 1,121 md; these values typify the better sandstone reservoirs of&apos; Venezuela. The Welge gas-flood technique,&apos; based on fundamental Buckley-Leverett frontal displacement theory, was introduced in about 1952 and is widely accepted in the industry. The laboratory procedure is relatively simple, rapid, and can be performed on small core samples. While there have been some minor variations in sample preparation and laboratory procedure in the tests used for the correlation, these tests can be generally summarized as follows. The core sample was first sol vent-extracted and dried. Connate-water saturation was restored by the oil-flushing or evaporation-blow down methods. At the beginning of gas flood the hydrocarbon pore volume was completeiy saturated with the test oil phase. Unsteady-state gas-oil displacement then began with the injection of nitrogen or helium. while the displaced oil and gas phases were incrementally metered at the out-flow face. From the test data, the k,,/k,, curve was calculated by the Welge method.&apos; The individual oil and gas relative permeabilities were also calculated." CORRELATING PROCEDURES In attempting to establish a basis of correlation, we found that broad mid-range sections of 105 of the 107 k,,/k,, test curves could be closely duplicated by a straight line. Only two curves did not show a degree of linearity in this region. Correlation-curve definition parameters were subsequently developed from this observation of consistent mid-range linearity. Possible correlating variables were limited to the physical properties measured on core samples that (1) were widely available as common test data and (2) could be easily and cheaply obtained through future laboratory work. The more obvious possibilities were porosity, permeability and

Jan 1, 1966

By Claus G. Goetzel

SOME of the reactions and procedures upon which modern techniques in the production of metal powders are based were used for 2000 years by the ancients to reduce iron and other metals from their ores. Despite this, however, the art of powder metallurgy is relatively new and probably stems from the introduction of incandescent electric lamp filaments. Attempts to improve upon Edison&apos;s carbon filaments led to the production, in order. of metallic filaments of osmium. tantalum.. and finally of tungsten, which ha, replaced the others and is the commercial product of today. These metallic filaments were originally manufactured by the extrusion and sintering of a mixture of the metal or its oxide with a reducing agent which also served as a binder. Further progress in this direction was in the pressing of a small percentage of nickel with the tungsten. The sintering operation was carried out in an atmosphere of hydrogen, at a tem-

Jan 1, 1944

By G. R. Wilms

A study has been made of the structural changes in polycrystalline high purity aluminum during the tertiary stage of creep under conditions of constant tensile load. It appears that there is no basic modification in the particular mechanism of deformation that characterized the preceding secondary stage of creep, but that the changes in crystalline structure produced during the tertiary stage are only a consequence and not a cause of the accelerated strain. Intercrystalline fissures were observed on entry into the tertiary stage, and these might supplement the accelerated rate of strain owing to local stress concentrations. There is evidence that the formation of these fissures may be associated with the presence of surface imperfections, and it is suggested that a more generalized treatment of the results may explain certain creep characteristics of commercial alloys. IN previous work&apos;-4 a study was made of the changes produced when specimens of annealed aluminum were deformed at various temperatures and rates of strain, especially under conditions leading to creep under constant tensile load. It was shown that, as the temperature was increased or as the rate of strain was decreased, elements of the substructure produced within the grains became coarser, and with the strain rate constant at a given temperature, their size tended to an equilibrium value. The preliminary process of the breaking down of the grains into a substructure was identified with primary creep.&apos; The subsequent equilibrium, condition was associated with secondary creep. The question then arose whether the tertiary stage corresponded to any further significant change in the substructure. The question is also of interest in view of the opinion, expressed for instance by Andrade,5 that the tertiary stage is merely an accelerated rate of strain due to the reduced area of section of a specimen under continuous tensile load, and the other opinion, as suggested by the observation by Sully, Cale, and Willoughby6 of a tertiary stage in com-pressive loading, that this third stage is a real effect in its own right. The object of this paper is to record some observations on the tertiary stage of high purity aluminum. Experimental Procedure The material was aluminum of 99.98 pct purity as previously used. The specimens had a rectangular section of l/8 x l/2 in., and extensions were measured over a 1 in. gage length. After machining to shape, the specimens were annealed to give a standard grain size of 0.2 mm and then electropolished. The general procedure involved metallographic and X-ray diffraction examination at progressive stages of elongation (marked by arrows on the curves shown in Figs. 1 and 2), the specimen being extended to fracture under constant load at a given temperature. The X-ray tests were made by the back-reflection method from a stationary specimen, using CoK radiation. The longer edge of the micrographs in the paper corresponds to the direction of applied stress. Results The previous work showed that, in the secondary stage of creep in aluminum, three basic types of structure could be developed according to the temperature and rate of strain. These were: 1—slip, which predominated at the lower temperatures and higher rates of strain and produced the finest and least perfect substructure; 2—cell structure, which superseded slip as the temperature was raised and the rate of strain decreased and which was characterized by a coarser and more perfect structure and an absence of slip lines; and 3—a stage termed "boundary microflow," which predominated at still higher temperatures and lower rates of strain when the cell size had increased and become comparable

Jan 1, 1955

By Myers, J. F.

The purpose of the mill tests reported herein, was to determine the relative power efficiency of fast and slow rod mill speeds on the ores of the Tennessee Copper Co. The tests were carried out at the lsabella Mill of the Tennessee Copper Co. under normal operating conditions. Every effort was made to keep the ore supply and other conditions constant, but it will be noted that some slight variation did occur. The open circuit 6 by 9 rod mill, and ore, used in these tests have been previously described.&apos; Four motor drive pinions were available and the tests were performed in the following manner: each pinion was used to drive the mill for a period of one week. Constant sampling prevailed during the test run, and a composite sample for each speed test was made. Realizing that some slight liner wear took place during the four-week test-run, and that some slight variation of the ore may have taken place, a second and then a third series of four-week test- runs were made with the four different pinions. The screen analysis of each of the thee-week run samples at the various speeds were composited and the results are shown in Table 1. The authors feel that the 12 weeks of operation consumed during these test-runs would represent fairly the effect of each mill speed. The data of line 37 show that within the error of sampling and plant operation, the tons of minus 65-mesh material generated per horsepower hour was the same at all four speeds.

Jan 1, 1949

By A. M. Gaudin, D. W. Fuerstenau

By streaming potential techniques, the zeta potential of quartz has been measured as a function of the concentration of dodecylammonium salts at different pH values. These experiments indicate that adsorption of dodecylammonium ions takes place as individual aminium ions until a certain critical concentration is reached in the double layer, at which point the adsorbed collector ions begin to associate into patches of ions, called hemi-micelles. Because of its effect on the surface potential of quartz, pH controls the adsorption of dodecylammonium ions. The value of cooperating agents and nonionized constituents of flotation systems is discussed. A PREVIOUS investigation&apos; of the role of pH in the flotation of quartz with anionic collectors is here extended to an inquiry of how the cationic collector, dodecylammonium acetate, is adsorbed at the quartz-solution interface. The equilibrium amount of this collector adsorbed by quartz has already been measured as a function of concentration and pH.2,3 The weight of prior evidence has suggested that two mechanisms are involved in the adsorption of this collector by quartz, but with existing adsorption measurements alone it is not possible to determine what the mechanisms are. Gaudin and Bloecher2 postulated that a polymolec-ular adsorption coating begins to form before the first monolayer has been completed. Gaudin and Morrow4 indicated that a similar situation might exist in the film of dodecylammonium ions on hematite. A study of electrokinetic potentials at the quartz-solution interface provides some detail toward a fuller understanding of the adsorption mechanism. Experimental Results The zeta potential at the quartz-solution interface was calculated from streaming potential data measured with the apparatus described in detail in a thesis by Fuerstenau5 and briefly in a paper by Gaudin and Fuerstenau.1 The quartz used in these experiments was a 48/65-mesh fraction prepared in the manner described previously.&apos; Zeta potential of quartz was obtained for various amounts of the amine salt at pH 4, 7, 10, 11. In

Jan 1, 1956

By R. E. Cuthbertson

AN early appreciation by the management that Climax ore presented a challenging problem of economic concentration was responsible for the establishment, in June 1926, of an ore-testing department at the experimental plant of the Colorado School of Mines at Golden, some ninety miles from Climax. An engineering office was later organized in the same community for the design of all ore-treatment units erected at Climax during the period of rapid growth. Work of the ore-testing and design staffs was effectively co-ordinated under a common head. The primary reason for having the ore-testing and plant design departments in Golden, was to place these activities under the able supervision of A. J. Weinig, consultant for the Climax Molybdenum Co., and director of the experimental plant. A secondary consideration was the availability of excellent facilities for research in ore dressing in a highly favorable environment. Concentration of molybdenite by flotation from an ore of simple mineral composition does not appear, superficially, to present a serious problem in ore dressing but experience belies this apparent simplicity. The molybdenite content of average Climax ore is low and it is finely

Jan 1, 1946

By A. H. Larson, R. J. McClincy

The activity of Sb,03 in PbO-Sb,03 slags containing less than 50 mol pct Sb,03 was determined by the inert-gas saturation method at 700°C. In this composition range, the activity gf SbzO3 shows a strong negative deviation from ideality. The activity of PbO in these slags was calculated by application of the Gibbs-Duhem iniegration to the Sb203 activity data. The calculated activity of PbO in slags containing more than 63 mol pct PbO was found to deviate in a positive direction from ideality uthile a negative deviation was found for slags containing less PbO. The standard Gibbs free energies of formation of Sb,03 and PbO. Sb203 have been calculated and compared with existing data in the literature. The activity of Sb203 in PbO-Si0,-Sb203 (PbO/SiO, = 2) slags containing less than 25 mol pct Sb,03 was also determined by the inert-gas saturation method at 700°C. In this composition range, the activity of Sbz03 shows a very large negative deviation from ideality. VERY little experimental work has been published in the past to determine equilibrium data in the oxide systems connected with the refining of lead. These data are of value since impurities such as antimony, arsenic, and tin must be removed from lead and recovered for further treatment. Equilibrium studies on antimony and arsenic systems are also of interest for the design of new processes for lead refining and lead dross treatment. Maier and ~incke&apos; first determined the liquidus curves for the PbO-Sb203 system and identified the compound PbO . Sb203. They found the phase diagram for this system to be two simple eutectics located on either side of the congruent melting compound. They also determined a very limited amount of vapor pressure data for Sb406 abbve PbO-Sba3 melts at 697"~. A second phase diagram investigation on this system was reported by Hennig and Kohlmeyer&apos; who confirmed the existence of the compound PbO . Sb203 as well as the form of the diagram. A disagreement was noticed, however, in that their liquidus temperatures over nearly the entire composition range were higher than those reported by Maier and Hincke. Barthel~ and pelze14 redetermined the liquidus curve at the PbO-rich end of the PbO-Sb@, system and agreed very closely with the results of Maier and Hincke. None of the investigators mentioned above reported any mutual solid solubility in the PbO-SbD3 system. Zunkel and Larson5 have determined the phase diagram for the PbO-rich end of the PbO-Sb203 system by slag-metal equilibrium studies in the Pb-PbO-Sb203 system and by thermal analysis studies in the PbO-Sbz03 system. A maximum solid solubility of 5.6 mol pct Sb203 in PbO was observed at the eutectic temperature of 604°C. Their results for the phase diagram agree favorably with those of Maier and Hincke. The vapor pressure of Sb2O3 in the temperature range from 470" to 800°C has been determined by Hincke, using a modification of the transportation meth~d.~ His results for temperatures below the melting point of Sba3 are the only data reported in the published literature. The predominant vapor species has been shown to be Sb,06 by Norman and staley.? Myzenkov and Klushin,8 using the boiling-point method, have determined the pressure of Sb406 above liquid SbD3 in the temperature range from 715" to 1025°C. The agreement between these two studies is not very close. A portion of the discrepancy lies in the fact that Hincke used silica crucibles, which were attacked by the liquid Sbz03 at high temperatures. This fact does not account, however. for the large difference observed at the melting point. ~aier&apos; gives a brief summary of vapor pressure data for Sb,O, above pure liquid Sbz03 which agree quite well with the data of Myzenkov and Klushin at temperatures near the melting point. This paper describes the determination of Sb2O3 activity data in the PbO-Sb203 and Pb0-Si02-Sb203 (PbO/SiOz = 2) systems by the inert-gas saturation method. These activity data are compared with the data calculated by Zunkel and arson. EXPERIMENTAL Materials. The materials used in this investigation were analytical reagent-grade PbO (99.8 pct PbO, 0.14 pct insoluble in CHsCOOH, 0.02 pct not precipitated by HB, 0.1 pct CaO, and 0.08 pct SiOz), Sbf13 (99.6 pct Sb203, 0.004 PC~ C1-, 0.005 PC~ SO;-, 0.15 p~t AS, 0.001 pct Fe, and 0.03 pct other heavy metals such as Pb), and SiOz (chromatographic grade). Apparatus for Vapor Pressure Determinations. The apparatus used in this investigation consisted of a transportation reaction system with two separate gas trains. The argon transporting gas was first mixed with a small amount of hydrogen, metered, and dried by passage through silica gel and anhydrone drying tubes arranged in series. After this preliminary drying, the argon was passed through copper wool at 500°C to convert the residual oxygen to water vapor which was removed by three anhydrone drying tubes. A second stream of argon was metered and dried and then passed around the outside of the alumina reaction tube to flush away the volatile species to pre-

Jan 1, 1970

By Wittenau, E.

OPERATION of a pilot mill of 100 tons&apos; daily capacity during 1930 and 1931 proved that the copper minerals of the Colorado and Clay sections of the Morenci ore body could be successfully concentrated by the flotation process. Economic conditions caused postponement of further testing work until late in 1938 when the former No. 6 Concentrator at Morenci was converted into an experimental mill of 1500 tons&apos; daily capacity which was known as the Test Concentrator. The Test Concentrator began continuous operation on April 3. 1939, using such crushing and grinding equipment of the No. 6 Concentrator as was appropriate. Modern classifiers and certain flotation machines were installed and later other types of flotation machines, a large grate-type grinding mill. mechanical screens, a short-head cone crusher, and a disk filter were added to the test equipment. Operation was uninterrupted until Dec. 31, 1941.

Jan 1, 1942

By W. B. Humes

The use of high vacuum on a large industrial scale in the ferrosilicon process for the production of magnesium marks the coming of age of an important new metallurgical technique. The economical production of reactive metals, such as magnesium, which combine with all the well-known furnace atmospheres, has until recently been successfully carried out only by electrolytic methods. It is now apparent that, through the use of high vacuum, the distillation or sublimation of many metals can be done industrially at much lower temperatures, and hence in much simpler equipment, than heretofore has been thought possible. At the beginning of the present emergency, when the ferrosilicon process of producing magnesium was brought to the fore, little was generally known about vacuum engineering, practices, and techniques. In a comparatively short time, the available equipment has been adapted, new equipment designed and built, and a fund of know-how evolved to make possible the production of thousands of pounds of magnesium per day at pressures less than 1/ r0,000 of an atmosphere. Pilot-plant operations have been consistently maintained at pressures even as low 2s one micron (0.001 mm.). These low pressures, which previously were regarded as prohibitively costly or impossible to attain, have been demonstrated as economically feasible on an industrial scale. Necessity for Vacuum The main function of vacuum in the ferrosilicon process, and hence in most vacuum smelting processes, is to lower the temperature at which the metal may be distilled or sublimed from the reduction mixture. A secondary function is to protect the distilled metal from attack by the furnace atmosphere and to permit the formation of a dense condensate. In the ferrosilicon process, magnesium is formed by the reaction between dolomite and ferrosilicon: 2(Mg0-Ca0) -\- HFeSU / t=> aMg + MFe + (CaO)2-SiO2 The metal is distilled from the pelleted charge at a free air pressure of about 0.100 mm. of mercury (100 microns). This low pressure is not needed for the reaction, but rather serves to protect the metal vapor from the oxygen or nitrogen of the atmosphere and permits the formation of a condensate free of pyrophoric material. The reaction proceeds at air pressures as high as several millimeters of mercury, and evidence has been offered to show that the actual equilibrium pressure of magnesium at operating temperatures of 2I50°F. is somewhat higher. Experimentation indicates that the yield begins to decrease at pressures above 500 microns. While no real operating data are yet available on the relationship between

Jan 1, 1944