By Tabbetha A. Dobbins

We report studies concerning the time frame for catalytic reactions between NaAlH4 (sodium alanate) and TiCl3 during high energy milling. Spectral features in x-ray absorption spectra were analyzed for samples milled for various times (0 minutes, 1 minute, 5 minutes, 25 minutes, and 125 minutes). A structural transition from Ti3+ to Ti0 is observed within the first 5 minutes of milling. The Ti0 structure persists for samples milled for times longer than 5 minutes?even after those samples underwent a subsequent single hydrogen desorption/absorption cycle. Samples milled for less than 5 minutes retain Ti3+. For samples milled for 1 minute, the Ti-K edge position shifts from Ti3+ to Ti0 after a single desorption/absorption cycle. However, the first coordination sphere around the Ti0 absorber occurs at longer distances for 1 minute milled sample. These results hint at the formation of Ti0 pure metallic clusters upon desorption/adsorption cycling of 1 minute milled sample. Previously reported x-ray absorption spectroscopy studies have demonstrated the structural transition from Ti3+ (in TiCl3) to Ti0(determined to be TiAl3 found at the surface of the alanate powder). Aluminum deficiency on the NaAlH4 lattice is responsible for controlling hydrogen absorption capacity. These time-resolved spectroscopy studies suggest the possibility for controlling aluminum deficiency, while still maintaining titanium activation of the alanate powder, by manipulating the coordination environment of the titanium dopant during the first five minutes of high energy milling. Specifically, a possible approach to mitigating aluminum deficiency during doping would be to introduce an alternative species to which the to Ti3+ catalyst would form a metallic bond after the TiCl3 has attached at the surface of the sodium alanate powder and before the Ti3+ forms the TiAl3 intermetallic species.

Jan 1, 2006

By Bart Blanpain, Muxing Guo, Zhuangzhuang Liu

In order to stabilize free lime in the basic oxygen furnace (BOF) slag to achieve high value products, quartz sand and other additives are injected into slag. However, the current hot stage slag stabilization does not work in case of slag (before treatment) with a liquid fraction lower than 90%, where the slag containing solid particles is too viscous. Therefore, it is essential to understand how solid phases affect the viscosity of the slag system. In this study, the industrial BOF slags were investigated with respect to the correlation between volume fraction of solid phases and its viscosity. Slag viscosity was measured with a rotating type viscometer at temperatures below the liquidus. The volume fraction of solid phases was quantitatively calculated with FactSage. The Einstein-Roscoe equation was employed to predict the viscosity of BOF slag.

Jan 1, 2016

By N. Kanari

The kinetics of oxychlorination of MgO by C12+02 was studied in the temperature range of 850 °C - 1025 °C, using thermogravimetric analysis. The effects of C12/02 ratio, gas velocity, temperature and partial pressure of reactive gases on the reaction rate were investigated. The oxychlorination process was characterized by an apparent activation energy of about 214 kJ/mol. The reaction orders with respect to C12+02, C12 and 02 at 950 °C were about 0.65, 0.98, and -0.37, respectively. Some data about oxychlorination kinetics of MgO, Cr2O3, and MgCr2O4 contained in chromite were compared. Efficiency of using oxychlorination for the removal of iron oxides contained in magnesia was demonstrated.

Jan 1, 1999

By Wayne Bell, Matthew Andriese, Shuqian Xie, Jiann-Yang Hwang, Zhiwei Peng

"Pyrolyzed carbons are generally known as good microwave absorbers and their dielectric properties still remain to be fully explored. In the present study the dielectric properties and dielectric polarization-relaxation phenomenon of a typical activated carbon was investigated. The experimental results indicate the complex permittivity is highly dependent on temperature and frequency. The decrease of permittivity with increasing temperature from room temperature to ~100 °C is probably ascribed to the release of the water vapor adsorbed on the surface of activated carbon, and the variations of permittivity with temperatures between 100 °C and 450 °C in the frequency range of 300 MHz to 3000 MHz are mainly attributed to the decreased relaxation time of dielectric polarization.IntroductionPyrolyzed carbons have been identified as excellent microwave absorbers owing to their high dielectric and electrical loss under microwave irradiations. Among them, activated carbon continues to attract more and more attention from researchers. Due to its special physical properties, the production, modification and regeneration of activated carbon with the assistance of microwave have been widely studied over the last few decades [1-6]. However, only few attempts have been applied to explore the dielectric properties of such materials due to the complexity and variability of their organic precursors and activation processes [7,8]. In order to shed a light on this problem, a typical sample, Norit® A Supra USP powdered activated carbon, was adopted to perform dielectric characterization, which may provide useful information for its wide application in the fields of purification, energy (hydrogen) storage and so on."

Jan 1, 2011

By Katie Schumacher, Greg Roset, Dayle Flynn

The Columbus Processing Complex of the Stillwater Mining Company began operations at Columbus, Montana in 1990 based on electric furnace smelting treating a precious metals concentrate from the nearby Stillwater mine and mill. Since that time, the smelter plant has been expanded in stages in order to treat recycled materials in addition to the concentrate. This paper describes a number of changes made at the plant to effectively handle recycled materials.

Jan 1, 2014

By Zhang Qin

Dolomite is main impurity mineral in phosphate ores. In practice of phosphate ores production, the grade of concentrates is only containing P2O5 31-32%.In this study, even the increasing of floatation reagent consumption and decreasing of floatation recovery, economic performance is estimated high according to the decreasing of H2SO4 consumption in subsequent production of phosphate fertilizer and the increasing of products value. In floatation stage, influence factor include the synergism impacts of floatation collector, the stages, time, concentration of ore pulp, which were discussed respectively in this paper. Raw material is characterized by mineralogy, chemical analysis, the grain size analysis and milling test . The results show that the grade of concentration can reach to P2O5 36% by deeply de-magnesium oxide from phosphate ores by floatation , which yield a high added value.

Jan 1, 2009

By Katsutoshi Inoue, Shafiq Alam

Several novel types of chemically modified chitosan were prepared by immobilizing functional groups of EDTA and DTPA onto polymer matrices of chitosan in order to investigate their potential for mutual adsorptive separation among rare earths. Following the batch wise adsorption tests to elucidate their basic adsorption characteristics for rare earths, mutual separation was carried out using a column packed with the chemically modified chitosan. The separation between Sm(III) and Y(III) was tested using a column packed with EDTA-type chitosan while mutual separation among 4 light rare earths, La(III), Ce(III), Pr(III) and Nd(III) was tested using a column packed with DTPA-type chitosan. In both cases, satisfactory mutual separation was achieved by the chromatographic operation using these chemically modified chitosan.

Jan 1, 2014

By W. G. Davenport

This chapter extends our mathematical description of flash smelting to -nitrogen in the flash furnace blast. As in chapters 4 and 5, the discussion is limited to auto thermal smelting (no hydrocarbon combustion). Hydrocarbon combustion is introduced in Chapter 9. Outokumpu flash furnace blast is a mixture of air and industrial oxygen. Most of its N2 originates in the air portion of the blast. A small portion originates as an impurity in the industrial oxygen. The nitrogen entering a flash furnace must always be heated from its input temperature, 298 K in this chapter, to its off gas temperature, -1500 K. Energy must be supplied for this purpose. With auto thermal smelting, the energy is-provided by oxidizing extra Fe-and S.

Jan 1, 2001

By Monteirom Sergio N., Romulo L. Loiola, Giulio R. Altoe, Noan Simonassi, Frederico M. Margem

"The environmental concern is creating pressure for the substitution of high energy consumption materials for natural and sustainable ones. Compared to synthetic fibers, natural fibers have shown advantages in technical aspects such as flexibility and toughness. So there is a growing worldwide interest in the use of these fibers. Buriti fiber extracted from buriti palm tree (Mauritia flexuosa), presents some significant characteristic, but until now only few studies on buriti fiber were performed. This work aims to make the analysis of the tensile strength of epoxy composites reinforced with buriti fibers. This analysis was performed in fibers with diameters between 0.1 and 0.4 mm. Those fibers were incorporated into the epoxy matrix with volume fraction from 0 to 30%. The fiber diameters were measured by a profile projector. After fracture the specimens were analyzed by a SEM (scanning electron microscope).IntroductionNatural fibers with high amount of cellulose, also known as lignocellulosic fibers, have been used from primeval times of our civilization. In the last century, synthetic fibers such as nylon, carbon, aramid and glass fibers gained interest owing to superior strength and precise dimensional control. Natural fibers were then replaced by synthetics in many fields such as textiles, sports goods and appliances. In the past decades, however, environmental issues drawn, once again, the attention to lignocellulosic fibers as possible substitute for intensive energy-consuming and long term polluting synthetics, specially the glass fiber(1). In particular, research works have disclosed the potential advantages associated with the use of lignocellulosic fibers as the reinforcing phase in polymer composites(2-3). Among the advantages it is worth mentioning the renewability, recyclability, biodegradability and the fact that natural fibers are neutral with respect to CO2 emissions responsible for global warming. In addition to environmental benefits(l,10) the lignocellulosic fibers present economical advantages, such as worldwide abundance and comparatively low costs as well as some technical properties associated with flexibility and toughness( 4), which contribute to the performance of automobile components fabricated with natural fibers composites(l 1-13)."

Jan 1, 2013

By Richard D. Hagni

Ore microscopy is a useful technique to detect and study the ore minerals that are associated with sediment-hosted and volcanic-hosted deposits of finely disseminated gold and silver. Ore microscopy can be used to determine the: 1) precious metal-bearing minerals in some ores, 2) associated ore minerals that may form geochemical exploration halos, 3) character of iron sulfide grains, 4) extent of sulfide oxidation, 5) character of oxidized iron minerals, 6) character of original sulfide grains from a study of the hypogene and supergene oxidized ores, 7) relative time of oxidation, 8) character of organic matter, 9) minerals that may consume excessive amounts of cyanide solution, 10) extent of silicification and silica encapsulation, and 11) possibility of salting.

Jan 1, 1987

By Bingyi Bai, Wangjun Peng, Yanling Guo, Jieyu Zhang, Guoding Gao

The phase transformation of bayan obo ore with high concentration of iron and calcium was reduced at temperatures no more than 1000℃ were investigated in this study. The samples with insufficient carbon were treated at the temperature using a vertical furnace with a thermogravimetry (TG). The mineral phases and content were examined using Xray diffraction (XRD) and X-ray fluorescence spectroscopy (XRF) respectively. The complex phases of bayan obo ore transformed to some simple phases after treated with different content of carbon at the same temperature for 10 hours. The result of XRD、 XRF and TG showed that the reduction degree of Fe3O4 phase formation varied with the temperature and the carbon content of bayan obo ore.

Jan 1, 2015

By Gong-yi Guo, Yu-li Chen

"A partially-stabilized zirconia powder was prepared by metalorganic precipitation process from technical-grade zirconium oxychloride and the effluent of an acrylic acid plant. The effluent contained low molecular weight carboxylic acids, i. e., acrylic acid and acetic acid. The· developed process is based on the selective precipitation of acrylic acid at suitable pH values by the addition of zirconium oxychloride to the effluent. The resulting precipitate is a precursor that can yield a pure, ultrafine, and partially-stabilized zirconia powder. The evolution of formation of the partially-stabilized zirconia in the present process was investigated using thermal analysis, infrared spectroscopy, and X-ray diffraction technique. Environmental, technological and cost advantages will make the present process feasible for manufacturing advanced zirconia ceramics.IntroductionIn recent years the superior mechanical, thermal, electrical and chemical properties of stabilized zirconia have become the focus of growing scientific and technological interest, and hence resulted in various structural and functional applications. The great potential of the material has given rise to numerous preparation approaches to obtain the material with the excellent properties; nevertheless, an extensive number of programmes are underway worldwide aimed at understanding and improving both the preparation and behavior of stabilized zirconia ultrafine powders. (1 – 8)."

Jan 1, 2000

By John Snowberger III, J. Brent Hiskey

The electrochemical dissolution of super alloys containing different amounts of rhenium was investigated. The initial part of the investigation focused on the anodic dissolution of rhenium from second-generation (3% Re) and third-generation (6% Re) nickel based alloys. Exploratory electrochemical tests were conducted to evaluate solution chemistries and to establish fundamental dissolution behavior of the alloys. These included rotating disc electrode (RDE) cyclic voltammetry, linear sweep voltammetry, and chronoamperometry tests. Electrolytes comprising sulfuric acid, hydrochloric acid, and ammonium sulfate were examined. Of these, a 0.1 M HCl solution proved to be extremely effective for electrochemical dissolution of samples of CMSX-4, CMSX-10, and SC-180 alloys. This paper discusses in detail the electrochemical behavior of these alloys.

Jan 1, 2014

By Marietta Canty

A paper is presented in which an innovative biological process is described for the treatment of cyanide-, metals-, and nitrate-contaminated mine process water. The technology was tested for its ability to detoxify cyanide and nitrate and immobilize metals in wastewater from agitation cyanide leaching. A pilot-scale demonstration is described in which a pilot plant was constructed to demonstrate the technology on a mine process waste stream at a mine in Nevada. The demonstration was performed Jointly under the Mine Waste Technology Program (MWTP), which is funded by the U.S. Environmental Protection Agency (EPA) and is jointly administered by the U.S. Department of Energy's (DOE) Western Environmental Technology Office (WETO) and the Superfund Innovative Technology Evaluation (SITE) Demonstration Program under Interagency Agreement Number DW89938513-0 I-0. MSE Technology Applications, Inc. (MSE) located in Butte. Montana, was the contractor responsible for conducting the project, and Pintail Systems, Inc., of Aurora. Colorado, was the technology provider. The pilot-scale unit was field-tested at the Echo Bay McCoy/Cove Mine southwest of Battle Mountain, Nevada. The biotreatment process was considered to be successful in destroying cyanide in the mine process water. The process was also determined to be effective in removing metals. The pH was consistently neutralized, and nitrates were successfully removed from the mine process water. As a result of conducting these pilot-scale tests, the biotreatment process was concluded to be an innovative, cost-effective alternative for the treatment of mining wastewaters.

Jan 1, 1998

By Deventer Johanna van

Ore bodies around the world are declining in grade, whilst increasing in complexity. The level of impurities relative to the valuable metal is steadily increasing, posing new challenges to existing operations. Ion exchange is widely used in the hydrometallurgical industry for both primary recovery of metals and the removal of impurities. The superior selectivity of ion exchange resins makes them exceptionally suitable for the removal of target impurities to very low levels, thereby saving operating costs, increasing the value of the final product and significantly improving revenue. The ion exchange process in these applications is very simple, using standard ion exchange equipment and acid regeneration. The process can be fully automated, requiring minimal operator interference and supervision Examples of impurities that are successfully removed via ion exchange include iron, antimony and bismuth from copper electrolyte. In the copper electrolysis process, antimony, bismuth and arsenic tend to form slimes which are dispersed in the electrolyte. These slimes contaminate the cathode and/or decrease the quality of the copper deposition. A special chelating resin was developed to remove antimony and bismuth, while at the same time ensuring minimal chloride leakage to the sulphate matrix. The work is described in more detail in this paper. Ion exchange is also used to remove copper, zinc and nickel from cobalt electrolyte. This paper addresses a few of these examples in more detail.

By Richard D. Hagni

An enhanced Interest in pyrometallurgical dusts has recently emerged due to increased world-wide environmental concerns. Mineralogical study of dusts samples from lead sinter plants. lead smelters, and secondary steel mill electric arc furnaces has shown that they can be readily studied by reflected light microscopy. These dusts typically are composed of small particles sufficiently large that their mineralogical identification and characterization can be conducted under the reflecting light microscope. Scanning electron microscope-energy dispersive spectroscopic analysis (SEM-EDS) has been used to confirm optical identifications and chemical compositions. The sinter and blast furnace dusts at the Doe Run Smelter at Herculaneum, Missouri are commonly about 20-150 11m. They consist predominantly of galena, chalcopyrite, sinter. slag. coke. and particles. Dusts from remote sampling sites 112-1 mile from the lead smelter are composed of similar particles and abundant fine-grained particles, less than 10 um. of locally derived calcium-aluminum silicates. Electric arc furnace (EAF) dusts are mostly spherical and less than 10 11m. They consist predominantly of iron oxides (magnetite. franklinite. jacobsite and solid solutions of these spinels), zincite. and calcium-iron silicate glass, together with smaller amounts of hematite. sylvite. coke and metallic iron. Reflected light microscopy is rapid provides mineralogical data on individual grains within dust particles. and allows direct observations of textural intergrowths in pyrometallurgical dust particles.

Jan 1, 1991

By Y. H. Liu

Several foaming aluminum samples of different density were prepared in a semi?industrial scale experimental system, Their properties such as the energy absorption characteristics, mechanical properties, heat conductivity and acoustical properties were measured. The results showed that the foaming aluminum with a density of 0.5 to 0.6 g/em3J has the best energy absorption and this makes it suitable as the ensuring bar of the automobiles and also as a cushion material for the engine. The foaming aluminum with a density of 0.25 to 0.4 g/em3 has the best acoustical properties and heat conductivity resistance, which is suitable for the door filling material, the ceiling and the partition or the car engine.

Jan 1, 2003

By Zachery Zanetell

Flotation circuit performance has become increasingly more challenging due to the complexity of available ore sources. To optimize value mineral recovery, the mineralogical composition of the ore should be evaluated and understood. Utilizing a variety of mineralogical and analytical tools, flotation processing challenges can be overcome and potential limitations understood. In this paper, several case studies will be discussed in terms of the value that has been provided through the use of mineralogical analysis to optimize flotation performance.

By Jin-Chun Kim

Nanosized W based powders (W, WC, WC-Co) were produced by chemical vapor condensation (CVC) process. Two different solid W(CO)6 and Co2(CO)8 metal-organic materials were used as precursors. CVC experiment was conducted in the temperature range of 400-1100. As-CVC WC1-x powder which had non-stoichiometric composition was carburized by using of the CH4-H2 mixed gas in temperature range of 750-850. The CVC W and WC1-x powders showed loosely agglomeration structure, and the Co powder had intricate long stand structure because of intrinsic magnetic properties of Co phase. Carbon content of the CVC powders controlled by gas-phase carburization was well matched with theoretical WC stoichiometry (6.13wt%).

Jan 1, 2006

By C. Allen, A. Roy, J. W. Evans

A spouted bed electrode (SBE) has been used, in laboratory experiments, to electrowin zinc from zinc chloride electrolytes with the objective of determining the suitability of this electrode for commercial application. Zinc was successfully electrowon at current densities ranging up to 4,38 lA/m2, which are an order of magnitude larger than those used at present in the zinc industry. Current efficiencies, for the cell with the SBE, have been as high as 90% and DC energy consumption as low as 2.8 kWh/kg zinc deposited. The performance of the cell has been measured as a function of current density, anode type, cell diaphragm, addition of tributyl ammonium chloride and purging of the electrolyte (to remove dissolved chlorine).

Jan 1, 2000