Synthesis Of W, WC & WC-CO Nanopowders By Chemical Vapor Condensation Process

Nanosized W based powders (W, WC, WC-Co) were produced by chemical vapor condensation (CVC) process. Two different solid W(CO)6 and Co2(CO)8 metal-organic materials were used as precursors. CVC experiment was conducted in the temperature range of 400-1100. As-CVC WC1-x powder which had non-stoichiometric composition was carburized by using of the CH4-H2 mixed gas in temperature range of 750-850. The CVC W and WC1-x powders showed loosely agglomeration structure, and the Co powder had intricate long stand structure because of intrinsic magnetic properties of Co phase. Carbon content of the CVC powders controlled by gas-phase carburization was well matched with theoretical WC stoichiometry (6.13wt%).