By Marco Antônio Siqueira Rodrigues

The possibilities for treating rinse waters fiom chromating bath by electrodialysis are discussed together with the possibilities of optimizing the treatment process for waste reduction and reuse of water and chemical products. An industrial effluent with 4600 ppm of Cr(VI), besides other metallic contamination, was used as work solution. This solution has been recirculated on an electrodialysis cell of three compartments, using exchange membranes Selemiom AMT and CMT. A migration of dichromate ions into the anodic compartment was obtained, so that an extraction of circa 99.9 % of Cr(VI) present on the solution was observed, resulting in water with a Cr(V[) concentration of 4 rnd. These results show that electrodialysis can be used to treat these effluents, and this water could be reused as rinse water. The solution of the anodic compartment, consisting at the beginning of the experiment of H2S04, 0.1 N, reached 7200 mg/l of Cr(VI). This concentrate could be reused on the chromating bath itself.

Jan 1, 1999

By José Luiz Rodrigues Bravo

The production of electrolytic copper with assured quality corresponding to international standards, in a conventional electrorefkery of a custom smelter, is a hard and cautious task, if no advanced technologies for selective control of electrolyte impurities are available. The improper control of the amount of As , Sb and Bi in the anode that enter the tankhouse , attributable either to a bad schedule of concentrate input or to the unavailability of clean concentrates in the international market , as well as the lack of means to maintain the suitable level of these elements in the electrolyte together with other operational circumstances, can result in off-grade copper, as well as affect the starting sheet chemically and physically. This paper presents in a practical way the relationship between the operational conditions and the cathode and starting sheet quality produced at CMSA, covering the period of the last five years of operation, discusses the technologies available in the market for antimony and bismuth removal and compare the results of testwork, achieved in the laboratories of CMSA, using two resins not associated with patented technologies.

Jan 1, 1997

By T. Malvik

Norway is a big producer of ferrosilicon and silicon metal. The raw material is quartz and quartzite and large quantities from both Norwegian and foreign sources are used. The demands maade on both the chemical purity and the thermomechanical qualities of the quartz/quartzite have increased in recent years in an attempt to reduce energy consumption and to improve utilization. Control of the chemical quality of the raw material is relatively easy by means of routine analysis, but it is more difficult to find a suitable method for testing the thermomechanical properties. A rapid test method to define high quality quartzite deposits for use in the metallurgical industry has been developed. The method is based on a combination of chemical analysis, dilatometry, thermosonimetry and cathodoluminiscence.

Jan 1, 1989

By J. P. Evans

The modem copper smelter today utilizes tonnage oxygen for smelting concentrates, generating a high strength S02 off-gas leaving the smelter vessel. This gas stream, which also contains any unreacted oxygen, plus C02, N2 and H20, also carries with it the volatilized portion of heavy metals in the feed, plus partly oxidized sulfide concentrates. The time/temperature history and subsequent treatment of this off-gas stream emerging from the smelting furnace exit up to the acid plant can influence the partitioning and segregation of heavy metals in the off-gas circuit. Depending on this history, the type and characteristics of the chemical and physical reactions which. occur in the gas handling system can be influenced. This fact can also be used as a tool to adjust the separation of copper from heavy metals. In this paper, the impact of different time/temperature histories of the gas, due to different furnace geometries .and design, on the subsequent formation and characteristics of the smelter dust is examined. Based on the available data, several case histories drawn from examples using both bath and flash smelting technologies are analyzed from this perspective.

Jan 1, 1992

By J. P. Evans

The modem 'copper smelter today utilizes tonnage oxygen for smelting concentrates. ,generating a high strength S02 off-gas leaving the smelter vessel. This gas stream. which also contains any unreacted oxygen, plus CO2; N2 and H20. also carries with it the volatilized portion of heavy metals in the feed, plus partly oxidized sulfide concentrates, The time/temperature history and subsequent treatment of this off-gas stream emerging from the smelting furnace exit up to the acid plant can influence the partitioning and segregation of heavy metals, in the off-gas circuit. Depending on this history. the type and characteristics of the chemical and physical reactions which occur in the gas handling system 'can be influenced. This fact can also be used as a tool to adjust the separation of copper from heavy metals. In this paper, the impact of different time/temperature histories of the gas, due to different furnace geometries and design. on the subsequent formation and characteristics of the smelter dust is examined. Based on the available data. several case histories drawn from examples using both bath and flash smelting technologies are analyzed from this perspective.

Jan 1, 1992

By L. Sh. Tsemekhman

The results of laboratory, large-scale laboratory and commercial scale investigations regarding the process of slag melts cleaning by oxidizing-reduction gas mixtures with a wide range of Po2 and the use of matte of various compositions as an extracting phase are presented. The copper, nickel and cobalt behavior during the cleaning process has been studied based on SEM and x-ray Microprobe of the quenched slag melts. The general cleaning mechanisms have been found. On the basis of the obtained data the most efficient cleaning methods have been proposed.

Jan 1, 2003

By Merete Tangstad, Gabriella Tranell, Jeff Kline

"Raman spectroscopy as an instrumental technique for the determination of silicate structure is widely accepted. This method was utilized for analysis of structural modifications associated with the addition of network modifying species. Silicate melts are described by the extent of oxygen bridging. Therefore, understanding the effect different oxides have on modifying the silicate structure will provide valuable information regarding the removal of boron from silicon in slag refining processes. Samples ranging from CaO/SiO2 = 0.56-1.2 were evaluated with and without varying concentrations of B2O3. The addition of CaO to SiO2 revealed Q2 species constitute 45% of the Qn species and addition of B2O3 to the high concentration CaO system results in an increase in Q2 and a decrease in Q0 . The disappearance of the Raman band associated to the three-member ring in the low concentrated CaO system indicates boron addition and destruction of the ring.IntroductionExtensive studies on the structure of silicate systems have been performed using Raman spectroscopy with consensus on the Raman shift associated with different bridging oxygen units [1]. Most of these studies are motivated by the lack of a fundamental understanding of the processes involved in petrology. Due to this, an opportunity exists to build on the knowledge obtained from these studies and conduct more research on slag structures relevant to industrial applications, as these systems are often compositionally similar to magmatic melts. Raman spectroscopic studies of industrial slags will provide insight into the possible structural modifications necessary to enhance removal of impurity species from the metal phase to the slag phase."

Jan 1, 2012

By John A. Clark, Danylo Oryshchyn, Casey Carney, Stephen Gerdemann, Cathy Summers, Thomas Ochs

"Limited analysis of combustion gas streams where carbon capture is not of interest is done mainly to ascertain operation parameters. Stringent regulations on acid gases and particulates promote careful flue gas analysis. Unregulated components are typically not analyzed. Typically not more than four points (two in the boiler, and one each in the flue and the stack) are sampled. A successful oxy-fuel process with carbon capture and compression is anticipated to require as many as 12 sample points with analysis for water, nitrogen, oxygen, argon, NOx, SOx, and carbon monoxide. Carbon dioxide captured for beverages produces a high value product and the cost associated with analysis is warranted. However, carbon capture for disposal must keep all costs to a minimum. This paper will compare alternative approaches for cost-effective sampling and analysis of the carbon dioxide product streams from oxy-fuel combustion, through all stages of production through compression and pipeline/vessel delivery.IntroductionAnalysis of gases in an oxy-combustion process with carbon capture is essential to the operations of the oxy-fired boiler and the subsequent collection, compression, and purification of carbon dioxide. The process is charged with pure oxygen and not-so-pure carbon in the form of coal at the front end, generating a product of mainly carbon dioxide with traces of argon, nitrogen, sulfur compounds, nitrogen compounds, oxygen, hydrogen, and mercury. It is possible that hydrogen chloride and hydrogen sulfide may also be present in trace amounts [1]. The trace components primarily come from impurities contained in coal such as water, sulfur, nitrogen, and volatile organic compounds. Coal also contains a good deal of mineral matter that is transformed into ash during combustion, becoming particulates that can complicate the analysis regimes utilizing standard analytical equipment."

Jan 1, 2010

By Bemd. E. Langner

At Norddeutsche AfFmerie the CollaMat is an important instrument for controlling the activity of glue in copper electrolyte. Thanks to on-line measuring of the glue activity appropriate action can to taken in the event of sudden changes, such as an intemption in the glue supply, as well as long-term trends, such as continuously decreasing glue activity over days or weeks. Laboratory tests on the dependence of glue degradation on temperature have shown that relatively small increases in temperature of only 3OC cause the half change value of the glue degradation to reduce by 25 %. It is a similar picture with the sulphuric acid concentration in electrolyte. An increase in the acid concentration from 160 g/l to 200 g/l can - depending on the temperature - likewise result in a decrease in the half change value of up to 25 %.

Jan 1, 1995

By A. V. Tarasov

The proposed process is based on creating a controlled frothed layer of molten slag, in which fine particles of carbonaceous reductant and raw material to be processed are mixed with emulsified iron. Frothing of the slag layer without external blowing occurs as a result of intensive evolution of gaseous reduction products. The froth reaction process is maintained due to the heat of an electric arc in the slag layer. When the metal bath is heated by the arc to 1400- 1 500°C, the low temperature of the slag surface of about 1200-1 300°C is maintained due to low thermal conductivity of slag froth preventing heat loss. In order to maintain the required slag froth level and control the process temperature, air tuyeres are installed above the slag bath; blowing air serves also for oxidation of zinc in fumes and for its transportation. High adsorption and thermal insulating properties of slag froth ensure virtually complete elimination of dust and mist entrainment along with low heat losses. The main macrokinetic regularities of the carbon thermal reduction of zinc-containing slag melts have been studied under frothing conditions. The mechanism of formation of gas-slag emulsion has been identified under the conditions of reaction [C]+[O]=CO occurring locally at the slag-metal interface. It has been demonstrated that under the froth reduction conditions the zinc removal rate from the melt increases on the average by 3 to 5 times. Based on the physical and chemical data obtained, basic principles of the dezincing technology have been developed for different intermediate oxide iron-containing products produced in the process of ferrous and non-ferrous metals production.

Jan 1, 2002

By T. H. Jeffers

The U.S. Bureau of Mines' Salt Lake City Research Center. has developed porous polymeric beads containing immobilized non-living biological materials for extracting metal contaminants? from wastewater&. Immobilized biological materials include peat moss, algae, biological polymers, and other materials that demonstrate high .affinities for heavy metals. The beads, designated as BIO-FIX beads, have distinct advantages over traditional methods of utilizing biological materials in that they have excellent handling characteristics . and can be used in conventional processing equipment or low-maintenance systems.. Toxic metals such as copper, cadmium, zinc, lead, and mercury are several of the many heavy metals effectively removed from mine wastewater& using B'IO"FIX beads. Continuous cyclic testing indicated that the beads continued to produce treated effluents which met National Drinking Water Standards (NDIJS) after 175 loading-elution cycles, Adsorbed metals were removed from the beads using dilute ?mineral .acids. In many cases" the extracted metals were further concentrated to enable processors to reclaim the metals, thus minimizing the generation of a hazardous sludge. Tests indicated that use of the beads in a low-maintenance system was particularly effective for treating remote acid mine drainage waters? and small toxic seeps from hardrock mining districts ..

Jan 1, 1991

By H. Y. Sohn, S. PalDey

"Fine particles of nickel aluminides and Ni4Mo were synthesized by reducing mixtures of, respectively, A1Cl3 + NiC12 and NiC12 + MoC12 vapors with hydrogen. Though thermodynamically favorable, the coreduction of NiC12 and A1Cl3 by H2 to form Ni3Al did not readily happen experimentally. The addition of a small amount of aluminum vapor was needed to initiate the coreduction reaction. The product particles as observed by TEM were very fine but usually agglomerated. The electron diffraction pattern of particles identified NiAl and NiA13 along with Ni3Al and metallic Ni. The content of Ni3Al was maximized at 52 mol% at 1050°C under the partial pressures ofH2, A1Cl3, and NiC12 at 57, 1.4, and 0.5 kPa, respectively. When a mixture of NiC12 + MoC15 was reduced by hydrogen, Ni4Mo particles with some Ni or Mo particles were obtained, the maximum content of Ni4Mo obtained being 93 mol % . The particle size was in the range of 100 to 200 nm. An Ni4Mo coating of 700 nm thickness on an Ni substrate was also prepared.IntroductionThe search for new high-temperature structural materials has stimulated much research on intermetallic compounds. Nickel aluminides have low densities, relatively high melting points, and good high-temperature strength properties. They show an increase, rather than a decrease, in yield strength with increasing temperature (1). Ni4Mo is also of interest as a high-temperature structural material. The major shortcomings of these intermetallics are their inherent brittleness at room temperature when they are in polycrystalline form. For much the same reason, the conventional casting of intermetallics is difficult. Ingot metallurgy and powder metallurgy are two other processing techniques. The first technique is quite energy consuming. In powder metallurgy, the powders of metals and alloys are consolidated in near net shape and then subjected to secondary processing. It would, therefore, be advantageous if intermetallic compounds can be produced in fine powder form from inexpensive raw materials, using less energy."

Jan 1, 1998

By Fu-Shen Zhang, Mengjun Chen, Jianxin Zhu

"A novel approach for foam glass preparation, namely vacuum-aided powder sintering technique, was preliminarily investigated in the present communication. The key point of which was to prepare foam glass at a negative pressure. Compared to normal powder sintering process, the new approach could benefit the foaming process by shorting the holding time, reducing the amount of foaming agent and especially decreasing relative density of the product. Optimum conditions were 750 °C, 1000 Pa, 5 min and 1 wt.% foaming agent, respectively.IntroductionFoam glass represents a highly valuable solution for thermal and acoustic insulation, since it possesses a generally higher mechanical, chemical and thermal stability than other foams'1'. The first industrial processing for foam glass production, the direct introduction of gases (""blowing"") into the special molten glass, can be dated back to the end of 1930s'2'. At present, almost all foam glasses is prepared by powder sintering technique instead of blowing,3 since it reduces the temperature by several hundred degrees. Moreover, as fine glass powders or similar powders can be used to substitute corresponding glasses by this technique, considerable attention has been focused on the production of foam glass by considering fully recycled glasses, coal fly ash, or other solid wastes as raw materials,4 especially CRT glasses'3' 5', on the point of environmental protection.In a previous report'6', when discussing the lead removal and recovery from CRT funnel glass by a pyrovacuum process, we found that foam glass could be prepared at a negative pressure. Therefore, in this communication, the similarities and differences between the powder sintering process for foam glass at normal and negative pressure was preliminarily discussed."

Jan 1, 2011

By Jim A. King

The total pressure oxidation of copper concentrates is a potentially viable option for treating copper concentrates that are either low grade or contain significant impurities. Both concentrate types are heavily penalized in smelter contracts. The total pressure oxidation process involves autoclaving the copper concentrate at temperatures of 200-220 C under oxygen pressure. The autoclave discharge can be separated into a solid (oxidation residue) and a liquid (oxidation solution) product. The oxidation solution can be treated for copper recovery by solvent extraction - electrowinning or by direct electrowinning. The direct electrowinning recovery of copper requires prior removal of selenium and tellurium by cementation on finely divided scrap copper. The oxidation residue is washed thoroughly to remove acid and dissolved copper prior to precious metals recovery by conventional cyanidation in the presence of lime. The results of a benchscale investigation involving a number of copper concentrates are reported. Copper recoveries in autoclave oxidation and gold recoveries by cyanidation of the oxidation residue exceeded 99%. The results of benchscale experiments to demonstrate copper recovery are described. Various flowsheet options are presented.

Jan 1, 1993

By Marcio Toshio Tanaka, Marcelo Breda Mourao, Cyro Takano, Cesar Yuji Narita

"The concerns in questions related to the environmental impact in the steelmaking industries caused mainly on the gas emissions such as the dioxide carbon are due to its raw material such as the coal, a fossil and non renewable resource. The purpose of this paper is to replace from 10% to 50% of the coal used in cokemaking by mixing it with a renewable source (wood charcoal). The powder (- 325 mesh) from both raw materials (coal and wood charcoal) were mixed in order to obtain a briquette that was then heat treated at 1100°C to obtain the biocoke. Results of usual analysis (coke reactivity index, coke strength after reaction and cold crushing strength test) were employed to compare to regular coke briquettes. It was found that biocoke with different amounts of wood charcoal present features enabling it to be used in some ore reductionprocesses.1. IntroductionThe iron and steelmaking industry is a heavy emitter of carbon dioxide; according to the World Steel Association, 6.5% of global emissions of this greenhouse gas is due to the production of ferrous materials [ 1]. This is due to the fact that the fuel and reductant employed in the blast furnace is metallurgical coke, obtained from fossil coal. There are some projects aiming to reduce or even eliminate the emission of fossil GHG in the iron and steelmaking process [2]. Most of them propose the capture and storage of the gas (CCS) [3], a technology not yet proven. Other studies point out that the coke consumption in the blast furnace could be reduced by using high reactivity coke; this could lead to lower temperatures in the thermal reserve zone of the blast furnace and consequently less fuel rate in the furnace.The use of biomass in the iron ore reduction process is known as an environmentally accepted solution, as biomass does not release already fossilized carbon."

Jan 1, 2013

By Jingyuan Wang, Hengyi Zhang, Peng Lan, Ruitian Zhang, Jiaquan Zhang, Yang Li

"For the determination of mould taper and wall thickness, a 3-D numerical model of ingot-mould-hot top system has been made to evaluate the related ingot solidification process and the final soundness. The effect of mould wall thickness and the taper of its hot faces on the thermal history and the as cast structure of steel ingot has been revealed through the numerical simulation. It is shown that the ingot soundness can be improved remarkably by increasing the mould wall thickness, which is possibly beneficial to the mould life as well owning to an improved mould thermal state. The mould taper is vital to the ingot soundness but much less coherent to the mould temperature profiles. Under given casting situations, a larger mould taper can lead to a less intensity of the shrinkage porosities at the top part of ingot.IntroductionIngot casting is still one of important processes for steel production, which is adopted especially for the supply of large-sized semi-products of high quality special steels. The understanding to the solidification process is vital to both the yield improvement of casting production and the quality control of steel ingots, such as their soundness and homogeneity.The ingot processing and service performance are closely related to its defects, such as porosities and pipes[1,2], which are the most common but serious defects during ingots casting. In the late 1960s, Mahadevan and Murthy et al.[3], Irani and Kondic[4] began to analyze criteria for the prediction of shrinkage porosities in light metal casting. In 1980s, Niyama and Uchida[5], Hansen and Sahm[6,7] et al have successfully presented some related porosities and pipes criteria for steel casting. At the same time, numerical solidification simulation was well developed and applied to ingot quality studies[8-10]. However, due to the quick development of continuous casting, less emphasis has been given to the further study on ingot casting process. There leaves much work to be made for the comprehensive understanding to ingot quality improvement and the mould design by the aid of modern solidification technology[11, 12]. In this paper, the effects of mould taper and wall thickness on its thermal history, ingot solidification and the final soundness are numerically studied through solidification simulation, which has been adopted in mould design and industrial production of both the mould and its steel ingot."

Jan 1, 2012

By Nils Eivind Kamfjord, Roar Jensen, Ingeborg Solheim

"SINTEF has carried out several pilot scale silicon process experiments in the past, but always with an open off gas system. In order to test the possibilities in running a semi closed furnace operation, a new off gas hood has been designed and tested. The off gas hood is designed to collect all off gases to gain insight into the phase compositions in the off gas and at the same time have the opportunity to monitor and maintain the charging/stoking of the furnace. The furnace hood has regulation and control of the air inlet into the combustion zone in two different heights. The off gas temperature and composition was continuously monitored and analyzed during the experiment. In order to expand the knowledge on NOx- formation in silicon metal production, such information is vital.IntroductionBecause of the negative environmental impact, the attention towards all kinds of NOX emissions increases in Norway. The authorities’ demand towards better surveillance and control of emissions increases as well.Earlier and new industrial measurements in FeSi- and Si-metal furnaces reveal quite high NOX-emission. The measurements also show that the NOX formation (mainly as thermal NOX) is distinct connected to the formation of dust (SiO?SiO2) in the combustion chamber above the furnace surface, when the temperature is high and the access to N2/O2 is good. This means that stoking, charging and temperature straight above the furnace surface is important factors for the NOX formation."

Jan 1, 2012

A new technology for the treatment of copper nickel-containing concentrate after high-grade matte flotation to blister copper with the production of liquid silicate slags in a vertical autogenous unit with upper oxygen blow has been considered. The copper and nickel behavior in the process of sulphide copper concentrate interaction with silicate melt containing oxide copper has been studied. The general mechanisms of such interaction are found.

Jan 1, 2003

By M. A. Cocquerel

The future economic necessity of mining copper ores with a high impurity content and increased environmental awareness will require closer examination of the distribution of arsenic within copper smelting processes. A generalized approach is developed which can be adapted to specific projects for the determination of an overall process configuration to satisfy all requirements in a cost effective manner.

Jan 1, 1983

By J. P. Downey, T. Salisbury, M. Berlin, E. Rosenberg, G. Pinson, R. Christianson, K. Gleason, W. Gleason, S. Davis

"Direct digital manufacturing offers promise as a technique for fabricating complex hydrogen purification membrane support structures. Free form fabrication methods can produce parts with complex structures, and sintering parameters can be controlled to adjust the density, pore structure, pore pathways and strength in catalytic substrate constructs. Efforts are underway to define the influence of selected process variables on the chemical and mechanical properties.IntroductionThe Center for Advanced Mineral and Metallurgical Processes (CAMP), in collaboration with the Metallurgical and Materials Engineering Department at Montana Tech and the Chemistry Department at the University of Montana, is engaged in the development of new methods and materials for hydrogen purification membrane production. Because hydrogen readily passes through palladium, a structurally sound palladium-based membrane is capable of separating relatively pure hydrogen from other gases. In order for this technology to succeed, a suitable substrate material must be identified.High purity hydrogen is produced by various means. A common method involves a two-stage process for separating hydrogen from a hydrocarbon gas stream: 1) hydrogen-rich syngas is produced by the catalytic reaction of natural gas or another light hydrocarbon gas with steam, and 2) hydrogen is separated from the other syngas components by pressure swing adsorption (PSA) (US. Energy Information Agency, 2011). In PSA, gases enter a column that is packed with a material that absorbs gases as the chamber is filled and pressurized. As the pressure is slowly relieved, the absorbent material releases hydrogen at a higher pressure than the impurity gases. PSA processes produce 99.99% pure hydrogen at a high recovery rate. These systems typically demand a high capital investment due to the high pressure and multiple stages (columns) needed to attain high hydrogen production rates.Research geared toward reducing hydrogen production cost is focused on the development of improved catalysts and adsorbent materials as well as more effective single-stage separation processes. An interesting method combines hydrogen reduction catalysis and filtration. Nascent hydrogen is separated from other gases as it selectively permeates the filter. Catalyst filters may be made of gold, silver, platinum, palladium or precious metal alloys (Davis, 2009)."

Jan 1, 2012