By Charles A. Sorrell

Two red muds, two fly ashes, and several aluminosilicate minerals were subjected to direct treatment with concentrated H2SO4 at temperatures of 175°C and below. X-ray analysis showed that virtually all the sulfate reaction products remained in the solid residue because of their low solubilities in x SO Substantial portions of the Al2O3 Fe2O3TiO2, Na2O, and K2O components of the materials reacted to form water soluble sulfates, which were then removed by H2O leaching at 55°C. The solid residue after water leaching consisted largely of amorphous silica and, in lime bearing compounds, CaSO4, The reaction and leaching processes were effective in removing all or nearly all the Al2O3. Fe2O3, TiO2, Na2O, and in lime components in the fly ashes, red muds, china clay, bentonites, the nephelioe fraction of nepheline syenite, and a plaster insulating brick composed of anorthite and mullite. Reaction with potassium feldspar and petalite took place, with formation of alkali aluminum sulfates, but the reaction rates and yields were extremely low. Potassium feldspar can be heated with Na2O and x O in air at 700°C for 24 hours, or with CaO at 1000°C for 24 hours, after which the reaction product kaliophilite, nepheline, and leucite-like phases, prove to be very susceptible to H2SO4, reaction and H2O leaching, providing yields near 100% of the Al2O2 content. An alternative method of H SO treatment consists of heating the sample in a silica tube and passing H2SO4 vapor over it. Preliminary results indicate that this method can be effective in enhancing the kinetics of reaction with the Al O component of potassium feldspar and offer the possibility that formation of Al2 (SO ) Fe2(SO4)3 and TiOSO4 can be accomplished selectively by taking advantage of the fact that the upper stability limits of the respective sulfates in the presence of H2SO4 vapor will be different.

Jan 1, 1982

By Ender Keskinkilic

Pyrometallurgical studies conducted for Mn extraction using Turkish Mn-ore reserves were reviewed. Turkish Mn-ores are low-grade ones having *30% Mn. The most important Mn ore reserves in Turkey are in the Denizli-Tavas region, where more than 2 million tons of proven reserves are reported. Mining rights to the Denizli-Tavas manganese belongs to EregliIron and Steel Works Co. (ERDEMIR). The ore is usually charged to the blast furnaces of ERDEMIR during hot metal production. So far, nearly 20 Master’s thesis studies have been conducted for the analysis of manganese extraction in Turkey. In the scope of the present work, only pyrometallurgical and related activities (i.e. ore beneficiation, calcination, etc.) relevent to the treatment of a specific ore were examined.

Mar 1, 2017

By Jafar Safarian

Bauxite is the main raw material used for the production of alumina (Al2O3) through the well-known commercial Bayer process. This process has significant challenges such as limitation in using low-grade bauxites as they contain significant amounts of impurities such as Fe, Si, Ti. The Bayer process residue, which is known as red mud, is also a global environmental challenge due to huge amount of this low value residue production. An alternative sustainable process with high potential to solve these problems and produce valuable and consumable by-products is a pyrometallurgical-hydrometallurgical process in which the low-grade bauxite ore is treated through a smelting-reduction process, yielding iron alloys and a calcium-aluminate slag. Alumina is then produced from the slag by hydrometallurgical treatment. In the present work, the reduction of pellets produced from different bauxite ores by hydrogen is studied and it is shown that complete iron oxides reduction is possible. Further smelting and smelting-aluminothermic reduction of the reduced pellets show that iron and silicon ferroalloys can be produced, in addition to a proper slag for alumina extraction.

By L. Filip

The roast-leach-electrowinning (RLE) process for zinc was modified to treat two typical complex concentrates containing zinc, lead, copper, gold and silver. Laboratory testwork results indicated that the optimum roasting temperature ranged from 700 to 800°C, in order to produce acceptable residual sulfur levels. The calcined concentrate was subjected to a three-stage leach sequence. The resulting leach solution was purified by hematitic precipitation and directed to the recovery of copper and zinc by solvent extraction and electrolysis. Alkaline smelting and subsequent electrolytic purification recovered the lead and precious metals from the leach residue. A flowsheet was developed based on the laboratory testwork results, and demonstrated in a large-scale pilot plant. The recoveries produced during the pilot plant operation ranged from 90 to 92% for zinc and copper, 85% for lead and 90% for gold and silver, respectively.

Jan 1, 1999

By Weida Guo, Sangsang Liao, Bart Blanpain, Muxing Guo, Qing Liu, Lingling Cao, Keshe Ren, Yannan Wang, Lefei Sun

The interaction between a supersonic oxygen jet and liquid metal is a dominant factor affecting transport phenomena during the converter process. A systematic description of the interaction is of significant importance for a quantitative understanding of the transport phenomena. In this paper, cold model experiments and the corresponding numerical simulations were carried out to investigate the gas-slag-metal interaction inside an 80 t BOF converter. The effects of the operation parameters, such as inlet pressure, slag thickness and slag viscosity on the multiphase interaction have been studied. It has been found that the cavity profile is closely related to the operational conditions. The cavity depth increases with an increase in oxygen inlet pressure, whereas the cavity width is much less affected. The cavity profile is also clearly influenced by the thickness of the slag layer. The influence of slag viscosity on cavity profile is not significant under the present simulation conditions.

Mar 1, 2018

By Y. A. Chang, J. Woodford, C. R. Kao

Reactive diffusion studies between NbC and Si were carried out at 1300 °C under a vacuum of 10-5 torr and a uniaxial pressure of 1 MPa. The annealing time ranged from 8 to 100 hours. The Si used was single crystal silicon; the NbC was hot-pressed powder compact. A NbSi2+SiC two-phase reaction layer formed with NbSi2 as the matrix and SiC as discontinuous particles. The microstructure of the reaction product is homogeneous, dense, and fine. The NbSi2 grain size and SiC particle size are in the micron range. The growth of the reaction products follows parabolic kinetics. Extrapolation of the data to zero thickness suggests an apparent incubation time of 3.5 hours. However, for short annealing time «60 hours), the thickness data can be approximated by linear kinetics with an initial growth rate of about 2 11m/hr. Based on these experimental observations, a growth mechanism for the reactive diffusion between Si single crystal and NbC powder compact is proposed. We propose that the nucleation sites for the SiC particles are at the voids of the NbC powder compact. This proposed nucleation mechanism offers a potential way of controlling the SiC particle size by changing the void size and void density of the NbC powder compact. This hypothesis, if proven to be true, will allow us to control mechanical properties of the composites by tailoring the SiC particles formed. It is also pointed out that the microstructure requires Si to be the dominant diffusing species and to diffuse through the reaction layer, while Nb and Conly have to undergo local rearrangement.

Jan 1, 1996

By Kerri-Ann Hue, Kerry Hasapidis, Ken Babcock, Patrick O'Hagan

"Metallic nanoparticles exhibit properties that are significantly different from individual atoms or bulk materials. Their applications are diverse and have varying uses in areas such as cancer treatment, biochemical sensors, nanoelectronics, and drug delivery. For each application extensive characterization must be performed in order to probe the unique properties of these nanoparticles. In this study, ultra-high resolution mass sensors consisting of MEMs-fabricated, suspended microchannel resonators (SMRs) were used to determine the size and concentration of metallic nanoparticles. With femtogram (10- 15 g) mass resolution, ultra-high resolution mass sensors can weigh individual particles suspended in fluid, and so measure their mass, density, and size. Particle size analysis with these sensors provides excellent accuracy and resolution compared to mature technologies such as light scattering. This technique also provides quantitative information via the ability count particles.IntroductionThe unique electronic, chemical, and optical properties associated with nanoparticles vary with their size, shape, and composition[ 1-4]. These properties are attributed to increased surface area and nanosized mean free path of electrons to the particle surface. Nanoparticle colloidal solutions have been prepared and are commercially available. In recent years, noble metals such as gold, copper, and silver have been extensively researched[5-7]. In order to tailor the optical, electronic, and electrical properties of nanoparticles, size and shape must be controlled. For many applications a monodisperse colloidal solution is ideal. Methods of size characterization include Transmission Electron Microscopy (TEM), Dynamic Light Scattering (DLS), and Electrophoretic Mobility Measurements to name a few[6, 8]. Although TEM can provide shape and size distributions, sample preparation requires that samples be dried on a metal grid and cannot be analyzed in solution. DLS uses curve fitting algorithms that while useful for determining mean particle diameters are not ideal for polydisperse colloidal solutions. New technologies are therefore needed to accurately determine the particle size distributions of metallic nanoparticles."

Jan 1, 2011

By J. W. Matousek

Copper losses in smelter slags are :typically normalized with some form of the distribution coefficient, written as the ratio of the weight percent assays of metal in slag to the metal in matte or its inverse: L(s/m) = %(Cu)/%[Cu] or L(m/s) = %[Cu]/%(Cu) However, this simple approach ignores the dynamics of the smelting process. It overlooks the effect of the chemical work done in producing a given matte grade from concentrates of different grades -- or from a single concentrate blended with varying quantities of copper bearing precipitates or reverts. This paper examines the combined influences of matte grade and the work done in smelting on the copper content of smelting furnace slags. A simple model for the relationship is proposed.

Jan 1, 1999

By Tomoji Kawai

"The Pulsed Laser Deposition method using multi-targets is extremely useful for the creation of functional multi-layers and variety of artificial lattices. The topic of the present talk is on the creation of ''Function hannonized artificial lattices by laser ablation"" made of the combined magnetic, ferroelectiric and superconducting layers. The outline of talk is,1. Features of Pulsed Laser Deposition method (Laser Molecular RHEED and S1M/AFM.2. Creation of magnetic, dielectric and superconducting artificial lattices by Pulsed Laser Deposition.3. Novel properties of function harmonized artificial lattices: especially on the magnetic and magnetoresistive artificial The outline of talk is, lattices made of3d transition metal oxides."

Jan 1, 2000

By Chen Chen, Wang Yanze, Hong Xin

Furnace superalloy was applied in harsh environment within the erosion of high temperature and oxidizing atmosphere. With plasma powder surfacing technology, iron-based alloy powder was sprayed on the surface of 310S stainless steel to form oxidation layer that increases the oxidation resistance and reduces the cost of materials. With optimum technological parameters, in this paper, oxidation test of 100 hours on iron-based cladding alloy and furnace alloy were carried out at 1200 . The technique of XRF, XRD and EDS were used to characterize composition, oxide morphologies and surface mechanical properties. The results showed that Element composition of cladding layer formed by Plasma powder surfacing was well distributed. Its oxidation weight gain rate of 100 hours was 0.4552g/m2h, belonged to antioxidant level. The oxidation weight gain rate of furnace alloy was 1.4617g/m2h, belonged time-antioxidant level. And on the mechanical comparison test, surfacing alloy is relatively excellent than furnace alloy.

Jan 1, 2016

By V. Ramachandran

Over the past 20 years, water treatment plants have been built at various Asarco facilities to effectively handle the process waste streams that need to be bled from the system. The current paper review the several operations with reference to (a) waste streams processed, (b) process chemistry, (c) discharge options and recovery of treated water, and (d) sludge disposal.

Jan 1, 1994

By Keizo Uematsu, Satoshi Tanaka, Nozomu Uchida, Ronne Hendrajaya

"The influence of microstructural defects on strength in Si3N4 is reviewed. The presence of cracks, pores and inclusions greatly affects the strength of Si3N4. The micron order crack size and distribution were quantified by micrographic technique. The observed defect size was range from 4 µm to 28 µm.The density of defect increases as the defect size decreases. The correlation between defects size and density was better represented on the logarithmic graph. The correlation was linier. IntroductionFracture in ceramics materials occurs from. In order to understand the relationship between strength and defects, it is necessary to examine the fracture process quantitatively.1In this study, the micrographic technique is used to determine the defects size and distribution in Si3N4. The observed data will be used to predict the material strength by using fracture mechanics rnodel.2Experimental ProcedureThe sintered Si3N4 specimens ( SNl, Japan Fine Ceramics Center) were sliced into 1mm thick . The both sides of specimen surface were polished into by using diamond slurries with particle size down to 2µm. The final thickness was 0.045 mm. The optical microscope (NIKON OPTIPHOT02-POL) was used to observed the internal defects with transmission mode. The reflection mode was used to determine the surface defects, so that the internal defect could be distinguished from surface defect. The measurement and counting was taken on the micrograph and the longest part of the defect was measured as the defect size. The size density distribution of internal defect is taken."

Jan 1, 2000

By Daniel C. McLean

Extraction data for Cu, Zn and Fe were obtained from 4.5" and 10" columns using massive sulfide ore and natural acid mine water. The purpose was to determine if recycling of solution through the column would produce leach liquors of 4 g/l Cu and Zn at extraction rates of 1 g/l per pass at typical flow rates of 0.002 to 0.006 gpm/sq.ft. Test results exceeded expectations. Cu and Zn concentrations of 4 g/l were obtrained within 4 to 6 cycles. Concentrations greater than 6 g/l Cu and 8 g/l Zn were reached within 10 cycles. Concentrations of greater than 40 g/l of Fe and free sulfuric acid were obtained with no decrease in biological activity being observed. No reagents were used.

Jan 1, 1995

By Walter E. McCulloch

Recent laboratory bench scale and pilot plant metallurgical tests at Mountain States R and D International have demonstrated that some copper ores because of relatively coarse copper sulfide mineralization can be preconcentrated by heavy media separation (HMS). In tests with a copper ore from the AMT Copper Creek project near San Manuel, Arizona, HMS preconcentration rejected about 75 to 80 percent of the feed as a minus 13 mm gravel. The HMS concentrates copper recoveries were about 93 to 95 percent. With the incorporation of HMS preconcentration, significant capital and operating costs savings have been projected for the proposed AMT Copper Creek concentrator. An overview of the HMS preconcentration step development for the AMT Copper Creek project is presented. Also presented are other potential applications of HMS preconcentration for copper ore processing.

Jan 1, 1999

By Ilona Johnson

United States metals and non-metallic minerals manufacturing consume about 5,000 trillion Btu annually. Various studies estimate that as much as 20 to 50 percent of this energy is lost as excess or waste heat. Recovery of waste heat can conserve energy, reduce operating costs, and lower environmental emissions. It would be valuable to quantify recoverable waste heat sources and identify the barriers that hinder its recovery. This paper provides an overview of waste heat losses specific to high temperature processes in primary metals and minerals manufacturing. It summarizes findings from a broader study conducted for the Department of Energy Industrial Technologies Program; the study evaluates energy losses, recovery practices and opportunities, and R & D needs for waste heat technology development.

Jan 1, 2008

"The pyrometallurgical method of recycling car batteries suffers from a potential for air pollution violations, which prompts the desire for a viable hydrometallurgicaJ alternative. Several Processes have been proposed, including leach-electrowinning routes using HBF4 and/or HzSiF6 based electrolytes, along with anodes of PbO2 on inert substrates.A study has been carried out to evaluate the proposed systems, with the intention of demonstrating a six month life of an electrolyte-anode combination. The work, which focused on the use of HzSiF6, has indicated that there was no acceptable anode, and has lead to the development of a technique to produce smooth, glassy, adherent coatings on graphite, and to the development of an anode composed of a series of copper cored graphite rods.The paper will present results on leaching and electrowinning experiments, as well as the description of a flowsheet for a pilot plant that will be used to produce one tone per day of refined lead from spent battery paste."

Jan 1, 1997

By O. M. Popoola, A. P. I. Popoola, D. O. Okanigbe, A. A. Adeleke

The physical, chemical, mineralogical and morphological characteristic of the waste copper smelter dust (CSD) from Palabora Copper (PTY), Limpopo, South Africa, has been reported in the open literature. The bulk of this material falls within the −53 μm particle size fraction with a copper weight percent of 18.02 as determined with the XRF. The high presence of reactive gangue minerals such as mullite (42.97 wt%) and quartz (11.45 wt%) necessitates that the waste CSD be first upgraded of its copper value in the falcon gravity concentrator before subsequent hydrometallurgical treatment. As an initial step, a sample preparation was carried out to make the sample amenable to both real density determination and copper upgrade experiment, thus resulting in 97% of the particles passing the 300 μm sieve aperture (d97 = 300). The laser particle size analyzer (LPSA) was used to analyze the d97 = 300 and the results showed a %change from 90.82% to 95.59%, with a real density of 2.830 for the waste CSD. The result of the copper upgrade showed that test 8 with treatment combination of 80 rpm and 4.5 l/min gave the highest % copper grade of 1.37 which is still less than the %grade of copper in the feed (1.49%). It thus lead to the recommendation that another type of centrifugal separator that will allow the introduction of the feed as slurry so that the pulp density and feed rate can factored into the whole upgrade experiment, consequently reducing the significant amount of losses and the chances of an improved grade and recovery of copper from this waste CSD.

Mar 1, 2018

By Hua Hou, Xiaofeng Niu, Wei Liang

"The explicit finite difference (EFD) method is used for calculating the casting temperature field during solidification. Because the time step is limited, the computational efficiency of the EFD method is lower. In order to improve the computational efficiency, a fourth-order in space and second-order in time model based on the equivalent specific heat method and the alternating direction implicit (ADI) method is established. The degree of similarity between the simulation results and the experimental results is analyzed. The results show that the simulation results of this high order mathematical model are close to the experimental results.IntroductionThe 3D heat transfer equation of temperature field during solidification process is as the following: [1-3]."

Jan 1, 2013

By Chuan-fu Zhang

In present work, the physical properties of molten FenO-MgO-CaO-SiO2 slags were measured .It is shown by the results that when the slag composition is as follow: MgO 8%~12%, CaO 2%~8%, Fe/SiO2 1.2~1.6, the viscosity of the slags decreases with the increase of temperature. When the Fe/SiO2ratio and the MgO content are fixed, the electrical conductivity increases and the viscosity decreases as CaO content increasing, while the content of CaO exceeds 6% its influence weakens. When the MgO content is 11% and the CaO is 6%, the viscosity of the slag decreases markedly as the increase of Fe/SiO2 ratio. Its influence to viscosity is inconspicuous when the Fe/SiO2 ratio exceeds 1.5. When the CaO content is 6% and Fe/SiO2 is 1.2, the electrical conductivity decreases with the increase of MgO content as temperature is below 1290, but increases when temperature is above 1290. When the MgO content is 11% and the Fe/SiO2 ratio is 1.2, the electrical conductivity increases with the increase of CaO content. When the CaO content is 6% and MgO content is 11%, the electrical conductivity increases as the increase of Fe/SiO2 ratio, while its influence weakens as the temperature increases continuously. The electrical conductivity rises when temperature increases at any slag content. The melting temperatures of FenO-MgO-CaO-SiO2 semi- synthesis slags from this work were below 1290.

Jan 1, 2006

By Yasuhiro Konishi, Yoshiyuki Noda

"This paper describes a new processing of rare-earth oxide precursor, in which rare-earth carbonate powders are precipitated directly from emulsions of rare-earth loaded carboxylate solutions, using CO2 gas and water. This synthetic route of rare earth carbonate is a combined process of the stripping and precipitation stages in a conventional solvent extraction. Using this technique, lanthanum carbonate and yttrium carbonate were prepared at temperatures of 10 to 80°C and CO2 pressures of 0.1 to 3.0 MPa for 120 min. The rates of carbonate precipitation in a batch autoclave were sensitive to processing parameters such as CO2 pressure, temperature, and organic-phase composition. The particle size distributions of the carbonate powders were markedly dependent on temperature and C02 pressure.IntroductionSolvent extraction is the most appropriate commercial technology for separation and purification of rare earths. In typical commercial processes, the rare earths are stripped from loaded solvent extractants using aqueous solutions of mineral acid. After adjusting the pH of the aqueous strip solution, the rare earths are precipitated as insoluble powders of oxalates or carbonates, from which oxides can be produced by calcination. Such conventional processing can be simplified when the stripping and precipitation stages are combined by emulsifying rare-earth loaded solvent extractant with aqueous oxalic acid solution. It is likely that the single-stage precipitation stripping results in a marked decline in the consumed amounts of precipitating and neutralizing agents, thereby saving on both running and capital costs.Yoon and Doyle1) first demonstrated that oxalate powders of lanthanum and yttrium are directly precipitated from rare-earth loaded carboxylic acid solvent extractant when contacted with aqueous oxalic acid solution at ambient temperature and atmospheric pressure. Yttrium oxalate pow4ers were also prepared by precipitation stripping of di-(2 ethylhexyl) phosphoric acid. (D2EHPA) extractant using oxalic acid-hydrochloric acid solutions. 2) Moreover, neodymium oxalates were directly precipitated from organic solutions of tertiary aliphatic monocarboxylic acid and 2-ethylhexyl phosphonic acid mono-2- ethylhexyl ester using aqueous oxalic acid solutions, and powder characteristics of the resulting oxalates were compared with those of powders by the conventional solvent extraction routes. 3 • 4) Recently, attention has been directed towards the influence of processing parameters on the particle size distributions of yttrium oxalate precipitates. 5)"

Jan 1, 2000