Measurement Of Physical Properties Of FenO-MgO-CaO-SiO2 System

In present work, the physical properties of molten FenO-MgO-CaO-SiO2 slags were measured .It is shown by the results that when the slag composition is as follow: MgO 8%~12%, CaO 2%~8%, Fe/SiO2 1.2~1.6, the viscosity of the slags decreases with the increase of temperature. When the Fe/SiO2ratio and the MgO content are fixed, the electrical conductivity increases and the viscosity decreases as CaO content increasing, while the content of CaO exceeds 6% its influence weakens. When the MgO content is 11% and the CaO is 6%, the viscosity of the slag decreases markedly as the increase of Fe/SiO2 ratio. Its influence to viscosity is inconspicuous when the Fe/SiO2 ratio exceeds 1.5. When the CaO content is 6% and Fe/SiO2 is 1.2, the electrical conductivity decreases with the increase of MgO content as temperature is below 1290, but increases when temperature is above 1290. When the MgO content is 11% and the Fe/SiO2 ratio is 1.2, the electrical conductivity increases with the increase of CaO content. When the CaO content is 6% and MgO content is 11%, the electrical conductivity increases as the increase of Fe/SiO2 ratio, while its influence weakens as the temperature increases continuously. The electrical conductivity rises when temperature increases at any slag content. The melting temperatures of FenO-MgO-CaO-SiO2 semi- synthesis slags from this work were below 1290.