By N. Krishna

The utilization of Electrochemical Impedance Spectroscopy (EIS) in conjunction with Atomic Force Microscopy (AFM) is a powerful surface characterization technique to study the role of sulfur formation during acidic oxidation of chalcopyrite. It has been established that the chalcopyrite dissolution kinetics is controlled by the formation of passive sulfur layer during leaching. The objective of the study was to characterize the intermediate sulfur layer formation at different oxidation conditions in acidic solution. The chalcopyrite samples were subjected to anodic oxidation and the oxidation process was analyzed using impedance spectroscopy. The sulfur growth on the chalcopyrite surface during oxidation was further analyzed using Atomic Force Microscope for sulfur roughness and grain size, peak height and sulfur growth.

Jan 1, 1999

By Thor Pedersen

Elkem's technologies for the processing of waste materials, dusts, sludges and other residues, are based on the use of their Multi-Purpose Furnace as the primary processing component. The Multi-Purpose Furnace? is an electric slag resistance reduction furnace equipped with a hot media, Modular Freeze Lining and Elkem's proprietary, air tight electrode seals. The oil cooled? freeze lining allows specific heat fluxes 2 to 3 times higher than furnaces lined with conventional refractory. Reduction activities taking place within the furnace are free from the reoxidation potential of infiltrated air as Elkem's electrode seals are positively gas tight. Small quantities of highly concentrated off gas of controlled composition are produced to suit the requirements of downstream processing. The high electrical thermal efficiency achieved by generating heat within the slag itself, combined with the ability to operate at high melting rates and intense power density, makes the Multi-Purpose Furnace 9 an unique implement for the design of furnace products. These characteristics are utilized in the processing example cited, "Elkem's EAF Dust Processing Technology", which combines two proven technologies in an economically feasible system for the recovery of contained metal values from K061 wastes at the same time producing a disposable slag product. The portion of the example dealing with the condensation of zinc was prepared with the assistance of Imperial Smelting Processes, Limited of Bristol, England with whom Elkem has a non- exclusive license.

Jan 1, 1990

By Takeo Fujino, Nobuaki Sato, Junichi Hasegawa, Masato Nakazawa, Kohta Yamada

"Tantalum oxide thin films were deposited on quartz substrates by laser ablation of Ta2O5 target using Nd:YAG pulse laser. Deposition-was observed when a laser light energy higher than 200 mJ and its repetition rate higher than 3 Hz. A thin film of 0.1 µm thickness was obtained by the ablation using a laser light of 300 mJ and 6 Hz for 2 sec. The thickness of the film increased with increasing energy, repetition rate and irradiation time of laser. By the SEM observation, it was found that many island-like particles were deposited on quartz substrate forming a thin film. The obtained thin film, which was identified as ? Ta-O by X-ray diffraction, was oxidized to Ta2O5 by the heat treatment in air at I273 K for 3 h.IntroductionTransition metal oxides have a potential to show special characteristics in electrical, magnetic and/or optical properties. When such compounds are fabricated in the form of thin film, the special properties would be improved or new characters would appear in comparison with bulk materials. Tantalum penta-oxide is widely used as a capacitor since Ta2O5 shows high dielectric constants up to high temperatures. The tantalum solid capacitor has been fabricated by the electrical oxidation of sintered Ta metal cylinder followed by MnO2 film coating. However, further improvements, reduction and layered structure formation, are required for compacting the devices. The layered structure of thin films would be applicable for the above requirements. The formation ofTa2O5 film by low pressure CVD1), photo CVD2) and magnetron sputtering3l were reported. The laser ablation -method is one of the most convenient techniques for the deposition of thin films from their compounds, such as oxides. Formation of Ta2O5 film by pulse laser deposition (PLD) method using ArF excimer4), Nd:YAG (533nm)5) and TEA CO2 6 lasers was reported. In these PLD studies, ablation was carried out in relatively high oxygen pressures resulting in formation of Ta2O 5 film. In this paper, the deposition of tantalum oxide thin film by the laser ablation of Ta2O 5 using Nd:YAG pulse laser was examined at a viliety oxygen pressures ranging from 10-8 to 10 Torr. The morphology of the films was also investigated in relation with substrate temperature and oxygen pressure."

Jan 1, 2000

By A. Galvan

High rate compressible media filter (CMF) tests produced exceptional total suspended solids (TSS) removal at hydraulic loading rates ranging from 97.8 to 122.2 m/h. The compressible media is manufactured from a robust resin fiber that can withstand low pH and temperatures up to 149 °C. The media porosity can be varied by applying compression onto the media. At 40% compression, the CMF can remove particles greater than 4 μ. Three synthetic test-samples were generated by Hazen Research Inc., (Golden, Colorado) to simulate the copper Pregnant Leach Solution (PLS), Raffinate and Electrolyte solutions used for the testwork conducted at their facility. The preliminary results showed that the CMF was very effective in removing TSS without the use of chemical conditioning from the above test-solutions with efficiencies of 98%, 97%, and 96%, respectively. Given the remarkably high hydraulic loading rates, the industrial equipment footprint would be minimized appreciably over conventional clarification and alternative filtration systems.

By Juha Järvi

Outokumpu Zinc Oy has two separate roasting lines with fluidized bed furnaces and waste heat boilers for calcine collection and heat recovery. During the last 30 years, zinc production in Kokkola plant has increased continuously and at the same time the raw materials have changed. Therefore, the waste heat boiler has been under continuous research and development. The waste heat boiler plays a significant role in the process and consequently the reliability and efficiency of the device is important for the effectiveness of the entire process. Many changes have been made to the boiler in the last decades. New radiation tube screens, tube bundles, and baffle-plate constructions have been added to the boiler and also rapping systems for the dust have been developed. The latest improvement to the boilers was a baffle wall, located in the middle of the radiation section roof in the first boiler, and baffle plates in the lower part of the convection section in the second boiler. The new boiler design and optimization were carried out using physical water and air-dust modeling as well as computational fluid dynamics. The modeling work agrees well with experiences in practice. The latest developments have increased the operating hours per year and the effectiveness of the waste heat boiler.

Jan 1, 2002

By Steven R. Pittman, Colin McCullough, Peter Galuska

"Traditionally Continuous Fiber Aluminum Matrix Composites have been fabricated using high strength fibers and high strength matrices, often commercial alloys, with the goal of producing high strength composites. However the specific role of the choice of matrix alloy on composite properties has not been well established. One way to control composite tensile strength is to use coatings to introduce a low strength interface between fiber and matrix which tends to reduce the importance of the matrix selection, but unfortunately renders the transverse strength unacceptably low. Thus using a system with strong bonding between fiber and matrix is desirable, such as an alumina fiber / aluminum alloy matrix system. In this case the transverse strength is a strong function of the matrix strength. However the longitudinal strength then depends largely on the characteristics of the matrix. The important role of the matrix is discussed using examples of alumina fibers in various aluminum alloy matrices. The key attributes are matrix constituent phases, alloy chemistry, alloy reactivity with the fiber, and matrix strength. From the understanding developed in these systems a set of design rules may be established for selecting an optimum matrix. IntroductionAluminum matrix composites (AMC's) reinforced with continuous fibers offer very attractive property gains over AI alloys, such as strength, stiffness, and fatigue resistance. These gains are magnified when specific mechanical properties are compared which make them attractive candidates for replacing steel, nickel, titanium and aluminum alloy parts in weight critical applications (1). Many systems have been tried in the past; B/AI, C/AI, SiC/AI, Si-Ti-C-O/AI and AI203/AI. Technically B/AI was a very good system but was expensive in regard to both fiber cost and fabrication and SiC/AI and C/AI systems are still plagued with reactivity problems. The Si-Ti-C-O/AI appears to be a good strength system but with lower stiffness. Until recently, the AI203/AI was a low strength system, in part due to a lack of a high strength fiber. Recently 3M introduced a high strength AI203 fiber - Nextel™ 610, which leads to high strength composites (1,2) and may also be both low cost and also compatible with less expensive casting approaches for fabrication."

Jan 1, 1996

By Valery Kaplan

Sulfur emission in the form of SO2 in flue gases is one of the most serious atmospheric pollutants associated with coal combustion and non-ferrous metals production. The carbonate eutectic method for removing SO2 from flue gases at 723–923 K was initially proposed in the 1970s but despite its great efficiency (SO2 concentration in the flue gas after purification reached 0.003 volume %), it could not be implemented by industry due to the complexity of the carbonate melt regeneration stage. Earlier we proposed a method suited to coal-firing power stations where the melt was regenerated using CO as a reducing agent. However, most metallurgical plants do not use coal and therefore lack a large source of CO. Here we propose a method for removing sulfur from the carbonate eutectic melt by purging it with natural gas or a natural gas/air mixture, which are available in the vast majority of metallurgical plants. This reaction leads to the reduction of sulfate to H2S gas that leaves the melt. The experiments we conducted show that nearly complete sulfur removal from the melt is possible at 823 K and that the reaction rate is sufficiently high for a large scale process. One can foresee that this carbonate melt-based SO2 removal technique may become a practical and economically attractive method for limiting sulfur emission to the atmosphere from non-ferrous metallurgical processing plants.

By J. Sjöblom

New copper and nickel processes, flash converting and DON, direct high-grade nickel matte smelting, have been developed in order to replace the conventional and not so environmentally friendly PS-converting process. With a laboratory scale laminar-flow furnace the combustion reactions of sulfidic feed particles can be investigated under simulated flash smelting conditions. In the present study, finely ground and screened feed fractions of a copper matte and a nickel matte were flash oxidized in a laminar-flow furnace. The experiments were carried out using 20, 21 vol% and 75 vol% O2 in nitrogen, at temperatures 1100 and 1300 °C and reaction zone length of 7.5-16 cm. The samples were quenched in a water film after a specified reaction time. The matte particle reactions were stopped after short residence time intervals in order to obtain a better understanding of the reaction mechanisms. Chemical analysis was used to determine oxidation degree, and optical and scanning electron microscope combined with energy dispersive analysis was used for characterization of the reacted particles. On the basis of the experimental results the reactivity of the mattes is discussed and possible reaction and dust formation mechanisms are considered.

Jan 1, 1999

By Wang Yun-yan

In order to examine the adaptability and the kinetics of leaching different gold ores in alkaline thiourea system, six kinds of gold concentrate and/or calcine with different physical and chemical properties were chosen as objects. The leaching behaviors in alkaline thiourea system with high stability, acidic thiourea system and alkaline cyanide system were compared. Changes of phase, surface appearance, particle distribution and specific surface area of six kinds of gold ores before and after leaching were studied in virtue of modern analytic techniques, e.g., XRD, SEM, and so on. The results indicate that alkaline thiourea solution can be used to leach gold ore, for oxidized gold concentrate removed arsenic by microbe pretreatment(4#) the leaching rate of gold is up to 82.68%, such conclusion overthrows the parlance reported that pH value must be less than 1.78, or gold can not dissolve in thiourea solution. Chemical components and phase are related to gold leaching rate, different gold ores are fit for different leaching system, and alkaline thiourea solution is suitable for the pretreated oxidized gold ores with low content of sulfur and in which the main phase was SiO2, phase almost does not change after leaching basically. Generally speaking, when leaching in alkaline thiourea solution, surfaces of gold ores with glaze change greatly to ones with coarseness, distinct trace and holes of corrosion. Particle size decrease and specific surface area increase of gold ores after leaching in alkaline thiourea solution with high stability except gold concentrate of Zhongyuan gold smelter(5#).

Jan 1, 2006

By N. Kanari

Reactivity of MgO towards C12+air, C12+N2 and C12+CO gas mixtures was studied up to 1000 °C. Carbochlorination of MgO occurs at temperatures lower than that of its oxychlorination. Effects of gas flow rate, temperature and partial pressure of the carbochlorinating gas mixture on the reaction rate were investigated. The apparent activation energy of MgO carbochlorination is 49 kJ1 mol between 425°C and 600°C. At 550 °C, the apparent reaction orders with respect to C12+CO, C12 and CO, are 2.37, 1.47 and 0.89, respectively. At this temperature, the maximum reaction rate was obtained using a C12+CO gas mixture having a Cl2lCO molar ratio equal to about 0.6.

Jan 1, 1998

By Jose Carlos D’Abreu, Edelink Efrain Tinoco Falero, Mauricio Marcos Otaviano, Helio Marques Kohler

Nowadays the most important Direct Reduction - DR processes in shaft furnaces has to deal with carbon fines precipitation and DRI carburization issues. Based in a cooperative research program joining Catholic University (PUC-Rio) and SAMARCO Mining Co, a project dealing with pellets reduction and those two phenomena was established. This work analyzes kinetically the three reactions mentioned before, considering typical values for the operational variables temperature, flowrate, pressure and gas composition, parameters commonly used to control the DRI formation in the Reduction Zone - RZ of the shaft furnaces. From laboratories experimental results, the kinetic equations for those reactions were established and, using the superposition principle, generated a specific global kinetic model for the iron oxide reduction and the soot formation. Finally, using those experimental results and applying a planned statistical factorial analysis for the experiments, the numerical coefficients for each equation were calculated and the correlation factor determined for the proposed global kinetic equation.

Jan 1, 2015

By Anupam Madhukar

The essence of an atomistic unified kinetic model of strained thin film growth and defect initiation is presented along with a comparison of its consequences obtained from computer simulations with experiments. Within the competing kinetics of a strain dependent activated incorporation of atoms and an asymmetry between upwards and downwards inter-layer migration, the model provides a consistent description of 2D versus 3D morphology evolution accompanied by the appearance of surface vacancies and steps at no energy cost. The correlated migration of these precursor defects offers an atomistic mechanism for the emergence of surface half-loops from the growth front (thus accounting for configurational and thermal entropy) governed by activation energies closer to their correlated motion under the evolving strain fields and thus substantially less than those calculated with respect to the perfect crystal as the reference state. The essential mechano-chemical nature of the problem is compared and contrasted with the historical literature of such phenomenon as precipitation hardening and sintering in metallic and ceramic composites.

Jan 1, 1994

By Rodney Hundermark, July Ndlovu, Lloyd Nelson, Phillimon Mukumbe, Paul van Manen, Whitey Seyanund, Bart Pieterse, Bertus de Villiers, Diale Mokwena

The 2003 redoubling in power to 68MW on the Polokwane Smelter furnace represented a significant intensification in platinum group metal (PGM) smelting. Combined with onerous ‘green’ PGM concentrate smelting requirements, this yielded conditions unusually corrosive to copper coolers and refractories. This presented unexpected operational and design challenges to reliable crucible operation and maintenance. Combined with specific operational control intervention, development of protective coatings has led to the life of water-cooled copper components improving from 9 to 40 months. The furnace matte endwall was extended in 2010 to address accelerated wear of refractories and the potential risk for contact of copper components by superheated matte. An 18 month planned endwall rebuild cycle has been demonstrated (versus catastrophic failure within 9 months). Finally, benefits including lower energy consumption, improved metal recoveries and higher productivity resulting from operational and in-house design developments will be described, that justify “Celebrating the Mega-scale” in PGM smelting.

Jan 1, 2014

By Ray Y. Lin, Randall A. Blue

"Joining of silicon carbide with infrared using a mixture of Si-30wt.%C as the brazing material has been investigated. Joining was performed at a temperature of 1500 °C in a flowing argon atmosphere for processing times ranging from 5 to 60 seconds. The joining filler materials include thin film silicon obtained by thinning down silicon wafers to about 70 /!m and graphite powder of a 15 /!m average particle size. Joint strengths were determined with a specially designed shear-in-compression jig for testing shear strengths of brittle materials. Cross section examinations of the joined specimens with optical microscopy, scanning electron microscopy and transmission electron microscopy have shown that all joints are essentially void free with excellent wetting between the base SiC and the brazing material. Silicon carbide in the B form has been identified as the reaction product in the joining zone with a transmission electron microscope (TEM) and selected area diffiaction (SAD) analysis. At 1500 °C with a joining time of 60 seconds, the joint has consisted of primarily SiC. With such a high SiC content in the joint, the joint strength is comparable to those by other joining techniques, such as diffusion bonding, as reported in the literature. A kinetic model for the formation of SiC from liquid silicon and carbon is proposed to explain the observed joint microstructural evolution.IntroductionSilicon carbide is of great interest for high temperature structural applications because of its excellent high temperature strength, wear resistance and anticorrosive characteristics [1]. Even though the interest in SiC is high, the use of the material has been limited by the high cost and difficulties involved in forming components of complicated shapes [2]. It is these limitations that necessitate the development of effective joining techniques that are cost effective and able to provide strong joints."

Jan 1, 1996

By N. Kanari

One of the criteria to define the market value of chromite concentrate is its chromium to iron ratio. Changing this ratio for a definite chromite mineral is impossible by physical processing. This study investigated the possibility of increasing this ratio through the carbochlorination and the oxychlorination of chromite concentrates. Experiments are carried out up to 1000 °C. The characteristics of samples and reaction products are determined by SEM, XRD and chemical analysis. The carbochlorination of a chromite concentrate at about 600 °C leads to the . selective partial elimination of iron allowing a higher Cr/Fe ratio of the treated concentrate. Selective extraction of iron could also be achieved at about 950 °C by oxychlorination. In this case, a part of chromium contained in the concentrate is recovered as chromium oxychloride. The obtained residue had high content of Cr, Mg and A1 oxides. Such material has probably better chemical and thermal properties that may. be useful for foundary and refractory applications. Two flow-sheets for the beneficiation of the chromite concentrates using carho- and oxychlorination are suggested.

Jan 1, 1997

By R. Stefaniuk, T. Le, J-Y Huôt, H. Henein

"One of the most important process variables in gas atomization is the gas to metal (G/M) mass ratio as it has a direct effect on the mean particle size of the atomized powder. If this ratio can be controlled during the atomization process, the powder produced would be more uniform and the d50 more predictable. Thus, atomization using a tundish or gravity feed from a crucible would be more stable. In gas atomization, the gas flow rate can be easily monitored; while it is very difficult to determine the molten metal flow rate. This research paper presents a new method of recording the molten metal height with time using a conducting metal height detector. The metal height recorded in real time during atomization was used to characterize using a model the friction losses in the metal delivery system. It is found that the integrity of the metal delivery tube and the cleanliness of the melt play a key role in the maintaining a stable metal feed.IntroductionIn the gas atomization process, molten metal is normally fed to the system either continuously using a tundish or in most cases a certain amount of metal is melted in a crucible and flows into the atomizing chamber under gravity. In the first case, the metal flow rate is believed to be constant during the atomization process despite the presence of slag or dross on the molten metal surface. In the second case, the amount of molten metal is depleted with time and the rate at which the metal flow decreases with time varies from test to test in a seemingly unpredictable fashion.' Furthermore, most atomization systems are confined units and the metal level in the crucible cannot be detected by a visualization method. In industry as well as in laboratories, the metal flow rate is normally calculated on either the mass of input material or the mass of total production divided by the duration of the test. This figure is not accurate enough and obviously cannot be used as a control parameter for the gas to metal ratio as it is only determined after the completion of an atomization run. The need exists for a metal flow rate measurement and control methodology; thereby the d50 of the powder produced may be estimated and controlled in real time. Clearly, the smaller the variation of the G/M ratio during the atomization process the more uniform the powder produced and hence the size of the particles can be predicted."

Jan 1, 1994

By S. Seetharaman

The present paper presents. the concept of micro-models and illustrates the application of the same in the simulations metallurgical processes. Development of micromodels requires access to accurate thermodynamic, thermophysicaland kinetic information for the relevant systems with suitable models to extrapolate the data as functions of temperature and composition. Experimental measurements and modelling of the thermodynamic properties, sulphide capacities and viscosities of oxide melts carried out in the department are presented. The incorporation of these models in process models, with special reference to ladle refining of steel is illustrated. Typical example of micro-modelling of solid-gas reactions is also presented.

Jan 1, 1999

By Batric Pesic

Recovery of gold from refractory ores was studied by pressure oxidation as the method of ore pretreatment followed by bromination of oxidized residues. Three different ores were examined, Au-Ag, Au-Ag-Te, and Au-silver free ore. Pyrite was the major host mineral for gold in these ores. The effect of pressure oxidation parameters (temperature, pressure of oxygen, time, and pulp density) on subsequent bromination under standard conditions was examined. Bromination of residues produced under standard pressure oxidation conditions was examined as a function of: temperature, bromine and sodium bromide concentration, and time. Recovery of gold on activated carbon, from the pulp after bromination, was studied too. Recovery of gold from silver containing ores was lower (87-91%) than the recovery of gold from silver free gold ore (97%). In each studied case, the presence of activated carbon in the pulp further increased the recovery of gold.

Jan 1, 1992

By R. G. Reddy

To better understand the behavior of bacterial-mineral interfacial reactions, a thermodynamic model based on the- studies of bacteria adhesion on mineral surfaces has been evaluated. The bacteria adhesion to the mineral surface would be increased by l ' d1;1creasing the change in Gibbs free energy of adhesion and it would be reduced if the change in Gibbs free energy of adhesion of the system is increased. From the combination -of Young's equation and equation of state, the change in Gibbs free energy of adhesion -for bacterium-mineral system- was calculated. Influence of liquid surface tension, mineral surface tension on the change in Gibbs free energy of adhesion and consequently bacteria behavior on mineral systems- has been discussed.

Jan 1, 1991

By José Carlos Abreu

This work presents a kinetics study covering the effects of temperature over the reduction rates of a carbon composite briquette, aiming its use as burden in some of the new alternate ironmaking technologies, such as the Tecnored process. It is reported that increases in the temperature increases the reaction rate. Additionally, the morphology of the iron phase generated during the reduction of these briquettes is presented. It was possible to verify that three types of iron morphology occurred during the process: an external, dense and continuous iron layer, the presence of iron globules at the center of the briquettes and whiskers at the briquette's core. The measurement of the carbon content on the globules and the external iron layer is also presented.

Jan 1, 2003