By A. Tonejc, A. Bonefacic

As can be seen from the phase diagram A1-W1 the equilibrium solubility of tungsten in aluminum is practically nil at room temperature. By quenching from the liquid state (50,000°C per sec), Varic, Burov, and Kolesnicenko2 obtained A1-W solid solutions up to 0.15 at. pct W. The quenched alloys were in the form of foils, 0.2 to 0.3 mm thick. Considering the results of Duwez and Willens,3 it is obvious that this thickness, which makes impossible a sufficiently rapid quenching, was the main reason for the relatively low content of tungsten dissolved in aluminum found by varic.2 he present note shows that the metastable solubility of tungsten in aluminum can be appreciably extended in aluminum-rich A1-W alloys. The quenching technique and the procedure employed for the preparation of the alloys have been described previously.475 The resulting quenched flakes varied in thickness from 1 to 20 µm from experiment to experiment. However, the measurements of the lattice parameters were carried out only with flakes thinner than 5 µm. The areas of quenched flakes were between 0.1 and 15 mm2. The quenched flakes were placed into a 0.3-mm glass capillary tube which was then mounted in a 114.6-mm-diam Debye-Scherrer camera. Straumanis asymmetric film position and nickel-filtered CuKa radiation were used. The lattice spacings were computed taking X(CuKa1) = 1.54050A for resolved and ?(CuKa) = 1.54178A for unresolved doublets. All specimens were rotated at room temperature, 26o +2°C. The lattice parameters were estimated from extrapolation against the Nelson-Riley function. It was estimated that the error in the lattice parameter of the measurements on a single film lies within +0.0004A for lower and about +0.001A for higher concentrations of tungsten. The lattice parameters of the metastable solid solutions A1-W are plotted vs the concentration of tungsten in Fig. 1 together with the parameters measured by previous investigators.' Each point of the present measurements represents a determination of the lattice spacing on different quenched flakes, for a given concentration of tungsten. With experimental accuracy, the lattice parameters of the metastable solid solutions fall on the straight line passing through the already known data.' As estimated from the uncertainties in the lattice spacings of the solid solutions, the alloys were homogeneous within 0.1 at. pct W. The solubility of tungsten in aluminum-rich A1-W solid solutions obtained by a very rapid quenching technique is increased to about 0.95 at. pct W. This value is 6 times greater than the amount known up to now. -he lattice parameters of the resultant aluminum solid solutions with higher concentrations of tungsten than 0.95 at. pct W did not remain constant AUGER electron spectroscopy has been used to clarify the role of impurities in the embrittlement of AISI 3340 steel. Analysis of fracture surfaces has shown that the embrittled condition is correlated with appreciable antimony segregation at grain boundaries. The low temperature (400" to 600°C) temper embrittlement of low alloy steels containing various combinations of Cr , Ni , Sb , Mn , P , Sn , and As has been examined extensively for many years. General reviews of the area have been made by McMahon1 in 1968, LOW' in 1959, woodfine3 in 1953, and Holloman4 in 1946. Recent work by Low, Stein, Turkalo, and LaForce5 has done much in separating the alloy and

Jan 1, 1970

Jan 1, 1887

By J. A. Fellows, Earnshaw Cook, H. S. Avery

THE increased use of heat-resistant alloys (26 per cent Cr, 12 per cent Ni, 16 per cent Cr, 35 per cent Ni, 12 per cent Cr, 60 per cent Ni, etc ) in recent years has been accompanied by continued demands by the consumer for improvement in properties The manufacturers of these materials, of necessity, have resorted to more critical studies of the basic causes of variations in fundamental properties To keep pace with the need for augmented information, previous techniques of investigation have been refined and new test methods and instruments created It is the purpose of this paper to describe the apparatus, experimental technique and precision of measurement that were employed in the exploration of properties of heat-resistant alloy presented in a companion paper† The detailed precautions in experimental procedure essential for attainment of accurate and comparable data at elevated temperatures cannot be too highly emphasized THE CREEP TEST Since the fundamental concepts of creep testing have been recognized for the past 20 years, present interest is restricted to refinements in equipment and experimental procedure The creep-test laboratory constructed for the American Brake Shoe and Foundry Co is designed to permit 1000-hr tests in the temperature range of 1200° to 2200°F with a choice of applied stress extending from 50 to 50,000 lb per sq in in increments of 50 lb per sq in To simplify the calculation of weight combinations, the loading beams (Fig I) are provided with counterweights to eliminate the tare The precision of the knife-edges (10 1 ratio) is such that a 10-gram weight placed on the upper specimen grip will be exactly balanced by a 1-gram weight attached to the loading shackle Check of the loading weights proved the maximum error to be 0 06 per cent Axial alignment is provided by crossed knife-edges in the grip seats The furnaces are similar in design to those of Crane and Company, Battelle Memorial Institute, and the U S Steel Corporation An 80 per cent Pt, 20 per cent Rh No 19 B and S gauge wire is used as the heating element The details of construction are shown in the radiograph reproduced in Fig 2 The windings are held in place on an alundum tube with alundum cement, the distribution of turns is adjusted to give a maximum temperature gradient of ± 1°F over a 4-in gauge length (Fig 3) To avoid sharp temperature differentials at the ends of the test section, the length of the furnace is four times the gauge length Sixteen-inch coupons are used to reduce the temperature of the threaded

Jan 1, 1942

By AIME AIME

THE following brief description of the main features of the, engineering work was prepared for the use of members of the American Society of Civil Engineers and members of the American Institute of Mining Engineers on the occasion of their visits to the tunnels at the time-of their respective. annual meetings in New York, January and February, 1905. DESCRIPTION. Those portions. of the Pennsylvania Extension into Manhattan and Long Island, lying east of the Terminal Station and west of the East River, have been designated as the " Manhattan ?Cross-town:. Tunnels." They traverse a section of the city second in importance only to the financial district, and one that includes the larger hotels, retail shops and theaters and the residences of many of the best known citizens. Section "D," consisting of twin tunnels for west-bound express and local passenger traffic, lies under Thirty-third Street from a point 400 ft. west of the west line of Sixth Avenue, eastward to the river shaft, situated in the block between Thirty-third and Thirty-fourth Streets east of First Avenue. Beginning at the east end, the tunnels are in separate excavations, leading westward from the subaqueous tubes, on a curve of large radius, gradually closing together until it is found more appropriate to drive them in a single excavation. At a point just west of Second Avenue they reach the tangent, aid from there westward lie directly under Thirty-third Street. At a point about 180 ft. west of the west line of Sixth Avenue, the center concrete-wall between the twin tunnels is omitted, and the excavation somewhat widened to make room for a third storage-track, and the tunnel continues to tile station portal in three-track section. Here reprinted through the courtesy of The United Engineering and Contracting Co. The half-tone blocks used for the illustration of this paper have been kindly supplied by the Chasmer-Winchell Press of New York, Pittsburgh and Cleveland.

Mar 1, 1908

By W. Vickers

SALKOVITZ1 has given a number of useful angles between planes for use with the Laue method in determining the orientation of bismuth single crystals. Bismuth is usually considered as having a face-centered-rhombohedra1 structure with its axial angle 87°34', Fig. 1. A similar figure given by Sal-kovitz appears to be in error in that the angle there marked as 87°34' should be 92°26. The primitive cell is a single rhombohedron of axial angle 570 14. The structure is almost face-centered-cubic and hence high accuracy in measurements is essential if there is to be no confusion in indexing poles or zone axes. It is easier to get this accuracy if zone axes are plotted on the stereogram because they will lie near the basic circle where the net has a more open scale. The zone axes can be read from the film, using a Greninger chart, and can be plotted more accurately than poles. Also, the angles between points near the basic circle can be read more accurately than those between poles near the center. In order to use the zone axes the angles between directions have been calculated from a formula given by Niggli,2 and are given in Table I. Miller indices

Jan 1, 1958

By N. J. Grant, B. C. Giessen, U. Wolff

With the aid of the splat-cooling technique of rapid quenching, metastable alloy phases based on antimony ad bismuth have been prepared. At room temperature, simple cubic phases were found in the Sb + Au, 56 + Yd, and Sb + Ni systems. Another phase was retained in the Au-Bi system at -190°C; in this systent, a microcrystalline phase and a rhombohedrally distorted phase were also observed. The crystal chemistry of these phases is discussed in terms of their valence electron concentration range. A remarkable five-step Phase sequence was found upon heating and equilibration of certain metastable Au-Bi alloys. USING the splat- cooling technique of rapid quenching from the liquid,' a large number of metastable intermediate alloy phases have been prepared in recent years. Thus, Hume-Rothery phases of the hexagonal type based on the valence electron concentration have been produced in systems where they are missing in equilibrium, e.g., Ag-Ge 1 or AU-Sb. 3 In a comprehensive study of metastable alloys based on tin, simple hexagonal metastable y phases were found, raising the total of stable and metastable y phases from 3 to 13. 4 In the In-Bi system, five new metastable intermediate phases were retained.' In most cases, the new metastable phases have some crystal chemical characteristics in common: a) They have rather simple, elementlike structures with few atoms per unit cell, e.g., y phase,4'5 or the metastable primitive cubic phases in the Ag-Te and and Au-Te systems.= b) Their structures are often related to those of the terminal phases, or to elements that are straddled in their position in the periodic table by the constituent elements; this is the case for metastable ß (In-Bi) with the structure of white ß Sn,' or metastable a (Cd-sn). 4 c) They seem to represent the crystal structures appropriate to certain average group number (AGN) ranges in which no or few single-phase structures exist in equilibrium. These average group number ranges can probably be equated in the case of many elements of the Ba(Zn)-Bs(As) groups with the averaged valence electron concentration. In the present work, the splat-cooling technique has been applied to the alloys of antimony and bismuth. In equilibrium, neither element forms intermediate alloy phases with other B elements from groups Bl(Cu) to B4(Si) that contain more than 66.7 at. pct of Sb or Bi, respectively, e.g., AUSb 2. 7 Thus, antimony- or bismuth-rich phases, which might be closely related to antimony or bismuth, and which would reflect struc- tural changes occurring on alloying with small amounts of addition elements, do not exist. Also, the terminal solubility of antimony and bismuth for all B metals is very small. It was therefore of interest to investigate the influence of enforced, nonequilibrium solid solution of addition elements in antimony and bismuth on their crystal structures. It was found that additions of group B 2-B4 metals act distinctly differently than additions of group T 10 and B1 metals. The latter set of additives will be treated here. EXPERIMENTAL TECHNIQUES Alloy preparation and splat-quenching followed closely the procedures described in Refs. 1, 4, and 5; they consisted of the preparation of master alloys from high-purity starting materials (99.99+ pct) and blast-atomizing of 20-mg quantities onto copper sheets. The resulting approximately 1 to 5 u thick foils were investigated by X-ray diffraction. The cooling rates obtained are of the order of 107 to 10 8 C per set,'" causing solidification to proceed at a rat; of approximately 100 cm per sec.' Powder patterns of the resulting fine-crystalline materials were taken with filtered CuK, radiation. For antimony alloys the substrates were held at room temperature and for bismuth alloys at -190°C both during splat foil deposition and X-ray investigation. Annealing treatments at several

Jan 1, 1969

By Walter Weeks

THE process of cooling air by allowing it to expand and do work in an engine is well known, but the theory of obtaining cold air by free expansion without the aid of an engine operating with cutoff has been little discussed. CASE I If compressed air is allowed to expand to the atmospheric pressure through an orifice in an air line that is supplied by a running compressor, no cooling results except the negligible one due to the Joule-Thompson effect, which will not be considered in this discussion. The effect of moisture will also be neglected.

Jan 1, 1937

By John V. Hamme

ONE of Tungsten Mining Corp.'s Vance County, N. C., mill near Henderson was the installation of a new crushing plant with a capacity of 45 to 50 tph. During 1953 the milling rate was jumped from 650 tons to 800 tpd simply by expanding existing facilities, eliminating bottlenecks, and making changes in the existing and new circuits. Previous expansions in 1951 and 1952 raised mill capacity from 300 tons to 650 tpd. In its latest move, Tungsten Mining decided that expansion of existing facilities would be more economical than building that normal production was uninterrupted. For the engineering and design of the new crushing plant and mill expansion the services of the Southwestern Engineering Co., Los Angeles, were obtained. The Southeastern Construction Co., Charlotte, N. C., carried out construction, alterations to existing facilities, and the installation of equipment

Jan 10, 1954

By C. Hays, R. E. Swift, E. G. Kendall

Investigations of the Zr-Pt system, by metallography, incipient melting, and X-ray diffraction, determined the phase relationshifis from 0 to 50 at. pct Pt. Phase fields in the Pt-~ich region were outlined, and three intermetallics (ZrPt, Zr2Pt, and ZrPtd were located. A eutectic between Zr and Zr2Pt, and a eutectoid veaction between Zr and a Zr + Zr2Pt, were established. The maximum solubility of Pt in P Zr was approximately 13.5 wt pct, as opposed to less than 1 wt pct solubility in a Zr. EARLIER work on the Zr-Pt system was limited to an X-ray study on the intermetallic compound, ZrPt3, by H. J. Wallbaum,1 It was reported that ZrPt3 existed at 86.52 wt pct Pt, and had a hexagonal structure, isomorphous with TiNi3. Wallbaum's data revealed the following structural particulars: a = 5.633A, c = 9.21A, and c/a = 1.635A. Other studies allied to Zr-Pt alloys concerned only 1) Pt-rich alloys (0.05 to 5.0 pct Zr) for corrosion resistance,2 2) a Zr-base alloy with 5 pct Pt and 0.124 pct C for oxidation resistance,3 and 3) electroclad-ding of Zr with Pt for in-pile corrosion resistance of Zr to uranyl sulphate. 4 Metallographic, incipient melting, and X-ray diffraction techniques were applied to accurately resolve the phase relationships in the 0 to 50 at. pct (68.2 wt pct) Pt region, and to outline the phase fields in the Pt-rich area. Three intermediate phases: Zr2Pt, ZrPt, and ZrPt3, were also established by the same methods. PROCEDURE Melting stock for this program was of the highest purity obtainable. The Zr was iodide crystal bar with a low hafnium content of about 0.05 wt pct (Westinghouse "Grade 3"). The as-received Zr was treated to remove the surface film of corrosion product that resulted from a standard autoclave grade designation test. Next, the bars were processed to yield material suitable for arc melting and free of contaminants. Sheet platinum metal (Baker and Co. "Grade 2") was used for alloying additions. This material con-

Jan 1, 1962

By Arthur R. Still, Paul Gilmour

The ore deposit of the Iron King mine occurs in a group of steeply-dipping metamorphosed eugeosynclinal volcanic and sedimentary rocks of Precambrian age. Within this sequence, the ore deposit lies at the contact of a unit made up of rhyolitic tuff and interbedded andesite and a structurally underlying series consisting of andesitic tuffs, minor rhyolitic tuffs, and argillaceous sediments. Field evidence suggests that these rocks have been overturned. The ore deposit is made up of a series of overlapping, conformable or bodies consisting of massive pyrite and associated lenses of massive quartz. These contain recoverable amounts of gold, silver, lead, zinc, and copper. A parallel zone of copper mineralization occurs within the hanging-wall rocks. The deposit is considered to belong to a large and important group characterized by mineralogical composition and the lithology and structural type of the host rocks. Evidence regarding the origin of the deposit is reviewed, and it is concluded that the ore bodies were formed through the agency of volcanic hot springs on, or near, a submarine surface of deposition

Jan 1, 1968

By J. T. Lapsley, I. I. Cornet, A. E. Flanigan, R. Hultgren, J. E. Dorn

With the greatly expanding use of magnesium during the war, it appeared necessary to the War Metallurgy Committee that procedures of heat treating common magnesium casting alloys be investigated systematically. Accordingly, the National Defense Research Committee of the Office of Scientific Research and Development placed a research contract with the University of California, supervised by the War Metallurgy Committee. Research on the solution heat treatment and aging of magnesium alloy AZg2, (formerly ASTM No. 17; also known as Dowmetal C or AM26o) which was done under "Restricted" Project NRC-2I, in 1942-1943, and reported in detail in a final report to the OSRD on September 3, 1943, is the basis of this paper, which has been released for publication by the OSRD. American experience with magnesium alloys prior to World War II was limited, although some of these alloys had been in commercial use since 1909. Requirements of the aircraft industry for light alloys made it imperative to understand and utilize the advantageous strength-weight properties of magnesium castings. Magnesium casting alloys are commonly solution heat- treated to increase their ultimate tensile strength and ductility; this treatment may be followed by an age hardening at elevated temperatures, which raises the tensile yield strength but diminishes the ductility. In the present investigation, AZp was studied to determine the effects on properties of various solution heat treatment and aging schedules. The principles of heat treatment of magnesium alloys are the same as for other non-ferrous alloys. The alloy studied, AZp, has a nominal composition of 9 pct aluminum, 2 pct zinc, and minor constituents. Fig I shows, by the projection of isothermal sections on the concentration plane, the solubility surface1 of the ternary magnesium-rich solid solutions as determined by X ray 'analysis. From this figure it may be seen that above approximately 375°C (707OF), AZp alloy is a single phase alloy at equilibrium; below this temperature the equilibrium condition is a two phase alloy. The beta constituent which precipitates from the solid solution exerts a hardening effect. Because the zinc concentration is only 2 pct, ancl because of its solubility relations, AZqz resembles a binary alloy of magnesium with aluminum. The solubility curve1 of Fig 2 shows how rapidly the solubility of the beta phase decreases with decreasing temperatures. Unlike many aluminum alloys, magnesium alloys do not age harden at room temperatures; precipitation hardening of AZ² alloy is performed at about 177°C (350°F). At this temperature about 3 pct aluminum

Jan 1, 1949

By W. A. Backofen, M. L. Ebner

SINCE the early work of Gough with Hanson and Wright,l-3 the study of fatigue has been characterized by experiments on single crystals only in recent times.9-10 Now, increasing attention is given to this aspect of fatigue research for the insight that it may provide into details of mechanism. The investigations have concentrated to a large extent on the development of deformation markings on fatigued crystals, and have shown the cracks to originate in slip bands possibly preceded or accompanied by slip-band extrusions. Experiments of special interest to the present work were conducted by paterson5 on copper crystals and involved both metallographic examination and measurement of change in flow stress. Crystals were cycled in alternating tens ion-compress ion with a constant plastic shear-strain amplitude of approximately 0.8 pct, and were particularly revealing for their demonstration of hardening with accumulated strain similar to that in unidirectional straining, through an easy-glide stage I followed by a stage II of rapid hardening; deformation was not continued beyond 40 cycles, however, so that the eventual course of the hardening curve could not be decided. For the conditions used by Paterson, surface slip markings were similar to those observed in unidirectional straining, but there were no X-ray asterisms and no deformation bands on the surface. In current thinking about the nature of fracture in fatigue, two views relative to mechanism are generally acknowledged, with the reservation that both could apply simultaneously in some measure. As one possibility, fracturing across a slip plane is regarded as a result of loss of cohesion from the creation of many point defects by dislocation movement under the cyclic loading.'' On the other hand, fracture has also been taken to follow as a consequence only of the geometry of slip at a free surface, consisting of offsets and crevices which eventually become fatigue cracks.12, l3 The work of McCammon and Rosenbergl4 showing fatigue in polycrystals at 4.2oK makes clear that any long-range diffusion of point defects is unnecessary, yet studies such as those of Forsyth and stubington15 show that accelerated diffusion may be a characteristic of deformation under fatigue loading. Interest in obtaining data of possible use for resolving such questions led to the experiments described below. Copper crystals were conveniently loaded in alternating four-point bending at constant deflection, a test condition shown to approximate a constant plastic strain amplitude for a wide range of axial orientations. The method of testing was not readily adapted to extensive study of temperature effects, but an investigation of the geometry of crack formation could simply be made by orienting,the slip direction at different angles to the surface. EXPERIMENTAL PROCEDURES Single crystals were grown by a modified Bridgman method in a stationary gradient furnace under an atmosphere of purified dry nitrogen. Purity of as-grown crystals was 99.999 pct as determined by spectrographic analysis plus vacuum fusion and gravimetric analyses for oxygen and sulfur, respectively. Crystals were of reasonable perfection as evidenced by a critical resolved shear stress at 10 deg from (110) of 60 g per sq mm and half-width of a (400) X-ray diffraction line from one crystal of

Jan 1, 1960

By Peter R. Morris, Alan J. Heckler

THREE angles are required to specify the orientation of a crystallite with respect to a physical reference frame. The distribution of crystallite orientations in a polycrystal is thus a function of three angular variables. The most widely used experimental techniques for studying orientation in polycrystals lead directly to the pole figure representation, i.e., the distribution of the poles of certain crystallographic planes in terms of two angular variables. In recent years1-5 methods have been developed which permit determination of the (three-angle) crystallite orientation distribution from several (two-angle) pole figure distributions. In this work Roe's method has been applied to the study of orientation in hcp materials. The method is illustrated for commercial purity titanium sheet (Ti-70) which was cold rolled (65 pct reduction), annealed at 1450°F for 3 min, and air cooled. The grain shape was observed to be equiaxed after this treatment. EFFECTS OF PHYSICAL, CRYSTALLOGRAPHIC SYMMETRY In Roe's method the crystallite orientation distribution, w(?,?,F), is expanded in a series of generalized spherical harmonics 11(?,?,F) = E E E W^Zirmtye-tote-in* [l] 1=o ,,,=-I ,,=-I where { = cos 8. The set of Euler angles employed here is illustrated in Fig. 1. The axis for each rotation is denoted by a double arrowhead. The positive sense of each rotation is that of a right-handed screw advancing in the direction of the double arrowhead. The X, Y, and Z directions correspond to the rolling direction, cross direction, and normal direction, respectively. In the initial orientation (10.O), (12.O), and (00 . 1) planes are perpendicular to the X, Y, and Z directions, respectively. The IC/ rotation about the Z axis is carried out first by rotating X into X', Y into Y', and leaving 2 unchanged, i.e., Z' = Z. The 8 rotation about the Y' axis is carried out second by rotating X' into X", 2' into Z", and leaving Y' unchanged, i.e., Y" = Y'. The I$ rotation about the Z" axis is carried out last by rotating X" into X"', Y into Y"', and leaving 2" unchanged, i.e., 2"' = 2". Any specified orientation of the X'", Y'", and Z'" crystal-fixed axis system relative to the X. Y, and Z physical axes (rolling direction, transverse direction, and sheet normal direction, respectively) can be obtained by appropriate IC/, 8, and (F rotations. The Zl,, of Eq. [l] are the Jacobi polynomials, augmented by the square root of the weight function. The Zl,, are symmetric in m,n, i.e., Zl,,= Zlnm. For orthotropic physical symmetry and hexagonal crystallographic symmetry, the coefficients, W!,,, of the series are all real, W!mn = Wzfi, = Wlm~ = Wlfi~, 1 and m are even and n is restricted to 6k, where k = ...,-2,-1, 0, 1, 2, .-.. The determination of the Wlmn from pole figure data has been previously described.'~~ The Zl,, may be written in multiple angle form

Jan 1, 1970

Jan 1, 1884

By Stanley Herold

As an accompaniment to the interesting papers which discuss the practical aspects of forced drive, or flooding, in our oil fields, and to others which deal with laboratory or field tests on the same subject, a few remarks on the theoretical principles concerned may not be considered inappropriate at the present time. Without claiming to have had the field experience which some of you certainly possess I venture to present some of the results of an analytical investigation upon this method of increasing the recovery of oil from our natural reservoirs. I firmly believe that these results will accord with your experience. I shall confine the present discussion to the consideration of a perfectly ideal situation Let us assume that the productive formation lies perfectly horizontal, that it is of uniform thickness, of perfectly homogeneous texture, and that it contains oil with gas in solution, and no water, throughout a definite, although undefined, lateral extent. We shall furthermore assume that the pressure existing within the reservoir as thus specified, is such that some of the gas is in the free state, spread uniformly throughout, in the form of minute bubbles within the pores of the formation. We now have an ideal reservoir subject to the peculiar action of capillarity as described by the French physicist Jules Jamin. In all directions within the reservoir we see these bubbles of gas, separated by globules of oil which tend to remain in the capillary channels that connect the pores. The action of these bubbles and globules under the application or release of pressure has been fully described by Jamin.1 Most of our oil fields in the Mid-Continent and Eastern districts are subject to this action of capillarity: The fact that the actual reservoir is often far from being ideal in the manner specified above does not preclude the, influence of this phenomenon. The oil, existing under a pressure exerted by the compressed gas, is securely locked in place

Jan 11, 1926

By L. S. Austin

I. Introduction............ 431 II. Organization............ 432 III. Production............ 434 IV. Transportation............ 435 V. Sampling..........436 VI. Concentration............ 440 VII. Blast-Furnace Plant........... 442 1. Construction........... 442 2. Operation............ 450 VIII. Advantages of Large Furnaces........ 455 1. Saving in Fuel........... 455 2. Saving in Jacket.Water..... 455 3. Quick and Large Discharge of Matte and Slag... 455 4. Decrease of Incrustation... 456 5. Elasticity of Operation..457 6. Large Flow Through Fore.Hearths...4. 57 7. Alterations Without Interruption..458 8. Variations in the Composition of Slag....458 9. Less Labor-Cost.......... 458 10. Less Initial Cost.......... 460 IX. Briquetting.Plant........... 460 X. Roasting-Plant............ 462 1. Kilns............ 462 2. Reverberatory Furnaces...468 XI. Converter-Plant........... 474 1. Construction ..........474 2. Operation.......... 476 XII. Flues and Stacks........... 478 XIII. Arsenic-Plant............ 480 XIV. Coke-Washing Plant.... 452 XV. Slime.Ponds ........... 483 XVI. Brick-Plant............ 484 I. Introduction. The Washoe plant; in Anaconda. Mont., together with the local street-railroad, ranches. a foundry and machine-shop. A

Jan 1, 1907

By W. O. Hotchkiss

RECOVERY and profits in the mining business do not go hand in hand. Some part of an orebody can usually be recovered at a lower cost per ton than the whole orebody or a higher proportion of it. Similarly, the total of the profits that may be made from mining an orebody is in itself not a true measure of the value of the business. The yardstick for money value should be present worth, and this is particularly so for purposes of com-parison. A simple example, well within the bounds of practicability, illustrates these points: Assume a mine to have known ore reserves of 4,000,000 tons. The ore is of uniform grade but is so situated that 1,000,000 tons could be mined more cheaply than the remainder. Present operations are on the basis of complete recovery of the ores. Output is 100,000 tons per year at a profit of $1 per ton. It is estimated that the 1,000,000 tons of readily accessible ore could be mined at the same production rate but at a profit of $2 per ton. For an output of 100,000 tons each year at a profit of $1.00 per ton, the mine will have a life of 40 years; will produce $4,000,000 of total profit, and, at Hoskold rates of 8 and 4 per cent, will have a present value of $1,104,690. If only the easy one-quarter of the ore is considered, with an output of 100,000 tons each year, at a profit of $2.00 per ton, that part of the mine will have a life of 10 years, will produce total profits of $2,000,000, and at rates of 8 and 4 per cent will have a present value of $1,224,800. . Under conditions such as these, then, one-quarter of the reserve ore promptly mined is worth some 10 per cent more than the entire reserve would be on an average basis extending over the longer period. Assume further that one-half, or 2,000,000 tons, of the reserves could be promptly mined at the same yearly rate of 100,000 tons at a profit of $1.50 per ton. Then this part of the mine would have a life of 20 years, would produce total profits of $3,000,000, and would have a present value of $1,320,630; approximately 20 per cent greater than for the whole ore-body on an average basis for the longer period.

Jan 1, 1936

By Robert W. Hendricks, John B. Newkirk

A simple method is described for determining the orientation of a single crystal by means of a cylindr cal X-ray camera. Orientation setting to within ±1 deg is attainable by a stereographic analysis of a single cylindrical Laue pattern produced by the originally randomly mounted crystal. Final precision adjustments which permit orientation of the crystal to within ±5 min of arc from the desired position can be made by the method of Weisz and Cole. A chart, originally Presented by Schiebold and schneider7 and which allows a direct reading of the two stereographic polar coordinates of the corresponding pole of a given Laue spot, has been recomputed to aid in the stereographic interpretation of the cylindrical Laue X-ray photograph. Detailed instructions for the use of the chart, a simple example, and a comparison with the conventional flat-film Laue Methods, are presented. 1 HE problem of determining the orientation of the unit cell of a single crystal relative to a set of fixed external reference coordinates is fundamental to most problems of X-ray crystallography and to many experimental studies of the structure-sensitive physical properties of crystalline materials. Several techniques for measuring these orientation relations have been developed which correlate optically observable, orientation-dependent physical properties to the unit cell. Examples of such procedures include the observation of cleavage faces or birefringence, as discussed by bunn,1 or the examination of preferentially formed etch-pits, as discussed by barrett.2 Each of these methods is limited, for various reasons, to an orientation accuracy of approximately ±1 deg—a serious limitation in some experimental studies. Several other limitations decrease the generality of these methods. Of these, perhaps most notable is the absence in many crystals of the physical property necessary for the orientation technique. The most widely used methods for determining crystal orientation are variations of the Laue X-ray diffraction method. Because of the indeterminacy of the X-ray wavelength diffracted to a given spot, the interpretation of Laue photographs is now limited almost exclusively to the procedure of using a chart to determine the angular coordinates of the corresponding pole for each spot. For the flat-film geometries, either a leonhardt3 or a Dunn-Martin4 chart is used in interpreting transmission patterns, whereas a greninger5 chart is used for interpreting back-reflection patterns. A less common method of interpreting flat-film transmission Laue photographs is by comparing the Laue pattern with the Majima and Togino standards,6 or with the revised standards prepared by Dunn and Martin.4 Although this last method is applicable only to crystals with cubic symmetry, it can be very rapid and just as accurate as the graphical methods. The primary limitation of all the X-ray methods mentioned is the relatively small number of Laue spots and zones which are recorded on the flat film. Often, few, if any, major poles appear, thus making interpretation tedious and sometimes uncertain. The use of a cylindrical film eliminates this problem. Schiebold and schneider7 prepared a chart by which the orientation of the specimen crystal could be determined from a cylindrical Laue photograph. However, it was only drawn in 5-deg intervals of each of the two angular variables used to identify the Laue spots, thus limiting the accuracy of orientation to about ±3 deg. An examination of this chart indicated that if it were drawn in 2-deg intervals, crystal orientations to ±1 deg would be attainable. Subsequent use of the replotted chart has confirmed this accuracy. It is the purpose of this paper to describe the redevelopment and use of this chart, and to point out its advantages and limitations. I) CAMERA GEOMETRY AND CHART CALCULATIONS The geometry of the cylindrical camera with a related reference sphere is shown in Fig. 1. The X-ray beam BB&apos; pierces the film at the back-reflection hole B, strikes the crystal at 0, and the transmitted beam leaves the camera at the transmission hole T. One of the diffracted X-rays intersects the film at a Laue spot L. The normal OP to the diffracting plane bisects the angle BOL between the incident and diffracted X-ray beams. The point P on the reference sphere can be located uniquely by the two orthogonal motions 6 and 8 on the two great circles ENWS and BPQT respectively. Because the Bragg angle 8 (= 90 - < BOP) is always less than 90 deg, P always remains in the hemisphere BENWS. Therefore, if every possible pole P is to be recorded on the same stereographic projection, it is necessary that the projection reference point be at T with the projection plane tangent to the sphere at B.* The great

Jan 1, 1963

By J. Greenspan

The anisotropy of fracture and slip, that is, the brittleness and ductility of the beryllium single crystal, is characteristic also of po1ycrystalline beryllium in which the grains are oriented in a preferred manner. Beryllium with grain orientations resulting from hot working either unidirectionally or bidirectionally is ductile or brittle in directions given by the anisotropy and orientation of the grains. Textures developed from various hot-working sequences are given, and tensile results are correlated with textures. Not only texture, but fine grain size is necessary for obtaining high tensile elongation. Ultimate tensile strength and elongation are both correlated with grain diameter. Of particular interest is the case in which unusually high tensile elongations of 30 to 40 pct are obtained when basal planes are oriented to carry THE beryllium crystal (of nominal purity) is probably unique among metals with respect to its unusually acute anisotropy of slip and fracture. While extensive slip can occur on the system (1010) [ll20] starting at about 19,000 psi, the (0001) plane is particularly vulnerable to fracture at 4500 psi or less. Fracture occurs also on the (11zo) plane at about 26,000 psi.1"3 Further, there seems to be no other slip System which contributes significantly to

Jan 1, 1960

By H. Conrad Meyer

The wizardry of nucleonics has added new and greater dimensions to the almost inseparable "twins"-zirconium and hafnium. So close is their relationship that neither element is found free of the other in any presently known mineral. Although zirconium in the form of its oxide was discovered in 1789 by Klaproth, the metal in an impure, nonductile form was not isolated until 1824 by Berzelius. About 100 years later -1925-van Arkel and deBoer developed and patented a technique for the deposition in vacuo of crystalline, coherent, highly ductile metal of extreme purity on an electrically heated filament through the dissociation of gaseous zirconium tetraiodide. Within the past five years both zirconium and hafnium have been dramatized by the press and in popular science magazines. This has led to the false assumption that practically all of the world consumption of zirconium ores is used in the production of the metals. Recent statistics on the subject show that not over 15 pct of the zirconium ore consumed in 1958 went to ferrosilicon zirconium and zirconium metal. The rest was consumed in refractories, foundry sand and facings and ceramics. The importance of zirconium as a component in compact, relatively lightweight nuclear energy units, such as those now used in the submarine Nautilus,6 is well established. A rival of zirconium metal as a casing for atomic fuels is a newly developed ceramic body. It is claimed to be cheaper than zirconium-to withstand higher temperatures-and to be more resistant to corrosion. Whether such ceramic casings have the required low thermal neutron absorption cross section, high strength and easy formability of zirconium is yet to be demonstrated. Hafnium, because of its low order of abundance and its close chemical relationship to zirconium, was not definitely recognized as a new element until around 1923, despite prior claims. A study of the X-ray spectra of zirconium led to its identification. The circumstances leading to the discovery of hafnium were much less fortuitous than those surrounding zirconium. The more precise tools of arc and X-ray spectrometry lent themselves admirably to the search for elements to fill certain gaps in the periodic table. [ ] Pure, ductile hafnium-a metal similar in appearance to stainless steel-has a specific gravity of 13.3 (zirconium 6.52) and a melting point of 2,200°C. In other respects it closely resembles zirconium except in one important respect which gives it a preeminent position in nuclear energy development, namely, a high thermal-neutron absorption cross section. This explains the necessity of hafnium-free zirconium in atomic piles. The ability of hafnium to capture thermal neutrons makes it an excellent "moderator" of "governor" when used as control rods in nuclear reactors (Table 1).

Jan 1, 1960