By R. H. Oliver

The purposes, types, preparation, and testing of flocculants are discussed. A flocculation compendium is included, indicating choice of flocculant for a given set of conditions. An economic evaluation of the process is presented. Solid-liquid separation is a major expense in most mineral processing flowsheets today. Proper use of flocculation can often lower the overall cost of a solid-liquid separation by reducing the size of sedimentation or filtration equipment. PURPOSE OF FLOCCULATION When is use of a flocculant justified in terms of overall process economy? 1) when it results in process improvement, such as producing a clear liquor for electrolysis, precipitation, ion exchange, or solvent extraction; 2) when it results in satisfying requirements of pollution abatement ordinances; 3) when it results in increased recovery of values that would otherwise be lost; or 4) when it results in considerable savings in capital expenditure due to use of smaller equipment. When can the use of a flocculant adversely effect overall process economy? 1) when it results in increased filter cake moisture, 2) when it results in decreased filtration rates, 3) when it results in considerable bulking of sedimentation underflow, 4) when it contaminates either the supernatant or sludge, or 5) when the cost of using the flocculant is greater than the savings due to its use. First step in consideration of flocculants for a given application is establishment of desired goals in terms of increased clarity of effluent, increased recovery of solids, or decreased size of equipment. The most economical solution to a solid-liquid separation problem is that combination of equipment and flocculant costs which meets the established goals at the lowest total annual expenditure. This economic decision can be made only after technical data has been obtained as outlined in next four sections. TYPES OF FLOCCULATION Flocculation is a process wherein individual particles are united into more or less tightly bound agglomerates or flocs, thereby increasing effective particle size of solids suspended in a liquid. Degree of flocculation of a suspension of finely divided solids in a liquid is controlled by a combination of probability of collision between particles and probability of adhesion after the collision has occurred.' Probability of collision can be increased commercially through use of a paddle-type flocculator, combination flocculator, and clarifier or flocculating-type feedwell. Probability of adhesion usually can be increased by addition of a reagent known as a flocculant. Reagents act as flocculants through one or a combination of three possible mechanisms. The first is electrolytic neutralization of inter molecular repulsive force due to Zeta potential. This neutralization enables Van der Waal's cohesive force to hold the particles together after they collide.' The second is the precipitation, within a definite pH range, of voluminous metallic hydroxide flocs which entrap fine particles. This process is known as coagulation.14 Third is the bridging of two or more particles by either natural or synthetic long-chain, high-molecular-weight organic polymers. This bridging is accomplished by adsorption of two particles at different sites on the same molecule or by bonding of two molecules, each adsorbed to a different particle. Considerable effort has been expended in explaining the action of these polyelec-trolytes and detailed accounts are available in the literature. CHOICE OF FLOCCULANTS It is impossible, at the present time, to specify the optimum type or amount of flocculant for a given application from a knowledge of the material to be treated. The standard procedure is to choose reagents or combination of reagents most likely to be effective on the slurry; then test them.' The accompanying Flocculation Compendium (Table I) contains details of all currently available reagents sold as flocculants and it should be used when selecting the group of reagents for tests. This selection can be based on information listed in columns 4 and 5. Column 4 presents industries in which each floc-

Jan 1, 1961

By R. Gibala

Internal-friction measurements on hydrogen-charged iron over the temperature range 4° to 300°K are reported. Two relaxation peaks, the hydrogen Snoek peak at 48 °K and the hydrogen cold-work peak in the range 145" to 2200K, are observed at 80 kc per sec. The effects of hydrogen-charging, aging, and deformation on the internal-friction results are determined and are used to show evidence of partitioning of hydrogen between solid solution and dislocations. The hydrogen-dislocation binding energy is estimated from the behaviors of the relaxation tiwzes and relaxation strengths of the Snoek peak and the cold-work peak. Its value is approxi,mately 6400 cal per mole. MANY investigators have demonstrated the usefulness of internal-friction measurements in determining the manner in which interstitial impurities interact with dislocations in bcc metals. Part of this success has resulted from the existence in bcc interstitial alloys of two anelastic relaxation peaks—the Snoek peak' and the cold-work or Koster peak2 (designated hereafter by SP and CWP, respectively). The SP has its origin in the redistribution of interstitials in solid solution among sites made energetically nonequivalent by an applied stress. The rate at which the redistribution occurs, measured by the relaxation time for the process, is related in a simple way to the diffusion rate of the interstitial in the free solution. The relaxation strength is proportional to the concentration of interstitial in solid solution. The CWP appears to have its origin in the relaxation of an interstitial-dislocation complex for which the relaxation time at a given temperature is much longer than that for the SP. The relaxation strength depends strongly on the concentration of interstitial and the amount of deformation at relatively low concentrations and deformations.2-8 From the dependence of the relaxation strength on interstitial concentration, the SP and CWP may serve as measures of the concentrations of interstitials in free solution and bound at dislocations, respectively. Thus their behaviors have been used to investigate interstitial-dislocation interactions in Fe-C, Fe-N, and several refractory metal systems.'-' However, the Fe-H system has not been studied extensively,? even though disputes in recent years over the mechanism of hydrogen embrittlement in steels involve argument over the extent to which lattice hydrogen and hydrogen-dislocation interactions play an important role.?-'' Previous work on Fe-H indicates the internal-friction behavior to be qualitatively consistent with that for other systems. Apparently, both a SP and a CWP are observed in the temperature ranges 30" to 50°K and 100°to 140°K, respectively (at 1 cps). However, there is neither sufficient nor accurate enough information to identify convincingly these peaks with their supposed counterparts in other systems. Nor have there been any attempts to make quantitative use of these peaks to study hydrogen diffusion, aging, or interaction processes. In this paper, an attempt is made to obtain more complete information on internal friction of hydrogen in iron than presently available. Internal-friction measurements in the range 4° to 300°K on hydrogen-charged iron show that the two peaks discussed above are in fact the hydrogen SP and CWP. Several effects of hydrogen charging, aging, and deformation on these peaks are observed and are used to determine the partitioning of hydrogen between solid solution and dislocation sites in iron. EXPERIMENTAL Materials. The starting material for this investigation was a high-purity iron supplied by National Research Corp. as a 1-in.-diam rod. The following analysis was given (inwt pct): C, 0.004; N, 0.0003; 0, 0.007; P, 0.002; S, 0.005; Si, 0.006; Mn, 0.001; Cu, 0.002; Ni, 0.005; Cr, 0.001; Mo, 0.001. After an initial vacuum anneal (-5 XTorr) at 700°C, the rod was cold-

Jan 1, 1968

By Charles H. Jacoby

In 1774 a Swedish chemist, C. W. Schule, first recognized manganese as an element. That same year Schule's associate, J. G. Gahn, isolated the element manganese for the first time. In 1856 the Bessemer process of steelmaking gave birth to the economic importance of manganese. Later, in 1882, Robert Hadfield discovered high manganese steels. Although the primary use of manganese is in the ferroalloy industry, two additional important uses for manganese are making chemicals and dry cell batteries. Manganese is also vital to plant and animal life. Various chemical compounds of manganese are used in fertilizers, feeds, glass manufacture, paints, varnishes, and for numerous medicinal and chemical purposes. For the study of industrial minerals and rocks, only the chemical and battery grade material is of- concern, but for the sake of comparison, metallurgical aspects are included in this presentation. Although currently the world's largest consumer of manganese, the United States is producing only minor amounts of ore at the present time. This is due primarily to the fact that although huge deposits of manganese occur within our borders, all are of such low grade as to be economically unfeasible to mine. For many years various government agencies and segments of private industry have devoted sizable sums of money and time in an attempt to upgrade ores from the various deposits, and also in an attempt to recover manganese from blast furnace slags. In view of current world prices, and the quantity of high grade material available, there is little likelihood that any of these approaches will be found to be economically feasible in the near future. Geology and Mineralogy Mineralogy There are over one hundred minerals that contain manganese. These minerals vary from those with compositions that are predominantly manganese to those having only minor percentages. [Chemical Mineral Composition % Mn Hausmannite Mn304 72 Polianite MnO2, 63.1 Pyrolusite MnO24 60-63 Cryptomelane KR8O16R (R=Mn) Variable PsilomelaneBa Mn Mn8O16 (OH).45-60 CoronaditePb R8O16R (R=Mn) Variable Hollandite Ba R8O16R (R=Mn) Variable Manganite Mn2O3•H20 62 Braunite 3 Mn2O3•MnSiO3 62 Tephroite 2 MnO•SiO2 54.3 Rhodochrosite MnCO3 47 Rhodonite MnSiO3 42 Spessartite 3 MnO•AI2O3•3SIO2 33.3 WadHydrous Mn OxidesVariable Franklinite(Fe Mn Zn)O(Fe Mn)sO3 Variable Asbolan Cobaltiferous wad Variable AlabanditeMnS63.14] Geology From a geological standpoint most manganese deposits are complex. In general, it can be said that all primary deposits of manganese are carbonates or silicates. The most productive and profitable have been those of sedimentary origin and residual concentrations. Examples of these residual types of deposits are associated with the metamorphosed lodes of Madhya, Pradesh, India, and the lateritic deposits of Orissa and Bihar, India; nodules in the residual clays of the Philippine Islands, US southern Appalachians and Arkansas, Ghana, and Brazil. Sedimentary manganese deposits are best exemplified by the Nikopol district of Russia and the Tchiatouri area of Georgia, USSR. Hydrothermal replacements are characterized by the rhodochrosite deposits of Butte and Phillipsburg, MT. In general, the hydrothermal type deposit has not resulted in any large tonnages being produced, but may have given

Jan 1, 1983

By V. R. Garfias R. V. Whetsel

Production of crude petroleum in Mexico during 1935 totaled approximately 40,082,000 bbl., an increase of 1,925,000 bbl. over the previous year. Successful development continued in the Poza Rica field during the year, increasing production in that area from 3,708,000 bbl. in 1934 to 9,542,000 in 1935. The output of the South fields (Golden Lane) area decreased by 3,000,000 bbl. during the year, and the heavy-oil district of the Northern fields by 1,500,000 bbl. Production in the Tehuantepec fields showed a slight gain. Production of natural gasoline increased from 430,000 to 600,000 bbl. in 1935. Crude run to stills in local refineries is estimated at 30,000,000 bbl., some 4,000,000 bbl. more than in the previous year. Exports of crude and refined products were approximately 22,000,000 bbl., or 2,000,000 bbl. less than in 1934. Exclusive of ships bunkers, domestic consumption increased about 900,000 bbl. during the year, reaching an estimated total of 14,500,000 barrels. Only 74 wells were completed, as compared to 148 in 1934 and 91 in 1933. In proven areas 58 completions resulted in 33 producers and 25 failures. In northeastern Mexico, near the United States border, six wildcat wells were completed, all of which gave little or no encouraging results, except Rancheria No. 3, near Camargo, which is a fair-sized gas well. Four wildcats were drilled just northeast of the Northern fields (heavy-oil district), all of which were failures. A deep test was completed a short distance southeast of the Golden Lane (South fields) in Palo Blanco, which encountered small production not sufficient to exploit. On the Isthmus of Tehuantepec a wildcat well was completed for an estimated initial production of 2000 bbl. daily, a short distance south of the old Jalapa field, which was perhaps the most important new development of the year. Four other wildcats drilled in the Isthmus district resulted in failures. Fields Northern Fields (Heavy-oil District).—In the Northern fields, 18 producing wells and 20 failures were completed, as compared to 34 producers and 71 failures in 1934. The initial production of the new

Jan 1, 1936

By V. R. Garfias R. V. Whetsel

Production of crude petroleum in Mexico during 1935 totaled approximately 40,082,000 bbl., an increase of 1,925,000 bbl. over the previous year. Successful development continued in the Poza Rica field during the year, increasing production in that area from 3,708,000 bbl. in 1934 to 9,542,000 in 1935. The output of the South fields (Golden Lane) area decreased by 3,000,000 bbl. during the year, and the heavy-oil district of the Northern fields by 1,500,000 bbl. Production in the Tehuantepec fields showed a slight gain. Production of natural gasoline increased from 430,000 to 600,000 bbl. in 1935. Crude run to stills in local refineries is estimated at 30,000,000 bbl., some 4,000,000 bbl. more than in the previous year. Exports of crude and refined products were approximately 22,000,000 bbl., or 2,000,000 bbl. less than in 1934. Exclusive of ships bunkers, domestic consumption increased about 900,000 bbl. during the year, reaching an estimated total of 14,500,000 barrels. Only 74 wells were completed, as compared to 148 in 1934 and 91 in 1933. In proven areas 58 completions resulted in 33 producers and 25 failures. In northeastern Mexico, near the United States border, six wildcat wells were completed, all of which gave little or no encouraging results, except Rancheria No. 3, near Camargo, which is a fair-sized gas well. Four wildcats were drilled just northeast of the Northern fields (heavy-oil district), all of which were failures. A deep test was completed a short distance southeast of the Golden Lane (South fields) in Palo Blanco, which encountered small production not sufficient to exploit. On the Isthmus of Tehuantepec a wildcat well was completed for an estimated initial production of 2000 bbl. daily, a short distance south of the old Jalapa field, which was perhaps the most important new development of the year. Four other wildcats drilled in the Isthmus district resulted in failures. Fields Northern Fields (Heavy-oil District).—In the Northern fields, 18 producing wells and 20 failures were completed, as compared to 34 producers and 71 failures in 1934. The initial production of the new

Jan 1, 1936

By Allan B. Tanner

The effects of radon in drillholes on gamma-ray logs have been described by L. S. Hilpert and C. M. Bunker1 Since these effects may cause drastic error in the evaluation of uranium deposits, it is useful to know the conditions under which significant amounts of radon tend to accumulate in drill- holes. In the studies described here, atmospheric conditions were found to dominate in the control of the behavior of radon in drillholes in the vicinity of a uranium orebody. The site of the investigation was in McKinley County, New Mexico, about 12 miles north of Grants. Drillholes of 4 ¼ -in. diam, on 25-ft and 100- ft centers, penetrate ore in dry rock at a depth of about 100 ft. A geologic log of the drillhole of primary interest is shown in Fig. 1. Gamma-ray logs revealed three zones of ore-grade mineralization in the Todilto limestone. A 6-ft zone, the lowest of the three, assayed 0.20 pct U3O8 by chemical analysis. The limestone ores in this area contain disseminated uraninite and some yellow and orange secondary minerals.

Jan 7, 1959

By W. F. Holbrook

In a previous paper1 a method for the measurement of the comparative desulphurizing power of slags was described and data were presented covering the range of likely slags containing up to 10 per cent MgO. In the present work the range is extended to include slags containing up to 20 per cent MgO, and the effect of temperature on 5 per cent and 15 per cent MgO slags over the range 1475' to 1525' C. is included. The method used was that described in the previous paper except that some of the temperature measurements were made with a noble-metal thermocouple instead of a tungsten-graphite thermocouple. Twelve-gram charges of 0.8 per cent sulphur-metal and 5-gram charges of slag were subjected to heating for 30 min. at a prescribed temperature. The charges were analyzed for sulphur content. For purposes of comparison, desulphurizing power is defined as the ratio of the percentage of sulphur found in the slag to that found in the metal. Six slag and metal charges were made coincidentally in 5/8in. holes in a section of an electrode graphite rod. One slag and metal charge was used as a control by means of which adjustment in the desulphurization value could be made for small variations in temperature and other factors. For convenient presentation of the data, the slags are arranged in groups in each of which one of the four main slag components is constant. Thus, the 15 per cent MgO slags are presented separately from those containing 20 per cent MgO. Slags with Magnesium Oxide Constant 15 Per cent Mg0.—The data on slags containing 15 per cent MgO cover a composition range of 24 to 50 per cent SiO2, 5 to 27 per cent A1203 and 24 to 53 per cent CaO. Variation in composition has been in steps of 2 per cent over much of the area. Because the change in desulphurization power is generally gradual with gradual change in composition, certain sections have been covered in steps of 4 per cent and even

Jan 1, 1938

By W. F. Holbrook

In a previous paper1 a method for the measurement of the comparative desulphurizing power of slags was described and data were presented covering the range of likely slags containing up to 10 per cent MgO. In the present work the range is extended to include slags containing up to 20 per cent MgO, and the effect of temperature on 5 per cent and 15 per cent MgO slags over the range 1475' to 1525' C. is included. The method used was that described in the previous paper except that some of the temperature measurements were made with a noble-metal thermocouple instead of a tungsten-graphite thermocouple. Twelve-gram charges of 0.8 per cent sulphur-metal and 5-gram charges of slag were subjected to heating for 30 min. at a prescribed temperature. The charges were analyzed for sulphur content. For purposes of comparison, desulphurizing power is defined as the ratio of the percentage of sulphur found in the slag to that found in the metal. Six slag and metal charges were made coincidentally in 5/8in. holes in a section of an electrode graphite rod. One slag and metal charge was used as a control by means of which adjustment in the desulphurization value could be made for small variations in temperature and other factors. For convenient presentation of the data, the slags are arranged in groups in each of which one of the four main slag components is constant. Thus, the 15 per cent MgO slags are presented separately from those containing 20 per cent MgO. Slags with Magnesium Oxide Constant 15 Per cent Mg0.—The data on slags containing 15 per cent MgO cover a composition range of 24 to 50 per cent SiO2, 5 to 27 per cent A1203 and 24 to 53 per cent CaO. Variation in composition has been in steps of 2 per cent over much of the area. Because the change in desulphurization power is generally gradual with gradual change in composition, certain sections have been covered in steps of 4 per cent and even

Jan 1, 1938

By S. S. Clarke

Late in 1942, the increasing demand for zinc, coupled with the growing shortage of miners and the knowledge that some abandoned mines would have to be reopened for prospecting and development, led to considerable thought as to the possibilities of further mechanization in order to conserve man power. The ore bodies, locally termed "sheet ground," are an important ore bed in some mines and are in the lower part of Boone formation of the Mississippian Series. Some mines contain interbedded layers of nearly pure galena and sphalerite in horizontal sheets ranging in thickness from a thin seam to several inches and is persistent over large areas. This type of ore body offered the best opportunity for study and experiments. The use of Jumbo drill carriers was advanced but some doubt was expressed as to the adaptability of Jumbos as then in use to mine headings as compared to post and arm mounting (Fig I). Another consideration was the introduction of truck haulage when several mines were trackless. A drill frame, built to carry 2 4-in. drifters, was mounted on a truck chassis. This design proved a failure as it was not rigid and the resiliency of the tires and springs allowed too much play. Long screw jacks were then used to hold the truck firmly in place, but placing the jacks and securing the truck required more effort and time than setting up post drills, so the truck carrier was abandoned. The use of a bull dozer underground had been under consideration for some time to be used in "brunoing" the broken dirt from behind pillars and other inaccessable places so the slusher drags could load without double dragging the dirt. A dozer with hydraulic blade lift was purchased and R. I. Tuthill, Superintendent of Section 30 Mines, suggested that a long drill arm be substituted for the blade, and the drills mounted on the cross member. The hydraulic lift would permit drilling holes at any required spacing. The "cat" was very mobile and answered the problem of a trackless mine. The initial tests showed that the "cat" would make a good carrier, but the hydraulic controls were not positive enough to keep the drills in alignment while drilling. The next step was to build a small hoist. This hoist was attached to the power take-off on the "cat" and by means of sheaves and a double line of 3/8-in. hoist cable, a positive control for raising and lowering the boom was obtained. To avoid serious injuries to the drillers should the cable break, a safety chain was fastened to the drill boom and hooked into a slot in the back of the "cat" frame. A different power unit was obtained for the "cat," as a state law prohibited the use of internal combustion engines in mines. A custom machine shop had just placed on the market a small hoist powered by a Model A Ford engine that had been very ingeniously converted to a slide valve engine using compressed air. To use this unit on a "cat," our master mechanic de-

Jan 1, 1949

By Adrien Berton

For nearly a century, the Corocoro deposit has been renowned among geologists from the fact that it shares with the Lake Superior deposits of the United States the distinction of being the only important copper districts where native copper is worked commercially. The Corocoro district, named after the city of Corocoro, the capital of the Province of Pacajes (Department of La Pas, Bolivia) is situated towards the western edge of the Bolivian high plateau, at an altitude of a little over 13,000 ft. The most interesting part of the district is that immediately surrounding the city of Corocoro, at a distance, by railway, of 65 miles from La Paz and 210 miles to the Chilean port of Arica on the Pacific Coast. The climate of the region is that of the semi-desert, dry and relatively cold, with big differences of temperature between day and night. The rainy season begins in December and ends in March. The cupriferous lodes of Corocoro have not attracted as much interest as the silver mines of Potosi but they have been known for a long time. In the precolonial period the Indians were using the charquis, or natural native copper sheets, to make small brass objects, and the beautiful pale green brochantite of the outcrops as a source of green pigments. During the colonial period, the oxidized ores of the outcrops were worked for copper, which was used by the mint at Potosi for making currency. The native copper ores were neglected because the Spanish miners were at a loss how to concentrate and smelt them. About 1830, work by rudimentary processes, which were improved little by little, was begun on the native copper ores. The total production of native copper in the following hundred years amounted to 100,000 tons. This native copper, which was remarkably pure, was much appreciated on the European markets before the introduction of electrolytic copper. It was useful for making special ornamental brass or bronze and the granular concentrates of native copper, called barrilla, containing 80 to 85 per cent copper were suitable for making copper sulfate by direct oxidation and subsequent leaching with sulfuric acid.

Jan 1, 1937

By M. J. Richards, A. Szirmae, G. R. Speich

The formation of austenite from ferrite, ferrite plus retastable carbide, spheroidite, and pearlite has been studied in a series of irons, Fe-C alloys, and plain-carbon steels using fast heating techniques. In the absence of carbide, austenite nucleates at ferrite/ferrite grain boundaries; nucleation is followed by the rapid growth characteristic of a massive transfornation. The trarnsformation occurs at 950°C at heating rates of 106º C per sec and cannot be suppressed. Metastable carbide dissolves before austenite forms and does not influence the transformation kinetics. For spheroidite structures, austenite nucleates preferentially at the jinction between carbides and ferrite grain boundaries. Growth from these centers proceeds until the carbide is completely enveloped; subsequent growth occurs by carbon diffusion through the austenite envelope. For pearlite structures, austenite nucleates preferentially at pearlite colony intersections. Carbide la)?zellae dissolve at the advancing austenite interface but complete solution of carbide does not occur; the residtial carbide is eventually dissolvled or spheroid-ized depending on the carbon cuntent. The magnitude and temperature dependence of the austenite growth rate into Fe-C pearlite when incomplete carbide dissolution is assumed are satisfactorily explained by an approximate colume diffusion model. The impurities present in plain-carbon steel reduce the growth rate of austenite in comparison to that jound in an Fe-C alloy. The formation of austenite has been studied in much less detail than the decomposition of austenite. This is primarily a result of the importance of harden-ability in determining the mechanical properties of steel. Recently, more interest in the kinetics of austenite formation has resulted from the discovery by Grange1 that rapid heating techniques strengthen steel by refining the austenite grain size. Although the strengthening effect is not large, it is accompanied by no loss in ductility. In addition, interest continues in rapid heat treatment of low-carbon steel sheet for tin plate applications.2,3 Among the few systematic studies of austenite formation are the early work of Roberts and Mehl4 on formation of austenite from pearlite and recent work of Molinder5 and of Judd and paxton6 on formation of austenite from spheroidite. Also, Boedtker and Duwez7 and Haworth and paar8 have recently studied the formation of austenite from ferrite in relatively pure iron, Kidin et al.9,10 have studied the formation of austenite in 8 pct Cr steels, and Paxton has recently discussed various aspects of austenite formation in steels." The present work was undertaken to determine the kinetics of austenite formation for a variety of starting structures including ferrite, ferrite plus metastable carbide, ferrite plus spheroidal cementite, and ferrite plus pearlitic cementite. Emphasis was placed on determining the active sites for austenite nucleation, determining the temperature and time range of austenite formation, and in the case of pearlite a careful study of the growth rate of austenite was made in the absence and presence of impurities. By using a variety of heating techniques including laser-pulse heating, it has been possible to study austenite formation in an isothermal fashion over a wide range of temperatures. EXPERIMENTAL PROCEDURE The alloys studied in the present work are a zone-refined iron with 4 pprn C, an Fe-C alloy with 130 pprn C, 2 Fe-C alloys with 0.77 and 0.96 wt pct C, and a plain carbon steel with 0.96 wt pct C. The zone-refined iron and Fe-C alloys contained 60 pprn and 200 pprn total substitutional impurities, respectively. The plain carbon steel contained 2400 pprn Si, 2000 pprn Mn, and 900 pprn Cr. Various heat treatments were given to these alloys to produce different starting structures of equiaxed ferrite, ferrite plus metastable carbide, fine pearlite, and spheroidite. These heat treatments are given in Table I. A wide range of heating rates were employed in this work because many of the reactions occur so quickly at temperatures in the austenite range that they are completed during the initial heating cycle unless very fast heating rates are used. Essentially the same heating techniques employed by Speich et a1.12 and Speich and Fisher13 were used in this work. For time intervals of 2 sec to 20 hr, simple hand immersion of 0.010-in. thick specimens in a Pb-Bi bath was employed. These specimens were quenched in a 10 pct NaC1, 2 pct NaOH aqueous bath. For time intervals of 100 m-sec to 2 sec, an automatic dunking and quenching device was employed with 0.002-in. thick specimens. Again, liquid Pb-Bi baths were used for a heating medium but now helium gas quenching was employed. For time intervals of 2 to 100 m-sec a laser heating device was employed with 0.002-in. thick specimens; a helium plus fine water-droplet spray was now used for quenching. Additional information on heating times shorter than 2 m-sec was obtained by study of the zones around the centrally heated laser spot. Here diffusion of heat from the centrally heated zone raises the temperature of the specimen locally to all temperatures between ambient and the peak temperature, but for times of the order of microseconds. All the heat-treated specimens were examined by

Jan 1, 1970

By Andrew Cosgarea, William R. Upthegrove, Morteza Mirshamsi

The capillary-reservoir technique was used with lead-210 and cadmium-115m to determine the self-diffiLsion coefficients of both cadmium and lead in the liquid binary Cd-Pb system. The self-diffusion coefficients of pure cadmium and pure lead were obtained and were compared with the theoretical predictions. Good to excellent agrement between the experimental and predicted values was obtained. The self-diffusion coefficients of cadmium were tneasuved in alloys containing 2.50, 9.13, 17.40, 31.00, 45.00, 69.00, and 97.00 lot pct Cd by determining- the amount of cadniiutn-115m which diffused out of a small-bore capillavy into an infinite reservoir during- a given time peviod. Sinzila7-measurements were made with lead-210 to determine the self-diffusion coefficients of lead in these identical alloys. Diffusivities were determined from measurenzents performed in the temperature interval of 290" to 480°C. The results were correlated with the Ar-vhenius equation, and the maximum variation of the equation parameters (Q and Do) was also inrestigated . THE theory of diffusion in liquids, particularly liquid metals, is relatively undeveloped in contrast to that for the gaseous and solid states. Although the practical application of liquid metals as heat-transfer media has become increasingly important, few liquid-metals systems have been investigated. Experimental data of fundamental significance in this field are not readily obtained, which may explain but not justify the present lack of knowledge. What work has been completed is primarily restricted to liquid diffusion of pure metals; little work has been done in liquid-metal diffusion of binary mixtures. A review of liquid-metal diffusion theory and research is available elsewhere.1-4 In an effort to add to the knowledge of liquid-metal systems and to increase the basic understanding of the diffusion process in liquids, a study of diffusion in the binary-liquid system, Cd-Pb, was undertaken. The capillary-reservoir technique5 was employed to measure the self-diffusion coefficients of cadmium and lead in molten binary alloys. Measurements were made with seven selected compositions and over a temperature range from 290° to 480°C. The experimental apparatus consisted essentially of the following items: constant-temperature bath, diffusion cells, capillaries, capillary-filling device, and a radioactive tracer counting system. EXPERIMENTAL APPARATUS Constant-Temperature Bath. A cylindrical steel vessel, 8 in. in diam and 15 in. deep, surrounded by an insulated heating coil was used with a sodium-potassium nitrate salt mixture heating medium. The bath was maintained slightly below the desired control temperature by the furnace-heating element; and a 250-w heater, actuated by a Bayley proportional temperature controller, was utilized for the final control of the temperature. A constant-speed mixer stirred the salt to insure a uniform temperature within the bath. Four calibrated Chromel-Alumel thermocouples were placed at various positions in the salt bath to verify the absence of temperature gradients. The observed temperature variation during any diffusion run was less than 0.l°C. The entire furnace assembly was mounted on four shock absorbers to exclude building vibrations and the stirrer propeller blades were adjusted so not to induce vibrations within the reservoir. A schematic diagram of the furnace and the constant-temperature bath is shown in Fig. 1. Diffusion Cell. The diffusion cells and associated parts were the same, except for slight modification, as the one used by walls1 in this laboratory, and are shown in detail elsewhere.' A graphite crucible, 4 in. long and 40 mm (1-1/2 in.) ID, enclosed in a 60-mm (2-1/4 in.) Pyrex tube cell about 18 in. long, was used as a container for the melt. The reservoir (molten alloy in the graphite crucible) was usually about 2 to 2-1/2 in. deep. Graphite was used because of its satisfactory nature as a refractory material and the low solubility of carbon in molten Cd-Pb alloy.677 The Pyrex cell was closed at the bottom and fitted at the top (open end) with a 2-in. Dresser coupling. A brass flange was welded to the top of the coupling. The upper part of the diffusion assembly was bolted to this flange with an O-ring seal. The lower part of the diffusion cell was supported in a 3-in. brass cylinder which was open to allow for circulation of salt around the cell. The top assembly consisted of two synchronous motors, a drive shaft, a thermocouple well, and controlled-atmosphere inlets and outlets. One motor was used for rotation of the capillaries at a rate of 1/2 rpm in the reservoir during the diffusion run. The other motor was used for the vertical positioning of the capillaries and the capillary holder by means of a simple screw drive. The capillary holder and drive assembly were lowered into the reservoir for the run and raised after the desired diffusion time at a rate of approximately 0.4 in. per min. Capillary holders were made of graphite. These

Jan 1, 1967

By Neil H. Cole

Cost and price inflation and financial gearing through loans are characteristic of modern resources projects. Conventional discounted cash flow and 1P.R analyses, in real terms, and without financing, have inadequacies which can yield misleading results. The degree of improvement in value for project equity owners is limited to the value of the additional tax benefit accorded through the financing instrument used. Debt financing may be low in price and value, but its priority means that the equity owners assume a higher risk, thereby increasing the cost, or price, of their capital. The cost of equity capital, or investment hurdle rate, is related to the Capital Asset Pricing Model. Distortions do occur, with inflation, due to depreciation effects, which can cause the adoption of misleading project rate of return or hurdle rate criteria. For investment decisions, the greatest accuracy possible in forecasting is essential, especially for inflation rates,

Jan 1, 1985

By P. T. Gallagher, W. A. Oates

THE partial excess entropy of interstitial solutes in metals, SXS , has usually been interpreted as being principally vibrational ever since the initial statistical treatment of hydrogen in metals by Fowler and Smith-ells. The vibrational entropy is considered being due to the optical modes of the light interstitial atom. Little attention has been given to the magnitudes of the values of SXS'. Leiser and Witte2 and Ebisuzaki and O'Keeffe3 have noted that for hydrogen in metals Si is approximately constant for different metals. On the other hand if it is assumed that the interstitial solute is an isotopic defect then, as shown by McLellan, SXS should vary from metal to metal as follows: where S is the standard entropy of the solvent and Mi, M, are the masses of the interstitial and solvent atoms. respectively. Fair agreement with this equation was found for oxygen in silver and nitrogen in iron4 and for carbon in iron.= Ln a subsequent analysis of metal- hdrogen systems McLellan' found a variation of $' from metal to metal but not in a manner expected from the isotopic impurity equation. However, a possible correlation between the energy of solution, Ei, and sf was noted. Similar correlations have been noted for certain dilute substitutional solid Solutions 7, 8 and recently Kubaschewski 9 has demonstrated a correlation between integral heats and ex-

Jan 1, 1970

By Frederick N. Rhines, Robert F. Mehl

It has been shown elsewhere1 that the data on the rates of diffusion in solid metals are fragmentary and in many cases unacceptable. As a result, relatively little is known concerning the factors determining rates of diffusion and the variations in these rates with temperature. The first form of Fick's law (equation 1 below), in which the diffusion coefficient D is assumed invariant with composition, has been recognized for many years as only an approximation. The differential equation representing the second form of Fick's law (equation 4 below) has only recently been integrated by Matano,2 and unfortunately only in cases where a full diffusion-penetration curve (concentration-distance curve) has been obtained can the Matano solution be applied. The proper analysis of diffusion data is thus confined to the data of Grube and Jedele and of Jedele. 8 These data are essentially for one temperature alone and do not furnish any information on the variation of the activation heat of diffusion, Q, with concentration: no information exists on the variation of Q with concentration within a single solid solution field. 11 Much of the argument concerning the properties of metals that determine D and Q has been drawn from data in which variations of the quantities with concentration are unknown, for these data have been taken from experiments that could not furnish this information. Speculation concerning the properties of metals that may be effective in determining D and Q on the basis of data in which the chosen D and Q values are averages over wide concentration ranges of values at particular concentrations, ranges often of 100 per cent, is likely not to be fruitful.

Jan 1, 1938

By Frederick N. Rhines, Robert F. Mehl

It has been shown elsewhere1 that the data on the rates of diffusion in solid metals are fragmentary and in many cases unacceptable. As a result, relatively little is known concerning the factors determining rates of diffusion and the variations in these rates with temperature. The first form of Fick's law (equation 1 below), in which the diffusion coefficient D is assumed invariant with composition, has been recognized for many years as only an approximation. The differential equation representing the second form of Fick's law (equation 4 below) has only recently been integrated by Matano,2 and unfortunately only in cases where a full diffusion-penetration curve (concentration-distance curve) has been obtained can the Matano solution be applied. The proper analysis of diffusion data is thus confined to the data of Grube and Jedele and of Jedele. 8 These data are essentially for one temperature alone and do not furnish any information on the variation of the activation heat of diffusion, Q, with concentration: no information exists on the variation of Q with concentration within a single solid solution field. 11 Much of the argument concerning the properties of metals that determine D and Q has been drawn from data in which variations of the quantities with concentration are unknown, for these data have been taken from experiments that could not furnish this information. Speculation concerning the properties of metals that may be effective in determining D and Q on the basis of data in which the chosen D and Q values are averages over wide concentration ranges of values at particular concentrations, ranges often of 100 per cent, is likely not to be fruitful.

Jan 1, 1938

By E. Luttgen

The substance referred to in the title is the artificially prepared basic carbonate of magnesia, a compound of the carbonate with the hydroxide. It is the "block-magnesia " of commerce, the magnesia alba of the pharmacist. Its composition, though somewhat indefinite, may usually be expressed by the formula : 4MgCO3,Mg(OH)2, 5H2O; it is found to vary slightly with the details of the method of preparation. This substance has been employed recently with much reported success, as a non-conductor of heat. It is moulded to form coverings suitable for steam-pipes and their fittings and sectional jackets for boilers and cylinders; it is furnished also in forms suitable for lining refrigerators, walls and roofs of buildings, fire-proof safes, etc. It was with a view of ascertaining the efficiency of this material as a non-conductor, or, rather, its relative efficiency among the various non-conducting materials in use, that the writer made the experiments about to be described. A block of magnesium carbonate or magnesia alba exhibits some interesting physical qualities. It is a smooth, white, close-grained solid, in outward appearance resembling a block of Paris plaster. It possesses the lightness of cork, the porosity of sponge, and withal a degree of firmness and strength that, in view of its levity, is quite remarkable. To examine more closely the properties of this substance, a number of 1-inch cubes were sawed from the commercial block-carbonate, also some bricks, that is, blocks measuring accurately 2 x 4 x 8 inches, the dimensions of an ordinary brick. The cubes weighed from 2.2 to 2.7 grammes, the bricks weighed 140 to 175 grammes (5 to 6 ounces). The bricks were carefully measured and weighed, and placed in vessels containing distilled water, in which they became gradually submerged, owing to the displacement by water of the air inclosed in the structure of the magnesium carbonate. After twenty-four hours the blocks were removed from the water, dried superficially by contact with filter-paper and weighed. From the increase in weight, the volume of the water absorbed, and consequently that of the air displaced by it, were obtained. For example: a block which when dry weighed 155

Jan 1, 1887

By C. J. Guntner, R. P. Reed

A commercial 18Cr-8Ni iron alloy (AISI 304L) was examined in tension at 300°, 76°, 20°, and 4°K. Continuous stress-strain recordings were made, X-ray analyses at periodic stress (strain) intervals were obtained, and the magnetic measurements were taken. From this data the percentage of martensitic products [bcc(a) and hcp (E)] was computed as a function of stress (strain). It was found thatup to 15 pct E phase forms at low temperntures. The amount of E formed increases to a maximum at about 5 pct strain, then decreases. This decrease indicates the additional transformation of E to a'. The total amount of E and a' was suppressed at constant stress (strain) at 4°K as compared to 76°K. It is proposed that the suppression of E and a' is associated with the decreased mobility of extended dislocations at very low temperatures. The yield strength decreased as the temperature was depressed below room temperature and then increased rapidly near 4°K. SOME ferrous alloys which are austenitic (fcc ?) at room temperature appear to be unique in that two martensitic products (hcp e and bcc a') may form on cooling to lower temperatures or on application of mechanical stress. The most common room-temperature austenitic ferrous alloys are 18Cr, 8Ni stainless steels. Most aspects of the spontaneous transformations have been previously described for these steels.' Several previous papers have described special aspects of the stress-induced transformations at low temperatures for the stainless steels, such as the existence of the hcp phase (c) after straining at 76oK,2-7 the morphology after straining using electron microscopy,7 and the decrease in E at higher strains at 76oK.4 However, for a complete representation, one must know the stress-strain characteristics and the dependence of both martensitic products on applied stress and temperature. It is the intention of this paper to provide that documentation. To accomplish this, continuous stress vs strain recordings were made at four temperatures: 300°, 76", 20°, and 4°K for annealed AISI 304L (a commercial 18Cr-8Ni alloy). At periodic stress intervals at each temperature the integrated X-ray line intensity of a selected peak for each phase (y, E, and a') was measured. In addition, photomicrographs of the strained surfaces were taken and magnetic measurements were made. The magnetic readings can be directly converted into percent a'.',e With these measurements the percentage of each phase may be plotted as a function of stress (or strain) and test temperature. It was found that up to 15 pct E phase forms upon stressing the AISI 304L alloy at low temperatures. The E percentage increases abruptly after the alloy yields, but then decreases gradually at higher stresses. The rapid increase in e at 76°K is associated with an "easy-glide" portion of the stress-strain curve. The total amount of a' + .G is suppressed below 76°K at a constant stress or strain. The yield strength decreases down to 76°K but increases rapidly below 20°K. EXPERIMENTAL PROCEDURE Tensile test specimens were cut parallel to the rolling direction from 0.1-in.-thick sheet. Continuous stress vs strain recordings were obtained at each test temperature (300°, 76o, 20°, and 4°K) using equipment and methods described elsewhere.' The specimens which were used in the X-ray analysis were stressed to successive increments of strain at each temperature, analyzed at room temperature, then restressed at the test temperature. This procedure was repeated until approximately ten X-ray analyses had been performed with approximately 1.0 pct strain increments. The specimens had a reduced section 1 in. long, 1.2 in. wide, and 0.1 in. thick. They were electro polished prior to testing and after each strain increment. Table I lists the chemical composition, grain size, and hardness for the alloy which was used. This is the same alloy for which extensive mechanical-property tests3 and morphological studies of the spontaneous transformations' have previously been made. For the low-temperature tests (76o and 4°K) below the Ms temperature the specimens were initially cooled to the test temperature, held for 1/2 hr, then warmed and X-rayed at room temperature. The results are listed in Table 11. From earlier work8 it was known that additional transformation on the second cycle would be considerably less (-0.1 pct

Jan 1, 1964

By S. Stutz

Coal, like most other minerals, only exceptionally occurs in a sufficiently pare state to he directly available for general manufacturing purposes. And even where this is the case, the small coal or slack is usually more impure than the lump coal, as the slate, clay, etc., from the roof and bottom of the vein become mixed with it in the handling it undergoes. These impurities often exceed ten or more per cent. in addition to the impurities of the coal itself. The most common impurities of the coal are slate, or shale, clay, and sulphur. The latter occurs in different forms, but moat frequently as bisulphide of iron, or iron pyrites, and as sulphate of lime, or gypum. In both cases the impnrities add greatly to the amount of ash, and where they are present in considerable quantities the raw coal, and still more the coke made from it, is unfit for the manufacture of iron. Coke will coutain on an average at least fifty per cent. more ash and sulphur than the ram coal from which it is made. To the manufacturer of iron every additional per cent. of ash which his coal or coke contains is a source of additional expense, seemingly small, and yet very important in the aggregate. In the blast-furnace, for instance, the ash must be heated up to the melting-point, and, since it is composed largely of refractory substances, the consumption of carbon in melting it will be equal to at least one-half of its weight; that is, a certain part of tile coke is consumed for the melting and fluxing of the ash and is lost. Besides this, it is well enough known to the iron-master that coke containing lees ash makes the &lag or cinder more liquid and less incliner1 to stick to the walls of the furnace. Fuel containing much sulphur produces generally a white iron, poor in carbon, while from the same ore arrd flux, with a pure fuel, a good foundry iron might be obtained. The work of separating slate, sulphur, etd, from the coal has as yet only been successfully accomplished by the washing process. This process depends for its success on the differences in the specific

Jan 1, 1881

By Bruce W. Gonser, Robert I. Jaffee

Recent work by the authors1 established the constitutional diagram of the gold-germanium system. Of particular interest in the simple euctectiferous system was the eutectic alloy at 12 per cent Ge, which melted at the very low temperature of 356°C and had an unusually fine eutectic structure. It was of interest to investigate the effect of third components on the melting point, microstructure, and strength of this alloy, and in this work the effect of copper is discussed rather completely, with less complete data on the effects of silver, platinum, nickel, and zinc. No reference in the literature has been found on ternary systems with gold-germanium. Materials and Alloying -4s in the work on the binary system, gold-germanium, the germanium used in this investigation was the cyanide-reduced, 99.9 per cent product, produced by the Eagle-Picher Co. Fine gold sheet from Handy and Harmon, pure platinum sheet from the American Platinum Works, copper magnet wire from Anaconda, nickel wire assaying 99.6 per cent Ni. and electrolytic zinc were used for alloying. To make the alloys, charges of the pure metals were put in a graphite crucible and melted in an atmosphere of pure hydrogen. The temperature was brought up to about I050 C, and the metal allowed to freeze in the crucible. Except with alloys containing zinc, melting losses were consistently less than a few milligrams. When zinc was a component, weight losses up to half the weight of the zinc present were incurred, and the alloy compositions were calculated by assuming the entire weight loss to be that of zinc. In all other cases the composition of the alloys could safely be taken as that of the charge. The ingots, as solidified, were segregated, the heavier primary phases being at the bottom and sides of the ingots and the lighter primary phases at the top, but by sectioning the entire ingot vertically for microscopic examination, this factor could be evaluated. Ingots for microscopic examination weighed one gram, and those for thermal analysis weighed three grams. Thermal Analysis In this work, the eutectic line composition and thermal arrests were desired, and, after microscopic exploration had established the position of the eutectic line at a given percentage of the third component, a thermal analysis was run at that composition. The method of thermal analysis used in the work on the binary Au-Ge system,' a method particularly well suited for a small quantity of material, was used in this work. Clearly defined arrests were obtained, although with some alloys containing platinum

Jan 1, 1946