By Masahiro Yoshimura, Sergiy Korablov

"Hydi-othermal corrosion ofTiN, TlAlN and CrN PVD films (3 µm thick) deposited on SUS-304 substrate was studied in 100MPa water in 20-950°C temperature range up , to 750h. The beginning temperature of their reaction was determined as 200°c for TiN and TiAlN and 500°C for CrN films, which are quite low in comparison with that of air oxidation of those powders. Very thin oxide scales. of TinO; n-I homologous series phases were formed above 300°C. TiO2 anatare. is observed for TIN and TiAlN films at 400°C. The· feature of hydrothermal corrosion of CrN films seems to be CrNxOy phase formation.Distinguishable weight changes were observed at higher temperature than 700°C for TiN, 750°C for· TiAlN and 800°C for CrN respectively. Hydrothermal corrosion kinetics .was constructed to calculate the activation energy of hydrothermal corrosions. On the base of obtained data, hydrothermal corrosion resistance was as follows: TiN – TiAlN - CrN. Facetted oxide crystals were formed at higher temperature than 500°C for TiN, TiAlN and 850°C forCrN.IntroductionThe metallic nitride (TiN; TiAlN, CrN) PVD films have high hardness, strength and wear resistance. Therefore these films are widely used in industry for wear resistij.nce application such as cutting tools and die molds. Their performances depend on not only the mechanical properties but also corrosion resistance of coated films. High temperature oxidation of metalliq nitride and nitride films was well studied [1-5]. However there are no reliable data concerning the .corrosion resistance of coated nitride materials. In high-temperature and high-pressure water. There are a few reports on hydrothermal corrosion of nitride films [6,7]. The increase of corrosion resistance of CVD films was observed in following succession TiC - TiCNO - TiCN - TiN at 300-680°C temperature interval and I 00 MPa pressure water according to data of the first report. Kawana et al. [7] have reported about excellent corrosion resistance of CrN films under 290°C and 8, 6 MPa water during I 000 h in the circulating type experimental loop. The films thickness was about 7-10 µm in both cases. However it remains unclear the chemical state of the surface species and especially in-depth distribution, oxide scale thickness and its growth, and defects formation in the oxide film."

Jan 1, 2000

By K. R. Barrett

The cupellation of dore/lead bullion to recover precious metals is one of the oldest metallurgical processes known to man. In recent times this has been carried out in small reverberatory furnaces but the process suffers from a number of disadvantages. A new process has been developed at the Northfleet refinery of Britannia Refined Metals Ltd, which gives much improved performance. The process depends upon the injection of oxygen through a nitrogen shrouded lance at the bottom of the furnace. The lance is consumable and of unique design. Reaction rates are high giving short process time; fuel consumption is low; oxygen efficiency is high and dore recirculation is low. The new process has resulted in substantially lower operation costs.

Jan 1, 1989

By Hector Carreon

During fretting, high points or asperities of the mating surfaces adhere to each other and small particles are pulled out, leaving minute, shallow pits and powdery debris. Sometimes these surface conditions are neglected, but they are important in some application such as the aerospace industry. In this research work, non-contacting and contacting thermoelectric power techniques are performed in fretted 7075-T6 and Ti-6Al-4V samples. It has been found that the contacting and non-contacting thermoelectric power measurements are associated directly with the subtle material variations such as work hardening and residual stresses due to plastic deformation produced in the fretting zone but surface topography. Therefore, both techniques could be used for a global characterization of the most relevant fretting induced effects. Potential of these techniques to monitor subsurface changes in other severe surface plastic deformation processes are clearly envisaged.

Jan 1, 2015

By Nagahiro Saito, Takahiro Ishizaki, Daisuke Yata, Akio Fuwa

"Ternary compound-semiconductor, CuInTe2, film was deposited cathodically under potentiostatic conditions on titanium substrate from aqueous solution containing CuCl2, InCl3, TeO and HCI in this study.The deposition parameters such as electrolytic solution composition, potential and temperature were optimized· for electrodeposition of CulnTe2. Structural characterization of the: deposited film was also carried out using XRD and SEM. Electrodeposited films Were prepared and analyzed for their chemical composition using ICP. The ICP analyses showed that the stoichiometry of the films could be controlled by (1) the deposition potential and/or by (2) the electrolytic bath composition.1. IntroductionThe ternary chalcopyrite type compound semiconductors exhibit such electrical, chemical and optical properties that make them promising for photovoltaic devices (Kazmerski and Wagner 1985)(1). Many researches have been devoted to the characterization of these materials for over one and a half decades. High efficiency solar cells based on p-CulnSe2/n-CdS have been reported (Mickelson and Chen 1983)(2).The electrodeposited fil ns of semiconductors have more advantage than other physical and chemical deposition techniques; it is relatively easy and economic technique and the semiconducting properties such as band-gap variation, concentration of dopant stoichiometric composition and so on can be controlled with some accuracy. The electrodepositions of the ternary CuInS2, CulnSe2 have been reported by many workers (Hodes and Cahen 1986, Bhattachaya 1983, Singh et al 1986, Lokhande and can be prepared as both p-type and n-type. Therefore, its potential for application in optical and photovoltaic devices is one of the great interests. Bhattacharaya and Rajeshwar (1986)(9) reported the electrodeposition of CuInTe2 from an acidic bath· on indium tin oxide (ITO) and Mo substrate. Triethanolamine (TEA) was used as a complexing agent for indium. The electrodeposited CuInTe2 films were non-stoichiometric in composition under all their experimental conditions by electron-probe micro analysis (EPMA) and Auger depth profile analysis. In this paper, we report our results on the behavior .of Cu-In-Te electrodeposition from ·acidic baths; the preparation of CulnTe2 and the effect of bath composition on electrodeposited films obtained."

Jan 1, 2000

By L. A. Barta

A new process for the leaching of chalcopyrite concentrates has been developed and tested in miniplant campaigns and locked cycle testwork carried out between 1996 and 1999. The process involves pressure leaching in a sulphuric acid solution, e.g. raffinate from copper solvent extraction. Iron in the feeds is precipitated predominantly as hematite in the autoclave, simultaneously with copper extraction. Gold and silver in the pressure leach residue are recoverable by conventional cyanidation, following flotation to remove elemental sulphur by-product. The results of recent miniplant tests and batch locked cycle tests are provided.

Jan 1, 1999

By A. A. Trickett

In the treatment of gases from pyrometallurgical processes prior to acid manufacture, volatile components, sulphur trioxide and particulates ,are removed in wet gas cleantng systems. In the process a weak acid stream is generated, typically less than 10% H2S04, contaminated with volatiles such as arsenic, fluoride and chloride', plus metallic particulates. This effluent stream has, in the past, been disposed of in a variety of different ways. As a result of changing environmental legislation, smelters are having to review alternative solutions for treating this effluent stream. This paper' will describe a process developed by Chemetics which treats this effluent stream, generating a small dry metal sulphate stream plus a clean acid stream which is suitable for recycling to the smelter acid plant.

Jan 1, 1992

By Sung-Joo Lee, Gi-Chon Han, Nam-Il Um, Hee-Chan Cho

"In Korea, almost all of bottom ash produced by coal power plants is disposed of in ash ponds. Ash storage areas comprise more than 80% of most coal power plant sites. This disposal method is causing environmental problems and a managerial burden for plant operators. In this study, investigations to develop a beneficiation process for separating coal pond ash into various products were undertaken. To improve efficiency of the separation, coal ash was separated by sizes and each size fraction was subject to various beneficiation processes. The separation process used were flotation (-200 mesh size), hindered settling (16x200) and tabling (16x200 and 8x16 mesh). The results showed that various marketable products, such as lightweight aggregate, sand, high-carbon fuel, could be recovered from coal pond ash using simple physical separation techniques.IntroductionDue to the increased use of coals every year, about fifty million ton of coals were used in 2007 alone. As a result, about 6 million tons of coal ash were generated. In Korea, the coal bottom ash is classified as a general industrial waste and is usually disposed of in ash ponds. The costs for this disposal method continue to increase due to rising costs of site management and development and more strict environmental regulation. Therefore, utilities are constantly looking for ways to increase utilization of coal ash. In this study, various beneficiation processes were evaluated to examine the possibility of separating coal pond ash into various products which can be used as aggregates and high-carbon fuel."

Jan 1, 2008

By Roberto Parada

In a long term program for the optimization of the Outokumpu Flash Smelting Furnace at Chagres Smelter many different subprograms are being developed. One of them is the design and application of a sampling method that can allow the direct diagnostic of the quality of the copper concentrates combustion. We present in this paper the evolution of the sampling devices used in a ten months of continuous sampling campaigns and an example for the sulfur elimination and magnetite formation in the flame from 60 cm to 100 cm under the burner. These type of information combined with the appropriate mathematical modeling of the combustion must propose some considerations to correct the classic criteria in the preparation of the charge for the smelting of copper concentrates based only on the mass and energy balance from the chemical and mineralogy composition of the concentrates.

Jan 1, 2006

By C. H. Quan

Solvent extraction tests were carried out on a rare earth chloride solution derived from monazite processing to determine the effect of extractant and diluent on the distribution coefficients between organic and aqueous phases, and the separation factor between rare earths. The extractants were 20% by volume di-2-ethyl-hexyl phosphoric acid (DZEHPA) or 2-ethyl-hexyl phosphonic acid (Ionquest® 801). Four Shellsol diluents were tested ranging from nil to 100% aromatic content. D2EHPA gave the highest rare earth extraction for a given pH but was less selective than Ionquest. The geometric mean separation factor between adjacent rare earths varied from 2.41-2.56 for D2EHPA to 2.62-3.01 for Ionquest. The nil-aromatic diluents (Shellsol 2037 and 2358) gave better separation factors in Ionquest but, in D2EHPA, were slightly inferior to the 100% aromatic diluent Shellsol AB. Yttrium behaved as a pseudo-heavy rare earth with a distribution coefficient lying between Ho and Er, as expected from its ionic radius.

Jan 1, 1992

By J. P. Rodier

Despite the good years that the non-ferrous business is now enjoying, one should not forget that in this business growth rates are low, fixed assets are high and prices are more cyclical than in other businesses. Increasing environmental concern puts the industry under pressure. Lead and zinc companies are now profitable and profitability in the next ten years will depend on size of units, location, and choice between new technology and upgrading current ones. Implementation of Metaleurope was a strategic move. It produced a company of sufficient size to achieve new steps in cost cutting and yet remain flexible enough to deal with rising variety of primary and secondary raw materials.

Jan 1, 1990

By J. L. Liow

Studies have been carried out on the causes and effects of slopping in an annular cylindrical geometry such as the top submerged combustion reactor. Properties of standing waves formed such as the wave profile, period, pressure distribution and velocity have been derived analytically. The wear profile due to wave erosion was calculated based on the assumption of linear motion and that the wear is a dissolution process. The use of the j, factor showed that the wear was proportional to the square root of the wave velocity at any point. Using the dimensions of the lsasmelt reactor given by Errington et al. (1987)[11, the wear profile due to wave erosion was calculated using the analytical solution. The wear profile calculated was shown to have a maximum just below the initial bath surface. The wear was found to be concentrated in the region where the first asymmetric standing wave was most active. The results showed that the refractory near the bath surface will be affected by wave erosion, more so than any other parts of the reactor. The contribution of wave erosion on wear must be accounted for in assessing the total refractory wear of a vessel in which slopping exists.

Jan 1, 1991

By Jianxun Song, Hongmin Zhu, Qiuyu Wang, Jungang Hou, Shuqiang Jiao, Xiaobo Zhu

This work presents the results of a study on the Ti3+/Ti2+ couple redox potentials vs. Cl–/Cl2 at the temperature range (673 to 1073 K) in fused LiCl-KCl eutectic by direct potentiometric method. Initial concentrations of TiClx in solvents did not exceed 5.0 mol%. Basic thermodynamic properties of the reactions TiCl2+1/2Cl2(g)=TiCl3 were calculated using the temperature dependencies of apparent standard potentials of the couples E* Ti3+ /Ti2+.

Jan 1, 2014

By Peter J. Koros

The current wave of interest in this topic is the result of increased use of titaniferous ores or ilmenite in blast furnace burdens for the purpose of repairing hearth damage. The titanium compounds that promote deposition of ?patching? materials in blast furnaces are the cause of downstream problems in the steelmaking shops. Steelmakers historically have objected to significant amounts of titanium in hot metal (>0.10 % Ti) for several reasons: 1) accretions caused by the TiC.TiN needles that float out of the iron as it cools in transit and in transfers make the accompanying slag sticky and crusty, causing problems in desulfurization and increasing time and Fe yield loss at the subsequent raking, 2) defensive measures have been taken in treatment, such as use of argon for carrier gas, but without technical rationale for this approach, 3) difficulty in removal of the ladle slag by the raker, with subsequent sulfur addition to the vessel charge, and 4) transfer into the BOF and/or formation of a very corrosive TiO2 containing acid slag during the early part of the BOF blow which, in addition to causing lining damage, results in loss of sulfur removal capability by the vessel slag. Based on a conceptual analysis of the metal-slag-atmosphere interactions during transfer ladle desulfurization treatment, a mechanism is postulated for the apparent effectiveness of the use of argon in reducing the deleterious effect of titanium and an alternate technique, possibly more effective, is proposed. As probably the use of argon causes increased exposure to atmospheric oxidation of the titanium carbonitrides contained in the ladle slag, the same benefit can be obtained by use of either oxygen or an air blast to oxidize the noxious reaction compounds. Validity of the concept has been demonstrated in a pilot plant setting. These issues, and related effects on testing the hot metal, are examined in detail with reference to the literature and plant and laboratory experience.

Jan 1, 2006

By Guozhu Ye

Hydrometallurgical zinc recovery from EAF dust has several advantages compared to pyrometallurgical alternatives in terms of low temperature operation, lower energy consumption and higher flexibility. Many hydrometallurgical processes have been suggested and tested over the years without success. The main reasons are: -Low leaching yield of zinc due to the fact that a high fraction of ZnO in the EAF dust exists in the zinc ferrite structure which makes selective leaching of ZnO not possible -Many of the proposals could not handle the halide in the EAF dust To eliminate these two disadvantages, two zinc ferrite elimination concepts have been tested and developed in the REZIN project of the EU 5th Framework Programme. The two concepts for zinc ferrite elimination could be shortly described by the following chemical reactions: A. ZnOFe2O3 + 2CaO = Ca2Fe2O5 + ZnOfree B. ZnOFe2O3 + C = Femet + CO/CO2 + ZnOfree These two concepts were investigated in details in combination with a subsequent leaching step using the novel EZINC process for recovery of zinc from EAF dust. Leaching of pretreated samples has shown great increases of a zinc recovery yield. A zinc recovery of over 90 % could be reached, as compared to about 50 % for no-pretreated samples. This paper will describe the two concepts in details.

Jan 1, 2006

By José Roberto de Oliveira

Based on literature review one can see that the main objectives of MnO reduction is the comprehension of slag interactions and reactions with other elements beyond carbon. That's because it is worthwhile to study pure MnO reduction, where there will be not oxides interaction and just carbon will be the reduction agent. By a thermodynamic analysis we know that Si can react with MnO, then it's important to study this influence, so as Mn content. Our work aims to develop kinetics parameters for the MnO reduction, varying Mn and Si contents in bath. This has been given by pressure measure of CO in a Fe-C bath. The CO is generated by the oxide reduction with carbon. It has been proved that: - Mn content decreases the MnO reduction; - the MnO reduction is mainly influenced by Si content in a bath containing Iron, Carbon and Manganese so as Silicium

Jan 1, 1997

By Yingtao Zhang, Shaofeng Du, Yiming Rong, Wenjun Zhao, Gang Wang

"20Cr2Ni4A steel is a kind of high quality steel mainly used for manufacturing high-duty gears in the world. The high-duty gear with good performance must have wear and fatigue resistance properties. In order to get the good properties, the high-duty gear needs a high hardness gear surface and a good hardness gradient along the depth direction. In this paper, the samples were designed and a vacuum carbonitriding process was put forward to improve the surface hardness of parts for 20Cr2Ni4A. The process contained carbonitriding, quenching, cryogenics, and tempering process. The surface hardness and hardness gradient of carbonitrided samples were measured and the good microstructure was gained. The surface hardness is 67.SHRC and the case depth is 1.2mm.IntroductionSteels are widely used in industry, but the fatigue strength and the wear resistance of steel is much low. So the heat treatment process is put forward to improve the mechanical properties of steel. It can be improved by high-energy heat treatment methods for medium-carbon and highcarbon steel. Those methods will not alter the chemistry of the base metal [ 1].For low-carbon steels, carburizing and quenching should be used to improve the steels' mechanical properties, especially the surface properties. Compared with the carburizing, carbonitriding has more advantages, such as a short production cycle, low temperature and small deformation of parts. Carbonitriding is a modified form of gas carburizing, rather than a form of nitriding. The modification consists of introducing ammonia into the gas carburizing atmosphere to add nitrogen to the carburized case as it is being produced. Nascent nitrogen forms at the work surface by the dissociation of ammonia in the furnace atmosphere; the nitrogen diffuses into the steel simultaneously with carbon. Typically, carbonitriding is carried out at a lower temperature and for a shorter time than is gas carburizing, producing a shallower case than is usual in production carburizing [2]. As a material surface strengthening technology, carbonitriding has been widely used in the production [3]. And vacuum carbonitriding process is better than carbonitriding, because the vacuum carbonitriding temperature can be higher than carbonitriding without surface oxidation."

Jan 1, 2014

By W. L. Cornell

The processing of lead tailings for removal of the heavy metals produces concentrates upgraded in Co and Ni values. Reflected light microscopy, scanning electron microscopy, image analysis, and Vickers hardness measurements were used to identify mineral species, associations, degree of liberation, and distributions to the test products. Siegenite and bravoite were the most common species encountered, but violarite and enriched pyrite and marcasite phases were also identified. Liberation for the Co and Ni minerals contained in the tailings was 20 micrometers or less.

Jan 1, 1993

By W. L. Cornell

Ore microscopy was used in support of both bench-and large-scale continuous beneficiation testing programs. Reflected light microscopy and Vickers hardness measurements were utilized to help identify problems relating to mineral identification, mineral association, mineral liberation, mineral distribution in product streams, and froth entrainment. Specimens studied were size fractions of concentrates and tailings resulting from Bureau of Mines research to recover a siegenite-enriched product by beneficiating chalcopyrite concentrates. Other specimens were size fractions of bulk sulfide concentrates recovered during the enhanced amine scavenging of final tailings by froth flotation. The findings from studies directly affected flowsheet development.

Jan 1, 1987

By Mingchun Lu, Zhijia Liu, Xueqi Zhang, Jianliang Zhang

"In order to solve the problem of shortage of scrap, especially high quality scrap, a new substitute for scrap or DRI has been developed. The decarbonization mechanism of granular pig iron has been analyzed and the technical process and decarbonized granular pig iron have been evaluated in this paper. The research result shows that this new process is superior to direct reduction process in product quality, construction investment, operation flexibility, production efficiency etc. Decarbonized granular pig iron (DGPI) not only can be used as conventional scrap but also can be charged into EAF as high purity .burden equivalent to heavy scrap:IntroductionIn the past years, with the universal application of continuos casting technique in China, the amount of scrap generated inside steelworks has been reducing continually. On the other hand, the EAF steel proportion is increasing and this gives to the obvious change in structure of steel product. At present, the requirement on both scrap quantity and scrap quality is being paid more and more attention. Because China is a country which is devoid of scrap and poor in resource (nature gas and high grade iron ore) for developing direct reduction iron (DRI) so that sponge iron can not be produced cosmically in China and has to be mainly imported. Instead of part of scrap, some cold pig iron in cold state has been charged into EAF in China. However the high carbon content in pig iron has limited its proportion in EAF metal burden. Because the price of pig iron is lower than that of imported DRI in China, the technique of granular pig iron decarboniztion is hopeful to become effective way to produce substitute for scrap or DRI."

Jan 1, 2000

By S. Vukcocic

A long term research project is in progress to establish the parameters of an acid leach process to recover alumina 'froui' high-iron and/or low-iron white bauxites, kaolinite, coal. ash and copper mine tailing. In this paper the results of acid leaching of copper flotation tailing for the removal of alumina are presented. The tailing is very complex material which contains 25% Al203 in the -10 lim fraction. X-ray diffraction indicates presence of quartz, kaolinite and minor 'alunite. After classification and ,separation of the -10 lim fraction, the raw material is fired to 550GC and leached at 90GC. Filtration is applied for the separation of white silicate residue form leach liquid. After the purification step, aluminum salt is crystallized from the solution, and calcined to alumina. Kinetic correlation and regime, of the processes are defined and presented in the paper.

Jan 1, 1992