Experimental Study on the Influence of Vacuum Carbonitriding Process for 20Cr2Ni4A Steel

"20Cr2Ni4A steel is a kind of high quality steel mainly used for manufacturing high-duty gears in the world. The high-duty gear with good performance must have wear and fatigue resistance properties. In order to get the good properties, the high-duty gear needs a high hardness gear surface and a good hardness gradient along the depth direction. In this paper, the samples were designed and a vacuum carbonitriding process was put forward to improve the surface hardness of parts for 20Cr2Ni4A. The process contained carbonitriding, quenching, cryogenics, and tempering process. The surface hardness and hardness gradient of carbonitrided samples were measured and the good microstructure was gained. The surface hardness is 67.SHRC and the case depth is 1.2mm.IntroductionSteels are widely used in industry, but the fatigue strength and the wear resistance of steel is much low. So the heat treatment process is put forward to improve the mechanical properties of steel. It can be improved by high-energy heat treatment methods for medium-carbon and highcarbon steel. Those methods will not alter the chemistry of the base metal [ 1].For low-carbon steels, carburizing and quenching should be used to improve the steels' mechanical properties, especially the surface properties. Compared with the carburizing, carbonitriding has more advantages, such as a short production cycle, low temperature and small deformation of parts. Carbonitriding is a modified form of gas carburizing, rather than a form of nitriding. The modification consists of introducing ammonia into the gas carburizing atmosphere to add nitrogen to the carburized case as it is being produced. Nascent nitrogen forms at the work surface by the dissociation of ammonia in the furnace atmosphere; the nitrogen diffuses into the steel simultaneously with carbon. Typically, carbonitriding is carried out at a lower temperature and for a shorter time than is gas carburizing, producing a shallower case than is usual in production carburizing [2]. As a material surface strengthening technology, carbonitriding has been widely used in the production [3]. And vacuum carbonitriding process is better than carbonitriding, because the vacuum carbonitriding temperature can be higher than carbonitriding without surface oxidation."