Search Documents

By Xuling Chen, Zhiyun Ji, Min Gan, Tao Jiang, Liang Yin, Xiaohui Fan

Straw char exhibited considerably faster burning speed than coke breeze for its porosity, which significantly degraded sinter quality when it replacing coke breeze as sintering fuel. In this investigation, preforming technology has been employed to densify raw straw. The properties of straw char preformed show that its density was increased, and the structure was also densified, which made the difference of combustibility between the straw char and coke breeze smaller. The proper preforming temperature, residence time and pressure were 200℃, 1min and 120MPa respectively. Sinter pot trials show that the product carbonized from preformed straw made the proper replacement ratio to coke breeze increase from 20% to 40%, and the emission reduction of SOx, NOx in flue gas increase from 11.50%, 14.15% to 37.85%, 23.60% respectively, compared with non-preformed straw char.

Jan 1, 2015

By Z. Yang

The flotation behavior of the. green algae Chlorella vulgaris and a wild Chlamydomonas spp. was studied in the presence of Zn(II) using dodecylammonium chloride as collector. At about pH 6. both organisms readily float as amine concentration approaches lx10-3 kmol/m3. In addition, electrokinetic measurements were made on the organisms as a function of pH in both the presence and absence of Zn(II). It was found that the Zn(II) has a considerably greater effect on the zeta potential of C. vulgaris than on Chlamydomonas. Zn(II) adsorption studies also indicated that C. vulgaris is able to accumulate more Zn from solution than the Chlamydomonas.

Jan 1, 1991

By Mansoor Barati, Leili Tafaghodi Khajavi

"This study involves employing solvent refining as a purification process in which silicon recrystallization takes place from an iron-silicon melt. It is believed that iron will act as the impurity “getter” and purified silicon crystals will grow from the alloy melt, while the impurities are segregated to the liquid alloy. Phosphorous is a problematic impurity to remove since its segregation coefficient in pure silicon is relatively large. To assess the feasibility and efficiency of phosphorous removal through solvent refining, it is critical to study its equilibrium distribution between solid Si and the Fe–Si alloy phase.The distribution of phosphorous between solid silicon and iron-silicon melt at 1210-1310 °C was measured to evaluate the impurity removal potential of each alloy. Interaction parameter between phosphorous and iron was calculated by varying the concentration of phosphorous in silicon.IntroductionAmong various semiconductor materials for manufacture of solar cells, silicon accounts for over 90 percent of today's PV materials [1, 2].The major challenge in producing solar silicon that operates efficiently is to meet purity level requirement through a cost efficient route. Silicon solar cells can play a significant role in answering the world's need for energy if cost reductions can be achieved through manufacturing process. Considerable effort has been made to replace the expensive, complex vapor-phase purification by a simpler and less costly process. One of the refining approaches that have attracted wide research interests is producing low-cost solar grade silicon by purification of metallurgical grade silicon. Since metallurgical processes are selective in removing impurities, a combination of various purification processes can be used to reduce the impurity level in silicon. Considering different thermodynamic characteristics of impurities, each refining step is responsible for lowering specific impurities."

Jan 1, 2012

By Chonghe Li, Xionggang Lu, Wei Xiao, Xingli Zou, Weizhong Ding

The reduction degree and rate of the initial ilmenite concentrate and pre-oxidation samples by hydrogen were investigated by using thermogravimetric analysis system. H2-TPR was used to detected reduction properties of the pre-oxidation products which were oxidized at different temperatures. The phase transformations and micromorphology changes during pre-oxidation and hydrogen reduction were identified by XRD and SEM. The FeTiO3 was decomposed into TiO2 and Fe2O3 at the temperature below 900 oC. With the temperature rising, Fe2TiO5 was the only stable phase in high temperatures. The reduction of pre-oxidation ilmenite concentrate was faster than the natural sample, which was attributed to the micropores generated on the surface of ilmenite concentrate during oxidation. The main phases of the reduction product were metallic iron, ferrous pseuodbrookite.

Jan 1, 2014

By E. Krystad, G. Tranell

"The kinetics of boron removal from liquid silicon during slag refining, as a process step in the production of solar grade silicon, has been investigated by means of small scale mass transfer experimental series at 1600°C, using a graphite crucible. The slags were SiO2-CaO based, with or without addition of approx. 19 wt% MgO. Experiments were carried out at slag-metal ratios of 1 or 2, where the silicon initially contained approx. 250 ppm boron. The metal-slag mass transfer coefficients for boron were found to be in the order of 1-3 · 10-6 m/s and were largely influenced by slag composition. The mass transfer rate was higher for the MgO-containing slag than the slags without MgO. The final equilibrium distribution of boron between metal and slag, LB, was determined to be in the order of 2.3-3.3.I. INTRODUCTIONRecent years have seen a race in industry and research aimed at obtaining a reliable metallurgical route for production of silicon for solar cells (SoG-Si) from metallurgical grade (MG) silicon. Metallurgical routes can successfully challenge the traditional chemical routes for production of SoG-Si if they generate metal of sufficient purity while being less expensive in terms of production cost and energy consumption. Efficient removal of boron is one of the greatest obstacles in the refining of silicon by a metallurgical route, because the segregation coefficient of boron in silicon makes directional solidification unfeasible; in addition, the vapour pressure of boron is not high enough for removal by vacuum refining. However, the thermodynamic properties of boron makes removal from silicon by oxidation possible, and thus the process of slag refining of silicon has been receiving increasing attention as a method for boron removal."

Jan 1, 2012

By Fjeldstad Karin Jusnes

Two quartz types used in the silicon and ferrosilicon industry were heated to temperatures of 1600 and 1700 °C. The parameters varied were the temperature and the holding time at maximum temperature. The amount of quartz, cristobalite and intermediate amorphous phase were measured using XRD and the internal standard method. Type P showed a much larger ability to transform to cristobalite at lower temperatures than type A. Type P had a larger amount of alkali and alkaline earth impurities. This could have enhanced the transformation to cristobalite. For quartz type A the amount of cristobalite was larger at 1600 °C than 1700 °C. This can also be seen for some of the samples of type P at shorter holding times.

By Yuanpei LAN, Minren XU, Deliang NIU, Zhu WANG, Qingcai Liu, Shan Ren

Removal of gas is the major function of RH degasser. To optimize the RH refining craft in Chongqing Iron and Steel Co. Ltd, the degassing effect of RH degasser at different degrees of vacuum was investigated using a vacuum induction furnace. In addition, the effect of processing time on the gas content dissolved in molten steel was also studied. The results showed that degree of vacuum was one of the important factors that determined the degassing efficiency in RH refining process. High vacuum degree is helpful in the removal of gas, especially in the removal of [H] dissolved in molten steel. The processing time could be reduced from 25-30 min to 15 minutes and gas content could also meet the demand of RH refining

Jan 1, 2015

By Cheng Pan, Xuewei Lv, Guibao Qiu, Chenguang Bai, Meilong Hu

"Physic-chemical properties of slag at high temperature play an important role in the pyrometallurgical process of production of ferronickel alloy. It determines the operation efficiency, metal recovery ratio, energy consumption and the distribution of elements like S and P between the slag and metals. In the present work, the effect of MgO content in the slag on melting features and viscosity of the slag was investigated. The MgO content in the SiO2-CaO-MgO-Al2O3 -FeO in the quinary slag system varied from 14.5% to 22.5%. The results shown that all slag samples begin to softening at the same temperature, the softening temperature, melting temperature, flowing temperature decrease with the increase of MgO content when the MgO content is in range of 14.5 and 20.5 pct mass, and when MgO content up to 22.5 percent, the temperatures increase sharply. Besides the inflection point temperature of viscosity-temperature curve increase with the increase of MgO when the MgO content is in range 16 and 22.5 pct mass.IntroductionNickel is very important to modern society, without it, we would not be able to share many things in our daily life, such as airplanes, computers and many stainless steel appliances in our homes and workplaces1.. It is the essential element of the stainless steel making, and about 65% of the nickel consumed in the world is used to make stainless steel2., so with the increase of stainless steel, the nickel production and demand has continued to increase3.Nickel is produced from two distinct ore types: nickel sulfide deposits and oxide nickel laterite deposits. The great majority of world’s known nickel resources are contained in laterite deposits3.. The laterite ores are normal classified into two groups: the high-iron laterite ore and high-magnesia laterite ore1. Typical composition of high-magnesia laterite ore is in the range 1-3%, and these ores are suitable for pyrometallurgical process to produce ferronickel4."

Jan 1, 2012

By J. K. S. Tee

Using a novel method, zinc has been selectively removed from galvanized steel scrap on a laboratory scale. The separation is based on thermodynamic principles: during chlorination in air-chlorine (10:l) mixtures at 800 OC, zinc forms a volatile product (zinc chloride) while iron does not chlorinate as its oxides are more stable than the respective chlorides. As much as 92 % of zinc is removed from the surface of steel within 10 minutes. This process overcomes tedious and costly preparatory stages associated with leaching - electrowinning methods.

Jan 1, 1999

By Gennady I. Gulyayev

A mathematical model of plastic deformation occurring in cold plug drawing of mother tubes with initial cross-sectional wall thickness variations (CSWTV) has been developed. The main provision of the model is that eccentricity em is of such value that projection of all forces acting upon the plug in the deformation zone along the axis perpendicular to the drawing axis equals to zero. Calculations have proven that with other conditions being equal increase in the die cone angle and the deformation cycle number reduces CSWTV. Theoretical findings were confirmed by practical results. Keywords: cold, drawing, plug, die cone, plastic deformation.

Jan 1, 2003

By Katsuya Kase, Kaname Takeya, Keaji Ohmori, Yoshiyuki Asakawa

"The reduction-diffusion process (the R-D process) using Ca as a reducing agent has been practiced in industry in the production of the SmCos type, the Nd-Fe-B type and the 1b-Fe-Co type magnetic materials. The advantages of the R-D process are the generally high yield of rare earth metals and the single-stage conversion of a mixture of oxides and metal powders into a product of rare earth alloy powders. On the other hand, one of its disadvantages is the slightly high contents of oxygen and calcium. This disadvantage is remarkable in the Nd-Fe-B type. Singe-phase Nd2Fe14B alloy powders with low content of 0 and Ca, is obtained by choosing appropriate raw materials and performing the R-D process in a controlled way. These alloy powders are very suitable for the production of Nd-Fe-B sintered magnets and expected higher magnetic properties by adopting advanced magnet production method.IntroductionThe hard magnetic rare earth transition metal intermetallics, especially, have attained considerable technical importance. Examples are the alloys based on the intermetallics SmCo5[1], SmC017[2], NchFet4B[3], or the recently developed alloy SnuFe11Nx[4]. The reduction-diffusion process using Ca as a reducing agent has been well known as an economical method of producing rare earth based magnet materials[5]. The reduction-diffusion process has been practiced in industry in the production of the SmCos type, the Nd-Fe-B type and the 1b-Fe-Co type magnetic materials. The advantages of the reduction-diffusion process are the generally high yield of rare earth metals, the single-stage conversion of a mixture of oxides and metal powders into a product of rare earth alloy powders, the elimination of the crushing process of the alloy ingot, the inessentiality to special equipment, etc. On the other hand, one of its disadvantages is the slightly high content of oxygen and calcium. This disadvantage is remarkable in the Nd-Fe-B type. An outline of basic studies of the reduction-diffusion process was reviewed from the particular viewpoint of the production of magnet materials by Ogawa [6]."

Jan 1, 1998

By N. Kanari

The thermal decomposition studies of two zinc basic carbonate samples were carried out up to 400 "C by thermogravimetric analysis, boat experiments and differential scanning calorimetry measurements 'DSC'. The initial samples and the solid decomposition products were analyzed by scanning electron microscopy, x-ray diffraction and laser particle size analyzer. The thermal decomposition of both samples started at about 150 "C and the rate of decomposition became significant at temperatures higher than 200 "C. The apparent activation energies 'Ea' in the temperature range 150-240 "C for sample decomposition were between 132 and 153 kJ1mole depending on the sample origin. The XRD analyses of the intermediately decomposed samples and the DSC results up to 400 "C suggest that the decomposition reaction probably occur in a single step.

Jan 1, 2002

By C. M. F. Vieira

Crushed fired brick waste, known as grog, screened at two different particle size, 840 (20 mesh) and 180 µm (80 mesh), was used in mixtures with clayey body to make typical red ceramics for bricks. The effect of the grog addition up to 20 wt.% on the properties of bricks fired at 700oC was evaluated. The results indicated that both the particle size and the amount of grog addition changed the fired properties of the clayey body. Additions above 5 wt.% of grog, with a coarser particle size, decreased the mechanical strength of both the dry body and the fired ceramic pieces. By contrast, grog with a finer particle size may be used up to 10% wt. without deteriorate the properties and corresponding microstructure of the clayey body.

Jan 1, 2009

By Adam J. Gesing

Eddy current separators are increasingly used by the auto shredder operators to produce higher grade of nonferrous metal concentrate for recycling. While this increases the unit price of the concentrate, metal losses through inefficient metal recovery quickly offset the price differential. We show how to optimize the eddy current separation system at the shredder to maximize mate- rial throughput, nonferrous metal recovery and grade of the nonferrous metal concentrate.

Jan 1, 1998

By H. Fukuyama

The wetting behavior of single crystalline MgO by fayalite-type slag melts has been studied by the sessile drop technique incorporated with high temperature X-ray radiography. The experiments were performed under oxygen partial pressures of 10-6 and 10-4 Pa at 1473 K. Mass ratios of iron to silica, Fe/Si~, in the slag employed were 1.4 and 2.0. To investigate the interfacial reaction, experiments using high density MgO crucibles were also conducted. The reactions at the interfaces were examined by Electron Probe Microanalysis. The contact angles between the slag melts and the MgO substrates were found to be relatively low, ranging from 30 to 10 degrees. The surface tension of the slag was 0.4 N/m for a slag of Fe/Si02 = 2.0. Two phases, magnesiowiistite and olivine, were observed at the interface. Interdiffusivity in magnesiowiistite solid solution was determined as a function of iron oxide content. Phase relations between magnesiowilstite and olivine, and the growth rates of both phases, are also discussed

Jan 1, 1996

By Min Chen, Lei Xu

Sintering behavior and performance of high alumina refractory based on the ternary subsystem MgAl2O4-CaAl4O7-CaAl12O19 were investigated using ZrO2 as an additive up to 8 wt.% by solid state reaction sintering. It was found that the added ZrO2 could dissolve in the CA6 grains in the form of a solid solution, which enhanced the isotropic growth of CA6 grains and then improved the sintering. As a result, the densification process was improved and areas with enrichment of ZrO2 showed a more compact structure. With further increase of ZrO2 addition, tetragonal ZrO2 were found to locate in the grain boundaries for exceeding the solid solubility limit, which enhanced the thermal shock resistance, indicating that addition of ZrO2 exhibited a positive effect on sintering behavior and performance of this refractory. In addition, it is considered that the optimal amount of ZrO2 addition was about 4% considering the performance together with the cost.

Jan 1, 2015

By Juan Hernández Ávila

This work studies the Molybdenum effect on the microestructure, mechanical properties of an as-cast ductile iron. For this study five ductile irons with different amounts of Molybdenum each were made in an induction furnace. In this material nodule count and nodularity is affected by the Molybdenum additions; The iron´s matrix, nodules and the phase were analyzed using scanning electron microscopy detecting Molybdenum only in the matrix. Mechanical properties such as hardness, microhardness, tensile strength and yield strength show increments as the Molybdenum amount is increased. In the same way, ferrite and pearlite phases display a variation in their percentage as the contents of the alloy element increase. This element has a marked influence on the pearlite interlaminar spacing. From the obtained results we conclude that Molybdenum in these quantities dissolves in solid ferrite solution during the solidification process, improving the material´s mechanical properties.

Jan 1, 2009

By XUEWEN WANG, Bowen Li, Mingyu Wang

A novel technology characterized by higher extraction of vanadium and recovery of valuable elements was developed to recover vanadium from stone coal. The brief flow of the novel technology mainly includes low temperature sulphation roasting, water leaching, recovering potassium, aluminum, copper and selenium, solvent extraction enrichment vanadium, precipitation of red vanadium, removal sodium from red vanadium and calcinations. The total recovery of vanadium reached 76.3%, which was higher than the current applied technology. The novel technology was environmentally-friendly and could extract vanadium from the stone coal, in which the content of V2O5 was less than 0.8%.

Jan 1, 2015

By S. Mondon

Hibi Smelter which is a Copper Smelter lining a blast furnace, produces 2,700 metric tons of anode copper per month. Generally, in a copper refinery, arsenic and antimony are considerably troublesome impurities. With regard to the elimination of antimony, Hibi Smelter has two handicaps described as follows. (1) Smelting under the slightly oxidizing atmosphere in the blast furnace. (2) Recycling the converter slag to the blast furnace after cooling. Therefore antimony and arsenic, mainly antimony, elimination tests, in which the alkaline flux was injected through the two tuyeres in the blowing stage, were carried out in the rotary anode furnace. Antimony and arsenic were respectively removed more than 90 96 from the molten copper, and their high eliminations are discussed by application of the transitory and permanent reaction model with the flux injection, which was presented by T. Lehner.

Jan 1, 1983

By Martin E. Nelson

Several heavy metal separation techniques are currently being developed for soil remediation at various Department of Defense and Department of Energy (DOE) Facilities. The majority of these techniques involve a wet process using water, PH modifiers or other compounds. The United States Naval Academy (USNA) has developed a dry process for heavy metal separation. The process uses air classification technology to concentrate the metal contaminant into a fraction of the soil. The advantages of this dry process are that it creates no contaminated by product and uses commercially available technology. The USNA process is based on using a Gayco-Reliance air classifier. Tests have been conducted with the system at the Naval Academy and the University of Nevada-Reno (UNR). The USNA tests used soil from the Nevada Test Site mixed with bismuth at a concentration of 500-1000 ppm. The UNR tests used soil from four DOE sites mixed with uranium oxides and plutonium at an activity level of 100-700 pCi per gram. Concentration of activities and volume reduction percentages are presented for the various soils and contaminants tested.

Jan 1, 1995