Preparation Of Straw Char By Preformation-Carbonization Process And Its Application In Iron Ore Sintering

Straw char exhibited considerably faster burning speed than coke breeze for its porosity, which significantly degraded sinter quality when it replacing coke breeze as sintering fuel. In this investigation, preforming technology has been employed to densify raw straw. The properties of straw char preformed show that its density was increased, and the structure was also densified, which made the difference of combustibility between the straw char and coke breeze smaller. The proper preforming temperature, residence time and pressure were 200℃, 1min and 120MPa respectively. Sinter pot trials show that the product carbonized from preformed straw made the proper replacement ratio to coke breeze increase from 20% to 40%, and the emission reduction of SOx, NOx in flue gas increase from 11.50%, 14.15% to 37.85%, 23.60% respectively, compared with non-preformed straw char.