By Gerardo Fuentes

The stoichiometry and kinetics of the hydrothermal reaction of enargite in copper sulphate solutions was investigated in the range 140–300 °C, and particle size under 15 and 50 μm. The stoichiometric experiment was performed at 300 °C, using one gram of sample (96% enargite, 4% tennantite) and 100 mL of copper sulphate solution (10 gpl) at 1.2 pH. Enargite reacted completely after 80 min. A solid product was obtained and characterized by XRD. The main product was chalcocite (M) and some traces of djurleite and chalcocite (Q). Tennantite did not react under these conditions. The kinetic experiments were conducted at 140 °C, 190 °C, 250 °C and 300 °C. From fitted data and Arrhenius equation the calculated activation energy (Ea) was 51 kJ/mol. According to the hydrothermal transformations studied, the reactivity of different phases found in the copper concentrates was bornite > chalcopyrite > covellite > sphalerite > pyrite > enargite > tennantite.

By Xun Hu, Jian Pan, Hongbin Yu, Deqing Zhu, Yanhong Luo

Lump ores are one kind of important burdens for blast furnace (BF), their metallurgical properties have significant influence on BF performance. In this paper, the relationships between the mineralogy of five natural lump ores and the metallurgical performance have been studied. The mineralogy study includes mineral compositions, microstructure and porosity, and the metallurgical performance covers reducibility index (RI), low-temperature reduction degradation index (RDI) and decrepitation index (DI). The results show that the complex lump containing hematite, and goethite has better overall metallurgical performance. For single lump, the RI of goetihte ores is higher, the RDI and the DI is strongly influenced by porosity. The hematite and magnetite ores have good anti-decrepitation and anti-RDI, but generally the RI is lower due to lower porosity, and the RI is related to the grain size, the smaller grain size is, the better reduction will be.

Jan 1, 2015

By Lucio Fabio Cassiano Nascimento, Luis Henrique Leme Louro, Sérgio Neves Monteiro, Jheison Lopes dos Santos, Fernanda Santos da Luz, Fábio Oliveira Braga, Rubens Lincoln Santana Blazutti Marçal, Hugo Concolato de Oliveira Freitas, Édio Pereira Lima Júnior

Epoxy matrix composites reinforced with up to 10, 20 and 30 vol% of continuous and aligned natural mallow fibers and 30 vol% of mallow and jute hybrid fabric were for the first time ballistic tested as personal armor against class III 7.62 mm FMJ ammunition. The ballistic efficiency of these composites was assessed by measuring the dissipated energy and residual velocity after the bullet perforation. The results were compared with that in similar tests of aramid fabric (Kevlar™) commonly used in vests for personal protections. Visual inspection and scanning electron microscopy analysis of impact-fractured samples revealed failure mechanisms associated with fiber pullout, rupture and layers delamination. When compared to Kevlar™, the mallow fiber and hybrid fabric composite displayed practically the same ballistic efficiency. However, there is a reduction in both weight and cost, which makes both, mallow fiber and hybrid fabric composites, a promising material for personal ballistic protection.

Mar 1, 2018

By Weizhi Zeng, Michael L. Free, Shijie Wang

Copper electrorefining is an old technique that is generally performed in electrolytic cells with a bottom inlet and top outlet that are convenient for electrolyte flow control. Nevertheless, this configuration cannot effectively direct electrolyte flow to the regions between electrodes, which results in weak convection and inadequate delivery of chemical species and additives. In this article, we discuss the innovations in electrore fining cell design to improve electrolyte flow for better cathode quality and simulation of fluid flow field and particle movements based on finite element modeling method. The resulting fluid flows in cells can transport suspended slime particles to the cathode, where they can be incorporated as impurities. The concentration of suspended slime particles is inversely related to slime adhesion, which is strongly influenced by slime particle sintering, and sintering is dependent on temperature and slime particle composition. Thus, the combination of innovative fluid flow and slime particle sintering can play important roles in improving cathode quality.

Mar 1, 2017

By Linfeng Zhou, Rong Sun, Guanghui Li, Zhiwei Peng, Tao Jiang

Dust, or airborne particulate matter, from metal smelting can be either mechanically or thermally generated and it negatively affects the indoor air quality as well as the fugitive emissions from the plant. The thermally generated dust is often referred to as fume and it is typically generated whenever liquid metal comes into contact with air. For practical reasons, such as vehicle access, etc. it is often difficult to collect 100% of the fume. It is therefore highly desirable to develop processes and optimize operational procedures so that fuming can be kept to a minimum. In this series of experiments, the mechanism of active oxidation and fume formation from liquid silicomanganese under an impinging air jet in the temperature range 1400-1600°C has been explored. Characteristic properties of the fume have been established; particle diameter, shape, size distribution, and elemental composition are reported. The oxidation process is described in terms of vaporization, oxidation and agglomeration. In the boundary layer, two competing mechanisms seem to be operative in parallel: a direct oxidation of Mn vapor, and a two-step oxidation of silicon. The thermodynamic and kinetic conditions governing the two mechanisms are discussed.

Jan 1, 2016

By H. P. Wang, E. M. Perry

"Analytical solutions for investigating the solidification of casting problems with initial superheat and natural boundary conditions have been derived using an integral method. There are two moving interfaces in the solution field, one for the phase change line and the other for the superheat line. Two coupled nonlinear differential equations, representing two moving layers, were calculated by the Runge-Kutta numerical integration scheme. The solutions are in terms of six dimensionless parameters: phase change number, two Biot numbers for interfaces, diffusivity ratio, and dimensionless superheat temperature and time. Parametric studies on these parameters have been conducted to provide generic information about this phase change problem. This analytical information is extremely useful for validating numerical solutions. A simplified I-D finite element model was constructed for the purpose of comparison. The excellent agreement between the analytical and finite element solutions has proven that they are mutually validated.This validated finite element modeling tool was then used for modeling an investment casting process of a super-alloy with a simple geometry: a two-step plate. The nonlinear latent heat release, a common property of alloy materials, was approximated by several piecewise linear segments. The transient temperature response of this 2-D finite element solution, including a metal/mold gap resistance, shows excellent agreement with experimental data.This fundamental work provides a solid basis for further work on the development of a process modeling tool for the complex investment casting process.IntroductionAt present, the investment casting process is used in a variety of industries. In the aircraft engine industry, in particular, investment casting is used to produce parts ranging from turbine blades to engine frames. Because a large single casting can replace many component parts that require machining, fabrication, and assembly, this one-piece casting approach becomes a very cost-effective manufacturing process.The main constraint in using this process for mass production is the long design-to-production lead time. The standard rigging design is still an art, based on the experience of casting experts, rather than on scientific methods. Many trials are often required before making a sound final casting. In order to .reduce the number of expensive casting trials, the development of computer-aided tooling technology is needed.The fundamental physics describing this manufacturing process can be simply described. They reduce to a solid/liquid phase change problem, with two parts - first, the thermal balance of the initial superheat temperature of the molten metal and the preheat temperature of the ceramic shell through heat conduction, and second, the energy release from the mold surface to the ambient by radiation."

Jan 1, 1986

By Jaeheon Lee

Gold-copper alloys are shown to form during the cementation of gold on copper in a solution containing 0.25M [S2O32-] at 25oC. The alloy composition is strongly dependent on the initial Cu:Au ratio in solution and ranges from Au3Cu to AuCu3. XPS results for Au, Cu, S, and O are reported as a function of depth through an entire deposited film with an initial solution containing 20 ppm [Au] and 30 ppm [Cu]. The deposit contained about 20 atomic % gold and was predominantly Cu3Au. Underpotential deposition (UPD) theory is discussed as a mechanism for explaining the formation of these alloys. Several other systems that produce alloys during contact reduction/cementation are also discussed.

Jan 1, 2003

By Hee Dong Jang

Crystalline metal oxide nanoparticles such as lithium cobalt oxide (LiCoO2) and indium tin oxide (ITO) were synthesized from sprayed droplets of aqueous precursor solution by flame spray pyrolysis. Complete thermal decomposition of the aerosol precursors was obtained at high flame temperature. Molar concentrations of the precursor solution, and the flow rate of combustion gas such as hydrogen, oxygen and air were varied to control particle size, size distribution and crystal structure. The crystalline nanoparticles synthesized were nearly spherical, and their average primary particle diameters ranged from 11 to 35 nm for LiCoO2 and from 8 to 15 nm for ITO.

Jan 1, 2006

By Andre L. De Vegt

For the past eight years Paques has been engaged in the development and installation of treatment systems based on biotechnological processes to remove sulfur compounds from water, air and gaseous streams. Metal and sulfate can be removed from mine waters using two biological steps: 1. Sulfate reducing bacteria convert sulfate to hydrogen sulfide (HzS). The HzS reacts with the dissolved metals to form insoluble metal sulfide precipitates. 2. Sulfide oxidizing bacteria convert excess H2S to elemental sulfur. Paques has designed and installed a groundwater treatment system for the Budelco zinc refinery in the Netherlands to remove metals and sulfate as described above. The system has been operating since May 1992 treating a flow of 5000 m3/d. A test program, utilizing a large scale pilot plant, will commence in November 1995 at a copper mine in the U.S.A. to remediate groundwater contaminated with sulfate and heavy metals. Biological reactor performance and selective metal recovery will be studied. Sulfur dioxide (S00 can be removed from fluegas using a combination of scrubber technology and the two biological steps. The end product is elemental sulfur. A commercial size biological desulfurization plant has been in operation since July 1994 treating 50,000 Nm3/h of fluegas. Sulfide can be removed from mining waters or anaerobic wetlands using a THIOPAQ® Sulfide Oxidizing reactor.

Jan 1, 1996

By Jian Li, Pei Liu

In recent years FIB has become a powerful instrument to perform ion beam sectioning and site-specific TEM specimen preparation. However, there are still gaps in understanding FIB-induced artifacts. Gallium ion beam damage and specimen heating during FIB milling can produce unwanted artifacts during FIB work.Calculations ofmaximumspecimentemperature increaseshavemostlybeen based on the assumption that ion beam implantation into substrate of infinite size. This deviates from finite specimen volume in FIB TEM specimen preparation that impedes specimen heat dissipation. In this paper, the authors will demonstrate a few commonly observed FIB artifacts, and discuss the concerns of specimen temperature rise during FIB milling process.

Mar 1, 2017

By Fuming Wang, Lifu Hu, Changrong Li, Ruipeng Pang

The solidification structure of 430 ferritic stainless steel has been calculated in the solidification process by using 3D-CAFE model under the condition of water cooling. The calculated results consistent with those obtained from experiment. Under watercooling condition, the solidification structure consists of chilled layer, columnar grain zone, transition zone and equiaxed grain zone

Jan 1, 2015

By Shengfan Zhou, XUEWEN WANG, Bianfang Chen, Mingyu Wang

Vanadium was leached from roasted stone coal by NaOH solution, and the effect of leaching temperature, leaching time, addition of NaOH, liquid to solid ratio, the grinding fineness of stone coal, and stirring speed on the vanadium leaching rate was studied. The kinetics analysis for the process is presented by the shrinking core model. The results show that the vanadium leaching ratio of roasted stone coal can be beyond 75% at the 6% NaOH addition, leaching temperature of 95°C, leaching time of 7h, liquid to solid ratio of 1.2mL/g, and grinding fineness of 0.111mm. The leaching process is controlled by interfacial reaction kinetics and the apparent activation energy was 59.36kJ/mol.

Jan 1, 2016

By Edmundo Manilla, Merete Tangstad, Daniel Davila, Eli Ringdalen

FeMn alloys are typically produced with lumpy ore or sinters. Minara Autlan, the Mexican FeMn producer, is however making Mn-nodules as a raw material for Mn-alloy production. The Mn nodules have been characterized by XRF, XRD, by wet chemical methods and by EPMA. The Mn/Fe ratio is somewhat lower compared to commercial Mn ore on the marked. The basicity of the ore is however close to 1, and additional fluxes may not be used. The Mn-nodules will be in a state of manganosite (MnO), tephroite ((Mn, Ca)2SiO4) and galaxite ((Mn,Mg)Al2O4). This leads to a low melting temperature area. A low porosity and low amount of higher Mn-oxides gives a high thermal strength to the nodules.

Jan 1, 2016

By Xiaolong Lin, Yuanbo Zhang, Guanghui Li, Zhizhong Li, Zhiwei Peng, Tao Jiang, Yan Zhang, Yutian Ma

Pyrometallurgical processes for recovering platinum group metals (PGMs) from spent catalyst have been the focus of current research for many years. They suffer from high energy consumption, large trapping agent consumption and huge slag production. Because of versatility of PGMs-containing spent catalysts, comprehensive recovery of valuable metals from these catalysts from an experimental point of view remains a challenge. In this study, thermodynamic analysis of pyrometallurgical smelting process in the presence of various additives for ef ficient recovery of PGMs was performed. It showed that addition of sodium salts would promote the migration and separation of the precious metals from carrier of the spent catalyst. By replacing calcium oxide with sodium carbonate and sodium borate, the smelting temperature could be reduced by more than 200 °C, which agreed well with the experimental findings.

Mar 1, 2018

By Rollie E. Dutton, David A. Stubbs

"A sensor has been developed and tested that is capable of emitting and receiving ultrasonic energy at temperatures exceeding 900°C and pressures above 150 MPa. The sensor works with standard ultrasonic pulser-receivers and has demonstrated the capability of measuring workpiece deformation during hot isostatic pressing (HIP). Details of the sensor design, performance, and coupling of the ultrasound to the workpiece are described. Ultrasonic data acquired by the sensor, in situ, during HIP runs and at elevated temperatures in air are presented.INTRODUCTIONHigh temperature structural components, such as structural castings for jet engines, nickel-base superalloy turbine blades, and ceramic and metal matrix composites made from powders are often densified by hot isostatic pressing (HIP). For powder consolidification, the HIP process involves sealing the powder (and reinforcing fibers for composites) within an evacuated ""Can"" made of a material that softens at high temperatures. A hydrostatic pressure is then applied by pressurizing the inside of the HIP vessel with argon gas (up to 140 MPa). The hydrostatic pressure densities the powder through the elimination of the porosity between the powder particles.This paper presents details of the development and preliminary testing of an ultrasonic displacement sensor that can be used to monitor materials processing, in situ, at temperatures and pressures significantly higher than current ultrasonic displacement sensors. The target processing environment for this sensor is that typically found in a hot isostatic pressure (HIP) vessel, i.e., temperatures exceeding 1000°C and pressures above 138 MP a."

Jan 1, 1997

By Xiaobing Yang, Animesh Jha, Greg Doughty

"Successful use of inert anodes should reduce the CO2 footprint in aluminum production. The search for a “holy grail” inert anode for metal electro-winning from constituent oxides using molten salt bath as an electrolytic medium is continuing. In this article we demonstrate the engineering approaches for the fabrication of intermetallic anodes, based on a quaternary Al-Ti-Cu-M (M:Ni, Fe) system for primary aluminium production. In particular, we examine the microstructural and electrochemical properties of alloys, based on the quaternary compositions. We explain the aspects of phase stability under anodic potential, which leads to the loss of anodic materials in the temperature range of 850-1050oC. The results are analysed in the context of oxidation reaction and formation of oxide layers which readily dissolve in the cryolite melt and prevent passivation. The paper also describes the conditions under which the reduction of aluminium at the graphite cathode occurs which also strongly depends on the molten salt chemistry for the nucleation of molten aluminium at the cathode.1. IntroductionOxygen-evolving inert anodes are an alternative to the conventional consumable carbon anodes for the production of primary aluminium. In this paper the materials selection criteria chosen for the engineering of anode is based on the understanding of the thermodynamic stabilities of aluminide intermetallic phases, some of which are formed and remained stable in fluoride melts. For example, the formation Al3Ti dispersed in aluminium metal via molten-fluoride flux reaction is well known in the context of aluminium casting and grain refining [1-3]. It is for this reason in our research we concentrated on the engineering of stable intermetallic phase mixture in the Al-Ti-Cu ternary system, shown in Figure 1 [4]. In this figure two compositions in the Al3-0.5zTi1-0.5zCuz family are shown with the substitution of 7 atomic % and 11 atomic % copper. However initial investigations showed that these two compositions were unsuitable due to the formation of low-temperature liquid (~540oC) and intermetallic phase, Al2Cu along the Al-Cu binary edge during solidification. The Al2Cu phase segregated along the boundaries of Al3Ti and Al5Ti2Cu, and dissolved away when electrolysis was carried out using these anodes above 800oC. The presence of consequential porosity in the anode material increased the corrosion of the alloy through local heating due to high current density at 0.8 A cm-2. The early tests were carried out with cryolite melts, shown in Figure 2, having 3 weight percent of Al2O3 in the bath at 850oC."

Jan 1, 2010

By Ying Wang, Min Chen, Cuihuan Huang, Haohua Deng, Nan Wang, Ming Chen

Adding limestone directly into converter is considered to be favorable to energy conservation and emission reduction by transferring the decomposition reaction of limestone from the shaft or rotary kiln to the converter. In this paper, the kinetics of limestone decomposing in early converter slag was studied at 1300–1400 °C, and the effects of slag temperature and stirring speed introduced to the slag bath were examined. The kinetic results based on shrinking core model analysis showed that the limestone decomposition was a mixed rate control of chemical reaction and heat conduction through the lime layer, which could be promoted at higher slag temperature by supplying more heat to the converter bath. In addition, the chemical reaction rate constant and effective thermal conductivity were determined.

Mar 1, 2018

By Jinliang Zhang, Jian Pan, Deqing Zhu

"Limestone and burnt magnesite were added to vary MgO content and basicity (CaO/SiO2 ratio) of pellets for investigating their influences on the properties of specularite pellets. At fixed MgO content, the addition of limestone does not affect on the properties of green balls significantly. The addition of burnt magnesite has obvious influence on the quality of green balls, especially on the thermal shock temperature. Without burnt magnesite, the thermal shock temperatures are about 400°C, and, the thermal shock temperature increases to 600~630°C by adding burnt magnesite. For preheated pellets, when the burnt magnesite is added, the compressive strength will be decreased. For roasted pellets without burnt magnesite, the calcium additives can form binding phase of calcium-ferrite, and suitable liquid phase will improve recrystallization of hematite, but excessive liquid will destroy the structure of pellets, so the compressive strength of pellet increases firstly and then decreases. When adding burnt magnesite, the compressive strength will increase as the basicity increases. When the basicity is more than 0.2, the compressive strength of the pellets various MgO content and basicity is above 2500N/pellet and then MgO-bearing fluxes can be added to prepare pellets with good high temperature properties.IntroductionWith the rapid development of the steel industry in China, oxidized pellets, possessing good mechanical and metallurgical properties, are becoming indispensable burdens for blast furnace ironmaking [1-3]. However, this has resulted in the shortage of domestic iron concentrates, so many Chinese steel plants begin to use imported hematite concentrate to prepare pellets. Compared with magnetite pellets, the hematite pellets require high roasting temperature and narrow roasting temperature range (1300–1350°C) and possess low compressive strength [4,5].1"

Jan 1, 2012

By Rak-lun Choi

Plasma-induced damage of InGaN/GaN multiple quantum well (MQW) light-emitting diodes (LEDs) has been studied in terms of forward turn-on and reverse breakdown voltages, together with etch rate and surface morphology. The physical degradation of sidewall along with rough surface morphology of n-GaN caused by increased ion scattering induced the deterioration of the forward and reverse voltages. It was found that the turn-on voltage is sensitive to the surface roughness of the etched n-GaN and the breakdown voltage is strongly affected by the sidewall contamination. Annealing under nitrogen after the mesa etching improved the electrical properties of the InGaN/GaN MQW LEDs. Efficient blue light-emitting diodes (LEDs) were fabricated using InGaN/GaN triangular MQWs. The LEDs with triangular QWs showed a lower operation voltage and 2.4 times higher light output power than those with the rectangular MQW LEDs at 20 mA and 20 °C. The intensity of electroluminescence (EL) at 20 mA was almost independent of ambient temperature in the triangular QW LED, but decreased substantially in the rectangular one.

Jan 1, 2003

By Wen Liangying, Zou Chong, Tan Xiuqin, Bai Chenguang, Zhang Shengfu

"Eight typical metallurgical byproducts containing iron were selected based on the effect of the chemical composition, particle size, additives on the burnout degree of pulverized coal. Effect of three typical byproducts including fine iron ore, BOF dust and BOF sludge on combustion reactivity and combustion efficiency were investigated using TG-DSC method. The results indicated that the three additives have obvious catalytic effects on pulverized coal. By comparison, the relative active sequence of byproducts to the catalytic combustion can be described as follows: BOF dust>BOF sludge>fine iron ore. Moreover, adding BOF dust as component of additives also shows significant catalytic effects on combustion efficiency during rapid heating process.IntroductionChina is the largest producer in the world with an annual output reaching over 6 billion tons. Solid wastes arising from iron and steel making increases the environment pressure in recently years. For instance, annual output of dust during the production of iron and steel making in China reach up to 5 million tons, which is close to 8%~15% of the amount of steel [1]. Another characteristic of these byproducts is they are finer particle which are just harder to deal with. Since some of solid wastes, including dusts, scales, and sludge, usually contain high iron content, sintering plants have traditionally been used to recycle byproducts in integrated steel plants in China. However these byproducts also have noticeable effects on sinter quality, sinter strength and productivity and, therefore, waste recycling is limited depending on the analysis of the waste materials [2]. Another method which is pre-treatment of byproducts in pelletizing process, increases of energy consumption and production cost. In addition, metallurgical byproducts often contain heavy metals and alkalis. For these reasons, recycling rate of the byproducts in China is very low. Therefore, how to recycle the byproducts in iron and steel making process is an important subject."

Jan 1, 2012