By T. A. George, David J. Sellmyer

"The concept of achieving a useful high-energy-product magnet through appropriate nanostructuring of known hard and soft phases has been tantalizing researchers since the idea was first proposed. The fabrication of exchange-coupled nanocomposite magnets faces several challenges including aligning the easy anisotropy axes of the hard-phase grains. Here we investigate experimentally two-phase nanostructures of hard Lio-ordered FePt and soft iron-rich/cc Fe(Pt). The Fe-Pt thin films were produced by epitaxial cosputtering onto MgO (001) single-crystal substrates which lead to strong (001) texturing. The measured hysteresis loops indicate nearly ideal exchange coupling. Excellent magnetic properties are obtained, with largest values of coercivity (51 kOe), saturation magnetization (1287 emu/ cm3, J, = 16.2 kG), and nominal maximum energy product (58 MGOe).1. IntroductionA key figure of merit for permanent magnets is the maximum energy product (BH)rrw.x. The achievable maximum energy product is determined by a magnet's saturation magnetization M, and its magnetic anisotropy. For example, it is well known that (BH)rrw.x :S 4n2M,2• In the past, record energy products have been the result of discovering new compounds with high values of magnetization and anisotropy. However, finding new compounds with better magnetic properties than the current record-holding magnet Nd2Fe14B has proven to be difficult. A different approach is to exploit the exchange coupling mechanism between known hard and soft magnetic phases to enhance the maximum energy product [1-5]. In such a composite system, high coercivity is achieved due to the anisotropy of the hard phase as well as a nanostructure which prohibits large-scale domain wall reversal mechanisms. Magnetization is enhanced by the soft phase and loop squareness results from texturing of the hard phase easy-axis as well as complete exchange coupling between the coexisting hard and soft grains."

Jan 1, 2012

By J. B. Vander Sande, I. G. Solórzano, B. S. You, P. M. Jardim, W. W. Park

"Alloys with six different compositions in the system Mg-Ca-Zn were produced by melt spinning. The aging behavior of alloys was investigated by measuring the changes in microhardness after isochronal aging and the microstructure was analyzed by means of transmission electron microscopy (TEM), energy dispersive X-ray spectrometry (EDS), scanning transmission electron microscopy (STEM) and scanning electron microscopy (SEM). All six compositions in the as-solidified condition show a difference in microstructure between the wheel contact side (zone A) and the free surface side (zone B) as a result of the differences in the solidification rate across the ribbons. One of the alloys (Mg-l.5wt%Ca-6wt%Zn) was chosen to be more deeply investigated in this work as it exhibited grain boundary films and an age hardening behavior was produced in that alloy.IntroductionMagnesium is the lightest of all the commonly used metals, and very attractive for applications in transportation. It also has a number of other desirable features, including good ductility, better damping characteristics than aluminum, and excellent castability. However, there are some negative features, such as high reactivity in the molten state, inferior fatigue and creep resistance as compared to aluminum, poor corrosion resistance and high production cost.In recent years there has been a significant increase in magnesium use as a structural material. These structural applications include aerospace, automotive and nuclear industries as well as appliances and sporting goods (1 ). According to reports on Mg-Zn alloys, the addition of Zn (2) in magnesium increased strength. Also, since the maximum solubility of Zn in magnesium is 6.2wt%, a considerable amount of Zn can be retained in solid solution in magnesium alloys by rapid solidification. In addition, Ca is known (3) to be one of the most potent alloying elements for refining the microstructure and precipitates in magnesium alloys, and also to improve mechanical strength and corrosion resistance."

Jan 1, 2000

By Ozgul Dere Ozdemir, Muge Sari Yilmaz, Sabriye Piskin, Deren Sibel Kasap

"Galvanic sludge is generated at the end of the waste water treatment process of metal plating system. The waste sludge is one of the main hazardous solid wastes produced by metallurgical industries. It is caused the harm of human health and damage of the environment due to containing reasonable amounts of toxic metals (e.g., nickel, zinc, copper, chromium, iron, lead, cadmium, etc). The concentration of those toxic metals in the wastewater might reach 30% (w/w, dry weight) making their removal and recovery an interesting issue.In this study, synthesized titanium dioxide is used as adsorbent to remove nickel in leachate of galvanic sludge. The adsorption experiments were carried out isothermally at four different temperatures. The effects of pH, temperature, and contact time on nickel adsorption efficiency were investigated, and the optimum parameters were determined from the experimental studies. The experimental results indicated that pH, temperature, and contact time played a significant role on the adsorption capacity of nickel.IntroductionRapid industrialization has caused increasing the heavy metal concentration in biosphere with the industrial wastes. These wastes are generated in various industrial processes such as electroplating. Galvanic sludge is a hazardous waste that generates from metal plating industry by chemical precipitation of heavy metals from acidic or alkaline solutions during the waste water treatment process. Heavy metals are tend to bioaccumulate thus they are treated the living organism [1-2].Galvanic sludge is mainly disposed on landfills for these reason it is a big problem for environment. Galvanic sludge containing nickel (II) is common because nickel (II) is used in electroplating process [3]. In drinking water, nickel may cause health problems if found in amounts greater than the health standard set (MCLG: 0.1 mg/L) by the United States Environmental Protection Agency (EPA). The higher concentration of nickel (II) in ingested water may cause severe damage to lungs, kidneys, gastrointestinal distress, e.g., nausea, vomiting, diarrhea, pulmonary fibrosis, renal edema, and skin dermatitis [ 4]. For these reasons, it must be treated before disposed to landfill."

Jan 1, 2011

By C. A. Nogueira, F. Pedrosa, F. Margarido, R. N. G. Guerra

"A hydrometallurgical process for recycling spent Zn-MnO2 batteries was developed, involving leaching with sulfuric acid, purification by precipitation and metals separation for further recovery. Leaching of zinc oxide was easily attained while for manganese oxide was rather difficult depending on temperature and acid concentration. At 90°C and with the liquid/solid ratio of 20 L/kg, more than 95% of zinc is recovered in 30 minutes with 0.5M H2SO4. To attain similar recovery for manganese, higher levels of acid concentration and time are needed (e.g 0.7 M and 2 hours). After leaching a purification step is necessary to remove iron co-dissolved through Fe(III) precipitation. Separation of zinc from manganese by solvent extraction with 1M DEHPA follows in the process route. The countercurrent multistage separation diagram developed allows the production of a zinc electrolyte with 120 g/L Zn and 0.005 g/L Mn, and a raffinate with 16 g/L Mn and 0.013 g/L Zn.IntroductionThe recycling of spent Zn-MnO2 batteries is carried out by dedicated recyclers using several process alternatives [1]. Most of the running processes use pyrometallurgical technologies [2] based on zinc distillation. Alternative treatments by hydrometallurgy have been reported [3-5] but its application is scarce.In order to contribute to the development of alternative solutions, a process for recycling batteries based on Zn-MnO2 systems has been studied. The process is based on the hydrometallurgical treatment of spent batteries in sulfuric acid media (Figure 1). The process starts with the physical processing by shredding using cutting grinders, where the batteries are opened and size reduced, allowing the liberation of the interior electrode particles or pastes. The fines can be then separated and the coarse material containing the steel scrap can be treated to remove the remaining aggregate electrode. The final scrap also contains some plastics and other non-metal materials and can be further valorized."

Jan 1, 2008

By Gjergj Dodbiba, Toyohisa Fujita, Takahiro Kikuchi, I-Chen Wu

"In order to separate molybdenum (Mo) from the high-level radioactive liquid waste (HLLW), Pb-Fe based adsorbents were synthesized. The adsorbents were precipitated by adding sodium hydroxide in mixture of 1 mol/L lead nitrate and 1 mol/L ferric nitrate aqueous solutions. Each precipitate was then filtered, dried and ground to obtain a fine powder, which has been used as an adsorbent. Two main parameters were considered when synthesizing the adsorbents, i.e. the pH value at precipitation of adsorbent precursor and the calcination temperature of Pb-Fe based adsorbent. Moreover, the structures of the synthesized adsorbents were investigated by means of an X-ray diffractometer.The experimental results indicated that the calcination temperature of the Pb-Fe based adsorbent has a great influence on adsorption capacity of the adsorbent for Mo. It was found that when the Pb-Fe based adsorbent was calcinated at 500 oC, the sorbed concentration of Mo was the highest.1. IntroductionThe high-level radioactive liquid waste (HLLW), arising from the reprocessing of nuclear fuel are generally immobilized in an alkali borosilicate glass matrix. Broadly speaking, alkali borosilicate glasses are the matrix of choice for the immobilization of the HLLW, since they permit vitrification of waste stream of variable composition, [1]. Within this frame, the incorporation of molybdenum (Mo) is of particular interest in the vitrification of HLLW. Molybdenum is know to have a low solubility in borosilicate glass compositions and its presence in excess results in the phase separation of a complex yellow molten salt during vitrification, [1]. The formation of so-called “yellow phase” material during the vitrification process is undesirable since it leads to the accelerated corrosion of the inconel crucible liners. Furthermore, the “yellow phase”, which is reported to contain also other fission products, is soluble in aqueous solution providing a potential route for the leaching of radionuclides from the vitrified waste, should it come into contact with water, [1]."

Jan 1, 2008

By Bora Derin, Adnan Aydin, Onuralp Yucel, Hakan Morcali

"The steelmaking industry which uses electric arc furnaces (EAF) generates approximately 250.000 tons of EAF flue dusts annually in Turkey. These flue dusts contain valuable metals such as zinc, iron and lead. For example, if these flue dusts can be treated efficiently, disposal problems certainly decreases and annually almost 40.000-75.000 tons of zinc can be recovered. In this study, powder and pellet forms of EAF flue dusts taken from a steel mill were carbothermally treated in a temperature controlled pilot scale rotary furnace via carbothermal reduction in order to investigate the reduction behavior of Zn and Pb. Temperature (900-1000 and 1100 °C) and time (0-90 minutes) were selected as reaction parameters. The chemical analysis was performed for the sample residues.IntroductionTurkey’s steel production reached to 23.3 million tons in 2006. There are three integrated steel plants of which capacities vary from 0.7 to 3 million tons per year and seventeen EAF steel plants of which capacities vary from 0.06 to 2 million tons per year [1]. When it is considered that more than 74 % of the Turkish steel production is produced by EAF method and approximately 10 - 15 kg of dust is formed per ton of steel during this process, the amount of annual generated EAF dust may be estimated at approximately 0.25 million tons. EAF dust which contains valuable metals such as zinc, lead, iron, cadmium, and chromium, is considered as hazardous waste product in steelmaking industry. If these flue dusts can be treated efficiently, not only the disposal problems certainly decrease, but also annually almost 40.000-75.000 tons of zinc can be recovered. Many studies which exist on recovering of the valuable metals from EAF dust, propose and practice many hydro-metallurgical and pyro-metallurgical treatments [2- 7]. In this study a laboratory scale work were performed to investigate reduction behavior of zinc and lead in EAF dust by carbothermal process in a rotary furnace."

Jan 1, 2008

By Wander. L. Vasconcelos, Virgínia. S. T. Ciminelli, Angela. M. F. Guimarães

"The present work was aimed at synthesizing nanostructured hybrid materials derived from the functionalization of smectite clays with ligands containing thiol (-SH) groups for application in cadmium adsorption processes. An in nature Brazilian bentonite was investigated. The modification route was based on the grafting reaction between hydroxyl groups present on clay surface and the hydrolyzable alkoxy group of the (3-mercaptopropyl)trimethoxysilane in dry toluene under reflux. The present work showed that the proposed modification route was effective for the grafting of the thiol groups in the clay structure. The thiol-functionalized bentonite samples showed average binding capacities 160% higher with respect to Cd2+ to those obtained with the ungrafted material. These results support a mechanism of adsorption involving primarily ion complexation by the thiol groups (specific) instead of cation exchange (unspecific). The proposed modification processes are suggested for the preparation of novel adsorbent materials with controlled selectivity and specificity and therefore with good potential for separation and pre-concentration purposes.IntroductionMany efforts have recently been devoted to the design and preparation of inorganic-organic nanomaterials because of their potential application in novel functional materials. The intercalation of organic species within the spaces between interlayers of inorganic layered crystals provides nanostructures consisting of alternating layers of inorganic and organic compound. The intercalation reactions occur by insertion of mobile guest species (neutral, molecules, or ions) into the accessible crystallographic-defined vacant sites located between the layers (interlayer spacing) of the layered host structure [1}.Silane coupling agents, used widely for the modification of silica surfaces, have also been employed more recently for modification of layered silicates [2,3,4,5]. Modification with organosilane involves grafting reactions by establishing covalent bonds between the reactive groups of the layer, normally hydroxyl groups, and silane molecules. These reactions can be restricted to the external surface (the basal spacing remains unchanged) or to the interlayer surface, in which case an interlayer expansion occurs. The resulting material can be defined as a hybrid material or, more specifically, functionalized inorganic layered material [1]."

Jan 1, 2008

By Ludy C. Motta, Denise C. O. Nascimento, Sergio N. Monteiro

"Natural cellulose-based fibers are nowadays of growing interest for modern industrial composites. Relatively unknown fibers like piassava, curaua and gourde have shown promising behavior as reinforcement of polymeric composites. However, the hydrophilic characteristics of the natural fibers impair its adhesion to the normally hydrophobic polymeric matrix. Surface treatments can, in principle, improve this adhesion and the fiber/matrix interfacial strength. In this paper, the effect of alkali treatment of the surface of piassava (Atallea funifera) waste fibers was investigated in terms of the change in strength of epoxy composites reinforced with these waste fibers.IntroductionThe consequences of global warming and the increase in the price of petroleum are motivating the use of natural materials as substitute for energy intensive synthetic materials [1]. In particular, natural fibers obtained both, from cultivated plants such as jute, sisal, hemp and flax as well as from industrial waste such as sugar come bagasse and coir, are being considered to replace synthetic glass fibers [2,3]. These natural fibers, also known as lignocellulosic fibers, present the comparative advantages of being renewable, recyclable and biodegradable. Moreover, lignocellulosic fibers require less amount of processing energy and are neutral with respect to CO2 emission, which causes the atmospheric greenhouse effect responsible for the global warming [4]. Low cost is another important economical advantage of the natural fibers over the synthetic ones and the application of lignocellulosic is also associated with a lower wear of processing equipment and better finishing of molded components [5]. Moreover, for some fibers, properties such as the mechanical strength and impact resistance can be superiors to the corresponding properties of synthetic glass fiber [6]. The characteristics and properties of several lignocellulosic fibers are, nowadays being extensively discussed in the literature. It is beyond the scope of this work to comment on the hundreds of papers dealing with this subject. However, there are still less known fibers with great potential as engineering material that deserves investigation."

Jan 1, 2008

By Felipe P. D. Lopes, Jr. dos Santos, Sergio N. Monteiro, Frederico M. Margem

"Natural fibers are gaining attention as a class of low cost, biodegradable and renewable materials that also exhibit some interesting properties for specific applications. In particular, the incorporation of some natural fibers in polymeric matrix composites is nowadays providing opportunity of manufacturing a variety of industrial items, for instance automobile interior components. Among these fibers, ramie (Boehmeria nivea) is one of the least investigated and only recently was studied as polymeric composite reinforcement. Therefore, the objective of this work was to evaluate the possibility of ramie waste reinforced polyester composites to replace conventional building materials, such as plywood, plastic boards and gypsum panels in terms of a cost-benefit analysis.IntroductionThere is a growing concern over the environmental questions that are presently affecting our society in a global sale such as climate changes and generalized pollution. Among the solutions for these questions, the replacement of energy intensive materials, especially those long term degradable such as the synthetic fibers, is already being considered [1]. As a consequence, the past decades have witnessed an increase in research devoted to new biodegradable materials obtained from natural resources mainly the biomass. Important examples are the renewable natural fibers as well as composites incorporated with them [2,3]. In addition to their friendly status with respect to the environment, well know natural fibers like jute, sisal, wood, coir, hemp and flax are relatively low cost and recyclable. In recent works [4,5], the use of these cultivated and abundant lignocellulosic fibers was investigated as the reinforcement phase in polymeric composites.Other less know lignocellulosic fibers have also been recently investigated [6,7]. These are fibers that likewise show a potential of incorporation into the polymeric matrix of composite materials. Most of these less know fibers are typical of tropical regions and, in principle, their application in industrialized composites would represent job opportunities for developing countries in Africa, South Asia and Latin America."

Jan 1, 2008

By P. Balachandran

The paper outlines the existing facilities and working practices at the Khetri electro-refinery of Hindustan Copper Limited. Plans have been drawn up to mechanize some key operations to improve the quality of cathodes and the working environment as well as economize the refinery operations. The economic analysis for determining various optimum operational parameters under conditions existing in India have also been outlined. The impact of capacity utilization and mechanization under different sets of conditions on operational costs have been highlighted.

Jan 1, 1987

By W. L. Cornell

The processing of lead tailings for removal of the heavy metals produces concentrates upgraded in Co and Ni values. Reflected light microscopy, scanning electron microscopy, image analysis, and Vickers hardness measurements were used to identify mineral species, associations, degree of liberation, and distributions to the test products. Siegenite and bravoite were the most common species encountered, but violarite and enriched pyrite and marcasite phases were also identified. Liberation for the Co and Ni minerals contained in the tailings was 20 micrometers or less.

Jan 1, 1993

By Kurt Westerlund

Cooling of hot sticky gases with solids in a circulating fluidized bed called FLUXFLOW is described. Fluxflow is used for gas streams from metallurgical reactors, e.g., Isasmelt copper in Australia and TBRC for lead in Sweden. The features and potential of this technology in metallurgy and waste treatment ie described. The FluxfLow la a new, cost efficient high availability solution to treat hot sticky gases that has made new gas handling and heat recovery flow sheets available to the process industry.

Jan 1, 1994

By M. L. Free

Electrowinning is directly impacted by many parameters that include electrolyte composition, voltage, current density, contact resistance, temperature, electrode spacing, and fluid flow as well as many other interrelated factors. The effects of these parameters are primarily related to thermodynamics, mass transport, and electrochemical kinetics. In this study thermodynamic, mass transport, and electrochemical kinetic equations are simultaneously solved to determine the effects of such parameters on electrowinning current efficiency, power consumption, electrodeposit morphology, and electrodeposit distribution. Modeling predictions will be compared with experimental results.

Jan 1, 2006

By Pragna Bhakta

Newmont has investigated potential treatment options for low-grade refractory gold ores since 1988. After extensive R&D at Newmont?s laboratories, biooxidation pretreatment followed by ammonium thiosulfate leaching was selected for application to sulfidic preg robbing ores. A heap biooxidation and ammonium thiosulfate leaching demonstration facility was constructed in 1995 to conduct large-scale pilot tests at Newmont?s Carlin Operations. This paper presents Newmont?s experience with the recovery of gold from preg robbing ores using ammonium thiosulfate.

Jan 1, 2003

By Marcela Morvová, Mário Janda, Morva Imrich

"The possibilities of greenhouse gas mitigation using various methods are brought out. The special case of utilization of mixture of CO2 with other greenhouse gases in a synergetic way inside non-thermal plasma based system is described in detail.Measurements on pilot system comprising pyrolysis chamber as alternative energy system (production of hydrogen and liquid tar) were made for various biomass and waste as the input material. The exhaust from this system was treated with non-thermal plasma gap suitable for up to 650Nm3/hour of exhaust gas flow. Condensable portion of exhaust is liquefied in distillation unit; produced hydrogen is stored on-line inside nano sized carbon of our own production.The CO2 removal efficiency varies depending on exhaust composition between 45 to 98%. Other oxides as CO, NOx, SOx and several hydrocarbons and VOC are also removed. The main product connected with CO2 removal is a solid powder of proteinoid nature. There exist strong probability, that precursor of the origin of life on the Earth from primary atmosphere were formed in the similar way as it is present in the electric discharge system used. Our system is equipped with on-line as well as ex-post analysis of all forms of products. We have also developed a system for recuperation of all forms of produced heat. It is stored inside as latent heat of waxes.IntroductionNatural greenhouse effect on the Earth is caused mainly by water vapour with the average absolute concentration about 4%. Other gases able to absorb long-wave radiation and thus this causing greenhouse effect are CO2, CH4, N2O, halocarbons and as precursors ozone and NOX. Some of them we produce and introduce into atmosphere in large quantities during production of energy and in transport. This factor leads to permanent increase of average temperature of air, sea and oceans, so called global warming.Nowadays large amount of data exists showing that the temperature of Earth in the last 150 years has been continually increasing. It represents about 03°C per ten years and the most of climatologist believe, that the increased concentration of greenhouse gases in the atmosphere is responsible for this effect.The most important greenhouse gas is carbon dioxide CO2. Majority of CO2 emissions comes from electric power stations working with fossil fuels, cars and industry. Burning of fossil fuels contribute up to 80% to world wide anthropogenetic emissions of CO2."

Jan 1, 2010

By L. M. Bianchi

"Oxide, nitride and other compound coatings often do not have adequate properties for newer applications when produced using very high deposition rates and simple evaporation techniques. Solar control, abrasion resistance, low reflectance and barrier effective engineered coatings require exacting properties. Such properties can be obtained by adapting the activated reactive evaporation (ARE) technology to Web production processes. Adaptions of the HAD and MAD processes will be described along with data on the high deposition rates obtained. These fast production capabilities were developed in order to make the processes economically competitive.IntroductionThe Physical Vapor Deposition technique (PVD) has been used to coat steel strip for over 20 years. (1) However, its use as a production process has been very limited because of the high cost of the PVD coating process and because, in some instances, the properties of the coating were not good enough to meet the customers requirements. Nevertheless, the PVD process has found wide application in the airplane engine and electronic component markets. These production processes have stimulated further development and advances in the technology.In 1971, Profession R. F. Bunshah developed the Activated Reactive Evaporation (ARE) process which was then used to produce hard coatings such as carbides, nitrides, oxides and other refractory compounds. (2) The process from a fundamental viewpoint -produces a coating on the substrate via the evaporation of metal in the presence of a low pressure (typically around 1 millitorr) of reactive gas, with a plasma created in the space between the metal source and the substrate.The plasma may be created by many means but its function is two-fold. First, it activates the reaction between the metal vapors and the reactive gas atoms/molecules resulting in the formation of a compound that deposits on the substrate. Second, because the plasma is in contact with the substrate, it results in a negative bias on the substrate and produces bombardment of the growing film with ions and energetic neutrals from the plasma. This bombardment causes many significant changes in the microstructure, properties and appearance of the coating.Recently another new technology Pulsed Magnetron Systems (PMS) has been introduced into PVD. This new technology has been pioneered in production scale equipment by Dr. S. Schiller (3) and associates. The use of a pulsed power supply on the magnetron prevents the problem of the anode being coated with a insulating layer which will then lead to micro and macro arcing producing defects in the coating."

Jan 1, 1998

By Hongmin Zhu, Suning Liu, Kai Huang

"Recovery of silicon particles from the cutting slurry for the manufacturing of solar grade silicon is very important to recycle this kind of special resource. The challenge is to separate the silicon particles from the mixed abrasive particles which contain SiC. Various methods such as sedimentation, centrifugation, and flotation have been conducted, while in present work, a simple and effective novel method was proposed to study the separation of Si and coexisting SiC particles in the cutting slurry. The new process is based on the size difference between the two kinds of microparticles. And the membranes with the different pore sizes of 1µm, 2µm, 3µm and 5µm were used to test the pass ratio and separation efficiency of the suspension. Results shows that the effective separation of Si and SiC microparticles was obtained under the optimal conditions, and indicating great potential of practical enrichment of Si from the coexisting abrasive particles.IntroductionWith the development of the world economy, energy shortage and environment problem is becoming more and more seriously. Solar energy, which is regarded as one of the most important new energy in the word, has received much attention and interest from the scientists [1, 2]. More than 80% solar cells are manufactured by the high purity polysilicon as the raw material. The main process of producing silicon wafer is by multi-wire slicing. In this slice processing, large amount of slurry is produced. The slurry contains more than 30% wt silicon powder, silicon carbide powder as the abrasive, scraps of metal chips, as well as cutting abrasive suspension polyethylene glycol (PEG). The high-purified silicon powders are worth recycling and reusing as the materials for preparing solar-grade silicon though it is a big challenge [3].Most of the current studies were focusing on the recycling of the silicon carbide and PEG, while work on the recycling of the high-purified silicon is not so been focused since there is lacking of very effective separation and recovery technologies till up now. Nishijima utilized the method of superconducting magnetic to recycle the abrasive [4]. Wang applied a combinational process of chemical treatment, high-gravity centrifugation, high-temperature precipitation technique and directional solidification to enrich the silicon [5]. And other purification methods, such as centrifugation [6], froth flotation technologies [7], electrical filed separation [8] and phase-transfer process [9] have been employed. The disadvantages such as using poisonous media or complex equipments decrease the feasibility and efficiency of the above mentioned techniques."

Jan 1, 2014

By Jinqian Zhao, Jiarong Li, Shizhong Liu

"Creep cavitation of in single crystal (SX) superalloy was investigated. The constant load creep tests, in single crystal superalloys DD6, were conducted at the conditions of 800°C/700MPa, 850°C/550MPa and 900°C/450MPa, respectively. It was found that there were square facets on the stress fracture surface, and microscopic cavities in the ruptured specimens in the vicinity of the fracture surface. Both the square facets on the fracture surface and microscopic cavities in the section of the ruptured specimens show the morphology of the same thing at the different views, namely creep cavities, which are take the form of flatten cuboid. In fact, creep cavities are the longitudinally tensiled creep cracks slowly growing during the stress tensiling. The factors of creep cracks nucleation and growth conditions include: (a) enough high temperature to activate diffusion (b) casting pores as nucleation origination (c) high strains and strain rates. Eventually, the instantaneous fracture mechanism of creep specimen is cleavage fracture.IntroductionFor the materials used in elevated temperature service, creep behavior has to be accounted for. It is well recognized that creep rupture in polycrystalline materials at high temperature occurs principally by the nucleation and growth of microscopic cavities at grain boundaries, followed by microscopic cavities linkage to form micro- and eventually macro-intergranular cracks[l,2]. Without the usual grain boundaries, SX superalloys have superior capabilities at high temperatures to polycrystalline superalloys, and have become an established feature of gas turbine technology where they are commonly employed in the manufacture of high performance blades[3]. A considerable amount of work has been done over the past tens of years, and many models for nucleation and growth of creep cavities have been proposed, however, those are mainly for polycrystalline materials.In order to improve creep resistance that single crystal superalloys, in which grain boundaries are removed, have been developed. Because there don't exist grain boundaries in SX superalloy, the mechanism of nucleation and growth of creep cavities must be different from that in polycrystalline materials.Understanding the formation and characteristics of creep cavitation is crucial to model the lives of single crystal superalloys.M. Marchionni and L.G. Zhao et al. found that there were square facets on the stress fracture surface [4,5]. Roger C. Reed pointed out creep cavities lie in the necked region[6]. In this paper, the effects on the formation of creep cavities are discussed, as well as the morphology of creep cavities and fracture mechanism of SX superalloys."

Jan 1, 2013

By E. A. Chavarriaga, L. J. Jaramillo, O. J. Restrepo

"This paper presents the results of the manufacturing ceramic pigments with spinel structure, using methods of synthesis of low temperature. In this work we obtained spinel structures type by the methods of Self-combustion, Coprecipitation, Microemulsion, Gel citrate and Pechini. These methods become an attractive alternative to traditional method (ceramic method), since we can work at a lower temperature, reducing manufacturing costs, lower fuel consumption, less wear on equipment and other environmental and economic implications. Also it is possible to have control over features such as stoichiometry, morphology of the products, reaction times and structures. The products obtained by these routes will be used in the manufacture of ceramic pigments and characterized using different techniques such as X-ray diffraction (XRD), scanning electron microscopy (SEM) and UV-VIS spectrophotometry.IntroductionSpinels are ternary oxides AB204, where A and B are cations occupying tetrahedral and octahedral positions respectively. These oxides exhibit interesting electrical, magnetic and catalytic properties [1-4], depending on its nature, charging and intrinsic distribution of ions [5].The most widely used method to prepare spinels has been through solid state reaction, which consists of mixed oxides at high temperatures [6, 7]. In the last years, there have been a strong tendency to use chemical routes for the synthesis of crystalline ceramic particles at low temperatures [8,9]. Unconventional methods currently employed for the synthesis of complex oxides are Gel citrate method, Pechini, Spontaneous combustion, Microemulsion and Coprecipitation. Pechini method [10, 11], based on polymeric precursors, does not require high temperatures and allows stoichiometric control for greater reproducibility. This method involves the formation of a polymeric resin between a metal quelate and polyhydroxy acid of alcohol by polyestirification.Coprecipitation is important for many environmental problems related to water resources, including acid mine drainage, migration of radionuclides in waste repositories dirty, transport of contaminant metals in the industry, metal concentrations in aqueous systems and the technology of wastewater treatment. The coprecipitation process can vary in each case; the partition in the solid phase can be carried out by surface adsorption, ion exchange, surface precipitation, occlusion and formation of solid solution. The formation of solid solution is the result of structural incorporation of the marker in structural support sites resulting in a minor component in the solid solution with the host phase that has a very low solubility of pure solid [12]. Synthesis by gel citrate method allows the use of a route to obtain ceramic pigments from a very simple experimental system in which the stoichiometric control, the size and shape of the particles and the purity of the phases obtained can be controlled more accurately [13]."

Jan 1, 2012

Novel techniques were developed to obtain samples from and make measurements in the shaft of the flash furnace at the Kalgoorlie Nickel Smelter. The data obtained was used to validate mathematical models of the burners and the reaction shaft. Particle, gas and wall temperatures were measured along with the oxygen potential of the molten particles. Collected particles were characterised by sizing, chemical analysis and optical microscopy. The region of the shaft immediately beneath the burner where the rate of change was most rapid received special attention.

Jan 1, 1993