By B. W. Frazier

Jan 1, 1882

By W. Chubb

By measuring the hardness of metals at temperatures just above and just below their allotropic change point, it has been established that crystal structure has a real effect upon the strength of metals. The DPH of cobalt, iron, titanium, uranium, and zirconium have been measured at temperatures up to 1000°C. It was found that the body-centered-cubic crystal structure is always the softer structure when it is involved in an allotropic transformation. The close-packed and more complex structures are inherently harder, and may be expected, therefore, to be better base materials for high strength alloys. IT has been observed that for metals with nearly the same melting point (i.e., tin and lead, magnesium and aluminum) the metal with the more complex crystal structure has a higher tensile strength and hardness. It might be asked whether this effect is really caused by the difference in crystal structure; and, if so, just what is the contribution of crystal structure to the strength of these metals. A qualitative answer to these questions can be obtained by measuring the change in hardness produced by the change in structure in metals exhibiting allotropic forms. The evidence for changes in mechanical properties during allotropic transformations is rather meager. In 1909, Rosenhain and Humfrey' observed that "ß" iron showed much less deformation at the transformation temperature than a iron. By means of a torsion test, Lee found that iron bars were "critically plastic" at the a-7 transformation temperature. Sauerwald and Knehans have shown that the dynamic hardness of iron increases between 900" and 1000°C. In 1930, Albert Sauveur' presented data on the hardness, tensile strength, and torsional strength of pui-e iron up to 1000°C. He concluded, "At 900°C, the a iron transforms into y iron, and this is accompanied by increased strength and stiffness and decreased ductility." The same year, Schischokin" obtained data on the hardness of thallium at temperatures above and below its transformation temperature. His data are replotted on semilogarithmic coordinates as Fig. 1. The fact that his data fall on straight lines in this type of plot is believed to attest to the purity of his metal and the accuracy of his results. In 1941, Nadai and Manjoine" obtained tensile data on pure iron with an indicated increase in strength at about 900°C. These experiments make it quite evident that changes in mechanical properties occur when a metal transforms from one crystal structure to another; but, except for Schischokin's data on thallium, none of the measurements seem accurate enough to determine the relative magnitude of the mechanical property change. Materials The metals that have been examined for changes in hardness during transformation include l—as- deposited commercial electrolytic cobalt about 99.7 pct pure, 2—Armco ingot iron, 3—are-melted iodide titanium of a purity in excess of 99.8 pct, 4—uranium of a purity in excess of 99.5 pct, 5—are-melted iodide zirconium of a purity in excess of 99.8 pct, 6—annealed, 0.08 pct C, rimmed steel, and 7—commercially pure RC55 titanium. While the purity of the first five of these materials leaves something to be desired, it will be noted that the observed hardness discontinuities occurred at the accepted transformation temperatures. (These temperatures are indicated by vertical arrows in Figs. 1 and 3 through 7.) The last two materials are commercial alloys introduced to show the effect of minor alloying elements upon the hot hardness curve. Apparatus Hardnesses at elevated temperatures were determined by means of a vacuum hot hardness machine. A diagram showing the basic features of this machine appears as Fig. 2. This machine is essentially a deadweight hardness .machine in a furnace within a vacuum chamber. The sapphire-tipped indentor

Jan 1, 1956

By L. T. Leyson, U. C. Tainton

Some time ago, at ameeting of the Institute Prof. J. W. Richards1 said, "I take exception to the statement that all the factors in the production of electrolytic zinc were known long ago.... There is possible in my opinion an improvement of perhaps 50 per cent. in the new electrolytic processes." An examination of the literature of the subject will show the justness of Professor Richards' contention. The work of the earlier investigators was carried on in the shadow of difficulties that, today, are hardly more than memories. We seldom hear now of zinc sponge, that bête noir of the electrolytic-zinc pioneers. Zinc sponge was the name given to a peculiar, soft, black, non-adherent form of zinc deposit that was utterly useless for melting into ingot form. At the big plant at Cockle Creek, New South Wales, in 1897, Edgar Ashcroft2 said that the solution in the plant would suddenly, and without ascertainable cause, go' "bad" and begin to deposit spongy zinc. The most delicate, even spectroscopic, methods of analysis were unable to detect any difference between "good" solution and "bad" solution; either form might change to the other on being kept for a while. When it is added that an outbreak of this insidious disease (which appeared to be infectious, or at least contagious) could be dealt with only by discarding the solution and washing out all tanks and pipe lines, some idea may be gathered of the troubles of the zinc electrometallurgist in what may be spoken of as the "sponge age" of electrolytic zinc. Thanks to the efforts of a number of investigators, we are today able to diagnose with considerable certitude the nature of the malady that puzzled Ashcroft and his co-workers. The researches of Mylius and

Jan 1, 1924

By John V. Beall, John Cameron Fox

Organization In 1948, the Committee on Divisionalization and Publication Program of AIME, known as the Johnson Committee, recommended the reorganization of the Institute into three branches, Mining, Metals and Petroleum. This recommendation was accepted and the new organizational structure was implemented in Jan., 1949. The Mining Branch, at the time of the formation, had three divisions: the Coal Division formed in 1929, the Industrial Minerals Division (IndMD) dating from 1935, and the Minerals Beneficiation Division (MBD) formed in 1948 from the Milling Methods Committee, which had existed for many years. There did not exist, however, a division for the geologists and mining engineers. From the time of the founding of the Institute, this group was the main stem of AIME and never felt the need to segregate. The disciplines of mining and geology were served by a number of technical standing committees of AIME. With the birth of the new Branch, a new Division, the Mining, Geology and Geophysics Division (MGGD) was formed, completing the divisional structure of the Mining Branch and providing a home for all members. The governing body was the Mining Branch Council, with two members from each Division of the Mining Branch and one each from the Mineral Industry Education Division and the Mineral Economics Division. These last two divisions served all three Branches of AIME. The Division is such an important unit in the organization structure that it is of value to explain that it appoints committees to handle pro- grams, publications, and awards - representing the main functions of the Institute - as well as many others. There is enough flexibility in the organization so that each Division may have its own special committee structure as long as primary functions are provided. The past is indeed prologue to the future, for in 1957 the Johnson "Branches" gave way to the Fletcher "Societies." The Fletcher Committee, in 1958, recommended a new reorganization into Societies, each with the authority to administer its own finances and to designate certain officers and directors to the AIME Board. The date on which the Society of Mining Engineers was formed in Feb., 1957, has become known as "R" Day. A smooth transition from the loose Branch structure to Society organiza-

Jan 1, 1971

By R. E. Boehler, N. C. Ludwig

At Buffington Station, Gary, Ind., Universal Atlas Cement operates fourteen 8 x 10Y2 x 155-ft cement kilns in mill 6 and two 11 x 360-ft kilns in the Harbor plant. The No. 11 and 12 kilns in mill 6 are equipped with Manitowac recuperator sections. This report describes studies in measuring exterior shell temperatures on several of these kilns and the development of a traveling radiation pyrometer with certain novel features.

Jan 2, 1960

By R. G. Green, R. L. Dowdell

LEAD POISONING as a result of eating lead pellets deposited in marsh areas is a cause of high mortality among ducks, geese, and other waterfowl ingested lead shot become trapped in the gizzard with gravel and are slowly ground away by the grit. Absorption of lead as it passes through the intestine in a finely divided state produces severe lead poisoning which is usually fatal. Ducks and geese with lead poisoning develop first a typical green diarrhea. Later, paralysis of the wing muscles prevents flight. As the poisoning continues with further grinding of the shot trapped in the gizzard, increasing paralysis reduces the bird to helpless-

Jan 1, 1937

By F. R. Jones

T Tahawus, N. Y., National Lead Co. operates the MacIntyre development. Here the world's largest titanium mine produces 5200 long tons of ore per day and pours 8000 long tons of waste rock over its dumps. Concentrated ilmenite is sent by rail to National Lead Co. pigment plants, and a second product, magnetite, is sold to steel producers in raw form or is agglomerated and shipped as sinter. Several earlier attempts had been made to produce iron from the deposits, which have been known since 1826. These attempts failed, chiefly because of titanium impurity. In 1941 the present owners re-established the operation for production of war-scarce ilmenite, and the impurity became the main product.

May 1, 1956

By Arthur A. Center

WAR demand- motivated developments in the zinc industry during 1942. Stocks of Prime Western were built up and High-Grade remained tight. The Prince The Prime Western stocks are expected to be cut down and the demand for High-Grade more easily filled as the Depue reflux plant of the New Jersery Zinc Co. increases - production. Subistition of steel for brass in artillery shell cases will have a considerable effect on the zinc situation of the country one estimate of the saving in zinc in 1943 by this substitution being a little under 100,000 ton, of metal. The metal saved will, of course be High-Grade. If the substitution occurs, the present tight situation in High-Grade may be entirely relieved as new production comes on the market and zinc may find itself approaching a situation as comfortable as that of lead provided the supply of zinc-hearing raw materials is sufficient to keep all reduction plants tip to capacity production. The premium price of the per pound of zinc over set quotas which went into effect early in 1942, helped to bring about the new lead-slag-fuming plant and other new sources of raw materials.

Jan 1, 1943

By J. L. CAHUTHERS

MANY different methods are used for transporting coal from the working face to the tipple. The common methods are animal haulage, locomotive haulage, conveyor systems, and combinations of these three, supplemented, at times, by the miner pushing his own car. Haulage may also be classified into gathering and main line. Gathering haulage is the collecting of loaded cars to a point whence they are hauled to the tipple. In this there is perhaps more lost-time than on the main line because there are .more units in the operation to be synchronized. Also, conditions on the gathering haul- age, such as bad track, poor timbering, insufficient motive power, etc., cause delays; usually these are corrected on the main-line haulage.

Jan 1, 1931

By Clark A. Sumner, D. Arthur Burnham

A process for recovery of greater than 99% of the copper contained in acid leach solutions by sulfide precipitation using hydrogen sulfide as a hydrometallurgical reagent has been developed. The process incorporates the concept of hydrogen sulfide addition to recycled copper sulfide solids in a turbulent flow area where further precipitation or agglomeration occurs to increase the effective particle size of the copper sulfide precipitate. Because the recycled solids provide a larger number of particles upon which momentary excesses of hydrogen sulfide are absorbed, oversulfidization of the product is prevented. Copper sulfide precipitates produced in this manner in a laboratory test reactor showed greatly improved physical characteristics compared to copper sulfide precipitates obtained by conventional direct precipitation in which H2S is bubbled directly into acid leach liquor. Copper sulfide precipitates were evaluated and compared by use of filtration tests and settling rate studies. Electron microscopic examination of the solids confirmed the presence of larger particles in reactor-precipitated copper sulfide. Flotation was examined as an alternative to filtration for recovery of CuS precipitates and was found to achieve complete CuS removal without addition of collector or frothing reagents in a period of 2 min. In the same test reactor, a rapidly floatable CuS precipitate was also formed by mixing H2S with acid liquors used to leach crushed copper oxide-copper sulfide ore (LPF process). In the presence of gangue from the crushed ore, flotation of both natural and reactor-produced copper sulfides resulted in recovery of better than 90% of the copper contained in the crushed ore.

Jan 1, 1974

By AIME AIME

WHEN I was getting data for my books on ore dressing, I traveled across the continent, visiting a great many mills, always accompanied by my vanning shovel, and I got to be a joke among the millmen. They would say "Here comes the Professor with his vanning shovel." With the aid of this vanning shovel, I examined the tailings of all the mills I visited and I found it to be universally true that they contained some extremely fine, free mineral. I looked everywhere to see if I could find a machine or a process that would save this fine mineral. But nowhere did I find anything that made any bid for success until I visited the Kennedy mill, with its Gates canvas plant, on the Mother Lode of California. There I found that the tailings of the Frue vanners were put into a one-spigot classifier of good design which yielded a spigot product entirely free from this fine, free mineral which only assayed 40c. to the ton in gold. The overflow was extremely fine and as¬sayed $3 to the ton. This overflow was fed to ten canvas tables each 10 ft. square, with the grain of the canvas running across the table to make for the roughest surface. The canvas used was No. 6 cotton duck sail cloth.

Jan 1, 1934

By R. M. Brick

The etched mierostructures of cold-worked alpha brasses, after reductions in excess of about 20 per cent, exhibit dark lines or markings, which have been termed "deformation bands," "etch bands," and "strain markings." The terms will be used synonymously in this report. The markings are similar in their general appearance to etch figures found in cold-worked iron, aluminum and other cubic metals but in certain respects may differ noticeably. At reductions of from about 20 to 50 per cent in brass, they appear as straight dark lines of irregular spacing and at random directions in different grains, but apparently intimately associated with definite crystallographic planes, usually {ill), in each crystal. At higher reductions, the markings on the rolling plane tend to appear in a direction transverse to the rolling direction in all crystals but may bend away at considerable angles, particularly near grain boundaries. Samans,1 on the basis of X-ray and micrographic studies of two single crystals of brass, rolled to a 50 per cent reduction, showed that the lines of deformation were the edges of thin mechanical twins parallel to octahedral planes. Barrett and Levenson2-4 have made comprehensive studies of the deformation of iron and of aluminum. They show that in these two metals the deformation markings originate by division of the original homogeneous crystal into banded areas differing in orientation by an amount that increases with the degree of deformation. The markings thus cannot be twin bands, and Barrett, in a review of this subject,2 attributed Samans' results on brass to an accidental choice of deformation that left the bands in approximately a twinned relationship. On the other hand, Mathewson6 has suggested that in some cases mechanical twinning offers a better rationalization of the coverage of some (111) pole figures of worked brass than the assumption of band rotation into symmetry positions. Considering next a deformed and annealed alpha brass, the most striking aspect of its microstructure is the multiplicity of twin bands.

Jan 1, 1940

By R. M. Brick

The etched mierostructures of cold-worked alpha brasses, after reductions in excess of about 20 per cent, exhibit dark lines or markings, which have been termed "deformation bands," "etch bands," and "strain markings." The terms will be used synonymously in this report. The markings are similar in their general appearance to etch figures found in cold-worked iron, aluminum and other cubic metals but in certain respects may differ noticeably. At reductions of from about 20 to 50 per cent in brass, they appear as straight dark lines of irregular spacing and at random directions in different grains, but apparently intimately associated with definite crystallographic planes, usually {ill), in each crystal. At higher reductions, the markings on the rolling plane tend to appear in a direction transverse to the rolling direction in all crystals but may bend away at considerable angles, particularly near grain boundaries. Samans,1 on the basis of X-ray and micrographic studies of two single crystals of brass, rolled to a 50 per cent reduction, showed that the lines of deformation were the edges of thin mechanical twins parallel to octahedral planes. Barrett and Levenson2-4 have made comprehensive studies of the deformation of iron and of aluminum. They show that in these two metals the deformation markings originate by division of the original homogeneous crystal into banded areas differing in orientation by an amount that increases with the degree of deformation. The markings thus cannot be twin bands, and Barrett, in a review of this subject,2 attributed Samans' results on brass to an accidental choice of deformation that left the bands in approximately a twinned relationship. On the other hand, Mathewson6 has suggested that in some cases mechanical twinning offers a better rationalization of the coverage of some (111) pole figures of worked brass than the assumption of band rotation into symmetry positions. Considering next a deformed and annealed alpha brass, the most striking aspect of its microstructure is the multiplicity of twin bands.

Jan 1, 1940

By D. G. Westlake

Polycrystalline tensile specimens of various Zr-0-H alloys have been tested at 298°, 178°, and 77°K. Solute oxygen and hydride precipitates in quenched alloys made individual contributions to the yield strength at 0.2 pct strain which combined to produce a resultant strength increment, a,., Ductility changes which were ohserved can he interpreted in terms of the various oxygen and hydrogen concentrations, testing tem -peratures, and dispositions of the hydride. ADDITIONS of oxygen in solid solution were known to increase the yield and tensile strengths of polycrystalline zirconium as early as 1951.' More recently, the critical resolved shear stress (CRSS) for prism slip in zirconium single crystals was also shown to be affected by the solute oxygen impurity.' This latter work also demonstrated that large increments of strength could be contributed by the finely dispersed zirconium hydride precipitates that are present in quenched Zr-H alloys.3 It was concluded that the combined strengthening due to alloying could be expressed by where to is the increase in the CRSS due to solute oxygen alone and TH is the increase due to finely dispersed hydride precipitates. Eq. [I] is analogous to one used to express the combined strengthening effects of work hardening and neutron radiation damage.4 Eq. [1] was verified only indirectly and for only small amounts of the impurities—up to 0.14 at. pct 0 and 0.63 at. pct H. The present investigation was undertaken to obtain a more direct verification of the validity of the form of Eq. [1] for this system and also to determine the combined effects of oxygen and finely dispersed hydride precipitates on the tensile strength and ductility of polycrystalline zirconium. EXPERIMENTAL PROCEDURE Tensile specimens were machined from the same rolled billet of Kroll zirconium used in the earlier study.' These measured 38 by 4.7 by 0.5 mm and had 10-mm gage lengths which were 2.8 by 0.5 mm. Each specimen was ß-annealed in vacuo at 1173°K for 15.5 hr and a-annealed at 1073°K for 4 hr to D. G. WESTLAKE, Member AIME, is Associate Metal l ur-gist, Metallurgy Division, Argonne National Laboratory, Argonne, III. Manuscript submitted July 17, 1964. IMD______________ give an equiaxed structure with grain diameters averaging 0.06 mm. Oxygen was added by allowing the metal to react with a known quantity of oxygen during the 0 anneal and known quantities of hydrogen were added during the a anneal. Each alloy was encapsulated in Pyrex under vacuum, annealed at 873°K for 4 hr, quenched into ice water, and polished by immersion in a solution of 46.75 vol pct H2O, 46.75 vol pct concentrated HNO3, and 6.5 vol pct HF (49 pct) at 298°K. Special heat treatments given to a few specimens are described in the results below. Tensile tests were done on an Instron machine and were begun within 20 min after the quench, except where specified otherwise. Tests at 298°K were in air, at 178°K in acetone, and at 77°K in liquid nitrogen. All tests were at a strain rate of 8x sec-1. RESULTS AND DISCUSSION Yield Stress at 298°K. The compositions of alloys and the corresponding yield stresses (0.2 pct strain) are given in Table I. A plot of the yield stresses of the oxygen alloys, A, B, C, and D, indicates that varies linearly with CO1/2, where Co is the oxygen concentration, Fig. 1. This is in accord with Fleischer's6 theory for solution strengthening if the oxygen atoms do not cluster, or the cluster size remains constant with increasing oxygen concentration. In Fig. 1, it appears that if one could prepare some oxygen-free zirconium its yield stress would be very low. Therefore, we shall assume that for the oxygen alloys is equivalent to O0, the strength increment contributed by the presence of oxygen. The relationship between0.2and Co is expressed by 0.2 = 31.3 CO1/2, when the yield stress is in kg per sq mm and the concentration is in at. pct. Each of the hydrogen alloys, Al, A2, A3, and A4, contained 0.081 at. pct 0 as an impurity. In Fig. 1, it appears that this small amount of oxygen makes a significant contribution to the strength which cannot be ignored when we evaluate the contribution of the finely dispersed hydride. Let us assume the validity of the following equation: a0.2 = (a2o+a2R)1/2 [2] which is analogous to Eq. [I] for single crystals, and calculate values of UH for the hydrogen alloys by using the experimental values of 0.2 and o (0.081 at. pct) = 8.9 kg per sq mm. For 0.36 at. pct H, oH = 6.47; for 0.72 at. pct H, OH = 11.30; for 2.16 at. pct H, OH = 19.4; and for 3.60 at. pct H,

Jan 1, 1965

By George Stern

The purpose of this investigation has been to study one method for making ordinary carbon steel by the powder metallurgy technique. This method con- sists of pressing and subsequently sintering an intimate mixture of iron powder and gaphite in a suitable atmosphere to Produce a steel. Two types of iron Powder have been studied, electrolytic and reduced. The sinkring of mixtures of loose Car-bonyf iron and carbon black for several hours at I000 to 1100 C. (1830' to 2010°F.), followed by forging of the resultant ingots to bars, has been studied by Offermann.' TrailZ has reported on the properties of hydrogen-reduced and electrolytic iron powders, both containing 0.5 per cent carbon. Methods for making steel bodies by powder metallurgy have also been sug- gested by Goetzel13 who recommends the addition of steel powder of well-defined carbon content to pure iron powder, and Volterra,~ who suggests compaction and subsequent sintering of a mixture of steel powder, iron oxide and iron powder. Additional methods for making steel bodies by powder metallurgy have been reported in the literature by Kohering Allen,6 Balke,7 Wulff,8 Boegehold,9 and others.,0,11,12 It is felt that the method of pressing iron powder and graphite, as described herein, lends itself best to production be-Cause of the lubricating action of the

Jan 1, 1946

By George Stern

The purpose of this investigation has been to study one method for making ordinary carbon steel by the powder metallurgy technique. This method con- sists of pressing and subsequently sintering an intimate mixture of iron powder and gaphite in a suitable atmosphere to Produce a steel. Two types of iron Powder have been studied, electrolytic and reduced. The sinkring of mixtures of loose Car-bonyf iron and carbon black for several hours at I000 to 1100 C. (1830' to 2010°F.), followed by forging of the resultant ingots to bars, has been studied by Offermann.' TrailZ has reported on the properties of hydrogen-reduced and electrolytic iron powders, both containing 0.5 per cent carbon. Methods for making steel bodies by powder metallurgy have also been sug- gested by Goetzel13 who recommends the addition of steel powder of well-defined carbon content to pure iron powder, and Volterra,~ who suggests compaction and subsequent sintering of a mixture of steel powder, iron oxide and iron powder. Additional methods for making steel bodies by powder metallurgy have been reported in the literature by Kohering Allen,6 Balke,7 Wulff,8 Boegehold,9 and others.,0,11,12 It is felt that the method of pressing iron powder and graphite, as described herein, lends itself best to production be-Cause of the lubricating action of the

Jan 1, 1946

By W. A. Selvig

BY plotting fixed carbon against British thermal units of coals free from mineral matter, and ranging in rank from anthracite to lignite, it is found that the coals of higher rank, from anthracite to the higher rank of the high-volatile bituminous coals, inclusive, can be separated into groups according to their degree of metamorphism by reference to their fixed carbon. Such charts show also that the coals lower in rank can be best separated into groups with respect to B.t.u., especially when plotted on the moist basis, that is, coal containing its natural bed moisture. A tentative scheme for coal classification was presented at the October, 1932, meeting of the Technical Committee on Scientific Classification, of the American Standards Association Sectional Com-mittee on Coal Classification. This scheme was sponsored by Sub-committee IV on Tentative Classification of Coals, under the chairmanship of W. T. Thom, Jr. It proposed the grouping of coals according to rank by reference to fixed carbon and B.t.u., on the basis of coal containing its natural bed moisture but free from mineral matter. This scheme proposed classifying coals into four broad classes: (1) anthracitic, (2) bituminous, (3) subbituminous, (4) lignitic.. The anthracitic class was divided into three groups designated as meta-anthracite, normal anthracite, and semianthracite. The bituminous class also was divided into three groups, low volatile, medium volatile, and high volatile. The high-volatile group was further subdivided into four subgroups according to moisture content, as follows: (1) less than 5 per cent, (2) 5 to 10 per cent, (3) 10 to 15 per cent, and (4) 15 per cent and more. The subbituminous class was divided into two groups, group, 1 including subbituminous coals having calorific values of 10,500 B.t.u. or more, and group 2 including those with less than 10,500 B.t.u. , The lignitic class of coal was divided into two groups both below 8,000.B.t.u., the one group consisting of consolidated and the other of unconsolidated

Jan 1, 1934

By E. H. Rennhack

Phase equilibria of the zinc-rich portion of the Zn-Fe-A1 system containing up to 20.0 wt pct Fe and Al have been investigated at 600°C (1112°F), 450°C (842°F), and room temperature by metallographic and X-ray diffraction techniques. The phase relationships were found to involve only those phases present in the three binary systems. THE presence of small quantities of aluminum (approx. 0.2 wt pct*) in zinc galvanizing baths is known to suppress the formation of Zn-Fe alloy layers within the coating.' As part of an extended investigation of this suppression effect and the alloy reactions involved, the zinc-rich corner of the Zn-Fe-A1 equilibrium system containing up to 20.0 pct Fe and Al was determined at 600°C (1112°F), 450° F (842° F), and room temperature. The present paper reports the findings of this study. The constitution of the Zn-Fe system has been reported by Raynor2 based mainly on the work of Schramm3-3 and Truesdale et a1.6 The solid solubility of iron in zinc is extremely small and lies between 0.0009 and 0.0028 pct in the range 150° to 400°C (302°to752°F). Within the temperature and composition range of interest, a eutectic reaction involving nearly pure zinc, liquid = Zn+FeZn13, is observed at about 419°C (786° F) and 0.018 pct Fe along with a peritectic reaction, FeZn7+ liquid e FeZn13, at 530°C (986° F) and 6.2 pct Fe. The latter reaction is sluggish due to the large proportipn of solid phase involved in the transformation. Halla et al.,7 identified the compound FeZn13 as monoclinic with a = 13.68, b = 7.63, c = 5.07, and B = 128°44'. The structure of FeZn7 was reported by Bablik, et al.,8 to be of hexagonal symmetry, belonging to either the C6v = C6/m mc or D46h = C6/mc space group. Divensions of the unit cell are a = 12.81A and c = 57.6a. The Zn-A1 diagram as composed by Raynor9 and later Gebhardt10 is characterized by a eutectic decomposition, liquid 382°C (720°F) and 95.0 pct Zn and a eutectoid decomposition, at 275° (527°F) and 78.0 pct Zn. The eutectoid reaction cannot be suppressed permanently by quenching. Above 275° (527° F), a and a' co-exist in a closed miscibility gap between 31.6 and 78.0 pct Zn. Both phases are fcc and have nearly the same lattice parameter. The maximum solubility of aluminum in zinc (B) is approximately 1.0 pct at the eutectic temperature. PROCEDURE Materials. The experimental alloys were prepared from both massive and powdered material. Cast alloys were composed from three zinc-base master alloys containing 8.0 pct Fe, 16.0 pct Fe, and 50.0 pct Al which were made from C.P. zinc, Armco iron, and

Jan 1, 1962

By E. H. Dix

All commercial aluminum contains small percentages of copper, iron, and silicon as unavoidable impurities. The purest metal obtainable commercially, special grade high purity ingot, contains a maximum of 0.50 per cent. impurities of which the usual minimum amount of copper is 0.01 per cent.; silicon, 0.12 per cent.; and iron, 0.20 per cent. This grade is too costly for most purposes. The two standard grades, Nos. 1 and 2, containing a minimum of 99.0 and 98.0 per cent. aluminum, respectively, are more generally used. Other grades of secondary aluminum often contain as high as 3 or 4 per cent. of impurities, which include 1 per cent., or more, of zinc. Specifications for high-grade aluminum-casting alloys generally allow a maximum of 1.7 per cent. for total impurities. The S. A. E. Specification No. 33, which is intended to cover alloys made from secondary aluminum ingot, gives the iron maximum as 1.5 per cent. and the maximum for silicon (including manganese and tin) as 0.75 per cent. The effect of even relatively small amounts of impurities on the physical properties of ingot aluminum is shown by the following cornparison of two lots of aluminum, which may be taken as representative of special grade and grade No. 2 ingot, respectively. AnalysEs Special Grade, Gbade No. 2, Per Cent. PeR CBnt. Copper................................. 0.01 0.32 Silicon................................. 0.12 0.32 Iron................................... 0.42 0.82 Aluminum.............................. 99.45 98.54

Jan 1, 1923

By E. H. Dix

All commercial aluminum contains small percentages of copper, iron, and silicon as unavoidable impurities. The purest metal obtainable commercially, special grade high purity ingot, contains a maximum of 0.50 per cent. impurities of which the usual minimum amount of copper is 0.01 per cent.; silicon, 0.12 per cent.; and iron, 0.20 per cent. This grade is too costly for most purposes. The two standard grades, Nos. 1 and 2, containing a minimum of 99.0 and 98.0 per cent. aluminum, respectively, are more generally used. Other grades of secondary aluminum often contain as high as 3 or 4 per cent. of impurities, which include 1 per cent., or more, of zinc. Specifications for high-grade aluminum-casting alloys generally allow a maximum of 1.7 per cent. for total impurities. The S. A. E. Specification No. 33, which is intended to cover alloys made from secondary aluminum ingot, gives the iron maximum as 1.5 per cent. and the maximum for silicon (including manganese and tin) as 0.75 per cent. The effect of even relatively small amounts of impurities on the physical properties of ingot aluminum is shown by the following cornparison of two lots of aluminum, which may be taken as representative of special grade and grade No. 2 ingot, respectively. AnalysEs Special Grade, Gbade No. 2, Per Cent. PeR CBnt. Copper................................. 0.01 0.32 Silicon................................. 0.12 0.32 Iron................................... 0.42 0.82 Aluminum.............................. 99.45 98.54

Jan 1, 1923