By A. Josefsson

The transition temperatures of 0.01 to 0.02 pct carbon steels are shown to be strongly influenced by cooling rate in the a range, quenching from A, causing a very low transition temperature even after strain aging. In a titanium-stabilized steel and in a steel with 0.05 pct C this effect is absent. NORMAL mild structural steels usually show a structure of more or less pure ferrite, as a matrix, in which cementite grains or pearlite are embedded. Of these components, ferrite is by far the most interesting one as far as ductility and brittle (cleavage) fracture are concerned. Obviously, pear-lite and carbide are by no means necessary for a cleavage crack to nucleate and grow in the ferrite, as steels with a very low carbon content (Armco iron with 0.02 pct C) have an impact transition temperature just as high as semikilled steels with 0.26 pct C.1 Although it has been argued that a very embrittling effect is to be expected from cementite, precipitated as continuous films along the ferrite grain boundaries,'. " the micrographic evidence for a direct causal connection between the brittleness and these films does not seem to be very convincing. On the other hand, it has been stated that cementite particles in ferrite are able to stop ferrite cracks.4,5 In any case, the properties of the ferrite itself seem to be of overwhelming importance to the ductility of steels, justifying a thorough study of steels consisting of ferrite of different compositions, but principally free from pearlite, which means a carbon content below 0.02 pct. Such investigations have been carried out using the impact transition temperature as a criterion of the tendency to brittle fracture and have given some rather unexpected results. One result is the profound influence of carbon on the transition temperature of the steel in normalized condition. If the carbon content is reduced from 0.02 to 0.015 pct and below, a nearly discontinuous decrease in transition temperature appears even with high percentages of such elements as phosphorus and nitrogen present. This will be reported elsewhere." The present paper deals with another effect of carbon upon transition

Jan 1, 1955

By G. Das, S. V. Radcliffe

The substructural features developed in tungsten as a function of annealing temperature (up to 2200°C) and type of material [undoped and doped powder metallurgy (PM) tungsten and electron beam melted tungsten] have been investigated by transmission electron microscopy. For doped PM tungsten wires, characteristic "par-ticulate" substructural features developed rapidly with increase in annealing temperature above 700°C. The features consisted of parallel rows of elongated or circular shapes (500 to 1000A diam) lying along the direction of the wire axis and were identified as internal voids by diffraction contrast experiments. In recrystallized doped PM rod, larger voids were observed and were identified by precision dark field analysis to be cubic in shape and bounded by (100) planes. In marked contrast with both the doped PM materials, recrystallized undoped PM rod exhibited only very occasional and randomly arranged voids. Furthermore, no voids were observed in either material after electron beam melting. The high concentration of voids in the doped PM materials is attributed primarily to vaporization of doping additions or their pvoducts situated at the original grain boundaries , whereas the few voids in undoped material are considered to be traces of microporosity which were not eliminated during sintering. A tentative mechanism is suggested for the dezlelopment of the voids in relation to the processing sequences (sintering and working) and to the subsequent annealing. In recent years, a characteristic substructural feature consisting of rows of small elongated or circular regions of light contrast lying along the direction of working has been seen in thin foil electron microscopy studies of annealed sheet, wire, and rod tungsten. These features were present in the published micrographs of sheet by Weissmann et al.1 and of wire by Meieran and Thomas2, although the authors did not draw attention to them. Wronski and Fourdeux3 observed similar features in sintered rod tungsten (it was not specified whether or not the material was doped*) and interpreted them on the basis of their ap- particles, based on extraction replica evidence from the fracture surface of the initial hot-rolled slab material from which the sheet was prepared. No diffraction contrast experiments on the features were reported in any of these studies. The present investigation was undertaken with the primary objectives of: a) identifying the nature of these substructural features in tungsten by electron diffraction contrast experiments, since the contrast for voids can be expected to differ from that for crystalline or glassy particles, and b) elucidating the origin of the features and their development. For the latter purpose, doped and undoped powder metallurgy tungsten was obtained as rod and wire to represent different stages of reduction during final processing. These materials were examined both in the as-processed condition and after annealing to successively higher temperatures. In addition, the same doped and undoped materials were examined after vacuum melting in rod form. I) MATERIALS AND PROCEDURE Doped powder metallurgy (PM) tungsten wire (commercial purity 99.9 pct W) was obtained in the as-drawn and surface ground condition (0.030 in. diam "ground seal rod"). Doped and undoped tungsten rod (0.075 in. diam) representing an earlier stage of final processing was obtained from the same commercial source (Refractory Metals Division, General Electric Co.). Lengths of both the doped and undoped rod materials were single-pass melted in an electron-beam zone refiner to examine the effect of vacuum melting on the substructure. Annealing was carried out in a tungsten crucible in a tantalum strip resistance furnace under a vacuum of l0-15 mm Hg. Longitudinal sections of the wire and rod materials were examined by light and electron microscopy. The preparation of thin foils suitable for electron transmission from 0.030 in. diam tungsten wire and the rod specimens was carried out by means of a high-precision microjet technique developed to provide lack of jet stability and precise control of the area thinned. The method is described in detail elsewhere.' The foils were examined in a JEM 6A electron microscope using a goniometer stage (±20 deg tilt, 360 deg rotation) and operated at 100 kV. To minimize contamination problems a 200 µ condenser aperture was used in conjunction with a useful beam current of 50 µA. II) RESULTS AND DISCUSSION A) Diffraction Contrast Analysis. In order to determine the optimum conditions for the development of the substructural feature, a series of isochronal 30 min annealing experiments were carried out on specimens of the doped PM tungsten wire. The transmission electron microscopy analysis showed that the as-drawn wire, Fig. 1(a), consists of 'fibers' whose long axis is closely parallel to the wire axis of (110). The fiber width averages some 0.5 µ. Dense disloca-

Jan 1, 1969

By R. H. Martinson, E. Teghtsoonian

The effects of magnesium-rich surface layers of varying thickness on the mechanical properties of LiF have been studied. The yield stress, critical tensile stress, and work-hardening slope increase linearly with layer thickness, while the strain to fracture decreases yapidly with increasing layev thickness. The results of tension tests, supplemente!d by metallogvaphic evidence, indicate that the yield stress and the critical tensile stress of LiF are not determined by surface-source operation. DESPITE many studies, which have recently been reviewed,' certain fundamental aspects of the plasticity of LiF remain obscure. For instance, one question still awaiting a satisfactory resolution is: does the nucleation and/or multiplication of dislocations in LiF occur preferentially near the crystal surface? It is now well-known that mobile dislocation half-loops are readily introduced into LiF by surface damage and that the mechanical properties of LiF are affected by such surface damage. However, it is not known whether, in the absence of large numbers of artificially introduced surface sources, dislocations arise more easily near the crystal surface than in the crystal interior. It is also not known to what extent existing mobile dislocations multiply preferentially near the crystal surface. The present work is an experimental study of these matters. A short investigation of the effect of magnesium -alloyed surface layers on the deformation of LiF single crystals has been published by Westwood.~ Some relevant conclusions drawn from this research are restated here for purposes of comparison with the present work. 1) Tests on as-cleaved, chemically polished, coated and uncoated specimens show that a coating can restrict the operation of artificially introduced surface sources, thereby raising the yield stress. A coating also decreases the initial rate of work hardening of as-cleaved LiF crystals by reducing the number of active dislocation sources, so that mutual dislocation interference effects are lessened. 2) A catastrophic breakthrough of groups of edge dislocations piled up against the coating can cause stress drops in the stress-strain curve. 3) A surface coating can act as a stable barrier to the egress of dislocations, causing pile-up,

Jan 1, 1965

By D. A. Dahlstrom

Although the liquid-solid cyclone is a relatively recent innovation in the field of coal preparation, various authors have already indicated three distinct applications to operations encountered in the modern tipple. Driessen's articles and work at the Dutch State Mines exhibited its possibilities in the beneficiation of fine coal with apparently high efficiencies down to the 200-mesh fraction. 1 2 3 4 Other publications point out its use as a recoverer, thickener, and preliminary dewatering agent of fine coal which in too many cases is being wasted due largely to former high operating cost limitations 5 6. Finally, certain authors have emphasized the practicability of applying the cyclone to the elimination of coarse and fine solids from water slurries in the tipple in order to produce a water suitable for recycle purposes containing only minute particles far below the 200-mesh size.6 This would result in a closed water system for many cases, with its accompanying economic and operating advantages to locations where water quantity and quality problems are severe; better operation of washing equipment using a consistent water devoid of injurious fine particles; lowered maintenance costs due to the lesser abrasion resulting when the fine abraiding particles are removed; and the greater ease of disposing of refuse streams of reduced volume containing greater percentages of solids.

Jan 1, 1949

By C. J. Haigh

Stockpiled and currently produced zinc plant residues containing zinc ferrite are to be treated at a rate of 350 tonne per day in a plant that is being constructed at the Risdon works of the Electrolytic Zinc Company of Australasia Limited (E.Z.). Start-up of the plant is scheduled for December, 1970. The residue is to be treated by a hydrometallurgical process that was developed by E.Z. in Australia, by Det Norske Zinkkompani in Norway, and by Compagnie Royale Asturienne des Mines (Asturiana de Zinc) in Spain. The process, as it is to be used at Risdon, is simple, consisting essentially of two stages : 1. A leaching stage at atmospheric pressure in which the zinc ferrite contained in zinc plant residue is dissolved in spent electrolyte, fortified with make up sulphuric acid, at a temperature in the range 70 to 95ºC. Undissolved solids containing lead and precious metals are separated for sale to a lead smelter. 2. An iron precipitation stage at atmospheric pressure in which ferric iron is precipitated from a slightly acidic solution at 90 to 95ºC as ammonium jarosite, a crystalline double sulphate which is relatively coarse, and is easily filtered and washed free of zinc-bearing solution. Calcine is used to neutralise the acid that is liberated during precipitation of the iron. Also included in the Risdon plant are a separate stage for oxidation of ferrous iron by injection of air, and a pre-neutralisation stage, using recycled oxidation stage pulp, to neutralise excess acidity from the leaching stage before the jarosite precipitation stage. The residue treatment plant consists of conventional equipment such as covered agitated vessels, thickeners and filters. Operation will be continuous and product solution will join the main zinc plant circuit for further purifications and electrolysis. Marketable zinc production will be increased by 70 tonne per operating day by the treatment of residue.

Jan 1, 1970

By Carl Scholz

DURING November And December, 1907, Four Serious Mine-explosions Occurred In The Appalachian Coal-Field, Which Resulted In The Loss Of Nearly A Thousand Lives And Caused An Enormous . Damage To Property. These Accidents Attracted More Than The Usual Attention; Coal-Trade And Engineering Papers Contained Many Comments And Suggestions On The Cause And Prevention Of Accidents; The Daily Press In Many Instances Condemned The Coal-Operators And Charged These Accidents To Their Negligence, Or Their Anxiety To Make Money Without Adopting Precautionary Measures. Immediately After Each Accident The Respective State ..Authorities Ordered Close Investigations To Be Made, With The View Of Establishing The Cause And Suggesting Remedies To Prevent Recurrence. Representatives Of The Technologic Branch Of The U. S. Geological Survey, To Whom The Investigation Of Mine-Accidents Had Recently Been Delegated By The Secretary Of The Interior,. Visited The Mines And Co-Operated With The Local Authorities In Their Determinations. It May Be Safe To Say Here That An Investigation Of A Mine After An Explosion Has Occurred Discloses But Little, Because. The Causes Have Been Removed And Conditions Have Been Entirely Changed. On Jan. 8, 1905, The Coal-Operators Of West Virginia Organized An Association At Washington For The Purpose Of Making Extensive Investigations, And Sufficient Funds Were Pledged To Carry Out This Work. At This Organization Meeting, The Representatives Of The Geological Survey Present Had No Suggestions To Offer As To The Cause Of These Accidents. An Examination Of The Various Reports Concerning These Accidents Indicates That The Explosions Were Caused By The Ignition Of Gas Or Dust; They Show The Point Of Origin And The Direction In Which The Force Was Expended, And Give A Detailed Description Of The Damage Done. Very Little Has Been Said As To What

Jan 7, 1908

Jan 1, 1927

By P. Chiotti, J. T. Mason

Ther?nal, X-ray, metallographic, and vapor pressure data were obtained to establish the phase diagram and standard free energy, enthalpy, and entropy of formation for the compounds in the Sw-Zn system. Four compounds, SmZn, SmZn2 , SmZn4.s, and SmZn8.5, melt congruently at 960°, 94Z°, 908°, and 940°C, respectively. The cornpounds SlnZns, Sm3Znll, and SnzZn7.3 undergo peritectic decomposition at 855", 870°, and 890C, respectively. Another compound of uncertain stoichiometry, SmZn11, undergoes peritectic decomposition at 760°C. Four entectics were observed with the following compositions in weight percent zinc and eutectic tenzperatures in degrees Centigrade: 12 pct, 680°C; 36 pct, 890°C; 58 pct, 850°C; and 72 pct, 900°C. An allotropic transformation and a composition range were observed for the SmZnz compound. The transfor)nation varies from 905" to 865°C as the zinc content increases from 16.0 to 48.5 wt pct, respectively. The free energy of formation of the compounds at 50PC varies between -15.9 kcal per mole for SmZn to -51.1 kcal per mole for SmZn,.,. Corresponding enthalpies vary between -19.2 to -78.3 kcal per mole. The ther-modynamic properties for the liquid alloys are described by the relations: A search of the literature revealed very little information on the Sm-Zn system. Chao et al.&apos; as well as Iandelli and palenzonai have reported the structure of SmZn to be cubic B2 type and Kuz&apos;ma et al3. have reported the structure of -sm2zn17 to be of the Th2Ni17 type. The purpose of this work was to establish the phase diagram of this system, to determine the zinc vapor pressure over the solid two-phase regions of the SYstem, and to calculate the thermodynamic properties of the compounds. MATERIALS AND EXPERIMENTAL PROCEDURES The metals used in this investigation were Bunker Hill slab zinc 99.99 wt pct pure and Ames Laboratory samarium. Analysis of the samarium by chemical, spectrographic, and vacuum-fusion methods gave the following average impurities in ppm: Nd, <200; Eu, <100; Gd, <100; Y, <50;Ca, 225; Ta, 400; Mg, 10; Cu, ~50; 0, 175; H, 20; and N, 15. The elements Fe, Si, Cr, Ni, Al, and W were not detected. The samarium was received as sponge metal and was kept under argon except when being cut with shears and when being weighed. Tantalum was found to be a suitable container for alloys with zinc contents up to the Sm2Znl, stoichio-metry. At higher zinc contents the grain boundaries of the tantalum containers were penetrated by the alloy and the containers failed during prolonged annealing. About 25 g of massive zinc and samarium sponge were sealed in tantalum crucibles equipped with thermocouple wells. These crucibles were in turn sealed in stainless-steel jackets. All closures were made by arc welding under an argon atmosphere. The samples were equilibrated in an oscillating furnace and in some cases were given various heat treatments in a soaking furnace. After appropriate heat treatment the steel jackets were removed and the alloy subjected to differential thermal analysis. The apparatus was calibrated against pure zinc and pure copper and found to reproduce the accepted melting points within 1°C. Alloys were subsequently subjected to metallographic examination and those of appropriate compositions were used for X-ray diffraction analysis and for zinc vapor pressure determinations. The vapor pressures were determined by the dewpoint method. Both the differential analysis and dewpoint measuring apparatuses have been described in earlier papers.4, 5 All alloy samples were etched with Nital (0.5 to 3 pct nitric acid in alcohol) except the samarium-rich alloys. These more reactive alloys were electro-polished in a 1 to 6 pct HClO4 in methanol solution at -700c at a potential of 50 v. EXPERIMENTAL RESULTS Phase Diagram. The results of thermal analysis are indicated by the points on the phase diagram, Fig. 1. Eight compounds and four eutectics were observed. The composition of the compounds and their melting or peritectic temperatures are given on the phase diagram. The four eutectic compositions in wt pct zinc and eutectic temperatures in % are: 12 pct,- 680°C; 36 pct, 890°C; 58 pct, 850°C; and 72 pct, 900°C. The stoichiometry of the most zinc-rich compound is still uncertain, but is very likely either SmZnll or SmZnlz. However, to simplify the presentation which follows it will be referred to as SmZnll. As shown on the phase diagram the phase regions for some of the samarium-rich alloys have not been unambiguously established. A sample of pure samarium was observed to transform at 924°C and to melt at 1074"C, in good agreement with corresponding val-

Jan 1, 1968

By D. C. Jackling

I BESPEAK your indulgence for a brief expression of the views of a patriarch in the field of mineral industry technology relative to young men&apos;s problems in that sphere of education and endeavor. Wherever hereafter I employ the terms "technical education," "engineer," "technologist," or similar expressions, these are intended to be understood as relating to the broad field of the sciences and arts applicable to the mineral industries. First, the usefulness of technical education to either the possessor of it or those to whom its services may be made available industrially depends primarily upon the quality of the education and the capabilities of the educated to put his talents to effective and constructive employment in his chosen field of applied science.

Jan 1, 1940

By R. H. B. Jones

This paper reviews pertinent geology of the Biwabik iron formation, Mesabi Range, Minnesota. This iron formation is divisible into four members. Each member is distinctive and contains marker horizons, which are recog nizable throughout all phases of alteration from lean, fresh rock to high-grade iron ore. Some beds have a larger magnetite content than others. During the process of ore genesis, which is essentially an oxidation process, the magnetite content is lowered. Alteration from iron formation to ore includes both oxidation of iron minerals and silica removal by leaching and these distinct processes progress at variable rates for different locations and structures. Magnetic intensities, of each horizon of the iron formation are dependent chiefly upon its preoxidation magnetite content, upon the subsequent degree of oxidation, upon the character of the enclosing rocks, and on the extent of fracturing, folding, or faulting. The results of a number of magnetic surveys are described and are correlated with results of drill-hole and mine exploration and developmerit. The magnetic anomalies obtained are discussed in relation to phases of formation of ore within the iron formation. General Information One hundred years ago a party of surveyors, applying the principles of geophysical prospecting, discovered iron ore in the state of Michigan in the Lake Superior district. This event was officially reported as follows:&apos; On Sept. 19 (1844) while running the east line of Town 47 North, Range 27 West, they observed by means of the solar compass remarkable variations in the direction of the needle, amounting to 87" from the normal. Ascribing this phenomenon to iron ore, they sought and found it in ledges or outcrops at several points. The solar compass referred to was invented by William A. Burt, deputy surveyor in charge of this party.2 It is used for determining the true meridian by an observation on the sun. Eight years later, on July 7, 1852, the first iron &apos;re, consisting of 6 bbl. of Ore, was shipped from Marquette, Michigan. It was another 40 years before the first or> shipment left the Mesabi Range in Minnesota, in October 1892. It totaled 4245 tons. Fifty years later, 90 years after the original shipment, during 1942 the Lake Superior district shipped 93,495,392 gross tons of iron ore. Production came from Minnesota, Michigan, Wisconsin, and Ontario, Canada. Throughout the 90-Year period it was known that magnetic properties of most of the ore bodies, and of the iron formations in which they occur, affected the compass. This phenomenon, later to be made use of to outline areas of ground favorable for exploration, was at first a

Jan 1, 1949

By R. H. B. Jones

This paper reviews pertinent geology of the Biwabik iron formation, Mesabi Range, Minnesota. This iron formation is divisible into four members. Each member is distinctive and contains marker horizons, which are recog nizable throughout all phases of alteration from lean, fresh rock to high-grade iron ore. Some beds have a larger magnetite content than others. During the process of ore genesis, which is essentially an oxidation process, the magnetite content is lowered. Alteration from iron formation to ore includes both oxidation of iron minerals and silica removal by leaching and these distinct processes progress at variable rates for different locations and structures. Magnetic intensities, of each horizon of the iron formation are dependent chiefly upon its preoxidation magnetite content, upon the subsequent degree of oxidation, upon the character of the enclosing rocks, and on the extent of fracturing, folding, or faulting. The results of a number of magnetic surveys are described and are correlated with results of drill-hole and mine exploration and developmerit. The magnetic anomalies obtained are discussed in relation to phases of formation of ore within the iron formation. General Information One hundred years ago a party of surveyors, applying the principles of geophysical prospecting, discovered iron ore in the state of Michigan in the Lake Superior district. This event was officially reported as follows:&apos; On Sept. 19 (1844) while running the east line of Town 47 North, Range 27 West, they observed by means of the solar compass remarkable variations in the direction of the needle, amounting to 87" from the normal. Ascribing this phenomenon to iron ore, they sought and found it in ledges or outcrops at several points. The solar compass referred to was invented by William A. Burt, deputy surveyor in charge of this party.2 It is used for determining the true meridian by an observation on the sun. Eight years later, on July 7, 1852, the first iron &apos;re, consisting of 6 bbl. of Ore, was shipped from Marquette, Michigan. It was another 40 years before the first or> shipment left the Mesabi Range in Minnesota, in October 1892. It totaled 4245 tons. Fifty years later, 90 years after the original shipment, during 1942 the Lake Superior district shipped 93,495,392 gross tons of iron ore. Production came from Minnesota, Michigan, Wisconsin, and Ontario, Canada. Throughout the 90-Year period it was known that magnetic properties of most of the ore bodies, and of the iron formations in which they occur, affected the compass. This phenomenon, later to be made use of to outline areas of ground favorable for exploration, was at first a

Jan 1, 1949

By Francis A. Thomson

IN reviewing mineral industry education a year ago, occasion was taken to congratulate the Institute in general and to felicitate the Education Di- vision in particular on "the most gratifying growth which is taking place in Institute consciousness in regard to its responsibility for the recruitment and adequate training of student personnel and for the successful bridging of the difficult gap between graduation and achievement of professional status." Continuation of this growth of interest throughout 1939 is a recognition of the validity of the splendid statement of George Otis Smith that the mining students of today are the ore reserve of the Institute for the future. In this connection one recalls the equally apt expression of another distinguished geologist, George M. Fowler, who, speaking of exploration for ore deposits, says, "The place to look for elephants is where elephants have been found."

Jan 1, 1940

By W. Rostoker, R. P. Elliott, B. W. Levincer

Phase equilibria in the Ti-Cr-Mo system have been investigated for alloys containing 100 to 40 pct Ti in the temperature range 550° to 1300°C. Five experimental isothermal sections and a surface of incipient melting are presented in addition to a summary projection of the space. Seven vertical sections have been constructed from the isothermal sections. A STUDY of the system Ti-Cr-Mo was undertaken as part of a program sponsored by Watertown Arsenal toward the development of titanium-base phase equilibrium diagrams of potential technical importance to alloy development. The scope of the investigation included the composition range contained by the titanium corner and the line of 64 pct Ti (all compositions are by weight) and the temperature range 550" to 1100°C. A surface of incipient melting was constructed from measurements on a large number of alloys. The system Ti-Cr has been established.&apos;-? The phase diagram is characterized by a wide miscibility field of the solid solution at elevated temperatures and a eutectoid reaction of the type: (15 pct Cr) + TiCr, (685C). The a solid solution has a very limited capacity for solution of chromium (< 0.5 pct Cr). The intermediate phase TiCr2 has at best a very narrow composition range. It has been shown that two allotropic modifications of this phase exist. However, this behavior does not appear to be perceptibly reflected in the form of phase boundaries of the type + TiCr,. In the system Ti-Mo,9-10 the phase is stabilized to successively lower temperatures with increasing molybdenum content. There are no known intermediate phases. The a solid solution is limited to less than 0.5 pct Mo. Because of the very extensive range of the phase, the ternary system was ideally suited to the determination of the phase boundaries by the parametric method of Andersen and Jette." A parametric surface was constructed to provide the necessary basis for the application of this method. Preparation and Treatment of Alloys More than 60 alloy compositions were prepared for the study of this system. Alloy buttons of 10 grams were arc-melted in a nonconsumable electrode furnace using inert atmosphere protection and a water-cooled copper crucible. The construction and operation of this type of melting unit have been adequately described elsewhere.&apos;&apos; To insure complete solution of alloy additions, the buttons were remelted alternately on top or bottom as many as five times. This was accomplished by a suitable mechanism for "flipping" over the ingots. Iodide titanium (99.97 pct Ti) was used as the alloy base. An especially high quality chromium (99.9 pct Cr) was obtained from the National Research Corp. Molybdenum sheet (0.005 in.) of 99.9 pct purity was used.

Jan 1, 1954

By Morris Cohen

STAFF: Editor, Gerhard Derge Acting Editor, Paul G. Shewmon Carnegie Institute of Technology Schenley Park Pittsburgh 13, Pa. Editorial Assistant, M. A. Redmerski Production Editor, Otto T. Johnson THE METALLURGICAL SOCIETY: Karl L. Fetters, President; J.S. Smart, Jr., Past-President; R. C. Cole, Vice President; R. L. Hennebach, Treasurer; R. W. Shearman, Secretary. PUBLICATIONS COMMITTEE OF THE METALLURGICAL SOCIETY: W. O. Phil-brook, Chairman; H. L. Bishop, R. C. Cole, J. N. Hobstetter, W. A. Krivsky, E. R. Morgan, F. C. Langenberg, R. E. Lund, Paul Queneau, L. L. Seigle, R. L. Smith, and T. V. Wainwright. Review and selection of manuscripts is under the supervision of the following Publicotions Committes: Extractive Metallurgy Division: R. E. Lund, Chairman; M. E. Wadsworth, Vice Chairman; D. H. Baker, Jr., G. M. Bell, R. E. Grace, W. A. Krivsky, R. A. Lewis, Charles O&apos;Neill, A. W. Schlechten, R. E. Shinkoskey, and W. W. Stephens. Iran and Steel Division: T. V. Wainright, Choirman; H. L. Bishop, R. E. Boni, T. E. Dancy, D. W. Murphy, Johannes M. Uys, J. B. Wogstoff, and R. G. Ward. Institute of Metals Division: J. N. Hobstetter, Chairman; P. A. Beck, J. J. Becker, G. F. Bolling, J. 0. Brittain, J. B. Clark, R. S. Davis, A. E. Dwight, R. W. Fountain, L. R. Girifolco, J. C. Gurland, H. S. Kalish, E. L. Harmon, J. J. Heger, A. A. Hendrickson, L. Himmel, J. P. Hirth, H. H. Johnson, Jr., R. R. Nosh, T. N. Rhodin, R. H. Richman, H. C. Rogers, W. Rostoker, C. Sherby, C. W. Spencer, L. Slifkin, J. K. Stanley, R. Steinitz, H. C. Stumpf, and R. Swalin. Published bimonthly by the Americon Institute of Mining, Metallurgicol, and Petroleum Engineers, Inc., 345 East 47th Street, New York 17, N. Y. Telephone PLaza 2-6800. Subscription $30 peryear for non-AIME members in United States and North, South, and Centrol America; $32, foreign; $30per$7.50 for AlME members. Single copies, $6.00, single copies foreign, $6.50. The AlME is not responsible for any stotement made or opinion expressed in its publications ... Copyright 1962 by the American Institute of Mining, Metallurgical, and Petroleum Engineers, Inc. . . . Registered cable address, AlME New York . . . Indexed in Engineering Index, Industrial Arts Index, and Chemical Abstracts . . . Second class postage paid at New York, N. Y., and Ann Arbor, Mich. Volume 224, Number 4.

Jan 1, 1962

By Nicholas J. Grant, Yoichi Ishida, Arthur W. Mullendore

An inert particle -marker technique was developed to provide a direct measurement of grain boundary sliding during creep in tile interior of aluminum specimens. Groin boundary sliding in the interior as measured by this technique was found to be nearly the same or slightly lower than that measured on the surface. These data disagree with those obtained by the grain-counting technique developed by W. A. Rachinger. In tests where both techniques were used, the grain-counting technique gave large and variable values of grain boundary sliding. It is shown that the grain-counting technique gines erroneozcs results because of a preferred direction of grain growth during creep. A question which has long plagued those who study grain boundary creep is whether or not surface measurements yield a true representation of the deformation in the interior of a specimen. The first attempt to measure grain boundary sliding in the interior of a creep specimen was made by Rachinger.1 His technique is based on the measurement of average grain diameters, both parallel and perpendicular to the tension axis, followed by a calculation of the grain elongation from these measurements. The difference between total elongation, Et, and the calculated grain elongation, Eg, is considered to be the result of grain boundary sliding, Egb. Surprisingly large values of Egb/ Et (90 pct) came out of creep tests of pure aluminum at temperatures above 250°C (480°F), utilizing the Rachinger technique. This value is very much larger than the values of 8 to 15 pct measured by numerous investigators on the surface of a specimen. Values obtained on the surface by Rachinger, however, were consistent with those measured by the displacement of reference scratches. Chaudhuri and Grant2 repeated the Rachinger method for A1-10 pct Zn, and found the same large values of Egb/Et inside the specimen. However, from purely geometrical considerations, grain boundaries cannot slide without grain deformation; therefore, they questioned the validity of Rachinger&apos;s grain-counting method. Several authors2,3 have suggested that grain boundary migration during high-temperature deforma- tion may tend to restore the equiaxed grain shape in order to minimize interfacial energy. Rachinger4 tested this hypothesis and found that it did not hold. Grains elongated by rapid extension retained their elongated shape during a subsequent slow creep test. It appears that some other factor was responsible for the abnormally high values of .Egb/El. McLean and Gifkins5 made a survey of the effect of grain size on the ratio Egb/ Et, and proposed that the high values were the consequence of a small grain size. They failed to explain the low value of Egb/Et which Rachinger observed on the surface of the small grain size specimens, and suggested that the surface effect on the value of Egb/Et does not always occur. Many of the disagreements arising from Rachinger&apos; s work stem from the fact that there was only one method of estimating grain boundary sliding in the interior of a specimen, and that method was of an indirect nature. If a marker line of some sort could be introduced inside of the specimen, one could make measurements just as clearly as on the surface. In the present investigation, the technique utilizes a layer of finely dispersed oxide particles inside the specimen introduced by hot press-bonding of two pieces of aluminum. Rachinger attempted a similar technique but with the oxide distribution he obtained there was so much interference with grain boundary motion that quantitative measurements were not attempted. MATERIALS AND EXPERIMENTAL PROCEDURE A) Materials Preparation. Two pure aluminum rods (impurity content in percent: Si, 0.002; Cu, 0.004; Fe, 0.002; Mg, 0.000: Zn, 0.000; V. 0.001) 1 in. diameter by 2 in. high were jacketed end to end in a 4-in.-diam cylinder of commercial-purity aluminum, 4 in, high, which had a l-in.-diam hole. The l-in.-diam mating surfaces of the two pure aluminum rods had been electropolished initially. This interface provided the oxide-film internal -marker plane after the hot press-bonding process, see Fig. 2. The composite was annealed for 1 hr at 900 F and hot upset more than 50 pct reduction in height in one step. The resulting slab was then rolled to 1/2 in. thickness; the pure aluminum test material was cut out and annealed at 900°F for 1 hr and cold cross-rolled to 1/8 in. thickness. The sheet was machined into specimens with a 1/8-in.-square cross section and a 1/2-in. gage length. The following heat treatment was given the specimens: Specimen 5A series: annealed at 1000°F for 5 min for grain-size control and then cooled to 700°F and held for 15 hr for stabilization.

Jan 1, 1965

By G. D. Cody, D. S. Beers, B. Abeles

The thermal diffusivity (thermal conductivity divided by specific heat) of Armco iron has been measured over the temperature range 30º to 1025ºC. The results are in good agreement with the thermal diffusivity computed from published values of thermal conductivity and specific heat, except near the Curie point and at the a to y phase transition, where the measured diffusivity undergoes rabid variations. The differences observed are ascribed to a rapid variation in the electronic thermal conductivity near the Curie point, and a decrease in the lattice thermal conductivity, at the a to ? phase transition. A major difficulty in measuring the thermal conductivity of materials at high temperatures is the determination and elimination of radiation losses. It has been shown, however, that in measuring thermal diffusivity D (thermal conductivity/specific heat) radiation losses can be taken into account exactly.&apos; In order to test the performance of a newly designed apparatus for measuring thermal diffusivity of solids,&apos; we measured Armco iron to an accuracy of 2 pct in the temperature range 30" to 1025°C. This material was selected since both the thermal conductivity,3&apos;4 k, and specific heat,5 C, are known accurately in this temperature range and thus the measured values of D could be compared with D computed from the pub-

Jan 1, 1962

By S. T. Wlodek

The surface and subscale oxidation reactions were followed by means of continuous weight-gain and metallographic techniques over the range 1600" to 2200°F (871° to 1204 °C) for up to 400 hr. Full identification of all scale and subscale reaction products was obtained by electron and X-ray diffraction. At or below 1800°F (982°C) a linear rate of reaction (QL = 46.0 kcal per mole) governed the oxidation process, extending for up to 100 hr at 1600°F (871 "C). During linear oxidation the surface scale consisted of an amorphous SiO2 film overgrown with Cr 2O 3 and NiCr204. This initial linear process was followed, and above 1800°F completely replaced, by two successive parabolic rate laws (Qp = 60 and 57 kcal per mole). This parabolic reaction involved the formation of a complex scale consisting of Cr2 O3 and smaller amounts of NiCr2O4. Parabolic oxidation appeared to coincide with the disruplion of the silica film present during linear oxidation and was followed by subscale (internal) oxidation of crystobalite and NiCr2O4. The balance between the subscale and surface oxidation reactions controls the oxidation of this commercial alloy. The amorphous silica film appears to result in the linear rate and diffusion through Cr2O3 is the more likely rate-limiting step during parabolic oxidation. THE oxidation of a multicomponent composition is a complex phenomenon not presently amenable to a rigorous classical interpretation. Nevertheless, even a qualitative understanding of the scaling and subscale reactions that occur in a commercial composition can illuminate the reactions that limit its high-temperature stability in an oxidizing environment. This study of the oxidation of Hastelloy Alloy X presents the first of a series of studies with the above approach in mind. Hastelloy X exhibits one of the best combinations of strength and oxidation resistance available in a wrought, solution-strengthened, nickel-base alloy. Although during long time exposure some precipitation of M6C and M23C8 carbides as well as a complex Laves phase occurs, the amounts are probably small enough to have no appreciable effect on the chemistry of the matrix. Radavich has identified the oxidation products on Hastelloy X oxidized for 5 min to 10 hr at 1115°F as NiO and the NiCr2O4 spinel. Oxidation for 5 to 15 min at 1500°F produced a scale of spinel, NiO, and a rhombohedra1 phase, probably Cr2Os. Sannier et 2. have reported continuous weight-gain data for Hastelloy X at 1650" and 2010°F and internal-oxidation measurements after 150 hr at 2010°F. In addition, much of the data on binary Ni-Cr alloys recently reviewed by Kubaschewski and okins&apos; and Ignatov and Shamgunova4 as well as studies of binary Ni-Mo alloys5 are also pertinent to the oxidation of this composition. EXPERIMENTAL Continuous weight-gain measurements and metallographic measurements of subscale reactions were the main experimental techniques used in this study. X-ray and electron diffraction backed up by a limited amount of electron-microprobe analysis served to characterize the nature of the scale- and subscale-reaction products. Two heats of commercial sheet of the composition given in Table I and identified as A and B were used in the bulk of this study. Internal-oxidation measurements were made on a third heat of material in the form of a 0.5-in.-diam bar. In order to assure homogeneity, all heats were reannealed 4 hr at 2175°F prior to sample preparation. weight-Gain Measurement. All specimens (1.5 by 0.4 by 0.03 in.) were abraded through 600 paper, electropolished, and lightly etched in an alcohol-10 pct HCl solution. An electrolyte of 150 cu cm H,O, 500 cu cm HsPO4 (85 pct conc), and 3 g CrO3 at a current density of 0.9 amp per sq cm or a solution of 10 pct HaW4 in alcohol used at 4 v and 0.3 amp per sq cm was used for electropolishing. The resultant surface exhibited a finish of 3 ± 1 p rms. Continuous weight-gain tests were made at 1600°, 1700°, 1800°, 1900°, 2000", and 2200°F on auer&apos; type balances capable of recording a total weight change of 110 mg with an accuracy of k0.1 mg. All tests were made in air dried to a dew point of -70°F and metered into the 2-in.-diam reaction

Jan 1, 1964

By J. F. Enrietto

It is shown that one cannot approximate the broad internal friction Peaks observed in the Fe-Mn-N system as the sum of a number of subsidiary Peaks and still vetain the concept of a single relaxation time. Furthermore, the approximation of manganese affectirg only nearest neighbor interstitial sites is shown to be incompatible with the experimental results. The results of this experiment show that the influence of manganese in the ferrite lattice extends over 3 to 4 atomic distances. NUMEROUS experiments have shown that the presence of relatively small amounts of substitutional alloying elements can profoundly affect the profile of the damping spectrum in the vicinity of the Snoek peak in bee metals.1-7 Dijkstra and Sladekl observed this phenomenon in Fe-Mn-N alloys where it appeared as a broadening and shifting of the Snoek peak to higher temperatures. The authors interpreted this as being the result of a superposition of two damping maxima—the normal Snoek peak, located at its usual position and having a normal half-width, and an interaction peak having a normal half-width, but occurring at a somewhat higher temperature. They prclposed that the interaction peak was caused by nitrogen atoms jumping from Fe-Mn sites to Fe-Fe sites, the Fe-Mn interstitial sites having one manganese and one iron atom as nearest neighbors, and the Fe-Fe sites having two iron atoms as nearest neighbors. They further suggested that the Fe-Mn sites had a lower energy than the normal Fe-Fe sites because of the presence of the adjacent manganese atoms. From the relative heights of the two postulated damping peaks, the dif-

Jan 1, 1962

By FRANK RIEBERS

IN DISCUSSING the selection of a geophysical method, much of what the writer will say is applicable to any of the various methods and to their use in prospecting, whether for oil or for other minerals. Specifically, the writer&apos;s subject is the problem, particularly pressing on the Pacific Coast, of checking the rising cost of the discovery of new fields by the proper employment of geophysical methods. Table I was prepared from statistics published by the California State Milling Bureau. The writer selected five of the largest a:ld most active companies operating in California, segregated the number of wild-

Jan 1, 1930

By C. M. Wayman, J. F. Breedis

The crystallography of the martensitic transformation in the Fe-30 Ni alloy was reinvestigated. The scatter in the habit Plane as determined from measurements on the mid-rib plane was smaller than reported previously, and the orientation relationship was determined from a martensite plate having known direction cosines. From agreement with crystallographic theory and from observations of the morphnlogy of the martensite plates, it is suggested that the mid-rib plane represents the starting region of the transformation. THE crystallography of the martensitic transformation in the iron-nickel system has been the subject of many investigations.&apos;-7 However, for iron alloys containing approximately 30 wt pct Ni, a wide scatter in the reported habit planes exists. In only one instance has a Laue determination of the orientation relationship been made, but the habit plane of the martensite plate studied was not determined experimentally. Because the most successful thermodynamic and kinetic analyses8 of the martensite transformation have been based on Fe-30 Ni alloys, it was considered desirable to reinvestigate the crystallographic features of the transformation in this alloy. Lieberman9 suggested that the most significant information for use in a theoretical treatment involves the determination of all the crystallographic observables from a single plate of the product phase. This was first done in essence by Greninger and Troiano10 for Fe-22 wt pct Ni-0.8 wt pct C, and is the method followed in this investigation. Some theoretical approaches11-13 in describing the martensitic transformation consider the overall transformation distortion to be comprised of a Bain distortion, or lattice deformation (PI, which produces the structure change, and a lattice invariant deformation (G), such as twinning, which together leave the interface or habit plane un-distorted. The incorporation of a rigid body rotation (R) results in a transformation distortion (E) such that the interface plane is left both undistorted and unrotated. In matrix notation, E = RPG where the lattice invariant deformation has "taken place" in the austenite. Bowles and Mackenzie14-16 in formulating a theoretical approach proposed an adjustable scaler quantity, denoted as 6, which represents a uniform dilation in the interface plane. This dilation acts to adjust the lattice spacings of the parent and product structures at the plane of contact. Using the dilation parameter as a variable, these authors were able to account for a continuous variation of habit planes in steels along a curve in the stereogram between {225}A and {259}A. she invariant line strain14 of the transformation is 6 RP, and the corresponding transformation distortion is E/6.) With the dilation parameter known, the invariant line is computed as the triple coincidence of the habit plane, the shear plane of the lattice invariant deformation, and the initial Bain cone.14 The contraction axis for the Bain distortion can be taken9&apos;17 as [010]A, and the correct permutation of the habit plane indices used. Kelly and Nutting 18 have established the shear plane (of twinning) in the tetragonal martensite of Fe-22 Ni-0.8C to be {112)M by means of transmission electron microscopy. The reasonable shear system is then {112}M which is equivalent to {011}A <01l>A. The as-

Jan 1, 1962