By Djona M. Gaballah I.

Selective chlorination of unroasted and roasted spent hydrorefming catalysts was studied between 300 and 600°C using the following gas mixtures : C12+CO, C12+N2 and CI2+air. Such materials contain Co, Ni and Mo compounds supported by alumina and/ or silica. They also contain variable amounts of V compounds, C, S, etc., accumulated during the life time of the catalyst. Direct oxychlorination of the C+S rich sample allows higher extraction rates than those obtained by the carbochlorination of the same roasted one. It seems that the roasting step doesn't favor the economic metals' recovery. Results of the chlorination of C+S poor spent catalysts, in the presence of CO, in the chlorinating gas mixture, or of carbon added to the sample, were comparable. Cobalt and nickel chlorides were .extracted from the chlorination residues by their dissolution with acidified water, whereas molybdenum and vanadium chlorinated compounds were recovered by selective condensation from the vapor phase. The recovery rates of valuable metals as well as the selectivity were higher for the chlorination of spent catalysts than results obtained by the hydrometallurgical processing of the same sample. Results of the scale-up of the oxychlorination of the unroasted sample confirmed those of the laboratory scale. The global recovery rates were about 88 pct of cobalt, 93 pct of molybdenum and 76 pct of vanadium. The carbochlorination was applied to the recovery of W and Ti from Denox catalyst that is a carbon and sulfur free one. Recovery rates higher than 99 pct at temperatures lower than 500 °C could be obtained. This may indicate that the chlorination process can be applied to the treatment of various industrial wastes or by-product containing transition and/or refractory metal compounds A flow - sheet for the pretreatment of these materials is proposed.

Jan 1, 1995

By F. F. Lins

There is a large use of mercury in Brazil by the gold miners in the so called "garimpos" (non registered mining operations), where it is usual to recover the gold contained in the gravity concentrates by amalgamation, which is highly deleterious to environment if not conducted properly. Unfortunately, this is a common practice there. After presenting in brief the modus operandi generally practiced in the garimpos and the environmental problems, this work reviews some of the research conducted in CETEM according to two approaches: (i) replace amalgamation by other processes and (ii) develop technology to treat mercury-contaminated soils and effluents. Conventional processes like froth flotation, to recover gold from gravity concentrates, and centrifuges were considered. Also as alternatives to amalgamation, innovative process like the recovery of gold by coal-oil agglomerates and a technology that is currently under development in our laboratory, called gold-paraffin process, are described in brief, some results presented and their potential use assessed. To reclaim sites already polluted a technology was developed to float mercury selectively from contaminated soils. The potential use of centrifuges to pre-concentrate the mercury is also discussed. The scope for applying the last techniques is to concentrate the pollutants in a small volume of mass which would be suitable for recycling or isolation from the environment. A prospective technology to treat contaminated soils, or mercury concentrates, is the immobilization of mercury by adding inorganics. Concerning the ionic mercury which may be present in effluents, precipitation of the ions and flotation of the precipitates are being studied.

Jan 1, 1994

By Zuhair A. Munir

"The use of self-propagating combustion reactions to synthesize metallic, ceramic, and composite materials is described. The limitation of this process because of the porous nature of its products is discussed. The formation of dense bodies through the simultaneous application of pressure is shown for a metal-matrix composite. The effect of an external electric field on the synthesis of ceramic and composites is described. The nature of the effect of the field on the mechanism of synthesis is analyzed theoretically and experimentally. The use of the self-propagating combustion to synthesize intermetallic thin films is presented for the Ni-Al and Ti-Al cases. The formation of functionally gradient materials (FGM) by centrifugally-assisted self-propagating high-temperature synthesis is described.IntroductionThe use of self-propagating combustion reactions for the synthesis of a large number of simple and complex materials has been described in numerous publications. These have been amply discussed in several review articles [1-4]. The many benefits of this method of materials synthesis are commonly examined in light of its most significant limitation: the porous nature of its products. The porosity in the products of self-propagating high-temperature synthesis (SHS) is an intrinsic characteristic of the process and its elimination has been the focus of numerous attempts. Various experimental methods have been used to accomplish this goal."

Jan 1, 1994

By Wenzhou Yu, Cong Zhang, Wenhui Ma, Gang Wang, Kuixian Wei

"A novel technique was successfully developed for nickel further purification by vacuum directional solidification. The removal effect of impurities in nickel was studied based on theoretical analysis and experiments. High removal efficiency of impurities in nickel can be realized according to theoretical analysis. The experimental results show that the vacuum directional solidification treatment could increase the nickel purity from 99.96% to 99.996%. Since vacuum directional solidification could effectively remove the impurities from nickel with low contamination and low cost, it is a potential route to obtain high-purity nickel for commercial application.IntroductionNickel is widely used in metallurgy, machinery, petroleum industry, chemical industry, construction industry, light industry, and other industries for its ductility, medium hardness, ferromagnetism and high chemical activity. Nickel-based alloy is an important material for the key parts of aircraft, tanks, submarines, radars, nuclear reactors and aerospace fields [1-5]. Generally, nickel contains Si, P, S, Fe, Cu, Zn, As, Cd, Sn, Sb, Pb, Bi, Al, Mn, Mg and other impurity elements, which may hinder the commercial application of nickel. Therefore, it is necessary to refine the crude nickel for the high purity nickel."

Jan 1, 2014

By Rainer Schmid-Fetzer

"Isothermal solidification can be used to form strong bonds at low temperature which remain solid at much higher temperatures. The exploitation of this principally known technique for new high temperature processing steps and applications in electronic assemblies is the aim of this study. Three basically different variants of this bonding process are given. A comprehensive metallurgical screening is performed and the feasibility of binary material systems is given on a quantitative scale. Very attractive systems are spotted that have never been studied before. Detailed examples for the realization of bonding with complex ternary and multilayer systems are given. A highly innovative example is the chip stack or wafer to wafer bonding of unmetallized Si or SiC at 250°C. The proposed bond remains stable above the melting point of Si and enables entirely new semiconductor manufacturing steps. An improved die bonding process was proposed and verified experimentally.1. IntroductionIsothermal solidification can be applied to form strong bonds at relatively low temperature which remain solid at higher temperatures. The general principle of this type of joining processes is illustrated in Fig. 1. An interlayer of a low melting component, Lo, is provided as a foil or a thin film coating between the high melting joint components, Hi. The assembly is heated under moderate pressure to the bonding temperature, T 8 , and a liquid filler forms, either because the melting point of Lo is exceeded or due to a eutectic reaction between Lo and Hi. This molten filler initiates a rapid interdiffusion or reaction diffusion between Lo and Hi and the subsequent approach to an equilibrium state results in isothermal solidification. The solid phases formed at T 8 in the joint region exhibit a remelt temperature above T8 •"

Jan 1, 1996

By J. Wong

We report a successful use of x-ray absorption spectroscopy to probe the chemical and structural environment of trace elements in coal. When applied to vanadium in coal, it was found that vanadium exists in at least two environments: a trivalent site 6-fold coordinated by oxygens at ca. 2.0~ and a tetravalent site 5-or 6-fold coordinated also by oxygens, one of which forms a short V=O bond at ca. 1.6a. No evidence of nitrogen (porphyrin)1'or sulfide environment was found. It was also found that the vanadium environ-ments in the raw coal did not survive unchanged in a liquefaction process. These findings have implications for coal cleaning processes and for trace element release into liquefaction process streams.

Jan 1, 1982

By E. vanHuyssteen

A method of establishing the relationship between the mineralogy of a sinter and its subsequent processing behaviour in a lead blast furnace is demonstrated. It involves: 1) analyzing the Zn-spinels, hardystonite, larsenite, Pb-silicates, Pb-arsenates, Pb-(Ca)-sulphates and other femtes with an electron microprobe; 2) determining the extent of elemental substitutions in various mineral structures; 3) establishing a sequence in which the various phases formed during sintering. In this manner the relationship between the bulk chemistry of a sinter formulation and the speciation of elements into various phases in the sinter can be established. Specifically, the-substitution of Mg for Zn in hardystonite significantly influences sinter production. Mg substitution releases Zn into the surrounding matrix. This Zn reacts with the Pb-silicate to form larsenite thereby reducing the amount of Pb-silicate available for anhydrite digestion. Excessive amounts of residual anhydrite thus result if the sinter formulation is based solely on the CaO/Si& ratio.

Jan 1, 1993

By M. C. Furerstenau

Adsorption behavior of various surfactants on sulfide minerals is very much affected by the nature of the surface of the mineral. Since sulfides are naturally meta-stable, oxidation occurs when they are exposed to air, especially in aqueous environments. As a result. oxygen assumes a major role in sulfide flotation. Mechanisms of adsorption of various thiol collectors on sulfide minerals have been reviewed. The electrochemical behavior of various sulfide minerals has also been reviewed. Flotation behavior of galena, chalcocite, sphalerite, pyrite, chalcopyrite and pentlandite has been presented together with the. flotation of copper sulfide- nickel sulfide ore.

Jan 1, 1993

By W. Kunda

A laboratory study was carried out on the treatment of sulphidic copper concentrates in aqueous chloride systems under elevated temperatures and oxygen overpressure. Exploratory tests showed that chalcopyriteoxidizes with various chloride salts to form, depending upon the pH of the system, soluble copper chloride or insoluble copper oxychloride salts; the copper can then readily be recovered from the solution or residues respectively. During the leaching, iron was oxidized to iron oxide and remained in the leach residue while the bulk of the sulphide sulphur was oxidized to the elemental form with a minor portion oxidized further to sulphate. The presence of metal chloride salts in the system increased the oxidation rates of chalcopyrite and depressed the solubilization of iron in the system. A systematic oxidation leach study carried out in (1) ammonium chloride and (2) sodium chloride systems showed that the former system required little or no HC1 addition while the latter required 2 mol of HC1 per mol of dissolved copper (plus zinc). The copper was recovered from the cuprous or cupric chloride leach solutions by cementation with iron. Extractions of 99% copper and zinc, 97% silver, and negligible iron were obtained. Sulphur was oxidized to the elemental or sulphate form; the relative proportions of the total sulphur were 60 and 30% for system (1) and 80 and 10% for system (2). A flowsheet for a conceptual process with minimal reagent requirements was proposed.

Jan 1, 1976

By Tom Lewis

The metal finishing and electronic industries are searching for ways to recycle materials · and reduce costs. The areas of heavy metal waste and water recycling has gained new interests with the potential of impacting the operation's bottom line. Lewis Environmental Services, Inc. has completed numerous heavy metal recovery and effluent recycling projects with its ENVIRO-CLEAN PROCESS for government and private sector clients. This patented process utilizes a proprietary chemically treated granular activated carbon with enhanced heavy metal adsorption capabilities combined with electrolytic metal recovery to produce a saleable metallic product. The process generates no sludge or hazardous waste and the effluent meets EPA .limits. This paper covers several heavy metal removal projects, two fullcscale commercial installations, and one treatability case study.

Jan 1, 2000

By J. Méndez-Nonell

The thermodynamic and chemical properties of SrSO4 and SrS in a gaseous flow of CO and CO2 at high temperature are discussed. The thermodynamic analysis of the system was made using data from the literature. The results obtained from the thermodynamic analysis were experimentally verified using the thermogravimetric technique. The experimental results suggest the formation of a complex compound between SrO and SrSO4. It was also found a change in the chemical mechanism of the process between SrSO4 and CO-CO2 and in the chemical mechanism of the process between SrS and pure CO2.

Jan 1, 1995

By K. Robinson

Following the longest Smelter campaign in BCL?s history it was planned to completely rebuild the flash smelting furnace in 1987. This was the fourth major overhaul and the most extensive so far attempted. Detailed planning took place over several year$ preceding the shutdown and implementation was completed in 54 days. The key to minimising shutdown time was the method designed for installation of the new uptake shaft and reaction shaft. Major repair work was also undertaken in the waste heat boiler and electric furnaces. Both of these activities had an impact on the critical path of the flash smelting furnace overhaul.

Jan 1, 1993

By S. Suda

Hydrogen storage materials have been investigated for more than 30 years, particularly on metal hydrides. These materials are, however, considered today impractical because of their poor hydrogen capacity measured by mass density and their poor surface properties and characteristics against impurities. Recent R&D activities have been located in new categories of materials such as complex hydrides and chemical hydrides. Among these materials, NaAlH4 (one of alanates), Li-based complex hydride, and NaBH4 (SBH: sodium borohydride) are 3 major candidates as hydrogen storage materials. In the presentation, SBH as a non-reversible on-site but recyclable off-site is described in view of its practical availability as the source of H- (protide) applied for a new type of fuel cell named Direct Borohydride Fuel Cell (DBFC) and H2 (hydrogen) for Proton Exchange Membrane Fuel Cell (PEMFC).

Jan 1, 2006

By Hans von Michaelis

There has been a renaissance in gold and silver extraction and recovery that has taken place over the last fifteen years, since the price of gold was freed from the $3510~ level. Despite major advances in such areas as carbon adsorption processes for gold recovery, refractory gold ore treatment, crushing and grinding, process control, etc., there still remain several gold and silver mineral processing frontiers. Frontiers related to environmental management present significant challenges especially in the USA. More than ever it is appropriate to optimize total economics by adopting a "systems approach" that integrates mining, mineral processing and environmental management.

Jan 1, 1993

By Shengqi Chen

The reduction smelting of nickel laterites produces slag, consisting principally of the chemical components MgO, "FeO", SiO2, and A12O3, and ferro-nickel alloy. Despite the fact that the phase equilibria for the ternary MgO-"FeO"-SiO2 up to 1500°C is well established limited experimental data are available in the MgO-"FeO"-SiO2-Al2O3 system, which is relevant to commercial operation of the process. A methodology has been developed for the experimental investigation of the liquidus temperatures for the multi-component system MgO-"FeO"-SiO2-Al2O3-Cr2O3 in equilibrium with metallic iron. Experiments have been carried out using high temperature equilibration, quenching, followed by electron probe X-ray microanalysis (EPMA). Liquidus temperatures have been determined in the silica primary phase field in the composition ranges directly relevant to the Cerro Matoso S.A. ferro-nickel smelting slag. Liquidus isotherms have been determined for temperatures between 1450 to 1600°C. The study enables the liquidus to be described for a range of MgO/FeO ratios. It was found that liquidus temperatures in the silica primary phase field decrease significantly with the addition of AI2O3. Keywords: Liquidus temperature, ferro-nickel, pyrometallurgy, smelting

Jan 1, 2004

By Darrin Wikoff

"The data, compiled by the Department of Energy (DOE), indicates that the average industrial plant could reduce its total energy cost by 14.8% by implementing effective Life Cycle Asset Management processes. The actual savings varies by industrial classification, but in all cases the potential is substantial and could have a marked impact on the operating profit of the company.Improvements geared towards improving equipment reliability have distinctive linkages to environmental performance, such as reducing the amount of product and raw material waste through routine monitoring of system parameters through predictive technologies, and preventing interruptions to production cycles with a focus on Overall Equipment Effectiveness (OEE).Alcoa successfully reduced solvent disposal costs by more than 40% and GE reduced greenhouse gas emissions by more than 250,000 metric tons. This presentation will show you how companies have successfully reduced energy and disposal costs through a focused effort on manufacturing process reliability.IntroductionSmelter in the ParkThe quaint town of Portland, Victoria protrudes outward towards Antarctica from Australia’s southeastern coastline. Portland is a quiet rural community surrounded by agriculture that draws tourists by the thousands to the southernmost edge of Victoria by way of breathtaking cliff top views of the majestic Southern Ocean, the intrigue of shipwreck coves along the Great Ocean Road, and what most will call the eighth wonder of the modern world, the “Smelter in the Park”. Integrated within Portland’s beautiful landscape is a 356,000 ton/year aluminum smelter that stands as a symbol of collaboration between nature and industry. Nestled atop a ridge which faces “Sail Rock”, a popular destination of local and visiting fisherman, the smelter is engulfed in a mix of brush and wetland preserves that are home to many of Australia’s feathered and fourlegged natives. Also within its interior you’ll find parks and natural landscapes abundant where man and machines coexist with the native inhabitants."

Jan 1, 2009

By Makoto Ohtsuka

The ternary Ni2MnGa intermetallic compound is an intelligent material which has both a ferromagnetic property and a shape memory effect (SMB), The use of the shape memory alloy films for an actuator of micro-machines is very attractive because of its large recovery force, The purpose of the present study is to investigate the effects of fabrication conditions and to clarify the relationships between these properties and fabrication conditions of the Ni-Mn-Ga films, The Ni-Mn-Ga films with a thickness of nearly 5 um were deposited with a radio-frequency magnetron sputtering apparatus using a NisoMn2sGa25 or Nis2Mn24Ga24 target. They were heat-treated at various temperatures between 873 and 1273 K for homogenization and ordering and then cooled in a furnace, The composition of the films depended on the sputtering power. The as-deposited films were crystalline and had columnar grains, After the heat treatment the grains widened and the grain boundary became indistinct with the increasing heat treatment temperature, The martcnsitie transformation temperature of the heat-treated films increased with increasing nickel content. Furthermore the effect of plastic deformation and constraint aging on SME is also investigated, After plastic deformation, the two-way SME was shown through the martensitie transformation and its reversion, The intensity of X-ray diffraction peaks from stress-induced martensitie phase was found, The constraint-aged films also showed the two-way 5MB by thermal cycling,

Jan 1, 2003

Microstructural investigation has shown that grain splitting or deformation banding ( DB ) develops progressively with increasing strains during cold rolling. Of particular significance to simulating texture development in cold rolled BCC polycrystals is the operation of higher order slip systems other than 110 and, the occurrence of DB in the rolling plane since the latter allows a new relaxation of the shears. Deformation banding ( DB ) model includes grain subdivision in the rolling plane and applies the Relaxed Constraints ( RC ) mechanism for the other shears. An energy criterion for deciding whether deformation banding occurs or not has been postulated, referred to as Deformation Banding Criterion ( DBC ). This paper reports the results of the investigations into the effects of different slip systems, i.e., those based on 110, 112 and 123 slip planes and their combinations using RC, DB and DBC models, in developing simulated BCC rolling textures.

Jan 1, 1999

By M. Friák, L. G. Wang, M. Šob, V. Vitek

"The paper gives an account of applications of quantum-mechanical (first-principles) electronic structure calculations to the problem of theoretical tensile strength in metals and intermetallics. First, we briefly describe the way of simulating the tensile test and the electronic structure calculational method. Our approach is then illustrated on calculations of theoretical tensile strength in W, NiAl and transition metal disilicides MoSi2 and WSi2 with C11b structure. In Wand NiAl, we consider uniaxial tension along [001] and [111] directions. Although tungsten is elastically nearly isotropic (C44 = C”), theoretical tensile strength exhibits a marked anisotropy (oth/001 = 29 GPa, o'th/111 = 40 GPa). Calculated results compare favorably with experimental value of 24.7±3.6 GPa obtained for tungsten whiskers grown along the [110] direction. Similarly, in NiAl, the 'hard' orientation [001] differs very significantly from the [ill] orientation (oth/001 = 46 GPa, oth/111 = 25 GPa). This anisotropy is explained in terms of higher-symmetry structures present or absent on the calculated deformation paths. In disilicides, the theoretical strength is calculated for [001] loading (oth/001 = 37 GPa and 38 GPa for MoSi2 and WSi2 , respectively). The role of relaxation of internal structure parameter is discussed and changes in bonding conditions during the tensile test are analyzed.IntroductionIn most engineering applications, the strength of materials is limited by the presence of internal defects. If there were no defects, then, for example, the tensile strength could be several orders of magnitude higher and its value would be comparable with that of shear modulus. Therefore, the strength of ideal (defect-free) crystal represents an upper limit of attainable stresses, which is called the ideal strength. While it may not be possible to achieve the ideal strength in practice, it is not possible to exceed it. However, the ideal strength is already approached in situations which are technologically relevant. These include the low-temperature deformation of inherently strong materials, such as diamond, Si, Ge and some of the transition-metal carbonitrides, deformation of whiskers, nanoindentation of materials with low defect densities, hardened thin films and coatings etc. The ideal strength sets the limits of elastic stability of a solid. Its knowledge is useful for estimation of the ideal work of fracture stresses needed for homogeneous nucleation of dislocations and for modelling of crack propagation."

Jan 1, 2001

By Hideki Minoura

"Two novel electrochemical techniques for the preparation of highly crystallized CdS film have been presented. One is cathodization of a conductive substrate in an acidic chemical bath containing cadmium salt and thioacetamide, where electroreduction of proton at small current densities induces a growth of highly crystallized CdS thin films, whose growth is not disturbed by the reactions in the solution phase. The other technique is electoreduction of aqueous Cd2+— SCN complex. An advantage of this technique lies in no formation of solid particles in the bulk, of the bath.IntroductionIn recent years much attention has been paid to materials preparation by solution processing because of its advantages in lowering the cost as well as the stress to the environment, as compared to the conventional gas phase techniques which unavoidably require high temperature and/or vacuum. We have been trying to explore novel techniques for preparing functionalized compound semiconductors by aqueous solution process. Semiconductors which we have been mainly focusing on are CdS and ZnO, which are important semiconductors finding applications in various devices. In the present paper, some of the techniques that we have recently established for the preparation of highly crystallized CdS will be presented.Methods of the CdS film processing in solution phase (wet process), which have been reported so far can be divided into two major groups; one is chemical bath deposition (CBD) in alkaline solution containing Cd2+ and thiourea 1)4) and the other is electrodeposition (ED) in acidic solution containing Cd2+ and thiosulfate ions - 5)-8) or organic solutions containing dissolved sulfur 9)-11)."

Jan 1, 2000