By Ray Y. Lin, Randall A. Blue

"Joining of silicon carbide with infrared using a mixture of Si-30wt.%C as the brazing material has been investigated. Joining was performed at a temperature of 1500 °C in a flowing argon atmosphere for processing times ranging from 5 to 60 seconds. The joining filler materials include thin film silicon obtained by thinning down silicon wafers to about 70 /!m and graphite powder of a 15 /!m average particle size. Joint strengths were determined with a specially designed shear-in-compression jig for testing shear strengths of brittle materials. Cross section examinations of the joined specimens with optical microscopy, scanning electron microscopy and transmission electron microscopy have shown that all joints are essentially void free with excellent wetting between the base SiC and the brazing material. Silicon carbide in the B form has been identified as the reaction product in the joining zone with a transmission electron microscope (TEM) and selected area diffiaction (SAD) analysis. At 1500 °C with a joining time of 60 seconds, the joint has consisted of primarily SiC. With such a high SiC content in the joint, the joint strength is comparable to those by other joining techniques, such as diffusion bonding, as reported in the literature. A kinetic model for the formation of SiC from liquid silicon and carbon is proposed to explain the observed joint microstructural evolution.IntroductionSilicon carbide is of great interest for high temperature structural applications because of its excellent high temperature strength, wear resistance and anticorrosive characteristics [1]. Even though the interest in SiC is high, the use of the material has been limited by the high cost and difficulties involved in forming components of complicated shapes [2]. It is these limitations that necessitate the development of effective joining techniques that are cost effective and able to provide strong joints."

Jan 1, 1996

By Merete Tangstad, Gabriella Tranell, Jeff Kline

"Raman spectroscopy as an instrumental technique for the determination of silicate structure is widely accepted. This method was utilized for analysis of structural modifications associated with the addition of network modifying species. Silicate melts are described by the extent of oxygen bridging. Therefore, understanding the effect different oxides have on modifying the silicate structure will provide valuable information regarding the removal of boron from silicon in slag refining processes. Samples ranging from CaO/SiO2 = 0.56-1.2 were evaluated with and without varying concentrations of B2O3. The addition of CaO to SiO2 revealed Q2 species constitute 45% of the Qn species and addition of B2O3 to the high concentration CaO system results in an increase in Q2 and a decrease in Q0 . The disappearance of the Raman band associated to the three-member ring in the low concentrated CaO system indicates boron addition and destruction of the ring.IntroductionExtensive studies on the structure of silicate systems have been performed using Raman spectroscopy with consensus on the Raman shift associated with different bridging oxygen units [1]. Most of these studies are motivated by the lack of a fundamental understanding of the processes involved in petrology. Due to this, an opportunity exists to build on the knowledge obtained from these studies and conduct more research on slag structures relevant to industrial applications, as these systems are often compositionally similar to magmatic melts. Raman spectroscopic studies of industrial slags will provide insight into the possible structural modifications necessary to enhance removal of impurity species from the metal phase to the slag phase."

Jan 1, 2012

By Vojteh Leskov?ek

The tribological load is the load on forging tools resulting from the relative motions between the plastically deformed workpiece and the die. In comparison to many other forming processes hot die forging has an especially disadvantageous tribological system. The advantages of the application of hard coatings, which are well known for cutting tools, are to a much lesser extent explored for casting, extrusion, molding and forging tools. Increasing the lifetime of these tools is an important task in surface engineering because of the complex loading conditions and often complicated tool geometry. The plasma-assisted chemical-vapor-deposition (PACVD) technique is well suited to depositing hard coatings onto large dies and molds. The aim of this study is to present and discus results obtained on a duplex PACVD hard coating in an industrial application like the hot forging of automotive parts. A new generation of vacuum-melted and remelted (VMR) hot-work tool steels has been developed; these can reach a hardness of 58 HRc, and have a fracture toughness at this hardness equivalent to that of standard hot-work tool steels at 45 HRc. This offers one of two advantages: the steels can be used at the higher hardness to provide resistance to wear or deformation, or, when used at a hardness of 47?49 HRc for hot forging, to provide temper resistance, nitriding behavior and adhesive wear resistance. The results presented here are from a preliminary investigation. The experimental results indicate that the introduction of a proper duplex PACVD hard coating will lead to an improved wear resistance and a longer lifetime for the hot-forging dies. Furthermore, by using a hard, low-friction coating excellent anti-sticking properties can be obtained. At this stage of the investigation it is also necessary to carry out pilot trials to determine the wear resistance and the tool life in practice.

Jan 1, 2006

By Chris Doyle

From 1997-2000. PT INCO undertook the Fourth Line Expansion Project (FLEX) to increase annual production rates from 90-100 to 150 Mlbs Ni/year (68,000 MT Ni/yr). In 2003, PT INCO nickel production underwent a major sustainable step jump that finally exceeded the targeted rate. This paper presents the changes that led to this achievement. The focus of mining changed. Improving Ni grade was important but only if electric furnace feed met target chemistry so that on-specification slag could be produced. The intensity of diamond core drilling for exploration was dramatically upgraded, mine planning strategy was totally re- vamped and an ore chemistry quality assurance team was formed. In the processing plant, measurement systems were upgraded for better control. Teamwork between sections vastly improved. The final step jump in production occurred when the fifth hydro-electric power generator was added to the furnace grid to allow the power-starved furnaces to cruise in operation at 70+ MW. Keywords: Free cash flow, Ore Chemistry, Measure, Control, Improve

Jan 1, 2004

By Michael A. Markowitz, Alok Singh

"Molecular self-assembly of phospholipids and other amphipathic molecules offers a versatile approach to form self-organized microstructures in various morphologies. Stabilization of microstructures in specific morphologies by polymerization renders them useful for practical applications in areas ranging from controlled release technology to template mediated synthesis of metals. Our efforts are focussed on the development of polymerizable biomembranes derived from phospholipids, their properties and utility e.g., as stable templates for studying chemistry at the lipid interface. Polymerized vesicles formed from mixtures of 1,2-bis(tricosa-1 O,12-diynoyl)-sn-glycero-3-phosphocholine, 1, with corresponding lipids having phosphohydroxyethanol,2, or -hydroxypropanol,3, headgroups have been used in electroless metal plating of vesicle surface with gold utilizing selective binding of Pd(NH3)4 2 + to 2 or 3. The surface bound palladium ion served as catalyst for metalization. Metalization of polymerized vesicles constructed from charge neutral diacetylenic phosphocholine,1, did not occur using this process. The headgroup structure of the negatively charged phospholipids and the degree of vesicle polymerization had an effect on the stability of the vesicles after metalization. Vesicles formed from a mixture of 1 with polymerizable diacetylenic phosphatidic acid, nonpolymerizable 1,2- dipalmitoyl phosphohydroxyethanol or 1,2-diacyl phosphohydroxyethanol (from soy lecithin) were not stable to metalization process. The metal coating of the vesicles was examined by electron diffraction and revealed that the gold metal on vesicles was polycrystalline and face centered cubic. The results demonstrate the utility of polymerized synthetic membranes as template for easy and efficient synthesis of nanoparticles. IntroductionPhospholipids, synthetic or natural, provide a simple and straight forward route to construct membranes in a variety of morphologies due to their inherent property of selforganization in the presence of water[1]. Vesicles are closed spherical structures comprised of concentric walls made from lipid bilayers. Vesicles are morphologically simple structures with enormous technological potential. Polymerizable phospholipids prepared by incorporating a polymerizable group in the molecules demonstrate physical properties comparable to their non-polymerizable counterparts and have the added virtue of providing enhanced physical and chemical stability to the membranes[2,3]. The size, shape and properties of the organized assemblies are dependent on the lipid structure and the nature of the aqueous environment[4,5]. The headgroup geometry, surface charge density, and spatial arrangement of the phospholipids are known to affect the surface behavior of the lipid membranes, which is evident through their interaction with other molecular (hormones, antigens, antibodies etc) or lomc species. Since phospholipid headgroup structure and charge can be modified either synthetically or by chemical perturbation of the aqueous medium (e.g., pH or ionic strength), phospholipid membrane surfaces offer a potential for developing novel strategies in those areas which involve the use of molecular reactive sites. One such strategy which could be envisioned explores the use of molecularly engineered phospholipid assemblies to design and prepare template structures to regulate formation of ordered materials [6]."

Jan 1, 1994

By Onuralp Yücel, Mehmet Bugdayc, Murat Alkan

"In this study, iron based alloys (Fe-Mo, Fe-Cr-Ni, etc.) were produced by using aluminothermic methods starting from Mill Scales obtained continuous casting processes. Mill scales are an oxidised layer of steel alloys containing iron oxide, which includes + 2, + 3 values, on the surface of slabs and billets occurring during annealing in heating furnace at integrated iron and steel milling plant, and continuous casting unit. In the metallothermic experiments, different ratios of starting mixtures and addition of the oxide powders (Alz03, Si02, CaO, MgO) were examined, and their effects on the metal recovery and alloy compositions were carried out. The samples were characterized by using chemical analysis (AAS), XRD, XRF and SEM/EDS techniques.IntroductionSelf Propagating High Temperature Synthesis process (SHS) has many favour compared to the furnace applications, such as low energy requirement, low cost, very short processing time and simple operation, [l, 2]. In a SHS process, the ignition starts the combustion and propagates throughout the reactant mixture yielding the desired product. However, the disadvantages of the process such as inhomogeneous or unreacted products due to undesirable reaction rates needs to be overcome by changing some parameters such as ignition temperature, particle size, additive, atmosphere etc. [3, 4]. Mill scale is a layer of iron oxide which forms on ferrous materials cooling after being processed in hot rolling or continuous casting plants. Mill scale contains iron (II) and iron (III) oxides, which result in a 70% total iron content in oxide form. Not being able to reuse this material will prevent the raw material entering the production plant from being fully utilized [5]. This study aimed to produce Fe-based alloys via SHS (Self Propagating High Temperature Synthesis) metallurgy which is attractive process technique regarding fast and low-cost production ability of cast alloys by using high metallic iron content by reducing continuous casting mill scale."

Jan 1, 2013

By David Hughes

The paper covers the utilization of on-line analysis in process control of solvent extraction in nickel leach solvent extraction processes in Finland and Australia and in copper heap-leach and solvent extraction in Chile. The goals of and requirements for controlling the solvent extraction stages of the processes are reviewed. The applications at three plants are compared. The development of the technology used is reviewed and design considerations are discussed. Requirements for on-line control and analyzer performance are compared. A new generation of analyzers and its effect on the set-up process of a project is introduced.

Jan 1, 2003

By Anna Franzkowiak, Dean Gregurek, Alfred Spanring, Angelika Ressler

In order to determine the most suitable refractory products and improve the lining lifetime for the diverse furnaces used in the nonferrous metal industry, corrosion tests are performed at RHI’s Technology Center. The practical facilities include the cup test, induction furnace, rotary kiln, and drip slag test described in this paper, which enable a comprehensive understanding of the chemo-thermal brick wear on a pilot scale. The corrosion trials are performed with actual slags generated during operations at a customer’s plant. To determine the highest influencing wear parameter, every single test is combined with a detailed mineralogical investigation and thermochemical calculations performed using FactSage. Based on the results, tailored refractory solutions for the nonferrous metal industry can be provided in combination with trials conducted at the customer’s site.

Jan 1, 2014

By Raymond E. Healy

Circuit samples from the HBMS concentrator were assayed for l5elements, and image analysis was done to determine the modal quantities, grain size distributions and liberations of the minerals. Material balancing was done on these data to determine distributions of the minerals in each concentrator stream. The ore was mined during the waning phase of mining and is diluted with backfilled copper smelter slag. The mill feed grades 1.0 wt% Cu and 1.8 wt% Zn. The slag silicate phases contain approximately 1.5 wt% Cu and 6.5 wt% Zn; therefore the Cu and Zn head grades due to chalcopyrite and sphalerite, are only 0.9 wt% Cu and 1.2 wt% Zn, respectively. The recovery of Cu in the Cu-concentrate (Cu-conc.) is only 77.5 %, whereas that of chalcopyrite is 89.2 %. Similarly, the recovery of Zn in the Zn-concentrate (Zn-conc.) is only 40.2 %, whereas that of sphalerite is 71.0 %. The slag accounts for approximately 60 % of the Cu, and 85 % of the Zn in the tailings. The main loss of chalcopyrite is as unliberated grains to the tailings, and the main loss of sphalerite is as free grains to the Cu-concentrate and as unliberated grains to the Cu-concentrate and tailings. Approximately 85 % of the chalcopyrite and sphalerite lost to the tailings. accounting for 8 % and 10 % of the respective minerals in the concentrator feed, occur as middling and sub-middling grains. Extremely fine regrinding would be required to liberate these minerals.

Jan 1, 1989

By S. C. Grund

In secondary copper smelting as it is performed at Hüttenwerke Kayser plant in Lünen, tin-and lead-containing flue dusts are produced as intermediate products. These flue dusts are further processed in a hearth furnace. Followed by certain refining operations a saleable tin-lead-alloy is produced. Even though the hearth furnace technology has been in use for this purpose for a long time still its performance undergoes changes in search for optimum processing conditions regarding to the increasing complexity of the raw materials and tightening economical and ecological boundaries. The use of modern statistical tools for the calculation of accurate mass balances is demonstrated for the tin-lead hearth furnace. These reliable mass balances are the basis for any further modelling of the process with the aim of optimization. Incorporating metallurgical knowledge and experience as well as different mathematical modelling techniques, further studies are planned in which the recoveries of valuable and minor elements and their dependency from various process parameters are examined. The aim of this modelling is to optimize the recoveries of the valuable elements, to minimize the energy consumption and the processing costs and thus to keep the process competitive in a harsher economical and ecological surrounding. The modelling principles are transferable to other metallurgical operations and are especially suited for ill-defined pyrometallurgical processes.

Jan 1, 1999

By Hong Ouyang

A unified computational model has been developed for the Bridgman growth processes of B-NiAI and CdTe crystals. To handle the geometrical and physical complexities, a two-level approach has been developed. At the gtobatlevel, conjugate heat transfer, phase change dynamics, and variable material properties along with the realistic geometries and thermal boundary conditions are accounted for inside the entire crystal growth system. Refined calculations are then made within the ampoule, with the boundary conditions supplied by the global simulations. This model can optimize the use of computational source, help understand solidification behaviors, and improve designs of crystal growth system.

Jan 1, 1996

By Yuanbo Zhang, Zhixiong You, Li Qin, Guanghui Li, Tao Jiang

Low-grade manganese oxide ore is generally characterized by high iron content. In this work, sulfidation roasting of an iron-rich manganese oxide ore with elemental sulfur was characterized. The experimental results indicated that manganese dioxide can be selectively reduced over iron oxide by using elemental sulfur. The manganese phases in roasted product included low-valence manganese oxide, manganese sulfide and manganese sulfate, while those of iron mainly depended on the sulfur addition. Iron oxide would only be reduced or sulfidized at larger sulfur additions. The effect of roasting temperature and S/Mn mole ratio on the phase transformations was also investigated; extractions of Mn/Fe by sulfuric acid were evaluated. An extraction of Mn greater than 95% was obtained while that of Fe was controlled less than 10% under the optimal conditions.

Jan 1, 2016

By T. Lezhava

A new reactor model with rotating cathodes has been developed where various forms (dendrite, spongy) of metal depositions and their uninterrupted removal are accomplished by the realization of high current densities and low energy consumption. At the same time in contrast with the existing methods a high quality metal powder may be obtained from concentrated electrolytes without any specific organic or inorganic additives, which allows raising the intensity of the process. The reactor can be used for electrowinning of metals with low adhesive capacity (Pb, Ag, Cu, Zn, Ni, Co, etc.) and the powders. The obtained products may be utilized in general metallurgy as well as in powder metallurgy.

Jan 1, 2006

By E. Fregeau-Wu

The major obstacle in recycling steelmaking slags to the blast furnace is their phosphorus content. Removal of the phosphorus, which is primarily associated with the silicate and phosphate phases, would allow for greater recycle of these slags for their iron, manganese, and lime contents. Calculations show that separation of the silicates from the oxide phases would remove nearly 90% of the phosphorus from the slag. The variable grain size of the as-received slag made liberation by fine grinding difficult. Therefore, slow-cooling experiments were undertaken to improve the grain size distribution. The grain size distributions were determined using in-situ image analysis. The samples were ground to their apparent liberation size and high gradient magnetic separation was used to separate the magnetic oxides from the nonmagnetic silicates and phosphates. Liberation analysis and modeling was performed on selected separation products for discussion of benefication characteristics.

Jan 1, 1995

By Juárez T. Julio Cesar, Mendez R. Eliecer, Reyes P. Martín, Flores G. Mizraim Uriel, Teja R. Aislinn Michelle, Hernández C. Leticia, Reyes D. Iván Alejandro

The present study shows the characterization of a zinc concentrate collected at Hidalgo, Mexico, in order to identify its mineralogical species and to propose a leaching methodology for silver recovery. The results obtained by X-Ray Diffraction (XRD) show Sphalerite (ZnS) as the mineralogical matrix and silver into the specie proustite (Ag3AsS3). The techniques of Scanning Electron Microscopy-Energy Dispersive Microanalysis (SEM-EDS) and Polarized Optical Microscopy (POM) identified the presence of sulfides of Fe, Cu, Pb and Zn, in addition to silicates and feldspar. The proposed dissolution method of Ag(I) was carried out with [S2O3 2−] = 0.5 M and [NaOH] = 0.1 M to regulate the medium at pH = 9 for 12 h at 298 K. Oxidation of the concentrate was favored by injection of O2 to a partial pressure of 1 atm. Monitoring of the reaction was carried out by reading the [Ag] and [As] by AAS.

Mar 1, 2017

By Francis Vanbellen

Umicore Precious Metals Refining operates an integrated precious metals smelting and refining plant in Hoboken, Belgium. Once a smelter and refiner of complex concentrates, the plant today?s feed consists exclusively of industrial and consumer recycled products, making it the world?s largest recycling facility for precious metals. Unlike the fairy tale of the Frog Prince, it took much more than a princess? kiss to successfully realize this makeover. A completely renewed plant has been built over the past decade. The most visible technological innovation was the commissioning of the Pb-Cu smelter. Its flexibility towards very different types of feed makes it perfectly suited as main entry to the Hoboken flow sheet. A new Cu-leaching & electro winning plant and precious metals refinery make up the Precious Metals Operations (PMO) whose targets are fast throughput and maximized yields for gold, silver and the platinum group metals. The Base Metals Operations (BMO), flexibly process the by-products from the PMO, valorizing ?impurities? like indium, tellurium, selenium and others. Off gas and waste water treatments ensure compliance with strict environmental standards. Precious metals recycling is an art that goes beyond mastering a unique flow sheet. Umicore Precious Metals Refining offers a complete recycling service, taking care of sampling and assaying, metals management and logistics. The quality of this integral service is recognized through the attribution of ISO certifications for our operational activities, sampling and the environmental care. And it?s an art that follows Michelangelo?s experience: ?Art is 5% of inspiration and 95% of transpiration.?

Jan 1, 2006

By C. J. Newman

The new Kennecott Utah Copper smelter, started in 1995, was designed to be the cleanest smelter environmentally in the world. The plant is operating at production rates above the original design capacity. Copper concentrate is smelted in an Outokumpu flash smelting furnace. Matte is granulated and processed using Kennecott-Outokumpu flash converting. Copper anodes are processed in a modernized copper refinery using the Kidd Process while anode slimes are processed for precious metals recovery using a unique hydro-metallurgical process. To allow the production of high quality cathode, using modem smelting and converting technology to minimize emissions, impurity control had to be carefully addressed. All process bleed streams from the smelter and refinery are treated in a hydro-metallurgical plant to fix impurities in a stable form, allow for the rejection of impurities as required and recover valuable metals. Special technology was developed for the copper refinery to ensure production of high quality cathode from anodes containing high levels of impurities. The smelter routinely achieves a sulfur capture in excess of 99.9% which is equal to less than 2 kg of SO2 per tonne of copper produced. This paper describes the design of the smelter and refinery and includes recent production and emission data and modifications carried out to allow operation at above the original design rates. It emphasizes the unique features required to achieve environmental and quality goals and compares environmental performance data to that published on other smelting operations. The processing of intermediate streams, the management of recycled materials and the impurity control strategy will be covered in detail.

Jan 1, 1999

By Fu-Shen Zhang, Mengjun Chen, Jianxin Zhu

"A novel approach for foam glass preparation, namely vacuum-aided powder sintering technique, was preliminarily investigated in the present communication. The key point of which was to prepare foam glass at a negative pressure. Compared to normal powder sintering process, the new approach could benefit the foaming process by shorting the holding time, reducing the amount of foaming agent and especially decreasing relative density of the product. Optimum conditions were 750 °C, 1000 Pa, 5 min and 1 wt.% foaming agent, respectively.IntroductionFoam glass represents a highly valuable solution for thermal and acoustic insulation, since it possesses a generally higher mechanical, chemical and thermal stability than other foams'1'. The first industrial processing for foam glass production, the direct introduction of gases (""blowing"") into the special molten glass, can be dated back to the end of 1930s'2'. At present, almost all foam glasses is prepared by powder sintering technique instead of blowing,3 since it reduces the temperature by several hundred degrees. Moreover, as fine glass powders or similar powders can be used to substitute corresponding glasses by this technique, considerable attention has been focused on the production of foam glass by considering fully recycled glasses, coal fly ash, or other solid wastes as raw materials,4 especially CRT glasses'3' 5', on the point of environmental protection.In a previous report'6', when discussing the lead removal and recovery from CRT funnel glass by a pyrovacuum process, we found that foam glass could be prepared at a negative pressure. Therefore, in this communication, the similarities and differences between the powder sintering process for foam glass at normal and negative pressure was preliminarily discussed."

Jan 1, 2011

By G. Cifuentes

The kinetics of the electrolytic oxidation of cyanide to cyanate on PbO2-coated stainless steel anodes have been studied by both experimental and theoretical means. The anodes were based on 316 steel and performed in a satisfactory fashion. The pH of the studied KCN solutions exhibited a constant value about 11. Values for all the kinetic parameters have been determined and a mechanism for the studied reaction is proposed.

Jan 1, 1999

By Nobuhiro Oguma, Yuji Mizuta, Hideya Sato, Shigehiko Iwahori

"Recyclable materials containing copper and precious metals have been treated at the Mitsubishi Process in Naoshima. In 2003, a new incinerating and melting plant (pre-treatment plant) for waste materials, such as shredder residue of automobile and scrapped appliance, was constructed. All of produced slag/metal mixture is treated at the Mitsubishi Process, and which results in the significant increase of recyclable materials treatment. The combination of two processes has realized a highly efficient and environmentally friendly system for recycling valuable metals in the waste which used to be sent to a landfill. Naoshima continues to make efforts to achieve the highly efficient operations of the two processes, and plans to increase the treatment of recyclable materials further. This paper summarizes the recent operations and the various improvements implemented in the pre-treatment plant.IntroductionRecyclable materials containing valuable metals such as copper and precious metals have been treated at the Mitsubishi Continuous Copper Smelting and Converting Process (Mitsubishi Process) since the start-up in 1991. In the early stages, recyclable materials consisting mainly of metal scrap were charged into the process and the treatment had been increased steadily. In order to promote the recycling business, treatment of various kinds of materials including printed circuit boards was started. However, the treatment hit the ceiling due to a limitation of furnace boiler capacity, since they contained large amounts of combustible materials. In addition, severe corrosion of boiler tubes was caused by halogen contained in recyclable materials."

Jan 1, 2012