By Masafumi Maeda

Our aim in this project was to develop a new copper refining technology utilizing pyrometallurgical treatment and a raw materials preparation technique. In the recycling process; raw material is not an idealized concentrate of copper sulfide but is composed of various types of scrap, industrial wastes such as sludge, ash and slag, and municipal wastes. Since we cannot expect oxidation heat in this process as in sulfide smelting, organic materials are viewed as an alternative energy source. Quality of the copper produced is targeted as 99.99% and an intermediate grade will also be marketable. To benefit the plant, rare metals and other nonferrous metals will also be recovered The overall system is described in this paper, specific topics outlined and preliminary research presented. Current Japanese technology for recycling copper based materials is briefly reviewed.

Jan 1, 1995

By Tang Chaoho

Laboratory research on the reducing and matte smelting of Jamesonite concentrate has been carried out. The influence of the process conditions such as the smelting temperature, the amount of pyrite cinder (the agent of fixed sulfur) and the amount of additives on the smelting process have been studied. Under the optimum condition the direct recovery ratios of antimony and lead are 83.26% and 68.50% respectively. The ratio of fixed sulfur is 98.97% but more than 15% lead and 30% silver remained in the ferrous matte. The key problem to be solved of this new process is how economical and effective is the recovery of silver and lead in ferrous matte.

Jan 1, 2003

By Tang Chaoho

Laboratory research on the reducing and matte smelting of Jamesonite concentrate has been carried out. The influence of the process conditions such as the smelting temperature, the amount of pyrite cinder (the agent of fixed sulfur) and the amount of additives on the smelting process have been studied. Under the optimum condition the direct recovery ratios of antimony and lead are 83.26% and 68.50% respectively. The ratio of fixed sulfur is 98.97% but more than 15% lead and 30% silver remained in the ferrous matte. The key problem to be solved of this new process is how economical and effective is the recovery of silver and lead in ferrous matte.

Jan 1, 2003

By Markus A. Reuter, Robert Matusewicz

"Consumer products are a complex man-made mixture of sometimes in excess of 50 elements. In order to recover these complex mixtures of elements either as metals, compounds or energy requires versatile technology in physical separation but also smelting and energy recovery. This paper explores this by referring to the innovative application of Top Submerged Lance (TSL) technology and associated theoretical and environmental aspects to process (recycle) post consumer materials and industrial intermediate products and residues. A diversity of applications has been tested in Ausmelt’s pilot plant in Dandenong and many have gone to commercial scale globally. This paper reviews the varied applications ranging from e-waste recycling, lead and NiCd battery recycling, metals recovery from slags, zinc leach residue processing, electric arc furnace (EAF) dust, Municipal Waste Incinerator bottom ash processing, carbon containing residues such as retort ashes and spent pot liner from the aluminium production process as well as use of the technology for materials such as automotive shredder residue (ASR) and plastics. Introduction The modern resource cycle is a link between primary production of metals linked to the recycling of post-consumer goods. The sometimes complex combinations of materials and metals in consumer products such as televisions depicted by Figure 1, does require a range of technology to recover materials, metals and energy for reuse and/or recycling in an economically feasible as well as environmentally friendly manner."

Jan 1, 2008

Conventional ferronickel smelting has five main steps: Drying, calcination, prereduction, smelting and refining. In the scope of the current work, smelting experiments were conducted using Sivrihisar laterite ores (1.26% Ni) of Turkey. The ore samples previously subjected to drying, calcination and prereduction stages were smelted in alumina crucibles in a laboratoryscale horizontal tube furnace under argon atmosphere. Smelting experiments were performed at 1500, 1550 and 1600 oC. The amount of excess coal used in prereduction step was another variable. Sivrihisar laterite ore is a limonitic one with low MgO composition. Therefore, MgO was added to the smelting charge as a flux. The effects of experimental variables on metal Ni content and slag composition were investigated.

Jan 1, 2012

By Hidefusa Takahara, Koichi Miyake, Dierk Raabe

"Mechanical properties of copper wires were examined. The copper wires containing 5-10 mass % chromium and 1-3 mass % silver were produced through heavily cold deformation. It was expected that the copper wire was easily fractured during cold deformation because of the existence of brittle chromium phase in the alloy. In fact, the copper wire was fractured due to large work hardening, when the true strain [n] exceeded 5. However, the copper wire annealed at 1273K for 6 ks ·in the middle of deformation process could be smoothly drawn to 11=8. After precipitation treatment for silver phase at 473k for 1.8 ks, the wire was able to further drawn to n=8.4. The final deformed wire showed tensile strength higher than 1200MPa.IntroductionDownsizing of electronic devices has led to the demand of finer and higher strength materials for cables. Conventional copper alloys have about 800MPa in ultimate tensile strength. These strength are mainly obtained by precipitation hardening. Nowadays, a process for higher strength wire has been developed, where dual phase copper alloy is used. When it is drawn heavily, the' second phase is elongated along drawing direction and the wire gets high strength due to fiber reinforcement (1). That alloy is so called in-situ formed fiber reinforced ·alloy. Cu-Ag(2), Cu-Nb(3) and Cu-Cr(4) systems are well known as such alloys. It is also well known that chromium is brittle material except single crystal and high purity of chromium. However, Mihara et al. C5l have achieved 1 GPa in ultimate tensile strength in the Cu-Cr-Zr and Cu-Cr-Ti alloys by appropriate thermo-mechanical processing.In this study, the Cu-Cr-Ag systems were investigated: The alloys contained 10 or 5% chromium and 3 or 1 % silver. It was demonstrated that silver precipitated in copper matrix contributed on further hardening."

Jan 1, 2000

By Derk G. E. Kerfoot

The extractive metallurgy of nickel and cobalt has proved to be a particularly fruitful area for innovation in hydrometallurgy and electrometallurgy ever since the development of the Hybinette process for nickel in the early 1900's. In current practice, nickel concentrates are generally smelted to high grade mattes which are then refined to metal by a combination of hydrometallurgy and electrometallurgy, although low grade copper-nickel concentrates are refined directly by the ammonia pressure leach process. Matte refining processes in commercial operation include the direct electrolysis of matte, the ammonia pressure leach, sulphuric acid leaching using air or oxygen at elevated pressure, or at ambient pressure, and chlorine or chloride leaching. Refined nickel is recovered either as electrolytic cathode, or as metal powder by hydrogen, reduction. Hydrometallurgy has also found application in the treatment of nickel laterite ores, both in the reduction roast ammonia-ammonium carbonate leach process, pioneered by Caron and in the Moa Bay acid leach process. Cobalt is recovered as a co-product of copper in central Africa, and as a byproduct of hydrometallurgical nickel refining elsewhere. In the African plants, the copper-cobalt concentrates are roasted and leached in sulphuric acid solution, and copper and cobalt are recovered separately from the leach solution by direct electrowinning. A variety of hydrometallurgical techniques are used for the separation of cobalt from nickel, including selective precipitation and crystallization, solvent extraction, and ion exchange. Like nickel, refined cobalt is recovered either as electrolytic cathode or as metal powder by hydrogen reduction.

Jan 1, 1988

By Zhihua Wang

Through metallurgical calculation and process analysis based on metallurgical theory, it is aimed to raise the concentration of smelting oxygen and improve the update speed of reaction interface, accelerate the reaction and achieve a high-intensity smelting at the stage of converting. The PM plant has launched a theoretical research on model of high-intensity converting aiming at increasing the oxygen concentration of converting, carried out transformation of Kaldo furnace converting system, performed a series of industrial trial operations, conducted multiple rounds of tracking test and data comparison in reducing the furnace cycle, lowering the unit consumption of fuel and stabilizing the furnace lining life. The move has practically tested and verified the correctness of high-intensity smelting theory.

By Yoichi Takeda

Copper solubility in SiO2-CaO-FeOx slag equilibrated with copper matte in 10% SO2 atmosphere at 1573K was estimated. Essential parameters are activity coefficients of copper oxide and sulfide, oxygen and sulfur potentials and activity of copper in the slag-matte system. A large number of experiments provide proper parameters to calculate copper solubility in slag, A classical thcrmodynamic model postulating CuO0.5 and CuS0.5 moleculcs assists in estimating copper solubility in slag. Additions of Si02 and CaO reduce copper solubility almost in any condition. Copper loss, that is function copper solubility and slag volume, in the silica saturated SiO2-FeO. binary slag is minimally equilibrated with less than 66% copper matte while copper loss in the 50% FeO.-SiO2-CaO ternary slag saturated with 2CaOSiO2 is minimally equilibrated with over 66% copper matte. This slag composition has potential for continuous copper converting, direct copper production or high-grade matte production.

Jan 1, 2003

By Andrey V. Tarasov

To carry out a physicochemical substantiation of a transition to ?soft? modes of reduction of calcine obtained by desulfurizing roasting of nickel concentrate produced as a result of copper-nickel converter matte separation in a nickel anode production circuit, an analysis has been conducted of the macrokinetic behavior of actual calcine samples in the presence of gaseous H2-CO mixtures and solid reductant additives. Within a temperature range of 900°C to 1100°C the main regularities typical of the calcine reduction process with individual gases (H2, CO) also take place when using a gaseous mixture. Under the conditions of low-temperature (900°C to 1000°C) nickel oxide reduction with products of fuel oil conversion in the presence of coke, the role of the latter is insignificant from the technological viewpoint. As a result of the present investigations, we have obtained analytical expressions of macrokinetic parameters of the reaction interaction within the [NiO] calcine-H2-CO-C-CO2-H2O-O2-N2 system.

Jan 1, 2005

By Pinai Mungsantisuk

Keywords: Pd-Ni alloys, Pd-Fe alloys, Pd-Co alloys, Magnetostriction, Magnetic Properties The presence of congruent melting minima, the occurrence of ferromagnetic transition over a large composition range, and FCC type crystal structure make Pd-Ni, Pd-Co, and Pd-Fe based systems attractive candidates in our search for materials with no rare-earths, large low-field magnetostriction, and good mechanical properties. The presence of paramagnetic-ferromagnetic transition over a broad range of composition also provides opportunity for fundamental studies. In this work, we have examined the magnetic and magnetostrictive behavior of Pd-Ni, Pd-Co, and Pd-Fe alloys over the entire composition range. Alloy sample rods were prepared by arc melting and casting. X-ray diffractometer was used to obtain lattice parameter data. Magnetostriction was measured along the rod axis using strain gages. Magnetic properties were measured using a vibrating sample magnetometer.

Jan 1, 2005

By Toshiyuki Kawai

Copper concentrate smelting directly in P-S converters was started at Onahama Smelter in 1983. Thereafter, the tonnage of concentrate smelted through the P-S converters increased, such that by 2002, it equaled the tonnage smelted through the reverberatory furnaces. In 2003, 56% of the total copper concentrates treated at Onahama Smelter were processed directly through the P-S converters. Technical improvements are reviewed and advantages of direct smelting in P-S converters are reported.

Jan 1, 2005

By B. L. Chulu

In the carbothermic reduction of lead sulfate to produce lead, the inclusion of soda ash (Na,CO,) in the charge provides for the control of sulfur dioxide in the effluent gas. An important mechanism in the process appears to be the carbothermic reduction of the sodium carbonate whereby sodium gas and carbon monoxide are produced. These intermediates then participate in the reduction of the lead sulfate to produce lead metal and stable sulfur species in the molten slag phase. In addition, there is some evidence that the presence of lead metal in the charge may also serve to increase the lead recovery in the process. These aspects were investigated by conducting laboratory-scale smelting tests with small charges (;3g), at 1173°K(9000C). Recovery did not exceed 74w% and the role of incipient lead metal in the charge could not be clearly assessed.

Jan 1, 1993

By Xinli Wang, Matthew Andriese, Jiann-Yang Hwang, Zhiwei Peng, Byoung-Gon Kim

"The microwave reflection loss (RL) of ferric oxide is studied in the temperature range from 297 to approximately 1400 Kat frequencies of 915 and 2450 MHz. It is shown that the maximum microwave absorption with RL of -38.46 and -35.97 dB can be obtained for ferric oxide having thicknesses of 0.03 and 0.01 m at 915 and 2450 MHz, respectively. The maximum absorption peak with RL below -10 dB is in a 250 K temperature range from 723 to 973 Kat 915 MHz, which shifts to the range between 823 and 1073 K at 2450 MHz. This migration is in good agreement with the variation of the dielectric loss tangent of ferric oxide.IntroductionMicrowave irradiation has distinguishing characteristics such as volumetric and selective heating compared with conventional methods, leading to extremely broad applications in materials heating and processing [1-5].The efficiency of microwave heating was found to be dependent on various factors, such as microwave power [6], frequency [7,8], radiation time [8], applicator geometry [8], sample microwave absorption properties and position as well as dimension [9-11 ], etc. Among these parameters, sample dimension plays an important role but is usually neglected by researchers in microwave processing of materials. In fact, although numerous studies have been directed toward the utilization of microwave energy to assist materials heating and processing, few reports were released on the effect of sample dimension [12,13].This is because all aforementioned factors influencing microwave heating generally exert interactive effects to each other during the heating process, making clarification of the effect of sample dimension difficult. Therefore, it is necessary to propose a parameter or concept for quantifying the effect of absorber dimension on microwave heating, increasing heating efficiency."

Jan 1, 2013

By John C. Taylor

With growing emphasis on energy conservation and increased concern over the presence of heavy metals in the environment, it is fortunate that most metals are readily recycled. In this respect, metals have a significant advantage over plastics and similar materials used as metal substitutes. For many years a secondary industry has processed scrap copper, nickel, lead and zinc to produce refined metal which has, to varying degrees, influenced the price and displaced the production of primary metal. This paper reviews some of the challenges the industry will face and the changes in process technology which will be required as pressure mounts to increase the amount of metal recycled. In the case of most base metals, this will have an impact on primary metal production; as the tonnage of metal recycled increases, the requirement for primary production, or new metal, will depend more and more on the growth in consumption.

Jan 1, 1993

By J. R. Donald

Electric arc furnace (EAF) dust, which can be considered as a by-product of the steel recycling process, contains significant quantities of recoverable zinc and iron, as well as hazardous elements such as cadmium, lead and chromium, which can be leached by ground water. The zinc in the EAF dust is found almost entirely in the form of either zinc oxide or zinc ferrite, the latter accounting for 20 to 50 percent of the total zinc. It is important that an efficient process be developed which renders the dust inert, while reclaiming the valuable metals to off-set processing costs. During the conventional carbothermic reduction processes, iron is formed, and this iron can participate in the reduction of the zinc oxide in zinc ferrite. In the present work, the reduction of the zinc oxide in zinc ferrite by iron according to the following reaction: ZnO-Fe2O3(s,s) + 2 Fe(s) = Zn(g) + 4 FeO(s) was studied in an argon atmosphere using a thennogravimetric technique. First, a thermodynamic analysis was performed using the F*A*C*T computational system. Then, the effects of briquette aspect ratio (lid), temperature, zinc ferrite particle size, amount of iron added, as well as additions such as lime, sodium chloride, and calcium fluoride were investigated. It was found that, initially, the reaction was chemically controlled with an activation energy of 178.1 kJ/mol. Then, after a product layer had formed on the outer surface of the briquette, the reaction was restricted by the diffusion of zinc gas away from the reaction interface. The parabolic rate law was fitted to the experimental data, and the parabolic rate constant was found to be: = -6.2275 + 0.0054 T (K)

Jan 1, 1995

By K. V. Sreenivas Rao

Solidification experiments have been conducted to study the effect of interface heat flux and air gap formation on cooling rate of the casting during solidification of Al-4.5wt%Cu alloy. The thermal history of the casting and mold during solidification is recorded using thermocouples connected to computer interfaced data logger. The measured temperatures in the mold are used as input to the IHCP (inverse heat conduction problem) algorithm for simulating multiple heat flux components at the boundary. It is observed that the filling effects induce spatial variation in the thermal field in the mold and casting regions and greatly influence the cooling rate of the casting. The study demonstrates the use of IHCP and in-situ measured thermal profile in analyzing the cooling rate and microstructure.

Jan 1, 2008

By Vinicius Alves Gomes, Jean Igor Margem, Frederico Muylaert Margem, Sergio Neves Monteiro, Marina Rangel Margem

The interface between the matrix and the reinforcing fiber plays an important role in the efficiency by which an applied load is transmitted through the composite structure. The shear stress at the fiber/matrix interface can be associated with this load transference and, consequently, affects the composite strength. In the present work, pullout tests were used to evaluate the interfacial shear stress of malva fiber in epoxy matrix composites. A small critical length was found for the malva fiber embedded in epoxy, which corresponds to a relatively weak fiber/matrix bond and lower interfacial strength.

Jan 1, 2015

By Run Huang, Xuewei Lv, Songli Liu, Chenguang Bai

"Titanium alloy was prepared from titania-bearing blast furnace slag (Ti-BF slag) by aluminothermic process in an induction furnace. The effects of aluminum amount on the titanium silicon yield and titanium recovery ratio were studied. The phase transformation and chemical composition of the prepared alloy were investigated by X-ray diffractometry (XRD) and X-ray fluorescence (XRF) respectively. It was found that the mass fraction of silicon and aluminum increased with increasing the aluminum amount, however, the mass fraction of titanium increased first and then decreased with increasing the aluminum amount. Furthermore, both the titanium alloy yield and titanium recovery ratio increased with the increase of aluminum amount. The main phases of the alloy were TixSiy and AlTi3. The titanium alloy samples prepared in various conditions had a composition (wt.%): 38–50% Ti, 29-34% Si, 4-11 Al%, 1.6-2.2 Mn%.IntroductionPanzhihua and Xichang regions in the southwest of China are rich in vanadium-titanium magnetite containing iron, vanadium, titanium and gangue. According to the characteristics of the resource, iron and vanadium are successfully recovered with a blast furnace process and a converter process. However, most content of titanium are entered in the blast furnace slag with TiO2 22% -26% and metallic Fe 2%–6% called Ti-BF slag. Due to the dispersed distribution of Ti in various fine grained mineral phases with a complex combination between Ca, Al and Si, it is difficult to recover the Ti components[1]. This slag is generated at a current rate of 3.6 million tons per year, which adds to the existing 70 million tons of slag produced so far[2]. The slag has had to be piled as large as the mountains, which not only waste of resources but also cause a pollution of the environment. Therefore, the study of integrated utilizing Ti-BF slag has become very significant."

Jan 1, 2012

By Emmanuel N. Zevgolis Ismene-Polyxeni Kostika

Keywords: reduction, kinetics, laterites, rotary kiln, dust In this work, the reduction kinetics of dust from nickeliferous Greek laterites is investigated. The dust is a by-product from laterite treatment in rotary kilns and it comes from washing towers, electrostatic filters and polycyclones. Laboratory made pellets from this dust were also examined. Reducibility was studied in the temperature range of 700°C to 850°C in a laboratory tube furnace. Kinetic analysis of the results showed that at lower temperature values the mixed kinetic model verifies the experimental results of dust and pellet samples. At higher temperatures (800° and 850°C) diffusion becomes the rate controlling mechanism. The calculated activation energy values verify also the above mentioned results.

Jan 1, 2005