By P. K. Kaiser, C. Mackay

A circular shaft with a diameter of 6m was excavated by the conventional drilling and blasting method to a depth of 235m through 60m of glacial till, 1 Om of water bearing basal sand, 1 1 Om of clay shale (Bearpaw Formation) and finally a strata of coal, mudstone, siltstone and sandstone (Oldman Formation). The lined shaft was instrumented at three levels by multipoint extensometers to determine the displacement field near the shaft bottom, embedment strain gauges to measure the strains in the liner and IRAD-stress change gauges to observe the radial and tangential stress changes in the rock mass. The data from these gauges were used to determine the in situ stress field. An attempt to measure in situ stresses by overcoring was also made at a higher elevation. The performance of the shaft and its support was then evaluated by use of the "Convergence-Confinement Method". For this purpose the measurements of stress changes and displacements were combined to determine by extrapolation the displacements ahead of the shaft and after the liner installation. The convergence curves calculated in this fashion were then used to evaluate the performance of the cast-in-place concrete liner and of an alternate shotcrete shaft support system.

Jan 1, 1983

By Gerald Edmunds

Although the phenomenon of season cracking is still imperfectly understood, there seems to be ample evidence that season cracks are propagated by the combined action of corrosion and a stress of either internal (residual) origin or external origin. The factors that influence season cracking may therefore be grouped according to corrosive media, nature of stress, and character of the material. Thus the important mass of evidence pointing to ammonia as the most frequently active corroding agent causing season - - cracking of brass has naturally led to the development of laboratory tests of a moderately accelerated character based upon ammonia together with auxiliary agents such as air, water vapor, and carbon dioxide as the corroding agent. Similarly, the knowledge that stress must be present has led to the use of externally applied and therefore accurately measurable stresses in laboratory testing. A companion paper(^)^ to the present one discusses the development of these test methods in our laboratories. The present paper discusses data bearing on factors concerning the nature of stress such as its magnitude and direction of application. It also deals extensively with the character of the brass, particularly in regard to the copper-zinc ratio and the structure as developed by mechanical work-

Jan 1, 1945

By R. Agarwal, S. Boshkov, M. T. Wane

The majority of the work done in the field of rock mechanics uses as a basis for analysis the classical linear theory of elasticity. Most workers in rock mechanics realize that removing the assumptions of homogeneity and isotropicity will bring the analysis of stress-strain relationships for geologic materials closer to reality. However, the algebra involved in reducing these restrictions is usually heavy. It is the purpose of this paper to relax the condition of isotropicity to that of orthotropicity and examine the sensitivity of this change for some simple geometries. In addition some necessary relationships between stress and strain for orthotropic materials will be developed. The recent years have seen an increasing interest in the field of rock mechanics. This is amply demonstrated by the number of articles appearing in the technical literature. The majority of these articles use as a basis for analysis the classical linear theory of elasticity. In addition, the assumptions that the material under consideration is elastically homogeneous and isotropic reduce the number of constants necessary to write an analytical relationship between stress and strain to two, e.g., Young's modulus and Poisson's ratio. Most workers in the area of rock mechanics realize that removing the conditions of homogeneity and isotropicity will bring the analysis of stress-strain relationship for geologic materials closer to reality. However, the algebra involved in analysis without imposing these restrictions is usually heavy. It is the purpose of this paper to relax the condition of isotropicity to that of orthotropicity and examine the sensitivity of this change on stress concentration for some simple geometries. In addition, it is shown that the expression for maximum stress concentration for some simple geometries considered can be further simplified if further assumptions are made. The maximum stress concentration, under these additional simplifying assumptions, is shown graphical1y. In the linear theory of elasticity, generalized Hooke's law assumes the following form

Jan 1, 1965

By AUDLEY H. STOW

I. INTRODUCTION. THE general drift of the discussion as to the relative merits of pressure- and exhaust-fans has resulted, if we may judge from the prevailing practice, largely in favor of the latter. The subject has been hitherto treated, however, with special reference to highly gaseous mines, the effect of the form of ventilation upon dust-explosions having been too little considered. Even in mines containing practically no gas, dust-explosions may occur; and if, as I believe, pressure-fans are to be preferred for their effect upon dust, it may be worth while to reopen the debate, and to challenge the advisability of exhaust-ventilation under certain conditions. There are several forms of colliery-ventilation, which may be described as follows: Plain or simple pressure-ventilation, in which the fan acts as a pressure-fan, and the movement of coal is unobstructed at the surface by doors or equivalent devices in drifts or shafts, the traveling and haulage thus being in the return-current. Plain exhaust-ventilation, in which the fan acts as an exhaust-fan, the movement of coal being likewise unobstructed at the surface, and the traveling and haulage being in the intake. Obstructed pressure-ventilation, in which the movement of coal is obstructed at the surface, in order that the traveling and haulage may be in the intake. Obstructed exhaust-ventilation, in which the movement of coal is obstructed at the surface, in order that the traveling and haulage may be in the return. The apparent advantages in running a fan "pressure" during working-hours, and " exhaust" between shifts, seem to justify the recognition of this combination as a standard form of ven-

Feb 1, 1909

By Kenneth A. Gutschick, Robert S. Boynton

Lime has become a general and loosely used term to denote almost any kind of calcareous material or finely divided form of limestone or dolomite, as well as burned forms of lime. However, according to Webster, lime is only calcined limestone (known as quicklime, unslaked lime, or calcium oxide). It also embraces the secondary product of quicklime, i.e., hydrated lime or slaked lime (calcium hydroxide). There are two basic types of limestone used for lime manufacture-high calcium and high magnesium (dolomitic). The dolomitic quicklimes and hydrated limes correspond to their "high calcium" counterparts. The only difference is that the dolomitic types are a combination of the elements calcium and magnesium, in varying percents, whereas high calicum limes contain less than 5% MgO down to 1/2%. In either case a pure form of limestone of at least 97% combined carbonate content is needed to make salable lime, barring a few exceptions. The calcination of both types is diagrammed chemically as follows: [ ] In the foregoing reversible reactions the limestone is burned (calcined) in lime kilns, with the carbon dioxide content of the stone expelled as a gas. The weight loss during calcination of pure high calcium limestone is 44%; with equimolecular dolomitic limestone, the weight loss is 48%. Since lime has a strong affinity for CO_, particularly if moisture is present, it will readily revert to its original carbonate form. This occurs when quicklime "air-slakes" and adsorbs CO.. from the air. Thus, quicklime is perishable and should be stored in dry, water-tight areas. Depending upon the type of kiln used and the physical structure of the stone, the size of the quicklime may range from sandlike granules to 8 in. lumps. However, pebble sizes ranging from 1/4 in. to 2 in. are the most common. Screened quicklime fines are also com¬pressed (pelletized) into 1 in. pellets. For some purposes ground or pulverized forms of quicklime are used, ranging from No. 10 mesh to dust. Generally a pebble of quicklime is about the same size as the pebble of limestone before calcination (perhaps shrinking slightly). A more stable form of lime is hydrated lime. This is obtained by adding water to quicklime, slaking it into a dry, fine, subsieve size white powder. Because its affinity for moisture has been satisfied, it is not vulnerable to further moisture like quicklime. However, it has the same strong affinity for CO_. The following reversible chemical reactions illustrate how hydrated lime when heated (or dehydrated) can revert to the original oxide form:

Jan 1, 1975

By M. J. Hordon

Measurements of the 103 yield stress of ordered and disordered poly crystalline Cu ,Au were related to the ordered antiphase domain size determined by resistivity measurements. For undeformed material, a yield stress maximum wa obtained at a critical domain diameter of about 40A. Plastic deformation resulted in a marked increase in the yield stress and electrical resistivity of the ordered alloy compared to the disordered, the strain hardening rate increasing regularly with initial antiphase domain size. Order hardening was accompanied by a sharp reduction in size of the initially large domains. It has been observed that the yield stress of ordered and partially ordered Cu3Au alloy varies sensitively with antiphase domain size aid degree of order.ly2 In addition, ordering of the lattice leads to a marked increase in the strain hardening rate (order hardening) as compared to the rate for the disordered alloy. In the present investigation, changes in the electrical resistivity and yield stress of ordered polycrystalline Cudu with varying initial domain diameters were measured after tensile plastic deformation in order to examine the effect of cold work on the antiphase domain size. EXPERIMENTAL PROCEDURE Au-Cu alloy of 99.99 pct purity analyzing 50.85 wt pct Au-balance copper was obtained from the Handy-Harmon Co., N. Y., in the form of 0.061 in. diam drawn wire. Wire specimens 3 in. in length were given the following annealing treatment in nitrogen: 500" for 72 hr, 820" for 15 hr, and 450" for 5 hr, followed by a water quench. The annealing sequence resulted in a completely disordered structure with a grain size of about 0.2 mm. The disordered specimens were then reannealed at 360' in nitrogen for periods varying from 10 min to 150 hr followed by quenching to produce ordered structures with varying domain sizes. The degree of ordering and variation of domain size was followed by electrical resistivity measurements made at room temperature using a low resistance precision Kelvin double bridge apparatus. The specimen resistance was determined over a length of 4.0 cm between two brass knife-edge contacts while the specimen was immersed in an oil bath to minimize temperature variations. In addition, the current flow in the circuit was minimized by a current pulse technique in balancing the bridge in order to avoid heating the specimen. Using a sensitive galvanometer to detect the bridge null, the accuracy of the resistance measurement Wire specimens were plastically strained in tension with an Instron tensile unit at strain rates in the range 5 x 10"5 sec-' to 2 x 10"4 sec-'. Stress and extension data were fed into the Instron chart drive amplifier to obtain the actual stress-elongation curve from which the yield stress at 10"3 strain was determined. The maximum resolution of the apparatus was approximately 50 psi stress and 3 x 104 strain. At various plastic strain levels, deformation was interrupted and the electrical resistivity determined after removing the stress. RESULTS AND DISCUSSION 1) Yield Strength of Ordered Cudu. In order to determine the effect of the ordered antiphase domains on the initial yield stress, specimens were prepared with varying domain sizes ranging from zero for 5 completely disordered structure to about lo5A for a completely ordered structure by suitable annealing treatment. Domain sizes were estimated by comparing room temperature electrical resistivity data with the original data of Jones and sykes3 as modified by rdle.' In agreement with previous work, the resistivity varied sensitively with domain diameter and degree of order, decreasing from approximately 11.6 x l0- ohm-cm for the disordered structure to about 5.9 x l0- ohm-cm for ordered domains above 10"3 cm in diameter. Fig. 1 shows the change of the 103 yield stress with ordered domain size. It is evident that the maximum

Jan 1, 1963

By W. van der Knapp

A theoretical and experimental ana1ysis is given of the change in volume of a porous medium due to changes in external and internal pressures. The result enable one to deduce directly the effect of large increlents in stresses. It is shown that the three-dimensional representation of the volume of a nonlinear porous system is a cylindrical rules surface, the generating lines of Which have a slope according to the solid rock compressibility. Analytical expression for such a ,surface is very simple. It follows that the bulk and pore compressihilities depend only on the difference between pore fluid and external hydrostatic pressure, i.e., the effective rock frame pressure. From measurements on a number of sandstones as well as limestones it can be conduded that for practical values of this effective frame pressure the pore compressibility falls in the range between the compressibility of water and that of undersaturated crude oil. In general, pore compressibility is found to be higher the lower the porosity. For a particular limestone reservoir pore compressibility and porosity could he related by means of a simple empirical formula. Results from the described study find a direct applicxtion in material balance calculations and in prob1ems of liquid flow through porous media. Since the elastic constants of the rock bulk material enter into equatiorls for velocity of acoustic waves, the results are also of importance for calculating rates of wave propagation in these media. It is shown for sandstones with 1.5 to -10 prr cent porosity that laboratory measured porosities may differ from those lender reservoir conditions by about I per cent of their value. The difference for low porosity limestotnes can be of the order of 10 per cent. The subsidence caused by elastic deformation of reservoir rock is shown to he very small. General formulas relating pore and bulk volume to external and internal pressure can be derived, as has been shown by Biot1, Gassmann2 and Geertsma.2 Their theories describe the differential change in volume caused by a variation in pore fluid tension and external hydrostatic tension. It has been known for a long timei that the stress-strain relations of a packing of spheres are essentially noninear. Our experiments show that for almost all reservoir rocks which arc elastically deformable the relation between volume and loading is also a nonlinear one, resembling that of a packing of spheres very closely. The behavior of these media is often described by using the linear stress-strain relations for small incremental stresses and strains in the vicinity of a pre-stressed condition." The present study differs from these considerations in that it enables one to deduce the effect of large increments in the stresses directly. In analogy to the stress tensor for a homogeneous body the stress tensor for a porous body can be written in the conventional way: where the tensor components, o, and t, represent the total forces acting on the faces of a unit cube of porous material. This tensor can be split into two parts. a hydrostatic and a deviatoric part, as follows2,3,1 where the component of the hydrostatic stress system, a. equals The hydrostatic stress causes a change in volume whereas the deviatoric stress system gives rise to a change in shape only. One of the difficulties in describing changes of volume occurring in reservoir rocks is that the relations connecting these volume changes with external and internal stresses are essentially non-linear. A complete description requires the bulk volume, V,,, as well as the pore volume,V,,. to be known as a function of both the changes in pore fluid tension (v) and the hydrostatic tension on the outer boundary.

By H. I. Kaplan, C. Laird

Pulsating contpresslon experiments have been carried out on coppev single crystals in order to test the adequacy of mechanisms which have been suggested for stage I cvack grouth when tension-compression loading is the mode of- applying stress. Although dejorrrzation continues slowly for many millions 01 cycles under Pulsating compression stresses both within slip bands formed in the first cycle and by the creation of new bands, the morphology of these bands is not typical of fatigue slip bands in general and neither initiation of cracks nor propagation of artificially induced cracks was observed. It is therefore concluded that 1) initiation and growth of cvacks in fatigue is a consequence of repeatedly reviersed, microplastic deformation rather than intermittent, unidirectional deforma-tion, 2) gvowth of- cracks in polycrystalline specimens FAILURE of a plain specimen subjected to cyclic tension-compression stresses is known to take place by two stages of cracking.1,2 The first stage is characterized by propagation along slip planes roughly at 45 deg to the stress axis, in the outermost layers of the specimen, and at a rate of the order of angstroms per cycle. The average macro orientation of a stage I crack is normally at right angles to the stress axis,3 however, except in a few cases, e.g., single crystals in suitable orientation, when both the micro and macro directions of propagation are at 45 deg to the axis. After a stage I crack has penetrated to such a depth that the stress on the remaining section of metal is significantly increased, stage II crack propagation succeeds stage I, at right angles to the stress axis both micro and macroscopically. Direct evidence of the processes occurring during a subjected to pulsating compression stresses is caused by the setting-up of local tensile stresses due to interactions between grains, and 3) both unslipping mechanisms and operation of the "plastic blunting process " within a single slip band are adequate descriptions 01- stage I growth, being fundamentally similar. The slip mode of a material, however, is considered to control whether unslipping or the plastic blunting process takes place. Thus materials of planar slip mode fauor unslipping while those hacing a wavy mode, and capable of cross slip, can fail in stage I by the plastic blunting process. Similarly, and perhaps more importantly, reversed torsion and tension-compression modes of applying stress may be expected to cause the unslipping mechanism and the plastic blunting process, respectively. single stress cycle4,5 shows that stage II crack propagation takes place by a repetitive plastic rounding and closing of the crack tip. This mechanism has come to be called the "plastic blunting process".6 On the other hand, the extreme smallness of the phenomena occurring in stage I growth prevents elucidation of its mechanism by direct observation. Many suggestions have been proposed for this mechanism,'"-" most of them involving some kind of random or systematic unslipping process. It is possible, however, that the mechanism of stage I growth is essentially the same as that of stage 11, but occurring on a much smaller scale.6 In this situation, it has been observed that cracks propagate along slip bands comprising dislocation cell structures and bounded on either side by regions of different dislocation density and distribution." Since there is evidence that such bands are softer than their matrix, * it may be expected that the plastic blunting process occurs within a single slip band during stage I growth, rather than on two gross bands as in stage 11, when the acting stress is greater.= The blunting of the crack tip allowed by coordinated

Jan 1, 1968

By B. E. Mix

THE present methods of unloading ore and coarse-crushing at the Magna plant of the Utah Copper Co. are the developments of the past five years. Hand dumping and breaking have given way to the rotary car dump and large gyratory; and the bucket elevators and stationary screens have been replaced by conveyors and shaking screens. The coarse-crushing plant may be broadly divided into two units: the primary crushing and the secondary crushing, or primary roll, unit. The former was erected in 1923; with the exception of the excavation, the construction was carried on by forces of the company. Excavation was started in the middle of March, the first concrete was poured July 16, erection of the steel building started Oct. 30, and the unit was com-pleted and operating Dec. 30. The unit has a capacity of over 24,000 tons of ore per day, and cost more than a million dollars. Remodeling of the primary-roll unit extended over a period of years preceding this, some of the work having been done as early as 1918.

Jan 8, 1925

By W. A. Backofen, R. L. Fleischer

AN effect of orientation on the creep behavior of aluminum at 4.2 OK has been observed. Stress relaxation was measured in a hard-type tensile device after stopping the drive. From the spring constant of the device the load-time record could be converted to strain as a function of time. The strain sensitivity was 2-10-=, and the usual creep time of 1 min normally allowed a stress drop of about 25 g per sq mm. Further details of the apparatus and sample preparation appear elsewhere.' It should be noted that neither stress nor strain were constant, so that quantitative comparison with current creep theories will not be made. Shear strain (y) as a function of time (t) was consistent with logarithmic behavior: y = A In t, where A is a constant. In some cases t was made as large as lo3 sec. In the results the quantity A divided by t (the resolved shear stress, which is the driving force for creep) is plotted as a function of strain prior to creep. The quantity A/t is thought to indicate qualitatively the ease with which dislocations can move during creep. In Fig. 1 are drawn tensile stress-strain curves and A/T-strain measurements for single crystals of three orientations: l(a) and l(b) for the maximum resolved shear-stress orientation, l(c) for an orientation 2 deg from [211], and l(d) for a [111] stress axis. The following observations were made: 1) At low strains the A/t values are nearly the same for the three orientations. 2) As strains increase, A/t drops most rapidly for [Ill.] and less rapidly for [211], while for the maximum shear-stress orientation it is constant during easy glide and drops abruptly at the termination of easy glide. 3) In stage 11, A/t values are again approximately the same for the three orientations. These observations are regarded as evidence that 1) the initiation of slip produces obstacles of essentially the same effectiveness for all of these orientations, while 2) the rate at which slip obstacles are produced before stage I1 is fully developed is strongly controlled by the amount of slip on more than one system. This second statement is consis-

Jan 1, 1961

By R. A. Anderson, T. E. Tietz, J. E. Dorn

Recent investigations1,2,3,4 have conclusively shown that the strain hardened state of metals depends upon the temperature and strain rate of pre-straining as well as on the total plastic strain. A typical example of the effect of temperature of prestraining on the work hardening of metals is reproduced in Fig 1. When pure aluminum is strained at liquid nitrogen temperature the upper solid stress-strain curve (OFGH) is obtained. But when pure aluminum is prestrained to e2 = 0.153 at atmospheric temperature and the test is then completed at liquid nitrogen temperature, the curve OBCD results. Thus a prestrain E2 = 0.153 at atmospheric temperature gives a flow stress C when continued at liquid nitrogen temperature, whereas a higher flow stress G results when the specimen is strained exclusively at liquid nitrogen temperature to the same strain E2. Consequently the metal strain hardens more rapidly at the lower temperature. Obviously the strain alone is not a measure of the strain hardened state in metals. Inspection of Fig 1 reveals that the flow stress at C is identical with that at F. This fact suggests that a strain E2 = 0.153 at atmospheric temperature induces the same work hardened state as a strain E1 = 0.058 at liquid nitrogen temperature. But this concept of equivalent strains is also in error. If curve CD is shifted to the left so that point C falls on F, point D becomes D'. Inspection of the curves reveals that the rate of increase of stress with strain at C is greater than the rate of increase of stress with strain at F even though the flow stresses are identical. Consequently C and F do not represent identical work hardened states. It therefore becomes important to ascer- tain how the strain hardened states at C and F might differ from each other. In a more recent report1 it was shown that straining at higher rates of strain increases the amount of strain hardening in a manner quite analogous to straining at lower temperatures. These observations suggested that the flow stress is not only a function of the strain but also a function of the strain rate-temperature history of straining, perhaps in accord with the Zener- ?H Hollomon parameter p = Ee /RT (where

Jan 1, 1950

By R. G. Davies

WeERTMANI has shown that the high temperature steady state creep rate, i, in lead and indium-base alloys obeys an equation of the form where AH is the activation energy, o the applied stress, n the stress exponent, and R and T have their usual meanings. He observed a variation in n from 4.5 for pure metals to 3 for concentrated alloys, which he interpreted as due to Change in creep mechanism from the climb of dislocations in pure metals to a micro-creep mechanism in the alloys. The Cottrell-Jaswon microcreep mechanism of the moving dislocation taking its impurity atmosphere with it was considered to be the most likely process, although short-range order and the segregation of solute atoms to a stacking fault will also give a stress exponent of 3. Steady state creep has been investigated in a Au - 27 at. pct Cu alloy at temperatures above 1/2 TIM where TIM the absolute melting temperature. As the oxidation resistance of this alloy is excellent all tests were carried out in air with a furnace built to give a temperature variation of less than 1°C along the 60 mm gage length. A lever-arm arrangement applied the stress with a load being adjusted between each creep test to maintain a constant stress. As each test produced less than 0.5 pct creep strain, the variation in stress during the test was negligible. The creep strain was measured by a transducer at the end of one of the alloy-steel grips, with the out of balance potential being finally recorded on a variable speed chart recorder. A typical creep curve is shown in Fig. 1. The results, Fig. 2, confirm that n is nearer to 3 than to 4.5; the creep mechanism could be any of those given above. The activation energy, AH, which is independent of stress, is consistent with a diffusion controlled process; the activation energies for the self-diffusion of gold and for the diffusion of gold into Copper are both -45 kcal per ml., There is now considerable evidence, that, when the steady state creep is dependent upon diffusion, irrespective of the actual creep mechanism, the activation energy is independent of the stress. The author would like to acknowledge the financial assistance provided by the International Atomic Energy Agency, Vienna, and the Argentine Atomic Energy Commission.

Jan 1, 1962

By C. W. Macgregor

The observation of the flow layers, or Luders' lines, produced in mild steel when it is stressed into the plastic range often provides considerable useful information for the study of the fundamental mechanism of the plastic flow of metals. It is a commonly observed fact that as soon as the upper yield point in a mild-st'eel tensile-test bar is passed, an unstable condition develops in the equilibrium, the load on the testing machine drops and if the surface of the bar contains a thin mill scale, the latter begins to flake off rapidly along certain "lines." These "lines" are ill reality traces of wedge-shaped flow layers and are formed by the inter-section of the surface of slip and the surface of the bar. The average plane of the flow layer itself has been found by various experimenters to be inclined at an angle of approximately 45" to the axis of the test bar. In a body of more complicated shape stressed in possibly a different man-ncr, the tangent planes to the flow layers at each point seem in many cases to be inclined at an angle of about 45" to the principal stress direct-tions at the point. As examples of the latter may be mentionecl the logarithmic spirals obtained when a rivet hole is punched in a thin plate, or when a tube is subject,ed to internal pressure only, etc. IIencc if the flow layers are observed from an experiment, the shear-st'ress trajectories —the curves indicating the direct,ions of the maximum shearing stresses in the body—may then be approximately determined. Since the latter curves form an orthogonal family inclined at 45" to the principal stress directions, the family of principal stress trajectories, or the curves irldicating the directions of the principal stresses, may be thus obtained Although the discontinuous type of stress-strain curve at the yield point is commonly observed with test bars of mild steel, more recent experiments have shown that this is by no means the only material exhibiting this interesting phenomenon. A similar effect has been observed in zinc and cadmium crystals, by Becker and Orowai~; in duralumin and other aluminum alloys, by Dawidenkow,~Elam,~ Fell4 an(l others; in copper and copper-alloy crystals, by Elam;~ in brass by Elam;3 in brass wires by deForest;" in higher carbon steels, tungsten steel, and

Jan 1, 1939

By C. W. MacGregor

The observation of the flow layers, or Luders' lines, produced in mild steel when it is stressed into the plastic range often provides considerable useful information for the study of the fundamental mechanism of the plastic flow of metals. It is a commonly observed fact that as soon as the upper yield point in a mild-st'eel tensile-test bar is passed, an unstable condition develops in the equilibrium, the load on the testing machine drops and if the surface of the bar contains a thin mill scale, the latter begins to flake off rapidly along certain "lines." These "lines" are ill reality traces of wedge-shaped flow layers and are formed by the inter-section of the surface of slip and the surface of the bar. The average plane of the flow layer itself has been found by various experimenters to be inclined at an angle of approximately 45" to the axis of the test bar. In a body of more complicated shape stressed in possibly a different man-ncr, the tangent planes to the flow layers at each point seem in many cases to be inclined at an angle of about 45" to the principal stress direct-tions at the point. As examples of the latter may be mentionecl the logarithmic spirals obtained when a rivet hole is punched in a thin plate, or when a tube is subject,ed to internal pressure only, etc. IIencc if the flow layers are observed from an experiment, the shear-st'ress trajectories —the curves indicating the direct,ions of the maximum shearing stresses in the body—may then be approximately determined. Since the latter curves form an orthogonal family inclined at 45" to the principal stress directions, the family of principal stress trajectories, or the curves irldicating the directions of the principal stresses, may be thus obtained Although the discontinuous type of stress-strain curve at the yield point is commonly observed with test bars of mild steel, more recent experiments have shown that this is by no means the only material exhibiting this interesting phenomenon. A similar effect has been observed in zinc and cadmium crystals, by Becker and Orowai~; in duralumin and other aluminum alloys, by Dawidenkow,~Elam,~ Fell4 an(l others; in copper and copper-alloy crystals, by Elam;~ in brass by Elam;3 in brass wires by deForest;" in higher carbon steels, tungsten steel, and

Jan 1, 1939

By Michael Perch

The fact that coal is a complex organic material and heterogeneous in composition has made its study extremely difficult, particularly in regard to obtaining a fundamental concept of the processes involved in the formation of coke. It has been stated recently that coals are natural polymers and that in a complex reaction such as occurs during carbonization the differences between coals are quantitative and not qualitative. Such being the case, it would be expected, therefore, that a series of coals subjected to exactly the same conditions of coking would produce results that should be related quantitatively to the chemical analyses of the individual coals. In the past, however, this fact was not generally recognized and consequently many empirical test methods were devised for testing coals. The interpretation of the results obtained depended upon comparing a set of data with other data on coals of known characteristics. The testing procedure had to be con- ducted in precisely the same manner each time and not the least requirement in making the interpretation was experience. The test methods varied from those utilizing a gram of coal to the plant-scale tests in which one or more ovens were charged with the test coal. The aim had been principally to find some simple, inexpensive means by which the coke-making and other properties of coal could be predicted. It is not necessary to emphasize the importance of these endeavors, for anyone acquainted with the problems involved in the selection of coals for making coke is well aware of the time and expense involved in making a series of definitive tests.

Jan 1, 1949

By L. D. Jaffe, H. C. Mann, E. L. Reed

It has been generally believed that fracture originates at a point and, if the stress is suficient, propagates across the material from this point. Evidence to the contrary is given in Fig 1. This micrograph shows an area close to the fracture of a steel containing The material had been quenched from 1675°F and tempered at 1150°F as a round about 10 in, in diam, and had a static tensile strength of 132,000 psi and a static yield strength of 105,000 psi. The steel was broken in 3000 cycles of reversed bending at a nominal max. fiber stress of 110,000 psi at a speed of 10,000 rpm. It was in the form of a standard R.R. Moore specimen with 45" V-notch, 0.015 in. radius and 0.220 in. diam at base of notch. The fractured edge in Fig 1 is part of the central portion of the specimen which broke during the final sudden fracture. Attention is directed to the short cracks which appear as dark lines within the specimen. Similar cracks were found in another specimen of the material, broken in 1,798,000 cycles at a nominal stress of 40,000 psi. The cracks were found in several areas close to the path of the final sudden fracture. This final fracture appeared microscopically to be wholly brittle and transcrystalline. Closer to the surface of the specimens, near the path of progressive fracture, which presumably advanced gradually during many cycles, there was microscopic evidence of some local deformation, but no microcracks. Neither were microcracks observed in areas distant from the main fracture path. The following explanation is offered: In the sudden fracture of the specimen, a crack propagates along a crystallo-graphic plane, with little or no plastic deformation of the adjacent material, until it reaches a grain boundary or a particle of carbide or inclusion which stops its advance. (The particle or boundary may be outside the plane of polish and not visible in the micrograph.) A stress concentration occurs about the end of the stopped crack. One or more new cracks are likely to start in the zone of this stress concentration. They may lie in the same grain as the first crack or in an adjacent grain. New cracks may occasionally start in a nearby but not adjacent grain whose orientation with respect to the stress leads to more ready fracture than does that of the grain between. Once started, these cracks propagate along crystallographic planes in their grains and the process repeats. This leads to discontinuous, branching chains of microcracks. As the process continues, microcracks probably tend to link up by fracture of intermediate material under the influence of increasing stress concentration. Occasionally, too, there may be a series of nearby grains of similar orientation so that there is a certain continuity of fracture across them. In either case the effective size of a crack is increased, resulting in greater stress concentration at its ends and a greater likelihood of further increase of size of the continuously-fractured region. When one continuous crack crosses the entire specimen, macroscopic fracture has occurred. The fractured edge of the specimen in Fig 1 represents a series of microcracks which became continuous across the entire specimen. The short, dark-appearing cracks in the figure did not become continuous over a large area. The row of microscopic stress concentrations at their ends may link up with those of the "main crack" outside the plane of polish. The above explanation does not imply that microcracks develop at the same rate in all portions of the specimen. They will develop most rapidly where the macroscopic tensile stress and macroscopic stress concentration are greatest. Viewed on a scale large compared to the grains, the fracture would appear to progress continuously across the specimen. Although Fig 1 shows a specimen broken in a fatigue test, it is believed that the microcracks discussed do not depend on the repetitive nature of the stressing used, since they are in the region where "sudden" fracture occurred, presumably in a single stress cycle. The whole process of microcrack propagation outlined above is thought to have occurred during this single cycle. It is believed that discontinuous crack propagation may be universal in brittle transgranular fracture of crystalline solids. Further experiments are under way.

Jan 1, 1950

By W. D. Ludemann, J. E. Dor, L. A. Shepard

Recovery of the creep resistance of 99.99 pct pure Al was studied at temperatures 540°, 573°, 600°, and 611°K. Poly-crystalline specimens crept under a stress of 950 psi to a strain of 5.5 pct were allowed to recover for periods of from 1 min to 16 days under a residual stress of 4.4 psi. Increased creep rates upon reapplication of the 950 psi stress evidenced softening of the material. The activation energy for the recovery process was found to be 64,000 cal-per mol. THREE major observations have clearly revealed that the creep of polycrystalline aluminum above about 510°K is controlled by the rate of climb of jogged edge components of dislocations past the barriers impeding their motion: 1) Extensive polygonization, characteristic of climb, takes place during creep.'9' 2) The activation energy for creep equals the estimated activation for self-diffusion. 3) The stress law for creep coincides with theoretical predictions based on the climb mechanism.4,5 The decreasing rate during the primary stage of creep must be ascribed to the introduction of additional barriers to the glide of dislocations. During secondary creep the density of barriers must remain constant, the rate at which new barriers are formed being equal to the rate at which they recover. For this reason the nature of the barriers, and their rates of formation and recovery, are significant to a complete understanding of creep. It is proposed here to study the kinetics of the recovery of barriers to creep of high-purity polycrystalline aluminum in the climb range. The technique will consist of creeping a series of tensile specimens under a prescribed stress to given state following which the specimens will be recovered for various times and temperatures under approximately zero stress. The amount of recovery will be determined by comparing creep curves following the recovery. EXPERIMENTAL PROCEDURE The material used for this investigation was a 99.99 pct pure Al supplied by the Aluminum Co. of America in sheets of 0.001-in. thickness having an H-18 temper. The spectroscopic analysis of impurities gave Cu-0.004 wt pct, Fe-0.002 pct, Si-0.001 pct, others-0.000 pct. Creep specimens were machined with their tensile axes in the rolling direction of the sheets. Annealing in a molten potassium nitrate-potassium nitrite bath for 1 hr at 686K, followed by air-cooling, resulted in a grain diameter of from 0.22 to 0.27 mm. Creep machines were equipped with constant stress lever arms of the type suggested by Fullman, Carreker, and Fishher,' which maintained the applied stress to within 0.04 pct of the reported value of 950 psi. Creep strains were calculated from extensions over a 6-in. gage section to the nearest 3 X 10"5. The temperatures of testing, 540°, 573", 600°, and 611°K, were obtained by immersing the specimen and extensometer assembly in a molten KNO2-KNO3 bath. Temperatures during the periods of creeping could be maintained constant to within better than ± 1°K. Correlation of creep data at different temperatures of testing demanded the use of an appropriate temperature-compensated time 8. Previous investigations have shown that the creep of pure metals at temperatures above about 0.55 of their melting temperatures can be correlated by the functional relationship3" e=f(0), s= const. [1] where e = total plastic strain during creep f = a function that depends on stress a = stress 6 = te-Q/RT = a temperature-compensated time t = time under test Q = 35,500 cal per mol = activation energy for creep R = gas constant, and T = absolute temperature In the present series of tests all of the creep was conducted under the same stress of 950 psi. To provide identical initial conditions for the recovery all specimens were first crept to a temperature-compensated time of = 47 X 10-14 min which resulted in a creep strain of 0.055 + 0.005 regardless of the creep temperature. During recovery, a small stress (4.4 psi) was permitted to remain upon the specimens to maintain tautness in the pulling assembly and to prevent mechanical damage to the soft specimen. After each recovery period, the full stress was reapplied and

Jan 1, 1961

By T. C. Atchison, W. I. Duvall

Over the past ten years a series of investigations have been conducted to determine some of the pnysical processes involved in breaking rock with confined concentrated charges. Detailed discussions of many of these investigations have been published elsewhere.1-6 Laboratory experiments made by other investigators using Hopkinson pressure-bar techniques have shown that solid materials are fractured in tension by the reflection of an incident compressive stress pulse at a free surface.7-12 In these tests a small charge of explosive is placed in contact with one end of a bar. Detonation produces some plastic flow and crushing of the bar near the charge and generates a compressive stress pulse that travels along the length of the bar. At the free end of the bar the compressive stress pulse is reflected back into the bar as a tensile stress pulse. If the tensile strength of the bar is exceeded during this reflection process, a tensile fracture normal to the length of the bar is produced, and the broken end of the bar moves forward with a constant velocity equal to the average particle velocity trapped in the broken fragment. The new surface formed by the fracture becomes the new free end of the bar that reflects the remaining portion of the incident compressive stress pulse. This process is repeated any number of times until all of the incident stress pulse is reflected. Hino has demonstrated this kind of breakage for three rock types—marble, granite, and sandstone." He has defined a blastibility coefficient, B, as the ratio of compressive strength, C, to tensile strength, T, thus: C The quantity B is the maximum number of slabs that can be produced by reflection breakage. Normally fewer slabs are produced because of loss of energy as the stress pulse travels through the rock. Fig. 1 illustrates reflection-type fracture for a triangular compressive stress pulse. The number of slabs produced by the reflection breakage process is the first whole number less than the ratio of the peak stress of the incident pulse to the tensile breaking stress of the solid. Thus the number of slabs is given by the thickness of each slab is given by and the total length of rock broken is given by N = number of slabs S - peak stress in incident pulse T = tensile strength of the rock F = fall length of incident stress pulse h = thickness of each slab D = total length of rock broken During the reflection process the particle velocity at the free surface is twice the particle velocity in the incident stress pulse. Thus the velocity with which the broken fragments move forward is given by where v, = velocity of broken fragment, and v = average particle velocity contained in that portion of the incident pulse trapped in the broken fragment. Results of these laboratory experiments cannot be applied directly to rock blasting where the explosive charge is placed in a drillhole. In laboratory tests the charge is unconfined and in contact with the rock in only one direction. In a drillhole additional confinement is offered by the rock surrounding the charge and by the stemming placed above it. This additional confinement may be enough to allow the explosive gases to do additional work on the rock during their expansion. Other writers have discussed possible effects of gas expansion'on rock breakage.13-10 However, very few experimental data are available to determine to what extent expansion of the gases is responsible for rock fragmentation. The USBM has studied the physical processes involved in breaking rock with confined concentrated charges by using simple crater tests breaking to one free surface. Crater tests have been performed in four rock types: granite, sandstone, marlstone, and chalk. Table I gives some physical properties of these rocks. Fig. 2 shows plan and section drawings of two typical crater tests and illustrates some of the test variables measured. For these tests the charge was placed at the bottom of the drillhole and primed with an electric cap. The hole was stemmed to the collar with sand and the charge detonated. Size and shape of the crater were measured after it was cleared of broken rock. As a given charge size was buried deeper in a drillhole, the crater depth usually was equal to or

Jan 1, 1960

By W. L. Phillips

Stress-train curves were obtained for single crystals of silver, Ag-5 pct Zn, Ag-10 pct Zn, and Ag-20 pct Zn tested in tension and shear at 78°, 195°, and 297°K. At room temperature the critical resolced shear stress gC increased, the length of' the easy-glide region increased, and the rate of' work hardening dwving easy glide decreased with increasixg zinc concentration. The change in the ratio of uc at room temperature to that at lower temperatures was significantly greater for the alloys than for pure silver. It was found that an increment in stress was necessary to continue slip when the slip direction was rotated 60 deg. The magnitude of this increment increased with strain for all alloys, increased with zinc concentration for a given strain, and for a given strain increased with decreasing -temperature. DESPITE its practical importance in improving the mechanical properties, alloying is not fully understood. Except for copper alloys few sets of systematic data are available. Von Goler and Sachs' studied the deformation of Cu-Zn alloys of increasing zinc content and found that, for dilute alloys, the critical resolved shear stress increases linearly with concentration. The range of easy glide was found to increase with increasing zinc content. Schmid and seliger,2 Sachs and Weerts,3 and Osswald4 have shown that with Mg-A1, Au-Ag, and Cu-Ni crystals, respectively, the critical resolved shear stress also varies linearly with concentration. More recently, Linde and his coworkers have investigated the variation of the critical shear stress of copper alloyed with tin , antimony, indium, germanium, silicon, nickel, and gold. They found that the slope of the critical resolved shear stress is related to the change of lattice parameter with composition, and also to the difference in Goldschmidt's atomic diameter between solvent and solute atoms. Garstone, Honey-combe, and creetham6 have shown that similar relationships can be found for small additions of silver, gold, and germanium to pure copper. They found that, with increasing silver or gold concentration, the critical shear stress for glide is increased by alloying, and so is the range of easy glide, which reaches as much as 60 pct for 0.50 pct Ag alloy and 0.62 pct Au alloy, as compared to 6 pct for pure copper of similar initial orientation. They also found that the alloying additions had little effect on the rate of hardening during easy glide, the slope scarcely changing with increasing alloy content. General secondary slip was detected only when the crystals began to harden rapidly. Although the slip appeared to be very fine in the early stages of deformation, coarser slip bands were formed towards the end of the extensive easy-glide range. The present investigation describes the deformation characteristics of single crystals of Ag-Zn containing different concentrations of zinc. Tension and shear testing were used for this study. EXPERIMENTAL PROCEDURE The method of growing the single crystals, sample preparation, and method of testing have been described in detail previously.' EXPERIMENTAL RESULTS A) Tension-Room Temperature. The initial orientations and stress-strain curves of single crystals of silver, Ag-10.0 pct Zn, and Ag-20.0 pct Zn are shown in Fig. 1. It is evident that there is considerable change in the stress-strain characteristics as a function of zinc concentration. The effects of zinc concentration on the critical resolved shear stress for both CU-zn8 and Ag-Zn alloys are summarized in Fig. 2. At all concentrations the resolved shear stress of the Cu-Zn alloys is higher than that of the Ag-Zn alloys. The resolved shear stress increases parabolically as a function of composition for both alloy systems. The length of easy-glide region increased with increasing zinc concentration, Fig. 3b). As the length increased the slope (do/de) decreased slightly, Fig. 3(b). Metallographic investigations demonstrated two significant effects of increasing zinc concentration. First, the amount of clustering increased, compare Figs. 4(a) and (b). The slip lines changed from uniform in pure silver to clustered in the Ag-20 pct Zn and Ag-30 pct Zn alloys. Second, the amount of cross slip decreased as the amount of clustering decreased.

Jan 1, 1968

By Jeffrey N. Schuyler

In order to implement the most efficient and cost-effective hydraulic fracturing stimulation treatment within a particular region, a thorough understanding of the in-situ stress state and rock properties is paramount (Smith et al., 1978; Warpinski et al., 1982). Several studies conducted in order to "characterize" formations have provided invaluable insight into the relationship between lithologic properties, depth, in-situ stress magnitude and hydraulic fracture orientation. These studies have substantiated that at shallow depths, rock properties such as tensile strength and permeability can exert a substantial influence on the geometry of an induced hydraulic fracture. In turn, these "directional properties" can be related to existing geologic conditions during the time of deposition or major diagenetic alteration of the rock body. As the depth of the "payzone" increases, the role of the in-situ stresses and therefore the prevailing tectonic conditions becomes the dominant factor in determining fracture geometry. However, reservoir properties cannot be ignored. The porosity, permeability, pervasive fabric element and directional elastic properties can have a significant influence on the success of those tests conducted to measure the in-situ stresses either directly or through secondary observations... for instance, pore-pressure effects on measurements of in-situ stress. The purpose of this paper is to provide, through the use of appropriate field and laboratory examples, a more thorough understanding of in-situ stresses, rock properties and their integrated effect on hydraulic fracture properties. In addition to highlighting and expanding the wide body of existing literature, the case studies cited are designed to encourage mutual transfer of technology from petroleum-related, rock-mechanics efforts to other disciplines.

Jan 1, 1984