By Marcel R. Daly

The writer has devoted a number of years to practical operations and to the study of geology in the oil fields. In consequence, he has been brought to investigate the theories advanced to account for the accumulation of oil and gas in commercial deposits. It is the result of these investigations and his personal conclusions that he wishes to sum up in this paper. The writer is an advocate of the organic origin of petroleum found in pools. He has been led to believe that the present theories of oil and gas accumulations are incomplete and, in certain respects, incorrect, although they may embody certain elements of truth; that the forces that are called upon to explain the movement are only secondary forces in the process, and insufficient, by themselves, to cause this movement; and that the phenomenon of accumulation is of much larger order than heretofore admitted and bears an intimate relation with the general as well as with the local deformations of the crust and is a direct consequence and a mechanical effect of these deformations to which the term " diastrophie " has been applied. As a complement to this theory, the writer offers a new interpretation of the "rock pressure" and of the mechanism of the "sealing up" of this pressure in oil and gas pools. The Anticlinal Theory The theory most generally accepted to account for the accumulation of hydrocarbons in commercial deposits is the anticlinal or structural theory. This theory, the principles of which have been laid down by I. C. White, Orton, Winehell and others, and which has since been modified and perfected, is too well known to need a detailed statement. A clear interpretation of it may be found, in the paper of W. T. Griswold, in Bulletin No. 318 of the United States Geological Survey, and the reader is

Jan 1, 1917

By H. B. Smith, B. Egererg

In a previous paper1 the authors dealt with the physical properties of cold-rolled and heat-treated Britannia metal of the approximate composition Sn, 91 per cent., Sb, 7 per cent. and Cu, 2 per cent. It was found that cold rolling to more than 50 per cent. reduction produced a continuous softening of the metal when measured by the Brinell machine, whereas the Shore instrument indicated increased hardness; that the strength of the material followed the Brinell hardness and that the metal therefore became weaker the more it was cold-rolled; and further, it was found that hardness and strength could be largely restored to the cold-rolled metal by "baking" for about one hour at any temperature between 200" and 450" F., the melting point. The higher the baking temperature, the more effective was the heat treatment as far as increased hardness was concerned. It seemed to be of little importance whether the metal was soaked or not at the baking temperature for a great length of time and the rate of cooling seemed to be immaterial. The present paper deals with the same alloy and more particularly with the resistance towards various forms of stress — tensile, bend and deep drawing. The metallography of Britannia metal has in part also been covered and an explanation attempted for the abnormal behavior of this alloy. Tensile and Bend Tests Two ingots 73/4 in. wide, 11 in. long and ¾ in. thick were cast from the same pot. One ingot was cold-rolled in one direction to a strip 0.241 in. thick, which furnished the tensile test specimens; the other ingot was rolled in the same way to 0.253 in. and furnished the specimens for the bend tests. The ingots were cast as described in the previous paper and cold-rolled in six passes.

Jan 1, 1930

By Robert Palmer

So MUCH has already been written on this vast subject of ground movement and subsidence, and so many data collected and commented upon, that in this paper the author proposes to confine himself to the submission of some plans showing what has actually occurred in the mining of several of the orebodies which have, come under his direction during the last 20 years or so at Rio Tinto, Spain. Some notes are added for the purpose of describing the plans. The author does not attempt to give his opinion as to the reasons why the subsidences have occurred in the manner in which they are found, but confines himself to giving as true a picture as possible of the movements that have taken place.

Jan 1, 1930

By W. C. T. Yeh, T. G. Oakwood, A. A. Hendrickson, R. H. Hammar

The objective of the research is to determine whether solid-solution strengthening effects observed in dilute solutions of silver can be accounted for by the influence of the solute addition on the dislocation structure oj- the crystals. The additions of both tin and indium produced only small changes in the dislocation densities and arrangements in silver crystals. However, as found previously, small solute additions have large effects on the tensile properties; the inj-luence of the tin and indium additions on the temperature dependence of the flow stress and the easy-glide range is especially strong; It is concluded that the indirect strengthening effect of the solute due to variations in the dislocation density as proposed by Seeger is of minor importance and that solute atom-dislocation interactions are responsible for the observed strengthenirzg effects. The experimental results were combined with those of Rogausch to test the concenlvatiorz dependence of solute strengthening. Both the first and one-half power dependences of the critical resoleed shear stress on concentratiorz fail in very dilute solutions. THE objective of the research is to determine whether solid-solution strengthening effects observed in dilute solutions of silver can be accounted for, at least in part, by the influence of the solute addition on the dislocation structure of the crystals. It is recognized that the addition of solute atoms may influence the strength properties of a metal through both "direct" and "indirect" effects. The former refer to the strengthening mechanisms that result from the interaction of solute atoms with dislocations; in the latter case, the strengthening effects arise as a result of solute's influence on quantities such as dislocation density, dislocation arrangement, stacking-fault energy, diffusivities, the elastic constants, and so forth. It is clear that the correct interpretation of solid-solution strengthening phenomena cannot be given until the importance of indirect strengthening effects is properly evaluated. In the particular case of close-packed metal crystals, Seeger showed that solute strengthening effects in dilute solutions of copper and silver might be accounted for by an increase in dislocation density due to the addition of the solute. Seeger's argument was that the strengthening effects extrapolated from more concentrated solutions indicate that small concentrations of impurities raise the critical resolved shear stress much more than is predicted by a concentration-independent dislocation density. The above idea was a very reasonable one. The dislocation theories of work hardening of Taylor,2 Cot-trell, 3 Mott, 4 and seeger5 had already associated the increased flow stresses with increased dislocation densities in deformed metals; investigations of the dislocation structure of metal crystals had provided a logical basis for expecting an increased dislocation density in crystals containing impurities (see for example, Ref. 6). The numbers involved seem reasonable, too. It can be expected that the flow stress of the crystal would increase as the one-half power of the dislocation density.' Solute additions of 1 at. pct to metal crystals result in strength increases by factors in the range of three to ten. If one assumes that the strengths of the pure metal crystals are determined by their dislocation densities, then dislocation-density increases of one to two orders of magnitude as a result of solute addition would be required to account for the observed strengthening—not an unreasonable expectation. In addition to the effect of the solute addition on dislocation density, one might also anticipate important strengthening contributions to result from the solute's influence on the dislocation arrangement. Parker and washburns have reviewed a number of experimental evidences which show important strengthening effects due to the presence of subboundaries. Further, lattice strains due to impurity segregation would be expected to influence the distribution as well as the dislocation density of the as-grown crystal. As pointed out in the reviews of Chalmers,6 Elbaum,9 and winegard,lo micro segregation of impurities occurs at all interfaces of crystals in cellular growth; the impurity gradient results in lattice strains which can be reduced with the presence of dislocation arrays in the region of the impurity gradient. Hence, one would expect the presence of a solute to favor the formation of dislocation subgrain structures and that the subgrains would have an important influence on the strength of the crystal. The experimental observations that concern the possibility of an important strengthening contribution through the influence of the solute on the dislocation density or arrangement are not in agreement. Haasen has reviewed the observations of Meakin and Wils-dorf,12 Howie,13 and Bocek 36 and concluded that the solute's influence on dislocation density is not sufficient to account for strengthening effects in concentrated solutions but might, as seegerl suggested, make an important contribution in very dilute solutions. On the other hand, Hendrickson and Fine 14 concluded that changes in the dislocation density and dislocation width accounted for the solid-solution strengthening effects observed in silver-based aluminum solid solutions. Goss et a 1.I5 observed dislocation arrays in Ge-6 at. pct Si, Ge-0.2 at. pct Sn, and Ge-0.2 at. pct B crystals that were not observed in germanium crystals of

Jan 1, 1968

By H. Le Chatelier

Jan 1, 1894

By B. C. Allen

The interface energies of chronzium, molybdenunz. hugsten, and their solid-solution alloys Cv-35Re, MO-33Re, and UJ-25Re were studied at 0.6 to 1.0 of the absolllte liquidus ter)zpe,vature using fiz&apos;e )izethods. Liquid surface tension, yv , was deter mined clsing the pendant-drop and drop-weight methods. Results are, respectizlely, 1700, 2370, and 2480 +100 dynes per ct for the rhernium -containing alloys and essentially the same as tlwse reported for liquid chro)riln, trolybdenum, and tungsten. Average solid slrjace energy, rsv< xias ))zeasured using tlre fiber-extetlsion method. The ratio of ysS, the acerage high-angle grain-boundary energy, to ySV cclas jolnd fronz grain-bolzdary grooue angles fort)zed at the surface in an inert atrfizosphere. Absolllte iute?:face energies were deterawined using ?nultip/rase equilibria involzing suitable liquids of known surface tension (tin, silver). Interpretation of the experimented results in view of pvobable tenzperatzcre, orientation, and purity effects giz,e the follouling approximations in ergs per sq ctn: ysv (i2lo. Mo-33Re) - 2100, ySS (Mo, Mo-33Re) - 800, rr (defornzation twins in MO-33Re at 1200"C) - 800. ysV (Cr. Cr-35Re) - 2400. YSS (CY, Cr-35Re) - 1000. Probably Ylv- YSV- 2500 for tungsten and W-25Re, giving yss (It&apos;, W-25Re) - 900. The interface energies of solid and liqid ch?&apos;omiu?.z, nolybdenu?rr, and tungsten are not geatly aff&apos;ected by rhenium and therefore are not a ttlajor factor in the ductili zing rhenium effect in Croup VI-A metals. THE interface energies of the refractory Group VI-A metals, chromium, molybdenum, and tungsten, are not well-established. The objective of this investigation was to study the liquid surface tension, solid surface energy, and grain-boundary energy of these metals and compare them to those found for the bcc solid-solution alloys, Cr-35e,&apos; 0-33e,&apos; and -25e. Five techniques were used to measure interface energies in high-purity polycrystal rod, wire, and sheet at 0.6 to 1.0 of the absolute liquidus temperature. The alloys were chosen to see if there was any connection between interface-energy behavior and the ductilizing rhenium effecL4j5 EXPERIMENTAL WORK Materials. A description of the materials used is presented in Table I. Chromium rod was prepared by arc melting iodide process crystals supplied by Chromallo Cor., hot extruding, and warm swaging to 0.63-cm-diam rod.6 The sheet was prepared by rolling as-extruded rod to 95 pct reduction in area from a hydrogen furnace at 800" to 900°C and surface grinding off 0.02 cm from each face. Cr-35Re rod was prepared by arc melting sintered rhenium powder and iodide chromium crystals, warm rod rolling to 50 pct reduction in area in cans, and swaging to 60 pct reduction in area at 1100" to 1200°C. Some of the rod was warm-rolled to sheet and then surface-ground. Portions of swaged chromium and Cr-35Re were further reduced by swaging and drawing to 0.013-cm-diam wire by the General Electric Co. Mo-33Re and W-25Re rod, sheet, and wire were provided by Chase Brass and Copper Co. The molybdenum sheet consisted of two lots, both essentially the same except for the carbon content. Liquid Surface Tension. The liquid surface tension of Cr-35Re, Mo-33Re, and W-25Re was measured by a combination of pendant-drop and drop-weight methods using techniques already decribed." Following out-gassing, molten drops were formed on the ends of centerless-ground Mo-33Re and W-25Re rods by electron bombardment at 5 x 106 mm. Similar drops were formed on outgassed Cr-35Re rods by induction heating under 1 atm of 99.995 pct Ar. Solid Surface Energy. Solid surface energy was measured by conducting microcreep experiments on molybdenum, Mo-33Re, chromium, and Cr-35Re wires at 2350°, 2306, 1550°, and 180O°C, respectively. In preparation, gage marks -2.5 cm apart and -0.001 cm deep were circumferentially scribed on the wire with a razor blade. Weights of the wire material were then attached. Five to seven reasonably straight wires were hung in a container made out of the wire material. The free end was placed through a small hole in the removable top and secured by bending a small portion 90 deg. The containers not only tended to provide vapor-solid equilibrium for the wires but also protected them from gaseous impurities. They were nominally 2.5 cm in diam by 5 cm high and were made from extruded chromium rod, Cr-35Re arc casting, molybdenum bar stock, or welded Mo-33Re sheet. After deg re as ing, the assembly was outgassed at a relatively low temperature to 2 x 10"5 mm and then recrystallized 2 to 8 hr at the creep temperature in a rhenium-element resistance furnace. The static argon atmosphere was gettered by tantalum radiation shielding. Specimen temperature was measured optically to 25"C using calibration with known melting points and blackbody conditions. The wires generally developed a stable bamboo-type structure according to Fig, l(b), (c), and (d) and retained their gage marks [upper portion of Fig. l(d)]. One or two of the weights were clipped off to provide a low load for the creep anneal. To minimize the possibility of bending or breakage, the wires remained attached to the top of the annealing container which was held to keep the wires vertical. The distance between gage marks was

Jan 1, 1967

By J. Murray Riddell, Arthur E. Anderson, Grover J. Holt

OUT of the depths of each business cycle we emerge with a stimulus for greater efficiency and a realization of progress in industrial technique. The recent years have not been an exception to this rule, and in retrospect we sense that significant advances have been made in mining practices on the Mesabi Range, with emphasis on speed of production and economy of operation. A survey of such changes does not reveal anything that is fundamentally or basically new, but it is apparent that ideas and machines that have found wide application in industry elsewhere, with necessary modifications, are being put to productive use in mining iron ore. Innovations in transporting and conveying ore from the open pits stand out with greatest prominence, so that, in the main, it will be with these features that this paper will treat, in the review of progress made to this date. The late years have witnessed the development of small deposits for open-pit operation, the cleaning up of pits nearing exhaustion, and in two large operations the approach to the limit for haulage by steam locomotives, owing to grades, making it necessary to recover the ore in slopes, track benches and below the power-shovel limit by a milling and scram operation. For several years small standard-type dump trucks have been used in clean-up or scram operations within the pits, but during the seasor1 of 1936 the first effort was made to use heavy truck haulage in the transportation of stripping and iron ore. The new units in use today vary from 15 to 20 tons in capacity, and are equipped with powerful gasoline or Diesel engines and supplemented by trailers or wagons on rubber or crawler treads. The Diesel engine finds favor with most operators because of fuel economy. These units develop upward of 125 hp. in the 15-ton trucks. The speed of these trucks varies from 2 miles per hour in low gear to 35 in high gear. The transmission affords 12 speeds forward and 3 speeds in reverse.

Jan 1, 1938

By J. T. Mackenzie

Henry Marion Howe, in whose memory we are gathered together, was one of the great thinkers who develop from time to time to whom is given the rare gift of synthesis. Analysis is given to few, but synthesis, the ability to show the relation of all parts to each other and thus to give a clear picture of the whole, is reserved for the very few. Analysis can be achieved by honesty, intelligence, and industry, but synthesis is only given to genius. Professor Howe&apos;s crowning achievement is the picture of the whole iron-carbon series shown in Fig. I, which places steel, malleable, gray iron, mottled and chilled irons in their proper relation to each other and shows the essential unity of the series. Perhaps his best statement of the case is found on page go of the Metallography of Steel and Cast Iron in these words: " Each member of the gray cast-iron series consists of the metallic matrix approximately equivalent to that member of the steel-white-cast-iron series to which it corresponds in percentage of combined carbon with its continuity broken up—by masses of graphite ..." Apparently he had taken considerable interest in this idea around the turn of the century, for he refers to a discussion at the Franklin Institute in I900 in which he said: "Though many others had probably conceived this relation between the steels and cast irons, it was here enunciated for the first time, so far as I know. It was received with great incredulity." The concept was explained in some detail in a paper on "The Constitution of Cast Iron" presented before the A.S.T.M. in 1902 when Professor Howe was retiring president of that young society. In the discussion Dr. Sauveur stated that he was "very well acquainted with Professor Howe&apos;s theory of the constitution of cast iron," and went on to say that while he "shared it to the fullest extent, some foundrymen . . . claim cast iron is a metal entirely different from steel . . . that steel and cast iron have very little in common, and that therefore the knowledge gained in the study of steel is of little or no value in the study of cast iron." Dr. Moldenke, in discussing the same paper, said he had been working on the same theory for 12 years but he laid no claim to publication. Discussing the difference in the micro-structure of the metallic matrix, Professor Howe pointed out that "such minor structural differences are indeed to be expected, because of the difference in the conditions under which these constituents are generated. "One difference in these conditions is that the steel of most micrographs has been either forged or at least treated thermally in such a way as to give a new structure radically different from that which formed during the initial solidification, whereas the cast irons have not. Hence what we see in the steels is a transformation structure, but in the cast irons a solidification structure. By giving the cast

Jan 1, 1944

By J. T. Mackenzie

Henry Marion Howe, in whose memory we are gathered together, was one of the great thinkers who develop from time to time to whom is given the rare gift of synthesis. Analysis is given to few, but synthesis, the ability to show the relation of all parts to each other and thus to give a clear picture of the whole, is reserved for the very few. Analysis can be achieved by honesty, intelligence, and industry, but synthesis is only given to genius. Professor Howe&apos;s crowning achievement is the picture of the whole iron-carbon series shown in Fig. I, which places steel, malleable, gray iron, mottled and chilled irons in their proper relation to each other and shows the essential unity of the series. Perhaps his best statement of the case is found on page go of the Metallography of Steel and Cast Iron in these words: " Each member of the gray cast-iron series consists of the metallic matrix approximately equivalent to that member of the steel-white-cast-iron series to which it corresponds in percentage of combined carbon with its continuity broken up—by masses of graphite ..." Apparently he had taken considerable interest in this idea around the turn of the century, for he refers to a discussion at the Franklin Institute in I900 in which he said: "Though many others had probably conceived this relation between the steels and cast irons, it was here enunciated for the first time, so far as I know. It was received with great incredulity." The concept was explained in some detail in a paper on "The Constitution of Cast Iron" presented before the A.S.T.M. in 1902 when Professor Howe was retiring president of that young society. In the discussion Dr. Sauveur stated that he was "very well acquainted with Professor Howe&apos;s theory of the constitution of cast iron," and went on to say that while he "shared it to the fullest extent, some foundrymen . . . claim cast iron is a metal entirely different from steel . . . that steel and cast iron have very little in common, and that therefore the knowledge gained in the study of steel is of little or no value in the study of cast iron." Dr. Moldenke, in discussing the same paper, said he had been working on the same theory for 12 years but he laid no claim to publication. Discussing the difference in the micro-structure of the metallic matrix, Professor Howe pointed out that "such minor structural differences are indeed to be expected, because of the difference in the conditions under which these constituents are generated. "One difference in these conditions is that the steel of most micrographs has been either forged or at least treated thermally in such a way as to give a new structure radically different from that which formed during the initial solidification, whereas the cast irons have not. Hence what we see in the steels is a transformation structure, but in the cast irons a solidification structure. By giving the cast

Jan 1, 1944

By J. L. Craig, C. L. Edwards, M. D. Harper, J. M. Ray

The Los Alamos National Laboratory executed 19 intermediate scale cratering experiments in oil shale at the Colony Mine in Garfield County, Colorado. These experiments have led to a better under- standing of fracture characteristics and fragmentation of & - oil shale by use of a conventional high explosive. Geologic site characterization included detailed mapping, coring, and sample analyses. Site-specific geology was observed to be a major influence on the resulting crater geometry. The joint patterns at the experimental site frequently defined the final crater symmetry. Secondary influences included vugs, lithology changes, and grade fluctuations in the local stratigraphy. Most experiments, in both the rib and floor, were conducted to obtain data to investigate the fragmentation results within the craters. The rubble was screened for fragment- size distributions. Geologic features in proximity to the explosive charge had minimal effect on the rubble due to the overpowering effect of the detonation. However, these same features became more influential on the fracture and rubble characteristics with greater distances from the shothole. Postshot cores revealed a direct relationship between the grade of the oil shale and its susceptibility to fracturing. The Colony Mine experiments have demonstrated the significant role of geology in high explosive/oil shale interaction. It is probable that this role will have to be considered for larger applications to blast patterns and potential problems in retort stability in the future of oil shale development.

Jan 1, 1983

By J. M. Hodge

This paper represents a start on the problem of choosing alloy steels for a given application on the basis of toughness as indicated by the room temperature notched bar impact value at the desired hardness level, and as such, is very useful. I believe, however, that the authors will agree that it is only a start on this problem. The authors state that neglecting temper brittleness or other possible effects of the tempering temperature level, the impact values at a given grain size level will be determined principally by the hardenability. This is, of course, true inasmuch as the hardenability determines the microstructure, but it serves to emphasize the broad field that hardenability now covers, since this study apparently includes mi¬crostructures ranging from full martensite to coarse pearlite. Furthermore, the + or - 20 ft-lb spread in the correlation with hardenability, which certainly limits the usefulness of these results for many applications, indubitably reflects the wide range of microstructures corresponding to a given value of hardenability in terms of the difference between full martensite and asquenched hardness.

Jan 1, 1947

By C. H. Mathewson

COPPER and the copper-base solid solutions readily form twin crystals when plastically deformed at a suitably elevated temperature or annealed after cold deformation. In fact, no feature of the microstructure of these materials is more prominent or characteristic than these straight-sided bands or simple lines of division which sometimes come from groups of thin polysynthetic lamellae, penetrating part way or wholly through the parent grain substance, but often divide the grain into a few or perhaps only two crystallographically related parts. Nearly always the bands as seen in the usual microscopic examination of a specimen come into vivid contrast with the adjacent crystalline material owing to the inherent difference in orientation. Bands which under special conditions of orientation cannot be seen with vertically incident light are often visible under oblique illumination and, when this fails, contrasting effects usually may be obtained by using polarized light. There is no longer any doubt that these synthetic banded structures obtained in the ordinary course of working and annealing are due to twinning of the spinel type which was observed long ago in a number of metals crystallizing in the isometric system.1 It has been customary in metallurgical literature to designate these synthetic twins, which grow into prominence during an annealing process, as "annealing twins" without regard to the actual mode of their formation, which is, indeed, obscure and with scant recognition of the fact that prior deformation is essential, no twins having been observed in metal of known unstrained history. This is questionable; especially in view of. the fact that in a number of metals and minerals, reorientation into the twin configuration is known to occur as a result of a simple shearing mechanism along the recognized twinning planes and the

Jan 1, 1930

By Carl A. Zapffe, George A. Moore

IN a previous publication from this laboratory1 the conclusion was drawn that the embrittling effect of occluded hydrogen on iron and steel must result from the precipitation of the gas within small openings through the crystal structure. A review of the literature then published indicated the real existence of crystal sub- structures of the mosaic type and gave presumptive evidence that the "rift openings" associated with hydrogen occlusion are the same as the "disjunctions" of the mosaic theory. Inasmuch as no clear conception of the actual nature of the crystal fragments and openings inherent in these theories has been established, it was considered desirable to obtain direct micrographic evidence of their true configuration. In this direction the standard methods of metallographic attack have proved useless. Recourse was had, therefore, to the direct examination of the surfaces upon which failure by cleavage had resulted from the presence of hydrogen. It was expected that such a surface, un- affected by chemical attack and undistorted by polishing, would reveal the fine openings penetrated by the gas and thus indicate the real nature of the substructures. MATERIALS STUDIED In commercial steels, defects caused by hydrogen take various external forms ac- cording to such factors as structure and purity, and to the extent to which hydrogen either occludes or produces chemical changes. The present work relates only to the well-known transcrystalline hydrogen embrittlement-"pickling brittleness"-in which elemental hydrogen occluded within the grain develops cleavage characteristics. For example, hydrogen embrittlement resulting from hydrogen reaction products is excluded from detailed study. It was also desirable, as far as possible, to have the study uncomplicated by other elements which themselves cause brittleness. Three types of iron were used. These included ingot iron, decarburized free- machining steel, and a specially prepared, aluminum-killed, electrolytic iron. This , choice allowed a comprehensive selection of unavoidable minor impurities and inclusions, which could subsequently be shown to have no specific effects on the structures within the grains. Carbon, and any other impurities free to react with hydrogen, were first removed by a preliminary annealing treatment in hydrogen. Subsequent treatment in vacuo extracted much of this hydrogen and its gaseous reaction products. The resultant ductile iron was then embrittled either by a second anneal in hydrogen, followed by rapid cooling, or by cathodic electrolysis. Group I: Prepared from Armco Ingot Iron As shown in Table I, the principal impurity in this iron was oxygen, which survived the purifying treatment to a large extent. Two series were prepared. The first (Nos. SIO-24) was purified only one day in hydrogen and dehydrogenized one day in nitrogen. Containing both hydrogen and its

Jan 1, 1943

By R. A. Vandermeer, P. Gordon

The study of recrystallization in cold-worked metals is complicated by the impossibility of making direct three-dimensional optical measurements. Metallo-graphically, theinternal three-dimensional features of samples must be inferred from their intersections with the two-dimensional plane of polish. The inherent difficulties involved in this procedure have led— particularly during the last few years—to some instances of rather doubtful interpretations of experimental data in terms of nucleation and growth rates in recrystallization. In the present paper an analysis ; is given of the recrystallization characteristics in a polycrystalline alloy containing 0.008 wt pct copper in ZONE-refined aluminum *and an effort is madf to reemphasize the necessity in such studies for attention to the proper statistical relationships between one- two- and three-dimensional features of opaque samples. It is shown that, in common with several recently described cases for other types of transformations,1-5 recrystallization in this alloy can best be rationalized on the basis that all nucleation took place essentially at time zero—i.e., there is no significant time-dependent nucleation during annealing—and that the kinetics are controlled exclusively by the growth-rate parameters. This is true despite the fact that the number of

Jan 1, 1960

By E. C. Bain, E. S. Davenport

When annealed carbon, or low-alloy, steels are suitably heated the ferrite (alpha iron solid solution) and the carbide, of which they are composed, react together to form a single solid solution of carbon (and other elements) in gamma iron (austenite). This reaction may begin only at a certain minimum temperature called the eutectoid temperature. The first ferrite and carbide thus to react together do so in definite proportions known as the eutectoid composition. With further heating the original constituent that is present in excess is dissolved in the austenite until exhausted. Whether the excess constituent be ferrite (hypoeutectoid steels) or carbide (hypereutectoid steels) the procedure is much the same, and upon slow cooling the homogeneous austenite expels the excess of either (proeutectoid ferrite or carbide) until the eutectoid composition is reached. Thus the reaction upon heating is strictly reversed upon cooling and accordingly an equilibrium diagram of this process may be constructed. Such an equilibrium diagram concerns itself only with the temperatures involved and with the proportions and compositions of the phases developed under conditions that suffice to permit equilibrium. Specifically it has no concern for the type or mode of distribution of these constituents nor with any extra-equilibrium conditions such as undercooling, which is almost universally encountered in metals. Actually, however, of great importance is the sluggishness toward equilibration caused by the not inconsiderable time involved in diffusion. Thus instead of the theoretical transformation point AF, we find for a certain rate of heating or cooling the use of the designations Ar and Ac (transformation temperature found on cooling and upon heating). These figures obviously have no particular meaning except as measured and expressed for a definite heating or cooling rate, and represent the apparent temperature displacement caused by an inadequate time allowance. In this paper are presented the results of a study of the time required for the transformation of austenite to ferrite and carbide at a variety of temperatures and also of the time required for the reaction austenite? martensite at the temperatures at which this reaction occurs instead of

Jan 1, 1930

By Douglas J. Robinson

A pilot scale process has been developed to separate mercury, tin, silver, and copper from dental amalgam scrap. Laboratory research led to a process which was operated in 55 gallon drum sized reactors to treat 2000 Tr oz charges of scrap per day. This paper discusses the development work, presents a flowsheet and gives an indication of the equipment necessary to carry out the process on a commercial scale.

Jan 1, 1984

Alfred Stansfield, Montreal, Canada:—In Professor Howe&apos;s paper on the position of Ae3, he shows its industrial importance in determining the temperature to which steel should be heated for " grain refining." Several years ago I carried out a research on the " burning " of steel and found that while hypo-eutectoid steel should be heated to Ae3, hyper-eutectoid steel that has been very much overheated must be reheated to the curve Sa on the carbon-iron diagram, in order to redissolve the pro-eutectoid cementite and thus to obtain recrystallization and grain-refining. This treatment was necessarily only partly successful, and I should like to ask whether the conditions of heat treatment for refining overheated high-carbon steels have been ascertained. Speaking of the &&apos;Persistence of Solidificational Segregation " Professor Howe quotes an experiment made by Mr. Stead in which a bar of 1.2 per cent. carbon steel was immersed in a large mass of molten blast-furnace slag and allowed to cool with it. The steel was heated ; above the solidus (curve An on the carbon-iron diagram), but below the liquidus (curve AB). A drop of eutectic carbon-iron alloy, rich in carbon, had liquated out and hung below the bar. This agrees exactly with my own observations on the burning of steel, but my interpretation differs somewhat from that of Professor Howe. Professor Howe considers that the fusion of a part of the metal (rich in carbon) shows that the solidificational irregularities of composition had persisted through the rolling and heat treatment of the steel, as otherwise no part of the steel would have been sufficiently fusible to melt. It does not appear to me that such an explanation is necessary. A piece of steel represented in temperature and composition by any point within the area ABa will ultimately resolve itself into a solid phase and a liquid phase in equilibrium with each other. It may appear that if the steel were absolutely uniform no fusion could take place, but, the smallest nucleus of high-carbon, fusible alloy would ultimately bring about this separation into liquid and solid phases, by diffusion of the carbon from the solid to the liquid areas. A nucleus sufficient for the purpose might be provided by an area of pro-eutectoid cementite which had not become diffused during the

Jan 1, 1914

By Robert Goodrich

EXPERIMENTS ON A PORPHYRY COPPER ORE FROM BISBEE, ARIZ. THIS research was done partly in the non-ferrous laboratory of the Department of Metallurgy of Columbia University, under the direction of Dr. Edward F. Kern, and completed elsewhere. Acknowledgment is due to Prof. Arthur L. Walker, Dr. Edward F. Kern and Dr. William Campbell of the Department of Metallurgy, for their kind advice and for the inspiration derived from their instruction. This report is given under the following heads: Petrographic Description (Microscopic Study); Sampling and Preparing Ore for Treatment; Chemical Analysis; Treatment of Ore. PETROGRAPHIC DESCRIPTION Texture: Variable. Fine to medium mixed aggregate. Original structure: Obscure. Secondary structure: Fractured; healed.

Jan 8, 1915

By Earle Schumacher

COPPER-CALCIUM alloys are of interest as materials for use in deoxidized conductors of high conductivity. That calcium is effective in deoxidizing and degasifying copper is well known. Brandenberg and Wiens1 have described the use of calcium in the casting of sound copper and state that the deoxidation can be carried out without difficulty. The castings that they prepared were sound and sufficiently ductile to permit wire drawing. Pratt,2 in British Patent No. 1699 (1907), has claimed the use of calcium for the deoxidation and degasification of copper. Masing3

Jan 1, 1929

By M. G. Corson

INFORMATION regarding the use of manganese alloys has hitherto been incomplete and available only from widely scattered sources. This paper attempts a systematic description of properties .and uses of alloys other than manganese bronze, manganin and duralumin, which are probably the only non-ferrous alloys associated with manganese in the minds of most metallurgists.1 PROPERTIES OF MANGANESE Manganese can react either acid or basic; it is hard to obtain in the pure state; it has two different crystalline lattice structures, both of the cubic system, one stable above 850° C. and the other below 650° C., both coexisting in the intermediate range. Although the commercial product is hard and brittle, the pure metal seems to be ductile. In fact Zhemchuzhny, in Russia, was able to obtain ductile manganese and draw it to fine wires by the simple expedient of adding about 3 per cent. copper to the alumino-thermic product. Copper most probably brings the silicides, aluminides, nitrides and carbides present in the commercial product into a much less harmful form of distribution. One industrial use that can be foreseen for wrought manganese articles is as anodes for electrolytic processes in sulfate and nitrate solutions, particularly with high voltages. A practically insoluble skin of manganese peroxide is likely to form in such cases and an insoluble and strong anode material will be available.

Jan 1, 1927