Search Documents

By E. F. Koch, J. L. Walter

oriented crystals of iron and iron with 3, 5, and 6.25 pct Si were rolled to reductions of 10 and 70 to 97 pct at room temperature. Similarly oriented crystals were deformed in tension. Dislocation substructures of the deformed crystals were observed by transmission electron microscopy to determine the effect of silicon on the formation of substructures. Pole figures were obtained to relate orientation changes to substructure. When rolled 10 pct, the iron crystals and the 3 pct Si-Fe crystals formed cells, 1 and 0.2 u in diameter, respecliuely. Cells were absent in the higher-silicon crystals. Extended dislocations and possible stacking faults were observed in the 6.25 pct Si-Fe crystal rolled 10 pct and annealed at 650°C. The stacking-fault energy was estimated to be 20 ergs per sq cm. Rolling to 70 pct resulted in the formation of sub-bands (0.9 µ wide) ill the iron crystals and transition bands (containing 0.2-µ-wide subbands) in the 3 pct Si crystals. No subbands formed in the 5 pct Si-Fe crystal until it was ankzealed. SliP occurred on (112) planes ill tension. The slip traces on the 3 pct Si crystal were wary while those on the 5 pct Si crystal wvere straight. The strain-hardening coefficient for the 5 pct Si crystal was nearly zero. Cells did not form, at least at elongations up to 10 pet. The results suggest that cross slip of iron is restricted by additions of silicon beyond about 3 pct possibly by formation of immobile extended dislocations. IN a previous paper' the authors described the substructures developed in (100)[001]-oriented crystals of 3 pct Si-Fe which were rolled to reductions of 10 to 90 pct at room temperature. At low reductions (10 to 20 pct) cells, approximately 0.2 to 0.3 ja in diameter, were formed. The cell walls consisted mainly of edge dislocations. With increasing reduction (up to 50 pct) the cells were seen to elongate in the rolling direction. In certain regions of the crystal there were significant reorientations which were characterized as rotations about an axis normal to the (100) or rolling plane. These regions were called "transition bands". The regions in which there were no reorientations were called ('deformation bands". At reductions of 60 to 70 pct the elongated cells in the transition bands became sub-bands separated by low-angle tilt boundaries with angles of disorientation of about 2 deg. The elongated cell structure in the deformation band was replaced by a general distribution of dislocations. It was noted that the width of the subbands in the transition bands remained 0.2 to 0.3 µ; i .e., the width of the subbands was the same as the initial cell diameter for reductions up to at least 70 pct. From this, and from considerations of the mechanism of formation of the transition bands,' it was concluded that the subbands evolved directly from the initial cells. In order to check this conclusion, it was decided to examine the relationship between initial cell diameter and width of subbands produced by large rolling reductions. Cell size is known to be dependent upon the temperature of deformation.2,3 However, preliminary experiments with 3 pct Si-Fe crystals indicated that the change in cell size with increasing temperature of deform,ation was not sufficient for the present purpose. On the other hand, cell diameters generally reported for iron deformed at room temperature2'3 range from 1 to 2 p, a factor of 3 to 10 larger than the cells in 3 pct Si-Fe rolled to 10 pct reduction,' indicating the possibility of a marked dependence of substructure (at least in terms of cell size) on the amount of silicon in iron. Thus, the investigation was enlarged to include the study of the effects of varying silicon content on substructure in lightly rolled as well as in heavily rolled crystals of iron and iron with 3, 5, and 6.25 pct Si. The crystals used in this study all had the same orientation, (100)[001], with respect to rolling plane and rolling direction. These were rolled to reductions of from 10 to 97 pct and the substructures determined by electron transmission microscopy in both the rolled state and after annealing. In addition, stress-strain curves were obtained from (100)[001]-oriented crystals of iron and 3 and 5 pct Si-Fe to determine the effect of silicon on tensile properties. The dislocation substructure of the tensile specimens was also determined for Samples pulled to 2 and 10 pct elongation at room temperature for comparison with the substructures produced by rolling. 1) EXPERIMENTAL PROCEDURE Crystals with 3, 5, and 6.25 pct Si were prepared by annealing 0.012-in.-thick sheets of high-purity Si-Fe in purified argon at 1200°C to effect growth

Jan 1, 1965

By E. C. Houston

The phosphate ores mined in middle Tennessee typically consist of granular rock phosphate particles disseminated in a clayey matrix. In the TVA plant near Columbia, Tenn., the phosphate ore is mined, made into a slurry with the addition of a small amount of sodium hydroxide as dispersant, and treated in a hydroseparator to remove minus 10 micron material. The hydro-separator underflow, comprising a rough concentrate, is transported by pipeline to the plant; the hydro-separator overflow, comprising a tailing, is flocculated by addition of calcium sulphate and is discharged to settling ponds at a rate of about 1400 gpm. Sedimentation in the ponds produces a clarified effluent, which may be recycled for use as process water or discharged to surface drainage. This method of tailing treatment is not entirely satisfactory since poor sedimentation characteristics of the tailing result in poor ultimate utilization of pond storage volume.

Jan 1, 1949

"The reduction works of the Boston & Montana Reduction department, near the north end of this dam is one of the reduction plants belonging to the Anaconda Copper Mining Company, the other being at Anaconda. These works employ about 1,100 men and have a capacity of about 3,800 tons of crude ore per day. This plant is now being remodeled to embody results of experiments and investigations which have been made with a view to more economic.al treatment of ores. A brief description of the plant as it will be after the remodelling is as follows:Concentrator Department: Consists of six units or sections, each section treating from 550 to 600 tons of crude ore per day. This department is not being. remodelled at the present time. A concentrating process, however, has been developed and partially installed in the old mill, and an experimental section embodying this concentration process has also been installed at the concentrator at Anaconda."

Jan 1, 1913

By Arthur Knapp

The petroleum industry is confronted with the problem of conservalion. This is not a simple problem in view of a wide difference of opinion among authorities as to whether conservation is necessary and the specific direction that it should take. Many writers accuse the petroleum industry of wasting the natural resources of the country. Others link the consuming public with the industry in this waste. Let us define our terms; agree, if possible, on where and when waste occurs in connection with either the recovery or use of petroleum and select such plans for conservation as appear most practical. A plan for conserv3tion which appears to be logical today may not meet the problem tomorrow. The conservation of petroleum is closely linked with the advancement of marly arts and sciences and as these advance, the plan of conservation has to change. The need for conservation does not necessarily rest upon the elimination of waste. There is not necessarily a fixed connection between waste and conservation. Conservation may be necessary or desirable although there is no waste. Definitions Waste: Useless or unnecessary expenditure. Conservation: The preservation of the natural resources for economical use. Both definitions contain adjectives the interpretation of which is extremely difficult. It is the determination of what expenditures are "unnecessary" or what uses are "economical" that will require study and agreement. If one lets his automobile engine run in cold weather in order to keep it hot, it is difficult to measure that necessity. If an automobile is driven two blocks, when the driver is physically capable of walking, what is the measure of necessity. This question is in the realm of one of the oldest of sociological problems, "What is a luxury?"—a problem which has not been solved. The history of society indicates that the measure of a man's wealth has been the measure of necessity. What he can afford to buy without stinting himself in some other direction, is not a luxury to him and, if it fulfills his desires, may be considered his necessity.

Jan 1, 1927

By AIME AIME

IF the observation of our British friends is true that Americans put new records in bigness above everything else then the 150th meeting of the Institute was not the grand success it seemed to be. Just why the attendance slumped a little this year is anyone's guess, but the favourite explanation seemed to be that half the country is planning to come to the New York World's Fair this summer and that two trips from the hinterland to the me- tropolis, with another to San Francisco of course, can hardly be justified with the present condition of the stock market and the prices of the products of our mines. Certainly, some were pre- vented from coming too by the epidemic of respiratory afflictions that was rampant in February. Unfortunately. several succumbed after they had reached New York.

Jan 1, 1939

By F. A., King

THE problem of the proper size and capacity of the open-hearth furnace has been a predominant issue ever since its inception some sixty years ago. The original furnaces, built in 1868 at Landore, England, were only to 3 to 4 tons capacity, and from' this there has been a steadily increasing and almost uniform rate of expansion until furnaces producing 300 tons are in successful operation today. At the end of the first half of this 60-year period, or about the year 1900, 50-ton furnaces we're common. Up to this time the problems of expansion had been largely those relating to suficient capital and the engineering development of larger units. But as 75, 100-ton and larger furnaces were proposed apprehension grew and other questions assumed leading consideration.

Jan 1, 1928

By P. K. Koh, H. A. Lewis, H. F. Graff

New data on the distribution of silicon between slag and carbon-saturated iron at 1600Oand 1700OC are presented which, in combination with previously published data, permit the determination of silica activities over a broad range of compositions in the CaO-Al2O3-SiO2 system. The distribution of silicon between graphite-saturated Fe-Si-C alloys and blast furnace-type slags in equilibrium with CO has been described in previous publications.1"3 In this past work the silica-silicon relation was established at temperatures of 1425" to 1'700°C for slags containing up to 20 pct A12O3. This paper presents the results of additional studies at 1600" and 1700° C which extend the silicon distribution data at these temperatures for CaO-A12O3-SiO, slags over a range from zero pct Al2O3 to saturation with Al2O3, or CaO.2Al2O3. The upper limit of SiO2 is set by the occurrence of Sic as a stable phase when the metal contains 23.0 or 23.7 pct Si at 1600" or 1700°C, respectively. The activity of silica over the expanded range is determined directly from the distribution data.3 Recently4-7 other investigators have studied the activities of SiO, and CaO, principally in the binary system, using different methods and obtaining somewhat different results. EXPERIMENTAL STUDY The experimental apparatus and procedure have been fully described in previous publications.1, 3 Six new series of experimental heats have been made, four at 1600° and two at 1700°C. Master slags of several fixed CaO/Al203 ratios were pre-melted in graphite crucibles, and these were used with additions of silica to prepare the initial slag for each experiment. Slag and metal were stirred at 100 rpm and CO was passed through the furnace at 150 cc per min. The initial sample was taken 1 hr after addition of slag at 1600°C or 1/2 hr after addition at 1700°C. The run was normally continued for 8 hr at 1600°C or 7 hr at 1700°C, and the final sample was taken at the end of this period. Changes in Si and SiO2 content indicate the direction of approach to equilibrium, and in a series of runs where the approach is from both sides this permits approximate location of the equilibrium line. Fig. 1 shows the results of such a series of 15 runs at 1600°C for slags of CaO/Al,O3 = 1.50 by weight. Figs. 2 and 3 record other series at 1600°C and Fig. 5 a series at 1700°C with fixed CaO/Al0 ratios. The results of the experiments at 162003°C have been reported in part in a preliminary note.3 In the experiments recorded in Figs. 4 and 6, the slags were saturated with A12O3 (or with CaO.2A12O3 within its field of stability) by suspending a pure alumina tube in the melt during the course of the run. The final slag analyses were used to establish the liquidus boundaries8 in the stability fields of CaO.2Al2O3 and of Al20,. ACTIVITY OF SILICA The free-energy change in the reaction has been calculated by Fulton and chipman2 from recent and trustworthy data including heats of formation, entropies, and heat capacities. The more recent determination by Olette of the high-temperature enthalpy of liquid silicon is in satisfactory agreement with the values used and therefore requires no revision of the result which is expressed in the equation: SiO2 (crist) + 2C (graph) = Si + 2CO(g.) [1] &F° = + 161,500 - 87.4T The standard state for silica is taken as pure cristobalite and that of Si as the pure liquid metal. Since the melts were made under 1 atm of CO and were graphite-saturated, the equilibrium constant for Eq. [I] reduces to K1 = asi /asio2. The value of this constant is 1.77 at 1600°C and 16.2 at 1700°C. Through K1, the activity of silica in the slag is directly related to the activity of silicon in the equilibrium metal.

Jan 1, 1960

By P. E. Rider, K. A. Gschneidner, O. D. McMasters

The solid solubilities for thirteen rare-earth metals in gold were determined by using the X-ray parametric method. Solubilities ranged from 0.1 at. pct for lanthanum in gold up to 8.8 at. pct for scandium in gold. The solubilities from lanthanum to gadolinium were very small and essentially constant, but a sharp increase occurred from gadolinium to scandium. The large solubilities for the heavy rare-earth metals were not expected because of the large size and electrochemical differences between rare-earth atoms and the gold atom. Contributions from first- and second-order elasticity theory plus an electronic contribution were found to reasonably account for a more favorable size factor. Electron transfer from the rare-earth metal to the gold Is thought to occur such that the resultant rare-earth and gold electronegativities are favorable for solid-solution formation. It was also found that this mutual adjustment of size and electronegutivity does not occur if the pure-metal size factors are greater than a critical value of 25 pet. The eutectic temperatures for ten systems were determined and these remained fairly constant at approximately 809 "C for the lighter lanthanide metal-gold systems until the Er-Au system was reached, at which Point the eutectic temperature successively increased reaching a maximum of 1040°C in the Sc-Au system. This rise was correlated to the size factor becoming more favorable for solid-solution formation at erbium. The valence state of ytterbium was found to change from two in the pure metal to three when ytterbium is dissolved in the gold matrix. RECENT results1 reported concerning the solubility of holmium in copper, silver, and gold, showed that the solubility of holmium in gold was quite large, 4.0 at. pct, compared with 1.6 in silver and 0.02 in copper. The small solubilities of holmium in silver and copper are quite reasonable in view of the large size difference (22.2 and 38.2 pct, respectively), large electronegativity difference (0.59 for both systems), and possible unfavorable valency factor (assuming one for silver and copper and three for holmium). The large solubility in gold, however, is unexpected because these same factors are also unfavorable for holmium and gold (22.5 pct size difference and 0.69 electronegativity difference), and because the light rare-earth metals, lanthanum, cerium, and praseodymium, have negligible solid solubilities in gold.2 In view of this unexpected behavior, it was felt that a study of the solid solubilities of most of the rare-earth metals in gold would be desirable to better understand the factors involved in the formation of solid solutions. Of the rare-earth metals added to gold in this study, only ytterbium is divalent in the pure metallic state (the other rare-earth metals are all trivalent) and many of its physical properties (such as the metallic radius, electronegativity, and so forth) are much different from those of the normal trivalent rare-earth metals.' The properties of ytterbium are such that one would expect solid-solution formation to be less favorable for ytterbium in gold than for any of the normal trivalent rare-earth metals. But chemically ytterbium is known to possess a stable trivalent state, and it is quite possible that ytterbium may alloy as a trivalent metal under certain conditions rather than as a divalent metal. Because of the dual valency nature and because so little is known about the alloying behavior of ytterbium, the gold-rich ytterbium-gold alloys are of special interest. EXPERIMENTAL PROCEDURE Materials. The gold used in this investigation had a purity of 99.99 pct with respect to nongaseous impurities. In general the rare-earth metals were prepared by reduction of the corresponding fluoride by calcium metal.3 The impurity contents of the metals used in this study are given in Table I. Preparation of Alloys. Two- or 3-g alloy samples were prepared by arc melting. The samples, with the exception of some of the Er-Au alloys, had weight losses of 0.5 pct or less. All alloy concentrations noted in this paper are nominal compositions. After arc melting, the alloys were wrapped in tantalum foil, sealed off in quartz tubing under a partial atmosphere of argon, homogenized for approximately 200 hr at 780°C, and then quenched in cold water. X-Ray Methods. The X-ray parametric method was used in determining the solubility of the rare-earth metals in gold. filings were sealed in small tantalum tubes by welding under a helium atmosphere. The tantalum tubes were then sealed in quartz tubing under a partial argon atmosphere, and annealed for times ranging from 1/2 to 3 hr (the length of time was inversely proportional to the an-

Jan 1, 1965

By J. Philibert, A. G. Guy

Diffusion in the presence of deformation was studied by the method of vacuum dezincification of copper-rich and silver-rich solid solutions containing 7 to 30 pct Zn. The specimens were designed to permit the study of diffusion in separate portions of a given specimen characterized by strain rates ranging from essentially zero to approximately 10 sec-. No effect of deformation on diffusion was observed. BEGINNING with the work of Buffington and Cohen: interest in the question of the effect of stress or strain on diffusion has largely been concentrated on the enhancement of diffusion in specimens subjected to Continuous plastic deformation. The present research is a contribution to this limited area. However, as a preliminary to focusing attention on this special topic, it will be desirable to make a broad survey of the larger question, especially since there has been considerable foreign work in areas outside those of current interest in the United States. Since most of the topics referred to in the following section are both complex and imperfectly understood at present, it has been expedient in most instances to offer only a guide to the general nature of the work rather than a critical evaluation. PREVIOUS WORK The effect of elastic stress on diffusion has received considerable attention, especially with regard to the thermodynamic driving force for diffusion. The thermodynamic treatments have been based on the work of Gibb, Voigt, Planck, and Leontovich.' Konobeevskii and Selisski6 made a first attempt at treating the problem in 1933, and Gorskii7 a few years later gave a solution applicable to single crystals as well as to polycrystalline specimens. In 1943 Konobeevski8 published treatments that have been the basis of much Russian work up to the present. For example, Aleksandrov and Lyubov used his work in explaining the velocity of lateral growth of pearlite. Early work in the United States was that of Mooradian and Norton, which showed that lattice distortion tends to be relieved before it can significantly affect the diffusion process. Druyvesteyn and Berghoutl1 observed a slight effect of elastic strain on self-diffusion in copper, while de Kazinczy12 found that both elastic and plastic deformation increased the rate of diffusion of hydrogen in steel. On the other hand, Grimes58 observed no effect of either elastic or plastic straining on the diffusion of hydrogen in nickel. High-frequency alternating stresses have been reported by various investigator s13-l5 to increase the rate of diffusion. A special form of elastic stressing is the imposition of hydrostatic pressure, a condition that is amenable to Conventional thermodvnamic analysis. Most of the experimental results in this area are consistent in showing a slight decrease in diffusion rates at high pressures.16-l8 Although Geguzinl reported a pronounced effect of relatively small pressures, Barnes and Mazey20 failed to Corroborate this finding, while Guy and Spinelli21 advanced an explanation of the phenomenon observed by Geguzin. It has been recognized that the thermodynamic treatment of diffusion phenomena in an arbitrarily stressed body is complicated by the fact that the desired state of quasi-equilibrium of the shear stresses cannot be maintained during a general diffusion process. However, attempts have been made by Meix-ner22-24 and Fasto to treat certain restricted cases, such as relaxation. FastovZ7 has also incorporated the general stress tensor into the thermodynamics of irreversible processes. The lattice strain that accompanies the formation of a solid solution has been the subject of much study,28-s0 and indirectly it has entered into many recent theories of diffusion. However, some Russian investigators31'32 have taken other views of this matter and have predicted large effects on diffusion rates because of concentration stresses.o In completing this brief resume of previous work involving elastic strains and before proceeding to a consideration of the effect of continuous plastic deformation, it should be pointed out that deformation of various additional types may also influence diffusion. The effect of cold-working on subsequent diffusion has been studied directly by AndreevaS and by Schumann and Erdmann-Jesnitzer, while indirect evidence has been obtained by Miller and Guarnieri and by Vitman.38 Thermal stresses may also influence diffusion, contributions to this subject having been made by Fastovs7 and by Aleksandrov and Lyubv. The work of Johnson and Martin,o Dienes and Damask,3Band DamaskS considered the question of radiation-enhanced diffusion. In considering previous work on the subject of plastic deformation and diffusion, attention will be directed to those studies concerned primarily with diffusion rather than with its relation to Creep, e.g., the work of Dorn, or to the acceleration of diffusion -controlled reactions. Observations of the effect of

Jan 1, 1962

By Willard C. Lacy

Rather than attempting to present a summary of the many and highly varied papers that have been presented at this symposium on sampling and grade control, I will attempt to extract the general philosophy of analysis and approach, and attempt to identify the trend of future developments. First, the term "sampling" is used with its broadest connotations. A sample consists of a representative portion of a larger mass, and must represent the mass not only in the grade of contained metals or minerals, but also in all other respects in terms of mineralogy and mineral quality (1, 5), deleterious materials, recoverability of economic components, physical behavior, geophysical response (I), and even archaeological and environmental aspects (7, 11). The sample must be taken from a locality and in such a manner and quantity that it is representative of the larger rock mass. This calls for complete and accurate geological control and an understanding of the nature and distribution of the contained chemical and physical elements and a record of the effectiveness of the different sampling methods. Second, value of a given mass of ore material is based upon its profitability - the difference between recoverable value and costs to achieve recovery, beneficiation and sale. There is a strong movement in mining geology control toward more complete analysis in determining cutoff grades and in grade control, as illustrated by the kriging of metallurgical recovery factors as well as grade at the Mercur Mine (8). To achieve a "profit- ability factor" as a guide for economic mining practice requires further integration of: 1) the value of contained metal or mineral, 2) percentage recovery of values, 3) dilution of ore with waste rock, 4) addition to, or loss of value as a consequence of by-product materials or deleterious components, 5) cost of producing a saleable product plus mini- mum profit to justify the effort (cutoff), and 6) cost of land restoration (7, 11). All these parameters vary with the rock type, rock structure, mineralogy, depth, geometry, mining and metallurgical methods, but they must be sampled and analyzed if sampling and grade control are to reflect profitability. A wide variety of deposits has been presented at this symposium; each deposit with its own problems and special solutions. Deposits containing high unit-value components, e.g. precious metals and diamonds, present special problems in the obtaining of accurate samples and generally require statistical analysis control methods or may disregard or modify occasional high or occasional low values, based upon experience (12 ) Grade control may be accurate for the long term but may vary for the short term. Bulk sampling is always essential. Deposits containing metals or minerals with low unit value are very sensitive to transport costs, and they are often very sensitive to small amounts of deleterious components or differences in physical or chemical behavior. Problems of sampling and grade control change with the genetic type of deposit, with the stage of deposit development and with the size of the information base. Precious metal epithermal deposits (2, 6, 8), because of rapid vertical zonation and erratic lateral distribution of values, have always been difficult to evaluate and maintain grade control and ore reserves. On the other hand, evaluation and grade control are relatively easy in bulk-low- grade deposits (4, 13). However, these deposits generally have a low margin of profit and are sensitive to mining and beneficiaton costs, price fluctuations and political costs. Industrial mineral deposits (5) often must be evaluated on the basis of their behavior, rather than by chemical analysis. Environmental impact generally increases with the scale of the operation, but certain elements or minerals have especially high impact effects (7, 11). In the exploration phase there is no production control of sampling procedures and careful geological observations are particularly essential. The greatest number of problems is related to the oxidized outcrop where the chemical environment of the ore body has changed and the contained values may have been enriched, depleted or values left unchanged (2, 6). Present evidence suggests that gold values may be very mobile under certain conditions (2, 6) and stable under others. Everything must be sampled in detail. Principal values and by-product or deleterious elements may vary dependent upon their position within the soil profile. Such factors as geomorphic position, erosion rate, vegetation, climate, etc., may affect the interpretation (1, 3). During the development phase it is equally easy to overtest, to have "paralysis by analysis," as to undertest (3, 6). Bulk samplng and testing are

Jan 1, 1985

By R. A. Wood, R. I. Jaffee, H. R. Ogden, D. N. Williams

The tensile properties, creep resistance. and thermal stability of highly alloyed Ti-Al-Zr alloys were examined. On the basis of these studies, the Ti-7Al-1ZZr composition was selected for more complete evaluation. The alloy was found to be weldable and free from excessive directionality. In addition, it developed maximum properties without requiring heat treatment other than an annealing operation in the alpha field. The alloy was recommended for scale up and is presently being investigated on a production-level basis. One of the more attractive properties of titanium alloys is their ability to withstand stress at moderately high temperatures, and a considerable amount of effort has been devoted to increasing the maximum service temperature of titanium alloys. This work has suggested that the optimum alloys for high-temperature service will be single-phase a (close-packed hexagonal) alloys containing significant amounts of aluminum. However, the maximum amount of aluminum which can be alloyed with titanium is between 6 and 8 pct,l since at high-aluminum contents an embrittlement reaction occurs in the anticipated service temperature range, 800" to 1100°F. It has been shown that the embrittlement reaction involves decomposition of the high-aluminum a phase to one or more new phases.' Since this reaction does not occur at intermediate or low-aluminum contents, it was felt that intermediate Ti-A1 alloys might be strengthened by a-soluble ternary additions without inducing the embrittlement reaction. The first alloying addition considered was tin, which shows extensive solubility in a titanium and has moderate strengthening tendencies. Unfortunately, it was soon apparent that tin also promoted the embrittlement reaction, and that to obtain a stable alloy, the aluminum content had to be reduced as the tin content was increased. The second alloying addition considered was zirconium, which is similar to tin in its effects on titanium. This element did not contribute to the embrittlement reaction and, in fact, appeared to increase the maximum amount of aluminum which could be alloyed with titanium without inducing instability. This paper describes an investigation of the Ti-A1-Zr a alloy region. Alloys containing from 4 to 12 pct A1 and from 6 to 15 pct Zr were examined. The properties of these alloys are described and the bases for selecting an optimum composition is outlined. This composition, Ti-7A1-12Zr, is presently being scaled up in tonnage quantities, and is being evaluated extensively throughout the industry. In addition to presenting the basis for its selection, this paper presents a description of the properties developed in laboratory material as determined during the alloy investigation. These properties suggest that this alloy can fill an important position in applications requiring light weight, fabrica-bility, weldability, and strength to 1000oF or higher. EXPERIMENTAL PROCEDURES Titanium alloy ingots were prepared by inert electrode arc melting under an argon atmosphere. Alloying elements used were 110 Bhn titanium sponge, high-purity aluminum, and reactor-grade zirconium. Pancake-shaped ingots were prepared weighing approximately 300 g. The composition of the ingots was checked by weight measurements before and after melting. The pancake ingots were forged at 2000°F to approximately half their original thickness to give a flat plate roughly 1/2 in. thick. This plate was then rolled at 1800' to 1600°F to 0.250 in. thick. All of the alloys examined fabricated well. However, alloys containing 15 pct Zr tended to overheat due to exothermic oxidation, and scaling was excessive. As might be anticipated from its effect in decreasing the ß transus, increased zirconium appeared to improve fabricability somewhat, especially during rolling at lower temperatures. Except for a limited study of heat-treatment response, all alloys were examined in the a-annealed condition. Prior to heat treatment the a and ß tran-sus temperatures were determined by metallo-graphic examination of samples quenched after annealing at 50-deg intervals in the transformation region. These data are shown in Fig. 1. Recrystal-lization appeared to occur in about 1 hr in the range 1300º to 1500ºF. Therefore, alloys were annealed for 1 hr at 1550ºF (4 and 5 pct Al), 1600ºF (6 through 7-1/2 pct Al), or 1650°F (8 or more pct Al). This produced an equiaxed a grain structure. In most alloys, a "ghost" structure was visible after the a-annealing treatment, as shown in Fig. 2. This structure apparently resulted from the acicular

Jan 1, 1963

By AIME AIME

THE official opening at the 134th general meeting of the Institute was held on Oct. 6, but it was prefaced by two round table conferences on Oct. 5. The open-hearth group held the fourth of their semi-annual conferences at the William Penn Hotel, devoting the morning session to discussing a paper by R. L. Cain on the "Manufacture of Forging Steel by the Open-hearth Process," and the afternoon to discussing P. H. Shaeffer's paper on the open-hearth charge. At the Bureau of Mines, a round table conference on the combustibility of coke was held on Tuesday morning, and the afternoon was devoted to a similar conference on the testing of coke. The formal opening session of the meeting assembled in the Music Hall of Carnegie Institute at 10.30 a. m. Graham Bright, chairman of the Pittsburgh Section; called the meeting to order and presided. President Taylor welcomed the visiting members and guests to his home city and reviewed briefly the advancement of mining in the past half century during which, for ex- ample, the coal output had increased from 53,280,000 tons to 523,357,000 tons per year. He emphasized the important part Pennsylvania played in mining and brought out the principal changes that had taken place in methods. In part, his remarks were as follows: The centennial year, 1876, found the coal business of. this country, as a whole, producing 53,280,000 tons, of which amount the bituminous mines of this State yielded 24 per cent. In 1925, this country produced 523,357,000 tons of coal, of which Pennsylvania produced 24 per cent.

Jan 1, 1926

By F. C. Langenberg, J. Chipman

New data on the distribution of silicon between slag and carbon-saturated iron at 1600oand 1700oC are presented which, in combination with previously published data, permit the determination of silica activities over a broad range of compositions in the CaO-Al2O3-SiO2 system. The distribution of silicon between graphite-saturated Fe-Si-C alloys and blast furnace-type slags in equilibrium with CO has been described in previous publications.1"3 In this past work the silica-silicon relation was established at temperatures of 1425" to 1700°C for slags containing up to 20 pct Al2O3. This paper presents the results of additional studies at 1600" and 1700° C which extend the silicon distribution data at these temperatures for CaO-A1203-SiO2 slags over a range from zero pct A12O3 to saturation with A12O3, or CaO.2A12O3. The upper limit of SiO, is set by the occurrence of Sic as a stable phase when the metal contains 23.0 or 23.7 pct Si at 1600" or 1700°C, respectively. The activity of silica over the expanded range is determined directly from the distribution data.3 Recently, 4-7 other investigators have studied the activities of SiO, and CaO, principally in the binary system, using different methods and obtaining somewhat different results. EXPERIMENTAL STUDY The experimental apparatus and procedure have been fully described in previous publications.1, 3 Six new series of experimental heats have been made, four at 1600° and two at 1700°C. Master slags of several fixed CaO/A12O3 ratios were pre-melted in graphite crucibles, and these were used with additions of silica to prepare the initial slag for each experiment. Slag and metal were stirred at 100 rpm and CO was passed through the furnace at 150 cc per min. The initial sample was taken 1 hr after addition of slag at 1600°C or 1/2 hr after addition at 1700°C. The run was normally continued for 8 hr at 1600°C or 7 hr at 1700°C, and the final sample was taken at the end of this period. Changes in Si and SiO2 content indicate the direction of approach to equilibrium, and in a series of runs where the approach is from both sides this permits approximate location of the equilibrium line. Fig. 1 shows the results of such a series of 15 runs at 1600°C for slags of CaO/Al2O3 = 1.50 by weight. Figs. 2 and 3 record other series at 1600°C and Fig. 5 a series at 1700°C with fixed CaO/Al2O3 ratios. The results of the experiments at 162003°C have been reported in part in a preliminary note.3 In the experiments recorded in Figs. 4 and 6, the slags were saturated with A12O3 (or with CaO.2A12O3 within its field of stability) by suspending a pure alumina tube in the melt during the course of the run. The final slag analyses were used to establish the liquidus boundaries8 in the stability fields of CaO.2Al,O3 and of A120,. ACTIVITY OF SILICA The free-energy change in the reaction has been calculated by Fulton and chipman2 from recent and trustworthy data including heats of formation, entropies, and heat capacities. The more recent determination by Olette of the high-temperature enthalpy of liquid silicon is in satisfactory agreement with the values used and therefore requires no revision of the result which is expressed in the equation: SiO, (crist) + 2C (graph) = Si + 2CO(g.) [1] &F° = + 161,500 - 87.4T The standard state for silica is taken as pure cristobalite and that of Si as the pure liquid metal. Since the melts were made under 1 atm of CO and were graphite-saturated, the equilibrium constant for Eq. [I] reduces to K1 = asi /asio2 The value of this constant is 1.77 at 1600°C and 16.2 at 1700°C. Through K1, the activity of silica in the slag is directly related to the activity of silicon in the equilibrium metal.

Jan 1, 1960

By Ralph H. Sweetser

BENEFICIATION of iron ores from the blast-furnace point of view means more than the usual enrichment of the iron contents by the removal of a large part of the clay, carbonic acid gas, silica, or moisture of the natural ore; it includes all these, but it also embraces several other mechanical .processes made , necessary by the exacting requirements of present-day blast-furnace practice. The increasing use of iron- bearing by-products, to as much as a third or more of the total ore burden, has introduced still another series of processes for improving the blast-furnace ore burden. As we look back over the past three decades of blast- furnace practice 'in. this country, we see that many of the blast-furnace troubles were directly due to lack of proper preparation of the iron ore burden,, and we realize that beneficiation in one form or another would have remedied the trouble. This was particularly true in the smelting of magnetic iron ores, where run-of- mine ore included such big lumps of 'magnetite along with rich fines that the furnace operations were greatly retarded and control of the furnace such as is usual today, was completely unknown.

Jan 1, 1930

By W. L. Zeigler

DURING the middle 1880s, shortly after the discovery of silver-lead ores in the Coeur d'Alene district of northern Idaho, it became apparent that concentration of the ores would be necessary to obtain a profitable product. Too much siliceous material was present for direct smelting, and the majority of the ores found at depth were too low in metallic content for economic smelting processes at the time. As the ores occurred in quartzite shear zones with siderite and quartz gangue, a large quantity of waste material was present in all the mines. As the galena was not finely disseminated, this made possible relatively good extraction of the argentiferous galena by coarse concentration. The first concentrators consisted mainly of coarse crushing, screening and jigging, principally by Harz jigs, the slimes being treated on buddies. Later Wilfley tables took the place of sand jigs and vanners superseded the buddies. Because of the marketing conditions, no attempt was made until 1900 to effect a recovery on the zinc minerals present, which were found associated in varying amounts with the galena. All through this period, the greater part of the production was obtained from mines containing ore assaying high in lead and low in zinc. Parts of some ore bodies would be reversed in this respect, so that ores high in zinc were left intact. During the decade after 1910, several important mines, The Success and The Interstate Callahan, containing ores high in zinc, were put into operation and were a material aid in the needed zinc production during World War I. Gravity concentration by jigs and tables was used during this period, with bulk flotation increasing in popularity for the treatment of the fine material that had already been treated by ordinary slime concentrating machinery. No extra fine grinding for flotation concentration was thought profitable at the time. TAILINGS DISCHARGED INTO STREAMS From the start of mining and milling operations in this district until 1904, no attempt was made by the various mills in the upper district to impound or stack their tailings. They discharged them directly into the adjacent creeks or streams, to be carried away by high water. The Bunker Hill and Sullivan and the Last Chance mines, both in the relatively flat valley of the district, stacked huge piles of the coarse jig tailings on the near-by river bottom. Rain and snowfall are heavy in the Coeur d'Alene district, as it is on the heavily timbered Pacific slope of the Bitter Root Mountains. A heavy runoff occurs every spring and there is an occasional flood of disastrous proportions when warm "Chinook" winds accompanied by rain

Jan 1, 1947

By AIME AIME

FEW men are better known in fuel engineering circles in the Middle West than the present Chairman of the Coal Division of the A.I.M.E. - Julian Elnathan Tobey. Now vice-president in charge of engineering of Appalachian Coals Inc., of Cincinnati, he has served that pioneer regional marketing agency since Aug. 1, 1934, when he became manager of its engineering department. His duties have included field promotion work in the interest of use of the agency's coals from eastern Kentucky and Tennessee, south western Virginia, and southern West Virginia in new plants of all types. He has been especially interested in certain industries which have shown an alarming tendency to change to natural gas or hydroelectric power; also in the development and practical application of small stokers and other mechanical equipment.

Jan 1, 1941

By John H. Bassarear, Harold W. Sorstokke

The fourth expansion within 10 years was completed at Pima Mining Co. during late 1971. The first three expansions increased capacity from 3000 to over 40,000 tpd. Conventional crushing and grinding practices were used in the original 10-section mill. Total capacity is now approximately 54,000 tpd. Expansion IV includes a new primary crusher and a radial stacker conveyor that feeds stockpiles for both concentrators. The -8-in. primary product is fed from the reclaim stockpile to the new mill by two pairs of pan feeders, each pair feeding a separate conveyor. The reclaim conveyors each feed 28 X 12-ft semiautogenous mills operating with an 8% charge of 4-in. balls. Autogenous discharge is screened, oversize recycling by conveyors, with -%-in. undersize feeding two conventional 161/2 X 19-ft ball mills in closed circuit with cyclones. Cyclone overflow is pumped to three parallel rows of 300-400 cu ft flotation cells. Rougher and scavenger concentrates produced are sent to the original mill for regrind, cleaning, and filtering.

Jan 1, 1974

By Philip E. LaMoreaux

Fluoride, generally less than 0.5 ppm, is present in ground water from rocks of Paleozoic age and older, in northern and eastern Alabama. Some of the water-bearing formations in the Coastal Plain area of the State yield water with as much as 6.8 ppm fluoride.

Jan 8, 1950

APPLICATIONS for loan contracts for the exploration, development and mining of strategic and critical metals and minerals are now being accepted by the Department of the Interior. The RFC is authorized and directed by Executive Order 10161 to make such loans but the Secretary of the Interior must pass on the necessity for the loan. Applications should be addressed to James Boyd, acting deputy administrator, Defense Minerals Administration, Department of the Interior, Washington, D.C. rather than to the Field Offices of the Bureau of Mines as was first planned. Application forms are not yet available but it has been learned that data accompanying the application should include the known quantity and grade of reserves, the anticipated rate of production, the equipment, supplies, and man power required for the additional production, etc.

Jan 12, 1950

By M. Gell, G. R. Leveran

The high- and low-cycle fatigue properties of the nickel-base superalloy, Mar-MBOO, in columnar-grained and single-crystal forms were determined at room temperature. It was found that the fatigue lives of these materials were greatly affected by the size of preexisting cracks in MC-type carbides contained in the micro structure. Most of the data falls on two curves given by: (zN)'/A€= K, where Nf is the number of cycles to failure, Af is the total strain range, and K is a function of carbide size. No difference was observed in the fatigue behavior of the columnar-grained and single-crystal materials for the same MC carbide size. Matrix slip and crack initiation occurred at precracked MC carbides and, to a lesser extent, at micropores. Fatigue crack propagation was mainly in the Stage I mode, i.e., on cry stallo graPhic slip planes. The Stage I fracture in these materials was unusual in that distinct features were observed on the fracture surfaces. In high-cycle fatigue, these features resembled those commonly observed on the cleavage fracture surfaces of bcc and hcp materials. Yet, in this study, the cracks propagated slowly in a cyclic manner. In low-cycle fatigue, the Stage I facets contained equiaxed dimples, similar to those observed on the tensile fracture surfaces of ductile materials. These observations indicate that both local normal and shear stresses are involved in these Stage I fractures. A model is proposed to explain these results based on the weakening of the cohesive energy of the active slip planes by reversed shear deformation and the fracture of the bonds across the weakened planes by the local normal stress. RECENT developments in casting technology have produced cast nickel-base superalloys in columnar -grained and single-crystal forms.1'2 The tensile and creep properties of the nickel-base superalloy, Mar-M200, cast in these forms have been shown to be superior to the corresponding properties of the conventionally cast polycrystalline material.lp2 This improvement in properties results, in part, from the elimination of grain boundaries in the single crystals and the alignment of the grain boundaries parallel to the stress axis in the columnar-grained castings. As part of a program to evaluate the fatigue properties of nickel-base superalloys cast in single-crystal and columnar-grained forms, a study has been made of the cyclic deformation and fracture of Mar-M2OO at room temperature. M. fiFl I .hininr Mpmher AIMF ic ^pninr Rocoarrh Accn^iata anH I) EXPERIMENTAL PROCEDURE The composition range of Mar-Ma00 in weight percent is: 8 to 10 Cr, 9 to 11 Co, 11.5 to 13.5 W, 0.75 to 1.25 Cb, 1.75 to 2.25 Ti, 4.75 to 5.25 Al, 0.01 to 0.02 B, 0.03 to 0.08 Zr, 0.07 to 0.12 C, bal. Ni. All of the castings met the above specifications. The castings were solutionized for 1 to 4 hr at 2250°F followed by aging at 1600°F for 32 hr which resulted in a 0.2 pct offset yield stress of 150,000 psi at room temperature. The microstructure of the material consisted of cuboidal, coherent particles of ordered, fcc Ni3(A1,Ti) (commonly designated y'), approximately 0.3 p on edge, distributed in an fcc y solid-solution matrix. MC carbides together with shrinkage and gas micropores were also distributed throughout the materials. The MC carbides and micropores were located preferentially in the interdendritic interstices, as well as in the grain boundaries in the columnar-grained castings. The (100) direction of all the single crystals and the common (100) axis of the grains in the columnar materials were aligned within about 5 deg of the specimen axis. Fatigue testing was carried out in the high-cycle (HCF) and low-cycle (LCF) fatigue regions, with the major difference being gross yielding of the specimen occurred during the first cycle in the LCF region. This division also corresponded with the more usual one in which the life of a specimen in LCF is less than lo4 cycles and that in HCF is greater than lo4 cycles. The designs of the high-cycle fatigue and low-cycle fatigue specimens are shown in Figs. l(a) and (c), respectively. The gage sections of both HCF and LCF specimens were electropolished prior to testing. The HCF specimens were tested in an MTS, closed-loop, hydraulic fatigue machine at 10 cps in air. The specimens were cycled between a tensile stress of 5000 psi and a maximum tensile stress which ranged from 35,000 to 125,000 psi, Fig. l(b). The LCF specimens were cycled under strain control from zero to a maximum tensile strain, Fig. l(d), in a Wiedemann-Baldwin testing machine. The experimental procedure has been described elsewhere.3'4 Both HCF and LCF tests were interrupted periodically in order to replicate the development of slip and cracking at the specimen surface. This was accomplished by placing plastic replicating tape around the gage section of the specimen while the specimen was in the mahine. The size of the MC carbides for all specimens was measured on a polished longitudinal section through the gage section after fatigue testing. The method of measurement consisted of carefully scanning the entire polished section in order to locate the largest MC carbides. Photographs were then taken of the six longest carbides oriented approximately normal to the

Jan 1, 1969