By Hongli Wen, Guangkun Shen, Qiong Deng, Shoujian Huang, Min Gan, Xiaohui Fan

"Due to the low iron grade and high sulfur content, pyrite cinder is difficult to be directly used for iron-making. In this paper, technology of magnetic roasting -grinding and magnetic separation -acid leaching was put forward for reclamation of pyrite cinder. For pyrite cinder of TFe53.51%, S2.20 %, studies showed that good magnetic effect can be achieved at roasting temperature 650~7000, reducing atmosphere CO/(CO + C02) 10~20% and roasting time 10~30 minutes. In separation conditions of grinding size -0.045mm accounting for 96.09% and magnetic field intensity of 1240 GS, iron concentrate of TFe64.81 %, S0.18% and iron recovery rate 91.44% was achieved. Acid leaching was studied to strengthen desulfurization. Results showed that high-quality iron ore concentrate of TFe66.3 l %, S0.10% was obtained under the conditions of hydrochloric acid mass fraction of 5%, pulp density of30%, leaching temperature of70? and leaching time of2 hours.IntroductionPyrite cinder is produced as a by-product of sulfuric acid industry [1] Domestic production is more than 12 million tons every year and occupied area is over 10 million square meters [2,3]. The pyrite cinder outdoor not only pollutes air but also damages surrounding surface [4] It after treatment used for iron-making is an ideal reclamation approach for its rich iron which is commonly 40-60% [5]. But pyrite cinder gets low utilization for its low iron grade and high sulfur content in China [6]. Therefore, comprehensive utilization of pyrite cinder has profound significance to environmental protection and the development of domestic iron and steel industry."

Jan 1, 2013

By Zhihe Dou, Yu Fang, Zimu Zhang, Yan Liu, Xiaoli Jiang Dianhua Zhang, Guanting Liu

"With the idea of “waste control by waste itself”, we come up with the crafts of using waste calcium carbide to mineralize CO2 in electrolytic aluminum waste gas, design and make out “Venturi gas-liquid-solid three stage reactor”, do experiments under the system of CO2-Ca(OH)2, investigate the influence on gas absorption by pH meter; investigate the influence on diameter distribution , rise velocity of bubble and local gas hold-up by dual conductivity probes; investigated the absorption of CO2 in every stage reactor under different initial proportion of CO2 by intelligent gas measurement system. The results showed that the reactor can fully absorb the CO2 in waste gas, and it has largely shorten the time of absorption and improve the CO2 utilization compared with the single stage reactor.The residual proportion of CO2 in the gas is below 0.08% through the absorption of three stage reactor,which show that absorption is extremely improved.IntroductionCarbide slag is a kind of polluting hydrolysis reaction byproducts in producing carbide in wet reactor, and it is mainly comprised by Ca(OH)2, It's estimated that there are about million tons carbide slag are piled up per year. Carbide slag is a kind of industrial wastes that hard to deal with ,which are treated by land filled in the past. It would not only occupy a lot of land, but also lead to secondary pollution [1].CO2 is the main greenhouse gas by now. In 2010, global CO2 emission has reached 33.5 billion tons, while China has now become the world's second largest emitter of CO2, emissions accounting for about one-seventh of the world [2].As the experts estimates, the greenhouse gas emission of whole nonferrous metal industry may over 0.6 billion tons per year, while CO2 emission of electrolytic aluminum is 0.334 billion tons per year [3]. So it is necessary and pressing to discover the reusing CO2 of electrolytic aluminum. With the idea of “waste control by waste itself”, we came up with the crafts of using carbide slag to mineralize the CO2 in electrolytic aluminum waste gas, which was experimented on the counterflow-three stage-venturi reactor,and studied the local gas holdup, residual concentration of CO2 and the volumetric transfer coefficient in the reactor."

Jan 1, 2014

By Vinicius Alves Gomes, Jean Igor Margem, Frederico Muylaert Margem, Sergio Neves Monteiro, Marina Rangel Margem

The interface between the matrix and the reinforcing fiber plays an important role in the efficiency by which an applied load is transmitted through the composite structure. The shear stress at the fiber/matrix interface can be associated with this load transference and, consequently, affects the composite strength. In the present work, pullout tests were used to evaluate the interfacial shear stress of malva fiber in epoxy matrix composites. A small critical length was found for the malva fiber embedded in epoxy, which corresponds to a relatively weak fiber/matrix bond and lower interfacial strength.

Jan 1, 2015

By E. A. Werner, A. Pichler, A. Spalek, G. Reisner, P. Stiaszny

"Interstitial free (IF) sheet steels are used for complex shaped parts because of their excellent formability. If a deep drawn part is subjected· to a impact deformation at low temperature brittle fracture of the part may occur. This phenomenon\ is called secondary work embrittlement (SWE). One possibility to characterize this material/structural behavior is the drop-weight test. The result of .this .test is a temperature at and below which a crack can initiated in a deep drawn part under the investigated set of parameters. This paper addresses the influence of the preforming process on the sus- . . ceptibili.ty of IF steels to SWE.IntroductionInterstiiial:free (IF-) steels are frequently used in the automotive industry for complex· shaped p·arts because of their excellent deep drawability. The microstructure of the steel consists of a highly ductile ferritic matrix with embedded precipitates of nitrides and/or carbides. Brittle fracture can occur in deep drawn parts, if they are subjected to a high speed deformation at lo""w temperature. This phenomenon is called ~econdary Work gmbrittlement (SWE) [1-11]. Up to now there are no standardized testing procedures available to quantify the sensibility of IF-sheet steel to SWE. Neveitheless, a reasonable testing procedure which allows to quantify the tendency of a predeformed part to SWE is necessary for further material development. A commonly used test method is the drop-weight test performed at low temperatures. In such ·tests a cone-like drop weight expands a deep drawn cylindrical cup [l-3, 6, 8, 9, 11]. From this expansion experiment the temperature is determined at and below which a brittle crack can be initiated in the deep drawn cup under the investigated impact test parameters. The highest measured temperature at which a deep drawn cup fails by brittle fracture is called frack appearances !emperature (CAPT). The lower the value of the CAPT the lower is the sensibility of a deep drawn part of IF-sheet steel to SWE. This paper aims to clarify the role of the preforming process on the impact behavior of an IF steel. For this purpose a numerical analysis of the deep drawing process and cup expansion tests are conducted."

Jan 1, 2000

By S. P. Marsh, D. Banerjee

"Casting processes involve phenomena that occur on widely disparate length-scales. Simulation of macroscopic effects, such as heat transfer and convection, are generally addressed by solving the appropriate equations in discretized form on a finite-element mesh. Microscopic phenomena are described by micromodels that may be empirical or analytical in form. Coupling of phenomena in these two regimes is a critical issue in predicting microstructure and defect formation resulting from macroscopic process conditions. A formalism has been developed for expressing micromodels in a consistent manner using stereological parameters to quantify the geometric characteristics of the developing microstructure. This approach provides a robust and physically consistent method for coupling local micromodels with the macroscopic fields. The macroscopic state variables at each node serve as global constraints on the micromodels that are applied to a local unit volume. An outline of an equiaxed solidification model based on this approach is presented, along with preliminary simulation results. Coupling of convection and enthalpy effects between the micro and macro regimes is also discussed. IntroductionThe primary goal of casting simulations is to improve the reliability of cast parts while minimizing cost and development time. Effective simulations can speed up the mold design process and reduce the likelihood of defective parts by refining a particular casting process on a computer, reducing the dependence on cost- and time-intensive prototype castings. The challenge in developing effective simulations stems from the need to address physical processes that occur over a wide range of length-scales, from microscopic (atomic) and mesoscopic (microstructural) scales to macroscopic distances comparable to the size of the casting itself. Overviews of the various thermophysical phenomena and computational factors that are important in solidification modeling are provided in the literature by Rappaz [1] and Tseng et al. [2].Macroscopically, the solidification process is largely governed by the rate of heat flow from the alloy through the mold wall. Another important effect that occurs on the scale of the casting size is convective flow of the melt, which is driven by density-variations in the melt. Macroscopic calculations employ finite-element or finite-difference methods to solve the sets of equations that govern these effects, and the spatial resolution is determined by the grid spacings used for the calculations. Typical spatial resolutions are on the order of 10-2 to 10-3"" meters. This represents a compromise between the resolution required to simulate the continuum transport processes accurately, and the computational time required to model the entire solidification and cooling process."

Jan 1, 1994

By Masahiro Yoshimura, Sergiy Korablov

"Hydi-othermal corrosion ofTiN, TlAlN and CrN PVD films (3 µm thick) deposited on SUS-304 substrate was studied in 100MPa water in 20-950°C temperature range up , to 750h. The beginning temperature of their reaction was determined as 200°c for TiN and TiAlN and 500°C for CrN films, which are quite low in comparison with that of air oxidation of those powders. Very thin oxide scales. of TinO; n-I homologous series phases were formed above 300°C. TiO2 anatare. is observed for TIN and TiAlN films at 400°C. The· feature of hydrothermal corrosion of CrN films seems to be CrNxOy phase formation.Distinguishable weight changes were observed at higher temperature than 700°C for TiN, 750°C for· TiAlN and 800°C for CrN respectively. Hydrothermal corrosion kinetics .was constructed to calculate the activation energy of hydrothermal corrosions. On the base of obtained data, hydrothermal corrosion resistance was as follows: TiN – TiAlN - CrN. Facetted oxide crystals were formed at higher temperature than 500°C for TiN, TiAlN and 850°C forCrN.IntroductionThe metallic nitride (TiN; TiAlN, CrN) PVD films have high hardness, strength and wear resistance. Therefore these films are widely used in industry for wear resistij.nce application such as cutting tools and die molds. Their performances depend on not only the mechanical properties but also corrosion resistance of coated films. High temperature oxidation of metalliq nitride and nitride films was well studied [1-5]. However there are no reliable data concerning the .corrosion resistance of coated nitride materials. In high-temperature and high-pressure water. There are a few reports on hydrothermal corrosion of nitride films [6,7]. The increase of corrosion resistance of CVD films was observed in following succession TiC - TiCNO - TiCN - TiN at 300-680°C temperature interval and I 00 MPa pressure water according to data of the first report. Kawana et al. [7] have reported about excellent corrosion resistance of CrN films under 290°C and 8, 6 MPa water during I 000 h in the circulating type experimental loop. The films thickness was about 7-10 µm in both cases. However it remains unclear the chemical state of the surface species and especially in-depth distribution, oxide scale thickness and its growth, and defects formation in the oxide film."

Jan 1, 2000

By M. Omneya El-Hussaini, M. Galal Abdel Wahab, A. Mohamed Mahdy, M. Fathi El Shahat

"Um-Gheig Pb-Zn representative sample was collected from the main adite of Um-Gheig mine along Red Sea coast in Egypt. Its chemical analysis shows that, it contains 16% Zn, 2.3% Pb, 0.1% Cd and 0.1% B as elements of interest. After H2SO4 agitation leaching, the chemical composition of Um- Gheig Pb-Zn deposit ore residue assayed 2.26% Pb, 1.5% Zn, 0.085 % B and 0.01% Cd. This residue was leached with 20% HCl at S/L ratio 1/3 for 2 hours at 80o C. The chloride leach liquor was found to contain 18 g/l Pb, 13 g/l Zn, 0.1 g/l Cd and 0.75 g/l B with the corresponding leaching efficiencies 79%, 86%, 100% and 88% respectively. Lead was precipitated from the chloride leach liquor using concentrated H2SO4 to obtain PbSO4 with precipitation efficiency 96%. While boron was extracted by the selective resin Amberlite IRA743 with loading efficiency of 80%. On the other hand, Zn and Cd were precipitated using Na2S solution with 86.7% and 100% recovery efficiencies respectively.IntroductionLead-zinc ores occur in Egypt in a few localities distributed along the Red Sea coast between El Qusier and Ras Banas.. The reserve of the ore deposits has been estimated by Soviet and German Experts to be about 900,000 Ton, [1]. Onal et al., [2] recovered Pb from Pb–Zn sample containing 10.17 % Pb and 10.98 % Zn from Aladag in Turkey. El-Sherif, [3] used concentrated HCl to leach lead-zinc ore sample of Um-Sammuki area in Egypt. As had been published by Marchioretto et al. [4], the precipitation of heavy metals with lime, sulfide and caustic soda are the most commonly used economical methods for metal removal. Lead was completely removed from the anaerobically digested sludge by precipitation with NaOH and Na2S at waste water treatment plants. Mahdy et al., [5] had successfully extracted boron from the bittern solution of Qaron Lake by ion exchange resin (Amberlite IRA 743). The extraction of boron was mainly depending upon the pH value. They extracted 80% of boron at pH 5.5, while at pH 3.9 about 74% boron was extracted. Kabay et al. [6] used the column-mode to remove 1g/l of boron from geothermal waste water of the Kizildere-Geothermal Power Station by using Diaion CRB 02 Nglucamine- type chelating resins. In this regard, the removal of lead, cadmium and boron allow the residue to be reclassified as non hazardous material."

Jan 1, 2008

By S. Viswanathan, Q. Han, A. S. Sabau

"In spite of recent advances in the mathematical modeling of fluid dynamics for materials processing applications, no significant advances have been made in the numerical discretization of these equations. In this work, the application of two-step projection methods for the numerical simulation of interdendritic flows is discussed. Unlike previous methods, the methods presented here are constructed for the exact equations which are characterized by variable density and volumetric fraction of the liquid. The drag terms, which describe the momentum loss due to the flow around and through the dendrite structures, are treated implicitly. Numerical examples for shrinkage-induced flow during solidification of an Al-4.5% Cu alloy bar is used to illustrate the effectiveness of the proposed algorithm.IntroductionLiquid contraction during solidification plays an important role in the formation of casting defects such as shrinkage voids, microporosity, and macrosegregation. Owing to their importance, the study of transport processes during solidification have received considerable attention during the past years [1, 2]. By the use of volume-averaging techniques, the mass and momentum equations for flow through a stationary dendritic structure were derived [3]. By using the volume-averaging techniques for multi-phase systems, two-phase transport equations for solidification problems were derived [4]."

Jan 1, 1999

By Jun Enriquez

Kennecott Utah Copper aims to extend anode furnace campaigns to more than three years. As part of that goal improvements are sought on anode-furnace tuyere-area refractory performance. Kennecott and Praxair developed high pressure nitrogen refining for the Oxidation Stage which shortened anode furnace fire refining cycles by up to two hours per cycle. Future developments include optimizing the Reduction Stage’s steam-gas reforming and achieving coherent jet tuyereless refining.

By D. McConchie

Management of caustic red mud wastes at the QAL bauxite refinery uses an innovative approach . involving neutralising the red mud with seawater; solids settle in a Red Mud Dam and residual water (pH = 8.6) is discharged to a tidal inlet. A survey of 18 trace elements in sediment, water, mangroves and molluscs, and an ecological survey of benthic fauna in the inlet, and at near-pristine control sites, revealed no significant trends that were linked to the discharge, except for the concentration of Al which was slightly elevated within 100m of the outfall. Trace element concentrations in water samples were close to, or below, world average seawater values and oysters collected near the outfall were acceptable for human consumption. The impact of discharges is minimised by a high tidal range, >60% flushing of the inlet in each tidal cycle, and the very high trace element binding capacity of sediment in the dam (> 100meq/ 100g dry mud).

Jan 1, 1996

At its Copper Cliff Smelter, Inco Limited processes a bulk copper-nickel concentrate in two Inco oxygen flash furnaces. The furnace matte is converted to low iron matte for further processing, and the molten converter slag is recycled to the flash furnaces. The flash furnace slag is discarded. Natural gas or coke supplies a minor proportion of the process heat requirements, thus limiting the flash furnace matte grade to the target 45% CuNiCo. Coke addition to the furnace offers a potential means of establishing a reducing barrier on the surface of the molten bath. Such a practice would be conducive to producing sulfur deficient (partially metallized) matte. At the same iron content, the iron activity of sulfur deficient matte is higher than that of regular matte. A supernatant coke barrier could, therefore, be expected to lead to higher nickel and cobalt recoveries, reduction or even elimination of magnetite furnace bottom build-up and increased sulfur elimination as SO2 in the flash furnace. Preliminary experiments were conducted in a mini plant flash furnace to investigate the effect on process metallurgy of the suggested modified scheme. This paper presents the experimental results and discusses key aspects of the possible operation of the Inco flash furnace with a coke barrier separating the freeboard from the molten bath.

Jan 1, 2003

By Derk G. E. Kerfoot

The extractive metallurgy of nickel and cobalt has proved to be a particularly fruitful area for innovation in hydrometallurgy and electrometallurgy ever since the development of the Hybinette process for nickel in the early 1900's. In current practice, nickel concentrates are generally smelted to high grade mattes which are then refined to metal by a combination of hydrometallurgy and electrometallurgy, although low grade copper-nickel concentrates are refined directly by the ammonia pressure leach process. Matte refining processes in commercial operation include the direct electrolysis of matte, the ammonia pressure leach, sulphuric acid leaching using air or oxygen at elevated pressure, or at ambient pressure, and chlorine or chloride leaching. Refined nickel is recovered either as electrolytic cathode, or as metal powder by hydrogen, reduction. Hydrometallurgy has also found application in the treatment of nickel laterite ores, both in the reduction roast ammonia-ammonium carbonate leach process, pioneered by Caron and in the Moa Bay acid leach process. Cobalt is recovered as a co-product of copper in central Africa, and as a byproduct of hydrometallurgical nickel refining elsewhere. In the African plants, the copper-cobalt concentrates are roasted and leached in sulphuric acid solution, and copper and cobalt are recovered separately from the leach solution by direct electrowinning. A variety of hydrometallurgical techniques are used for the separation of cobalt from nickel, including selective precipitation and crystallization, solvent extraction, and ion exchange. Like nickel, refined cobalt is recovered either as electrolytic cathode or as metal powder by hydrogen reduction.

Jan 1, 1988

By Walter E. Dean

Twenty six samples of carbonaceous gold ores and associated rocks from outcrop and mine localities in northcentral Nevada were analyzed for concentrations of major. minor, and trace elements, total sulfur, and organic carbon. Q-mode factor analysis was used to define six distinctive carbonate, organic, and detrital associations of elements, and to group samples based on these associations. The trace metals that have clearly enriched the organic-carbon-rich samples are V, Zn, Ni, Cu, Cr, and Mo, although few of the samples could be considered "metal-rich" when compared to other organic-carbon-rich black shales. Rock-Eval pyrolysis was used to evaluate thermal maturity and hydrocarbon yield of the samples. Unfortunately, most samples were too thermally altered to be suitable for routine organic geochemical characterization of organic matter. The 813C values of organic carbon in rocks from different deposits have a trimodal distribution, but there is no clear distinction between the three groups of deposits that can be related to age, thermal history, or depositional environment.

Jan 1, 1987

By David J. Krichten

A method of retrofitting air-fuel burners with oxy-fuel capability overcomes the potential problems associated with oxygen combustion in aluminum melting furnaces. The retrofit burner uses the existing combustion air connection, burner housing, and burner tile and replaces the gas tube with an oxy-gas burner. Maintaining a portion of the air flow to the burner reduces the potential for localized overheating. Proper design of the burner reduces NOx emissions by moderating the flame temperature with furnace gas recirculation. Economic analysis of using oxygen shows the benefits are increased productivity and reduced overall unit cost of melting. In practice, the melt rate in rotary furnaces increases by up to 50% and by up to 35% in reverberatory furnaces. Oxygen utilization reduces total melting cost by 112-314 cents per pound of aluminum melted.

Jan 1, 1997

By Richard D. Hagni

Polished sections of pyrometallurgical intermediate products from a simulated commercial flash furnace were examined by reflected light microscopy, scanning electron microscopy-energy dispersive spectrometry and electron backscatter analysis, and microprobe analysis for phase and textural relationships. The smelter feed is a copper concentrate from a porphyry copper deposit. The concentrate consists primarily of chalcopyrite, bornite and pyrite with smaller amounts of covellite, chalcocite, molybdenite, magnetite, galena, and sphalerite. The flash furnace reactions for pyrite and chalcopyrite can be observed by reflected light microscopy. Reacted angular particles of pyrite exhibit successive rims of fibrous pyrrhotite and hematite or magnetite. Reacted angular chalcopyrite particles show successive rims of bornite, digenite, and chalcocite. Spherical particles, formed by the complete melting of former pyrite particles, consist of variable amounts of granular pyrrhotite with magnetite rims and minor hematite. Spherical particles, formed by the complete melting of former chalcopyrite particles, exhibit exsolution intergrowths with varying proportions of intermediate solid solution, bornite, digenite, and chalcocite and have rims of hematite, magnetite, and copper-iron spinel. Sphalerite and molybdenite do not show evident mineralogical reactions.

Jan 1, 1987

By W. L. Dalmijn, J. M. Krowinkel

A recycling concept of end-of-life televisions starting with shredding will produce a complex material mixture, very heterogeneous in size, shape and degree of liberation. Basically all materials in television scrap are valuable, which means that recovery is important for either economic, environmental or sustainability reasons. However glass, plastics and metals are the materials with the highest potential for recovery. Non-magnetic materials from shredded television sets can be separated into three characteristic size fractions that need further separation for a high value-added recycling of the materials. This study investigated the potential of physical separation of these size fractions into valuable material streams using polyseparator, tlrldy current separator, dry and wet shaking tables and electrostatic separator. An overall mass balance of the mechanically processed televisions was calculated. Evaluation of the produced material fractions showed that heterogeneity in particle shape and size together with the presence of unliberated materials caused sever difficulties in separation when exclusively based on mechanical techniques. The results indicate that a certain degree of dismantling is necessary to achieve products of appropriate quality in physical separation. In order to improve recycling of electronic scrap through design for recycling cooperation between the electronics industry, the manufacturers and the recyclers of electronic goods is necessary.

Jan 1, 2000

By E. Gutierrez-Miravete

A computational method for the simulation of mold filling processes is described. The method is based on the representation of the flowing or deforming medium as a collection of mutually interacting parcels of material. Instantaneous positions of individual material parcels are calculated by numerical integration of the dynamic equations, subject to appropriate initial and boundary conditions. So far, the method has been used to produce qualitative simulations of some flowing and deforming systems encountered in mold filling technology, and our findings are summarized herein. In all cases, individual material particle motions can be followed in detail, allowing critical examination of potentially problematic mold design features.

Jan 1, 1992

By William Petrul

Image analysis studies were performed on mill products from laboratory flotation tests of the Zn-Pb ore from the Faro deposit in Yukon, Canada, to determine mineral liberations at specific grinds and to predict recoveries at optimum flotation conditions. The minimum and optimum grinds for liberating sphalerite and galena were predicted from size analysis data for the minerals in large ore pieces, and determined by image analysis studies of the mill products. The determined optimum grinds are about 2 Tyler mesh sizes larger than predicted because sane of the fine grained sphalerite and galena occurs in interstices between coarser grained pyrite and is liberated when the pyrite grains are broken apart. Materials balance calculations were performed on the analyzed values for the liberated and unliberated sphalerite and galenaa to determine their distributions in the mill products. The laboratory flotation tests recovered 74% of the sphalerite and 83% of the galena in Zn and Pb concentrates respectively. The mineral evaluation study indicates that the optimum recovery for sphalerite and galena are 85 and 83% respectively. The company is currently recovering 80% 'of the sphalerite and 82% of the galena.

Jan 1, 1989

By M. H. Erten

Most of the fourteen workable coal seams in the State of Missouri have high ash and sulfur levels and need beneficiation in order to meet customer and Environmental Protection Agency requirements. If proper ash and sulfur removal methods can be designed, more Missouri coals will be mined and used within the state. One of the main objectives of this research is to investigate the possibility of removal of sulfur of Missouri coals by conventional beneficiation methods.

Jan 1, 1982

By Frame Ritzert, Dennis Keller, Vijay Vasudevan, David Arenas

"An investigation was conducted to describe topologically close packed (TCP) phase instability as' a function of composition in the advanced ·Ni-base superalloy Rene N6. TCP phases are detrimental to overfill high-temperature performance of Ni-base superalloys because of their brittle nature and because they deplete the Ni-rich matrix of potent solid solution strengthening elements. Thirty-four variations of polycrystalline .Rene N6 determined from a design-of-experiments approach were cast and homogenized at 13 l5°C for 80 hours followed by exposure at 1093°C for 400 hours to promote TCP formation. The alloys had the following composition ranges in atomic percent: cobalt 10.61 to 16.73, Mo 0.32 to 1.34%, W 1.85 to 2.52%, Re 1.80 to 2.11%, Ta 2.36 to 3.02%, Al 11.90 to 14.75%, and Cr 3.57 to 6.23%. Physical and chemical characteristics of all microstructures obtained were described using various analytical techniques. From these observations, a mathematical description of TCP occurrence (s and P phase) was generated for polycrystalline Rene N6.IntroductionNi-base superalloy single crystals represent the state-of-the-art for turbine engine airfoil application as they offer the best balance of properties to allow for the high operating temperatures required: for efficient engine operation.1 Current trends in alloy design take advantage of improved creep rupture strength with the addition .of higher levels of refractory elements. 2 In .particular, the addition of significantly higher levels of Re in third generation superalloys is key for both microstructural stability and creep rupture strength. 3 While the presence of the refractories is thought to provide strength benefits from solid solution hardening, a tendency for alloy instability in the form of topologically-close-packed (TCP) phases or secondary reaction· zone (SRZ) ·phenomena accompanies the high refractory content. 3 The formation of these phases in sufficient amount is detrimental to the overall high temperature performance of Ni-base superalloys because of their brittle nature and because they deplete the Ni-rich matrix of potent solid solution strengthening elements.4 The tendency for a particular composition to form TCP may not be immediately known since the precipitation of TCP phases in Ni-base superalloys is nucleation controlled, thereby requiring long times at elevated temperatures to precipitate. 5 They preferentially nucleate along the octahedral planes of the Ni-base superalloys, usually in areas of refractory metal enrichment at grain boundaries or inside dendrites.5-6 In Rene N6, two closely related TCP phases, a and P, have been observed.2"

Jan 1, 1998