Study on Iron Recovery and Desulfurization of Pyrite Cinder

"Due to the low iron grade and high sulfur content, pyrite cinder is difficult to be directly used for iron-making. In this paper, technology of magnetic roasting -grinding and magnetic separation -acid leaching was put forward for reclamation of pyrite cinder. For pyrite cinder of TFe53.51%, S2.20 %, studies showed that good magnetic effect can be achieved at roasting temperature 650~7000, reducing atmosphere CO/(CO + C02) 10~20% and roasting time 10~30 minutes. In separation conditions of grinding size -0.045mm accounting for 96.09% and magnetic field intensity of 1240 GS, iron concentrate of TFe64.81 %, S0.18% and iron recovery rate 91.44% was achieved. Acid leaching was studied to strengthen desulfurization. Results showed that high-quality iron ore concentrate of TFe66.3 l %, S0.10% was obtained under the conditions of hydrochloric acid mass fraction of 5%, pulp density of30%, leaching temperature of70? and leaching time of2 hours.IntroductionPyrite cinder is produced as a by-product of sulfuric acid industry [1] Domestic production is more than 12 million tons every year and occupied area is over 10 million square meters [2,3]. The pyrite cinder outdoor not only pollutes air but also damages surrounding surface [4] It after treatment used for iron-making is an ideal reclamation approach for its rich iron which is commonly 40-60% [5]. But pyrite cinder gets low utilization for its low iron grade and high sulfur content in China [6]. Therefore, comprehensive utilization of pyrite cinder has profound significance to environmental protection and the development of domestic iron and steel industry."