By Xinghua He, Shujing Zhu

"Cycled fluidized bed ash (CFBA), a significant portion of fly ash produced from coal-fired power plants and rejected from the ash classifying process, has remained unused due to its high free CaO and S03 content. It is necessary to extend research on the method to reduce the expansion and improve the compressive strength by some effective chemical activator. This paper presents experimental results on the expansion by Le chaterlier tester and the compressive strength. Hydraulic ash-zeolite (HAZ) cementitious material was blended as the chemical activator to study the effects of the activator on the expansion and the compressive strength. The results show that HAZ can not only reduce the expansion, but also increase the prisms compressive strength. Scanning electron microscope observation and X-ray diffraction analysis indicate that the main hydrated products of the sample are calcium hydroxide, ettringite, zeolite and calcite, which can explain the results of the expansion and the strength tests.IntroductionNearly 80% of the electricity in China is produced by coal-fired plants, which results in the production of a large quantity of coal combustion residues, among which coal fly ash is the major component. Because of that the air-pollution becomes heavier as time going on. Cycle-fluidized-bed-combustion systems are retrofitted to meet air-emission standards mandated by China Clean Air Act. Cycle fluidized bed ash (CFBA) will present new challenges for coal-combustion byproduct management. The use of cycle-fluidized-bed ash as a cement replacement in concrete is the most attractive one because of its high volume utilization and widespread construction. However, the replacement of cement with cycle fluidized bed ash in Portland cement concrete usually increases the expansion and decreases the early strength of concrete. In many research of this field, most of them were focus on the activation of pozzolanic activity of CFBA and to make all kinds of blend cement. A number of studies had been carried out on the activation of CFBA using chemical activators. These studies involved using different activating methods including alkali activation and sulfate activation 11, 2]. The former involved the breaking down of the glass phases in an elevated alkaline environment to accelerate the reaction [3, 4]. The later is based on the ability of sulfates to react with aluminum oxide in the glass phase of CFBA to produce ettringite that contributes to the strength at early ages [5-7]. With respect to sulfate activation, the use of gypsum and sodium sulfate had been well studied [5-8]. HAZ is one of HAS sub-products which is a patentd chemical activator made by Wuhan University (ZL98113594.3). It had been used to activate CFBA to produce blend cement in many Chinese engineering projects and time has told us that it is a good activator."

Jan 1, 2012

By Björn Hinzel, Joachim Rösler

"The most important characteristic of open-pored metals is porosity, since it enables all of their functional applications as filters or sound absorbers. Due to the notch effect of the pores, mechanical properties of porous metals are better than the ones of comparable structures made of polymers or ceramics. Consequently, only open-pored metals can be used in aircrafts to reduce flow noise or noise resulting from the core engine by acoustic absorption. Absorption properties depend highly on pore size and porosity of the material, which must be characterized as precisely as possible in order to analyze the correlation between morphology and noise reduction performance. Here, a line segmenting method is explained in order to characterize pore size and porosity of absorber materials using image processing based on two dimensional microscopy images, including sample preparation and specification of the set-up. Then, the influence of the pore structure on the measured absorption behavior is discussed. Finally, the correlation of acoustic behavior, pore morphology, and porosity is outlined.IntroductionSignificant noise loads affect everyone causing anxiety, depression, insomnia and other effects which impair health and productivity [1],[2]. Due to the rising number of flights and aircrafts, air traffic noise increases dramatically. To counter this development, various approaches have been developed to reduce the different noise sources resulting from airframe, jet or engine [3],[4],[5],[6]. One approach to reduce this noise is the application of noise reducing liners in the hot gas path [7]. This is especially important, since the engine is becoming the dominant noise source of modern airplanes during take-off [8]. Due to the elevated temperatures and high fatigue loading in this part of the aero-engine, conventional passive absorber materials cannot be used. Polymers would not be able to bear the heat and ceramic fibers would crack under the mechanical loading due to the notch effect. Consequently, this study focuses on metals with open pores, which can resist elevated temperatures and fatigue loading and additionally resemble geometrically conventional passive absorbers. Based on the production processes, e.g. sintering of metal fibers [7], powder processing using a foaming agent [9], coating of polymer foams [10], or using melt infiltration techniques [11], the characteristic dimension of the porosity is usually in the range of 0.01-10mm. In this work, sintered metals and metal sponges are analyzed after the theory of sound absorption is briefly outlined. Then, measurements of the acoustic absorption of metal sponges and sintered metals in an impedance tube are performed. To understand and predict the acoustic properties of metals with open porosity, it is necessary to characterize the materials as precisely as possible. This is explained in detail using a line segmenting technique, followed by a discussion of the connection of pore characteristics and acoustic absorption. Finally, a conclusion is given."

Jan 1, 2012

By Gaifeng Xue, Xiaohong Xu, Meng Liu, Yijie Song, Guotao Xu, Jixiong Liu

BN (Boron Nitride) based composites were prepared with hot-pressing by using h-BN as main material in ceramic preparation process. The relative density, bending strength, vickers’ hardness, thermal shock resistance, thermal expansion coefficient, thermal conductivity, phase composition and microstructure were tested and analyzed by using modern testing technology. The results indicate that the best formula is B, the relative density is 97%, the bending strength is 260 MPa, the hardness is HV5 343kg/mm2, the thermal expansion coefficient is 2.8×10-6℃-1, the thermal conductivity is 22 W/(m.K) and have no crack after thermal shock for 20 times by water cool. XRD analysis indicates that the main phase compositions are h-BN, β-Si3N4 and sialon. SEM studies show that the grains wrapped up by solid solution.

Jan 1, 2015

By Guo Xian Jian

In this paper, an alternative process to recover the value metals from polymetallic gold ore by FeCh leaching was proposed. In the process, gold was recovered by direct cyanidation from the leaching residue, the isolative electrolyte in chloride solution was selected to recover lead, the cementation with copper powder was used to recover silver and the solvent extracting was applied to recover copper and zinc. The total recovery of gold, lead, copper, silver and zinc in the process is 90.8%,96.05%,84.3%,81.98% and 54% to the bullion of gold, lead and silver and sulfate of copper and zinc, respectively. The process conditions selected for FeCh leaching are the temperature of 104°C, leaching time of 6 hours, Fe3+ content of 140 g/l and stoichiometry of FeCl3.

Jan 1, 1996

By P. D. Navarro

The behavior and operability of LIX 1104SM extraction was studied at laboratory scale on the Solvent Extraction at Sb3+, from high concentration sulfuric acid. In order to evaluate the reactant batch tests were made at laboratory scale as well for extraction as for re-extraction of Sb3+. Experiences achieved were: extraction kinetics, temperature effects, selectivity tests and re-extraction selectivity. A extraction kinetics was found, reaching equilibrium in 2 min, high selectivity of Sb3+ extraction in front of Cue , existing As5+ co-extraction and Fe3+ At the re-extraction stage, equilibrium was reached in 3 min, getting high Sb3+ re-extraction efficiency with HCl concentrations within 6 and 8 M. A high selectivity was achieved on Sb3+ re-extraction in front of As+5, existing Fe+5 re-extraction.

Jan 1, 1999

By S. A. Platias

Large amounts of dunile tailings can be recycled for olivine produdion from the existing beneficiation adivity of chromite ore in northern Greece. This olivine production aims at the preparation of a material suitable for the substitution of the environmental hazardous quartz sand in the foundries of Europe In smelting of chromite ore the losses that occur ore usually of the order of 6-8% Cr that report in the slag. Most of this is in the form of oxides that cannot be recovered, but usually 30-35% is in the form of FeCr alloy that can be recovered by gravity methods. About 90% of the produced slag is sold for road construdion after crushing to a desired grain size. Finally, recycling of chromites sludges from the ferrochrome produdion plant, through the preparation of pellets, improved the total chromite yield by 2%.

Jan 1, 1996

By Banqiu Wu, Ramana G. Reddy, Robin D. Rogers

Experimental studies on aluminum recycling via electrolysis in ionic liquids were carried out at the temperature of 105°C. Impure aluminum was dissolved at the anode and pure aluminum was deposited on a copper cathode. The products were characterized using an optical microscope, micro-image analyzer, X-ray diffraction, emission spectrometer, and atomic absorption analyzer. The electrorefining process with a current density of 310 - 730 AJm2, and current efficiency of about 99% was obtained. Impurities such as Si, Cu, Zn, Fe, Mg, Cr, Ni, Mn and Pb were removed as anode residue. Impure aluminum was purified from 79.8wt% to 99.9wt%. At a cell voltage of 1 volt, the energy consumption of about 3 kWh/kg-Al was obtained. The process has advantages of low energy consumption and low pollutant emissions, compared with the current industrial refining process.

Jan 1, 2000

By D. E. Larson

In cooperation with the National Institute of Environmental Health Science and the National Institute for Occupational Safety and Health the U.S. Bureau of Mines conducted grinding research on non-asbestiform tremolite. The goal of this effort was to prepare ground tremolite samples containing a considerable percentage of acicular grains with aspect ratios (approximately = 8um long with widths = 1 um) similar to those of asbestos particles suspected of causing cancer, Optical-and electron-microscopic examinations were used to monitor the size and shape of the grains in the ground products. Although customized milling techniques do have noticeable effects in producing acicular grains, the prismatic nature of fracturing in the non-asbestiform tremolites limited the number of acicular grains that could be purposely produced, and indicates that the likelihood of high concentrations of acicular particles occurring under normal mining and milling conditions is small.

Jan 1, 1991

By Wenbo Luo, Kang Liu, Fusheng Mao, Jilai Xue, Jun Zhu, Chunlei Yang

Extracting alumina from coal fly ash (CFA) is of great interest for both environmental protection and recycling valuable alumina content. In this study, ultrasonic aided leaching process as an effective method was investigated to enhance extracting Al2O3 from CFA via concentrated sulfuric acid sintering. The influence of ultrasonic power and processing time were tested under the conditions as the same as those without ultrasound. It is found that the alumina extraction rate can reach 90.5 % with ultrasound assistance, while the ultrasonic treatment can reduce almost 15 ~ 30 min in leaching time and 5 ~ 10 oC in leaching temperature than those without ultrasonic operation at the same Al2O3 extraction rate. In addition, the ultrasonic can reduce calcium content by 6 ~ 8 % dissolved into the leaching liquid. SEM analysis also shows that the residue particle size with ultrasound is smaller than that without ultrasonic treatment.

Jan 1, 2015

By Toshihiro Kuzuya

A hydro metallurgical process has been developed for the recovery of metal values such as Co, Ni and rare earths from the electrode materials of spent nickel metal-hydride(Ni-MH) secondary battery. MmNis_xCo. (Mm : Misch metal) intermetallic compound could be separated from the electrode materials mixture by sedimentation. A typical chemical composition of MmN5-xCox was approximately, in mass%, 56.0%Ni, 13.4%Ce, 10.6%La and 7.9%Co. The time dependency of leaching intermetallic compound with sulfuric acid solution was examined with processing factors such as sulfuric acid concentration, temperature and agitation intensity, The leaching of rare earth metals proceeded very rapidly, reaching completion in less than 1.8ks. On the other hand, the slow leaching of nickel was observed. The percent of nickel leached at 328K could only reach about 70%.

Jan 1, 2003

By Atsushi Shibayama

The aim of this research was to develop a copper recovery process from mine tailings (0.34%Cu) using flotation followed by high-pressure oxidative leaching (HPOL) and solvent extraction. The results of HPOL using the concentrate of mine tailings obtained by flotation under the optimal conditions of the previous study shown that an efficient copper dissolution of 94.4% was achieved in an H2O media, while the copper concentration of PLS reached to be 2.9 g/L. The solvent extraction of PLS obtained from the optimal HPOL showed that 91.3% copper was recovered in stripped solution under the determined optimum conditions, in which the copper concentration achieved to be 44.8 g/L. Finally, a proposed copper recovery process from the concentrate of mine tailings was developed by combination of HPOL and solvent extraction, while a total copper recovery of 86% was achieved.

By V. B. Chernyavsky, Ladokhin S. V.

Equipment and continuous casting technology for the production of small diameter copper rods and tubes are described. Industrial copper wastes, such as scrap and shavings, were used as the charge. An electron-beam installation for rod and tube production includes a crucible with an electromagnetic stirring system and a pouring hole in its bottom, a bottomless mold, .and a special cooling system, which includes an oil and water cooling devices. For the first time in the electron-beam technology, rods of 8 mm and 14 mm diameter mm tubes of 14 mm external diameter and 7 mm internal diameter were produced through continuous casting by pulling them out of the vacuum chamder into the atmosphere with depressurizing the vacuum chamber. The production capacity of a single strand continuous casting machine was 200 mm/tnin for rod casting and 150 mm/min for tube casting.

Jan 1, 2000

By Sesha S. Srinivasan

Mechanochemical synthesis has been employed to prepare new light weight complex borohydrides, Zn(BH4)2. The thermal calorimetric and gravimetric analysis of these complex borohydrides shows the hydrogen decomposition temperature (Tdec) of about 100° C with theoretical capacity of ~8.0 wt%. This advanced materials based technology is considered to be suitable for attaining the US-DOE grand challenge technical targets. The powder x-ray diffraction analysis of the mechanically milled Zn(BH4)2 exhibits the presence of zinc borate and NaCl phase. The FTIR spectra of BH4-ion in NaBH4 has a characteristic band at 2290 cm-1,whereas in Zn(BH4)2, it occurs at ~2061 cm-1 (bridging B-H bonds) and ~2451 cm-1 (terminal B-H bonds) as well. The reversibility of hydrogen decomposition and recombination process is carried out by PCT measurements with multi-cycling procedure.

Jan 1, 2006

By Na Wang, Chao Du, Yao Zhang Shuqiang Jiao, Hongmin Zhu

"Na2NbAlO5 was synthesized using Nb2O5 and NaAlO2 as raw materials in molten NaCl-CaCl2 by a solid reaction. With an addition of sodium into the melts, Na2NbAlO5 was subsequently reduced to form NbAl3 intermetallic compound with a particle size of 50-300nm.IntroductionThe intermetallic compounds of niobium aluminides have been a subject of research interests as high temperature materials because of their properties such as high melting temperature, large specific strength at elevated temperature, good resistance to high temperature oxidation, low density and large ductility [1,2]. They are applicable for turbine blades in aircraft engines and stationary gas turbines [3,4].In recent years, the methods of powder synthesis have been widely discussed. There are many methods to synthesis intermetallic compounds such as conventional melting and solidification [5], powder metallurgy [6,7], reaction sintering [8] and reaction sintering with prior mechanical activation [9,10]. There is a prominent weakness in such methods that they use metal to produce intermetallic compounds by the means of diffusion reaction. Although the metal can diffusion sufficiently, it is still hard to avoid maldistribution of the constituents which impairs the properties of the materials."

Jan 1, 2012

By Metehan Erdogan, Ishak Karakaya, Fuat Erden, Emre Ergül

"The FFC Cambridge process was suggested as a promising Si production technique for the expanding solar energy industry. Direct electrochemical reduction of bulk SiO2 plates and porous SiO2 pellets in molten CaCl2-NaCl salt mixture were investigated at 750°C by applying 2.8 V potential difference. The produced Si powder was brown and found to be contaminated by the Ni and stainless steel plates used as the cathode contacting materials. The reduction rates of the bulk SiO2 plates and porous SiO2 pellets were compared from variations of current and accumulative electrical charge that passed through the cell during the electrochemical reduction. The amorphous bulk SiO2 plates were reduced slightly faster than porous pellets of crystalline SiO2. The overall reduction potential of SiO2 pellets against the graphite anode at 750°C in molten CaCl2-NaCl salt mixture was determined as 2.3 V by cyclic voltammetry. This potential was supported by calculations.IntroductionMetallurgical grade Si cannot be directly used in electronic industry and some intermediate steps are required to produce industrial solar grade silicon (SOG-Si). A promising alternative solar grade silicon production technique is the FFC Cambridge Process [1]. Production of Si by electrochemical reduction of SiO2 at 850oC in molten CaCl2 electrolyte was first studied by Nohira et.al. [2]. In their study; Si formation was observed on bulk SiO2 cathodes after 1 hour of electrolysis. Complete electrochemical reduction of porous SiO2 pellets was first reported by Jin and his coworkers [3]. The mechanism of electrochemical reduction of SiO2 to Si in molten CaCl2 was explained in another study [4]. Reduction rates of bulk SiO2 and porous SiO2 pellets were also compared previously and it was found that reduction rates for bulk plates were higher [5]. Furthermore, it was reported that mixing Si into porous SiO2 pellet increased the reduction rate [5]. Mo [2, 4-7], Ni [3, 8, 9] or Si [6] were used as cathode contacting materials in various studies. Yasuda et. al. [6] produced Si with 99.80 % purity using Si plates as cathode contacting material to reduce metal contamination."

Jan 1, 2012

By S. V. Ketov, V. P. Menushenkov, V. S. Shubakov

"The glass samples were obtained by melting of the oxides mixture SrO-Fe2O3-B2O3(Al2O3) at 1200-1250°C with subsequent quenching of the melt on quickly rotating steel roller. Submicronsized Sr(Fe,Al)12O19 particles were formed in glass-ceramic matrix during the crystallization aging of glass. The aging temperature Tag varied in the range 650-950°C. The submicron-sized hexaferrite powder was obtained by removing of the matrix phases using etching. The samples were characterized by X-ray diffraction, scamiing electron microscopy and magnetization measurements. The glass-ceramic material exhibits very high coercivity value up to 10 kOe. The samples of magnets were obtained by pressing of the hexaferrite powder at RT and subsequent aging in the range 900-1200°C. The aged samples exhibit coercivity value up to 8 kOe.IntroductionStrontium M-type hexaferrites have been widely used in technology and industry mainly for production of permanent magnets owing to their appropriate magnetic properties, chemical stability and low cost [1,2]. The SrFe12019-based compounds are characterized by high magnetocrystalline anisotropy and single easy magnetization axis. The highest coercivity is received for monodomain, defect-free single crystal particles with size D - 100 mn. Finely grained strontium hexaferrite prepared by chemical methods such as sol-gel pyrolysis and oxide glass crystallization exhibits high coercivity up to 6-8 kOe [3-5]. Owing to the partial substitution of Al for Fe in the strontium hexaferrite leading to the increase in the magnetic anisotropy field Ha=2Ki/M,, the increase in the coercivity may be received [6]. The notable results were achieved using the SrO-Fe2O3-AlzO3-B2O3 glass crystallization and formation of perfect submicron crystals of alumina-doped hexaferrite [ 6, 7]. The coercive force of glassceramics reached values of up to 10 kOe. Hexaferrite particles are well faceted and have the shape ofhexagonal bipyramids with truncated vertexes [7].In the present paper, we report results of our investigation into the SrO-Fe2O3-B2O3(Al2O3) glass crystallization, hexaferrite powders and permanent magnets, which were prepared by pressing submicron-sized hexaferrite powders at RT and subsequent sintering at 900-1200°C."

Jan 1, 2012

By Philip L. Sibrell

A new process utilizing pulsed fluidized limestone beds was tested for the remediation of acid mine drainage at the Friendship Hill National Historic Site, in southwestern Pennsylvania. A 230 liter-per-minute treatment system was constructed and operated over a fourteen-month period from June 2000 through September 2001. Over this period of time, 50,000 metric tons of limestone were used to treat 50 million liters of water. The influent water pH was 2.5 and acidity was 1000 mg/L as CaCO3. Despite the high potential for armoring at the site, effluent pH during normal plant operation ranged from 5.7 to 7.8 and averaged 6.8. As a result of the high influent acidity, sufficient CO2 was generated and recycled to provide a net alkaline discharge with about 50 mg/L as CaCO3 alkalinity. Additions of commercial CO2 increased effluent alkalinity to as high as 300 mg/L, and could be a useful process management tool for transient high flows or acidities. Metal removal rates were 95% for aluminum (60 mg/L in influent), 50 to 90% for iron (Fe), depending on the ratio of ferrous to ferric iron, which varied seasonally (200 mg/L in influent), and <10% of manganese (Mn) (10 mg/L in influent). Ferrous iron and Mn removal was incomplete because of the high pH required for precipitation of these species. Iron removal could be improved by increased aeration following neutralization, and Mn removal could be effected by a post treatment passive settling/oxidation pond. Metal hydroxide sludges were settled in settling tanks, and then hauled from the site for aesthetic purposes. Over 450 metric tons of sludge were removed from the water over the life of the project. The dried sludge was tested by the Toxicity Characteristics Leaching Protocol (TCLP) and was found to be non-hazardous. Treatment costs were $43,000 per year and $1.08 per m3, but could be decreased to $22,000 and $0.51 per m3 by decreasing labor use and by on-site sludge handling. These results confirm the utility of the new process in treatment of acid impaired waters that were previously not amenable to low cost limestone treatment.

Jan 1, 2003

By Jorge Alberto Soares Tenório, Denise Crocce Romano Espinosa, Viviane Tavares Moraes

"The development of mobile phone technology has increased the replacement of outdated equipments for more modern models, transforming disposal of such devices into a serious environmental problem. Recycling appears as an attractive alternative to minimize the environmental impact of disposing such large quantities. Recycling can be accomplished by treating the printed circuit boards of used mobile phones by using the same techniques used in ore treatments with hammer mill; magnetic separation, electrostatic separation and grain size range. Before performing the recycling process a PCB characterization was performed to identify the fraction with the higher metals concentration/content. This study demonstrated that the electrostatic separation was not the best metals concentration of PCB aiming the recycling, while the non-magnetic residue had presented a more significant metal concentration. Furthermore, after the magnetic separation was possible to separate the following metals: iron and nickel.IntroductionPortable electronic devices have gained increasing acceptance over the last decades. Mobile phones sales in Brazil, for instance, have reached 104 million in 2007, and 128 million in 2008. It is estimated that, around the world, 100 million mobiles are thrown away every year, either because of loss of functionality or because newer models are launched in the market [1,2, 3]. Printed circuit boards in mobile phones are made of many materials, with approximately 83% in weight being metals and fiber-glass, and the balance being plastics pl. Several metals can be recovered from the electronics waste, such as copper, tin, iron, lead, nickel, titanium, aluminium as well as some precious metals such as gold, silver and palladium [4, 5, 6, 7, 8]. Concurrent with the increasing world demand for copper, there average metal content in ores has been decreasing. Economically interesting copper mines used to have 4% metal content, whereas presently, such content is around 1%, i.e., for every 1 ton of ore extracted, only 10 kg are copper [9, 10]. Approximately 33% of printed circuit boards (PCBs) composition is copper, that is, for every 1 ton of PCBs waste, 330 kg are copper [1]. Research in recycling PCB waste focuses on mechanical, electrometallurgy, pyrometallurgical and hydrometallurgical processes [3, 8]. Collecting and recycling obsoletes electro-electronic equipments is very important these days, in order to, not just preserve the non renewable natural resources but also to keep the environment and the population safe from the pollution caused by the toxic materials and heavy metals present in this kind of waste."

Jan 1, 2011

By Tzu-Chien Lin, Jack Tsai, Ming-Yu Lin, Der-Ray Huang, Jiin-Sen Chen, Jing-Xuan Lin

"In this paper, some DVD-R discs have been selected for long time light exposure test and high temperature and humidity test. Generally, recordable media under long time light exposure maybe be defected seriously. If we use Jitter value 8% as a reference to determine the life time of DVD-R samples, some discs defect after 5 hours of light exposure while some discs can endure over 25 hours. Also if we use reflectivity 45% to determine the life time, some discs defect after 30 hours light exposure while some discs can endure over 40 hours. From our results, the good samples show good characteristics of PI error. The absorption spectrum of recordable media is a good reference to justify the quality of dye media. These results can be used to estimate the life time of recordable discs.IntroductionIn general, the life time of DVD-R with a layer of organic dye recording layer is required for preservation in decades. In addition to optical characteristics and thermal properties, we still need to consider the stability of the dye in recording media. The presentation of the color on organic dye is not only related to the material's property but also related to the light exposure. In this study, we focus on the absorption characteristics and reflectivity of organic dye in optical recording layer after light exposure. The optical properties of discs depend on the functional groups and molecular structure [1]. According to ""DVD Specifications for Recordable Disc (DVD- R)"", the reflectivity should higher than 40%. From measured reflectivity, we can confirm that the important issue is whether dye be affected by light exposure or not. Because each specific functional group absorbs the specific spectrum, we can check the characteristics of functional groups from their UV/Visible Spectra. We also use High-performance liquid chromatography (HPLC) to detect the different components of dye on the recording layer [2]. The jitter value test is to test the error cause by digital signal of recording media. If we use jitter value 8% as a reference to determine the life time of DVD-R samples, the purpose of this study is to investigate the jitter values of recording media after high light exposure and high temperature/humidity test. The results of these test will be helpful for the development of long-life optical storage media."

Jan 1, 2012

By Akio Ohta

The Hyuga smelter has been producing ferronickel by a rotary kiln-electric furnace process in Miyazaki, Japan. Several approaches to improve our operation have decreased the electrical energy consumption. A new process was developed to decrease the cost of energy even further. Oil and technical oxygen are injected through lances to heat up the calcined ores (calcine) instead of the electric power. Main problems during the development of the process were the short life of the water-cooled lances, the check on security of the safety system and the eruption of combustion gases through the calcine bed. These problems have now been overcome successfully, and stable operation can be maintained. The addition of 1 Litre of heavy oil per tonne of ore can save the electrical energy requirement by 8.6 kwh per tonne of ore. The new process has resulted in a reduction of the electrical energy consumption by more than 10 percent

Jan 1, 1992