By Fumitaka Tsukihashi

Phase diagrams of the CaO-SiO2-FeOx-MgO, Al2O3 systems arc necessary for the analysis of copper smelting reactions and sintering process of iron ore. The effect of MgO and Al2O3 addition on the liquidus of the phase diagram of the CaO-SiO2-FeOx system at low oxygen partial pressure was observed. The liquid phase area changed bi the addition of MgO and Al2O3 with a changing oxygen partial pressure from 10-8 to 10-3 atm (10-3 to 10 2 Pal at 1573K. The effect of Fe3+ / Fe2+ ratio on the melting mechanism is discussed.

Jan 1, 2003

By Andreas Dietrich

Laser off-gas measurement of CO, O2 and temperature has been carried online in EAFs. A visualization screen shows the values of CO and Oxygen and temperature for the entire heat, and includes the status of furnace equipment. The historical data of the heats are stored such that the furnace performance can be evaluated and optimized. A short comparison between laser based and conventional systems has been carried out related to speed, influence of dust, water, pressure, protection for bag house explosions. A high water and/or dust content in the sample does not represent a problem for this type of system. The measurement method works without interruption even under worst conditions such as dirty scrap, carbon injection etc. The installation was developed in conjunction with Marienhuette, Graz. They are 100% scrap based with a tap to tap time of ca. 46 min. Keywords: Laser Measurement, Off Gas, CO, O2, Temperature

Jan 1, 2003

By V. R. Voller

"The World Wide Web (the web) provides a very useful resource for the enhancement of teaching and research dissemination. This paper advocates that researchers take control of this resource and become actively involved in creating web content. Two examples of the use of the web in a materials setting is provided. The first illustrates how a concept quiz for teaching can be developed. The second shows how a materials processing model can be run in real time over the web. The paper closes with a summary of some resources that can be used to create web materials.IntroductionA recent copy of a newspaper advertisement read""Share what you know, learn what you don't""This neat phrase sums up a powerful teaching and research philosophy. In an educational setting a prime motivation for research is to uncover the unknown and venture in directions previously uncharted. The balance to this search for knowledge should be a desire to share that knowledge with others; whether it be with students in the classroom or research colleagues in a wider setting.The .World Wide Web and its associated multi-media software offer a perfect platform for researchers to share their knowledge with an extremely wide sector of the research community. To enable the use of this resource researchers must take the power that the web offers them into their own hands and create products that take maximum advantage of the medium. It is key that researches at the forefront become directly involved, otherwise a potential powerful medium will not realize it's true potential, and colorful products with no core content will proliferate. The object of this paper is to outline two ways in which the web can be used to enhance teaching and research objectives."

Jan 1, 2000

By S. P. Rivers

The stainless steel industry re1ies on nitric-hydrofluoric acid (HNO,/HF) pickling solutions to remove surface contaminants and maintain the corrosion resistance of the steel. More stringent environmental guide1ines are expected to be placed on the disposal of these solutions which could significantly increase processing costs. The U.S. Bureau of Mines has been conducting research to develop a process for recycling depleted pickling solutions, thus reducing the quantity of by product acids generated. Research has shown that F- can be liberated from the predominant iron fluoride species (FeF,') by using oxalic acid in an electrodialysis cell. Ion selective membranes allow dissolved metals in the depleted solution to be replaced with hydronium ions by metathesis, thereby regenerating the HF. The regenerated HN03/HF is then retained in the pick1ing solution. This paper reports on the research effort at the U.S. Bureau of Mines Rolla Research Center to apply electrodialytic recycling to HN03/HF pickling solutions.

Jan 1, 1993

By José Antonio, Silva Souza, Luis Alves Venancio, Emanuel Negrão Macedo, Antonio Ernandes M. Paiva

"The production of alumina from bauxite using the Bayer process generate 1.25 ton of the residue known by red mud and 460 kg of CO2 per ton of alumina.The direct use of exhaust gases from the alumina refineries to react and neutralize the bauxite residue may allow a double gain: open a wide range of new applications for bauxite residue reducing the reactivity of red mud and sequester approximately 15% or 67 kg of CO2 per ton of alumina.This paper shows the reaction of a suspension of bauxite residue-water with a simulation of the calcinator exhaust gases of the refinery. The influence of the temperature and the ratio water red mud is also analyzed.2 IntroductionThe production of millions of tons per year of alumina around the world generates around 1.25 tones of the residue known as red mud and 0.4 ton of CO2 per ton of alumina . The vast majority of the red mud is stored in large sealed lakes. Due to the high reactivity is considered dangerous and currently there is no operating process capable of reuse all the material at any refinery. These lakes after filled of solid material eventually have the surface revegetated. Otherwise will need monitoring for decades and remain as an environmental passive. The search of a industrial process that combine the reduction of the CO2 emission and the reduction the pH of the red mud opening the possibility of use in large scale in a economically viable way is the main objective of this work.The use of the exhaust gases of the refineries to neutralize the bauxite residue may allow a double gain: Open a large array of new applications for the residue with the reduction of its reactivity and sequester million of tones of CO2 plus other gases like SO2 [7] and NOx.This project main objective is to study the reaction of the CO2 with the Bayer process residue in order to obtain the basic parameters to design an equipment capable of process this reaction on a pilot scale. With this objective compositions of red mud on spray were processed with flow of gas containing CO2 at different temperatures and with concentration similar to the exhaust gases of the calcination process of the refineries. With the results, basic concepts of a pilot scale equipment were evaluated.A revision of the work already done on this type of residue were done [3, 9, 10]. Alternatives and potential barriers on chemistry and environmental fields were discussed. With the objective of industrial application the potential use of these materials were evaluated through the pH control, mass balance and x-ray diffraction."

Jan 1, 2010

By Luciano B. Oliveira, Angela O. Costa, Sergio N. Monteiro, Luis Guilherme C. Marques

"Biofuels are gaining a relevant role in today’s world not only as a solution for the decreasing petroleum reserves but mainly as a positive contribution to the efforts in global warming mitigation. In Brazil, since 1975, the replacement of gasoline by ethanol started a so-called PROALCHOOOL program, which is now being complemented with the replacement of petroleum diesel by biodiesel. This biodiesel program was officially created in 2005 with mandatory goals, supported by legislation, of 2% addition in 2008 and 5% addition in 2013 into all commercialized regular diesel. In this work, a critical analysis of the Brazilian biodiesel program is presented. The technical aspects related to the different raw materials, including wastes, available for biodiesel conversion as well as the economical conditions associated with production costs and market logistic are discussed. The environmental benefits associated with the retention of greenhouse gases are also discussed.IntroductionToday the commonly accepted fact that the petroleum world reserves are probably passing through a maximum and start declining in terms of the total amount that can be extracted by existing technologies is motivating significant changes in our society. The continuous increase in the price of gasoline and other liquid fuels is an immediate worrisome and visible consequence. However, more than an economical problem, our civilization is already facing the effects of global warming, due to CO2 emission from burning fossil fuels, mainly from coal and petroleum. It is now realized that a large scale solution for these problems demands the prompt substitution of non-renewable fossil fuels by others that, in addition of being renewable, have a relatively lower contribution to the greenhouse gases."

Jan 1, 2008

By Mario H. Castro-Cedeno

"A design for a handheld MEMS chemical detector is proposed. The detector will be used to detect trace amounts of chemicals in air. It can detect drugs, toxic chemicals and/or explosives. The proposed detector will use ion mobility spectrometry (IMS), a technique that is well known for accuracy and has been used in the past in suitcase sized chemical detectors. The separation and detection of the chemicals occurs in the drift channel and the process was modeled using the finite element method and CoventorWare modeling software. A manufacturing process sequence for the drift channel is proposed and was demonstrated.IntroductionThe goal of this effort is to design, mode~ and prototype a MEMS chip that will be the key component in an ion mobility spectrometer (IMS). This technique uses and asymmetric potential to separate the various ion species in a stream of incoming air [1-4]. One advantage of IMS is its ability to separate chemical species from air at atmospheric pressure and temperature. This is a requirement for a simple to use handheld drug or chemical detector. IMS can be used to detect drugs, toxic chemicals and explosives and it is well known for accuracy in detecting very small amounts of chemicals. This chemical detection technique has been used in the past, but not in handheld detectors.One variant of IMS is the high-field asymmetric waveform ion mobility spectrometry or FAIMS [3]. The FAIMS process, shown in Figure l, works as follows: a gas sample is admitted into the instrument where gas molecules are ionized, typically by a weak radioactive isotope source, ultraviolet light source; and more recently through field emission. The ions move along the length of a channel while they are separated in the transverse direction by an asymmetric electrical potential. The potential, in the form of an asymmetric waveform, causes relative motion between the various chemical species. The species that hit the charged top and bottom plates are neutralized and only those ions that move along the center are detectable as charged chemical ions at the end of the channel."

Jan 1, 2004

By Feng Gao

A general unsteady- state model, based on a cracked substrate, has been developed to account for reaction and diffusion within porous substrate during oxidation of Carbon Fiber Reinforced Carbon matrix (CIC) composites. The effects of several parameters, such as diffusion and reaction rate ratio, oxygen concentration, and composite density, on oxidation process are explored. Also, theoretical results for a set of parameter values of the CIC composites are compared with experimental data. It shows that the model predicted values agreed well with the experimental data in weight loss. Based on this model, quantitative predictions of oxidation of a composite with cracked substrate can be made.

Jan 1, 1993

By M. E. Myers

An experimental program is being carried out to determine the thermodynamic characteristics of zinc solubilization in high-temperature iron and iron-carbon alloys. Two versions of an isopiestic technique are being used, with zinc at a lower temperature being equilibrated with pure iron foils or molten iron-carbon alloys at a higher one. The lower temperature sets the partial pressure of zinc vapor, and thus the activity relative to a given reference state. Initial results show Henrian behavior for dilute zinc solutions in austenite and a molten 4.6% C alloy, with unit-pressure solubilities in pure Fe that closely match the predictions of Wriedt.

Jan 1, 1992

By Randy Martin

"Greenstone Resources Ltd. constructed and operates the Santa Rosa open pit, heap-leach gold mine in Veraguas, Panama. The project was commissioned in 1995 at a designed capacity of 1.8 million tons per year. The ore exhibits a long leach up to three years, and requires three stage crushing to minus 3/8 inch to achieve on average a 74% gold recovery. The crushing plant is required to handle high volumes of clay and the circuit includes a Barmac Crusher. Panama receives over 3 meters of rain annually and Greenstone is using innovative means to control the project's water balance. Greenstone has developed a successful approach to operating a low grade (1.5 gm Au/T) deposit under difficult operation conditions.ABSTRACT ONLY"

Jan 1, 1997

By Anjan Kumari, B. K. Soni, Manis Kumar Jha, A. Vidyadhar, Vinod Kumar

"In the present paper, recovery of valuable metals from the poly-cracked ash obtained by pyrolysis of discarded PCBs has been studied following physical beneficiation and a hydrometallurgical process alternate to smelting. The ash is subjected to comminution for the separation of metallic components from non-metallic fractions by scrubbing, tabling and froth flotation which enriched the metal in the concentrate -97% which was further screened to separate high and low metal concentrate. The finer fraction containing -12% metallic value was leached in acidic solution. Almost all (Cu, Pb, Fe, etc) were leached in 4M HN03 at 90°C in 75 min at a pulp density 100 g/L. The characterization of both ash and residues were made by XRD, EPMA, EDS, etc. to validate the experimental results. The metals from the leach liquor could be recovered/separated using solvent extraction techniques which can further be processed to get pure metal salts/ sheets.IntroductionPrinted circuit boards (PCBs) are an essential component of electrical and electronic equipments (EEEs) as it plays an important role during operation of these devices. The world market of PCBs has reached nearly $60 billion in 2012, with 1.7 percent real growth over 2011 [1]. The diverse technology-driven global market is expected to grow at an average annual rate of 5% by 2014 [2]. The waste EEEs are generated due to replacement of obsolete equipments with modem ones and thus their demand is also increasing rapidly [3]. The discarded e-wastes are being piled up as landfills which affect the environment and cause health threats to living organisms, if not disposed of properly. These e-wastes contain metals some of which are precious, few are hazardous and others as valuable."

Jan 1, 2014

By Zongliang Zhang

Electrowinning is a significant step in metal extraction processes. Because the nature of electrowinning is to reduce metal from its oxidized state, substantial energy consumption accompanies it. Electrowinning processes of different metals have much in common—the deposition of the metal on the cathode and the counter-reaction on the anode. An advanced model was developed that can be applied to a variety of metal electrowinning processes. A model for specific metals can be readily obtained by modifying parameters such as potential, kinetics, and side reactions in the model. The model incorporates mass transfer, gas-liquid flow, electrochemistry, and deposition, making it a comprehensive electrowinning model. The model is applied to copper, nickel, and zinc and verified with the experimental results. In addition, the parameter settings and results of different metals were compared, showing that this model has great versatility and accuracy, thereby making it an efficient and effective research tool.

By Shilai Yuan, Huimin Lu, Zhijiang Gao, Panpan Wang

"Solvent refining of silicon through using Si-Al melts is a valid method to remove the impurities from metallurgical grade silicon (MG-Si) melt. The thermodynamic behavior of impurities Fe, Al, Ca, Ti, Cu, C, B and P in MG-Si during the solidification of MG-Si was studied based on the available thermodynamic parameters and experimental data. The morphology of inclusions was investigated by Scanning Electron Microscope (SEM). The chemical composition of inclusions in MG-Si and Al-Si melt was analyzed by EPMA. It is found that the amount of white inclusion reduces and most impurities are solved into the Al-Si melts. After solidification of Si–Al alloy using induction heating and acid leaching, impurities can be effectively removed. The solidification of silicon from the Si–Al melt is found to be more effective for purification than general silicon solidification.IntroductionPhotovoltaic energy is one of promising energy resources in a sustainable society because of its inexhaustibility and cleanliness. Although the production and installation of solar cells have increased significantly during the last decade, the cost of solar cell installation is still high. Multicrystalline silicon has now become the main material in the photovoltaic market because of its low production cost and because of the relative high conversion efficiency of solar cells made from this material, which has been studied for a long time [1-3].Electronic grade (EG) silicon (99.9999999% Si) is commonly used as the raw material to produce SOG-Si (99.9999% Si). Silicon produced from the chemical routes restricts the development of solar cells due to environment threaten, high energy consumption and low productivity. Purification of metallurgical grade silicon (MG-Si) is a low cost, environment friendly method. Although several metallurgical processes such as directional solidification, vacuum refining and electron beam melting [4], have been developed, the cost reduction and refining efficiencies for manufacturing silicon is still have to be further optimized.In the purification process, it is difficult to remove boron and phosphorus by the conventional metal refining method. The refining efficiency depends on the segregation behavior of different elements in solid silicon and the liquid phase. The segregation ratios of all investigated impurities were found to be much smaller than the segregation coefficients between solid and liquid Al-Si melts [5]. For instance, the segregation coefficient of B in Si is 0.8 at the silicon melting point (1687K), whereas it is around 0.2 when silicon is solidified from Si-Al melt at 1273K. For phosphorus the segregation coefficient is 0.06 when silicon is solidified from Si-Al melt at 973K°C, which is much less than 0.35 for recrystallization from liquid silicon. Since the segregation coefficient of boron in silicon is 0.8, it cannot be removed by directional solidification."

Jan 1, 2014

By Richard D. Hagni

The techniques of reflected light microscopy and cathodoluminescence microscopy are uniquely suited to the study of the products from many important industrial problems. Ref1 ected 1 ight microscopy provides the means to rapidly identify the mineralogy of an industrial sample, determine the abundance of each phase, and examine the mineral intergrowths or textures. Cathodoluminescence microscopy is a relatively new instrument that provides the means to cause many minerals to cathodoluminescence under the microscopy. The cathodoluminescence of a mineral allows it to be readily distinguished from other phases that differ in cathodoluminescence but are similar in optical properties. Cathodoluminescence microscopy is especially useful to detect cathodoluminescence minerals that are present in only small quantities. Reflected 1ight microscopy and cathodoluminescence microscopy have been successfully applied in studies of beneficiation products, prediction of beneficiation and leaching problems, phosphatic iron ores and mill products, pyrometallurgical products, roasted refractory gold-bearing sulfides, ceramic build-ups, electric arc furnace and smelter dusts, and other industrial products.

Jan 1, 1993

By A. Buzaianu, P. Motoiu, G. Popescu, C. A. Popescu, I. Rusu, A. F. Olteanu

"In recent years, the recycling magnesium metallurgy has developed new types of alloys, some of which exhibiting special electrochemical characteristics. Their application has found a fertile field in the energy conversion technologies. The paper introduces some technologic data on the recycling of aeronautical parts and scrap materials generated from the disassembling of magnesium alloy components, attempting to also solve the recycling of magnesium painted parts. The approach is meant to establish a superior quality method for recycling discarded parts or the excess of re-melting material in order to reduce environmental impact and costs. Magnesium-base alloys used as anodic materials are characterized by a high uniformity of the structural properties as well as by superior electrochemical performances, as compared to the ""classically"" used materials: Zn, Pb, etc. In nonconventional applications of magnesium alloys used as sacrificial anodes working in seawater, special alloying elements contribute to improving anodic processes. The influence of these alloying elements on magnesium sacrificial anodes was studied. It was found that the use of recycled materials in anode manufacture could reduce the Mg alloy cost by as much as up to 75% of the cost for virgin material, including the costs for the entire sequence of collection and transportation from a molding factory to a refinery, re-melting and composition adjustment.1. IntroductionMagnesium alloys are valuable materials because they exhibit low density, good forming and machining qualities, particular electrochemical properties and have a high recycling potential. There exists a false idea about the high costs of the use of magnesium alloys, partly justified by the lack of secondary materials suppliers and the insufficient knowhow in the diverse user industries to provide for an efficient substitution of conventional magnesium alloys for multipurpose applications. These circumstances have lately spurred the magnesium industry to develop new alloys and coatings and to improve processing techniques [1]. As a result, magnesium supply has greatly expanded and so have the research and development efforts to achieve complete recycling of Mg alloys.In consumer markets, magnesium is frequently selected because it helps reduce enery consumption. For example, an equal volume part made of magnesium is 23% the weight of a steel part and 64% the weight of an aluminium part."

Jan 1, 2008

By F. Sanchez, A. Mejias, C. Frias, G. Diaz

"Crude zinc oxides are the major source of secondary zinc and are produced from fuming processes like Waelz kilns. The impurities of crude zinc oxides make difficult their processing in primary zinc refineries due to mainly high chloride tenor. Washing with sodium carbonate is a costly operation and chloride removal efficiency is not good enough, so further purification steps are required. The crude zinc oxides are easily treated using ZINCEX™ technology based on leaching, solvent extraction, and electrowinning. The ZINCEX™ process is commercially available and is designed to be a perfect barrier for metallic impurities and halogens, allowing selective zinc extraction in mixed chloride and sulfate leaching solutions. Other valuable components as lead and silver can be efficiently recovered from the leaching residue using PLINT technology in chloride media. Silver is recovered as silver cement and lead is precipitated as pure lead oxide or carbonate, which can be smelted at low temperature.IntroductionZinc is a fully recyclable metal and at present approximately 70% of the zinc produced worldwide comes from primary zinc while 30% originates from secondary materials. Nowadays, the zinc recycling rate is continuously increasing mainly through galvanized steel scrap processing, and crude zinc oxides are the major source of secondary zinc [1]. Secondary zinc oxides are obtained from fuming processes like W aelz Kiln, Rotary Hearth Furnace or Primus Furnace. Waelz is the dominant technology accounting for 80% of total crude zinc oxides production worldwide. In the Waelz process, steel dust is mixed with solid fuel reductant (coke breeze) and pelletized. It is then fed to the kiln and heated to a reaction temperature of l ,200°C. In such conditions, zinc, lead, and other non-ferrous metals are vaporized into the flue gas together with chlorides and alkaline metals. Mixed oxides are drawn from the kiln with the process gases and separated to produce typical crude zinc oxides [2]."

Jan 1, 2011

By F. J. Arriagada

Where gold is present in a finely disseminated form within sulfide particles, the porosity and surface area of the calcined material strongly influence leaching since they control the penetration of solution inside the gold-bearing grains. On the basis of a stability diagram for the Fe-O-S in the temperature range of 400 to 750aC, the expected sequence chemical transformations associated with the oxidation of pyrite is discus-sed. By using analytical techniques which include scanning electron microscopy, X-ray diffraction and BET gas adsorption, the chemical and structural changes experienced by auriferous pyrite-arsenopyrite concentrates and pure pyrite samples are studied under an oxidizing roasting atmosphere of com-position 80% N + 20% O2 in the temperature range of 450 to 750°C. The results indicate that as the roasting temperature increases, the surface area of the calcines decreases sharply after a maximum value attained at about 450-500°C. SEM micrographs show that the needle-shaped tips which characterize the surface of the oxide product become wider and the size of the pores between them is decreased when the roasting temperature is in-creased from 550 to 750°C. This effect suggests that the formation of a more "closed" hematite product at higher temperatures is due to sintering associated with a faster growth and crystallization of the oxide. A strong correlation is shown between increasing roasting temperature and increase in gold lost in cyanidation tailings, an effect which may be partly attributed to the loss in surface area of the calcines.

Jan 1, 1982

By Raghavan Srinivasan, Y. V. R. K. Prasad, William G. Frazier, Steve C. Medeiros

"Aerospace gas turbine disks operate in an environment of relatively high stresses caused by centrifugal forces and elevated temperatures. These severe conditions necessitate the need for materials with good high temperature strength and low cycle fatigue resistance. One class of alloys used for this task is the nickel base superalloys, out of which, lN 718 is the most widely used in the aerospace industry [I]. The properties of IN 718 are attributed to the combined effects of the chemistry, heat treatment, and microstructure. The chemistry is tailored not only for solid solution strengthening but also for precipitation hardening developed during heat treatment, which combined with a fine grained microstructure lead to excellent mechanical properties such as low cycle fatigue resistance and elevated temperature strength. The properties of a gas turbine disk are sensitive to the microstructure, in particular the grain size, which is dependent on the processing history. The ability to precisely control the microstructural development during forging is dependent on controlling the process so that the workpiece is deformed within a ""safe"" region where no microstructural damage or flow instabilities occur. The microstructural mechanisms during deformation may themselves vary within the ""safe"" region and it is desirable to determine them within the range of parameters that are commonly used in industrial processing. The objective of this work is to establish a relationship between the grain size and the process control parameters i.e., temperature and strain rate, in the hot working of IN 178.BackgroundIN 718 belongs to a class of nickel-iron base superalloys with a face-centered cubic (FCC) austenitic matrix strengthened by precipitation of ordered intermetallic or carbide precipitates and is a nickel-rich alloy strengthened by ordered body centered tetragonal (BCT) precipitates, Y"". The alloying of nickel and iron results in the formation of the austenitic matrix, y, while the addition of chromium and molybdenum cause solid solution strengthening. Also, alloying with niobium causes precipitation of the metastable hardening constituent Y"" (Ni3(Nb,Ti)). Extended aging treatments in the temperature range 650 °C - 980 °C allow the more stable orthorhombic 8 phase (Ni3Nb) to form. Trace amounts of boron are also added to serve as grain boundary strengtheners for high temperature creep resistance. Hot deformation of IN 718 is performed between the Y"" and 8 solvus temperatures to facilitate recrystallization and to control grain growth. While deformation below the Y"" solvus (""""962°C) produces no change in grain size, deformation above the Y"" solvus but below the 8 solvus will lead to a dynamically recrystallized microstructure. The presence of the 8 precipitates will pin the grain boundaries after recrystallization and restrict grain growth so that a fine grain microstructure is obtained. Deformation above the 8 solvus ("""" 1038°C) will lead to a microstructure which has undergone grain growth during deformation."

Jan 1, 2000

By D. M. Hausen

Microscopic point-counting of polished sections, in combination with x-ray diffraction analyses of representative whole rock samples, provides an efficient means to compare the modal mineralogic composition of different rock types. Major gangue minerals, e.g., quartz, feldspars, micas, amphiboles, chlorite, clays, etc., are estimated semiquantitatively by x-ray diffraction techniques, utilizing optimum grind, gridded sample surfaces and a sample spinner during scanning. Opaque to semi-opaque oxide and .sulfide phases are estimated by microscopic "point-count" and "gross-count" scanning. Total mineralogic compositions are calculated and normalized to 100 percent from XRD and microscopic data by computer programming. Comparative mineral analyses for different rock types, as well as quantitative microscopic data for various parameters, including particle and crystal sizes, textures, degree of alteration, paragenesis, etc., provide useful guides in mineral exploration, both in early stages of geologic mapping and later stages of economic evaluation. Several case histories are described.

Jan 1, 1981

By D. M. Hausen

Multiple drill sections through many of the numerous breccia pipes in the American Eagle copper deposit at Copper Creek, Arizona, have been evaluated by means of alteration and geochemical data. Contoured plots indicate vertically plunging, concentric, cylindrical shells of alteration and mineralized rock that are similar in structure, geometry, magnitude and petrology to the San Manuel-Kalamazoo Deposit, located about 14 miles to the southwest. Both deposits are similar in dimension and consist of multiple, irregular, rod-shaped injections of porphyry into a granodiorite host. Analogous to the San Manuel-Kalamazoo Deposit, most of the porphyry plugs are oriented parallel to the cylindrical axis of the "ore shell". A continuously mineralized, elliptical shell, inferred from deep drilling, is capped by a flatter zone of copper mineralization. Above this flat zone, copper-bearing fluids were channeled upward along conduits that correspond with quartz-sericite "breccia pipes". At depth, zones of sericite and K-feldspar alteration products exhibit conformable relationships with the copper deposition. A "bullet-shaped" ore shell, with a nearly vertical axis, is proposed to explain the conformable zones of altered and mineralized rock. The "nose" or top of the "bullet" is 1800 to 2300 feet below the surface, and structurally controlled in part by steeply dipping Hi and ENE faults. If correct, this model suggests that the vertical ore shell may extend to great depth.

Jan 1, 1988