By Dumitru Mitrica, Vasile Soare, Elvira Alexandrescu, Mihai Ghita, Marian Burada, Petru Moldovan, Raluca Maria Florea

"Aluminum metal matrix composite Al-Si /SiCp was prepared by reactive gas injection and subsequent remelting. The influence of the remelting process on the microstructure and physicalmechanical properties of the resulted material was investigated. Samples resulted from the synthesis process contained silicon carbide agglomerations in the vicinity of primary silicon and large pore concentrations. In-situ formed silicon carbide presented mostly a polymorphic structure with particle sizes varying from 1 to lOµm. Physical and mechanical properties were largely influenced by the porosity distribution. The remelting process provided a decrease in the composite material porosity and pore size, with significant improvements in the particle distribution and physical-mechanical properties of the composite material. Additions of up to lwt.%Mg in the starting alloy improved the in-situ carbide formation and particles distribution in the solidified material. However, stable and large particle agglomerations were detected in the material in absence of conventional stirring or controlled solidification techniques.IntroductionThe remarkable properties of composite materials (yield strength, stiffuess, hardness and resilience at a reduced specific weight) make them attractive for applications in automotive, aerospace and military industries. Particle reinforced aluminum metal matrix composites (PAMMC) are known for their high strength to weight ratio. The recent development of P AMMC created the possibility to obtain large particles concentrations, exceeding 10% by volume ofreinforcement (SiC, AIN, Al203, etc.). The improvement ofhigh temperature strength and wear resistance made them appropriate for the use in automotive applications, such as the pistons, rotors, disc brakes, and propeller shafts [ 1]. The present main disadvantage of the P AMMCs is their high costs for obtaining and processing related to the final product performance. In order to benefit from the advantages that offer composite materials properties a reasonable production cost - performance ratio must be obtained [2]. Recent innovations in the manufacturing of aluminum-based metal matrix composites provided notable performance improvements but no feasible solutions were found for lowering their present high prices."

Jan 1, 2014

By Jae-Ho. Lee

For some electronic applications where a dispersed electrically-conductive particulate-phase is employed, the conductivity of the surface (or near-surface region) of the particles provides for the primary mechanism which determines its electrical conductivity. Particles of a less expensive material, which may have desirable thermal-expansion properties, when coated with silver offer a means of also obtaining desirable electrical properties and at low cost. The research conducted was focused primarily on the development of silver-coated tungsten particles for thick-film polymeric conductors. The ammoniacal electrolyte was formulated from silver-nitrate, glycine inhibitor and formaldehyde reductant. The reduction, and subsequent deposition, of silver occurred selectively on the surface of the tungsten particles. Coated particles were assessed by SEM imaging. The thickness of the silver coating was estimated to be approximately 100nm on the basis of a mass account and the coating being uniform. The electrical conductivity of a silver-coated tungsten-powder pellet was found to be similar to that of a silver-powder pellet, of identical geometry.

Jan 1, 1997

By Jingyuan Wang, Hengyi Zhang, Peng Lan, Ruitian Zhang, Jiaquan Zhang, Yang Li

"For the determination of mould taper and wall thickness, a 3-D numerical model of ingot-mould-hot top system has been made to evaluate the related ingot solidification process and the final soundness. The effect of mould wall thickness and the taper of its hot faces on the thermal history and the as cast structure of steel ingot has been revealed through the numerical simulation. It is shown that the ingot soundness can be improved remarkably by increasing the mould wall thickness, which is possibly beneficial to the mould life as well owning to an improved mould thermal state. The mould taper is vital to the ingot soundness but much less coherent to the mould temperature profiles. Under given casting situations, a larger mould taper can lead to a less intensity of the shrinkage porosities at the top part of ingot.IntroductionIngot casting is still one of important processes for steel production, which is adopted especially for the supply of large-sized semi-products of high quality special steels. The understanding to the solidification process is vital to both the yield improvement of casting production and the quality control of steel ingots, such as their soundness and homogeneity.The ingot processing and service performance are closely related to its defects, such as porosities and pipes[1,2], which are the most common but serious defects during ingots casting. In the late 1960s, Mahadevan and Murthy et al.[3], Irani and Kondic[4] began to analyze criteria for the prediction of shrinkage porosities in light metal casting. In 1980s, Niyama and Uchida[5], Hansen and Sahm[6,7] et al have successfully presented some related porosities and pipes criteria for steel casting. At the same time, numerical solidification simulation was well developed and applied to ingot quality studies[8-10]. However, due to the quick development of continuous casting, less emphasis has been given to the further study on ingot casting process. There leaves much work to be made for the comprehensive understanding to ingot quality improvement and the mould design by the aid of modern solidification technology[11, 12]. In this paper, the effects of mould taper and wall thickness on its thermal history, ingot solidification and the final soundness are numerically studied through solidification simulation, which has been adopted in mould design and industrial production of both the mould and its steel ingot."

Jan 1, 2012

By Rodríguez M. Esperanza

The efficient performance of Pachuca tanks is strongly linked to the suspension of mineral particles, which results from the motion of the liquid caused by injected gas rising, in general, through a central draft tube. This study reports a computational investigation on the effect of operating and design parameters on the suspension of particles. By extending the classical 2-phase drift-flux model to compute the gas hold-up, the three-phase (water-air-particles) system was simulated as consisting of a variable-density liquid plus the solid particles. These two phases were treated as interpenetrated continua using an Eulerian approach to set a turbulent recirculating flow model in 2-D and transient state. The model predicted adequately the measured critical superficial air velocity, uc, needed for maintaining particle suspensions, in pulps with 10-50 wt% solids. Additionally, the model was used to investigate the operation of industrial size reactors, obtaining results that agree well with the general trends reported in the literature, and highlighting important differences with respect to laboratory-scale reactors.

Jan 1, 2009

By Kexin Jiao, Huichang Song, Zhijia Zhang, Jianliang Zhang, Zhengjian Liu

A clear understanding of iron carburization reaction occurring between molten iron and carbonaceous materials is of great importance in blast furnace, and it is one of the hot spots that ironmaking workers pay close attention to. Although carburization rates between iron and coke have been studied, the factors directly controlling it have not been clearly identified. This study focused on the kinetics analysis of iron carburization reaction. Sulfur content was determined as having positive influence on graphite carburizing reaction rate in the range of 0.02% - 0.06%. The values of apparent activation energy calculated by the experiment are consistent with the existing literature, which in turn proved the reliability of the experimental data.

Jan 1, 2015

By Jesse White, Tyler Salisbury

Research projects contain many stages of development from the conception of an idea to a fullscale commercial operation. The transition from laboratory-scale research to bench-scale roasting can represent a significant increase in complexity and cost, depending on how many variables are being evaluated. Thermogravimetric analysis (TGA) can simulate roasting conditions and produce a small sample for chemical analysis or materials characterization. A simultaneous thermogravimetric and differential scanning calorimetry (TG–DSC) can identify endothermic and exothermic reaction temperatures. Using thermal analysis, some of the process variables can be tested and eliminated such as ore and reagent blends, retention times, operating temperatures, and some atmospheres.

Jan 1, 2015

By T. Johnson, B. Q. Li

"Electromagnetic stirring has found a wide application in metals processing for the benefit of obtaining refined solidification microstructures. This paper presents an experimental study on the melt flow and turbulent behavior in an electromagnetically stirred Woods metal pool. The experimental setup consists of metal bath unit equipped with temperature control to allow both cooling and heating, velocity probe positioning unit and data and signal acquisition and processing unit. The whole measuring system is under the control of an IBM personal computer. Velocity measurements are made using the incorporated magnet probes, which are calibrated using a turntable. The measured results showing the effect of the coil positions, coil arrangements and the applied currents on the melt flow are presented. Both mean flow and turbulence quantities are discussed.1. IntroductionElectromagnetic stirring is widely practiced in the metals industry for melt mixing and for casting microstructure refinement. Industrial examples are taken from induction furnaces where the electromagnetic forces are applied to generate desired melt mixing and also various types of electromagnetic stirrers used in various stages of steel and/or aluminum casting processes to produce fine grain solidification microstructure or to eliminate undesired defects such as TCG (twinned-columnar-grain) structure. For ultrahigh purity aluminum or high strength aluminum alloys containing zirconium or lithium, grain refinement can be difficult with the conventional technique, and electromagnetic stirring provides a particularly powerful means to obtain the refined solidification microstructure [1]. A fundamental understanding of the melt flow and the turbulence characteristics in these magnetically-driven flow systems is of significant engineering importance to both process design and product quality improvement.There exists extensive literature on the magnetically-driven melt flows in material processing systems. Nakanish. et al. [2] were perhaps among the early investigators to mathematically and physically model the magnetically-driven flow phenomena in molten metal systems. Subsequent theoretical and experimental work by Tarapore and Evans [3, 4], Szekely and Chang [5], Hunt and Moore [6] and Szekely and El-Kaddah [7] has contributed very significantly to our understanding of magnetically-driven flow in inductively stirred melts. They have developed mathematical models for the electromagnetic field and turbulent flow in induction furnace and validated the models by either laboratory experiments or direct measurements in the industrial-scale induction furnaces."

Jan 1, 1998

By F. J. Tavera

The column flotation technology, at first developed for application in mineral dressing, has received special attention in processing of non-mineral dispersions as a result of its low cost, high efficiency and relatively simple operation. This paper presents the results from the operation of a laboratory flotation column for the separation of vegetable oil and soap from aqueous industrial effluents, The flotation system was operated under continuous countercurrent conditions without and with additions of a cationic collector. The experiments show that it is possible to separate about 80% of the organic phase in a rougher flotation stage. These results suggest that the recovery of the organic phase is highly dependant on the dispersion characteristics (i.e. bubble size, gas holdup and bubble surface area flux) and the existing an optimum bubble size from which either smaller or larger, the recovery of the organic decreases.

Jan 1, 2003

By Hans Jürgen Maier, Hans-Bernward Besserer, Gregory Gerstein, Florian Nürnberger

The formation and development of voids in both the single-phase ferritic steel DC04 and the dual-phase ferritic-martensitic steel DP600 are discussed. Various mechanisms and kinetics of void formation are considered regarding the influence of dislocation glide, precipitates and other parameters. Different characteristic locations in the microstructure are investigated at which strain concentrations during plastic deformation can occur and cause the formation of voids and microcracks. For the specimen preparation ion slope cutting is applied. Voids and cracks revealing ductile damage are analyzed by Scanning Electron Microscopy (SEM). Stress concentrations in consequence of plastic deformation could be shown by extinction contours on images recorded by Transmission Electron Microscopy (TEM).

Jan 1, 2015

By G. A. Irons, D. Guo, D. Angheiina

To produce low-carbon (<30 ppm) steel in the tank degassing process, a ladle of steel with an oxidizing slag is placed in a vacuum tank equipped with bottom bubbling. The kinetics of this process are slow compared to the more prevalent RH degassing process, providing the impetus for the present work. There are several aspects to this work: water models of the fluid flow in the ladle; simulation of the decarburization (CO evolution) with C02 desorption in water; pilot-plant (60 kg) studies of the decarburization kinetics; mathematical modelling of the fluid flow in the ladle; mathematical models for each of the kinetic sites (plume, top slag and auto-nucleation); and full-scale trials. The results show that during the refining cycle the contribution from each reaction site changes, suggesting avenues for reducing cycling time and final carbon contents.

Jan 1, 2000

By Yasuo Kudo, Wu, Hayato Sato, Hiroshi Nakazawa, Shouming

"In order to recover copper from a waste nickel condenser powder, bioleaching experiments were carried out using Thiobacillus ferrooxidans in a shaking flask. The content of nickel and copper in the waste nickel condenser powder in this study were 8.0% and 3.5%. X ray analysis showed the peak of barium titanate. In the preliminary study using metal nickel and copper powders , the dissolutions of nickel and especially copper were accelerated with the addition of ferric iron in the bioleaching of nickel and copper powders while not in the absence of ferric iron. Ferric iron oxidizes both metals, and Thiobacillusferrooxidans oxidizes ferrous iron resulting from the oxidation of metals, whereby the dissolutions of metals proceeds. The dissolution rates of nickel and copper increased with increase in the concentration of ferric iron in the bioleaching of the waste nickel condenser powder.1. IntroductionNickel condensers rejected from manufacturing plants are crushed and landfilled. Waste nickel condensers contain nickel and copper and could be considered as nickel and copper ores. Since the capacity of landfills is diminishing, it is required to recycle metals of waste nickel condensers in order to reduce the amount of wastes landfilled. Conventionally, metals in the waste were recovered by dry metallurgy after the incineration.Nickel has been refined by solvent extraction - electrowinning method (SX-EW method). Recently the amount of copper refined by SX-EW method has increased (Takahashi, et al. 1994). This method is cleaner and consumes less energy than conventional methods. Nickel dissolved well in acid solutions, but copper is not. If copper is leached efficiently from a waste nickel condenser powder, SX-EW method will be applied to recover copper from them"

Jan 1, 2000

By Yuanbo Zhang, FENG ZHOU, Guanghui Li, Zhengwei Yu, RuijunWang, Tao Jiang

Composite agglomeration process (CAP) of iron ore fines has been proved an effective route for ironmaking burden production, and is characterized by low the fuel consumption and high the productivity compared with the traditional sintering process. Sintering behavior of pelletizing feed in CAP has not been studied fully yet. In this study, individual pellet and simulated CAP cells were roasted under the simulated sintering conditions. The compressive strength, FeO content and microstructures of roasted samples were investigated. The results show that pelletizing feed either from magnetite ore hematite concentrate can be indurated under the conditions of conventional iron ore sintering. Hematite pelletizing feed has better sintering property than magnetite pelletizing feed. Pelletizing feed consolidation in CAP cells is identical to the individual pelletizing feed, but the strength of CAP cells is much higher than the individual pelletizing feed. Higher basicity in both pelletizing feed and matrix feed is beneficial to the strength of CAP cells. Individual strength of pelletizing feed is not the decisive factor in CAP as the pelletizing feed has been embedded into the matrix with high basicity and formed an organic whole. The main chemical compositions and basicity of pelletizing feed and basicity matching with matrix feed is important.

Jan 1, 2015

By Bernd-Arno Behrens, Klaus-Georg Kosch

"In times of increasing energy costs automotive lightweight construction is gaining in importance. This paper deals with the production of hybrid steel-aluminum compounds by forging. The compound forging process is a promising method to successfully manufacture functional parts by applying resource-saving process steps. Nevertheless, challenges resulting from different material properties must be solved.The heating of hybrid material work pieces made of steel and aluminum is a great challenge. Steel is forged at a temperature of at least TSt =900 °C, while aluminum should not exceed a temperature of TA1= 500 °C. For achieving the required temperature gradient extensive experimental investigations have been carried out. Intermetallic phases form during the manufacturing process and can influence the bonding and the global part quality. In addition, methods for the characterization of the joining zone between the materials steel and aluminum are analyzed and the factors influencing the formation of intermetallic phases are determined experimentally.IntroductionIn times of increasing energy costs and stricter conditions relating to environmental protection, automotive lightweight construction is gaining in importance. The production of hybrid compounds by forging is a promising method to manufacture functional parts by applying resource-saving process steps. In compound forging a hybrid raw part consisting of a solid core, which is enclosed by a hollow casing, is joint in the forming process. This results in a graded material structure in the part in which the mechanical properties can be specifically adapted to the requirements. Compound forging is the form joining and/or firmly bonded joining of at least two different materials while plastic shape forming occurs (Figure 1)."

Jan 1, 2012

By Ehsan Khajeh

In this study, the permeabilities of Al-15.5wt%Cu and Al-19.5wt%Cu have been determined by solving the full Navier-Stokes equations on 3D geometries of interdendritic channels obtained by X-ray microtomography (XMT). The samples for XMT were sectioned from different positions in directionally solidified cylinders in order to obtain a variety of microstructures for each composition. The flow has been solved using a 2nd-order accurate Finite Volume Method (FVM) approach. The effect of employing uniform or unstructured mesh on the calculated permeability has been studied. The Marching-cube triangulation method was necessary to extract accurate surfaces for unstructured volume meshing. Calculated values of permeability for this range of solid fractions show partial agreement with previous experiments. Observed deviations are attributed to the difficulties of experimental permeability measurements.

Jan 1, 2009

By A. F. Giamei, F. Landis, M. O. Duffy, R. J. Mador

"The directional solidification of complex advanced gas turbine airfoils must be carried out without the nucleation of undesirable grains and with minimal shrinkage. Such problems are typically eliminated by using a number of mold design and process iterations. A more efficient approach is envisioned where a solidification model is generated and utilized to accelerate process development. Towards this end, the directional solidification (DS) of simple geometrical shapes in a crystal grower apparatus has been simulated with MARC finite element nonlinear thermal analyses.The finite element models of cylindrical (2D) and rectangular (3D) cross-section bars in the DS environment are presented. Temperature dependent properties, the impact of latent heat of fusion and a time-dependent radiation boundary condition constitute the more salient features of the MARC models. Solidification zone thermal behavior is predicted during the withdrawal transient for the specific case of nickel based superalloys grown in ceramic shell molds. Comparisons of analytical results with experiments demonstrate notable prediction accuracy. INTRODUCTIONSingle crystal and uni-directional crystal turbine blades require tightly controlled conditions if metallurgically and mechanically acceptable parts are to be produced. Gated blade geometry and process parameters must be precisely determined if incorrect grain structure, orientation and shrinkage are to be avoided. Since purely experimental development programs designed to evaluate these parameters can be excessively costly and time-consuming, an effort combining engineering analysis and verification by experiment has been initiated at Pratt & Whitney. Comparison of analytical predictions and measured data for geometries simpler than a turbine blade, namely cylindrical and rectangular bars, comprised the initial stage of this effort. Subsequent tasks involve modeling geometries of increasing complexity and ultimately the simulation of the directional solidification of the turbine blade, shown schematically in Figure 1. This paper summarizes the results of the initial stage of the effort."

Jan 1, 1986

By Ricardo Melamed

Metallic mercury has been extensively used for gold recovery. Although the solubility and mobility of metallic mercury is low, this metal can undergo many transformations, leading to mercury contamination in humans. The complexity of Hg chemistry in the environment reflects its different possible oxidation states and species, with different physical-chemical properties. The interaction of Hg in the terrestrial system, as well as in the aquatic environment, is important to understand the mercury cycle. This paper reports data on the adsorption of Hg onto an Oxisol soil. Results show that the interaction of Hg(II) at the soil-solution interface depends strongly on ligand concentration in solution, which can affect Hg mobility. The presence of the chloride anion in solution increases the mobility of Hg(II) through the soil, due to a relative lower affmity of mercury chloride at the oxide surface. In the absence of chloride, Hg(II) form strong complexes with the surface, and its adsorption behaviour is similar to the adsorption of other hydrolizable cations.

Jan 1, 1996

By C. M. F. Vieira

The main characteristics and physical and mechanical properties of clays from the county of Campos dos Goytacazes, located at the northern part of the State of Rio de Janeiro, Brazil, are presented. The characterization included mineralogical composition, chemical composition and particle size distribution. The properties related to water absorption, linear shrinkage and flexural rupture strength were obtained in samples that were prepared by 20 MPa uniaxial pressing and fired at 950 and 1100oC. The results showed that the clays are predominantly kaolinitic with high percentage of clay minerals. The kaolinitic structure associated with a small amount of fluxes confers a refractory behavior which makes difficult the sinterization and impairs the ceramic consolidation.

Jan 1, 2009

By Mei Yang, Wei Gao, Jian Yang, Qingcai Liu, Wenchang Xi

"TiO2 has been loaded on cordierite porous ceramic to prepare the SCR catalyst carrier by using both APCVD and sol-gel technology. In APCVD method, TiC14 and O 2 were used as reaction precursor. TiC14 was gasified by using N2 as carrier gas which was controlled to 500sccm. Its reaction temperature and reaction time were limited to 773K and 30min respectively. The physical properties, SEM and SEM-EDX of the TiO2-cordierite carrier and the properties of SCR catalysts prepared by these carriers have been tested. The tests showed that TiO2 loaded by APCVD method were of graininess shape and even accumulation. The loading rate of TiO2 and the specific area of carrier sample were increased 114% and 21 % respectively comparing with sol-gel technology. In the result of sol-gel method, the maximal difference of Ti content was 66.92%, while the result of APCVD method was 18.89%. It demonstrated that TiO2 was uniformly attached with the cordierite ceramic by using APCVD method, which would ensure more active ingredients well loaded on the Ti02-cordierite carrier. This difference made the denitrification ratio of catalyst prepared by APCVD method was 8.1 % higher than that of catalyst prepared by sol-gel method.IntroductionIn recent years, the emission of NOx, which were caused by coal-fired power plants, has gotten more and more attention. SCR (selective catalytic reduction) is the most effective technology to DeNOx [ll. The core technology of it is the catalyst. The SCR catalyst usually uses Ti02 as the carrier, and V2O 5 as the active component [2, 3] . However, the thermal stability and mechanical properties of TiO2 carrier are unstable, which would influence the performances of the catalyst. The commercial catalyst generally uses WO3 or MoO3 to promote its heat stability at present [4-7] Besides, TiO2 is expensive. Compared with TiO2, the cordierite is of good thermal stability and lower price. So loading Ti02 on cordierite porous ceramic as carrier to produce SCR catalyst is of good prospects [S, 91 • Currently, TiO2 is usually loaded on cordierite by the sol-gel method. But some research has shown that the sol-gel method easily reduced the loading performances of TiO2, such as distribution, combination, etc. APCVD (atmospheric pressure chemical vapor deposition) has many advantages to preparing TiO2 films, such as high bonding strength, fast reaction rate and so on [l0-13l_ In this paper, TiO2 has been loaded on cordierite porous ceramic to prepare the SCR catalyst carrier by using both APCVD and sol-gel methods. The properties of the carriers prepared by the two processes have also been compared."

Jan 1, 2011

By Takeshi Yoshikawa, Kazuki Morita, Kunitoshi Matsunaga

"In metallurgical grade silicon (MG-Si), most impurities mainly exist at the grain boundaries and distribute in silicon grains at extremely small contents. Grain boundary phases in MG-Si transform into liquid above the eutectic temperature, and migrate towards high temperature regions when heated under a temperature gradient. With the migration of all liquid phases in MG-Si to the surface, the impurity contents will be decreased less than their solubilities in principle.In the present work, the fundamental research was conducted to discuss the possibility for purification using the liquid phase migration technique. The purification limit was estimated by thermodynamic calculations, and metallic impurities were estimated to be effectively removed except for Fe and Al. The migration behavior of the liquid phase in the synthesized silicon substrate was investigated by unidirectional heating under infrared radiation at 1523-1548 K, and the proceeding of migration was confirmed. The migration velocity was 1.4--2.0xl0-7 mis, and found to be controlled by the liquid phase diffusion.IntroductionPhotovoltaic energy is one of promising energy resources in a sustainable society because of its inexhaustibility and cleanliness. Although the production and installation of solar cells have increased significantly during the last decade, the cost of solar cell installation is still high. To enable the widespread use of photovoltaics and for the photovoltaic electricity price to reach grid parity, a low-cost and abundant feedstock of solar grade silicon (SOG-Si) is essential. Recently, a modified Siemens process and a fluidized bed reactor process were developed to address the cost and energy issues associated with the conventional Siemens process. However, their cost reduction potential is limited because of the large energy consumption needed to convert silicon into gaseous compounds. Purification of silicon through metallurgical routes offers a promising way for producing SOG-Si from metallurgical grade silicon (MG-Si), because it enhances productivity and can also lower the process costs. Although several metallurgical processes such as directional solidification [l ], vacuum refining [2-4] and plasma oxidation [5-7], have been developed, processing times and refining efficiencies still have to be optimized."

Jan 1, 2013

By Liyuan Chai, Bing Peng, Ji Peng, Di Yu

"Electric arc furnace (EAF) stainless steel dust has been classified as a hazardous waste by various government regulatory agencies as it releases heavy metals to environment. The solidification of EAF dust is to stabilize the hazardous components to the amorphous silica-alumina-based clays. The process of solidification is investigated and the softening temperatures of dust and additive clay mixtures are measured for economical thermal treatment. The results indicate that the mixture of dust and local clay with the ratio of 1:1 has the lowest softening temperature 1100 °C and it could pass the toxicity characteristics leaching procedure (TCLP) test for the environmental regulatory limits after thermally treated at softening temperature for 15 min. Major phases of thermal solidification product clinker are CaAl2Si2O8, (Fe, Cr)2O3, (Fe, Mg)(Cr, Al)2O4 and Al6Si2O13.IntroductionThe yield of stainless steels in China arrived to 10 million tons in 2006 and more than 0.2 million tons of stainless steel dust are produced annually. Approximately 1-2 wt.% of scrap charged to an electric arc furnace (EAF) enters the off-gases and then is converted into the dust and reported to the bag-house. The disposal or landfill of the dust becomes a serious environmental problem in China due to the increased production of stainless steels in recent years. The dust contains elements such as chromium (Cr), nickel (Ni), lead (Pb), zinc (Zn), cadmium (Cd) and their solubility in leaching media exceeds the environmental regulatory limits [1]. Even though easily feasible for low-grade MgO, it is not appropriate to stabilize the heavy metals from the heavily contaminated soils after the dust landfill [2]. Several dust treatment technologies have been developed and they can be divided into two types. One is to recover the metals from the dust [3, 4] and another is to stabilize hazardous components present in the dust [5, 6]. Recycling of the dust generated in EAF is a remediation option for cleaner production. Direct recycling of EAF stainless steel dust was developed to recover the metal value from the dust and protect the environment [7], but it was only suitable for the dust with high contents of Ni, Cr and Fe. As for the dust with low valuable metal content, thermal solidification is an appropriate choice for the dust treatment."

Jan 1, 2012