By F. Sanchez, A. Mejias, C. Frias, G. Diaz

"Crude zinc oxides are the major source of secondary zinc and are produced from fuming processes like Waelz kilns. The impurities of crude zinc oxides make difficult their processing in primary zinc refineries due to mainly high chloride tenor. Washing with sodium carbonate is a costly operation and chloride removal efficiency is not good enough, so further purification steps are required. The crude zinc oxides are easily treated using ZINCEX™ technology based on leaching, solvent extraction, and electrowinning. The ZINCEX™ process is commercially available and is designed to be a perfect barrier for metallic impurities and halogens, allowing selective zinc extraction in mixed chloride and sulfate leaching solutions. Other valuable components as lead and silver can be efficiently recovered from the leaching residue using PLINT technology in chloride media. Silver is recovered as silver cement and lead is precipitated as pure lead oxide or carbonate, which can be smelted at low temperature.IntroductionZinc is a fully recyclable metal and at present approximately 70% of the zinc produced worldwide comes from primary zinc while 30% originates from secondary materials. Nowadays, the zinc recycling rate is continuously increasing mainly through galvanized steel scrap processing, and crude zinc oxides are the major source of secondary zinc [1]. Secondary zinc oxides are obtained from fuming processes like W aelz Kiln, Rotary Hearth Furnace or Primus Furnace. Waelz is the dominant technology accounting for 80% of total crude zinc oxides production worldwide. In the Waelz process, steel dust is mixed with solid fuel reductant (coke breeze) and pelletized. It is then fed to the kiln and heated to a reaction temperature of l ,200°C. In such conditions, zinc, lead, and other non-ferrous metals are vaporized into the flue gas together with chlorides and alkaline metals. Mixed oxides are drawn from the kiln with the process gases and separated to produce typical crude zinc oxides [2]."

Jan 1, 2011

By Yongyong Gong, Qijie Zhai, Zhichen Zhang, Qixin Li, Zhishuai Xu

"Microstructure of semisolid slurry of Al-4.5wt.%Cu alloy was investigated with pulse magnetooscillation (PMO) treatment, the results showed that the PMO treatment can refine the crystal structures of Al-4.5wt.%Cu alloy significantly. The discharging frequency of PMO had a great effect on the solidified structure transformation of semisolid slurry of Al-4.5wt. %Cu alloy, and the primary a-Al particles become much finer and rounder with an increase of discharging frequency. However, over a certain discharging frequency, the grains of primary a-Al become coarse.IntroductionOver the last decade, a lot of attentions have been paid on metal rheoforming process [1-4], since it has higher mechanical properties of formed components, strength to weight ratio and age hardenablity. Nevertheless, semi-solid forming is always performed at high solid fractions (40%-60%), so it has the limitation of viscosity, a tends to be difficult to pour semisolid slurry into the hole of the shot sleeve. Therefore, a series of novel semi-solid slurry preparation methods and rheoforming techniques have been invented, such as, semisolid vibration treatment [5], rheocasting [6], pulsed magnetic field process [7], annulus electromagnetic stirring [8], via ultrasonic vibration process [9], equal channel angular extrusion (ECAE) process [l0] and straininduced melt activation (SIMA) process [11].The electromagnetic field is characterized by its effective grain refinement, green, convenient manipulation and without contamination of melt. The mechanisms of dendrite was fragmentation by electromagnetic field have also been largely proposed [12-14]. The broken dendrite arms then undergo a coarsening process to provide the globular structures and obtain much finer and rounder a-Al particles. When compared with other external electromagnetic techniques, Pulse Magneto-Oscillation (PMO) has obtained more fuvors, owing to narrower pulse width and much lower energy consumption. Furthermore, the PMO treatment can reach finer grains with shorter time treatment [16, 17]. This work aims to study the effects of different discharging frequency ofPMO treatment on the microstructure transition of the semisolid slurry of Al-4.5 wt.%Cu alloy."

Jan 1, 2014

By Chris P. Pistorius

Over the past few decades the carbon intensity of ironmaking and steelmaking has been reduced considerably through improved efficiency in blast furnace ironmaking, partial replacement of coke with less carbon-intensive fuels, and increased use of scrap and direct-reduced iron in steelmaking. To evaluate possible further reductions in carbon intensity accurate process information is needed. A preliminary test of the fidelity of publicly reported data as a source of process information is reported here. The sources are industry roundups of electric furnace furnace steelmaking and blast furnace ironmaking (published by the Association for Iron and Steelmaking Technology), and data recorded by the Environmental Protection Agency under the US Greenhouse Gas Reporting Program. From a comparison for an integrated steelmaking plant and an electric furnace furnace plant, it appears that the values from the two data sources are consistent. The comparison does rely on process details such as the quantitative relationship between injected oxygen and carbon emissions in electric furnace steelmaking.

By Alex Luyima, Honglan Shi, Lifeng Zhang, Yongqing Jiang

"Leaching process has been suggested to recover most metals from waste PWBs. In this study, the leaching behavior of most metals present in waste PWBs is evaluated before and thermal treatment. Different leaching acids: hydrochloric acid (HCl), nitric acid (HNO3) and aqua regia are compared. The effects of acid concentration, particle size of sample, leaching time and temperature are examined. Results revealed that most metals are present in small particle size and sequential leaching of PWBs with a combination of HCl acid and aqua regia is capable of dissolving most of the metals content of PWBs. Leaching of thermally treated PWBs produced the highest leaching percentages for similar leaching conditions.IntroductionApproximately 20–50 million tonnes of electronic waste (e-waste) is produced globally per year. Waste Electrical and Electronic Equipment (WEEE) or E-waste is one of the fastest growing waste streams in the world. In developed countries, it equals 1% of total solid waste on an average [1]. The growing stockpile of used and obsolete consumer electronics has been called the “largest toxic waste problem of the 21st century [2]. Printed wiring boards (PWBs) is an essential part of almost all WEEE, and accounts approximately 3% of all WEEE by weight [3]. PWBs are a platform upon which microelectronic components are mounted. PWBs contain metals (~40 wt. %), ceramics (~30 wt. %) and plastics (~30 wt. %) [4]. The metallic part includes; Cu, Pb, Zn, Fe, Cd, Be, Cr, Au, Pt, Pd, Ag, etc. The plastic part of the PWBs is mostly epoxy resins. These plastic resins also contain very toxic halogenated flame retardants (HFRs) [5]."

Jan 1, 2012

By Liang Li

Thermodynamic analysis and experiments were conducted in order to verify the feasibility of preparing crude titanium tetrachloride (TiCl4) via the carbochlorination of low-grade titanium slag in molten salt. Titanium slag, assaying 74.6 wt% TiO2 with high calcium and magnesium oxide impurities, was treated by an optimized carbochlorination process in NaCl molten salt. These impurities in the titanium slag were chloridized simultaneously, and chlorination products FeCl2, MnCl2, MgCl2, CaCl2 and CrCl3 were collected in the furnace slag. XRD and SEM/ EDS analysis of residue shown that SiO2 and Al2O3 in titanium slag were difficult to chlorinate completely. Theoretical calculations and industrial-scale experimental studies reveal the content of TiCl4 in the products was more than 98.8 wt% and thus proved the feasibility of utilizing low-grade titanium slag for TiCl4 preparation by molten salt chlorination technology.

By Min Chen, Lei Xu

Sintering behavior and performance of high alumina refractory based on the ternary subsystem MgAl2O4-CaAl4O7-CaAl12O19 were investigated using ZrO2 as an additive up to 8 wt.% by solid state reaction sintering. It was found that the added ZrO2 could dissolve in the CA6 grains in the form of a solid solution, which enhanced the isotropic growth of CA6 grains and then improved the sintering. As a result, the densification process was improved and areas with enrichment of ZrO2 showed a more compact structure. With further increase of ZrO2 addition, tetragonal ZrO2 were found to locate in the grain boundaries for exceeding the solid solubility limit, which enhanced the thermal shock resistance, indicating that addition of ZrO2 exhibited a positive effect on sintering behavior and performance of this refractory. In addition, it is considered that the optimal amount of ZrO2 addition was about 4% considering the performance together with the cost.

Jan 1, 2015

By Denise Corrêa de Oliveira

Common dry batteries use zinc as the negative electrode. Producers commonly use additives such as mercury to prevent corrosion and to increase the mechanical resistance of the zinc anode. Alkaline batteries also contain it, as an anti-corrosive agent. When mixed with the common municipal solid waste, heavy metals as zinc and mercury pollute soil and ground water supplies, moving to the food-chain and affecting human health. Due to these possible damages, this kind of waste must be properly disposed, or recycled. Thus, even in low amounts (ppm) in batteries, mercury has to be eliminated or, at least, its content should be reduced. This work presents the use of pyromettalurgical processes, to reduce mercury content and recover zinc. The tests involved batteries treatment at temperatures from 300° to 1000°C. Mercury is eliminated up to 650°C, and zinc is evaporated at higher temperature treatment. C

Jan 1, 2001

By Tao Li

The development of DP(Dual Phase) steels and TRIP(Transformation Induced Plasticity) steels has received much attention in recent years due to their high strength and simultaneous good ductility, which provides the potential for weight reduce and resource savings on certain components in automobile or other industries. So a controlled rolling process was simulated in the present study by thermomechanical simulator (Gleeble 1500) for producing DP steels on a kind of low carbon steel containing a small amount of Si and Cr. F+M dual phase microstructures have been obtained during continuous cooling processes of a wide cooling rate range from 10°C /s to 60°C /s. The grain size of the dual phase steel developed can be refined to less than 5 m through the mechanism of deformation induced ferrite (DIF) transformation. The ultrafine ferritic grains are equiaxed with high-angle boundary, and the martensite islands of an average size less than 5m disperse uniformly in the ferrite matrix. The ultrafine martensite islands not only inhibit the growth of ultrafine ferritic grains and improve the bonding of F/M interface, but also increase remarkably the strain hardening rate in the processing of the present Dual-Phase steel. As a result, the tensile strength of ultrafine grained Dual-Phase steel reaches higher than 1000 MPa. The result shows that an ultrafine grained Dual-Phase steel of low carbon and low alloy is promised to exhibit desired F+M microstructure by means of this new TMCP process.

Jan 1, 2006

By Hoda Emami

In this study, a combined pyrometallurgical and hydrometallurgical technique has been designed and used to recover rare earth mixture elements (REE) and cobalt from a NdFeB magnetic waste. while addressing the cost of reagent and process facility. This process can be adjusted to different magnetic wastes regardless of their compositions. Prior to the leaching, the magnet scrap was pretreated by two rounds of roasting (750°C in air) and a mechanical grinding in between, to convert iron metal to ferric oxide. Subsequent leaching was performed using optimized conditions (pH, temperature and retention time) where the extraction ratio of REE to Fe III is the highest. After removing iron content from the leachate (pH ≈ 3), REE was precipitated selectively and purified further. The produced REE concentrate reaches 99% purity with 85% recovery in a single run. The cobalt oxide was isolated from the PLS as a by-product with 99.8% purity.

By Zhang Libo, Li Wei, Peng Jinhui, Guo Shenghui, L. Jing

Partially stabilized zirconia ceramics (PSZ) were prepared by microwave sintering using natural baddeleyite which was obtained by flotation of baddeleyite ore as starting materials. Because of using natural baddeleyite as raw and the process producing no waste, it realized shorter process, energy savmg, environmentally-friendly and non-damage processing. In this work natural baddeleyite stabilized with 3.8wt.% CaO were sintered at 1300°C for 60min in a multi-mode 2.45GHz microwave furnace. Microwave sintering could fast heating and sintering. Besides that, microwave sintering could heat materials wholly, low the sintering temperature, improve the materials properties and save energy. X-ray spectrum displayed the product composed by the tetragonal phase and monoclinic phase that also showed the product was PSZ. Fine and uniform microstructures were observed in the product through scanning electron microscopy. PSZ which was with high density was confirmed by the method of the Archimedes technique.

Jan 1, 2011

By A. Haxhiaj, Mitovica, E. Haxhiaj

"The paper discusses problems encountered during the release and possibility of using the thermal gas quantity Mathematical models are used to calculate the positive thermal effects of the gases and losses of thermal quantity with gases in the melting process of electric furnaces. The paper discusses in details the percentages of CO, CO2, H2S, O2 and the humidity in gases and their impact on the technological process in electrical furnaces in Drenas. The paper also confers the quantity and temperature of gases, the transfer of thermal quantity and dust with gases in the environment. The paper presents the percentage of humidity in the load which is added in electric furnace for melting and its impact on thermal and environmental balance in the technological process of melting in electric furnaces. Key words: Furnace, load, temperature, humidity, gases.IntroductionNickel easily reacts with gases in the atmosphere of the furnace in which the nickel ore is processed. Such reactions can explain challenges in producing high quality nickel. Reductive atmosphere with the surrounding gases composed of sulphurous anhydrite has harmful effects on the production of nickel. This is mainly due to solubility of hydrogen as well as nickel oxide in the melted metal. Nickel reacts with carbon monoxide and forms carbide of nickel and nickel oxide which dissolve in the melted metal. Carbon monoxide also dissolves in the melted metal. The presence of carbon dioxide and water vapor in the atmosphere of the furnace impact the decrease of acidity in reductive atmosphere of the furnace. The carbon dioxide reacts with nickel and forms nickel oxide and carbon monoxide. Water vapor reacts with nickel and forms hydrogen and nickel oxide that have negative impact on the structure of nickel and its alloys. In this paper the analytical and experimental analyses are proposed that lead to minimization of the negative effects of gasses and humidity in the melting process. As the practical example, the electrical furnace in Drenas is analyzed.1. The Load and Its CompositionThe basic function of the rotational furnace is drying and reductive roasting of the ore which directly is loaded into the electrical furnace for melting. It is important to mention that the degree of roasting and pre-reduction of iron-nickel oxides is reached if the roasting process of the load in the rotational furnace is done at the temperature of 900°C to 1000°C, with the reductive atmosphere in the furnace and with minimal amount of oxygen in the processing gas. The optimal process of roasting and pre-reduction of the load in its mass is around 13 wt%. With the removal of the humidity and the sterile pare of the ore, with the positive impacts in utilization of the thermal and electrical energy in the melting process in electrical furnaces."

Jan 1, 2013

By Martin Brueggemann

The Tyrone copper solution extraction and electrowinning plant was the first such facility built by Phelps Dodge Mining Company in 1984. Over the next 20 years, the aqueous flow rate capacity of the plant has been expanded from the original design of 12,000 gallons per minute (gpm) to 34,000 gpm to meet production goals in the face of declining copper grades in the leach solutions. The ability to process higher aqueous flow rates through existing equipment comes at the expense of increased organic loss through entrainment to raffinate. These losses of organic (diluent and extraction reagents) can account for up to 10 percent of the plant?s total operating costs. With the recent dramatic price increase of petroleum-based products, these operating costs due to losses are sure to increase. This paper will discuss recent improvements at the Tyrone SXEW plant that have resulted in a 40 percent reduction of organic losses. These improvements include picket fence modifications, new fence materials, organic recovery systems, and operational practices within the solution extraction process.

Jan 1, 2006

By C. M. F. Vieira

Crushed fired brick waste, known as grog, screened at two different particle size, 840 (20 mesh) and 180 µm (80 mesh), was used in mixtures with clayey body to make typical red ceramics for bricks. The effect of the grog addition up to 20 wt.% on the properties of bricks fired at 700oC was evaluated. The results indicated that both the particle size and the amount of grog addition changed the fired properties of the clayey body. Additions above 5 wt.% of grog, with a coarser particle size, decreased the mechanical strength of both the dry body and the fired ceramic pieces. By contrast, grog with a finer particle size may be used up to 10% wt. without deteriorate the properties and corresponding microstructure of the clayey body.

Jan 1, 2009

By Y. Fukunaka, M. Niinae, E. Kusaka, T. Kuzuya, R. Ishii

"Samarium oxalattr particles was precipitated in oxalic acid aqueous solution from samarium-loaded D2EHPA solution emulsified with a conventional impeller. The calculated fractional precipitation of samarium oxalate was reasonably compared with the value determined by chemical analysis. Morphological variation of oxalate precipitate particles was then examined with H2C2O4 concentration in aqueous solution, Sm(III) and D2EHPA concentrations in organic phase. The needle-like precipitate was identified as Sm2(C2O4)3 10H2O by XRD. Precipitates obtained at higher H2C2O4· or Sm(III) concentration greatly decreased the length of major axis of precipitate, while those at higher D2EHPA concentration increased it. The oxalate was further precipitated under ultrasonic irradiation. However, the morphological variation caused by theses processing variables was not so evident under ultrasonic irradiation as in an impeller or shaking mixer.IntroductionThe materials processing of the rare earth elements must be reviewed from the scope of industrial ecology, since they have the potential applications of magnetic materials as well as secondary battery in developing programs of the electric vehicle. The technological trend to develop the electric vehicle may greatly influence the concept of materials processing, since the global· environmental problem must accommodate with the sustainable development for mankind. The recycle design must be a key issue in the materials science and engineering.Solvent extraction provides a unique separation technology -in this sense. Doyle (1)(2) reported the integrating solvent extraction with processing of advanced ceramic materials, whose chemical composition and microstructure must be precisely controlled. In her paper, the higher productivity inherent to the present process superior to hydrolyzing metal alkoxides was emphasized. Oxalic acid has been used as precipitant for rare earth purification process, since rare earth oxalate has a very small solubility in water and can be easily decomposed to oxide. It is thus suitable for precipitation stripping agent in cationic exchange type extracting system (i.e. D2EHPA, VA-10, PC-88A and so on)."

Jan 1, 2000

By R. Y. Wan

Low grade sulfidic-carbonaceous refractory ore from Newmont Gold Company's Carlin deposit was microbially pretreated. The biological pretreatment process gave partial oxidation of the sulfidic components of the refractory ore but the preg-robbing carbon continued to be active resulting in approximately zero cyanide gold extraction. A 495 ton pilot plant test heap was conducted using acidic thiourea leach following biooxidation. Activated carbon and cation exchange resin adsorption were tested for gold recovery from the thiourea pregnant solution. The results obtained from the test heap were not satisfactory. Gold extraction was low due to slow reaction kinetics which was caused by relatively large particles and very low winter temperatures. Problems existed in the thiourea-test heap and are discussed in this paper. An alternative heap leach process using thiosulfate has been successfUl at the pilot scale for gold extraction following biooxidation pretreatment of refractory sulfidic-carbonaceous ores.

Jan 1, 1995

By G. R. Waters

NMR360 is developing a suite of chloride-based metals extraction processes, with the first commercial operation scheduled for commissioning late in 2018. It is critical, therefore, that with the introduction of any new technology, that the circuits do not suffer from mechanical failures which will compromise the operation. Although chloride leaching is at atmospheric pressure and relatively low temperature, the main challenge is preventing corrosion, since the high proton activity makes even a small amount of acid behaves as though it were concentrated. An additional challenge in concentrated chloride circuits is the potential for solids precipitation. In this context, therefore, correct valve selection is crucial, and NMR360 has partnered with CGIS to ensure that the Severe Service Valves (SSVs) needed will perform over and above the definitions of the Manufacturers Standardization Society (MSS) of the Valve and Fittings Industry. This paper outlines what the minimum requirements are for SSVs in chloride leaching applications, drawing on five decades of industry experience from one of Canada’s leading valve experts.

By Esa J. Peuraniemi

Copper smelting to form blister in one single step has been possible for a long time even from low grade concentrates. In spite of obvious benefits, it has been economically viable only with few special raw materials having high enough Cu/Fe and Cu/S ratio. Outokumpu Blister Flash Smelting is currently applied at three operations, and three others will be commissioned in the near future. With typical chalcopyrite concentrates two main obstacles have prevented wider adaptation of direct blister processing: slag formation and heat generation. Oxygen potential in the reaction shaft must be high in order to produce blister with targeted sulfur content below 1%. When large amount of iron is oxidized, as well as sulfur, copper is inevitably also oxidized into slag. High copper amount in substantial tonnages of slag lead on to costly down stream recovery operations to obtain discardable slag. Almost complete oxidation of sulfur and iron releases a high amount of heat which traditionally has been solved by lowering oxygen enrichment of the blast leading on to oversized off-gas line and acid plant. One challenge in direct blister smelting relates to the attack of aggressive high-copper containing slag against furnace refractory lining. In continuously operated Outokumpu Direct Blister Flash Smelting this is taken care of by preventing vigorous melt movement in the settler. Stable bath conditions and stationary slag against refractory lining enable the formation of a protective autogenous layer between aggressive slag and vulnerable refractory. These direct blister smelting challenges are addressed from equipment and process development point of view. New solutions to overcome the obstacles are presented and discussed.

Jan 1, 2006

By Fjeldstad Karin Jusnes

Two quartz types used in the silicon and ferrosilicon industry were heated to temperatures of 1600 and 1700 °C. The parameters varied were the temperature and the holding time at maximum temperature. The amount of quartz, cristobalite and intermediate amorphous phase were measured using XRD and the internal standard method. Type P showed a much larger ability to transform to cristobalite at lower temperatures than type A. Type P had a larger amount of alkali and alkaline earth impurities. This could have enhanced the transformation to cristobalite. For quartz type A the amount of cristobalite was larger at 1600 °C than 1700 °C. This can also be seen for some of the samples of type P at shorter holding times.

By XING Xiangdong, Zhang Jianliang, MA Jinfang, WANG Zhenyang

The non-equilibrium reflux reaction behavior of phosphorus was studied with synthetic slags formed by using the AR chemical reagents and changing the initial condition of basicity, FeO, MgO and Al2O3. Due to increase of viscosity, the dephosphorization slag with high basicity inhibits the full contact of slag with iron, which leads to the low reaction rate in the early stage. However, since the high basicity improves the activity coefficient of CaO, the dephosphorization rate and phosphorus capacity goes up in late reaction stage. FeO promotes the increase of reaction rate in early dephosphorization stage. But the polarization force of Fe2+ is stronger than Ca2+, which hinders the reaction between phosphate ion and CaO and reduces the stability of PO4 3-. Thus, high content of FeO will adversely impact on dephosphorization reaction. In addition, MgO has a promoting effect to the dephosphorization, whereas Al2O3 has a negative influence.

Jan 1, 2016

By B. Q. Li, Y. Shu, K Lynn

"This paper discusses the effects of magnetic field and internal radiation on the melt flow and solidification morphology during solidification processing of oxide crystals for optoelectronic and remote sensing applications. The numerical solution of the integral differential equation characterizing the internal radiation and the magnetohydrodynamic equations describing the magnetic and transport phenomena is obtained by applying the combined discontinuous and continuous finite element method. The results show that both internal radiation and an externally applied magnetic field can have important effects on the melt flow and solidification behavior during the melt processing of oxide materials.IntroductionOptical single crystals are widely used in optical and electronic devices. These crystals are often grown from high temperature oxide melts under strictly controlled conditions. As in the well-known single crystal growth processes for semiconductor wafers, thermal gradient in the melt is a major contributing fuctor to the oxide melt pool. Unlike the semiconductor single crystal growth processes, however, the oxide melt is semitransparent and internal thermal radiation plays an important role in redistributing the thermal energy in the melt pool. Our recent experience with pilot-scale plant measurements also shows that the oxide melt is electrically conducting, although its electrical conductivity is considered much lower than the liquid metal or semiconductor melt.The fact that the oxide melt is absorbing and emitting in the thermal radiation frequency range makes it difficult to study the thermal energy transport in the melt pool. This is because thermal radiation is governed by a hyperbolic differential equation, which is different from those describing the transport processes in liquids. Also, our understanding of how thermal radiation interacts with other transport mechanisms such as convection and conduction is rather limited at point in time, in particular in high temperature oxide melts for optical single crystal processing."

Jan 1, 2004