By Junwei Han, Wenqing Qin, Dawei Wang, Fen Jiao, Wei Liu

The removal of iron impurity from zinc calcine was studied by magnetization roasting and magnetic separation. The effects of roasting temperature, magnetic intensity, ore grinding, and leaching pretreatment on iron grade and recovery were investigated. The results indicated that iron recovery increased with the increase of roasting temperature or magnetic intensity, while iron grade was always less than 22%, depending on the fact that the magnetite were not liberated completely. The good liberation was difficult to be achieved by ore grinding but was easier by acid leaching, since the magnetite grains were very fine. After the leaching pretreatment, the recovery of 76.31% with iron grade of 53.24% was obtained by one roughing and cleaning. The SEM/EDS analysis showed that a part of sphalerite, zinc ferrite and other gangues were mixed into the iron concentrate, while some of fine magnetite was reported to the tailing.

Jan 1, 2016

By Shaohua Ju, Feng Jiang, Chuanhua Li, Jinhui Peng, Libo Zhang

A T-junction microchannel is proposed to overcome the existing problems in conventional solvent extraction of indium from zinc hydrometallurgical process. Experiments were performed to separate In3+, Fe3+ and Zn2+ from sulfate solutions using Di-(2-ethylhexyl)phosphoric acid (D2EHPA) as the extractant. The effect of parameters such as pH, microchannel size and contact time on the extraction behavior of In3+, Fe3+ and Zn2+ was investigated. At contact time of 2.52 s and initial solution pH of 0.48, the extraction efficiency of In3+, Fe3+ and Zn2+ was 99.13%, 8.31% and 2.45%, respectively and separation factor of In3+/Fe3+ and In3+/Zn2+ were almost 1229.54 and 4864.98, respectively. Then, the loaded organic phase was stripped in T-junction microchannel. At contact time of 33.6 s, 99.64% of stripping efficiency of In3+ and stripping equilibrium were reached, while concentration of Fe3+ and Zn2+ was lower than 0.01 g/L with good separation of In3+ from Fe3+ and Zn2+.

Jan 1, 2016

By R. David Prenganan

RSR has developed a new environmentally superior process to recover lead as high purity electn:1o'i0!1 cathode from battery scrap. The process involves crushing the batteries, separating the lead bearing material from the plastic, ebonite and separators, and separating the active material (paste) from the metallic lead fraction. The paste is desulfurized using Na2C03 to convert the PbS04 to PbC03 and produce a sodium sulfate solution. The paste is further treated to decompose the PbO2 and PbC03 to Pbo. The PbO from the treated paste is easily leached, using H2SiF6 and electrown from solution using Pbo2?coated graphite anodes. The electrown lead has a purity exceeding 99.99%. RSR is in the final design stages of a plant to produce 36,000 tons per year of electrcwon cathode from battery paste in a new plant adjacent to the present Indianapolis refinery. This paper describes the work of a pilot facility operated in the early 1980's. The paper describes the patented process in detail and compares the newly designed environmentally clean electrolytic plant to present recycling plants.

Jan 1, 1990

By Hojat Naderi

In this research assisted leaching of chalcopyrite using sodium peroxodisulfate was studied. Electrochemical techniques such as Tafel analysis and electrochemical impedance spectroscopy (EIS) were used to investigate the surface reactions of a chalcopyrite electrode in the presence and absence of Na2S2O8. According to the results, addition of sodium peroxodisulfate increases the current exchange of the corrosion process and prevents the formation of a passive layer on the surface of the electrode. EIS tests show the trans-passive dissolution of the passive layer on the chalcopyrite electrode in presence of Na2S2O8. Equivalent electrochemical circuits were modeled for Na2S2O8-free and -containing solutions and the model parameters were compared to determine the effect of S2O8 2− on chalcopyrite dissolution. Copper dissolution from pure chalcopyrite mineral and chalcopyrite concentrate was carried out using 15 g/L sulfuric acid solution with and without Na2S2O8. Simultaneous presence of 10 g/L ferric ion and 40 g/L peroxodisulfate salt results in about 40 and 18% of Cu extraction from chalcopyrite concentrate and pure chalcopyrite mineral, after 96 h, respectively.

By William Petruk

The concentrator of the Iron Ore Company of Canada consists of spiral circuits, a cone plant and a magnetics plant with regrind. The proportions of liberated and unliberated grains of iron oxides at each point throughout the concentrator were measured by image analysis, and recoveries were calculated for each particle type by the MATBAL materials balancing program. The results show that spirals and cones recover more than 92% of the liberated iron oxide grains in the size range of 848 to 150 um,, but the recovery drops off rapidly for finer grained particles. The tailings from the spirals and cones are reground and low intensity magnetic separators are used to recover liberated magnetite in the -37.5 um size range. The concentrator does not have a unit that efficiently recovers iron oxide grains in the size range of 150 to 37.5 um Consequently about 25% of the iron oxides in the ore are lost to tailings as liberated. grains in the size range of 150 to 37.5 um

Jan 1, 1989

By R. G. Reddy

Viscosities of alkaline metal oxide-silicate melts were estimated using our previously developed mathematical model. The structural based model considers depolymerization effects and related breakdown of the silicate network structure, on the addition of metal oxides to the melt. The developed expression: n =4.9x10 9 NO 0 T ½ exp(E/RT) poise was used to calculate the viscosities of various binary silicate systems such as, CaO-SiO,, MgO-SiO, and MnO-SiO,, as a function of temperature and composition. Excellent agreement was obtained between the calculated and experimentally determined viscosities.

Jan 1, 1991

By Rak-lun Choi

Plasma-induced damage of InGaN/GaN multiple quantum well (MQW) light-emitting diodes (LEDs) has been studied in terms of forward turn-on and reverse breakdown voltages, together with etch rate and surface morphology. The physical degradation of sidewall along with rough surface morphology of n-GaN caused by increased ion scattering induced the deterioration of the forward and reverse voltages. It was found that the turn-on voltage is sensitive to the surface roughness of the etched n-GaN and the breakdown voltage is strongly affected by the sidewall contamination. Annealing under nitrogen after the mesa etching improved the electrical properties of the InGaN/GaN MQW LEDs. Efficient blue light-emitting diodes (LEDs) were fabricated using InGaN/GaN triangular MQWs. The LEDs with triangular QWs showed a lower operation voltage and 2.4 times higher light output power than those with the rectangular MQW LEDs at 20 mA and 20 °C. The intensity of electroluminescence (EL) at 20 mA was almost independent of ambient temperature in the triangular QW LED, but decreased substantially in the rectangular one.

Jan 1, 2003

By Jana Dobrovska

Solidification and cooling of a continuously cast slab and simultaneous heating of a mould is a very complicated problem of transient heat and mass transfer. Nowadays, the solving of such a problem is impossible without numerical models of the temperature field not only of the slab itself, while it is being processed through the whole concasting machine (Caster), but of the mould as well. Two original numerical models have been developed and used in the investigation of a continuously cast steel slab. The first (one of two) 3D model of the temperature field of a concasting is capable of simulating the temperature field of a caster. Experimental research and data acquisition have to be conducted simultaneously with the numerical computation-not only to confront it with the actual numerical model, but also to make it more accurate throughout the process. After computation, it is possible to obtain the temperatures al each node of the network, and at each time of the process. The utilization of the numerical model of solidification and cooling of a concasting plays an indispensable role in practice. The potential change of technology-on the basis of computation-is constantly guided by the effort to optimize, i.e. to maximize the quality of the process. The user can therefore choose any appropriate longitudinal or cross-section of a slab and display or print the temperature field in a 3D or 20 graph whenever necessary. The second numerical model of dendritic segregation of elements assesses critical points of slabs from the viewpoint of their increased susceptibility to crack and fissure. In order to apply this model, it is necessary to analyze the heterogeneity of samples of the constituent elements (Mn, Si and others) and impurities (P, S and others) in characteristic places of the solidifying slab. The numerical model, based on measurement results obtained by an electron micro-probe, generates distribution curves showing the dendritic segregation of the analyzed element, together with the distribution coefficients of the elements between the liquid and solid states. The combination of both models enables the prediction of cracks and fissures in critical points of the continuously cast carbon-steel slab. Both models had been applied in the industrial investigation of a cast low-carbon-steel slab.

Jan 1, 2003

By Jan Dabrovska

Solidification and cooling of a continuously cast slab and simultaneous heating of a mould is a very complicated problem of transient heat and mass transfer. Nowadays, the solving of such a problem is impossible without numerical models of the temperature field not only of the slab itself, while it is being processed through the whole concasting machine (Caster), but of the mould as well. Two original numerical models have been developed and used in the investigation of a continuously cast steel slab. The first (one of two) 3D model of the temperature field of a concasting is capable of simulating the temperature field of a caster. Experimental research and data acquisition have to be conducted simultaneously with the numerical computation-not only to confront it with the actual numerical model, but also to make it more accurate throughout the process. After computation, it is possible to obtain the temperatures at each node of the network, and at each time of the process. The utilization of the numerical model of solidification and cooling of a concasting plays an indispensable role in practice. The potential change of technology-on the basis of computation-is constantly guided by the effort to optimize, i.e. to maximize the quality of the process. The user can therefore choose any appropriate longitudinal or cross-section of a slab and display or print the temperature field in a 3D or 2D graph whenever necessary. The second numerical model of dendritic segregation of elements assesses critical points of slabs from the viewpoint of their increased susceptibility to crack and fissure. In order to apply this model, it is necessary to analyze the heterogeneity of samples of the constituent elements (Mu, Si and others) and impurities (P, S and others) in characteristic places of the solidifying slab. The numerical model, based on measurement results obtained by an electron micro-probe, generates distribution curves showing the dendritic segregation of the analyzed element, together with the distribution coefficients of the elements between the liquid and solid states. The combination of both models enables the prediction of cracks and fissures in critical points of the continuously cast carbon-steel slab. Both models had been applied in the industrial investigation of a cast low-carbon-steel slab.

Jan 1, 2003

By K. Murayama, M. Kawakami, T. Takenaka, S. Yokoyama

"Cokes play an important role of spacer in blast furnace. However, they degenerate during Boudouard reaction. Blast furnace cokes are reacted with pure C02 at I 072 to 1673 K. Reaction rate was obtained by the weight change of spherical specimen. The specimen after reaction was examined by microscopic observation. The reaction rate increased with temperature and was expressed by two Arrhenius type lines. The activation energy was 126 KJ/mol at higher temperature than 13 73 K and 202 KJ/mol at lower temperature range. At the higher temperature range, the reaction proceeded from the surface leaving unreacted core, whereas homogeneously whole inside at lower temperature. The porosity increased from the center to surface at higher temperature, whereas it was almost constant at lower temperature.IntroductionThe cokes have the function of fuel, reductant and spacer to keep gas and liquid flow in the blast furnace. Thus, the reaction mechanism of coke with several gas and the strength after the reaction should be important factor to control the blast furnace operation. The reaction mechanism of coke with C02 has been studied extensively. The rate equations were derived by Gadsby[ I], Ergun[2] and Turkdogan and Vinters[3]. They were compared and discussed by Kobayashi and Omori [ 4]. Effect of crystallization degree on the reaction rate was examined by Kashiwaya and Ishii[5]. Catalytic enhancement effect of ash componets have been clarified by Kashiwaya et. al. [6]. Although degradation of coke in blast furnace has been examined recently[7], however, the degradation of coke after the reaction with C02 has not been well clarified yet. In the present work, the metallurgical coke specimen was heated in N2 and C02 and the reaction mechanism and degradation behavior after the reaction was investigated."

Jan 1, 2000

By José D. T. Capocchi

Viscosity of liquid lead, tin, and Pb-Sn alloys has been measured by the rotational viscometer method in the temperature range from 50 K above their respective liquidus temperature to 823 K. The results are accurate to within ±1.0 %. The variation of viscosity with temperature followed the Arrhenius-type equation µ = µo.exp(Q/RT). The composition dependence of the isothermal viscosity and the activation energy for viscous flow have not shown anomalous changes at the eutectic composition of the Pb-Sn system.

Jan 1, 2000

By G. Diáz

A basic technology coping with a wide range of secondary zinc sources has been developed. The process combines an electrowinning stage, a solvent-extraction unit and a leaching procedure. The acidity generated in zinc electrowinning, transferred by the organic solvent to the aqueous raffinate, is reused to leach the zinc secondary materials. The basic process recovering zinc is described in detail. The route recovering other valuable metals such as copper, cadmium and lead associated with zinc is also described. This non-ferrous metals recovery route is advisable for either ecological and/or economical reasons. Main results of an experimental program aiming at the demonstration of the suitability of the process for several feed materials are summarized. Waelz oxides, galvanizing ashes and EAFD coming from different sources were tested in laboratory and continuous pilot plant campaigns. High zinc recovery, low reagents and utilities consumption, and effluents meeting environmental regulation were confirmed. The paper also includes the main results of a feasibility study of an industrial "base case". A mixed raw material and Spanish EAFD and 20,000 ta of zinc ingots production were chosen. The SGH zinc recovery from secondary raw material by means of the clean, safe and profitable Modified Zincex Process has been demonstrated. This reliable technology is ready for industrial application.

Jan 1, 1995

By Jonkion M. Font, Ramana G. Reddy

A thermodynamic model for a priori predictions of arsenic and antimony impurity capacity in Ni-Cu mattes and slags was developed based on the Reddy-Blander (RB) capacity model. The As and Sb capacities were calculated a-priori considering the RB capacity model in Ni-Cu mattes and FeO-FeO1.5-MgO-CuO0.5-NiO-SiO2 slag at 1573 K and 0.1 to 1 atm partial pressure of SO2. The results showed an excellent agreement between the model calculated and experimental data of arsenic and antimony capacities between the mattes and slag. The impurity capacity model developed here, can be extended for prediction of impurity capacities in multi-component base metal slags and base metal mattes. Such a priori predictions of impurity capacities can lead to develop or improve the efficiency of impurity removal from the base metal smelting, converting and refining processes.

Jan 1, 2014

By Rak-Jun Choi

Plasma-induced damage of InGaN/GaN multiple quantum well (MQW) light-emitting diodes (LEDs) has been studied in terms of forward turn-on and reverse breakdown voltages, together with etch rate and surface morphology. The physical degradation of sidewall along with rough surface morphology of n-GaN caused by increased ion scattering induced the deterioration of the forward and reverse voltages. It was found that the turn-on voltage is sensitive to the surface roughness of the etched n-GaN and the breakdown voltage is strongly affected by the sidewall contamination. Annealing under nitrogen after the mesa etching improved the electrical properties of the InGaN/GaN MQW LEOs. Efficient blue light-emitting diodes (LEOs) were fabricated using InGaN/GaN triangular MQWs. The LEOs with triangular QWs showed a lower operation voltage and 2.4 times higher light output power than those with the rectangular MQW LEOs at 20 rnA and 20 "C. The intensity of electroluminescence (EL) at 20 mA was almost independent of ambient temperature in the triangular QW LEO, but decreased substantially in the rectangular one.

Jan 1, 2003

By B. C. Jena

Activities of carbon, cobalt and nickel were evaluated in the ternary systems iron-carbon-cobalt and iron-carbon-nickel for the temperature range 1300-1600°C for cobalt and 1300-1700°C for nickel. The carbon activities were determined from the knowledge of activities (1) in the binary system iron-carbon, (2) in the dilute ternary systems and (3) from the knowledge of carbon saturation data. The activities were mathematically expressed with the Taylor series expansion of Wagner's interaction parameter formalism modified to suit concentrated solutions. The cobalt and nickel activities were determined from the knowledge of carbon activities by applying the Gibbs-Schuhmann integration and from cobalt and nickel activities in the binary systems iron-cobalt and iron-nickel. Partial molar enthalpies of mixing were determined based on the temperature behaviour of the activity coefficients.

Jan 1, 1992

By L. M. Abrantes, A. P. Paiva

"A brief review of some innovative methods for the direct recovery of metals from loaded organic phases is presented; emphasis is given to electroreductive stripping and cementation, which are described and illustrated by examples: of current research. The recovery of silver using a two-phase electrolysis - by direct application of an electrical potential to a mixture of a metal loaded organic phase· containing Cyanex 471X, obtained by solvent extraction, and a stabilized sodium thiosulfate solution - is more extensively discussed. The overall efficiencies are analyzed and compared with data obtained by conventional stripping procedures. Some preliminary results achieved for the recovery of the precious metal using galvanic stripping, applied directly to similar organic solutions and involving zinc and iron powders as reducing agents, are also evaluated.Introductory ReviewThe application of hydrometallurgical methods to the recovery of metal values from ores and concentrates has been receiving a growing interest, either from researchers or from the mining industry [1].For the concentration / purification of the relatively low concentrated metallic solutions resulting from the leaching of those raw materials, solvent extraction (SX) is a well established technique [2]; the loaded organic solvent is then conventionally contacted with a suitable aqueous solution, the metal in its final form being usually recovered from this solution by electrowinning.As an efficient and / or selective stripping is sometimes difficult to achieve, depending on the specific characteristics of the system under consideration, some alternative procedures have been analyzed in order to overcome this problem. One of the chosen routes, mainly developed by Hirai and Komasawa, is to promote the reduction of the desired metal species in the organic phase, in such a way that the stripping stage becomes feasible; for the selective stripping of vanadium from a solvent containing a mixture of vanadium and molybdenum, the authors successfully used reductive [3], electro-reductive [4,5] and photo-reductive [6] techniques. The two latter methodologies have also been applied to the recovery of europium from a solvent containing europium, samarium and gadolinium [7,8].However, further processing is necessary to recover the metal in its solid state; therefore, methods causing the direct reduction of the metal species in the organic phase to their fmal metallic form would be of interest, as an intermediate step would be avoided"

Jan 1, 1997

By Zeng Zheng, Liu Chen, Yu Xing-Fu, Tian Su-Gui, Zhang Chao

"Single crystal nickel-base superalloy is prepared by using the various withdrawing rates. By measuring creep properties and microstructure observation, the influence of the element segregation on creep properties of the superalloys is investigated. Results show that the dendrite spacing and the segregation extent of the elements decrease with the enhancing withdrawing rate. The superalloy with smaller dendrite spacing has lower segregation of the elements and better creep resistance. The dislocations climbing over the rafted y’ phase is thought to be the deformation mechanism of the alloy during steady state creep. In the later stage of creep, the fact that some dislocations shear into the rafted y’ phase may twist the rafted y’ phase. As the creep goes on, the initiation and propagation of the cracks occur up to occurring creep fracture, which is thought to be the fracture mechanism of the superalloy during creep.1. IntroductionSingle crystal nickel-based superalloys consist of high volume fraction of ?? strengthening phase and ? matrix, and possess the excellent high-temperature mechanical and creep properties, therefore, they have become the main material to make the blades of the advanced aeroengines[1-3]. Some literatures report that the temperature-bearing and creep-resistance properties of the single crystal nickel-based superalloys can be remarkably improved as the increases content of the refractory elements, such as W and Re[4-6]."

Jan 1, 2012

By Jianxin Zhang

A process, in which arsenic in the residue is transformed directly into scorodite and copper dissolves into the solution simultaneously, was studied. The process was carried out in acidic ferrous sulfate solution under oxygen pressure. The optimum conditions of the process were determined as follows: the initial H2SO4 concentration of 10 g/L; liquid/solid ratio of 10; Fe/As molar ratio in the feedstock of 1; the addition of calcium lignosulphonate was 1% of sludge; oxygen pressure, temperature and reaction time were 1.5 MPa, 150 °C and 6 h, respectively. Under these conditions, arsenic transformed to crystalline scorodite in size of 5–10 μm, and the transformation efficiency reached 97.60%; meanwhile, the copper was leached with a high efficiency of 93.34%. The stability of the leaching residue was evaluated by TCLP testing, and the results indicated the concentration of arsenic in the leaching solution was extremely low as 0.04 mg/L and met the standard of safe stockpile.

By Pekka Taskinen

The converter-less nickel matte smelting technology (DON) adopted more than 20 years ago in Boliden Harjavalta smelter has been since that applied successfully to the processing of large number of nickel sulphide concentrates of various Ni-to-Cu ratios and MgO contents. The operational point of the technology is far from the conventional primary nickel smelting in the smelting-converting route. Therefore, a careful scouting of distribution equilibria of the base and trace elements in the smelting conditions of DON process has been conducted, in order to obtain quantitative information about the equilibria and thermodynamic properties of the nickel mattes at low iron concentrations, less than 10 wt% [Fe] in matte. The series of investigations has included novel experimental and analytical techniques for increasing the reliability and sensitivity of the phase equilibria as well as the element distribution observations carried out in typical high-grade nickel matte smelting conditions.

By Tuula Mäkinen

One of the latest applications of the Outokumpu Flash Smelting Technology is the direct smelting ,of nickel concentrates to metallised low-iron nickel mattes. Compared to the conventional nickel smelting, the new DON process needs a lower number of smelting vessels resulting in considerable economic and environmental benefits. Fundamentals of smelting nickel concentrates in one stage to low-iron mattes are presented. Properties of nickel. smelting slags with an emphasis of the slag fluidity at high MgO-levels are also discussed. Conditions prevailing in DON mattes at high oxidation degrees are presented as well as their influence on the behaviour of such mattes in the settler and on tapping the furnace. Distributions of elements in the direct smelting are presented and compared with the conventional process. A further comparison is made with pilot-plant data and the industrial scale.

Jan 1, 1998