By E. S. Bumps, W. F. Craig, M. Baeyertz

Metallurgists have looked at fractures macroscopically for many years and have evolved a vocabulary in which such words as "cleavage," "brittle," "shear," "ductile," "granular," "fibrous," and "silky" are used to describe the appearance of the fractured surface; but the meaning of these words in terms of metal structure is not well established. Observations of the structural meaning of "brittle" and "ductile" fractures in plate steels have been made, notably, by Kramer and coworkers1 and by Tipper.2 Grossman3 has studied the fracture of tempered martensite and combinations of ferrite and martensite. Notwithstanding these and other less concerted attacks on the problem, present understanding of fracture rests more on assumptions and logic than on experiment. It is the purpose of this paper to add a little to the growing fund of experimental observations of the nature of fractures in steel. The particular fractures to be described were obtained in conventional impact testing of an ordinary structural steel shape. In impact tests of the Charpy type, the specimens fail in a characteristic manner that depends on the steel and the temperature of testing. With ordinary structural and many other steel products, an appropriate range of testing temperature will cause a considerable change in the energy absorbed before fracture. This change is known as the energy transition and is accompanied, more or less closely, by alteration in the appearance of the fracture. At testing temperatures below the transition, the terms "brittle," "cleavage," or "granular" are used to describe the fracture; above it, "ductile" or "shear" are often used. Within the transition, the fracture changes from "brittle" to "ductile" by a progression in appearance, wherein the "brittle" portion of the fracture becomes restricted to a smaller and smaller central area of the fracture, as the testing temperature is raised and the "ductile" type of fracture is approached. All this is well known to metallurgists. The specimens under consideration are of the conventional V-notch Charpy type. They were taken from a structural steel shape of the following analysis: C Mn P S Si 0.17 0.46 0.009 0.029 0.03 Both longitudinal and transverse specimens were tested and examined. Fig 1 shows the energy values plotted against testing temperatures in the usual way. The curves for both longitudinal and transverse specimens show an energy transition, although the maximum energy absorbed at testing temperatures above the transition is greater in the case of the longitudinal specimens. Fig 2 illustrates the changes in the macroscopic appearance of the fractures that are associated with the energy transitions shown in Fig 1. Macrographs of the fractured surfaces of the specimens have been identified with the fracture ratings at intervals on each fracture curve. The numerical fracture rating on the ordinate of Fig 2 indicates the percentage of the area of each fracture that was considered to be "brittle" on macroscopic observation. Such rating of the fracture type in impact tests is now customary in many laboratories. Hereafter the specimens will be identified by reference to Fig 2 as 90 pct "brittle," 80 pct "brittle," and so on, in accordance with this macroscopic evaluation of the appearance of the fractured surface. The discussion of the fractures is divided into three parts. The first two are concerned with the mode of fracture and its relation to general structural features. As the same metal-lographic features occur in both longi-

Jan 1, 1950

By N. Brown, R. Kossowsky

Plain carbon steels with 0.48 and 0.95 pct C were quenched and tempered at 705°C to produce carbide dispersions with spacings on the order of 1 p. The morphology of the structure consisted of a carbide-dislocation network. The strengthening due to the dispersion was found to vary linearly with M-½ where M is the mean free-ferrite path determined by the entire network. No preyield microstrain preceded the upper yield point. After prestraining, the lowest stress at which dislocation movement could be detected was 104 psi; this frictional stress was independent of the dispersion and prestrains up to 6.5 pct. The Cottrell-Petch equation for grain-size strengthening was used to discuss the dispersion strengthening in this investigation. The results support an impurity mechanism for the upper yield point rather than one based on the Johns ton- Gilman theory. IT was pointed out by Gensamerl that the mean free path in the matrix is the important variable which controls the degree of dispersion strengthening. Gensamer's data on steels showed a linear relationship between the yield point and the logarithm of the mean free-ferrite path. The first theory was by Orowan,2 who suggested the mechanism of dislocations bowing between particles, with the resulting relationship that where a is the yield point, P is the distance between particles, and G is the shear modulus. The Orowan equation applies to that range of dispersion where P is large compared to the particle size and the particles are not coherent, so that the matrix is essentially free of internal stresses. As was pointed out by Orowan, there are different degrees of dispersion which, in turn, will influence the strength-controlling mechanism. However, in this investigation, we wish to confine ourselves to the region of coarse dispersion, where the Orowan mechanism should, intuitively, be applicable. It was soon evident that the data, which existed at about the time that the Orowan theory was proposed, did not agree with the Orowan equation in that the actual strengthening was always greater than the theoretical predictions. Thus, Fisher, Hart, and pry3 modified the Orowan theory by suggesting that the Orowan process took place in the microstrain region preceding macroscopic yielding and the subsequent, rapid work hardening in the form of residual dislocation loops around the particles largely determined the observed macroscopic yield point. The F-H-P theory stated that the increment of strengthening due to the work-hardening mechanism was proportional to f3/2 where f is the volume fraction of the precipitate. F-H-P used data by Shaw, Shepard, Starr, and Dorn4 on A1 3-5 pct Cu to support their theory. Roberts, Carruthers, and Averbach5 were the first to make a microstrain study of dispersion strengthening, and they found that for steel the Gensamer relationship was obeyed. Hayman and Nutting6 suggested that in the case of tempered steel 1) the ferrite grain boundary was the primary obstacle and 2) the carbide particles simply formed part of the grain boundary obstacles. They found that the strength varied as G"" where G is the ferrite grain size. Turkalo and LOW' determined the structure of quenched and tempered plain carbon steel using a replica technique; they concluded that the carbide particles did not necessarily lie in the ferrite grain boundaries. When they defined the mean free-ferrite path as being determined by both particles and the ferrite path boundaries, their data obeyed the Gensamer relationship. Meiklejohn and skoda8 showed that the strengthening from iron particles in mercury was a function of the particle size and the distance between particles. Dew-Hughes9 explained the Meiklejohn and Skoda results by the following theory: 1) grown-in dislocations which surrounded the particles were produced by the thermal stresses during the time the material was cooled to the testing temperature, and 2) the observed strengthening was associated with the cutting of the grown-in dislocations by the glide dislocations. Ansell and Lenel10 proposed a theory in which the glide dislocations pile-up or surround the particle until the number of dislocations in the pile-up is sufficient to yield or fracture the particle. The resulting theory says that the yield point varies as p-1/2, where P is the distance between particles. The Ansell-Lenel theory is almost identical to the

Jan 1, 1965

By Donald C. Barton

The theory of gravitation is based on Newton's law that any two bodies exert a mutual attraction which is proportional to the product of their masses and inversely proportional to the square of the distance between them; i. e., A = KMRm2 (1) where K is a constant, M and m are the respective masses of the two bodies, and R the distance between them. In the earth's gravitational system, the earth is one of the bodies; the other may be any body within or without the earth. In theoretical discussions and calculations,in regard to gravity, that other body usually is taken as a unit of mass: in the C:. C:. S. system, a body of one gram in mass. Gravity and Level Surfaces Gravity is defined in geophysics as the force of attraction exerted by the earth, towards itself, on a body of unit mass. The intensity of gravity is usually expressed in dynes of force or in centimeters of acceleration In geophysical work in America, most commonly it is expressed in dynes (per gram) with the "per gram" understood and not directly expressed. In geophysical work in Europe, most commonly it is expressed in centimeters per second per second (cm. /sec.2) and less commonly lrierely as centimeter-gram-second units (c. g. s). At sea level, the intensity of gravity amounts very nearly to 980 dynes. The vertical is the direction along which the attraction of gravity is exerted at any point. In most cases, it is very nearly, but not quite, perpendicular to the earth's surface. The path that would be taken by a body falling freely through space toward the earth is vertical at each point and may be spoken of also as ('the vertical," or as the line of the vertical, or as a line of force of gravity. At the earth's surface it comrrlonly is very nearly, but not quite, a straight line.

Jan 1, 1929

By E. H. Dix

All commercial aluminum contains small percentages of copper, iron, and silicon as unavoidable impurities. The purest metal obtainable commercially, special grade high purity ingot, contains a maximum of 0.50 per cent. impurities of which the usual minimum amount of copper is 0.01 per cent.; silicon, 0.12 per cent.; and iron, 0.20 per cent. This grade is too costly for most purposes. The two standard grades, Nos. 1 and 2, containing a minimum of 99.0 and 98.0 per cent. aluminum, respectively, are more generally used. Other grades of secondary aluminum often contain as high as 3 or 4 per cent. of impurities, which include 1 per cent., or more, of zinc. Specifications for high-grade aluminum-casting alloys generally allow a maximum of 1.7 per cent. for total impurities. The S. A. E. Specification No. 33, which is intended to cover alloys made from secondary aluminum ingot, gives the iron maximum as 1.5 per cent. and the maximum for silicon (including manganese and tin) as 0.75 per cent. The effect of even relatively small amounts of impurities on the physical properties of ingot aluminum is shown by the following cornparison of two lots of aluminum, which may be taken as representative of special grade and grade No. 2 ingot, respectively. AnalysEs Special Grade, Gbade No. 2, Per Cent. PeR CBnt. Copper................................. 0.01 0.32 Silicon................................. 0.12 0.32 Iron................................... 0.42 0.82 Aluminum.............................. 99.45 98.54

Jan 1, 1923

By S. Brunauer

The hydration of portland cement is treated as a chemical reaction and the changes in matter, in energy and the rate of change of the process are discussed, Portland cement is a mixture of four major and at least as many important minor constituents. In the hydration process, the four major compounds (trical-cium silicate, dicalcium silicate, tricalcium alumi-nate and tetracalcium aluminoferrite), plus gypsum and water form five or six new compounds. In spite o the great complexity of the reaction, considerable progress has been made in its understanding, primarily with the help of such research tools as X-ray diffraction and electron microscopy. The rate of the reaction can be followed by direct and indirect methods of measurements. The effects o composition, particle size (or specific surface), temperature and water-cement ratio on the rates of hydration are discussed. The hydration of portland cement is a chemical reaction accompanied by such highly important physical phenomena as heat evolution, setting and hardening. It is a vast and complex subject, on which hundreds of papers have been published. At the time of the writing of this paper, in October 1962, a two-volume book, which alone contains dozens of papers pertaining to cement hydration appeared in print.' The present paper deals with a few aspects of this vast subject, and the selection was not easy. The work reported here deals with some of the most recent investigations in the field. In any chemical reaction, the physical chemist is primarily interested in three things: changes in matter, changes in energy and the rate of change of the process or the speed of the reaction. This is true also of the chemical reaction between portland cement and water, and all three aspects of the reaction will be discussed. These three aspects are of vital interest to the engineer as well. Portland cement is not a cementing material — the hydration products, the new materials which form in the reaction, have the cementing action. The energy changes manifest themselves in a considerable evolution of heat, which may be useful or harmful. It is useful, for example, in winter concreting, but in very large concrete structures like dams, a large evolution of heat, which cannot be easily dissipated, may produce distress in the structure. Primarily for such a purpose was the Type IV or low heat portland cement developed. The speed of the chemical reaction is important because it determines the time of setting and hardening. The initial reaction must be slow enough to permit placing of the concrete before setting occurs. On the other hand, after the placing of concrete it is often highly desirable to obtain as rapid chemical reaction as possible. For this purpose the Type 111 or high early strength portland cement was developed. CHANGES IN MATTER Portland Cement: In a basic investigation, before one begins to study a reaction, one either knows the quantities and compositions of the starting materials, the reactants, or one determines them. This is obvious; the chemist expresses the changes in matter that occur in a reaction by a chemical equation, which has the quantities and compositions of the reactants on the left side of the equation and the quantities and compositions of the reaction products on the right side. The first question is then what to put on the left side of the equation in the reaction between portland cement and water? It is not very easy to answer this question. Portland cement is not a single chemical compound but a mixture of many compounds. Four of these are considered the major compounds, and at least four of the minor compounds also play important roles in the hydration reaction. In order to avoid complicating matters, the present discussion will be restricted primarily to the four major compounds, which constitute usually more than 90% of a portland cement. The relative amounts of these compounds vary from cement to cement. Actually not only the amounts but the compositions of these constituents also vary to some extent, but the variation in composition of the individual components will be neglected for simplicity.

Jan 1, 1963

By Milton E. Wadsworth, R. Ted Wimber

Cobalt sulfate solutions containing ammonium acetate and chloroplatinic acid were reduced by hydrogen in a pyrex-glass lined autoclave in the temperature range of 170o to 232°C and hydrogen partial pressure range of 115 to 830 psia. The reduction rate was directly proportional to the hydrogen partial pressure and surface area of the pyrex glass and was independent of the quantity of chloroplatinic acid added initially. Experiments involving the variation of the relative concentration of ammonium acetate indicated that the reducible cobalt complex was probably the diacetate complex of cobalt, Co(AC)4H20, or a new mononcetate complex Co Ac, which was in solubility equilibrium with a pink precipitate of CO(AC)-4HzO. THE reaction in which a metal is dissolved by an acid to produce gaseous hydrogen and a salt solution was discovered early in the history of chemistry. In 1859 Beketoff found experimentally that this reaction could be reversed; i.e., a salt solution could be reduced by gaseous hydrogen to produce a metal and an acid. A review of work done on this phenomenon since that time may be found elsewhere., The hydrogen reduction of a cobalt salt solution is facilitated by complexing the cobalt ion. An ammonia complex of cobalt has been reduced commercially in the recovery of cobalt metal. A new reducible complex of cobalt was discovered5 when it was found that a co-baltous sulfate solution containing ammonium acetate could be reduced by hydrogen at temperatures in the region of 200°C. When a cobalt sulfate-ammonium acetate solution was heated to a temperature below its normal boiling point, a violet color became apparent, indicating complex formation. The nature of this complex was investigated5 by the addition of NH4Ac to a CoSO4 solution maintained at 85o. During the first additions of NH, Ac, the pH of the solution remained fairly constant at about 5.85. However, as the ratio of NH,Ac to CoSO, approached two, the pH rose and then leveled off at about 6.05. The absorption spectra of a Co(Ac), solution and a CoSO,, NH Ac solution were obtained at 85°C and were compared and found to be the same. These findings suggested that the diacetate complex of cobalt, Co(Ac),.4H20, was formed at 85°C. When a cobalt sulfate-ammonium acetate solution was heated to a temperature above about 165o, a finely divided pink precipitate appeared. The X-ray diffraction pattern of this precipitate indicated that it was Co(Ac), - 4H,O. In addition, it was discovered that when chloroplatinic acid, H,PtCl;, was added initially to the cobalt sulfate-ammonium acetate solution, a faster reduction was obtained. The roles of the solution complex, pink precipitate and chloroplatinic acid in the reduction process were then investigated. APPARATUS The experimental work was carried out in a two-liter stainless-steel autoclave. Adetailed description of the autoclave and the auxiliary equipment used in maintaining constant temperature and pressure may be found elsewhere.= Because the stainless steel was corroded, and also because it acted as a hydrogena-tion catalyst, an all-glass liner was fabricated such that the solution came only into contact with flame-polished pyrex glass. EXPERIMENTAL PROCEDURE The solutions used in the experimental work were prepared by dissolving reagent grade chemicals in distilled water. Although variation of the brand of ammonium acetate appeared to have no effect on the experimental results, CoSO, 7H O from the J. T. Baker Chemical Co. of Phillipsburg, N. J.,was found to give faster reductions than that prepared by Allied Chemical and Dye Corp., N. Y. The former was used throughout the course of the experimental work and was weighed up at the outset of each experiment. The ammonium acetate was dissolved to form a 6M stock solution, which was stored under refrigeration. A 10 pct solution of chloroplatinic acid (J. T. Baker Chemical Co.) was diluted to a 1.15 x 1Q2 M stock solution, which was standardized by precipitation of K,PtCl, as outlined by Scott. The appropriate volume of the chloroplatinic acid, H,PtCl,, solution was pipetted into the clean, dry glass liner. The cobalt sulfate-ammonium acetate solution, which had previously been saturated with

Jan 1, 1962

IN the early period of steelmaking, ingot structure and segregation were of no practical importance. Crucible melting required very small ingots that gave little segregation, and a small inserted hot top prevented pipe. As larger ingots were poured from bessemer converters and open-hearth furnaces, segrega- [ ] tion, piping, and gas evolution became increasingly important. The techniques of making semikilled and rimmed ingots were developed with little knowledge of the actual mechanism of the process. The first studies of solidification were made by the Brearleysl and Gathmann,2 who used stearine to show the effects of shrinkage and mold shape. Fig 11-1 is a picture of a series of stearine ingots at various stages of solidification. These studies showed that the liquid solidifies at a nearly uniform rate from the sides and bottom of the mold and demonstrated the formation of

Jan 1, 1951

By A. S. Michaels, R. S. Timmins

A study of the effect upon oil recovery from an un-consolidated porous medium of chromatographic transport of selected reverse-wetting additives during water displacement is described. Flow tests were performed on hydrocarbon oil-saturated sand columns (containing connate water) into which small volumes of short-chain aliphatic amine solutions were introduced during water flooding. Concurrently, meusurements of oil-silica contact angles, oil-water interfacial tensions and oil-water distribution coefficients were measured us a function of additive concentration. Certain treatments were found to cause a slight reduction in oil recovery, while others produced a significant increase (up to 50 per cent of the normtzl irreducible rninimum oil saturation). Recovery eficiency was correlated most satisfactorily with the maximum degree of reverse wetting produced during additive transport; conditions which resulted in only mild oil wettability of the sand reduced recovery, while those favoring strong oil wetting increased recovery. A mechanism of reverse-wetting additive action during chromatographic transport is developed which ascribes the results to transient changes in oil-solid contact angle during flow, with consequent release of oil trapped by capillary forces. Implications of these observations with regard to improved waterflood efficiencies are discussed. INTRODUCTION The need for finding improved methods of oil production is amply illustrated by the large volume of oil considered economically unrecoverable by existing production practice. Water flooding has long been an excellent method of secondary recovery. However, even in those areas of a formation which are well swept by a water flood, 20 per cent or more of the oil remains trapped within the formation and is not recovered. This trapping of oil within the pores of the rock structure results primarily from interfacial forces. If these interfacial forces were altered, it is possible that the trapped oil could be released and recovered. The addition of surface-active agents to a water flood to alter the interfacial properties of the oil-water-solid system has received considerable attention as a method of increasing oil recovery. Studies of surfactant treatment have yielded varied and, in some cases, apparently conflicting results. Increased oil recovery using surface-active agents has been reported by a number of investigators. Others have found that use of surfactants in a water flood either has no effect upon oil recovery or decreases it. Since surface-active agents tend to alter the formation wettability and oil-water interfacial tension simultaneously, several investigators have tried to determine the role these two factors play in oil recovery. Data have been presented which indicate that the most desirable condition for the solid surface is strongly water-wet. Other results indicate that, although breakthrough recovery may be less, the greatest ultimate recovery is obtained when neutral wettability prevails.", " The desirability of low interfacial tension seems to depend upon the wettability of the formation. Reports of higher recoveries, when the interfacial tension is high in a water-wet system and low in an oil-wet system, are at odds with reports of increased recovery in water-wet systems when surfactants which decrease the interfacial tension are added to the water flood. A review of previous work studying the effects of using surface-active agents in a water flood shows that these agents produce widely different effects and that opinions as to the role of the various interfacial properties are diverse. The consensus, however, is that the interfacial properties are quite important in the displacement of oil from a porous medium by water. Even in those investigations where appreciable increases in oil recovery resulted from treatment with a surface-active agent, economic considerations generally made practical application of the treatment unattractive because surfactants tend to be adsorbed within the formation. This adsorption would necessitate using large quantities of surfactant if all of the flood water were treated to contain a given surfactant concentration, even if this concentration were quite low. Preston and Calhoun suggested that the principles of chromatography could be applied to the use of surface-active agents as a means of increasing oil recovery. A small volume of surface-active material is injec-

By W. E. D. Jr. Stokes

THE application of aviation to mining and petroleum operations, on the basis of economy and attainment, has become a demonstrated fact. According to Dominion Government records, 30. Canadian companies engaged in air transportation with northland mining camps, carried 13,000 tons of freight in 1935, and in 1936 carried 16,000 tons. In addition, many mining companies used planes to transport prospectors with canoes, outboard motors, gasoline drums and supplies to remote locations, and one company maintained a plane to take radium-bearing ore from its mine on Great Bear Lake nearly 1000 miles south to the rail-way at Waterways, Alberta. Heavy pieces of mining machinery weighing 2 tons are being carried by Ford trimotor planes over the Andes, at an altitude of not less than 15,000 feet. At Bulolo, New Guinea, 17,500 tons of disassembled gold-dredging equipment has been flown over inaccessible terrain, while supplies and building materials for a, community of 1000 whites have been transported by airplane. A 3 1/2-ton shaft was carried on one notable trip, while at another time an automobile, 2 tons of rice and a large safe went over the mountains in one plane. Fig. 1 shows an electric generator that was carried by plane to Bulolo.

Jan 1, 1937

By R. D. Carnahan, J. E. White

A study of dispersion strengthening in TD-Nickel (nickel plus 2 vol pct Tho2) was conducted employing microstrain techniques at ambient room temperature. It was found that optimum strength was due primarily to the incorporation of stored energy developed by a variety of thermal-mechanical treatments. The relatively low strength of the recrys-tallized condition implies that the dispersed particles themselves offer only token resistance to deformation. The development of resistance to large-scale recovery or recrystallization at temperatures near the melting point requires a more extensive sequence of strain-anneal cycles than does the development of optimum strength. A micro-Bauschinger effect was observed which appears to be related to the lattice resistance to the movement of free dislocations. The effect was nearly identical to that in pure nickel indicating that the presence of the dispersed phase and considerably increased dislocation density (stored energy) only alters the number or effectiveness of barriers. THE early stages of deformation of engineering materials can be conveniently studied by utilizing strain-gage techniques which permit resolution of strains less than 5 X 10-7 in. per in. for testing in four-point bending (Carnahan and white1). The present investigation, part of a continuing study on the very early stages of deformation, was designed to reveal the true role of a dispersed phase in promoting high strength in a commercially available dispersion-strengthened alloy. Although this technique has been used for some time to study microdeformation in pure metals and alloys, it has just recently received attention as a means of investigating dispersion strengthening. Studying the very early stages of deformation in alloys which depend upon a finely dispersed inert phase for strength may prove to be a very important method for a better understanding of these materials. It is essential to obtain considerable clarification of actual dislocation movement and the kinds of deformation barriers which exist before optimum properties can be designed into this type of material with any degree of confidence. Considerable research on a variety of dispersion-strengthened materials has resulted in two different schools of thought regarding the strengthening mechanism. One faction2-4 favors the idea that the particles themselves resist the motion of dislocations. The criterion for yielding is the fracture of the dispersed second-phase particles due to an array of piled-up dislocations. Other invesfigators5-a have shown that particles are effective primarily by allowing a greater buildup of stored energy or dislocation density through thermal-mechanical treatments in the composite than the pure matrix material. The particles themselves, then, are not exclusive obstacles, but the complex network of particles, dislocation tangles, subboundaries, and grain boundaries are strength determining. The development of such a complex dislocation network in SAP has been studied recently in some detail by Goodrich and Ansell. The ability of dispersion-strengthened alloys to resist softening or recrystallization is also of considerable importance; however, the criteria for maximum stability may not necessarily be those for maximum strength. In this study, in addition to the evaluation of the microstrain properties of TD-Nickel, it is felt that considerable clarification of the true dependence of strength and stability on the dispersed phase is shown. I) MATERIAL AND PROCEDURE TD-Nickel is a dispersion-strengthened alloy developed by the E. I. DuPont de Nemours Co., which contains 2 vol pct thoria (Tho2) in a pure-nickel matrix. The average ThO2 particle size is approximately 0.1 p and the interparticle spacing is less than 1 u. The material was supplied by DuPont in two conditions: hot-extruded bar stock, and stress-relieved cold-rolled sheet 0.025 in. in thickness. The bar was extruded at 2200°F from a cold-pressed and sintered billet. The sheet stock was prepared from the extruded material by a process involving ten or more 50-pct cold reductions by rolling with intermediate anneals at 1800° to 2000°F. Test specimens used in this study were prepared in the form of rectangular parallelepipeds measuring 0.375 by 1.375 in. in thicknesses ranging from 0.025 to 0.040 in. Samples prepared from sheet and extruded stock were mechanically polished before heat treatment and were handled with extreme

Jan 1, 1964

By C. E. Mills

STUDIES of ground movement and subsidence resulting from mining operations cover a broad field. It is also a very important consideration and one that eventually affects nearly every mining operation of any extent. The damage to surface buildings, removal of mine surface plants and replacements of main hoisting shafts must reach an astounding expenditure were these cost figures available over a period of years. Were the subject one of mathematical formula and dependent only on the angle of draw of the walls or country rocks, the problem would be relatively simple. Consideration must be given to depth and extent of workings; structural conditions of the orebodies and enclosing country rock; physical properties of these same rocks, including schistosity, bedding, jointing, slips, dikes, faults, and other structural weaknesses. The method of mining, extent of openings, supporting pillars, and amount of moisture or water underground are other pertinent factors. With such a large number of variable factors, it is apparent that the subject of subsidence is one that must be based largely on experience and results at other mines where conditions are somewhat comparable. In presenting this paper, it is the intent to describe the progressive results of past ground movements at the United Verde, to bring out physical conditions largely responsible for this movement, but to refrain from theorizing on the ultimate extent of subsidence resulting from future mining operations.

Jan 1, 1934

By T. E. Eagan, W. R. McCrackin

IN dealing with segregation in babbitt, and its effect on the final cast structure, which is a bearing, it is obviously impossible to cover all of the compositions manufactured. Each composition, of course, will exhibit certain specific types of segregation. However, as examples,, two compositions of babbitt are presented: one a tin-base of well-known analysis and the other a lead-base, which in the past few years has found wide usage. Bearings usually are cast either statically or centrifugally; therefore the effect of these two methods on segregation is presented. EXPERIMENTAL PROCEDURE A slab of babbitt 1/2 in. thick by 5 in. wide and 17 in. long was cast, using a book mold with the long edge vertical. An A.S.T.M. grade 2 babbitt was used (3.5 per cent copper, 7.5 per cent antimony, remainder tin), to which 0.10 per cent tellurium had been added. Unfortunately, no metal without tellurium was available. The mold to hold the babbitt was heated to approximately 300°F., the temperature being judged by the babbitter. The pouring temperature of the babbitt was 875°F. (470°C.). One slab was made by allowing the babbitt to cool without stirring. The other slab was stirred during the entire cooling cycle. This stirring consisted of a vigorous churning or puddling into the mold until complete solidification had taken place. Three samples were removed from these slabs. One was taken at the extreme bottom, another half way to the top, and another at the extreme top, all at the center of the width. Chemical, macroscopic and microscopic examination was made of all samples. Table I shows the chemical analyses obtained at the described positions [ ] in the slab. The analyses show no serious amount of gravity segregation. Microscopic examination from edge to edge of the slab showed little change in structure. From top to bottom there was a progressive coarsening of the grain size in the stirred slab but little change in the slab that was not stirred (Fig. I). No definite exhibit of segregation could be detected. In line with our experimental study on the tin-base babbitts, we cast an almost duplicate slab using A.S.T.M. Alloy No. 15, containing 0.9 to 1.25 per cent tin, 14.75 to 15.5. per cent antimony, 0.80 to 1.25 per cent arsenic and 0.4 per cent copper. The slab was 16 in. long and 3/8 in. thick, cast with the long side vertical. One slab was allowed to cool normally and the other was stirred continually during cooling. The pouring temperature of the babbitt was

Jan 1, 1944

By R. T. Southin

Cast ingots of 99.99 pct purity A1 and aluminum/copper alloys containing up to 2 pct Cu have been found to contain four zones rather than the three previously accepted, i.e., chill, colummar, and equiaxed zones. The fourth zone consists of a coarse dendritic layer across the top surface of the ingot which is open to the atmosphere. It is also found that the grains in the equiaxed region have a "cornet" shape, with a head which is coarsely dendritic and a tail which grew with the same structure as the columnar grains. Experiments using mechanical barriers, and others involving the elimination of the surface dendrile layer, have indicated that nucleation of the equiaxed zone is caused by the showering of dendritic particles from this surface dendrite layer. These particles are the dendritic heads found in the comet grains. A mechanism of nucleation and growth of these comet grains is put forward. Experiments with a number of other metals and alloys suggests that these conclusions may apply generally to ingots cast without the addition of nucleating agents, and solidified under normal conditions. THE macrostructure of cast ingots may contain the following three zones: i) a peripheral zone of fine equiaxed grains, commonly called the chill zone; ii) a zone of columnar grains extending inwards from the chill zone; iii) a central zone of equiaxed grains; these are normally larger than the chill grains. All three zones are not necessarily present in any particular ingot since their existence and magnitude depend upon the casting conditions and composition of the cast material. The mode of formation of zones i and ii is fairly well understood. However, the cause of the central equiaxed zone remains a matter of conjecture. Previous theories put forward to explain the mechanism of nucleation in the equiaxed zone have been examined by Chalmers1 and Winegard.2 At the time when the present work was carried out the most re -cent hypothesis was that due to Chalmers,1 who recognized more fully than previous workers that conditions in this zone during solidification were not conducive to nucleation. In his hypothesis, he suggested that nuclei were formed near the mould wall during the very early stages of solidification, and that they can drift into the central zone by convective motion. This was supported by evidence from experiments using mechanical barriers to stop the drift of nuclei. A similar hypothesis had previously been put forward by Genders.3 More recently, Jackson et al. 4 have observed that dendrite arms in organic compounds can melt off during solidification. They have postulated that this occurs in metals and alloys, and that the dendrite arms which have been freed from the main dendrite act as nuclei for the equiaxed zone. In the present work, critical metallographic examination has shown that there is a fourth zone in the macrostructure of cast ingots which is a dendritic layer over the top surface of the ingot. It is also shown that there is a relationship between this zone and nucleation of the equiaxed zone. EXPERIMENTAL DETAILS The alloys examined were prepared from super -purity aluminum of 99.99 pct min purity (spectro-graphically detected impurities of Cu, Fe, Si, and Mg) and copper of 99.98 pct min purity (spectrographically detected impurities of Si, Zn, As, Fe, Pb, Bi, Ni, Sn, Mn, Ag, Cr, and Al). Three compositions of ingots were examined, containing 0.0, 0.1, and 2 pct Cu, respectively. The alloys were melted in an alumina-lined salamander crucible using a medium-frequency electric induction furnace; when the appropriate casting temperature was reached, the alloys were cast without degassing or fluxing treatment. The mould used was made of electrode graphite and had the following dimensions: external diameter 6 in., height 9 in., with a mould cavity 8 in. deep and a diameter tapering from 5 in. at the top to 4 in. at the bottom. Casting temperatures used were generally in the order of 70" to 90°C above the liquidus and the mould was at room temperature before casting. Inserts kere placed in the mould cavity in some experiments. These consisted of either an 18-g stainless-steel tube of 2 in. diam held axially in the mould i in. off the bottom and extending 1 in. out of the top of the mould or a "trap-door" barrier of stainless-steel gauze of 24-mesh held horizontally in the mould 31/2 in. down from the top. The construction of this insert is shown in Fig. 1. All inserts were preheated prior to casting to prevent chilling. RESULTS The macrostructures of ingots of the three compositions are described, in terms of the three generally recognized zones, in Table I, and illustrated in Figs. 2(a) to (c). The most interesting observation in this table is that relating to the shape of the equiaxed grains, which were not in fact equiaxed but of almost tear-drop shape. Closer examination of these grains showed that each consisted of a head which had a coarse dendritic structure and a tail which always grew in the opposite direction to heat flow, and which had the same structure as that of the columnar material of the ingot concerned; i.e., in the pure aluminum and 0.1 pct Cu alloy it was cellular and in the 2 pct Cu alloy it was cellular-dendritic. Identification of original cast grains was greatly hampered in the super-purity aluminum ingots, and to a lesser degree in the 0.1 pct Cu alloy,

Jan 1, 1968

By F. A. Schaufelberger

Early work on chemical precipitation of metals from metal salt solutions is reviewed. The chemistry and thermodynamics of precipitating copper, nickel, cobalt, and cadmium metals by reaction with hydrogen are discussed. Mechanisms of metal precipitation, nu-cleation, growth, and agglomeration are reviewed, as well as some solubility phenomena of cleation,gases and solids at elevated temperatures. Experimental data presented deal mainly with the reaction of copper sulfate solution with Hz. METAL can be recovered from a leach solution either indirectly by precipitation as a compound that is later reduced or directly by electrolysis, cementation, or chemical reduction, for example, with hydrogen. The widely used electrowinning processes suffer from the inefficiency of converting fuel to low voltage dc and from low current efficiency when complete recovery is attempted. With the batch hydrogen reduction methods outlined here, a unit of fuel converted to hydrogen in modern gas reform plants will make two to three times as much metal as can be obtained with electrolysis. With continuous hydrogen reduction, four to six times as much metal is obtained. Precipitation by reducing a metal salt solution with H, has been known for almost 100 years.' Commercial use of the process, however, awaited the research and development program initiated by Chemical Construction Corp. Within the last few years this program has brought about construction of commercial plants, listed on p. 701. Ideal hydrogen reduction will precipitate a pure metal from a solution obtained by commercial leaching methods at a rapid rate without excessive temperatures and pressures. The metal precipitate will be of desired size and density, less than a percent left in the vessel being deposited on the wetted parts. The present discussion will outline Chemical Construction Corp.'s early development program and will discuss the chemistry and mechanics of reducing copper, nickel, cobalt, and cadmium from solution by H2. Work on selective reduction of nickel from cobalt has been described earlier.2 The article is not concerned with precipitation of copper by disproportionation of cuprous solutions where yield is limited" to 50 pet.* It does not discuss use of gaseous reducing agents other than hydrogen, such as SCV which may lead to contamination with sulfur, or CO," which is considerably more expensive than hydrogen and produces a gaseous reaction product, CO2.† The article does not include use of other nongaseous reducing agents: which are far more expensive than CO. Also, notes on the history, engineering design, and performance of commercial plants have been given elsewhere." It will be shown that a pure metal can be precipitated by reduction with hydrogen from solutions obtained by commercial leaching methods when the solution cohposition is controlled and proper acidity, proper metal ion concentration through controlled complex formation and hydrolysis, and adequate agitation for suspension of metal and for transfer of reducing gas are maintained. Reasonable temperatures and pressures are used which are less excessive than those used by previous workers, although they are maintained at above equilibrium values because of process kinetics.' It has also been found necessary to induce nuclea-tion and to control growth and agglomeration in order to get a powder product of suitable physical properties. Review of the Literature Muller, Schlecht, and Schubardt of I. G. Farbenm claimed a successive reduction of silver, copper, nickel, cobalt, and zinc from ammoniacal solution by applying progressively higher temperatures and hydrogen pressures. Metals produced by this technique were not pure, since no attempt was made to adjust the solution composition between the different reductions. It is doubtful that the zinc product contained any metallic zinc. The major contribution to the literature" was made by the Ipatiews,12 who prepared platinum, iridium, copper, nickel, cobalt, lead, tin, arsenic. antimony, and bismuth at often extreme conditions, up to the critical temperature of water (373"C), at 1500 to 7500 psi, for as long as several days. Even cadmium and zinc were claimed to have been observed in trace quantities precipitated together with basic salts. In the early experiments solutions were not stirred. Extensive formation of oxides and basic salts occurred. probably long before sufficient hydrogen could be supplied in the unstirred liquid to decrease the metal concentration in solution by reduction. The importance of hydrogen pressure was

Jan 1, 1957

Jan 1, 1902

By Chas. Y. Clayton, Francis B. Foley, W. E. Remmers

DuRing the summer of 1919, the late Dr. Henry M. Howe, then Chairman of the Division of Engineering of the National Research Council, organized a committee to obtain a better insight into the behavior of carbon steels under the influence of various treatments by a proper control of the time and temperature factors. During part of 1919 and 1920, work in connection with this investigation was carried on at Dr. Howe's laboratory at Bedford Hills, N. Y. During 1921 there was an enforced hiatus in the work, occasioned by the illness which resulted in Dr. Howe's death in 1922. At that time one of the present authors compiled the results of the work which had been done and this was published in 1923.' Following the publication of this work, it seemed desirable to carry on in the same manner an investigation of steel of C 0.75 per cent., which steel had not been as fully treated as had the other steels of C 0.34 and 0.52 per cent., used in the published work. Furthermore, certain unusual results have been obtained in the treatment of C 0.52 per cent. steel by quenching and drawing, and repetition of this part of the work seemed advisable. This has been done during the past year at the School of Mines and Metallurgy of the University of Missouri at Rolla, Mo., by a cooperative undertaking of the School and the Bureau of Mines, working in conjunction with the Committee on Heat Treatment of Carbon Steels of the National Research Council. The present paper is a report of the results obtained in this work.

Jan 1, 1926

By R. F. Mehl, C. S. Barrett, A. H. Geisler

THE studies of the mechanism of precipitation and of the resulting property changes in aluminum-silver alloys1-3 have presented some new concepts of the aging reaction-concepts that may be fundamental in establishing a complete quantitative theory of age-hardening. With both aluminum-copper and aluminum-silver alloys, thin platelike aggregates form parallel to the Widmanstätten planes of precipitation.1,4 These platelets grow in lateral dimensions and in thickness with aging time until they are thick enough to produce an X-ray diffraction line pattern. Their structure is that of a transition lattice which is coherent with the matrix, since the atomic spacings in the matrix and the precipitate are the same on each side of their common interface.2,4 The equilibrium precipitate forms later from and at the expense of the transition lattice. Since age-hardening occurs during the formation and growth of the transition lattice, the major contributor to the hardening no doubt is the stress condition in the matrix resulting from the matrix holding the precipitate in the coherent condition. The development of these stresses also appears to be responsible for an increase in the electrical resistance superimposed on the normal decrease resulting from a change in the concentration of the matrix during aging.3 The two consecutive reactions constituting the aging process are accompanied by characteristic microstructural alterations. The initial precipitation process results in the formation of a Widmanstätten figure, while the later transformation of the transition lattice to the equilibrium lattice is accompanied by a coalescence, in the case of aluminum-copper alloys,5 and by the appearance of light areas at the grain boundaries with aluminum-silver alloys showing a structural rearrangement of matrix and precipitate.3 This latter reaction is similar microscopically to the so-called "discontinuous precipitation." Possibly discontinuous precipitation is a process that often if not always follows true precipitation of a coherent lattice and during which the transformation of the coherent transition lattice to the equilibrium lattice takes place accompanied by matrix recrystallization.3 EXPERIMENTAL PROCEDURE The alloys were made using 99.97 per cent Al or distilled magnesium, with

Jan 1, 1943

By A. A. Blow

The productive area of the Leadville mining district immediately adjoining the city of Leadville, which, by its wonderful richness, has attracted the attention of the mining world for the past twelve years, may, with a few exceptions, he considered as divided into seven local mining centers, separated one from another by the topographical features of the country, and designated by common consent as Fryer Hill, Yankee Hill, Breece Hill, Rock Mill, Printer-Boy Hill, Iron Hill, and Carbonate Hill. Of these seven distinot mining localities, or groups of mines, the central one, Iron Hill, is the one of greatest importance and interest. It was the scene of the earliest discovery of carbonates, as far back as 1875, and since that time has always maintained its position

Jan 1, 1890

By Augustus Locke

In 1900, when. the public first heard of "secondary enrichment," the Butte chalcocite seemed clearly supergene. Mining, through successive regions of leached capping, bonanza sulfide, and sulfide less rich, had paused at lean bottom levels which, though chalcocite-bearing, suggested the waning of copper. The deepest chalcocite, at 1500 ft., was yet too shallow to disturb the supergene hypothesis. But, with deeper mining, lean levels yielded to fat ones. Here and there they showed, within the same vein, an inverted distribution, chalcopyrite above and chalcocite below. To the miners' astonishment, they carried chal-cocite, unaffected by cross faults, on an independent course to the depth of 2500 ft. The pattern of ore distribution, hitherto revealed only in fragments, was now appearing in perspective, and, in the depth of the chalcocite, was beginning to make Butte differ from all districts where the chalcocite is indubitably supergene. The idea of hypogene origin at length came into favor; by 1913, when Sales' advocated this origin, the argument had become a powerful one. This argument rested on field evidence; but, already, there was beginning to emerge microscopic evidence not included in this argument. Especially pertinent was the proof that (1) the deep chalcocite lies in-mixed with bornite, often microscopic; (2) the deep chalcocite often replaces bornite; and (3) replacement of bornite by chalcocite is accomplished more easily than that of pyrite, enargite, or chalcopyrite. The microscopic evidence has been accumulating for ten years and it demands

Jan 1, 1924

By R. B. Snow

THIS paper describes a technique of polishing and etching specimens of open-hearth furnace slags or hearth aggregates for identification of the crystalline constituents-lime (CaO), tricalcium silicate (3CaO•SiO2), dicalcium silicate (2CaO-SiO2), monticellite (CaO•MgO-SiO2), or forsterite (2MgO•SiO2), with especial emphasis on the mineral merwinite (3CaO-MgO.2SiO2). With proper standardization, this identification does not require the use of the petrographic microscope. The composition of basic open-hearth slags and furnace bottoms falls, almost without exception, within systems containing CaO, MgO, "FeO," MnO and SiO2, in which the number of basic molecules so greatly exceeds the orthosilicate ratio (two molecules of base to one of silica) that free basic oxides, and combinations between them such as aluminates or ferrites, are present in cooled specimens. Orthosilicates of (CaO + MgO) are the most common in such specimens, since in nearly all cases, except premelt slags, the molecular ratio of (CaO + MgO) to SiO2 is more than 2 to r. When sufficient lime is available it combines with the silica to form dicalcium silicate (2CaO•SiO2), which contains little, if any, MgO, FeO or MnO in solid solution whereas the latter oxides combine to form the oxide solid solution known as periclase. If the lime present is insufficient to form dicalcium silicate (2CaO•SiO2) it combines with MgO to form either merwinite (3CaO•MgO.2SiO2) or monticellite (CaO-MgO•SiO2); these minerals take little if any FeO or MnO into solid solution and the remaining MgO, FeO and MnO combine as periclase. This generalization seems to be valid for basic slags and furnace bottoms, since minerals such as CaO-MnO•SiO2 and CaO-FeO-SiO2 are found only in slags in which the lime-silica ratio is less than 2 and are not observed in specimens from furnace bottoms. The identification of crystalline constituents in such materials, especially of fine crystals in the groundmass, is difficult under the petrographic microscope. They are often masked by their neighbors because of their small size in relation to the thickness of the thin section and because of the presence of opaque or colored constituents. The indices of retraction and the optical sign of the mineral are sometimes difficult to determine because of the small size or because of twinning or of inclusions within the crystal. Moreover, the positive identification of merwinite (3CaO•MgO.2SiO2) from its optical properties is usually difficult in the presence of dicalcium silicate (2CaO•SiO2). CaO, MgO, 3CaO•SiO2 and 2CaO•SiO2 in open-hearth slags have been identified for a number of years in the U.S. Steel Corporation Laboratory by the usual

Jan 1, 1947