Iron and Steel - Influence of Temperature, Time and Rate of Cooling on Physical Properties of Carbon Steel. II.

DuRing the summer of 1919, the late Dr. Henry M. Howe, then Chairman of the Division of Engineering of the National Research Council, organized a committee to obtain a better insight into the behavior of carbon steels under the influence of various treatments by a proper control of the time and temperature factors. During part of 1919 and 1920, work in connection with this investigation was carried on at Dr. Howe's laboratory at Bedford Hills, N. Y. During 1921 there was an enforced hiatus in the work, occasioned by the illness which resulted in Dr. Howe's death in 1922. At that time one of the present authors compiled the results of the work which had been done and this was published in 1923.' Following the publication of this work, it seemed desirable to carry on in the same manner an investigation of steel of C 0.75 per cent., which steel had not been as fully treated as had the other steels of C 0.34 and 0.52 per cent., used in the published work. Furthermore, certain unusual results have been obtained in the treatment of C 0.52 per cent. steel by quenching and drawing, and repetition of this part of the work seemed advisable. This has been done during the past year at the School of Mines and Metallurgy of the University of Missouri at Rolla, Mo., by a cooperative undertaking of the School and the Bureau of Mines, working in conjunction with the Committee on Heat Treatment of Carbon Steels of the National Research Council. The present paper is a report of the results obtained in this work.