Conventional ferronickel smelting has five main steps: Drying, calcination, prereduction, smelting and refining. In the scope of the current work, smelting experiments were conducted using Sivrihisar laterite ores (1.26% Ni) of Turkey. The ore samples previously subjected to drying, calcination and prereduction stages were smelted in alumina crucibles in a laboratoryscale horizontal tube furnace under argon atmosphere. Smelting experiments were performed at 1500, 1550 and 1600 oC. The amount of excess coal used in prereduction step was another variable. Sivrihisar laterite ore is a limonitic one with low MgO composition. Therefore, MgO was added to the smelting charge as a flux. The effects of experimental variables on metal Ni content and slag composition were investigated.

Jan 1, 2012

By N. Ono, H. Fujiwara, S. Otsuka-Yao-Matsuo, T. Omata

"The electrical conductivity and the oxygen release and uptake of sintered indium tin oxide (ITO) upon heating and cooling under the condition that P(O2)/P*=4.9X10-4 (P* = atmospheric pressure), :when P(O2) was approximately 50Pa, were simultaneously measured by using a closed-system oxygen-gas analyzer. A large increasing in -the electrical conductivity - upon the· oxygen release detected in 1130<T<1273K was observed. Quantitative relationship between the number of oxygen atom released from ITO and the conduction electron density in ITO was studied. The release of one oxygen atom agreed with the generation of two conduction electrons, i.e., the efficiency-carrier-generation for the oxygen release from the ITO was almost one. The oxygen atom released must be originally at the quasi-anion site in the C-type rare-earth lattice, i.e., the 16c site in the space group of Ia3, as an interstitial excess oxygen, Oi"". It was concluded that the mechanism of conduction carrier generation and compensation upon SnO2 doping into In2O3 can be expressed by the defect equation, 2SnO2-2Sn1n +2(1-z)e'+zOi""+3O0 x+(l-z)/2O2, and that the oxygen release bringing the increase in the electrical · conductivity can be expressed by the equation, Oi""-1/2O2+2e'.IntroductionThin films of SnO2-doped In2O 3 (generally designated as ITO, for indium tin oxide), which have high optical transparency for visible light and high electrical conductivity, have been used as transparent electrodes for liquid crystal and electrochromic displays. It is well known that the electrical conductivity of ITO depends on the content of SnOi-dopant and oxygen. However, a reliable relationship between electrical conductivity and the absolute oxygen content in ITO has yet to be reported. The elucidation of such a relationship is one of the important clues for realizing extremely highly conductive ITO electrodes."

Jan 1, 2000

By Junbiao Liu

Rutile is mostly produced from placer sands. Its beneficiation from primary deposits has rarely been investigated. However, there is interest in primary deposit because of the depletion of sand deposits. The Zaoyang deposit in China is the only rutile primary deposit currently mined. The plant employs a Tabling-Magnetic process which recovers only 20% Ti02 at a grade of 87%. This study shows that significant improvement on the recovery (52% at the same grade) can be achieved. This study includes a detailed mineralogical examination and the development of a processing flowsheet of the ore. The gangues are primarily amphiboles, garnets, zoisites, and chlorites. The liberation of rutile occurs at about 200 mesh. Gravitational, flotation, and magnetic separations are all employed in the process developed, depending on the mineral characteristics and experimental results. The flotations circuit utilizes benzyl arsonic acid to float rutile and sodium fluosilicate to depress the gangues. This is a new reagent scheme for rutile flotation.

Jan 1, 1989

By O. Barbosa F.

The thermochemistry of the systems SCN-H2O, Au-SCN-H2O and Ag-SCN-H2O is discussed. Potential-pH diagrams at 25°C are drawn for each system considering several sets of concentrations of the species involved. The information provided by the potential-pH diagrams is.complemented by distribution curves for each series of gold and silver complexes with thiocyanate. The analysis includes comparisons between the thiocyanate systems and the analogous cyanide systems, pointing out analogies and differences between the leaching of gold and silver with thiocyanate and with cyanide. The possibility of using soluble oxidizing agents such as ferric ions, hydrogen peroxide and Caro&apos;s acid is evaluated. The thermodynamic data used in the calculations and the chemical reactions represented in the Pourbaix diagrams are all reported in three Appendices. The overall results indicate the thermodynamic conditions for gold and silver leaching by thiocyanate.

Jan 1, 1989

By C. A. Young, J. D. Miller

Adsorption isotherms previously determined by in-situ Fourier transform infrared/internal reflection spectroscopy (FT-IR/IRS) for oleate adsorption at calcite and fluorite surfaces near pH 9 and at various temperatures are compared. Results indicate that, at both mineral surfaces, chemisorption occurs at equilibrium concentrations below approximately l x l0-5 M oleate while calcium dioleate surface precipitation occurs at higher equilibrium oleate concentrations. The extent of chemisorption at the calcite surface is 3 to 5 times less than that at the fluorite surface while the extent of calcium dioleate surface precipitation on calcite is nearly a magnitude larger than that on fluorite. However, for both minerals, surface precipitation decreases with increasing chemisorption. Contact angle measurements and flotation recoveries show the hydrophobicity of fluorite to be greater than that of calcite at each of the temperatures and oleate concentrations studied. Significant differences are noted only in the chemisorption region. Unlike calcite, the hydrophobicity of fluorite was sensitive to the presence of oxygen in the system. Multichannel Laser Raman Spectroscopy (MLRS) showed this behavior was caused by the double-bond reactivity of adjacent chemisorbed oleate molecules and subsequent formation of an epoxide/polyether complex at the fluorite surface. Such a reaction product could not be detected at the calcite surface. These differences in adsorption density, hydrophobicity, and polymerization behavior are discussed in terms of the intrinsic surface properties of the minerals.

Jan 1, 1999

By P. S. Seryogin

R & D works supported by industrial-scale tests, which were carried out by joint efforts of the OAO Gipronickel Institute and MMC ?Kola? engineers, have accomplished with the production of 90?95% metallized nickel powder in tube furnaces (NPTF), with its ?active fraction? (AF) to be further used for decopperization of nickel electrolyte by cementation. Consistently positive results obtained in the course of the lab and industrial experiments have allowed the Severonickel Combine management to effectively replace all activated nickel powder (ANP), which was then employed for cementation, with the AF, having activity over 80%, and eventually shut down the entire operation of gaseous reduction. Ever since the developed technology has been implemented, its annual economic effect exceeds 2 ml. dollars.

Jan 1, 2006

By V. M. Paretsky

Oxygen-flame converting of a solid ground matte containing heavy non-ferrous metals in a wide range of concentrations is one of the perspective trends meeting the demands of modern non-ferrous metallurgy. As. a result, of semicommercial tests on oxygen-flame smelting of nickel matte containing 13,5-17,5% Ni; 0,45-0,65% Co under continuous autogenous conditions a converter matte containing 68 8-75,0% Ni and 0,48-1-,0% Co and ferrite -calcium slag containing 1,4-8,4 Ni and 0,16-0,56 Co were pro¬duced. Nickel recovery in a converter-matte was 76,2%, copper - 58,&apos;2% and cobalt recovery in. a slag was 90%. Slag cleaning in an electric furnace allowed to after-recover nickel and cobalt in an alloy to produce a dumpy slag containing 0,03% Ni and 0,02% Co. The development of modern&apos; ecologically pure energy-saving autogenous technologies of the treatment of sulphide raw materials containing heavy non-ferrous metals makes certain demands of the perfection of a process of converting rich sulphide-metallic intermediate products obtained at autogenous smelting. These-demands were connected first of all with the fact that converting process stages because of process periodicity are more unfavourable from the point of ecology, power intensity and unit stability. Besides, during rich matte treatment the problems connected with heat shortage when using air blast and heat excess-when using top oxygen blast to treat luquid matte a-rise and when enriching air blast by oxygen up to 26% fast erosion of the brickwork of a tuyere zone takes place. The technology of Outokumpu and Kennecott companies-on solid- copper matte converting in a flash smelting furnace using air blast is not universal as its possibilities are limited by certain composition of mattes. Besides, flash smelting to produce highly basic or combined slags requires larger enrichment-of blast by oxygen or extra fuel feed. Naturally a flowsheet with continuous converting of matte of various composition up to white matte production is simple,

Jan 1, 1993

By Robert D. Rogers

The demand for phosphate will continue into the future, because phosphate is currently irreplaceable as a plant nutrient and in many chemical applications. Phosphate is not recycled, so the supply must be replenished through a process of mining and purification. Numerous microbial isolates. obtained from the environment were screened find those which demonstrated the greatest promise of solubilizing PO4 from the ore of interest. Screening was accomplished in a step wise manner an agar plate bioassay, shake flask studies, and semi continuous growth conditions. It was found that with the proper conditions of nutrient supply and solution pH; the bacteria and. fungus used in the semicontinuous process were able to solubilize in excess of 80% of an Idaho rock phosphate ore (RP) within nine days. A significant amount of solubilization occurred within the first six days. There was a &apos;reasonable correlation between the occurrence of soluble Ca and PO.4 during the processing of the RP thus providing evidence that the RP was being disintegrated by the organisms. In all cases, HPLC analysis of the solutions in which PO4 had been. extracted from RP showed that organic acids, which have been implicated as the mechanism of solubilization, were present.

Jan 1, 1991

By José Luiz Rodrigues Bravo

The production of electrolytic copper with assured quality corresponding to international standards, in a conventional electrorefkery of a custom smelter, is a hard and cautious task, if no advanced technologies for selective control of electrolyte impurities are available. The improper control of the amount of As , Sb and Bi in the anode that enter the tankhouse , attributable either to a bad schedule of concentrate input or to the unavailability of clean concentrates in the international market , as well as the lack of means to maintain the suitable level of these elements in the electrolyte together with other operational circumstances, can result in off-grade copper, as well as affect the starting sheet chemically and physically. This paper presents in a practical way the relationship between the operational conditions and the cathode and starting sheet quality produced at CMSA, covering the period of the last five years of operation, discusses the technologies available in the market for antimony and bismuth removal and compare the results of testwork, achieved in the laboratories of CMSA, using two resins not associated with patented technologies.

Jan 1, 1997

By N. D. Schupp

The Doe Run Company's Herculaneum, Missouri lead smelter has existed in continuous operation since 1892. Throughout the history of the plant extensive developments have been made to improve throughput, increase productivity, decrease operational costs and improve technology, while remaining an environmentally responsible producer of high quality primary lead in the international market. This paper provides an overview of the Herculaneum smelter, focusing on the most recent configuration of the operations. The paper includes discussion on all the aspects of primary lead production at the Herculaneum smelter.

Jan 1, 2000

By Jaeheon Lee

Gold-copper alloys are shown to form during the cementation of gold on copper in a solution containing 0.25M [S2O32-] at 25oC. The alloy composition is strongly dependent on the initial Cu:Au ratio in solution and ranges from Au3Cu to AuCu3. XPS results for Au, Cu, S, and O are reported as a function of depth through an entire deposited film with an initial solution containing 20 ppm [Au] and 30 ppm [Cu]. The deposit contained about 20 atomic % gold and was predominantly Cu3Au. Underpotential deposition (UPD) theory is discussed as a mechanism for explaining the formation of these alloys. Several other systems that produce alloys during contact reduction/cementation are also discussed.

Jan 1, 2003

By Kuniaki Murase, Tetsuji Hirato, Yasuhiro Awakura

"Electrodeposition of CdTe was studied using aqueous ammonia-alkaline electrolytic baths in which Cd11-and Te1V-ions are dissolving as Cd11(NH3)/+ and Te1vol-ions, respectively. Ca-thodic polarization curves of the baths suggest the presence of strong interaction between the Cd11-and Te1V-ions; electrodeposition of tellurium is inhibited by the presence of Cd(NH3)/+ ions. The interaction makes it possible to electrodeposit CdTe films with stoichiometric composition. Polycrystalline CdTe thin film of about 1 µm thickness was electrodeposited at 343 K from ammonia-alkaline solutions (pH= 10.7) containing TeO32-(<20 mmol dm-3) and Cd(NH3)/+ ( < 60 mmol dm-3) ions. Increasing Cd(NH3)/42+/TeO32- mole ratio or decreasing total concentration of ammonia/ammonium-ion gave flat and smooth crystalline CdTe deposits at constant cathode potential-0.70 to -0.30 V vs SHE at 343 K.IntroductionCadmium telluride (CdTe) is well-known as a compound semiconductor whose band gap, i.e. 1.44 eV, is suitable for solar energy conversion with a photovoltaic cell. Various methods, such as CVD (chemical vapor deposition) and electrodeposition, of preparing CdTe thin films for solar cells have been investigated.Acidic sulfate solutions with a pH of 1-2 are usually employed for CdTe processing by electrodeposition.1-3) The electrodeposition of compound semiconductors is usually achieved (i) at a higher cathode potential than the redox potential of less-noble species, can in this case, and (ii) under the condition of diffusion-limiting current of a more noble species, Te1Y.4) There-fore, a suitable CdII/TeIV concentration ratio in the acidic electrolytic baths, resulting in the deposition of stoichiometric CdTe, is determined by the diffusion-limiting current density of TeIV- reduction, i.e. the concentration of HTeIVO2+ · Since the solubility ofTe1v species HTeIVO2+ in the acidic solutions is quite low, the rate at which CdTe is deposited from the acidic solutions is extremely slow."

Jan 1, 1998

By A. K. Kyllo

A study has been carried out on the dusts from Hudson Bay Mining and Smelting&apos;s Flin Flon copper smelter. The aim of the work was to determine the mechanisms of dust formation and the deportment of the various constituents. The work concentrated on the copper converters, but the electrostatic precipitators and baghouse also clean the reverberatory furnace off gas, so some mixing will have occurred. The dust composition was found to vary with distance from the furnace, and to be made up of three major components: solidified droplets, unreacted flux, and condensed particles. The solidified droplets were formed from material ejected from the converter during blowing, while the flux was blown out of the converters immediately after charging. The condensed particles contained the majority of the lead and zinc, as well as the volatile impurities. There was also a significant soluble content of the dusts, increasing with distance from the furnace. The condensed material may be separated from the remainder by a simple washing and sizing technique.

Jan 1, 1996

By C. P. Broadbent

The process metallurgy of many nickel laterite smelting operations is controlled largely by the physical chemistry of the slag system. Consequently, accurate phase diagram information and physicochemical property data are essential to interpret and predict the behaviour and optimisation of the overall process. The system (SiO2 - MgO - FeO) first described by Bowen et al. between 1914 and 1935 and the system (SiO2 - MgO - FeO - Fe2O3) determined by Muan and Osborne in 1956 are of particular relevance to the study of nickel laterite smelting slags as these systems form a reasonable approximation of many industrial slags. This paper will review the literature for these (and other relevant) phase systems. In addition data available from the ternary and (quasi)ternary phase diagrams will be compared with data obtained from industrial slags. The physico-chemical properties under consideration will include; melting and crystallisation behaviour (solidus and liquidus temperatures), viscosity - temperature relationships, heat flux considerations, electrical conductivity, surface and interfacial tension.

Jan 1, 1993

By Chai Li-yuan

The anodic behavior of AZ31 magnesium alloy in NaOH alkaline solution was investigated in this paper. The effects of anodizing parameters, such as applied current density, concentration of NaOH and temperature of the solution on the formation, structure and surface morphology of the anodic films were also studied. The formation of the anodic film was analyzed by analyzing the anodic polarization curves, the potential-time curves and XRD, SEM graphs of samples obtained at different anodizing time. The results of corrosion resistance tests, XRD and SEM observation showed that the temperature greatly affected the formation and anti-corrosion property of the anodic film, but the concentration of NaOH not. The film with best anti-corrosion resistance was obtained at applied current density of 10mA/cm2, 353k in 1mol/l NaOH solution.

Jan 1, 2006

By Anja Pfennig, Thomas Böllinghaus, Marcus Wolf

During CCS components are exposed to a corrosive environment and mechanical stress which results in corrosion fatigue and is inevitably followed by the lifetime reduction of these components. The lifetime reduction of the cyclically loaded high alloyed stainless injectionpipe steel AISI 420C (X46Cr13, 1.4034) constantly exposed to highly corrosive CO2- saturated hot thermal water is demonstrated in in-situ-laboratory experiments (T = 60 °C, brine: Stuttgart Aquifer, flow rate: 30 l/h, CO2) in an environment similar to the on-shore CCS-site in the Northern German Bassin. In-situ tension-compression experiments were established simultaneously along with electrochemical measurements using a newly designed corrosion chamber in a resonant testing machine at a frequency as low as 30 – 40 Hz. In addition technical CO2 was introduced into the closed system at a rate close to 9 L/h. S-N plots, micrographic analysis and surface analysis of the fracture surface are demonstrated. X46Cr13 (surface roughness Rz = 4) reached the maximum number of cycles (12.5 x 106) at stress amplitude of 173 MPa producing a low scatter range of 1:3.5. Hydroxide and siderite layers were found on pits and crack surfaces. No typical fatigue limit exists. Pit corrosion prior to crack initiation may be identified as failure cause.

Jan 1, 2016

By Charles L. Richman

The effect of the addition of Silver Sulfide on the rate of Chalcopyrite (CP) of Sulfuric acid (H2SD4 leaching is discussed, Although Ag2S in an expensive addition, a theoretical explanation of it&apos;s use will aid in the development of a economic substitution. We have used cyclic voltammography to show the presence reaction species at different potentials. Cyclic Voltammography maps the surface reaction current peaks on CP, to regions on the CP Phorbaix diagram. AC Electro-lmpedance spectroscopy (EIS) models the surface impedance properties, which control the rate of electron and ion transfer, and the surface kinetic reactions, with and with out light. EIS and other measurements show that AgCuS u Photo-reactive material- The EIS results are compared with the SEM and EDXA results to show the presence of diffusion pores, and diffusion controlled reactions during CP leaching without the addition of silver sulfate. We hypothesize that AgCuS is an ionic conductor like Ag2S. EIS shows an imposed negative leaching rate greatly. Our theory shows how the formation of Silver Copper (1) sulfide layer at open circuit potential gives an effect similar to negative potential, that is enhanced with illumination. We verify that AgCuAS is an N-type semiconductor that forms a diode type junction with the electrolyte with the Mott-Schoottly relation.

Jan 1, 2001

By Dirk Verhulst

The Altair Hydrochloride Pigment Process is a new ?third route?, besides the established high-temperature chloride process and the older sulfate process, to manufacture TiO2 pigment from ilmenite ore. It has been tested at a scale of 5 t/day feed. The ore concentrate is digested in high-acid, high total chloride solution (+/- 39% Cl). Titanium and iron both go into solution. Iron is separated as FeCl2 crystals after reduction and cooling. Titanium is transferred by solvent extraction into a purified, high-Ti stream. It is spray-hydrolyzed to produce a TiO2 hydrate and further calcined with additives into high-quality pigment. HCl solutions generated by pyrohydrolysis and spray hydrolysis are treated by pressure-swing distillation to regenerate HCl gas for re-injection into the digestion reactor. All chloride streams are recycled. Recent work has concentrated on optimization, particularly in 3 areas: - Solvent extraction: a new organic mixture, including a new diluent, makes it possible to work at room temperature, to avoid TiO2 hydrolysis problems and to improve phase disengagement and impurity separation. - Pigment finishing: a systematic study of the parameters involved, followed by long runs in the best conditions confirm pigment quality. - Flow sheet optimization: innovative modifications of the conditions of spray hydrolysis and pyrohydrolysis, combined with re-routing of streams achieve significant energy savings. A 100 t/year pilot plant including these features as well as other process improvements is under construction.

Jan 1, 2006

By K. L. Money, R. R. Bleakney, R. H. Hanewald

The processing of EAF baghouse dusts, rolling mill scales, and belt grinding swarfs from the specialty steel industry will be reviewed. In addition, the INMETCO process has been modified so as to recover nickel, chromium and iron from many other waste materials such as pickling solutions, filter cakes, spent nickel and chromium plating baths, super alloy wastes, and nickel-cadmium batteries. INMETCO is the only North American company presently capable of recycling nickel-cadmium batteries by high temperature metals recovery.

Jan 1, 2000

By Rudolf Keller

"EMEC Consultants is developing a process to extract oxygen, aluminum and silicon from lunar anorthositic soil. The process will provide oxygen in space for propulsion, aluminum as a structural material, and possibly silicon for the construction of solar cells.The evolution of the process concept in the course of our present NASA-sponsored SBIR effort is discussed. A molten salt electrolysis producing aluminum and oxygen is the central step; inert anode technology is to be employed. Silicon will be produced by reducing the anorthite, CaAI2Si20S' with aluminum. In a steady-state operation, all components of the ore added have to be removed from the process, and the removal of calcium is a major topic of our experimental studies.Utilization of Lunar ResourcesUtilization of lunar resources may play an essential role in the exploration of the solar system and the conquest of space. High costs are involved in overcoming Earth's gravity to supply missions in space. Even at a low projected cost of $ 300 for transporting a pound of payload into Earth orbit -- today's costs are many times higher -- it appears attractive to use resources in space to produce needed materials. Processing of lunar resources on the lunar surface is an obvious possibility.Oxygen is a product of major interest. It is required for support of human life in space. Even greater quantities may be needed for propulsion, to conduct further missions into space. To satisfy this demand for oxygen through lunar processing requires a quite different solution than to supply oxygen on Earth, where oxygen gas is abundant and easy to extract from air or water. On the lunar surface, solid oxide materials have to be used. Hydrogen reduction of ilmenite and subsequent electrolysis of the resulting water is being studied [1]. Other suggestions include fluorination of lunar soil [2], reduction with lithium and electrolytic decomposition of the resulting lithium oxide [3], and aqueous HF leaching [4]."

Jan 1, 1988