Anodizing Of AZ31 Magnesium Alloy In NaOH Solution

The anodic behavior of AZ31 magnesium alloy in NaOH alkaline solution was investigated in this paper. The effects of anodizing parameters, such as applied current density, concentration of NaOH and temperature of the solution on the formation, structure and surface morphology of the anodic films were also studied. The formation of the anodic film was analyzed by analyzing the anodic polarization curves, the potential-time curves and XRD, SEM graphs of samples obtained at different anodizing time. The results of corrosion resistance tests, XRD and SEM observation showed that the temperature greatly affected the formation and anti-corrosion property of the anodic film, but the concentration of NaOH not. The film with best anti-corrosion resistance was obtained at applied current density of 10mA/cm2, 353k in 1mol/l NaOH solution.