By Fangqing Yin, Qingyu Deng, Zhengfeng Qu, Mengjun Hu, Meilong Hu

Titanium bearing blast furnace slag, which contains 20%-30% TiO2, is a valuable secondary titanium resource. Based on the thermodynamics calculation effect of the temperature on the reduction of the slag in vacuum were studied at certain vacuum degrees. The results show that magnesium vapor and silicon monoxide vapor can be obtained at the condition of high temperature and low pressure. The purity of TiC increases with temperature increasing. When the temperature arrives at 1623K TiC can be obtained besides the reductant carbon. XRD result of the powder collected from the furnace cover show that magnesium and silicon in the titanium bearing BF slag leave the slag system during carbothermal reduction in vacuum. From the above it can be concluded that TiC can be obtained from the titanium bearing BF slag and silicon and titanium in the slag can be separated by carbothermal reduction in vacuum and acid leaching.

Jan 1, 2016

By Tiejun Chun, Jian Pan, Deqing Zhu, Zhiyong Ruan

"In this paper, the desulfuration of pyrite cinder pellets was carried out. Phase analysis shows that most sulfur of pyrite cinder exists in the form of elementary sulfur. Most sulfur was removed in preheating stage. 81.25% sulfur was removed and the average SO2 concentration of exhaust gas was 1365ppm when the pellets were preheated at 950oC for 9 min. The final product, assaying 62.42wt%Fe and 0.02wt%S content at 96.88% desulfuration was achieved under the conditions of preheating at 950? for 9 min and roasting at 1200? for 15 min, which can be used as the burden for blast furnace.IntroductionPyrite cinder, as a subsidiary product of sulfuric acid production by roasting of pyrite ores, was solid waste in sulfuric acid enterprises. According to the statistics, the annual production of pyrite cinder is about 15 million tons in China. Besides, there is lots of pyrite cinder deposited for many years [1-3]. The pyrite cinder consumed in the cement and other industries as auxiliary additives only accounts for less 30% of its total discharge and the left is stored in waste pond, occupying much land and polluting environment in China [4-5]. Moreover, pyrite cinder contains iron between 30-63% which can be utilized as a cheap raw material for ironmaking by sintering or pelletizing processes, which can not only prevent pollution but also provide cheap raw materials for ironmaking [6-7]. However, compared to traditional iron ore concentrate, pyrite cinder possesses higher sulfur content."

Jan 1, 2012

By ZHANG Ting

In view of the high consumption and contamination of traditional vanadium extraction technology, a new process of leaching the converter vanadium slag without roasting with titanium dioxide waste was proposed. Extraction mechanism of P204 in the leaching solution had been researched and single factor experiments show that after a prereduction of Fe, and under conditions: ambient temperature，leaching solution original pH=2.5, phase ratio (A/O)=1:3, shaking time 8min, the extraction rate of V is more than 98.62% meanwhile the separation rate between V and Fe is up to 135.3 in the 20%P204-10%TBP-Sulfonated kerosene extraction system.

Jan 1, 2015

By A. Tsubouchi, F. Noguchi, T. Takasu

"A high current density operation is desired to improve the productivity in copper electrorefining. However, a lot of problems still remain such as passivation at anode, dendritic deposition at cathode and impurity behavior during the electro refining.Effects of the current densitY on the morphology of copper deposition on the cathode, and passivation at the anode were investigated at various fluid velocity of electrolyte in the present study.Although a granular appearance of the copper deposition was obtained with increasing high current density, it was depressed by an increase of the fluid velocity of the electrolyte. A uniform deposition on the cathode was also observed when the fluid velocity of the electrolyte become higher. It was ascertained that passivation at the anode was suppressed by circulating electrolyte during electrolysis. INTRODUCTIONIt is desirable to operate at high current density in copper electrorefining in order to improve plant productivity without enlarging the size of electrodes(1). However, there are many problems in copper electrorefining at high current density with the usual commercial practice, for example, anode passivation, dendritic deposition and an increase of impurities in the cathode.In general, it is effective to agitate the electrolyte in order to suppress these problems(2). Smith et a1.(3) have performed electro refining experiments at various current densities in the range of 8 to 32 Aldm2 and at electrolyte fluid velocities in the range of 40 to 120 mlmin, and they obtained well consolidated, void free copper even at high current density in a high electrolyte velocity. However, they did not discuss the recovery ratio and the passivation behaviour at the anode. Walsh et a1.(4)(5)(6) experimented with the rotating cylinder electrode, and ascertained that electrolysis can be carried out at high current densities under the condition of pure electrolyte.With regards to anode passivation, there are several papers by previous workers(7)(8). Our group ascertained the process of producing anode slime during electrolysis(9). However, these experiments were carried out without forced circulation of electrolyte. Therefore, in the present study, to solve these problems, we electrolyzed at current densities in the range of 4 to 50 Aldm2 with circulating electrolyte in the range of 0 to 48 mlrnin. The effect of electrolyte fluid velocity on the surface morphology of deposited copper at cathode and passivation at anode were investigated when electrolysis were carried out with circulating electrolyte at high fluid velocity and at high current density."

Jan 1, 1997

By Duclerc Fernandes Parra, Washington Luiz Oliani, Christiano Gianesi Bastos Andrade, Ademar Benevolo Lugão, Danilo Marin Fermino, Francisco R. Valenzuela Diaz

This work concerns the study of the effect of discarded bond paper on the mechanical behavior of polypropylene/organophilic clay nanocomposites. A brown polycationic bentonite from the state of Paraíba, Brazil, was treated with sodium carbonate to transform it into a bentonite that swells in water and then treated with hexadecyltrimethylammonium ammonium chloride to transform it into a bentonite that swells in organic liquids. Polypropylene with 3 % polypropylene graft compatibilizer (PP-g-AM) was mixed with 1 % and 2 % by weight of discarded bond paper and with 1% and 2% by weight of organophilic clay using a twin-screw extruder. The specimens were prepared by the injection process. The clay as received and after organophilization was characterized by XRD, SEM, and capacity of swelling in water and in organic solvents. The nanocomposite specimens were characterized by XRD and thermal analysis. The mechanical behavior of the injected specimens was evaluated by strength, flexural and impact tests. The nanocomposites showed improved mechanical properties compared with the polymer without filler.

Jan 1, 2015

By Chuanhong Li, Zuohua Lin, Zhancheng Guo

"Catalytic mechanism of CeO2 in combustion of coals was investigated in this paper. Catalytic combustion of four kinds of coals with different metamorphic grades by CeO2 was examined, suggesting that catalytic function of CeO2 increases with increase of metamorphic grade of the coals. One important reason for CeO2 promoting combustion of the coals is that pyrolysis of anthracite is advanced by CeO2, which not only raises the pyrolysis rate and pyrolysis conversion ratio, but increases contents of light components in pyrolysis gas; and both pore space and specific surface area of the pyrolysis char are enlarged by CeO2, which is another reason. In order to realize in situ catalysis for reducing catalyst consumption, it is crucial to increase catalyst particle number and enhance the bonding force between catalyst and coal. In addition, remarkable energy saving effect was observed when a nanometer calcium-based rare earth catalyst obtained by hydro-thermal synthesis was applied to catalytic combustion of coal injection into blast furnace.Introduction Coal combustion is acknowledged as one of the most important coal applications. Since addition of catalysts could reduce the ignition temperature of pulverized coal and accelerate the coal combustion, catalytic combustion is generally accepted as an effective measure to realize fast combustion of coal. Furthermore, different catalysts added may produce different effects on ignition temperature of coal. It is reported activity of catalysts with the same cation follows this order: OH->CO3 2->Cl->SO4 2-; while that of the catalysts which have the same anion follows: Cs+>Rb+>K+>Na+>Ba2+>Li+>Sr2+>Ca2+>Mg2+>Be2+ [1-4] .Due to the special physical and chemical structure, CeO2 plays an important role in the catalysis field. Many literatures point out that CeO2 not only has great catalytic effect on energy conversion, succeeded in catalyzing combustion of gaseous fuels such as CH4, CO, etc. but also can catalyze combustion of some liquid and solid fuels such as JP-10, black carbon, carbon deposit in the automobile exhausts and so on [5-9].Pyrolysis, the first step of combustion, directly influences ignition temperature and combustion rate of coals. So a great variety of catalysts were applied to catalyze pyrolysis of coals. And plenty of studies suggest that the alkali and alkaline-earth metal compounds inherent in the coals show apparent catalytic effect on coal pyrolysis. Meanwhile, addition of alkali and alkaline-earth metals into coal combustion process also indicates obvious catalysis effect, accelerating coal pyrolysis, improving pyrolysis conversion ratio, increasing contents of pyrolysis gases and changing composition of the pyrolysis gases [10-15].Although alkali and alkaline-earth metal compounds have good catalysis effect on coal combustion, their application in the catalysis field was limited because of their erosive attack to the combustion equipments. In contrast, CeO2, as a substitution of the traditional coal catalysts, presents widely potential application due to its good catalysis ability, non-corrosive and nontoxic. However, investigation on CeO2 catalyzing coal combustion is rarely reported. In this work, catalytic mechanism of CeO2 in coal combustion was studied, in an attempt to provide theoretical foundation for developing new catalysis technologies."

Jan 1, 2009

By Hong N. Vu, Jitka Jandova

"Gypsum and limestone methods were examined in this study to process zinnwaldite wastes originating from dressing Sn-W ores mined in the Czech Republic. These wastes containing 0.20-0.30% Li and 0.10-0.20% Rb were subjected to magnetic separation to obtain a zinnwaldite concentrate with 1.36% Li and 0.94% Rb. It was observed that processing of the zinnwaldite concentrate with gypsum resulted in almost 96% recovery of Li into aqueous liquors, whilst rubidium extraction was only 25%. At the same time, it is possible to extract almost 92% Li and Rb from the identical zinnwaldite concentrate if the concentrate is processed by limestone method. Lithium carbonate, a final product of both methods was recovered from the refined sulphate solution using K2CO3 as a precipitation agent and/or from unrefined hydroxide solution using gaseous CO2. In the continuation of this study, rubidium will be separated from carbonate solutions after Li2CO3 precipitation as RbAl(SO4)2, an intermediate for Rb2CO3 production. IntroductionLithium is used as an alloying constituent in lightweight alloys, as a heat transfer medium in nuclear reactors and as a component in primary and secondary batteries. With the development of a new generation of electric vehicles, the lithium demand will dramatically grow. Lithium chemicals find extensive application in many industrial branches such as metallurgical, glass, ceramic and pharmaceutical industries. Rubidium compounds are predominantly used in psychiatry and medicine, in magneto-optic modulators, solid-state lasers, phosphors and components of electrolytes for fuel cells. The four most important lithium minerals are amblygonite, spodumene, petalite, and lepidolite. Spodumene LiAlSi2O6 (6.0-7.5% Li2O) and petalite LiAlSi4O10 (3.5-4.5% Li2O) belong to aluminosilcate minerals. Lepidolite (Li.Al)3(Al.Si)4O10(F.OH)2 (3.30-7.74% Li2O), lithium mica, is the most important representative of the mica minerals, a subgroup of the aluminosilicates. It frequently contains 3–5% Rb2O and eventually caesium. Zinnwaldite, which has the general formula K(Li.Al.Fe)3(Al.Si)4O10(F.OH)2 (2-5% Li2O), is regarded as a variety of lepidolite with a high iron content. Commercial amblygonite is a complex phosphate (Li.Na)Al(F.OH)PO4 (up to 9.88% Li2O), however, its deposits have not been commercially exploited because of their small size. Natural brines with a high lithium chloride content are important in the industrial production of lithium [l]"

Jan 1, 2008

By Akira Yazawa, Kazuo Koike, Mitsuhisa Hino

"The vapor pressures of MS (PbS, SnS and Sb2S3) in the molten Cu2S-MS, FeS-MS pseudo-binary and Cu2S-FeS-MS ternary systems were measured by means of a transportation method in the temperature range of 1323 and 1423K to calculate MS activities in the sulfide melts. The activities of MS in these systems show negative deviation from ideal behavior except the FeS binary systems which exhibit nearly ideal behavior in the homogeneous melts. The activities of the Cu2S-FeS pseudobinary system, which is fundamentals of the copper matte, were estimated from the activity values in the ternary systems and exhibit negative deviation from ideality.The distribution behavior of tin between the ·matte and silica saturated fayalite slag was investigated under the controlled partial pressures of S02 at l 523K. It was found that, in general, tin is distributed in the both phase, while tin is concentrated to the slag phase with increasing copper content in the matte. The activity coefficient of SnO in the slag was calculated based on the distribution ratio combined with the activity coefficient in the Cu2S-FeS system.IntroductionThe thermodynamic properties related to the Cu2S-FeS system and the Cu2S-FeS-MS systems (where MS can be PbS, SnS, Sb2S3, As2S3, Bi2S3, etc.) is required to be better understanding of the copper smelting process. However, thermodynamic analysis such as the distribution of impurities among the gas, slag and matte phases is difficult due to lack of thermodynamic data. In this study, the vapor pressures of MS (PbS, SnS and Sb2S3) in the Cu2S-MS, FeS-MS. and Cu2S-FeS-MS systems were measured by a transportation method. The distribution behavior of tin between the matte and silica saturated fayalite slag was also investigated. The results in the present experiments are useful to analyze thermodynamically the behavior of component in the copper matte smelting."

Jan 1, 2000

By Upali Siriwardane, Tushar V. Kudale, Naidu V. Seetala

"Cellulose acetate (CA) membranes with 25% triethyl citrate (TEC) as plasticizer were prepared with varying thickness for CO2 gas separation from water-gas-shift (WGS) reaction products. The AFM analysis of the CA membrane showed that the uniform coating had fewer and smaller pores as the film thickness increased, and corroborated by gas permeability studies. The CO2 permeability has decreased faster than CO permeability with the CA/TEC membrane thickness, and findings support that the CA membrane could be used to entrap CO2. Several CA/TEC membranes were also staked to increase the separation efficiency. Positron Annihilation Lifetime Spectroscopy (PALS) was used to estimate the nano-porosity (pore size and concentration) changes of CA/TEC films. PALS results show a decrease in pore size with increasing CA-TEC concentration in acetone, while the pore concentration increases. The PALS results are correlated with the CO2/CO permeability variations as the CA-TEC concentration change.IntroductionHydrogen is one of the main energy sources available for the future advancement of clean fuel technologies especially for fuel cells. Generation of hydrogen and CO2 from Water Gas Shift (WGS) reaction mixtures of CO and H2O is of interest to many researchers since it allows a large scale production of hydrogen [1, 2]. Once hydrogen is produced using the WGS reaction, the output products contain mixture of CO, CO2, H2, and water vapor. Metallic membranes have been used as hydrogen separation membranes [3-6]. As H2 is separated from the mixture using the metal membranes, we need to separate CO2, and find ways of sequestration of CO2 to avoid environmental problems by greenhouse gasses. Polymeric Membranes have been used for CO2 separation [7]. Plasticizer can control the micro-structural properties such as pore size and concentration of polymer membranes [8], which influence the size/molecular weight dependent diffusion rates of the gas molecules. We have used cellulose acetate with triethyl citrate as plasticizer to separate CO2 from the WGS reaction products. Positron annihilation lifetime spectroscopy (PALS) is very sensitive and able to identify different kinds of defects and their agglomerates such as vacancies, vacancy loops, and voids [9, 10]. PALS has been successful in determining the free volume in polymers that influence the properties of the polymers [11, 12]. Microscopic properties of the free volume obtained from PALS have been correlated to macroscopic properties [13, 14]. We used PALS to study the nanoporosity (pore size and concentration) and fractional free volume changes of CA/TEC films, and used to understand the variations observed in the CO2/CO permeability as the CA-TEC concentration in the membranes change."

Jan 1, 2014

By Zenjiro Asaki, Teruo Tanabe

"To clarify the formation of light rare earth (R =Ce, Pr, Nd or Sm) -Fe compounds in the reduction-diffusion (RD) process, two kinds of experiments were carried out: (a) RD experiment in which briquettes composed of R oxide powder, Fe (particles or wire) and CaH2 were reacted, and (b) immersion experiment, where an Fe plate was immersed into R-Fe melt having the composition of Fe-side liquidus line in Fe crucible. The compound formation was examined by using XRD, SEM and EPMA. The formation rates of RzFe17 measured by the RD experiment were compared with those obtained by the immersion experiment. The growth rates of compounds obtained in the RD experiment for Pr-Fe and Nd-Fe systems were much lower than those obtained in the immersion experiment. This result was explained by the difference of the reduction rates of R oxides by Ca. The parabolic rate constants for the formation of RzFe17 were separated in two groups of (a) Pr-Fe and Nd-Fe systems and (b) Ce-Fe and Sm-Fe systems. This was discussed in connection with the difference of their crystal structures and the driving force of diffusion. The parabolic rate constants for the formation of compounds in Ce-Fe and Sm-Fe systems decreased in the order of RFez, RFe3 and RzFe17.IntroductionTo understand reaction behaviors in the production of rare earth (R) -iron intermetallic compounds, which have excellent magnetic properties, is very important from engineering point of view. And the reduction-diffusion (RD) process<O has recently attracted attention as one of the promising processes to economically produce R-related materials. A few fundamental studies on the compounds formation in the RD process have previously been reported. Qi, Hino and Yazawa(2) observed the formation of R(Nd, Sm)-Fe and R-Co compounds in the process from various view points. Song and Ogawa(3) measured the growth rates of Nd-Fe and Sm-Fe compounds by using Nd or Sm vapor supplied from Nd-Ca or Sm-Ca melts. The authors have also carried out fundamental studies (4)-(8) to clarify the rate and mechanism in the production of R-Fe intermetallic compounds."

Jan 1, 1998

By Chuan-fu Zhang

The fibrous precursor can be obtained by coordination precipitation process, using oxalate, cobalt chloride and ammonia. XRD pattern of precursor precipitated at pH=9.0 is different from that of ß-CoC2O4?2H2O precipitated at pH=1.0 which indicates that the precursor powders are one type of cobalt complex. According to the results of element analysis and IR spectra, it can be inferred that the composition of the precursor is [Co(NH3)x]C2O4?H2O(x=1.2?..6) formed by the coordination reaction at pH=9.00 in the Co(II)-C2O42--NH3-NH4+-H2O system. It?s found that the fibrous cobalt powders greatly inherited the morphologies of the precursors. Many factors could affect the formation of the fibrous cobalt precursor powders, such as the initial Co2+concentration, pH value and so on. The SEM images show how they influence the morphologies of the precursor powders. By adding proper surfactant, the dispersion of the precursor powders would be improved. At last, the final product-fibrous cobalt powders which are about 0.3~0.5min size and 40~60 in aspect ratio were produced by thermal decomposition of fibrous cobalt complex at 400~500°C in the weak reducing atmosphere.

Jan 1, 2006

By René Winand

Due to chemical and electrochemical behavior of the most common additives in copper electrorefining i.e. gelatine, thiourea and chloride ions, it is essential to simulate as far as possible true industrial practice while performing laboratory experiments. The three additives must be studied simultaneously, and added continuously to the electrorefining cell. Ratio electrolyte volume to cathode area; ratio bleed flow to cathode area; hydrodynamic conditions; residence time of electrolyte in the cell; current density; electrolyte and soluble anode must be as near as possible to industrial ones. Experiments performed in the author&apos;s laboratory show that under these conditions, reproducible results can be obtained at normal industrial current density and at high current density as well. Problems are however still encountered when developing a sensor for additives monitoring, due to electrolyte redox potential and to substrate influenced thin layer deposition.

Jan 1, 1995

By Steven Wright

BHP Billiton?s Olympic Dam copper flash smelter employs the direct to blister process for smelting high grade copper concentrates. SO2 evolution during tapping gives rise to safety concerns. A thermodynamic model for the blister copper (Cu-Fe-S-O) was used to predict the volumes of SO2 evolved. The Multiple Phase Equilibria Model (MPE) was used to evaluate the slag chemistry inside the furnace. The blister copper model was used to explore the relationship between %S and %O in the copper and the amount of SO2 evolved on cooling. The volume of SO2 evolved was sensitive to the O content with reduction to levels below 0.2 ? 0.15% likely to suppress SO2evolution on cooling. Concentrations of S and O in copper samples from trials generally lay above the equilibrium line calculated for an average temperature of 1275C and a partial pressure of SO2 of 1 atm. Consequently there is a thermodynamic driving force for SO2evolution when cooling to this temperature during tapping. A number of potential process options to suppress SO2 evolution on tapping were investigated thermodynamically. Some of the options require treatment of the blister in a forehearth or separate furnace, while others impact on current practises in the flash furnace with slag present. The opportunities that these options present are discussed.

Jan 1, 2006

By Yuhsuke Mizukami

Crude high Cr containing steel such as tool steel, heat-resistant steel or stainless steel is produced by dissolution of high carbon ferro-chromium into molten crude steel. In the refining process, decarburization is performed at the first stage, and deoxidation is followed in the next stage. Therefore, the equilibrium relation between dissolved Cr and 0 in molten Fe-Cr alloy after decarburization is very important when yield of deoxidizer is considered for the ovemll control and optimization of the process. It is well known that the yield of deoxidizer does strongly depend on the kinds of refractories of furnace in the secondary refining process. In the present work, the equilibrium relation between dissolved Cr and O in molten Fe-Cr alloy has been measured in a Cr2O3, MgO or Al2O3 crucible at steelmaking temperature. O contents at given Fe-Cr components have been lower in order of Cr2O3, Al2O3 and MgO crucible. The present results have been discussed based on the activities of the constituents in pure solid Cr2O3, and FeO-Cr2O3, MgO Cr2O3 and (AI,Cr)2O3 solid solutions.

Jan 1, 2003

By P. A. Metz

The Fairbanks mining district has produced in excess of 7.5 million troy ounces of placer gold and 250,000 troy ounces of lode gold since gold was discovered in the area in 1902. The Fairbanks mining district is in the northwestern part of the Yukon-Tanana Upland Schist Terrane, an area of approximately 240,000 square km that has produced in excess of 21 million troy ounces of placer gold. All lode gold production from the terrane has been from the Fairbanks mining district, and all of this production has come from high-grade gold-quartz polymetallic sulfide veins. Gold grains in the vein systems range in size from several microns to several millimeters. The veins are localized in a complex metamorphic rock assemblage which includes greenstones and felsic metavolcanic and volcaniclastic rocks, meta-exhalatives and metasediments. Gold occurs in the metamorphic host rocks in association with arsenopyrite and arsenic-antimony sulfides which occur in lenses and disseminations within the host rock. Gold grains occurring in the metamorphic host rocks range. in size from sub-micron to a few microns in diameter.

Jan 1, 1987

By R. G. Reddy

The effect of solid particles on viscosity behavior of Na2O-O-B2O3-SiO2 melts of composition XSio2/XNa2o =0.5 and in the temperature range of 900- 1150 K was studied. Samples were analyzed by X-ray diffraction and optical microscopy. The results showed that a crystalline phase (NaBO2) was formed and its amount increases with decrease in X,, from 0.50 to 0.25. The experimental viscosity values were compared with the predicted values using our viscosity model developed earlier. At low temperatures, for low content of B2O3 , the experimental values exhibits a large deviation from the predicted values. It was concluded that the deviation was due to the formation of solid particles in the molten slags. The existence of these solid particles increased the viscosity values significantly. A new viscosity model was developed to include the effect of solid particles.

Jan 1, 1993

By Nobuaki Sato, Tetsuo Fukasawa, Akira Kirishima

To apply the fluoride volatility process for the treatment of fuel debris formed in the damaged nuclear reactors, study on the fluorination behavior of main constituents, such as fuel and cladding is essential. The mixture of uranium and zirconium oxides is formed under severe conditions such as high temperature and oxidizing atmospheres. In this paper, fluorination and volatilization behavior of uranium and zirconium oxides have been studied by TG-DTA method in the presence of fluorine. From the TG-DTA result of UO2 in F2 atmosphere, the weight gradually increased up to 7% at 350 oC followed by rapid weight decrease with exothermic peak showing the vaporization of uranium as UF6. ZrO2 showed similar fluorination behavior to that of UO2. However, fluorination of UO2-ZrO2 seemed to be suppressed with increasing ZrO2 amount. This may be caused by the formation of solid solution.

Jan 1, 2016

By W. K. Collins

Engineered Scavenger Compounds (ESCs), developed by the U.S. Bureau of Mines, are a novel class of compounds that can selectively recover a desired element from a solid or molten alloy. Lithium titanate (Li2Ti3O7 or L&apos;20-3T&apos;02) is being used as an ESC to recover lithium (Li) from Aluminum-Lithium (Al-Li) alloys. X-ray diffraction measurements have shown that lithium titanate undergoes a phase change from an orthorhombic structure to a hexagonal structure. This change is due to the incorporation of Li in the matrix of the material and the effect of temperature. Although both are metastable, the hexagonal phase that forms during the scavenging of Li from Al-Li alloys appears to be the more stable phase. Recovering Li from the ESC by electrodeposition does not cause the structure to revert to the orthorhombic phase. Both the orthorhombic and the hexagonal structures of Li2Ti3O7 have similar scavenging capacities for Li. This paper proposes a new mechanism for the phase transformation.

Jan 1, 1993

By P. Chris Pistorius

An example is presented to illustrate the joint effect of local reaction equilibria and mass transfer limitations, for reactions during ladle refining of steel. The example relies on some of the kinetic principles that David Robertson has employed to quantify many metallurgical processes. In calcium treatment of alumina inclusions in aluminum-killed steels, solid CaS forms as an intermediate reaction product. During subsequent reaction, CaS disappears and calcium aluminate forms; at the same time, aluminum and sulfur dissolve in the steel. Kinetic analysis shows that the rate of this reaction is not limited by mass transfer of dissolved aluminum and sulfur away from the reacting inclusions. The reaction rate is likely limited by transport of dissolved calcium. This example also illustrates the use of FactSage macros for kinetic modeling.

Jan 1, 2014

By Zhijing Zhang

Sodium borosilicate is the basic composition of coating materials, Vycor and Pyrex glasses. In the present study, viscosities of Na2O-Si02-B2O3 ternary melts were measured under various compositions and temperatures. Experiments were carried out using rotary viscometer and graphite components. Our experimental results were compared with those in literature. Based on present experimental results, the previous structure based viscosity model was modified. The predicted viscosity results are in excellent agreement with the present experimental data in the temperature range with molten state samples. The fitting ranges of the model cover the composition of XB2O3 from 0.1 to 0.6 combined with xSio2 / xNa2O = 0.5, 1,2 and 5 respectively.

Jan 1, 1998